CN109056152A - A kind of protective fabric - Google Patents
A kind of protective fabric Download PDFInfo
- Publication number
- CN109056152A CN109056152A CN201811071011.3A CN201811071011A CN109056152A CN 109056152 A CN109056152 A CN 109056152A CN 201811071011 A CN201811071011 A CN 201811071011A CN 109056152 A CN109056152 A CN 109056152A
- Authority
- CN
- China
- Prior art keywords
- protective fabric
- network
- warp
- follows
- strand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of protective fabric, by 2 strand 30s/1Aramid fiber 1313 single thread and 1 strand 18DConductive filament composition, and acid-proof alkali process is carried out, form the protective fabric with antistatic, anti-soda acid and flame retardant property.The technological parameter of its acid-proof alkali process is as follows: 130 DEG C of the dyeing temperature of protective fabric, and setting temperature is 180--185 DEG C, and anti-200 DEG C of soda acid feeding setting temperature, forming machine speed is 25 ms/min.Warp thread is sprayed above warp stop frame to warp beam after machine with manual watering can in weaving process, increases the lubrication of warp thread, mitigates each section friction, keeps silk fabric face more plentiful, quality grey quality reaches 98% or more.Protective fabric caused by being knitted using the present invention, while there is antistatic, anti-soda acid and flame retardant property.
Description
Technical field
The present invention relates to a kind of protective fabrics.
Background technique
The antistatic process of fabric uses more traditional and mature " implantation ".It is i.e. orderly according to a certain percentage
In warp, the weft threads implantable conductive fiber of fabric.Difficult point in production mainly needs the flame retardant property for solving fabric and anti-soda acid to invade
How the performance of erosion has both.Most importantly yarn used in fabric must also have while having excellent flame retardant property
Standby good acid-proof alkaline.Traditional textile raw material whether brocade in natural cotton, hair, silk, fiber crops or synthetic fibers
Synthetic fibre, terylene etc. do not comply with condition.
Summary of the invention
For the above technical problems, the present invention provides a kind of protective fabric, has antistatic, anti-soda acid and resistance
Fire performance.
The purpose of the present invention is achieved through the following technical solutions:
A kind of protective fabric, by 2 strand 30s/1Aramid fiber 1313 single thread and 1 strand 18DConductive filament composition, and carry out at acid-proof alkali
Reason forms the protective fabric with antistatic, anti-soda acid and flame retardant property.
Further, the acid-proof alkali process is matched using following auxiliary agent:
Water: 1L;
Waterproofing agent: 100ml;
Crosslinking agent: 10ml;
Softening agent: 10ml;
Catalyst: 1ml.
Further, the technological parameter of the acid-proof alkali process is as follows: 130 DEG C of the dyeing temperature of protective fabric, sizing temperature
Degree is 180--185 DEG C, and anti-200 DEG C of soda acid feeding setting temperature, forming machine speed is 25 ms/min.
Further, include the following steps:
S1: by 2 strand 30s/1Aramid fiber 1313 single thread and 1 strand 18DConductive filament is closed using spray net machine Tong Bu Merger;Merger sprays net when closing
The technological parameter of machine is as follows: (1) linear velocity is 500 ms/min;(2) two pressure pads are set on the tension pulley of spray net machine to complete
The control of Merger conjunction tension;(3) network nozzle is 300D;(4) air pressure of air compressor is 0.3MPa;
S2: using high speed cone winder, and cylinder is made in the fiber network after S1 Merger is closed;
S3: the fiber of cylinder is made of chemical fiber double-twister twisting S2 network;
S4: warping;
S5: weaving.
Further, described two pressure pad quality are 50g, by the steel of m12 × 4 gasket of a 35g and 15g
The combination of the plastic spacer of m12 × 5 is constituted.
Further, in the S2 step network be made cylinder technological parameter it is as follows: P1--P13 is technological parameter code;
(1) winding method code P01, using the network mode of filled type;(2) runing time code P02, is set as 16
Minute, each winder material net weight that network is produced is in 430g;(3) P03 originates traverse code: 285mm;(4) traverse code is terminated
P04: last traverse is 90mm when being the termination of network system;(5) initial frequency code P05 is set as 30 hertz;(6) frequency is terminated
P06:23 hertz of code;(7) P07 lag lifting speed is set as 75 mm/second of maximum value;(8) position is set as P08 always
7 millimeters, i.e. length of the winder initial position apart from network spool lower end;(9) P09 draws yarn and is delayed 5 seconds;(10) micro 3 milli of P10 difference
Rice;(11) the micro- number of P11 difference: 3;(12) P12 automatically resets: 0, after indicating that one batch of every winder material finishes, frequency converter will be instructed
Lag motor runs lag to initial position;(13) tension: pressure pad 80g.
