A kind of jute pad
Technical field
The present invention relates to a kind of mattresses, and in particular to arrives a kind of jute pad.
Background technique
As people pursue health, coconut palm palm fiber mattress is becoming increasingly popular in the mattress generally used now.And general bed
The fiber mat used is padded, brown bed course is the structure type using single layer, and uses being made for simple material, and function is more single
One.In addition, the product produced, by long-term use, client feedback give us, it is following to say that product haves the defects that: a part
There is lamination in the fibrous layer of product.The reason of through being layered is that the fibrous layer of finished product is to be made up of multiple layers, layer
Do not link entanglement staggeredly between layer.
Summary of the invention
In order to overcome above-mentioned deficiency, the purpose of the present invention is to provide a kind of integral structure fibrous layer, moisture absorption are ventilative
Jute pad.
In order to solve the above technical problems, the technical scheme adopted by the invention is that:
A kind of jute pad, it is formed by tossa and polyester fiber mixing hot pressing, in the fiber pad body, tossa
Weight percent be 82%~84%, surplus is polyester fiber, and the manufacture of jute pad includes lapping process, needle thorn process and heat
Process is pressed, it is in the lapping process, the plant fiber for being mixed with polyester fiber after combing is evenly laid out;The needle pierces process
In, fibrous layer is transported between needle group and knit stitch group, and upper needle group moves down the upper surface through fibrous layer and is pierced into fibrous layer,
Knit stitch group moves up the lower surface through fibrous layer and is pierced into fibrous layer, the needle in upper needle group and knit stitch group make back and forth to move up and down into
It assassinates and pricks, the depth of puncture fibrous layer is greater than the thickness of fibrous layer half, and the fiber in fibrous layer is made staggeredly to link entanglement, is formed
Integral structure fibrous layer;In the hot pressing process, the integral structure fibrous layer formed after needle is pierced enters baking oven hot pressing, fixed
Type forms finished product jute pad.
Further, the density of the fiber pad body is 800~1800g//m2 cm.
Beneficial effects of the present invention: due to using tossa material in fiber pad body, it has good hygroscopicity,
And scatter and disappear moisture also compare it is fast;Due to fiber pad body formed integral structure fibrous layer, solve prior art layer with
The problem of being layered between layer because staggeredly not linking entanglement.
Specific embodiment
Embodiment 1: a kind of jute pad, it is formed by tossa and polyester fiber mixing hot pressing, the fiber advance capital for
In body, the weight percent of tossa is 82%, and surplus is polyester fiber, and the manufacture of jute pad includes lapping process, needle thorn work
Sequence and hot pressing process, it is in the lapping process, the plant fiber for being mixed with polyester fiber after combing is evenly laid out;The needle thorn
In process, fibrous layer is transported between needle group and knit stitch group, and upper needle group moves down the upper surface through fibrous layer and is pierced into fibre
Layer is tieed up, knit stitch group moves up the lower surface through fibrous layer and is pierced into fibrous layer, and the needle in upper needle group and knit stitch group is made above and below reciprocal
Movement carries out puncture, and the depth of puncture fibrous layer is greater than the thickness of fibrous layer half, links the fiber in fibrous layer staggeredly and twines
Knot, forms integral structure fibrous layer, and the density of the fiber pad body is 800~1800g//m2 cm.The hot pressing process
In, the integral structure fibrous layer formed after needle is pierced enters baking oven hot pressing, and sizing forms finished product jute pad.
Embodiment 2: a kind of jute pad, it is formed by tossa and polyester fiber mixing hot pressing, the fiber advance capital for
In body, the weight percent of tossa is 84%, and surplus is polyester fiber, and the manufacture of jute pad includes lapping process, needle thorn work
Sequence and hot pressing process, it is in the lapping process, the plant fiber for being mixed with polyester fiber after combing is evenly laid out;The needle thorn
In process, fibrous layer is transported between needle group and knit stitch group, and upper needle group moves down the upper surface through fibrous layer and is pierced into fibre
Layer is tieed up, knit stitch group moves up the lower surface through fibrous layer and is pierced into fibrous layer, and the needle in upper needle group and knit stitch group is made above and below reciprocal
Movement carries out puncture, and the depth of puncture fibrous layer is greater than the thickness of fibrous layer half, links the fiber in fibrous layer staggeredly and twines
Knot, forms integral structure fibrous layer, and the density of the fiber pad body is 800~1800g//m2 cm.The hot pressing process
In, the integral structure fibrous layer formed after needle is pierced enters baking oven hot pressing, and sizing forms finished product jute pad.
Embodiment 3: a kind of jute pad, it is formed by tossa and polyester fiber mixing hot pressing, the fiber advance capital for
In body, the weight percent of tossa is 83%, and surplus is polyester fiber, and the manufacture of jute pad includes lapping process, needle thorn work
Sequence and hot pressing process, in the lapping process, the plant fiber for being mixed with polyester fiber after combing is evenly laid out, the fiber
The density of pad body is 800~1800g//m2 cm.
In the needle thorn process, fibrous layer is transported between needle group and knit stitch group, and upper needle group is moved down through puncture
The upper surface of fibrous layer is pierced into fibrous layer, and knit stitch group moves up the lower surface through puncture fibrous layer and is pierced into fibrous layer, upper needle group
Make reciprocal move up and down with the needle in knit stitch group and carry out puncture, the depth of puncture fibrous layer is greater than the thickness of fibrous layer half, makes
Fiber in fibrous layer staggeredly links entanglement, forms integral structure fibrous layer, the two sides of the needle are respectively provided with contrary
Hangnail, the process for being pierced into and pulling back can hook dimension of towing, and further increase fibre matting degree, improve the company between fiber
Knotting strength, improves the intensity of fiber mat product, and improves the ratio of plant fiber, improves production efficiency;The hot pressing process
In, the integral structure fibrous layer formed after needle is pierced enters baking oven hot pressing, and sizing forms finished fiber pad, due in one
The upper and lower surfaces for changing structural fibers layer have been laid with chemical fibre protective layer, form the finished product jute pad of three-decker, not only
Keep the top and bottom of fiber pad more smooth, and plays a protective role to fiber pad.
Implementation recited above is only that embodiment of the present invention is described, not to the spirit and scope of the present invention
It is defined, under the premise of not departing from design scheme of the present invention, ordinary engineering and technical personnel is to technology of the invention in this field
The equivalent structure and be directly or indirectly used in relevant technical field that scheme is made, should all fall into protection scope of the present invention.