CN109095878A - A kind of organic and inorganic composite adhesive - Google Patents
A kind of organic and inorganic composite adhesive Download PDFInfo
- Publication number
- CN109095878A CN109095878A CN201810488055.XA CN201810488055A CN109095878A CN 109095878 A CN109095878 A CN 109095878A CN 201810488055 A CN201810488055 A CN 201810488055A CN 109095878 A CN109095878 A CN 109095878A
- Authority
- CN
- China
- Prior art keywords
- parts
- organic
- inorganic
- water
- inorganic composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of organic, inorganic compounding adhesive, it is made of the raw material of following mass fraction: 50-70 parts of water, 1-2 parts of hydroxyethyl cellulose, 2-5 parts of polyvinyl alcohol, 5-10 parts of organic emulsion, 10-15 parts of inorganic sol, 1-5 parts of the alkali metal salt of silicic acid, 1-5 parts of sulfuric acid, 1-5 parts of attapulgite, 1-3 parts of bentonite, 1-2 parts of aluminium-magnesium silicate, 1-2 parts of allophane, 5-10 parts of low-melting glass, the invention manufacturing process is simple, there can be the excellent Newtonian rheology energy of organic bond in application, it is high just viscous, it is easy sizing advantage, but also with inorganic bond high temperature resistant solvent resistant water-resistant capacity after fully sintered solidification, it has both organic, inorganic two kinds of adhesive advantages, its disadvantage is largely avoided again, it can reach after sintering processes inorganic The performance of adhesive, has application value.
Description
Technical field
The present invention relates to technical field of adhesive, specially a kind of organic and inorganic composite adhesive.
Background technique
If traditional ceramic fibre, all-glass paper in bonding forming using individual inorganic adhesive, due to
Inorganic adhesive initial bonding strength is poor, causes to be difficult to be formed, using effect is very poor.
If individually using organic adhesive, since organic bond heat-resisting ability is generally bad, and solvent resistant
Ability is poor, cannot match the heat resisting temperature of glass, ceramic fibre completely, with solvent resistant water-resistant capacity, causes application range limited.
Glass fiber paper, ceramic fiber paper are particularly suitable for being used as due to big specific surface area, the structure of bulk multi-hole
Catalyst carrier.And catalyst carrier is made using these inorganic fibre papers because these paper forming abilities are bad, do not have
Thermoplasticity, thus need using the processing sizing of special technique, this proposes very high requirement to adhesive.And in the market viscous
Mixture has the inorganic bond of heat-resisting solvent resistant characteristic, and just viscous poor, application properties are poor, and style-ability is bad；Organic bond
Application properties are good, just glue, but water-fast heat-resisting solvent resistant ability is poor, cannot match the performance interval of inorfil, therefore, urgently
This in the presence of the prior art is solved the problems, such as to a kind of improved technology.
Summary of the invention
It is disclosed by the invention organic and inorganic compound the purpose of the present invention is to provide a kind of organic and inorganic composite adhesive
Adhesive can have the excellent Newtonian rheology energy of organic bond in application, high just viscous, sizing advantage is easy, complete
It, can very great Cheng using composite adhesive of the present invention but also with inorganic bond high temperature resistant solvent resistant water-resistant capacity after full sintering curing
Avoid ceramic fiber paper or glass fibre bad due to being glued in forming process on degree, bad caused loss of being formed, in glass
Before glass is fiber melting, organic component can almost burn mistake, and residue is almost inorganic matter at this time, it is of the present invention it is organic,
Inorganic compounding adhesive, polyvinyl alcohol, hydroxyethyl cellulose of organic component etc. have excellent film forming and splendid rheology
Performance also plays protective colloid action in organic and inorganic compounding adhesive, prevents from being demulsified, silica solution, the Aluminum sol of inorganic component
High temperature resistant, solvent resistant ability are strong, after organic component burns and loses, can also with the good combinations such as glass, ceramic fibre, aluminium-magnesium silicate,
Bentonite, attapulgite have thickening thixotropic transformation, and dry to improve reinforcing effect, low-melting glass is in organic component sintering processes
It burns before losing with regard to hot melt adhesive, avoids degumming during the sintering process, have both organic and inorganic two kinds of adhesive advantages, and largely
On avoid its disadvantage, can reach the performance of inorganic bond after sintering processes, have application value, to solve above-mentioned background
The problem of being proposed in technology.
