CN109111773A - A kind of silkwood furniture water paint - Google Patents
A kind of silkwood furniture water paint Download PDFInfo
- Publication number
- CN109111773A CN109111773A CN201810894715.4A CN201810894715A CN109111773A CN 109111773 A CN109111773 A CN 109111773A CN 201810894715 A CN201810894715 A CN 201810894715A CN 109111773 A CN109111773 A CN 109111773A
- Authority
- CN
- China
- Prior art keywords
- parts
- silkwood
- water
- modified
- water paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of silkwood furniture water paints, belong to water paint technical field, be made of following parts by weight of component: 60-70 parts of water-soluble resin, 20-24 parts of acrylic acid, 18-20 parts of polyethylene glycol, 23-25 parts of modified manometer silicon dioxide, modified upland soil 20-26 parts, 5-6 parts of nano zine oxide, 9-13 parts of lanthanum carbonate, 8-12 parts of sodium carbonate, 6-10 parts of cerous nitrate, 5-9 parts of benzyl carbinol oleate, 3-5 parts of polypropylene glycerol aether, 10-16 parts of sodium alginate, 40-50 parts of sterile water.Raw material of the present invention is reasonably combined, and the water paint adhesive ability finally prepared is strong, and dispersion performance is good, and transparency is high, and anti-light performance is strong, has good filming performance, not easy to crack, and is practically free of volatile solvent, and security performance is high, great market popularization value.
Description
Technical field
The invention belongs to water paint technical fields, and in particular to a kind of silkwood furniture water paint.
Background technique
Spun gold nanmu be have in some materials spun gold and similar silks and satins gloss phenomenon nanmu (including frame nanmu, Zi Nan, Phoebe bournei,
Machilus nanmu etc.) general term, the spun gold nanmu of broad sense refers to that nanmu showed spun gold all cries spun gold nanmu.Timber is aromatic, and texture is straight and structure
It is fine and closely woven, it is unlikely to deform and cracks, for superior woods such as building, noble furnitures.In history silkwood be exclusively used in imperial palace,
The building and furniture of a small number of temples.Crystalline solid in silkwood is significantly more than common nanmu, wood surface golden light in the sun
Glittering, spun gold emerges, and has simple and elegant delicate fragrance.The texture-rich of spun gold nanmu is changeable, in addition shadow is changed in its distinctive walk, (wood is divided into yin
Positive two sides, different angle different colours), it is directly proportional for being worth to texture, and lines is more beautiful and rare, and value is more
It is high.
Existing silkwood furniture carries out spray painting processing on its surface to increase silkwood after completing, often
The comprehensive performance of furniture, but existing paint often covers the textured pattern of silkwood furniture, reduces silkwood
Aesthetics, in addition present paint contains many volatile solvents, will cause certain harm to human body, water paint is due to using
Water, so what is volatilized when film forming is all water, would not also bring injury instead of organic solvent to human body.
Summary of the invention
The purpose of the present invention is being directed to existing problem, a kind of silkwood furniture water paint is provided.It is of the invention former
Expect reasonably combined, the water paint adhesive ability finally prepared is strong, and dispersion performance is good, and transparency is high, and anti-light performance is strong, has very
Good filming performance, it is not easy to crack, and it is practically free of volatile solvent, security performance is high, great market popularization value.
The present invention is achieved by the following technical solutions:
A kind of silkwood furniture water paint, is made of following parts by weight of component: 60-70 parts of water-soluble resin, acrylic acid 20-
24 parts, 18-20 parts of polyethylene glycol, 23-25 parts of modified manometer silicon dioxide, modified upland soil 20-26 parts, nano zine oxide 5-6
Part, 9-13 parts of lanthanum carbonate, 8-12 parts of sodium carbonate, 6-10 parts of cerous nitrate, 5-9 parts of benzyl carbinol oleate, polypropylene glycerol aether 3-5
Part, 10-16 parts of sodium alginate, 40-50 parts of sterile water.
Preferably, be made of following parts by weight of component: 65 parts of water-soluble resin, 19 parts of polyethylene glycol, changes 22 parts of acrylic acid
Property 24 parts of nano silica, modified 23 parts of upland soil, 5.5 parts of nano zine oxide, 11 parts of lanthanum carbonate, 10 parts of sodium carbonate, nitric acid
8 parts of cerium, 7 parts of benzyl carbinol oleate, 4 parts of polypropylene glycerol aether, 13 parts of sodium alginate, 45 parts of sterile water.
