CN109056189A - A kind of washable mould proof filling cotton - Google Patents

A kind of washable mould proof filling cotton Download PDF

Info

Publication number
CN109056189A
CN109056189A CN201810951511.XA CN201810951511A CN109056189A CN 109056189 A CN109056189 A CN 109056189A CN 201810951511 A CN201810951511 A CN 201810951511A CN 109056189 A CN109056189 A CN 109056189A
Authority
CN
China
Prior art keywords
fiber
washable
filling cotton
mould proof
cotton
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810951511.XA
Other languages
Chinese (zh)
Inventor
随月丽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201810951511.XA priority Critical patent/CN109056189A/en
Publication of CN109056189A publication Critical patent/CN109056189A/en
Pending legal-status Critical Current

Abstract

The invention mainly relates to textile processing technical fields, a kind of washable mould proof filling cotton is disclosed, is made of raw material from the following weight: acrylonitrile vinylidene chloride fibre 42 ~ 44, bombax cotton 23 ~ 25, milk protein fiber 10 ~ 12, soybean fiber 10 ~ 12, modified chitosan fiber 10 ~ 12, copper ammonia fiber 7 ~ 9, active carbon loading silver fiber 7 ~ 9；Washable mould proof filling cotton provided by the invention, structure is granular, it is easy dispersion, not conglomeration after washing avoids needing to tear bulk filling cotton when filling being filled, keeps filling uniform, filling cotton is made of multiple fiber ingredient simultaneously, breathable heat insulating can effectively inhibit the growth of multiple-microorganism, avoid the occurrence of Signs of Mould.