To achieve the above object, the invention provides the following technical scheme: a kind of organic and inorganic composite adhesive, by following
The raw material of mass fraction is made: 50-70 parts of water, 1-2 parts of hydroxyethyl cellulose, 2-5 parts of polyvinyl alcohol, 5-10 parts of organic emulsion,
1-3 parts of 1-5 parts of 1-5 parts of 1-5 parts of alkali metal salt, sulfuric acid, attapulgite, bentonite, the silicic acid of 10-15 parts of inorganic sol, silicic acid
1-2 parts of magnalium, 1-2 parts of allophane, 5-10 parts of low-melting glass.
Preferably, be made of the raw material of following mass fraction: 60 parts of water, 3 parts of polyvinyl alcohol, has 1 part of hydroxyethyl cellulose
Machine lotion 10 divides, 2 parts of 2 parts of 1 part of 1 part of alkali metal salt, sulfuric acid, attapulgite, bentonite, the silicic acid of 15 parts of inorganic sol, silicic acid
2 parts of magnalium, 2 parts of allophane, 5 parts of low-melting glass.
Preferably, hydroxyethyl cellulose, polyvinyl alcohol, organic emulsion are organic component.
Preferably, it is individually a kind of or more to can be EVA class lotion, acrylic emulsions, organic silicon lotion for organic emulsion
Kind compounding is constituted.
Preferably, Aluminum sol, silica solution, the alkali metal salt of silicic acid, sulfuric acid, attapulgite, bentonite, aluminium-magnesium silicate, water
Allophane, low-melting glass are inorganic component.
Preferably, inorganic sol can be Aluminum sol or silica solution or both compounding and constitute.
Preferably, the alkali metal salt of silicic acid can be sodium metasilicate, potassium silicate, and lithium metasilicate is one such.
Preferably, manufacturing process the following steps are included:
Step 1: the organic component of adhesive is dissolved in water and is put into blender allotment to solid content about 10-20%, A is made
Agent, it is spare；
Step 2: add water to be put into allotment in blender the inorganic component of adhesive and B agent is made to solid content about 10-30%；
Step 3: A agent is slowly added into B agent, sets 40r/min for blender revolving speed, is kept stirring and is avoided B agent de-
Water is uniformly mixed and organic and inorganic composite adhesive of the invention is made.
Compared with prior art, the beneficial effects of the present invention are:
(1) there can be the excellent Newtonian rheology energy of organic bond in application, it is high just viscous, it is easy sizing advantage, complete
But also with inorganic bond high temperature resistant solvent resistant water-resistant capacity after full sintering curing.
(2) it can largely avoid ceramic fiber paper or glass fibre bad due to being glued in forming process, sizing
Loss caused by bad, before glass fibre thawing, organic component can almost burn mistake, and residue is almost inorganic at this time
Object.
(3) polyvinyl alcohol of organic component, hydroxyethyl cellulose etc. have excellent film forming and splendid rheological characteristic
Can, protective colloid action is also played in organic and inorganic compounding adhesive, prevents from being demulsified, silica solution, the Aluminum sol of inorganic component are resistance to
High temperature, solvent resistant ability are strong, after organic component burns and loses, can also with the good combinations such as glass, ceramic fibre, it is aluminium-magnesium silicate, swollen
Profit soil, attapulgite have thickening thixotropic transformation, dry to improve reinforcing effect, and low-melting glass is burnt in organic component sintering processes
With regard to hot melt adhesive before losing, degumming during the sintering process is avoided, has both organic and inorganic two kinds of adhesive advantages, and largely
Its disadvantage is avoided, the performance of inorganic bond is can reach after sintering processes, has application value.
Specific embodiment
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment
Only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this field
Art personnel every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
The present invention provides a kind of technical solution: a kind of organic and inorganic composite adhesive, by the raw material system of following mass fraction
At: 50-70 parts of water, 1-2 parts of hydroxyethyl cellulose, 2-5 parts of polyvinyl alcohol, 5-10 parts of organic emulsion, 10-15 parts of inorganic sol,
1-2 parts of 1-3 parts of 1-5 parts of 1-5 parts of 1-5 parts of alkali metal salt, sulfuric acid, attapulgite, bentonite, aluminium-magnesium silicate, the water aluminium English of silicic acid
1-2 parts of stone, 5-10 parts of low-melting glass.
Embodiment one:
A kind of organic and inorganic composite adhesive, is made of the raw material of following mass fraction: 50 parts of water, 1 part of hydroxyethyl cellulose,
2 parts of polyvinyl alcohol, 5 parts of organic emulsion, 10 parts of inorganic sol, silicic acid 1 part of 1 part of 1 part of alkali metal salt, sulfuric acid, attapulgite, swollen
Moisten native 1 part, 1 part of aluminium-magnesium silicate, 1 part of allophane, 5 parts of low-melting glass.