Further, the preparation of the modified manometer silicon dioxide, comprising the following steps:
It 1) is that 1:5-6 is collectively disposed in reaction kettle according to weight ratio by nano silica and modification liquid A, the temperature in reaction kettle
Control is 300-400 DEG C, and the pressure control in reaction kettle is 10-20MPa, stir process 40-50min；
2) it when operating that reactor temperature is down to room temperature in 1), takes out nano silica and is placed in baking oven and is dried, do
It is dry to constant weight, dry temperature control is 80-90 DEG C.
Further, the modification liquid A, is made of following parts by weight of component: 12-18 parts of polyglycerol, silane coupling agent
20-26 parts, 18-22 parts of dioctyl succinate disulfonate acid, 16-20 parts of sodium glycocholate, 12-16 parts of beta-cyclodextrin, 6-8 parts of chloroform,
3-5 parts of acetone, 300-380 parts of sterile water.
Further, the preparation of the modified upland soil, comprising the following steps:
1) ethyl alcohol of upland soil and 95% is collectively disposed in triangular flask according to weight ratio for 1:10-12, is then heated, heating
Temperature control is 78-88 DEG C, is heated while stirring, while to the logical sodium hydroxide solution for instilling 4-8 drop 1mg/mL of triangular flask, being held
Continuous stirring 1-2h obtains mixed material；
2) will operate the mixed material 1) obtained and modification liquid B according to weight ratio is that 1:2.2-2.8 is collectively disposed in agitator tank, is stirred
The temperature control mixed in tank is 120-140 DEG C, stir process 1-2h；
3) mixed raw material in 2) after stir process will be operated and modification liquid B is placed in filter and is filtered, collected filter residue and set
In being dried in baking oven, dry temperature control is 70-80 DEG C, dry to constant weight.
Further, the modification liquid B, is made of following parts by weight of component: 23-25 parts of aminopropyl trimethoxysilane,
5-7 parts of nanometer iron powder, 14-18 parts of neopelex, 20-22 parts of turkey red oil, 4-8 parts of polyacrylamide, poly- second
4000 16-20 parts of glycol, 300-360 parts of sterile water.
It is necessary to have high transparencies compared with other are with water paint for nanmu furniture water paint, cannot influence spun gold
The characteristic of nanmu itself protects silkwood furniture not destroyed by light, soda acid etc. under the premise of playing nanmu advantage itself,
Extend the service life of silkwood furniture.The present invention provides a kind of silkwood furniture water paints, with water-soluble resin
For base-material, acrylic acid is added, the weatherability of water paint is improved, keeps paint film decorative performance good (plentiful bright, hardness height), chemically-resistant
Moral character can be good, and guarantor's light, unfading are excellent, high adhesion force, good mechanical performance.Add polyethylene glycol, modified nano-silica
SiClx, modified upland soil, nano zine oxide mutually act synergistically, and on the one hand arrange in pairs or groups with major ingredient water-soluble resin using composition film forming
Substance is effectively combined with silkwood surface and reacts, and forms a kind of in vitro netted mechanism, guarantees water paint and silkwood system
Degree of combining closely between product, and modified manometer silicon dioxide, modified upland soil, nano zine oxide three's appropriate proportioning,
The specific surface area for being conducive to improve water paint, increases the rheological characteristic of water paint, drops down conducive to water paint flat, promotes water paint dispersion equal
It is even；They can form a degree of cross-linked structure to still further aspect with water-soluble resin, improve water paint compactness and
Corrosion resistance forms the institutional framework of good electrochemical protection and physics radiation shielding action, improves the extinction of water paint
Degree makes water paint have good anti-uv-ray, can extend the service life of silkwood furniture.Add lanthanum carbonate, carbon
Sour sodium, cerous nitrate can promote water paint other components to form huge network molecular structure, keep water paint color soft, transparent
Degree improves, and mechanical performance and weatherability are greatly improved.It is high to add benzyl carbinol oleate, polypropylene glycerol aether, sodium alginate day
The viscosity of water paint, increases the degree of combining closely of water paint and silkwood furniture, and can eliminate the bubble in water paint
Foam improves the quality of water paint.
The present invention has the advantage that compared with prior art
Raw material of the present invention is reasonably combined, and the water paint adhesive ability finally prepared is strong, and dispersion performance is good, and transparency is high, anti-light
Performance is strong, has good filming performance, not easy to crack, and is practically free of volatile solvent, and security performance is high, and great market pushes away
Wide value.