Description

A kind of washable mould proof filling cotton
Technical field
The invention mainly relates to textile processing technical fields, more particularly to a kind of washable mould proof filling cotton.
Background technique
Filling cotton is generally used in filling clothes, bedding and toy, has preferable warmth retention property and fluffy sense, but at present There are many filling cotton type in the market, are divided into gum sprayed cotton, soft cotton, Song Mian, hot light cotton, washing cotton and imitative silk flosssilk wadding etc., various to fill out Cotton is filled with different property features and applications, and dazzling, quality is irregular, and consumer is allowed to be difficult to select.
Existing 108138403 A of patent document CN discloses a kind of filling cotton, is mixed by acrylic fibre and polyester fiber Close, have preferable fluffy degree and and heat insulating ability, but do not have certain antibacterial and antimildew function, and wash 10 times Fluffy degree will be made to reduce about 30%, washability is poor, however the frequency that clothes, bedding and stuffed toy use is higher, also holds very much Easily contamination spot, and these filling general volumes of article are larger, are difficult to be cleaned, Signs of Mould easily occur.
Summary of the invention
In order to make up the defect of prior art, the object of the present invention is to provide a kind of washable mould proof filling cottons.
A kind of washable mould proof filling cotton, is made of raw material from the following weight: acrylonitrile vinylidene chloride fibre 42 ~ 44, bombax cotton 23 ~ 25, milk protein fiber 10 ~ 12, soybean fiber 10 ~ 12, modified chitosan fiber 10 ~ 12, copper ammonia fiber 7 ~ 9, active carbon loading silver Fiber 7 ~ 9.
The modified chitosan fiber in 1 ~ 2% acetate fiber, stirs chitosan solution volume fraction to complete Fully dissolved makes 210 ~ 230mg/L of concentration of chitosan solution, to add concentration be 60 ~ 80mg/L polyphenol solution, Bian Jia Enter side stirring, the additional amount of polyphenol solution is the 1/3 ~ 1/4 of chitosan solution volume, mixes be placed on 60 ~ 70 DEG C of standings 1 completely ~ 2 hours, centrifugation took precipitating, spinning obtains modified chitosan fiber.
A kind of preparation method of washable mould proof filling cotton, comprising the following steps:
(1) by acrylonitrile vinylidene chloride fibre, bombax cotton, milk protein fiber, soybean fiber, modified chitosan fiber, copper ammonia fiber and load Active carbon of silver fiber is added in folic acid solution, is uniformly mixed, and impregnates 4 ~ 6 hours in 15 ~ 20 DEG C, promotes to be glued between fiber It connects, is conducive to that the soft and smooth sense and comfort of blended ratio can be improved smoothly at silk when fibre composition is blended, filters, obtain composite fibre；
(2) composite fibre is carried out blended, makes 1.14 ~ 1.18dtex of line density, length is 5 ~ 7cm, can be improved filling cotton Soft and smooth sense and dispersibility, while be conducive to blended ratio be added template mesh, avoid be laid with when cut again, improve filling cotton Production efficiency obtains blended ratio；
(3) blended ratio is placed in water, is uniformly mixed, is layed in template mesh by water flow, obtains web；
(4) web is subjected to spun lacing reinforcing, makes 60 ~ 70g/m of Unit Weight2, make filling cotton soft comfortable, it is smooth easily to divide It dissipates, improves the practicability of filling cotton, obtain washable mould proof filling cotton.
The folic acid solution of the step (1), concentration are 15 ~ 20mg/L.
The template mesh of the step (3) is the spherical of 0.5 ~ 0.7cm of diameter.
The spun lacing of the step (4) is reinforced, and doffer speed is 66 ~ 68m/min.
The application method of the washable mould proof filling cotton, for filling pillow, toy, cushion, back cushion, the pillow being filled Head, cushion, can directly machine-wash after being lined with spot at toy, dry after washing.
The invention has the advantages that washable mould proof filling cotton provided by the invention, structure is granular, easy dispersion, after washing Not conglomeration avoids needing to tear bulk filling cotton when filling being filled, makes filling uniformly, while filling cotton is by multiple fiber Ingredient is constituted, and breathable heat insulating can effectively inhibit the growth of multiple-microorganism, avoid the occurrence of Signs of Mould；The fiber of filling cotton Ingredient is mostly natural fiber, will fibre composition be added folic acid solution in mix, and carry out low temperature it is long when immersion, promote fiber Between be bonded, be conducive to fibre composition it is blended when can improve the soft and smooth sense and comfort of blended ratio smoothly at silk；It will mixing Fiber progress is blended, controls the line density and length of blended ratio, can be improved the soft and smooth sense and dispersibility of filling cotton, be conducive to simultaneously Template mesh is added in blended ratio, avoids being cut again when being laid with, improves the production efficiency of filling cotton；Again to web after laying Spun lacing reinforcing is carried out, the Unit Weight of filling cotton is controlled, makes filling cotton soft comfortable, smooth easy dispersion improves the reality of filling cotton The property used.
Specific embodiment
Illustrate the present invention with specific embodiment below.
Embodiment 1
A kind of washable mould proof filling cotton, is made of raw material from the following weight: acrylonitrile vinylidene chloride fibre 42, bombax cotton 23, milk protein Fiber 10, soybean fiber 10, modified chitosan fiber 10, copper ammonia fiber 7, active carbon loading silver fiber 7.
The modified chitosan fiber in 1% acetate fiber, stirs chitosan solution volume fraction to complete Dissolution, makes the concentration 210mg/L of chitosan solution, to the polyphenol solution that concentration is 60mg/L is added, stirs while adding, The additional amount of polyphenol solution is the 1/3 of chitosan solution volume, mixes be placed on 60 DEG C of standings 1 hour completely, centrifugation, it is heavy to take It forms sediment, spinning obtains modified chitosan fiber.
A kind of preparation method of washable mould proof filling cotton, comprising the following steps:
(1) by acrylonitrile vinylidene chloride fibre, bombax cotton, milk protein fiber, soybean fiber, modified chitosan fiber, copper ammonia fiber and load Active carbon of silver fiber is added in folic acid solution, concentration 15mg/L, is uniformly mixed, and impregnates 4 hours in 15 DEG C, promotes between fiber It is bonded, is conducive to that the soft and smooth sense and comfort of blended ratio can be improved smoothly at silk when fibre composition is blended, filters, obtain mixed Condensating fiber；
(2) composite fibre is carried out blended, makes line density 1.14dtex, length is 5 ~ 7cm, can be improved the soft and smooth of filling cotton Sense and dispersibility, while being conducive to blended ratio and template mesh is added, it avoids being cut again when being laid with, improves the production effect of filling cotton Rate obtains blended ratio；
(3) blended ratio is placed in water, is uniformly mixed, is layed in template mesh by water flow, mesh is the ball of diameter 0.5cm Shape obtains web；
(4) web is subjected to spun lacing reinforcing, doffer speed 66m/min makes Unit Weight 60g/m2, keep filling cotton soft Comfortably, smooth easy dispersion, improves the practicability of filling cotton, obtains washable mould proof filling cotton.
