CN109126072A - A kind of titanium alloy bar mallet manufacture craft - Google Patents
A kind of titanium alloy bar mallet manufacture craft Download PDFInfo
- Publication number
- CN109126072A CN109126072A CN201811363054.9A CN201811363054A CN109126072A CN 109126072 A CN109126072 A CN 109126072A CN 201811363054 A CN201811363054 A CN 201811363054A CN 109126072 A CN109126072 A CN 109126072A
- Authority
- CN
- China
- Prior art keywords
- profile
- titanium alloy
- stick
- caput
- tail
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of titanium alloy bar mallet manufacture crafts, specifically includes the following steps: S1, preceding working process: choosing the spiral titanium alloy plate of corresponding size respectively first and detected to the smoothness on titanium alloy plate surface and the integrality of titanium alloy sheet of selection, after detection is qualified, it is cut according to the size of titanium alloy sheet needed for each position of baseball rod by sheet cutting machine, is related to sports facility processing technique field.The titanium alloy bar mallet manufacture craft, the rigidity and hardness of baseball rod can be greatly enhanced, service life is greatly prolonged, baseball rod is avoided in long-term impact use process well, the case where pit or slight crack occur occurs, it realizes and the mechanical property of baseball rod is improved from material and production technology, realize and carry out heat treatment process, sand blasting process and hardening process in the production process of baseball rod to improve the anti-strike ability and mechanical property of baseball rod.
Description
Technical field
The present invention relates to sports facility processing technique field, specially a kind of titanium alloy bar mallet manufacture craft.
Background technique
Baseball is that one kind is played ball with ear of maize as main feature, the very strong ball game project of communality, antagonism, it
Carry out in the world relatively broad, be affected, be known as " combinations of sports and wisdom ", play ball used in ear of maize be exactly baseball
Rod, baseball rod are that batter is used to the ear of maize batted in baseball game, common are wooden stick, aluminium bar and three kinds of composite bat,
The material of middle composite bat is that poplar, maple and bamboo chip polymeric compressing form, also referred to as compressed rod, synthetic rod or bamboo stick,
The advantages of having merged wooden stick and aluminium bar due to composite bat, elasticity is preferable and not easy to break, and power when hitting in fact will not
It is defeated by aluminium bar, so not being allowed to use usually in general international regulation game occasion, but due to world stick at present
Ball always actively use instead under the policy of wooden stick comprehensively by expansion international sports event, and composite bat has been considered as before using wooden stick instead comprehensively
Transition bat, at home in three-level baseball game, bat is unlikely to be certainly made by fine aluminium, is usually with alloy composition
Main, the use of aluminium bar increasingly declines, but still sees aluminium bar sometimes in three-level baseball game at home at present
Figure.
Current baseball rod rigidity and hardness are lower, and service life is shorter, in long-term impact use process, it may appear that
Pit or slight crack can not achieve and improve from material and production technology to the mechanical property of baseball rod, be unable to reach and pass through
Wooden baseball rod and aluminum baseball rod are replaced using titanium alloy, make to improve baseball rod mechanical property under the premise of not increasing weight
Purpose, can not achieve and carry out heat treatment process, sand blasting process and hardening process in the production process of baseball rod
The anti-strike ability and mechanical property of baseball rod are improved, so that baseball rod, which is used for a long time, to people brings great inconvenience.
Summary of the invention
(1) the technical issues of solving
In view of the deficiencies of the prior art, the present invention provides a kind of titanium alloy bar mallet manufacture craft, existing baseball is solved
Rod rigidity and hardness are lower, and service life is shorter, in long-term impact use process, it may appear that pit or slight crack, Bu Nengshi
Now the mechanical property of baseball rod is improved from material and production technology, is unable to reach by using titanium alloy and replaces wood
Matter baseball rod and aluminum baseball rod make the purpose for improving baseball rod mechanical property under the premise of not increasing weight, can not achieve
Heat treatment process, sand blasting process and hardening process are carried out in the production process of baseball rod to improve the resistance of baseball rod
The problem of ability of beating and mechanical property.