The present embodiment manufacturing process the following steps are included:
Step 1: being dissolved in water for the organic component of adhesive and be put into blender allotment to solid content about 2%, A agent is made, standby
With；
Step 2: add water to be put into allotment in blender the inorganic component of adhesive and B agent is made to solid content about 2%；
Step 3: A agent is slowly added into B agent, sets 40r/min for blender revolving speed, is kept stirring and is avoided B agent de-
Water is uniformly mixed and organic and inorganic composite adhesive of the invention is made.
Embodiment two:
A kind of organic and inorganic composite adhesive, is made of the raw material of following mass fraction: 55 parts of water, 1 part of hydroxyethyl cellulose,
2 parts of polyvinyl alcohol, 7 parts of organic emulsion, 12 parts of inorganic sol, silicic acid 2 parts of 2 parts of 2 parts of alkali metal salt, sulfuric acid, attapulgite, swollen
Moisten native 2 parts, 1 part of aluminium-magnesium silicate, 1 part of allophane, 6 parts of low-melting glass.
The present embodiment manufacturing process the following steps are included:
Step 1: being dissolved in water for the organic component of adhesive and be put into blender allotment to solid content about 5%, A agent is made, standby
With；
Step 2: add water to be put into allotment in blender the inorganic component of adhesive and B agent is made to solid content about 6%；
Step 3: A agent is slowly added into B agent, sets 40r/min for blender revolving speed, is kept stirring and is avoided B agent de-
Water is uniformly mixed and organic and inorganic composite adhesive of the invention is made.
By comparison, organic and inorganic composite adhesive made from embodiment two is organic and inorganic more multiple than made from embodiment one
Close adhesive just viscous effect, style-ability, water-fast, heat-resisting, solvent resistance is more preferable.
Embodiment three:
A kind of organic and inorganic composite adhesive, is made of the raw material of following mass fraction: 60 parts of water, 2 parts of hydroxyethyl cellulose,
3 parts of polyvinyl alcohol, 8 parts of organic emulsion, 13 parts of inorganic sol, silicic acid 3 parts of 3 parts of 3 parts of alkali metal salt, sulfuric acid, attapulgite, swollen
Moisten native 2 parts, 2 parts of aluminium-magnesium silicate, 2 parts of allophane, 5 parts of low-melting glass.
The present embodiment manufacturing process the following steps are included:
Step 1: being dissolved in water for the organic component of adhesive and be put into blender allotment to solid content about 10%, A agent is made, standby
With；
Step 2: add water to be put into allotment in blender the inorganic component of adhesive and B agent is made to solid content about 15%；
Step 3: A agent is slowly added into B agent, sets 40r/min for blender revolving speed, is kept stirring and is avoided B agent de-
Water is uniformly mixed and organic and inorganic composite adhesive of the invention is made.
By comparison, organic and inorganic composite adhesive made from embodiment three is organic and inorganic more multiple than made from embodiment two
Close adhesive just viscous effect, style-ability, water-fast, heat-resisting, solvent resistance is more preferable
Example IV:
A kind of organic and inorganic composite adhesive, is made of the raw material of following mass fraction: 65 parts of water, 2 parts of hydroxyethyl cellulose,
5 parts of polyvinyl alcohol, 10 parts of organic emulsion, 15 parts of inorganic sol, silicic acid 5 parts of 5 parts of 5 parts of alkali metal salt, sulfuric acid, attapulgite,
3 parts of bentonite, 2 parts of aluminium-magnesium silicate, 2 parts of allophane, 8 parts of low-melting glass.
The present embodiment manufacturing process the following steps are included:
Step 1: being dissolved in water for the organic component of adhesive and be put into blender allotment to solid content about 15%, A agent is made, standby
With；
Step 2: add water to be put into allotment in blender the inorganic component of adhesive and B agent is made to solid content about 23%；
Step 3: A agent is slowly added into B agent, sets 40r/min for blender revolving speed, is kept stirring and is avoided B agent de-
Water is uniformly mixed and organic and inorganic composite adhesive of the invention is made.
By comparison, organic and inorganic composite adhesive made from example IV is organic and inorganic more multiple than made from embodiment three
Close adhesive just viscous effect, style-ability, water-fast, heat-resisting, solvent resistance is poor.
Embodiment five:
A kind of organic and inorganic composite adhesive, is made of the raw material of following mass fraction: 70 parts of water, 2 parts of hydroxyethyl cellulose,
5 parts of polyvinyl alcohol, 10 parts of organic emulsion, 15 parts of inorganic sol, silicic acid 5 parts of 5 parts of 5 parts of alkali metal salt, sulfuric acid, attapulgite,
3 parts of bentonite, 2 parts of aluminium-magnesium silicate, 2 parts of allophane, 8 parts of low-melting glass.