The application method of the washable mould proof filling cotton, for filling pillow, toy, cushion, back cushion, the pillow being filled Head, cushion, can directly machine-wash after being lined with spot at toy, dry after washing.
Embodiment 2
A kind of washable mould proof filling cotton, is made of raw material from the following weight: acrylonitrile vinylidene chloride fibre 43, bombax cotton 24, milk protein Fiber 11, soybean fiber 11, modified chitosan fiber 11, copper ammonia fiber 8, active carbon loading silver fiber 8.
The modified chitosan fiber in 1% acetate fiber, stirs chitosan solution volume fraction to complete Dissolution, makes the concentration 220mg/L of chitosan solution, to the polyphenol solution that concentration is 70mg/L is added, stirs while adding, The additional amount of polyphenol solution is the 1/3 of chitosan solution volume, mixes be placed on 65 DEG C of standings 2 hours completely, centrifugation, it is heavy to take It forms sediment, spinning obtains modified chitosan fiber.
A kind of preparation method of washable mould proof filling cotton, comprising the following steps:
(1) by acrylonitrile vinylidene chloride fibre, bombax cotton, milk protein fiber, soybean fiber, modified chitosan fiber, copper ammonia fiber and load Active carbon of silver fiber is added in folic acid solution, concentration 18mg/L, is uniformly mixed, and impregnates 5 hours in 18 DEG C, promotes between fiber It is bonded, is conducive to that the soft and smooth sense and comfort of blended ratio can be improved smoothly at silk when fibre composition is blended, filters, obtain mixed Condensating fiber；
(2) composite fibre is carried out blended, makes line density 1.16dtex, length is 5 ~ 7cm, can be improved the soft and smooth of filling cotton Sense and dispersibility, while being conducive to blended ratio and template mesh is added, it avoids being cut again when being laid with, improves the production effect of filling cotton Rate obtains blended ratio；
(3) blended ratio is placed in water, is uniformly mixed, is layed in template mesh by water flow, mesh is the ball of diameter 0.6cm Shape obtains web；
(4) web is subjected to spun lacing reinforcing, doffer speed 67m/min makes Unit Weight 65g/m2, keep filling cotton soft Comfortably, smooth easy dispersion, improves the practicability of filling cotton, obtains washable mould proof filling cotton.
The application method of the washable mould proof filling cotton, for filling pillow, toy, cushion, back cushion, the pillow being filled Head, cushion, can directly machine-wash after being lined with spot at toy, dry after washing.
Embodiment 3
A kind of washable mould proof filling cotton, is made of raw material from the following weight: acrylonitrile vinylidene chloride fibre 44, bombax cotton 25, milk protein Fiber 12, soybean fiber 12, modified chitosan fiber 12, copper ammonia fiber 9, active carbon loading silver fiber 9.
The modified chitosan fiber in 2% acetate fiber, stirs chitosan solution volume fraction to complete Dissolution, makes the concentration 230mg/L of chitosan solution, to the polyphenol solution that concentration is 80mg/L is added, stirs while adding, The additional amount of polyphenol solution is the 1/4 of chitosan solution volume, mixes be placed on 70 DEG C of standings 2 hours completely, centrifugation, it is heavy to take It forms sediment, spinning obtains modified chitosan fiber.
A kind of preparation method of washable mould proof filling cotton, comprising the following steps:
(1) by acrylonitrile vinylidene chloride fibre, bombax cotton, milk protein fiber, soybean fiber, modified chitosan fiber, copper ammonia fiber and load Active carbon of silver fiber is added in folic acid solution, concentration 20mg/L, is uniformly mixed, and impregnates 6 hours in 20 DEG C, promotes between fiber It is bonded, is conducive to that the soft and smooth sense and comfort of blended ratio can be improved smoothly at silk when fibre composition is blended, filters, obtain mixed Condensating fiber；
(2) composite fibre is carried out blended, makes line density 1.18dtex, length is 5 ~ 7cm, can be improved the soft and smooth of filling cotton Sense and dispersibility, while being conducive to blended ratio and template mesh is added, it avoids being cut again when being laid with, improves the production effect of filling cotton Rate obtains blended ratio；
(3) blended ratio is placed in water, is uniformly mixed, is layed in template mesh by water flow, mesh is the ball of diameter 0.7cm Shape obtains web；
(4) web is subjected to spun lacing reinforcing, doffer speed 68m/min makes Unit Weight 70g/m2, keep filling cotton soft Comfortably, smooth easy dispersion, improves the practicability of filling cotton, obtains washable mould proof filling cotton.
The application method of the washable mould proof filling cotton, for filling pillow, toy, cushion, back cushion, the pillow being filled Head, cushion, can directly machine-wash after being lined with spot at toy, dry after washing.
Comparative example 1
Remove acrylonitrile vinylidene chloride fibre, remaining preparation and application, with embodiment 1.
Comparative example 2
Remove bombax cotton, remaining preparation and application, with embodiment 1.
Comparative example 3
Remove milk protein fiber, remaining preparation and application, with embodiment 1.
Comparative example 4
Remove soybean fiber, remaining preparation and application, with embodiment 1.
Comparative example 5
Remove modified chitosan fiber, remaining preparation and application, with embodiment 1.
Comparative example 6
Remove active carbon loading silver fiber, remaining preparation and application, with embodiment 1.
Comparative example 7
Folic acid solution in step (1) is changed to water, remaining preparation and application, with embodiment 1.
Comparative example 8
Removing the length in step (2) is 5 ~ 7cm, remaining preparation and application, with embodiment 1.
Comparative example 9
Remove the template mesh in step (3), remaining preparation and application, with embodiment 1.
Comparative example 10
The spun lacing removed in step (4) is reinforced, remaining preparation and application, with embodiment 1.
Comparative example 11
108138403 A of patent document CN discloses a kind of filling cotton.
The stability of embodiment and comparative example filling cotton:
Antibacterial is carried out using standard GB/T/T20944.3-2008 " the evaluation third portion of antibacterial textile performance: succusion " Property quantitative test, before the filling cotton washing of testing example and comparative example, washing 50 times, washing 100 times and washing 200 times mould Bacterium bacteriostasis rate, and preceding and washing 200 times are washed according to the method measurement each group filling cotton in 108138403 A of patent document CN Fluffy degree, each test is repeated 3 times, and results are averaged, the stability of embodiment and comparative example filling cotton: is shown in Table 1.
Table 1: the stability of embodiment and comparative example filling cotton:
From table 1 the result shows that, the washable mould proof filling cotton of embodiment, with the increase of wash number, antibiotic rate decline slowly, It is able to carry out long-term antibacterial, fluffy degree is able to maintain 20% or more after washing 200 times, and washability is obviously strong compared with comparative example, shows this The washable mould proof filling cotton that invention provides has stable bacteriostasis property and fluffy degree.