Further, the technological parameter of twisting is as follows in the S3 step:
(1) ingot speed of chemical fiber double-twister: 10000r/min is adjusted;(2) by the balloon guide height of chemical fiber double-twister,
It adjusts to extreme higher position;(3) additional tension of tensioner: one is respectively placed in the flyer and ingot chamber of chemical fiber double-twister
The tension pearl of 9.53mm;(4) balloon tension of chemical fiber double-twister: overfeeding is selected as 112%;(5) twist: 627T/M;(6) orientation
S to;(7) 3 ° 42 ' of winding angle.
Further, the technological parameter of warping is as follows in the S4 step:
Warp arrangement: first 26: second 1,35 plumages of grade bars specification/when, grade bars threading method, 2 wear, grade bars width .7.9cm,
Upper cylinder number 216, item number 20 are displaced 1.95mm/r, 90 meters of coupe, warping breadth 163cm, warping speed 350m/min, roll up through vehicle
Fast 180m/min, warped length: 1620 meters;Volume is started to walk 0.4mpa through air pressure, is gradually decrease to 0.25mpa during volume warp;It is whole
Ensured that warp arrangement is accurate in the process, broken end change is clear, and leasing is clear, and it is long accurate to count, and volume is strictly controlled through tension
System, in bottoming, volume is rolled up after 30 meters through air pressure 0.25MPa, and air pressure is adjusted to 0.2MPa, when rolling up through 1200 meters, air pressure
It is adjusted to 0.15MPa.
Further, woven technological parameter is as follows in the S5 step: heald level time: 310 °, wefting insertion traverse are as follows:
70 °, sword head initially enters fell: 185 °, double sword handover: 290 °, double swords exit fell;The back rest of Weaving-machine presses scale height
Degree is 11.5cm, and warp stop frame altitude scale is 10.5cm;Keep continuous Yarn filoplume submissive in weaving process.
Further, the method for keeping continuous Yarn filoplume submissive is: using 15% textile emulsion wax, 1% emulsification is white
Oil, 1% demulcent are configured to lubricating fluid, are sprayed above warp stop frame to warp beam to warp thread after machine with manual watering can.
Further, pressure roller periphery is wrapped over using plastic cement or rough surfaced rubber covering when batching aramid fiber in S5 weaving process.
Warp, weft threads of the present invention using the aramid fiber dyed yarn of aramid fiber 1313 spinning as fabric.Aramid fiber 1313 is one
The emerging high-performance fiber (High Perfoman Fibrers) of kind is a kind of outstanding high-temperature fibre.Also it is referred to as by people
Super fiber (Super Fibers).It is to be connected with each other the linear macromolecule chain that meta position phenyl is constituted by amide group.From
Amido bond in its molecular structure is connected with meta position phenyl ring.Covalent bond inward turning indexing on meta position phenyl ring can be lower.Rotatable angle
It spends bigger.Because its macromolecular is flexible chain structure, close to common flexible chain fibre in mechanical property.Tool
There is excellent physical mechanical property, intensity is greater than cotton, and elongation and terylene are close, and soft, excellent wear-resisting property can knit
Property and taking are all relatively good.Hydrogen bond is existed simultaneously in two planes and is arranged in lattice type in its macromolecular structure, phase
Active force is very strong between mutually, to keep its chemical structure extremely stable.It is difficult to carry out with chemical reagent such as soda acids under normal circumstances
Reaction, therefore there is extremely good chemical corrosion resistance.
The glass transition temperature of aramid fiber 1313 is 270 DEG C, and thermal decomposition temperature is up to 400 DEG C.It is continuously heated at 200 DEG C
20000 hours, intensity kept 30%, and 260 DEG C of whens are continuously heated 1000 hours, and intensity keeps 65%, and heat resistance is obvious, is better than
General synthetic fibers, such as terylene.
