CN109054250A - A kind of wood plastic composite of high mallow stem hide fiber enhancing and its application - Google Patents
A kind of wood plastic composite of high mallow stem hide fiber enhancing and its application Download PDFInfo
- Publication number
- CN109054250A CN109054250A CN201810886762.4A CN201810886762A CN109054250A CN 109054250 A CN109054250 A CN 109054250A CN 201810886762 A CN201810886762 A CN 201810886762A CN 109054250 A CN109054250 A CN 109054250A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- high mallow
- plastic composite
- maleic anhydride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wood plastic composite of high mallow stem hide fiber enhancing and its applications, it is related to wood plastic composite technical field, this kind of material includes following raw material: polyvinyl chloride resin powder SG-5, high mallow stem hide fiber, maleic anhydride grafted ABS resin, calcium titanium tailing powder, villus powder, epoxy aliphatic acid methyl ester, glue easily element T-78, sheep bar powder, compounding coupling agent, compound antioxidant.Wood plastic composite of the invention mechanical strength, waterproofness, resistance to oxidation aging and in terms of it is upper promoted significant, improve the overall performance of wood plastic composite, improve application performance, service life is more secure, has good promotional value.
Description
Technical field
The present invention relates to wood plastic composite technical fields, and in particular to a kind of wood plastics composite of high mallow stem hide fiber enhancing
Material.
Background technique
Wood plastic composite is also known as Wood-plastic profiles, is with the plant fibers such as wood powder, agricultural stalk powder and plastics for main original
Material is process using advanced technologies, and product repeats recycling and reusing.In recent years, as global resources are increasingly withered
It exhausts, social environment consciousness is increasingly surging.Wood plastic composite is as clean compound of a kind of completely new green product, ecology
Material.Various waste plastic, culled wood and forest and agricultural biomass can be used in its raw materials for production.Help to slow down plastic refuse
Pollution, also contribute to reducing agriculture and forestry organic waste material burning and give the pollution of environment bring, while the production of wood plastic composite and making
With, the volatile matter for endangering human health will not be distributed to ambient enviroment, be substitute traditional timber energy conservation and environmental protection of new generation newly produce
Product, market application scenarios are extensive.Contain in the main components such as cellulose, hemicellulose and lignin due to composition wood materials
A large amount of polar hydroxyl groups and phenolic hydroxyl group functional group, surface exhibits go out very strong chemical polarity.Therefore, wood fibre-is being carried out
In the development process of plastic body chain timbers plastic composite materials, the maximum problem for needing to solve is how to make the wooden fibre of hydrophilic polarity
There is good compatibility, interfacial adhesion, to make wood materials between dimension and the non-polar plastic basal body interface of hydrophobic
Reach intermolecular between superficial layer and the superficial layer of plastics to merge, both, material of different nature is appropriate is compounded in one
It rises, generates the new material more more excellent than original homogenous material performance, be always the emphasis of research.
The patent application of Publication No. CN103613823A discloses a kind of anticorrosive wood-plastic composite sectional material formula, it be by
The raw material composition of following weight parts: polyvinyl resin particle 30-40, wood fibre 50-60, polyethylene glycol 400 2-3,2,6-
Dimethylphenyl boronic acid 1-2, maleic anhydride inoculated polypropylene 3-4, aluminium hydroxide 1-2, polyamide wax micropowder 2-3, modified plasticizer
3-4;This kind of Wood-plastic composite section bar has good bacteria corrosion-resistant and antiseptic property, but its mechanical strength performance is poor, application
It is restricted.
The patent application of Publication No. CN104672697A discloses a kind of wood plastic composite, by weight, by
Following components is mixed: 50-75 parts of polyvinyl chloride resin, 16-20 parts of wood powder, and 20-30 parts of light calcium carbonate powder, 6-8 parts of modification biological charcoal, calcium
1.3-1.5 parts of zinc stabilizer, 0.8-1 parts of haloflex, 0.3-0.5 parts of polyethylene wax, 0.5-0.8 parts of stearic acid, plasticizer
1.0-1.5 parts, 1.9-2.4 parts of ACR processing aid, 5-8 parts of feed back.This kind of wood plastic composite degradability is good, low-carbon environment-friendly,
But its shielding is poor, application is restricted.