(2) technical solution
In order to achieve the above object, the present invention is achieved by the following technical programs: a kind of titanium alloy bar mallet manufacture craft, tool
Body the following steps are included:
S1, preceding working process: the spiral titanium alloy plate of corresponding size and the titanium alloy plate table to selection are chosen respectively first
The smoothness in face and the integrality of titanium alloy sheet are detected, after detection is qualified, according to titanium alloy needed for each position of baseball rod
The size of plate is cut by sheet cutting machine, and is carried out at coding to three the stick body that cuts out, caput and stick tail parts
Reason, then by the stick body titanium alloy sheet cut out, caput titanium alloy sheet and stick tail titanium alloy sheet by l spiral forming machine carry out at
Shape processing, laser welding is then carried out, the forming titanium alloy plate of stick body, caput and stick tail can be obtained, after shaping later
The part that stick body titanium alloy plate both ends are rolled is welded, and stick body blank is made to reach standard, to complete baseball rod selection
Pre-treatment work；
S2, finishing processing: the stick body profile formed in S1, caput profile and stick tail profile are subjected to shaping respectively
Processing, makes stick body profile, the shape radian size of caput profile and stick tail profile and plumpness size reach requirement, then distinguishes
The port of stick body profile, caput profile and stick tail profile is ground, the end of stick body profile, caput profile and stick tail profile is made
Mouth is smooth and reaches fitted position requirement, carries out frictional behaviour to the port of stick body profile, caput profile and stick tail profile later
Detection respectively carries out the material of stick body profile, caput profile and stick tail profile using metal rigidity tester after detection is qualified
Rigidity test, and record test result；
S3, heat treatment and sandblasting: the temperature and time of heat treatment is calculated according to the result that S2 is tested, and after S2 is finished
Stick body profile, caput profile and stick tail profile are put into heat-treatment furnace and are heat-treated, and carry out rigidity again after the completion of heat nursing
Test, and determine whether the rigid nature of each component reaches standard, later by stick body profile up to standard, caput profile and stick tail type
Material carries out blasting treatment；
S4, combination cure process: selection FRP material first, and the FRP material of selection is subjected to volume item processing, it then will roll up item
Good FRP is mounted at the end of the stick body profile after S3 blasting treatment, caput profile and stick tail profile, will be installed respectively later
Stick body profile, caput profile and the stick tail profile of FRP volumes of item are combined assembly, and baseball rod blank body can be obtained, right later
Baseball bat blank body carries out after-hardening processing, and carries out hardness determination；
S5, coating and packing processes: the baseball rod blank body after S4 cure process is subjected to spray treatment, according to baseball rod coating
Design requirement, in the surface sprayed coating of baseball rod blank body, baseball rod after processing is completed, Zhi Houzai is can be obtained in drying
It is assembled and is packed, that is, may be sold or warehousing.
Preferably, the impact molding machine in the step S1 in use, can pass through the punching press on replacement press machine
Mold, to be processed to stick body titanium alloy sheet, caput titanium alloy sheet and stick tail titanium alloy sheet.
Preferably, the welding in the step S1 is welded using laser-beam welding machine, the model of laser-beam welding machine
DPF-W150, optical maser wavelength 1070nm, and pulse frequency is 1-2500Hz.
Preferably, the metal rigidity tester measurement force value range in the step S2 and step S3 is 0-750N, and under
Plate connects high-precision special pressure sensor.
Preferably, the blasting treatment in the step S3 is to use suction-type dry blasting machine, and sandblasting grade is Sa2.5
Grade.
Preferably, the cure process in the step S4 is to plate one layer of crome metal protection on the surface of baseball bat blank body
Film.
(3) beneficial effect
The present invention provides a kind of titanium alloy bar mallet manufacture crafts.Have compared with prior art following the utility model has the advantages that the titanium
Alloy baseball rod manufacture craft, specifically includes the following steps: S1, preceding working process: choosing the spiral of corresponding size respectively first
Titanium alloy plate simultaneously detects the smoothness on titanium alloy plate surface and the integrality of titanium alloy sheet of selection, and detection is qualified
Afterwards, the size of the titanium alloy sheet according to needed for baseball rod each position is cut by sheet cutting machine, and to the stick cut out
Body, caput and three, stick tail part carry out coded treatments, S2, finishing processing: by the stick body profile formed in S1,
Caput profile and stick tail profile carry out Shape correction respectively, make the shape radian ruler of stick body profile, caput profile and stick tail profile
Very little and plumpness size reaches requirement, then grinds, makes to the port of stick body profile, caput profile and stick tail profile respectively
The port of stick body profile, caput profile and stick tail profile is smooth and reaches fitted position requirement, S3, heat treatment and sandblasting: according to
The result of S2 test calculates the temperature and time of heat treatment, and stick body profile, caput profile and stick tail after S2 is finished
Profile is put into heat-treatment furnace and is heat-treated, and carries out rigid test after the completion of heat nursing again, and determine the rigidity of each component