Aramid fiber 1313 does not melt, and deterioration when temperature is more than 400 DEG C is until carbonization is decomposed.What is generated when pyrolytic is main
Gas is co.co2.Smoke density is significantly less than other synthetic fibers, self-extinguishing without fire.Fiber enters 900 DEG C~1500 DEG C high temperature rings
A kind of special heat-barrier coating can be generated when border, outside heat cannot temporarily be passed to inside, it is very effective to resist high temperature.With this
When being exposed to high fever or close to flame, fiber can gradually expand the fabric of fiber production, generate between the fabric and inner layer
The air gap plays the role of completely cutting off heat transfer, and protection human body preserves from.
The invention has the benefit that
Protective fabric caused by being knitted using the present invention, while there is antistatic, anti-soda acid and flame retardant property.
Specific embodiment
Below with reference to embodiment, the present invention will be described in detail.
Embodiment: a kind of protective fabric of the present invention, by 2 strand 30s/1Aramid fiber 1313 single thread and 1 strand 18DConductive filament composition, and
Acid-proof alkali process is carried out, the protective fabric with antistatic, anti-soda acid and flame retardant property is formed;Conductive filament selects 18 in this exampleD
Import unlicensed tour guide's electrical filament.
The acid-proof alkali process is matched using following auxiliary agent:
Water: 1L;
Waterproofing agent: 100ml;
Crosslinking agent: 10ml;
Softening agent: 10ml;
Catalyst: 1ml.
The technological parameter of the acid-proof alkali process is as follows: 130 DEG C of dyeing temperature, setting temperature is 180--185 DEG C, acid-proof
200 DEG C of alkali feeding temperature, speed are 25 ms/min.
The processing method of the protective fabric, includes the following steps:
S1: by 2 strand 30s/1Aramid fiber 1313 single thread and 1 strand 18DConductive filament is closed using spray net machine Tong Bu Merger;Merger sprays net when closing
The technological parameter of machine (the AG EIV-983 type of third textile machinery factory of Shaoxing, Zhejiang Province city production sprays net machine) is as follows: (1) linear speed
Degree is 500 ms/min, and highly efficient in productivity, end breakage rate is very low;(2) two pressure pads are set on the tension pulley of spray net machine to complete
Merger closes the control of tension, the pressure pad: 50g, and two are respectively the steel of m12 × 4 gasket and the plastic spacer of m12 × 5;(3) network
Nozzle specification: 300D, 2 strand 30s/1Aramid fiber 1313 adds 1 strand 18DItem part of import conductive filament closes 411.7D, using 300DNetwork spray
Mouth Jin Hang Merger is closed, and can satisfy production requirement;(4) air pressure of air compressor is 0.3MPa, and air pressure increases, and the load becomes large, nothing
Increase cost for ground: air pressure is too small, the bad , Merger of strand obvolvent close after when solution is moved back in next procedure, will cause it is asynchronous move back solution,
Directly affect the production of next procedure;
S2:, will using high speed cone winder (the RF303C high speed cone winder of Rifa Textile Machinery Co., Ltd., Zhejiang's production)
Cylinder is made in fiber network after step S1 Merger is closed;Specifically: (1) winding method P01, parameter 2, what is taken is the network of filled type
Mode processed, because of the influence of sliver filoplume, move back solution tension it is very big, if taking the network mode of the anti-network formula of network chemical-fibres filaments,
The end breakage rate of double twisting can not meet the requirement normally produced 85%~95% or so, take the network mode of filled type with
Afterwards, the end breakage rate of double twisting meets the requirement normally produced 2%~4% or so;(2) runing time P02 is set as 16 points
Clock, each winder material net weight that network is produced during double twisting twisting, meet the requirement of production in 430g or so;(3)
P03 originates traverse: 285mm;(4) traverse P04:90mm is terminated, last traverse is 90mm when being the termination of network system,
It terminates traverse and is set as 90, the yarn molding that network is produced is good, it is ensured that network produces the bobbin come when increasing package amount
In double twisting twisting, air ring is touched less than raw material;(5) initial frequency P05 is set as 30 hertz;(6) P06 terminates 23 hertz of frequency
Hereby;(7) P07 lag lifting speed is set as 75 mm/second of maximum value, it is therefore an objective to reduce when double twisting moves back solution and move back rich tension.