Summary of the invention
The purpose of the present invention is to provide a kind of wood plastic composite of high mallow stem hide fiber enhancing, this kind of wood and plastic composites
Expect that overall performance is excellent, application is good.
In order to achieve the above object, the present invention is achieved through the following technical solutions:
A kind of wood plastic composite of high mallow stem hide fiber enhancing, is made of following raw material according to parts by weight:
SG-556-66 parts of polyvinyl chloride resin powder;
35-42 parts of high mallow stem hide fiber;
5-6.5 parts of maleic anhydride grafted ABS resin;
9-12 parts of tailing powder of calcium titanium;
8-9.5 parts of villus powder;
2-2.7 parts of epoxy aliphatic acid methyl ester;
Glue easily T-781-1.6 parts of element;
1.5-2.3 parts of sheep bar powder;
Coupling agent 2.5-3.5 parts of compounding;
0.8-1.1 parts of compound antioxidant.
Further, above-mentioned wood plastic composite is made of following raw material according to parts by weight:
SG-556 parts of polyvinyl chloride resin powder;
35 parts of high mallow stem hide fiber;
5 parts of maleic anhydride grafted ABS resin;
9 parts of powder of calcium titanium tailing;
8 parts of villus powder;
2 parts of epoxy aliphatic acid methyl ester;
Glue easily T-781 parts of element;
1.5 parts of sheep bar powder;
2.5 parts of coupling agent of compounding;
0.8 part of compound antioxidant;
Above-mentioned maleic anhydride grafted ABS resin is made of the maleic anhydride grafted ABS of two breeds of horses, the grafting of the first maleic anhydride
ABS melt index is 2g/10min, grafting rate 1.25%;Second of maleic anhydride grafted ABS melt index is 1g/10min,
Grafting rate is 6.50%;And the mass ratio of the first maleic anhydride grafted ABS with second is 2:1.
Further, above-mentioned compounding coupling agent be tin coupled SSBR, titanate coupling agent 201, three kinds of rare-earth coupling agent at
Point merge according to mass ratio 2:4:1.
Further, above-mentioned compound antioxidant be antioxidant 1076, antioxidant 1010, tri- kinds of ingredients of antioxidant DSTP according to
Mass ratio 4:3:2 merges.
Further, above-mentioned composite material the preparation method is as follows:
(1) it the modification of fiber: takes the cleaning of high mallow stem hide fiber to be chopped, after drying, is placed in steam blasting tank, in steam temperature
Heat-insulation pressure keeping under the conditions of degree is 108 DEG C, pressure is 0.5MPa carries out Steam explosion treatment 8min;It is again that high mallow stem skin in tank is short
Fiber takes out drying, is then added to soaking and stirring 12min in the NaOH solution that mass fraction is 8%;It is then that high mallow stem skin is short
Fiber is placed in soaking and stirring 24min in organic solvent, and it is stand-by to impregnate end taking-up cleaning, drying;
Above-mentioned organic solvent by it is following according to parts by weight at being grouped as: 3 parts of ethyl acetate, 1 part of n-butanol, ethyl alcohol 1
Part, 1 part of dimethyl sulfoxide, 2 parts of dimethylbenzene;
(2) polyvinyl chloride resin powder SG-5, modified high mallow stem hide fiber, maleic anhydride grafting the mixing of raw material: are taken
ABS resin and villus powder are added in mixing machine, under conditions of operating temperature is 155 DEG C, working speed is 600r/min
8min is mixed;Calcium titanium tailing powder, epoxy aliphatic acid methyl ester and compounding coupling agent are added in mixing machine again, kept
Revolving speed is constant, and 6min is mixed under the conditions of operating temperature is 120 DEG C;Later by sheep bar powder, glue easily element T-78 and compounding
Antioxidant is added in mixing machine, keeps revolving speed and mixing temperature constant, stirs 5min, and mixture is obtained after mixing
Material;
(3) mixed material the melting extrusion of mixing: is delivered to melting extrusion in extruder.