Specific embodiment
Embodiment 1
A kind of silkwood furniture water paint, is made of following parts by weight of component: 60 parts of water-soluble resin, 20 parts of acrylic acid,
18 parts of polyethylene glycol, 23 parts of modified manometer silicon dioxide, modified 20 parts of upland soil, 5 parts of nano zine oxide, 9 parts of lanthanum carbonate, carbonic acid
8 parts of sodium, 6 parts of cerous nitrate, 5 parts of benzyl carbinol oleate, 3 parts of polypropylene glycerol aether, 10 parts of sodium alginate, 40 parts of sterile water.
Further, the preparation of the modified manometer silicon dioxide, comprising the following steps:
It 1) is that 1:5 is collectively disposed in reaction kettle according to weight ratio by nano silica and modification liquid A, the temperature control in reaction kettle
300 DEG C are made as, the pressure control in reaction kettle is 10MPa, stir process 40min；
2) it when operating that reactor temperature is down to room temperature in 1), takes out nano silica and is placed in baking oven and is dried, do
It is dry to constant weight, dry temperature control is 80 DEG C.
Further, the modification liquid A, is made of following parts by weight of component: 12 parts of polyglycerol, silane coupling agent 20
Part, 18 parts of dioctyl succinate disulfonate acid, 16 parts of sodium glycocholate, 12 parts of beta-cyclodextrin, 6 parts of chloroform, 3 parts of acetone, sterile water 300
Part.
Further, the preparation of the modified upland soil, comprising the following steps:
1) ethyl alcohol of upland soil and 95% is collectively disposed in triangular flask according to weight ratio for 1:10, is then heated, the temperature of heating
Control is 78 DEG C, is heated while stirring, while to the logical sodium hydroxide solution for instilling 4 drop 1mg/mL of triangular flask, persistently stirring 1h
The mixed material obtained；
2) will operate the mixed material 1) obtained and modification liquid B according to weight ratio is that 1:2.2 is collectively disposed in agitator tank, agitator tank
Interior temperature control is 120 DEG C, stir process 1h；
3) mixed raw material in 2) after stir process will be operated and modification liquid B is placed in filter and is filtered, collected filter residue and set
In being dried in baking oven, dry temperature control is 70 DEG C, dry to constant weight.
Further, the modification liquid B, is made of following parts by weight of component: aminopropyl trimethoxysilane 23 part, nanometer
5 parts of iron powder, 14 parts of neopelex, 20 parts of turkey red oil, 4 parts of polyacrylamide, 16 parts of Macrogol 4000,
300 parts of sterile water.
Embodiment 2
A kind of silkwood furniture water paint, is made of following parts by weight of component: 65 parts of water-soluble resin, 22 parts of acrylic acid,
19 parts of polyethylene glycol, 24 parts of modified manometer silicon dioxide, modified 23 parts of upland soil, 5.5 parts of nano zine oxide, 11 parts of lanthanum carbonate,
10 parts of sodium carbonate, 8 parts of cerous nitrate, 7 parts of benzyl carbinol oleate, 4 parts of polypropylene glycerol aether, 13 parts of sodium alginate, sterile water 45
Part.
Further, the preparation of the modified manometer silicon dioxide, comprising the following steps:
It 1) is that 1:5.5 is collectively disposed in reaction kettle according to weight ratio by nano silica and modification liquid A, the temperature in reaction kettle
Control is 350 DEG C, and the pressure control in reaction kettle is 15MPa, stir process 45min；
2) it when operating that reactor temperature is down to room temperature in 1), takes out nano silica and is placed in baking oven and is dried, do
It is dry to constant weight, dry temperature control is 85 DEG C.
Further, the modification liquid A, is made of following parts by weight of component: 15 parts of polyglycerol, silane coupling agent 23
Part, 20 parts of dioctyl succinate disulfonate acid, 18 parts of sodium glycocholate, 14 parts of beta-cyclodextrin, 7 parts of chloroform, 4 parts of acetone, sterile water 340
Part.