Whether performance reaches standard, and stick body profile up to standard, caput profile and stick tail profile are carried out blasting treatment, S4, combination later
Cure process: selection FRP material first, and the FRP material of selection is subjected to volume item processing, it then will roll up the good FRP of item and install
At the end of stick body profile, caput profile and stick tail profile after S3 blasting treatment, the stick of FRP volumes of item will be installed respectively later
Body profile, caput profile and stick tail profile are combined assembly, S5, coating and packing processes: by the baseball after S4 cure process
Rod blank body carries out spray treatment, is dried according to the design requirement of baseball rod coating in the surface sprayed coating of baseball rod blank body
The dry baseball rod that can be obtained after processing is completed, is assembled and is packed again later, that is, may be sold or warehousing, can be increased
The rigidity and hardness of strong baseball rod, service life are greatly prolonged, and are avoided baseball rod well and are used in long-term impact
In the process, there is the generation of the case where pit or slight crack, realize from material and production technology to the mechanical property of baseball rod into
Row improves, and has reached by using titanium alloy and has replaced wooden baseball rod and aluminum baseball rod, has made under the premise of not increasing weight
The purpose of baseball rod mechanical property is improved, realizes and carries out heat treatment process, sand blasting process in the production process of baseball rod
The anti-strike ability and mechanical property of baseball rod are improved with hardening process, so that greatly facilitating people is used for a long time stick
Mallet.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
The embodiment of the present invention provides a kind of technical solution: a kind of titanium alloy bar mallet manufacture craft specifically includes following step
It is rapid:
S1, preceding working process: the spiral titanium alloy plate of corresponding size and the titanium alloy plate table to selection are chosen respectively first
The smoothness in face and the integrality of titanium alloy sheet are detected, after detection is qualified, according to titanium alloy needed for each position of baseball rod
The size of plate is cut by sheet cutting machine, and is carried out at coding to three the stick body that cuts out, caput and stick tail parts
Reason, then by the stick body titanium alloy sheet cut out, caput titanium alloy sheet and stick tail titanium alloy sheet by l spiral forming machine carry out at
Shape processing, laser welding is then carried out, the forming titanium alloy plate of stick body, caput and stick tail can be obtained, after shaping later
The part that stick body titanium alloy plate both ends are rolled is welded, and stick body blank is made to reach standard, to complete baseball rod selection
Pre-treatment work；
S2, finishing processing: the stick body profile formed in S1, caput profile and stick tail profile are subjected to shaping respectively
Processing, makes stick body profile, the shape radian size of caput profile and stick tail profile and plumpness size reach requirement, then distinguishes
The port of stick body profile, caput profile and stick tail profile is ground, the end of stick body profile, caput profile and stick tail profile is made
Mouth is smooth and reaches fitted position requirement, carries out frictional behaviour to the port of stick body profile, caput profile and stick tail profile later
Detection respectively carries out the material of stick body profile, caput profile and stick tail profile using metal rigidity tester after detection is qualified
Rigidity test, and record test result；
S3, heat treatment and sandblasting: the temperature and time of heat treatment is calculated according to the result that S2 is tested, and after S2 is finished
Stick body profile, caput profile and stick tail profile are put into heat-treatment furnace and are heat-treated, and carry out rigidity again after the completion of heat nursing
Test, and determine whether the rigid nature of each component reaches standard, later by stick body profile up to standard, caput profile and stick tail type
Material carries out blasting treatment；
S4, combination cure process: selection FRP material first, and the FRP material of selection is subjected to volume item processing, it then will roll up item
Good FRP is mounted at the end of the stick body profile after S3 blasting treatment, caput profile and stick tail profile, will be installed respectively later
Stick body profile, caput profile and the stick tail profile of FRP volumes of item are combined assembly, and baseball rod blank body can be obtained, right later
Baseball bat blank body carries out after-hardening processing, and carries out hardness determination；
S5, coating and packing processes: the baseball rod blank body after S4 cure process is subjected to spray treatment, according to baseball rod coating
Design requirement, in the surface sprayed coating of baseball rod blank body, baseball rod after processing is completed, Zhi Houzai is can be obtained in drying
It is assembled and is packed, that is, may be sold or warehousing.
In the present invention, the impact molding machine in step S1 in use, can pass through the stamping die on replacement press machine
Tool, to be processed to stick body titanium alloy sheet, caput titanium alloy sheet and stick tail titanium alloy sheet.
In the present invention, the welding in step S1 is welded using laser-beam welding machine, the model of laser-beam welding machine
DPF-W150, optical maser wavelength 1070nm, and pulse frequency is 1-2500Hz.
In the present invention, the metal rigidity tester measurement force value range in step S2 and step S3 is 0-750N, and lower flat
Plate connects high-precision special pressure sensor.
In the present invention, the blasting treatment in step S3 is to use suction-type dry blasting machine, and sandblasting grade is Sa2.5 grades.