Further, above-mentioned wood plastic composite is made of following raw material according to parts by weight:
SG-566 parts of polyvinyl chloride resin powder;
42 parts of high mallow stem hide fiber;
6.5 parts of maleic anhydride grafted ABS resin;
12 parts of powder of calcium titanium tailing;
9.5 parts of villus powder;
2.7 parts of epoxy aliphatic acid methyl ester;
Glue easily T-781.6 parts of element;
2.3 parts of sheep bar powder;
3.5 parts of coupling agent of compounding;
1.1 parts of compound antioxidant;
Above-mentioned maleic anhydride grafted ABS resin is made of the maleic anhydride grafted ABS of two breeds of horses, the grafting of the first maleic anhydride
ABS melt index is 3.5g/10min, grafting rate 1.40%;Second of maleic anhydride grafted ABS melt index is 2.5g/
10min, grafting rate 7.20%;And the mass ratio of the first maleic anhydride grafted ABS with second is 2.7:1.8.
Further, above-mentioned compounding coupling agent be tin coupled SSBR, titanate coupling agent 201, three kinds of rare-earth coupling agent at
Point merge according to mass ratio 3.5:7:2.5.
Further, above-mentioned compound antioxidant be antioxidant 1076, antioxidant 1010, tri- kinds of ingredients of antioxidant DSTP according to
Mass ratio 5.5:4.5:3.5 merges.
Further, above-mentioned composite material the preparation method is as follows:
(1) it the modification of fiber: takes the cleaning of high mallow stem hide fiber to be chopped, after drying, is placed in steam blasting tank, in steam temperature
Heat-insulation pressure keeping under the conditions of degree is 112 DEG C, pressure is 0.65MPa carries out Steam explosion treatment 6.5min;Again by high mallow stem skin in tank
Staple fiber takes out drying, is then added to soaking and stirring 10.5min in the NaOH solution that mass fraction is 9.5%;Then by high mallow
Stem skin staple fiber is placed in soaking and stirring 27min in organic solvent, and it is stand-by to impregnate end taking-up cleaning, drying;
The organic solvent by it is following according to parts by weight at being grouped as: 4.5 parts of ethyl acetate, 1.8 parts of n-butanol, second
1.8 parts of alcohol, 1.8 parts of dimethyl sulfoxide, 2.7 parts of dimethylbenzene;
(2) polyvinyl chloride resin powder SG-5, modified high mallow stem hide fiber, maleic anhydride grafting the mixing of raw material: are taken
ABS resin and villus powder are added in mixing machine, under conditions of operating temperature is 162 DEG C, working speed is 750r/min
6.5min is mixed;Calcium titanium tailing powder, epoxy aliphatic acid methyl ester and compounding coupling agent are added in mixing machine again, protected
It is constant to hold revolving speed, 4.5min is mixed under the conditions of operating temperature is 128 DEG C;Later by sheep bar powder, glue easily element T-78 and
Compound antioxidant is added in mixing machine, keeps revolving speed and mixing temperature constant, is stirred 3.5min, must be mixed after mixing
Close material;
(3) mixed material the melting extrusion of mixing: is delivered to melting extrusion in extruder.
The wood plastic composite of above-mentioned high mallow stem hide fiber enhancing can be in building, gardens, packaging, shipping vehicle, toy, body
It educates, the application in farm implements field.
The present invention have it is following the utility model has the advantages that the present invention by ingenious selection to wood plastic composite raw materials for production and
The inventive improvements of its preparation process, polyvinyl chloride resin powder SG-5, high mallow stem hide fiber, maleic anhydride grafted ABS in raw material
The cooperative interaction of the compositions such as resin, calcium titanium tailing powder, villus powder, epoxy aliphatic acid methyl ester, makes composite material obtained
With following activity beneficial: mechanical strength is high, tensile strength up to 28.0MPa or more, bending elastic modulus up to 2300MPa with
On, tough is good, and hydrophobicity is strong, waterproof and dampproof, anti-oxidant aging, and dimensional stability is high, not will cause dilatancy
Problem, environmental stress resistance ability are strong;Flame retardant rating is high, freeze proof low temperature resistant up to B1 grades or more;Energy conservation and environmental protection, green non-poisonous nothing
Evil, preparation is convenient, low production cost, and waste and old product are recyclable;Material plasticity is strong, and good insulating is antistatic, and
With excellent electromagnetic shielding performance, application is improved.