Claims (7)

1. a kind of washable mould proof filling cotton, which is characterized in that be made of raw material from the following weight: acrylonitrile vinylidene chloride fibre 42 ~ 44, kapok Fiber 23 ~ 25, soybean fiber 10 ~ 12, modified chitosan fiber 10 ~ 12, copper ammonia fiber 7 ~ 9, carries milk protein fiber 10 ~ 12 Active carbon of silver fiber 7 ~ 9.
2. washable mould proof filling cotton according to claim 1, which is characterized in that the modified chitosan fiber gathers shell In the acetate fiber that sugar juice volume fraction is 1 ~ 2%, stir to being completely dissolved, make the concentration 210 of chitosan solution ~ 230mg/L is stirred while adding to the polyphenol solution that concentration is 60 ~ 80mg/L is added, and the additional amount of polyphenol solution is poly- for shell The 1/3 ~ 1/4 of sugar juice volume mixes be placed on 60 ~ 70 DEG C of standings 1 ~ 2 hour completely, and centrifugation takes precipitating, spinning obtains modification Chitin fiber.
3. the preparation method of washable mould proof filling cotton described in a kind of claim 1, which comprises the following steps:
(1) by acrylonitrile vinylidene chloride fibre, bombax cotton, milk protein fiber, soybean fiber, modified chitosan fiber, copper ammonia fiber and load Active carbon of silver fiber is added in folic acid solution, is uniformly mixed, and impregnates 4 ~ 6 hours in 15 ~ 20 DEG C, and filtering obtains composite fibre；
(2) composite fibre is carried out blended, makes 1.14 ~ 1.18dtex of line density, length is 5 ~ 7cm, obtains blended ratio；
(3) blended ratio is placed in water, is uniformly mixed, is layed in template mesh by water flow, obtains web；
(4) web is subjected to spun lacing reinforcing, makes 60 ~ 70g/m of Unit Weight2, obtain washable mould proof filling cotton.
4. the preparation method of washable mould proof filling cotton according to claim 3, which is characterized in that the folic acid of the step (1) Solution, concentration are 15 ~ 20mg/L.
5. the preparation method of washable mould proof filling cotton according to claim 3, which is characterized in that the template of the step (3) Mesh is the spherical of 0.5 ~ 0.7cm of diameter.
6. the preparation method of washable mould proof filling cotton according to claim 3, which is characterized in that the spun lacing of the step (4) It reinforces, doffer speed is 66 ~ 68m/min.
7. a kind of application method of any one of claim 1 ~ 6 washable mould proof filling cotton, which is characterized in that for filling pillow Head, toy, cushion, back cushion, the pillow being filled, cushion, can directly machine-wash after being lined with spot at toy, after washing It dries.
CN201810951511.XA 2018-08-21 2018-08-21 A kind of washable mould proof filling cotton Pending CN109056189A (en)