The present embodiment manufacturing process the following steps are included:
Step 1: being dissolved in water for the organic component of adhesive and be put into blender allotment to solid content about 20%, A agent is made, standby
With；
Step 2: add water to be put into allotment in blender the inorganic component of adhesive and B agent is made to solid content about 30%；
Step 3: A agent is slowly added into B agent, sets 40r/min for blender revolving speed, is kept stirring and is avoided B agent de-
Water is uniformly mixed and organic and inorganic composite adhesive of the invention is made.
By comparison, organic and inorganic composite adhesive made from embodiment five is organic and inorganic more multiple than made from embodiment three
Close adhesive just viscous effect, style-ability, water-fast, heat-resisting, solvent resistance is poor.
Embodiment six:
A kind of organic and inorganic composite adhesive, is made of the raw material of following mass fraction: 55 parts of water, 1 part of hydroxyethyl cellulose,
4 parts of polyvinyl alcohol, 10 parts of organic emulsion, 10 parts of inorganic sol, silicic acid 2 parts of 1 part of 1 part of alkali metal salt, sulfuric acid, attapulgite,
2 parts of bentonite, 2 parts of aluminium-magnesium silicate, 2 parts of allophane, 5 parts of low-melting glass.
The present embodiment manufacturing process the following steps are included:
Step 1: being dissolved in water for the organic component of adhesive and be put into blender allotment to solid content about 10%, A agent is made, standby
With；
Step 2: add water to be put into allotment in blender the inorganic component of adhesive and B agent is made to solid content about 15%；
Step 3: A agent is slowly added into B agent, sets 40r/min for blender revolving speed, is kept stirring and is avoided B agent de-
Water is uniformly mixed and organic and inorganic composite adhesive of the invention is made.
By comparison, organic and inorganic composite adhesive made from embodiment six is organic and inorganic more multiple than made from embodiment three
Closing adhesive, just viscous effect, style-ability are good, water-fast, heat-resisting, solvent resistance is poor.
Embodiment seven:
A kind of organic and inorganic composite adhesive, is made of the raw material of following mass fraction: 60 parts of water, 1 part of hydroxyethyl cellulose,
3 parts of polyvinyl alcohol, organic emulsion 10 divide, 2 parts of 1 part of 1 part of alkali metal salt, sulfuric acid, the attapulgite of 15 parts of inorganic sol, silicic acid,
2 parts of bentonite, 2 parts of aluminium-magnesium silicate, 2 parts of allophane, 5 parts of low-melting glass.
The present embodiment manufacturing process the following steps are included:
Step 1: being dissolved in water for the organic component of adhesive and be put into blender allotment to solid content about 10%, A agent is made, standby
With；
Step 2: add water to be put into allotment in blender the inorganic component of adhesive and B agent is made to solid content about 15%；
Step 3: A agent is slowly added into B agent, sets 40r/min for blender revolving speed, is kept stirring and is avoided B agent de-
Water is uniformly mixed and organic and inorganic composite adhesive of the invention is made.
By comparison, organic and inorganic composite adhesive made from embodiment seven is organic and inorganic more multiple than made from embodiment six
Closing adhesive, just viscous effect, style-ability are more preferable, water-fast, heat-resisting, more resistance to than organic and inorganic composite adhesive made from embodiment three
Solvent nature is more preferable.
Embodiment eight:
A kind of organic and inorganic composite adhesive, is made of the raw material of following mass fraction: 65 parts of water, 2 parts of hydroxyethyl cellulose,
3 parts of polyvinyl alcohol, 10 parts of organic emulsion, 15 parts of inorganic sol, silicic acid 2 parts of 2 parts of 2 parts of alkali metal salt, sulfuric acid, attapulgite,
2 parts of bentonite, 2 parts of aluminium-magnesium silicate, 2 parts of allophane, 5 parts of low-melting glass.
The present embodiment manufacturing process the following steps are included:
Step 1: being dissolved in water for the organic component of adhesive and be put into blender allotment to solid content about 10%, A agent is made, standby
With；
Step 2: add water to be put into allotment in blender the inorganic component of adhesive and B agent is made to solid content about 15%；
Step 3: A agent is slowly added into B agent, sets 40r/min for blender revolving speed, is kept stirring and is avoided B agent de-
Water is uniformly mixed and organic and inorganic composite adhesive of the invention is made.