Specific embodiment
Below with reference to embodiment, further description of the specific embodiments of the present invention, and following embodiment is only used for more
Technical solution of the present invention is clearly demonstrated, and not intended to limit the protection scope of the present invention.
It all raw materials in embodiment and its produces composition and can be obtained by disclosed commercially available channel;
Embodiment 1
The present embodiment is related to a kind of wood plastic composite and preparation method thereof of high mallow stem hide fiber enhancing, this kind of composite wood
Material is made of following raw material according to parts by weight:
SG-556 parts of polyvinyl chloride resin powder;
35 parts of high mallow stem hide fiber;
5 parts of maleic anhydride grafted ABS resin;
9 parts of powder of calcium titanium tailing;
8 parts of villus powder;
2 parts of epoxy aliphatic acid methyl ester;
Glue easily T-781 parts of element;
1.5 parts of sheep bar powder;
2.5 parts of coupling agent of compounding;
0.8 part of compound antioxidant.
Maleic anhydride grafted ABS resin in the present embodiment, compounding coupling agent, compound antioxidant selection and produce such as following table
Shown in 1:
Table 1
The preparation method of wood plastic composite substantially follows the steps below in the present embodiment:
(1) it the modification of fiber: takes the cleaning of high mallow stem hide fiber to be chopped, after drying, is placed in steam blasting tank, in steam temperature
Heat-insulation pressure keeping under the conditions of degree is 108 DEG C, pressure is 0.5MPa carries out Steam explosion treatment 8min;It is again that high mallow stem skin in tank is short
Fiber takes out drying, is then added to soaking and stirring 12min in the NaOH solution that mass fraction is 8%;It is then that high mallow stem skin is short
Fiber is placed in soaking and stirring 24min in organic solvent, and it is stand-by to impregnate end taking-up cleaning, drying;
Above-mentioned organic solvent by it is following according to parts by weight at being grouped as: 3 parts of ethyl acetate, 1 part of n-butanol, ethyl alcohol 1
Part, 1 part of dimethyl sulfoxide, 2 parts of dimethylbenzene;
(2) polyvinyl chloride resin powder SG-5, modified high mallow stem hide fiber, maleic anhydride grafting the mixing of raw material: are taken
ABS resin and villus powder are added in mixing machine, under conditions of operating temperature is 155 DEG C, working speed is 600r/min
8min is mixed;Calcium titanium tailing powder, epoxy aliphatic acid methyl ester and compounding coupling agent are added in mixing machine again, kept
Revolving speed is constant, and 6min is mixed under the conditions of operating temperature is 120 DEG C;Later by sheep bar powder, glue easily element T-78 and compounding
Antioxidant is added in mixing machine, keeps revolving speed and mixing temperature constant, stirs 5min, and mixture is obtained after mixing
Material;
(3) mixed material the melting extrusion of mixing: is delivered to melting extrusion in extruder.
Embodiment 2
The present embodiment is related to a kind of wood plastic composite and preparation method thereof of high mallow stem hide fiber enhancing, this kind of composite wood
Material is made of following raw material according to parts by weight:
SG-562 parts of polyvinyl chloride resin powder;
38 parts of high mallow stem hide fiber;
5.5 parts of maleic anhydride grafted ABS resin;
10 parts of powder of calcium titanium tailing;
8.5 parts of villus powder;
2.3 parts of epoxy aliphatic acid methyl ester;
Glue easily T-781.4 parts of element;
1.8 parts of sheep bar powder;
3 parts of coupling agent of compounding;
0.9 part of compound antioxidant.