Further, the preparation of the modified upland soil, comprising the following steps:
1) ethyl alcohol of upland soil and 95% is collectively disposed in triangular flask according to weight ratio for 1:11, is then heated, the temperature of heating
Control is 83 DEG C, is heated while stirring, while to the logical sodium hydroxide solution for instilling 4-8 drop 1mg/mL of triangular flask, lasting to stir
1.5h obtains mixed material；
2) will operate the mixed material 1) obtained and modification liquid B according to weight ratio is that 1:2.5 is collectively disposed in agitator tank, agitator tank
Interior temperature control is 130 DEG C, stir process 1.5h；
3) mixed raw material in 2) after stir process will be operated and modification liquid B is placed in filter and is filtered, collected filter residue and set
In being dried in baking oven, dry temperature control is 75 DEG C, dry to constant weight.
Further, the modification liquid B, is made of following parts by weight of component: aminopropyl trimethoxysilane 24 part, nanometer
6 parts of iron powder, 16 parts of neopelex, 21 parts of turkey red oil, 6 parts of polyacrylamide, 18 parts of Macrogol 4000,
330 parts of sterile water.
Embodiment 3
A kind of silkwood furniture water paint, is made of following parts by weight of component: 70 parts of water-soluble resin, 24 parts of acrylic acid,
20 parts of polyethylene glycol, 25 parts of modified manometer silicon dioxide, modified 26 parts of upland soil, 6 parts of nano zine oxide, 13 parts of lanthanum carbonate, carbon
12 parts of sour sodium, 10 parts of cerous nitrate, 9 parts of benzyl carbinol oleate, 5 parts of polypropylene glycerol aether, 16 parts of sodium alginate, sterile water 50
Part.
Further, the preparation of the modified manometer silicon dioxide, comprising the following steps:
It 1) is that 1:6 is collectively disposed in reaction kettle according to weight ratio by nano silica and modification liquid A, the temperature control in reaction kettle
400 DEG C are made as, the pressure control in reaction kettle is 20MPa, stir process 50min；
2) it when operating that reactor temperature is down to room temperature in 1), takes out nano silica and is placed in baking oven and is dried, do
It is dry to constant weight, dry temperature control is 90 DEG C.
Further, the modification liquid A, is made of following parts by weight of component: 18 parts of polyglycerol, silane coupling agent 26
Part, 22 parts of dioctyl succinate disulfonate acid, 20 parts of sodium glycocholate, 16 parts of beta-cyclodextrin, 8 parts of chloroform, 5 parts of acetone, sterile water 380
Part.
Further, the preparation of the modified upland soil, comprising the following steps:
1) ethyl alcohol of upland soil and 95% is collectively disposed in triangular flask according to weight ratio for 1:12, is then heated, the temperature of heating
Control is 88 DEG C, is heated while stirring, while to the logical sodium hydroxide solution for instilling 8 drop 1mg/mL of triangular flask, persistently stirring 2h
Obtain mixed material；
2) will operate the mixed material 1) obtained and modification liquid B according to weight ratio is that 1:2.8 is collectively disposed in agitator tank, agitator tank
Interior temperature control is 140 DEG C, stir process 2h；
3) mixed raw material in 2) after stir process will be operated and modification liquid B is placed in filter and is filtered, collected filter residue and set
In being dried in baking oven, dry temperature control is 80 DEG C, dry to constant weight.
Further, the modification liquid B, is made of following parts by weight of component: aminopropyl trimethoxysilane 25 part, nanometer
7 parts of iron powder, 18 parts of neopelex, 22 parts of turkey red oil, 8 parts of polyacrylamide, 20 parts of Macrogol 4000,
360 parts of sterile water.
Comparative example 1
This comparative example 1 the non-modified nanometer two of mass parts such as changes into compared with Example 2, by modified manometer silicon dioxide
Silica, method and step in addition to this are all the same.
Comparative example 2
This comparative example 2 compared with Example 2, saves modified manometer silicon dioxide, and method and step in addition to this is all the same.
Comparative example 3
This comparative example 3 the non-modified upland soil of mass parts such as changes into compared with Example 2, by modified upland soil, removes this
Outer method and step is all the same.
Comparative example 4
This comparative example 4 compared with Example 2, saves modified upland soil, and method and step in addition to this is all the same.
Comparative example 5
This comparative example 5 compared with Example 2, saves modified manometer silicon dioxide and modified upland soil, method in addition to this
Step is all the same.
Control group
Existing conventional nanmu furniture paint.