(8) P08 7 millimeters of position, i.e. length of the winder initial position apart from network spool lower end always;(9) P09 draws yarn and is delayed 5 seconds;
(10) micro 3 millimeters of P10 difference, it can be ensured that strand normally moves back solution when moving back solution;Difference is micro too big and too small, all will affect
Solution is moved back during double twisting twisting;(11) the micro- number of P11 difference: 3;(12) P12 automatically resets: 0, indicate that one batch of every winder has been expected
Bi Yihou, frequency converter will instruct lag motor to run lag to initial position;(13) tension: pressure pad 80g, in network process
In, pressure pad 80g is proper, increase or reduce all directly influence network be made cylinder molding and next procedure move back solution and
Twisting;
S3: it is twisted using chemical fiber double-twister (the RF310G chemical fiber double-twister of Rifa Textile Machinery Co., Ltd., Zhejiang's production)
The fiber of cylinder is made in S2 network processed;(1) ingot speed: 10000r/min, the broken end with 10000r/min ingot speed, during Yarn twisting
Rate can satisfy the requirement normally produced within 5%;(2) balloon guide height (balloon height), because of the short fibre of twisting
The air ring of kind is because move back that solution tension is big and the elongated slight of stature that seems, air ring silk guide frame will be adjusted to extreme higher position 9;(3)
The additional tension of tensioner: the tension pearl of a 9.53mm is respectively placed in flyer and ingot chamber;(4) balloon tension: overfeeding selection
It is 112%;(5) twist: 627T/M;(6) orientation S to;(7) 3 ° 42 ' of winding angle (9.0 times/one way);
S4: warping: the ASGV-231 type sectional warper produced using shining sun textile machinery factory, specifically: warp row
Column: first 26: second 1,35 plumages of grade bars specification/when, grade bars threading method, 2 wear, and grade bars width is cylinder number 216 on 7.9cm, item number
20, displacement 1.95mm/r (refer to every 1 circle of rotation of warping machine, the mobile 1.95mm of board), 90 meters of coupe, warping breadth 163cm,
Warping speed 350m/min is rolled up through speed 180m/min, warped length: 1620 meters;Volume is started to walk 0.4mpa through air pressure, and volume passes through
It is gradually decrease to 0.25mpa in journey, ensures that warp arrangement is accurate during warping, broken end change is clear, and leasing is clear,
Meter length is accurate, and volume wants strict control through tension, and volume is rolled up after 30 meters, air pressure adjustment through air pressure 0.25MPa when bottoming
To 0.2MPa, when rolling up through 1200 meters, air pressure is adjusted to 0.15MPa, volume through tension it is too small if, subsequent weaving process will be caused
In to move back solution difficult;
S5: it weaving: is weaved using the automatic rapier loom of Russia and the U.S. GA737, processing parameter setting are as follows: heald level time:
310 °, wefting insertion traverse are as follows: 70 °, sword head initially enters fell: 185 °, double sword handover: 290 °, double swords exit fell;Back rest pressure
Dynamic scale height should be 11.5cm, warp stop frame altitude scale 10.5cm, and since aramid fiber is rigidly larger, external manifestation is when weaving
" brittleness ", elasticity is relatively poor, weave the fabric of completion coiling process in order to avoid occur polishing scratch, fluff, press against it is disconnected etc. hard
Wound, when batching use flexible preferable plastic cement, rough surfaced rubber covering looping pressure roller, avoid silk fabric face occur polishing scratch, fluff, press against it is disconnected etc.
Hard defects.
For the soft and moist property for increasing warp thread, and continuous Yarn filoplume is submissive, and with 15% textile emulsion wax, 1% emulsification white oil, 1% is viscous
Lubrication prescription is configured to lubricating fluid, is sprayed above warp stop frame to warp beam to warp thread after machine with manual watering can, increases the profit of warp thread
It is sliding, mitigate each section friction, keeps silk fabric face more plentiful, quality grey quality reaches 98% or more.
Claims (10)
1. a kind of protective fabric, it is characterised in that: by 2 strand 30s/1Aramid fiber 1313 single thread and 1 strand 18DConductive filament composition, and carry out
Acid-proof alkali process forms the protective fabric with antistatic, anti-soda acid and flame retardant property.
2. protective fabric according to claim 1, it is characterised in that: the acid-proof alkali process using following auxiliary agent match and
At:
Water: 1L;
Waterproofing agent: 100ml;
Crosslinking agent: 10ml;
Softening agent: 10ml;
Catalyst: 1ml.
3. protective fabric according to claim 1 or claim 2, it is characterised in that: the technological parameter of the acid-proof alkali process is as follows: anti-
130 DEG C of the dyeing temperature of mask material, setting temperature be 180--185 DEG C, anti-200 DEG C of soda acid feeding setting temperature, forming machine speed
It is 25 ms/min.