Maleic anhydride grafted ABS resin in the present embodiment, compounding coupling agent, compound antioxidant selection and produce such as following table
Shown in 2:
Table 2
The preparation method of wood plastic composite substantially follows the steps below in the present embodiment:
(1) it the modification of fiber: takes the cleaning of high mallow stem hide fiber to be chopped, after drying, is placed in steam blasting tank, in steam temperature
Heat-insulation pressure keeping under the conditions of degree is 110 DEG C, pressure is 0.55MPa carries out Steam explosion treatment 7.5min;Again by high mallow stem skin in tank
Staple fiber takes out drying, is then added to soaking and stirring 11.5min in the NaOH solution that mass fraction is 8.5%;Then by high mallow
Stem skin staple fiber is placed in soaking and stirring 25min in organic solvent, and it is stand-by to impregnate end taking-up cleaning, drying;
Above-mentioned organic solvent by it is following according to parts by weight at being grouped as: 3.5 parts of ethyl acetate, 1.2 parts of n-butanol, second
1.2 parts of alcohol, 1.2 parts of dimethyl sulfoxide, 2.4 parts of dimethylbenzene;
(2) polyvinyl chloride resin powder SG-5, modified high mallow stem hide fiber, maleic anhydride grafting the mixing of raw material: are taken
ABS resin and villus powder are added in mixing machine, under conditions of operating temperature is 158 DEG C, working speed is 650r/min
7.5min is mixed;Calcium titanium tailing powder, epoxy aliphatic acid methyl ester and compounding coupling agent are added in mixing machine again, protected
It is constant to hold revolving speed, 5.5min is mixed under the conditions of operating temperature is 124 DEG C;Later by sheep bar powder, glue easily element T-78 and
Compound antioxidant is added in mixing machine, keeps revolving speed and mixing temperature constant, is stirred 4.5min, must be mixed after mixing
Close material;
(3) mixed material the melting extrusion of mixing: is delivered to melting extrusion in extruder.
Embodiment 3
The present embodiment is related to a kind of wood plastic composite and preparation method thereof of high mallow stem hide fiber enhancing, this kind of composite wood
Material is made of following raw material according to parts by weight:
SG-564 parts of polyvinyl chloride resin powder;
40 parts of high mallow stem hide fiber;
6 parts of maleic anhydride grafted ABS resin;
11 parts of powder of calcium titanium tailing;
9 parts of villus powder;
2.5 parts of epoxy aliphatic acid methyl ester;
Glue easily T-781.5 parts of element;
2 parts of sheep bar powder;
3.2 parts of coupling agent of compounding;
1 part of compound antioxidant.
Maleic anhydride grafted ABS resin in the present embodiment, compounding coupling agent, compound antioxidant selection and produce such as following table
Shown in 3:
Table 3
The preparation method of wood plastic composite substantially follows the steps below in the present embodiment:
(1) it the modification of fiber: takes the cleaning of high mallow stem hide fiber to be chopped, after drying, is placed in steam blasting tank, in steam temperature
Heat-insulation pressure keeping under the conditions of degree is 111 DEG C, pressure is 0.6MPa carries out Steam explosion treatment 7min;It is again that high mallow stem skin in tank is short
Fiber takes out drying, is then added to soaking and stirring 11min in the NaOH solution that mass fraction is 9%;It is then that high mallow stem skin is short
Fiber is placed in soaking and stirring 26min in organic solvent, and it is stand-by to impregnate end taking-up cleaning, drying;
Above-mentioned organic solvent by it is following according to parts by weight at being grouped as: 4 parts of ethyl acetate, 1.5 parts of n-butanol, ethyl alcohol
1.5 parts, 1.5 parts of dimethyl sulfoxide, 2.5 parts of dimethylbenzene;
(2) polyvinyl chloride resin powder SG-5, modified high mallow stem hide fiber, maleic anhydride grafting the mixing of raw material: are taken
ABS resin and villus powder are added in mixing machine, under conditions of operating temperature is 160 DEG C, working speed is 700r/min
7min is mixed;Calcium titanium tailing powder, epoxy aliphatic acid methyl ester and compounding coupling agent are added in mixing machine again, kept
Revolving speed is constant, and 5min is mixed under the conditions of operating temperature is 125 DEG C;Later by sheep bar powder, glue easily element T-78 and compounding
Antioxidant is added in mixing machine, keeps revolving speed and mixing temperature constant, stirs 4min, and mixture is obtained after mixing
Material;
(3) mixed material the melting extrusion of mixing: is delivered to melting extrusion in extruder.
Embodiment 4
The present embodiment is related to a kind of wood plastic composite and preparation method thereof of high mallow stem hide fiber enhancing, this kind of composite wood
Material is made of following raw material according to parts by weight:
66 parts of polyvinyl chloride resin powder SG-5;
42 parts of high mallow stem hide fiber;
6.5 parts of maleic anhydride grafted ABS resin;
12 parts of powder of calcium titanium tailing;
9.5 parts of villus powder;
2.7 parts of epoxy aliphatic acid methyl ester;
Glue easily T-781.6 parts of element;
2.3 parts of sheep bar powder;
3.5 parts of coupling agent of compounding;
1.1 parts of compound antioxidant.