In order to compare effect of the invention, measurement embodiment 2, comparative example 1, comparative example 2, comparative example 3,
The performance of the paint of comparative example 4, the water paint of comparative example 5 and control group.According to GB/T 6739-2006 " color
Paint and varnish pencil method measure hardness of paint film " measuring method measure hardness of paint film, according to GB/T 9286-1998 " colored paint and clear
The adhesive force intensity of method measurement water paint in the cross cut test of paint paint film ", spectrophotometric color measurement instrument measure the transparency of water paint
Specific experiment correlation data is as shown in table 1 below:
Table 1
Note: described in upper table 1, dL*> 0 indicates that brightness value rises, and water paint transparency can all decline.
Raw material of the present invention is reasonably combined it can be seen from upper table 1, and the water paint adhesive ability finally prepared is strong, dispersibility
Can be good, transparency is high, and anti-light performance is strong, has good filming performance, and it is not easy to crack, and it is practically free of volatile solvent,
Security performance is high, great market popularization value.
Claims (6)
1. a kind of silkwood furniture water paint, which is characterized in that be made of following parts by weight of component: water-soluble resin 60-
70 parts, 20-24 parts of acrylic acid, 18-20 parts of polyethylene glycol, 23-25 parts of modified manometer silicon dioxide, it is upland soil 20-26 parts modified,
5-6 parts of nano zine oxide, 9-13 parts of lanthanum carbonate, 8-12 parts of sodium carbonate, 6-10 parts of cerous nitrate, 5-9 parts of benzyl carbinol oleate, polyoxy
3-5 parts of propylene glycerin ether, 10-16 parts of sodium alginate, 40-50 parts of sterile water.
2. a kind of silkwood furniture water paint according to claim 1, which is characterized in that by following parts by weight of component group
At: 65 parts of water-soluble resin, 22 parts of acrylic acid, 19 parts of polyethylene glycol, 24 parts of modified manometer silicon dioxide, modified upland soil 23
Part, 5.5 parts of nano zine oxide, 11 parts of lanthanum carbonate, 10 parts of sodium carbonate, 8 parts of cerous nitrate, 7 parts of benzyl carbinol oleate, polyoxypropylene are sweet
4 parts of oily ether, 13 parts of sodium alginate, 45 parts of sterile water.
3. a kind of silkwood furniture water paint according to claim 1 or claim 2, which is characterized in that the modified Nano two
The preparation of silica, comprising the following steps:
It 1) is that 1:5-6 is collectively disposed in reaction kettle according to weight ratio by nano silica and modification liquid A, the temperature in reaction kettle
Control is 300-400 DEG C, and the pressure control in reaction kettle is 10-20MPa, stir process 40-50min；
2) it when operating that reactor temperature is down to room temperature in 1), takes out nano silica and is placed in baking oven and is dried, do
It is dry to constant weight, dry temperature control is 80-90 DEG C.
4. a kind of silkwood furniture water paint according to claim 3, which is characterized in that the modification liquid A, by following
Parts by weight of component composition: 12-18 parts of polyglycerol, 20-26 parts of silane coupling agent, 18-22 parts of dioctyl succinate disulfonate acid, sweet
16-20 parts of sodium taurocholate, 12-16 parts of beta-cyclodextrin, 6-8 parts of chloroform, 3-5 parts of acetone, 300-380 parts of sterile water.
5. a kind of silkwood furniture water paint according to claim 1 or claim 2, which is characterized in that the modified upland soil
Preparation, comprising the following steps:
1) ethyl alcohol of upland soil and 95% is collectively disposed in triangular flask according to weight ratio for 1:10-12, is then heated, heating
Temperature control is 78-88 DEG C, is heated while stirring, while to the logical sodium hydroxide solution for instilling 4-8 drop 1mg/mL of triangular flask, being held
Continuous stirring 1-2h obtains mixed material；
2) will operate the mixed material 1) obtained and modification liquid B according to weight ratio is that 1:2.2-2.8 is collectively disposed in agitator tank, is stirred
The temperature control mixed in tank is 120-140 DEG C, stir process 1-2h；
3) mixed raw material in 2) after stir process will be operated and modification liquid B is placed in filter and is filtered, collected filter residue and set
In being dried in baking oven, dry temperature control is 70-80 DEG C, dry to constant weight.
6. a kind of silkwood furniture water paint according to claim 5, which is characterized in that the modification liquid B, by with
Lower parts by weight of component composition: 23-25 parts of aminopropyl trimethoxysilane, 5-7 parts of nanometer iron powder, neopelex 14-
18 parts, 20-22 parts of turkey red oil, 4-8 parts of polyacrylamide, 16-20 parts of Macrogol 4000,300-360 parts of sterile water.