4. the processing method of protective fabric as described in claim 1, characterized by the following steps:
S1: by 2 strand 30s/1Aramid fiber 1313 single thread and 1 strand 18DConductive filament is closed using spray net machine Tong Bu Merger;The work of net machine is sprayed when Merger is closed
Skill parameter is as follows: (1) linear velocity is 500 ms/min;(2) two pressure pads of setting have carried out into Merger conjunction on the tension pulley of spray net machine
The control of power;(3) network nozzle is 300D;(4) air pressure of air compressor is 0.3MPa;
S2: using high speed cone winder, and cylinder is made in the fiber network after S1 Merger is closed;
S3: the fiber of cylinder is made of chemical fiber double-twister twisting S2 network;
S4: warping;
S5: weaving.
5. the processing method of protective fabric as claimed in claim 2, it is characterised in that: described two pressure pad quality are 50g, by one
The combination of the plastic spacer of the m12 of the steel of the m12 of a 35g × 4 gasket and a 15g × 5 is constituted.
6. the processing method of protective fabric as claimed in claim 2, it is characterised in that: the technique that cylinder is made in network in the S2 step
Parameter is as follows: P1--P13 is technological parameter code;
(1) winding method code P01, using the network mode of filled type;(2) runing time code P02 is set as 16 minutes,
Each winder material net weight that network is produced is in 430g;(3) P03 originates traverse code: 285mm;(4) it terminates traverse code P04: being network
System traverse last when terminating is 90mm;(5) initial frequency code P05 is set as 30 hertz;(6) frequency codes P06 is terminated:
23 hertz;(7) P07 lag lifting speed is set as 75 mm/second of maximum value;(8) position is set as 7 millimeters to P08 always, i.e.,
Length of the winder initial position apart from network spool lower end;(9) P09 draws yarn and is delayed 5 seconds;(10) micro 3 millimeters of P10 difference;(11)P11
The micro- number of difference: 3;(12) P12 automatically resets: 0, after indicating that one batch of every winder material finishes, frequency converter will instruct lag motor will
Lag is run to initial position;(13) tension: pressure pad 80g.
7. the processing method of protective fabric as claimed in claim 2, it is characterised in that: the technological parameter of twisting in the S3 step
It is as follows:
(1) ingot speed of chemical fiber double-twister: 10000r/min is adjusted;(2) by the balloon guide height of chemical fiber double-twister, adjusting is arrived
Extreme higher position;(3) of a 9.53mm respectively the additional tension of tensioner: is placed in the flyer and ingot chamber of chemical fiber double-twister
Power pearl;(4) balloon tension of chemical fiber double-twister: overfeeding is selected as 112%;(5) twist: 627T/M;(6) orientation S to;(7) it winds
3 ° 42 ' of angle.
8. the processing method of protective fabric as claimed in claim 2, it is characterised in that: the technological parameter of warping in the S4 step
It is as follows:
Warp arrangement: first 26: second 1,35 plumages of grade bars specification/when, grade bars threading method, 2 wear, grade bars width .7.9cm, upper cylinder
Number 216, item number 20 are displaced 1.95mm/r, 90 meters of coupe, warping breadth 163cm, warping speed 350m/min, roll up through speed
180m/min, warped length: 1620 meters;Volume is started to walk 0.4mpa through air pressure, is gradually decrease to 0.25mpa during volume warp;Warping
Ensure that warp arrangement is accurate in the process, broken end change is clear, and leasing is clear, count it is long accurate, volume through tension strict control,
Volume is rolled up after 30 meters through air pressure 0.25MPa when bottoming, and air pressure is adjusted to 0.2MPa, and when rolling up through 1200 meters, air pressure is adjusted to
0.15MPa。
9. the processing method of protective fabric as claimed in claim 2, it is characterised in that: woven technological parameter in the S5 step
It is as follows: heald level time: 310 °, wefting insertion traverse are as follows: 70 °, sword head initially enters fell: 185 °, double sword handover: 290 °, double swords move back
Fell out;It is 11.5cm that the back rest of Weaving-machine, which presses scale height, and warp stop frame altitude scale is 10.5cm;It is protected in weaving process
It is submissive to continue Yarn filoplume.
10. the processing method of protective fabric as claimed in claim 7, it is characterised in that: described that continuous Yarn filoplume is kept to fit perfectly
Method is: using 15% textile emulsion wax, 1% emulsification white oil, 1% demulcent is configured to lubricating fluid, is stopped after machine with manual watering can
Through being sprayed above frame to warp beam to warp thread.