Maleic anhydride grafted ABS resin in the present embodiment, compounding coupling agent, compound antioxidant selection and produce such as following table
Shown in 4:
Table 4
The preparation method of wood plastic composite substantially follows the steps below in the present embodiment:
(1) it the modification of fiber: takes the cleaning of high mallow stem hide fiber to be chopped, after drying, is placed in steam blasting tank, in steam temperature
Heat-insulation pressure keeping under the conditions of degree is 112 DEG C, pressure is 0.65MPa carries out Steam explosion treatment 6.5min;Again by high mallow stem skin in tank
Staple fiber takes out drying, is then added to soaking and stirring 10.5min in the NaOH solution that mass fraction is 9.5%;Then by high mallow
Stem skin staple fiber is placed in soaking and stirring 27min in organic solvent, and it is stand-by to impregnate end taking-up cleaning, drying;
Above-mentioned organic solvent by it is following according to parts by weight at being grouped as: 4.5 parts of ethyl acetate, 1.8 parts of n-butanol, second
1.8 parts of alcohol, 1.8 parts of dimethyl sulfoxide, 2.7 parts of dimethylbenzene;
(2) polyvinyl chloride resin powder SG-5, modified high mallow stem hide fiber, maleic anhydride grafting the mixing of raw material: are taken
ABS resin and villus powder are added in mixing machine, under conditions of operating temperature is 162 DEG C, working speed is 750r/min
6.5min is mixed;Calcium titanium tailing powder, epoxy aliphatic acid methyl ester and compounding coupling agent are added in mixing machine again, protected
It is constant to hold revolving speed, 4.5min is mixed under the conditions of operating temperature is 128 DEG C;Later by sheep bar powder, glue easily element T-78 and
Compound antioxidant is added in mixing machine, keeps revolving speed and mixing temperature constant, is stirred 3.5min, must be mixed after mixing
Close material;
(3) mixed material the melting extrusion of mixing: is delivered to melting extrusion in extruder.
Embodiment 5
The present embodiment is related to a kind of wood plastic composite and preparation method thereof of high mallow stem hide fiber enhancing, this kind of composite wood
Material is made of following raw material according to parts by weight:
SG-572 parts of polyvinyl chloride resin powder;
45 parts of high mallow stem hide fiber;
7 parts of maleic anhydride grafted ABS resin;
13 parts of powder of calcium titanium tailing;
10 parts of villus powder;
3 parts of epoxy aliphatic acid methyl ester;
Glue easily T-782 parts of element;
2.5 parts of sheep bar powder;
4 parts of coupling agent of compounding;
1.2 parts of compound antioxidant.
Maleic anhydride grafted ABS resin in the present embodiment, compounding coupling agent, compound antioxidant selection and produce such as following table
Shown in 5:
Table 5
The preparation method of wood plastic composite substantially follows the steps below in the present embodiment:
(1) it the modification of fiber: takes the cleaning of high mallow stem hide fiber to be chopped, after drying, is placed in steam blasting tank, in steam temperature
Heat-insulation pressure keeping under the conditions of degree is 114 DEG C, pressure is 0.7MPa carries out Steam explosion treatment 6min;It is again that high mallow stem skin in tank is short
Fiber takes out drying, is then added to soaking and stirring 10min in the NaOH solution that mass fraction is 10%;It is then that high mallow stem skin is short
Fiber is placed in soaking and stirring 28min in organic solvent, and it is stand-by to impregnate end taking-up cleaning, drying;
Above-mentioned organic solvent by it is following according to parts by weight at being grouped as: 5 parts of ethyl acetate, 2 parts of n-butanol, ethyl alcohol 2
Part, 2 parts of dimethyl sulfoxide, 3 parts of dimethylbenzene;
(2) polyvinyl chloride resin powder SG-5, modified high mallow stem hide fiber, maleic anhydride grafting the mixing of raw material: are taken
ABS resin and villus powder are added in mixing machine, under conditions of operating temperature is 165 DEG C, working speed is 800r/min
6min is mixed;Calcium titanium tailing powder, epoxy aliphatic acid methyl ester and compounding coupling agent are added in mixing machine again, kept
Revolving speed is constant, and 4min is mixed under the conditions of operating temperature is 130 DEG C;Later by sheep bar powder, glue easily element T-78 and compounding
Antioxidant is added in mixing machine, keeps revolving speed and mixing temperature constant, stirs 3min, and mixture is obtained after mixing
Material;
(3) mixed material the melting extrusion of mixing: is delivered to melting extrusion in extruder.