In the present invention, the cure process in step S4 is to plate one layer of crome metal protective film on the surface of baseball bat blank body.
It should be noted that, in this document, relational terms such as first and second and the like are used merely to a reality
Body or operation are distinguished with another entity or operation, are deposited without necessarily requiring or implying between these entities or operation
In any actual relationship or order or sequence.Moreover, the terms "include", "comprise" or its any other variant are intended to
Non-exclusive inclusion, so that the process, method, article or equipment including a series of elements is not only wanted including those
Element, but also including other elements that are not explicitly listed, or further include for this process, method, article or equipment
Intrinsic element.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (6)
1. a kind of titanium alloy bar mallet manufacture craft, it is characterised in that: specifically includes the following steps:
S1, preceding working process: the spiral titanium alloy plate of corresponding size and the titanium alloy plate table to selection are chosen respectively first
The smoothness in face and the integrality of titanium alloy sheet are detected, after detection is qualified, according to titanium alloy needed for each position of baseball rod
The size of plate is cut by sheet cutting machine, and is carried out at coding to three the stick body that cuts out, caput and stick tail parts
Reason, then by the stick body titanium alloy sheet cut out, caput titanium alloy sheet and stick tail titanium alloy sheet by l spiral forming machine carry out at
Shape processing, laser welding is then carried out, the forming titanium alloy plate of stick body, caput and stick tail can be obtained, after shaping later
The part that stick body titanium alloy plate both ends are rolled is welded, and stick body blank is made to reach standard, to complete baseball rod selection
Pre-treatment work；
S2, finishing processing: the stick body profile formed in S1, caput profile and stick tail profile are subjected to shaping respectively
Processing, makes stick body profile, the shape radian size of caput profile and stick tail profile and plumpness size reach requirement, then distinguishes
The port of stick body profile, caput profile and stick tail profile is ground, the end of stick body profile, caput profile and stick tail profile is made
Mouth is smooth and reaches fitted position requirement, carries out frictional behaviour to the port of stick body profile, caput profile and stick tail profile later
Detection respectively carries out the material of stick body profile, caput profile and stick tail profile using metal rigidity tester after detection is qualified
Rigidity test, and record test result；
S3, heat treatment and sandblasting: the temperature and time of heat treatment is calculated according to the result that S2 is tested, and after S2 is finished
Stick body profile, caput profile and stick tail profile are put into heat-treatment furnace and are heat-treated, and carry out rigidity again after the completion of heat nursing
Test, and determine whether the rigid nature of each component reaches standard, later by stick body profile up to standard, caput profile and stick tail type
Material carries out blasting treatment；
S4, combination cure process: selection FRP material first, and the FRP material of selection is subjected to volume item processing, it then will roll up item
Good FRP is mounted at the end of the stick body profile after S3 blasting treatment, caput profile and stick tail profile, will be installed respectively later
Stick body profile, caput profile and the stick tail profile of FRP volumes of item are combined assembly, and baseball rod blank body can be obtained, right later
Baseball bat blank body carries out after-hardening processing, and carries out hardness determination；
S5, coating and packing processes: the baseball rod blank body after S4 cure process is subjected to spray treatment, according to baseball rod coating
Design requirement, in the surface sprayed coating of baseball rod blank body, baseball rod after processing is completed, Zhi Houzai is can be obtained in drying
It is assembled and is packed, that is, may be sold or warehousing.
2. a kind of titanium alloy bar mallet manufacture craft according to claim 1, it is characterised in that: rushing in the step S1
Pressing machine in use, can be by the stamping die on replacement press machine, to stick body titanium alloy sheet, caput titanium alloy
Plate and stick tail titanium alloy sheet are processed.
3. a kind of titanium alloy bar mallet manufacture craft according to claim 1, it is characterised in that: the weldering in the step S1
Connecing is welded using laser-beam welding machine, the model DPF-W150 of laser-beam welding machine, optical maser wavelength 1070nm, and pulse
Frequency is 1-2500Hz.
4. a kind of titanium alloy bar mallet manufacture craft according to claim 1, it is characterised in that: the step S2 and step
Metal rigidity tester measurement force value range in S3 is 0-750N, and lower plate connects high-precision special pressure sensor.
5. a kind of titanium alloy bar mallet manufacture craft according to claim 1, it is characterised in that: the spray in the step S3
Sand processing is to use suction-type dry blasting machine, and sandblasting grade is Sa2.5 grades.
6. a kind of titanium alloy bar mallet manufacture craft according to claim 1, it is characterised in that: hard in the step S4
Change processing is to plate one layer of crome metal protective film on the surface of baseball bat blank body.