By comparison, organic and inorganic composite adhesive made from embodiment eight is organic and inorganic more multiple than made from embodiment seven
Close adhesive just viscous effect, style-ability, water-fast, heat-resisting, solvent resistance is poor.
Embodiment nine:
A kind of organic and inorganic composite adhesive, is made of the raw material of following mass fraction: 60 parts of water, 1 part of hydroxyethyl cellulose,
3 parts of polyvinyl alcohol, 10 parts of organic emulsion, 15 parts of inorganic sol, silicic acid 2 parts of 3 parts of 3 parts of alkali metal salt, sulfuric acid, attapulgite,
2 parts of bentonite, 2 parts of aluminium-magnesium silicate, 2 parts of allophane, 10 parts of low-melting glass.
The present embodiment manufacturing process the following steps are included:
Step 1: being dissolved in water for the organic component of adhesive and be put into blender allotment to solid content about 10%, A agent is made, standby
With；
Step 2: add water to be put into allotment in blender the inorganic component of adhesive and B agent is made to solid content about 15%；
Step 3: A agent is slowly added into B agent, sets 40r/min for blender revolving speed, is kept stirring and is avoided B agent de-
Water is uniformly mixed and organic and inorganic composite adhesive of the invention is made.
By comparison, organic and inorganic composite adhesive made from embodiment nine is organic and inorganic more multiple than made from embodiment seven
Close adhesive just viscous effect, style-ability, water-fast, heat-resisting, solvent resistance is poor.
Will organic and inorganic composite adhesive made from various embodiments of the present invention carry out just viscous effect, style-ability, it is water-fast,
Heat-resisting, solvent resistant experiment, obtains, organic and inorganic composite adhesive prepared by embodiment seven can reach best after comparison
Performance.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (8)
1. a kind of organic and inorganic composite adhesive, it is characterised in that: be made of the raw material of following mass fraction: 50-70 parts of water,
1-2 parts of hydroxyethyl cellulose, 2-5 parts of polyvinyl alcohol, 5-10 parts of organic emulsion, 10-15 parts of inorganic sol, silicic acid alkali metal salt
1-5 parts, 1-5 parts of sulfuric acid, 1-5 parts of attapulgite, 1-3 parts of bentonite, 1-2 parts of aluminium-magnesium silicate, 1-2 parts of allophane, low melting point
5-10 parts of glass.
2. a kind of organic and inorganic composite adhesive according to claim 1, it is characterised in that: by following mass fraction
Raw material is made: 60 parts of water, 1 part of hydroxyethyl cellulose, 3 parts of polyvinyl alcohol, organic emulsion 10 divide, 15 parts of inorganic sol, silicic acid
1 part of alkali metal salt, 1 part of sulfuric acid, 2 parts of attapulgite, 2 parts of bentonite, 2 parts of aluminium-magnesium silicate, 2 parts of allophane, low-melting glass 5
Part.
3. a kind of organic and inorganic composite adhesive according to claim 1, it is characterised in that: the hydroxyethyl cellulose,
Polyvinyl alcohol, organic emulsion are organic component.
4. a kind of organic and inorganic composite adhesive according to claim 1, it is characterised in that: the organic emulsion can be with
It is that individually one or more compoundings are constituted for EVA class lotion, acrylic emulsions, organic silicon lotion.
5. a kind of organic and inorganic composite adhesive according to claim 1, it is characterised in that: the Aluminum sol, silicon are molten
Glue, the alkali metal salt of silicic acid, sulfuric acid, attapulgite, bentonite, aluminium-magnesium silicate, allophane, low-melting glass are no unit
Point.
6. a kind of organic and inorganic composite adhesive according to claim 1, it is characterised in that: the inorganic sol can be with
It is that Aluminum sol or silica solution or both compounding are constituted.
7. a kind of organic and inorganic composite adhesive according to claim 1, it is characterised in that: the alkali metal of the silicic acid
It is one such that salt can be sodium metasilicate, potassium silicate, lithium metasilicate.
8. realizing a kind of organic and inorganic composite adhesive described in claim 1, it is characterised in that: manufacturing process includes following
Step:
Step 1: the organic component of adhesive is dissolved in water and is put into blender allotment to solid content about 10-20%, A is made
Agent, it is spare；
Step 2: add water to be put into allotment in blender the inorganic component of adhesive and B agent is made to solid content about 10-30%；
Step 3: A agent is slowly added into B agent, sets 40r/min for blender revolving speed, is kept stirring and is avoided B agent de-
Water is uniformly mixed and organic and inorganic composite adhesive of the invention is made.