Comparative example group
"-" indicates that the reduction of certain ingredient in embodiment uses in the following table 6;
Table 6
Comparative example 8
This comparative example is related to a kind of wood plastic composite, relative to above-described embodiment 2, there is only compounding coupling agent at
Divide difference;
The ingredient of this comparative example coupling agent are as follows: titanate coupling agent 201.
Comparative example 9
This comparative example is related to a kind of wood plastic composite, relative to above-described embodiment 3, there is only compounding coupling agent at
Divide difference;
The ingredient of this comparative example compounding coupling agent are as follows: two kinds of titanate coupling agent 201, rare-earth coupling agent ingredients are according to quality
Merge to obtain than 3:1.
Comparative example 10
This comparative example is related to a kind of wood plastic composite, and relative to above-described embodiment 4, there is only each in compounding coupling agent
The mass ratio of ingredient is different;
This comparative example compounds the mass ratio of each ingredient in coupling agent are as follows: compounding coupling agent is tin coupled SSBR, titanate esters idol
Three kinds of connection agent 201, rare-earth coupling agent ingredients merge to obtain according to mass ratio 1:1:1.
Comparative example 11
This comparative example is related to a kind of wood plastic composite, and relative to above-described embodiment 5, there is only wood plastic composites
Preparation method is different;
This comparative example wood plastic composite the preparation method is as follows:
(1) fiber is chopped: take the cleaning of high mallow stem hide fiber to be chopped, it is stand-by after drying;
(2) mixing of raw material: high mallow stem hide fiber, maleic anhydride grafting after taking polyvinyl chloride resin powder SG-5, being chopped
ABS resin and villus powder are added in mixing machine, under conditions of operating temperature is 165 DEG C, working speed is 800r/min
6min is mixed;Calcium titanium tailing powder, epoxy aliphatic acid methyl ester and compounding coupling agent are added in mixing machine again, kept
Revolving speed is constant, and 4min is mixed under the conditions of operating temperature is 130 DEG C;Later by sheep bar powder, glue easily element T-78 and compounding
Antioxidant is added in mixing machine, keeps revolving speed and mixing temperature constant, stirs 3min, and mixture is obtained after mixing
Material;
(3) mixed material the melting extrusion of mixing: is delivered to melting extrusion in extruder.
Comparative example 12
This comparative example is related to a kind of wood plastic composite, and relative to above-described embodiment 5, there is only wood plastic composites
Preparation method is different;
(1) it the modification of fiber: takes the cleaning of high mallow stem hide fiber to be chopped, after drying, is placed in steam blasting tank, in steam temperature
Heat-insulation pressure keeping under the conditions of degree is 114 DEG C, pressure is 0.7MPa carries out Steam explosion treatment 6min;It is again that high mallow stem skin in tank is short
Fiber takes out drying, is then added to soaking and stirring 10min in the NaOH solution that mass fraction is 10%;It is then that high mallow stem skin is short
Fiber is placed in soaking and stirring 28min in organic solvent, and it is stand-by to impregnate end taking-up cleaning, drying;
Above-mentioned organic solvent by it is following according to parts by weight at being grouped as: 5 parts of ethyl acetate, 2 parts of n-butanol, ethyl alcohol 2
Part, 2 parts of dimethyl sulfoxide, 3 parts of dimethylbenzene;
(2) mixing of raw material: all raw materials are delivered in mixing machine jointly, are 160 DEG C, working speed in operating temperature
For 12min is mixed under conditions of 800r/min, mixing terminates to obtain mixed material;
(3) mixed material the melting extrusion of mixing: is delivered to melting extrusion in extruder.
Comparative example 13
This comparative example is related to a kind of wood plastic composite, by weight, is mixed by following components: polyvinyl chloride resin
50-75 parts, 16-20 parts of wood powder, 20-30 parts of light calcium carbonate powder, 6-8 parts of modification biological charcoal, 1.3-1.5 parts of calcium zinc stabilizer, chlorination is poly-
0.8-1 parts of ethylene, 0.3-0.5 parts of polyethylene wax, 0.5-0.8 parts of stearic acid, 1.0-1.5 parts of plasticizer, ACR processing aid 1.9-
2.4 parts, 5-8 parts of feed back.
Performance detection
For the beneficial effect for verifying the present invention, wood and plastic composite obtained in above-described embodiment 1-5 and comparative example 1-13 is taken
The template material (having a size of 150 × 50 × 6mm) of material carries out the performance detection such as the following table 7, tensile strength, bending elastic modulus, punching
Toughness, expansion rate of water absorption, the detection method of water absorption rate and standard are hit referring in particular to building material industry standard " DB44T349-2006 wood
Plastic composite materials technical conditions " in content.(the template material of embodiment 1-5 is indicated using #1-#5 in following table, comparative example 1-13
Template material using &1-&13 indicate)
Table 7:
Remarks:
1) detection of electromagnet shield effect is carried out on flange shaft tester, test frequency be respectively 1000kHz,
1.5GHz;
2) detection of wet and heat ageing resistant is carried out in hydrothermal aging chamber, and detection temperature is 60 DEG C, humidity
90%RH or more, testing time 168h see whether the bad phenomenons such as cracking, bubbling, geomery variation occur.
Wood plastic composite of the invention is worthy of careful study in raw materials for production selection it can be seen from upper table 7, between raw material
The synergistic effect that assembles make wood plastic composite obtained in the side such as mechanical strength, waterproofness, resistance to oxidation aging and shielding
It is promoted significantly on face, improves the overall performance of wood plastic composite, improve application performance, service life is more secure, tool
There is good promotional value.
In conjunction with the beneficial effect of the present invention, applicant illustrates constituent part and preparation method of the invention as follows:
(1) modification of plant fiber: by having carried out Steam explosion treatment to the high mallow stem hide fiber after being chopped,
The effective loose institutional framework of stem hide fiber, especially improves the institutional framework of amorphous region, eliminates intrastitial fruit
The impurity components such as glue, and the supramolecular structure in cellulose is destroyed, the modified effect of subsequent alkali bubble, elution is enhanced, more
Conducive to the reservation of fibrous mechanical property;Then fiber is put into immersion treatment in lye, can further dissolved in wooden
The low molecules impurity such as part pectin, lignin and hemicellulose, does not change the chemical structure of main fibre element, and rotates fiber
Angle reduces, and molecularly oriented improves, to improve the breaking strength etc. of fiber, above-mentioned alkali cleaning can convenient for subsequent operation it is smooth into
Row;Fiber is put into immersion treatment in organic solvent later, selective wax elution is on the one hand carried out, on the other hand improves wood
Caking property between matter part and polymeric matrix improves the service performance of high mallow stem hide fiber.If in operation at steam blasting
The change of the technological parameter, the type and mass concentration of lye and organic solvent of reason, the modified effect that will lead to fiber have change,
It is unfavorable for the fine realization of beneficial effect of the present invention.
(2) compound coupling agent: the common coupling agent of wood plastic composite has silane series coupling agent, titanate coupling agent, aluminium
Acid esters coupling agent is used to merge organic polymer and inorganic filler reaction, find after many experiments, produces in many coupling agents
The effect that titanate coupling agent 201 generates in being applied to the present invention in product is best, but expected requirement is not achieved, because
This, the coupling agent that applicant attempts to add other ingredients merges with it using and then come reach the purpose of the present invention, herein basis
On, applicant finally surprisingly obtains by three kinds of tin coupled SSBR, titanate coupling agent 201, rare-earth coupling agent ingredients according to matter
Measure than (2-4): (4-8): (1-3) merges obtained compounding coupling agent, and it is very prominent that this kind compounds the beneficial effect that coupling agent obtains
Out, considerably beyond other types and the coupling agent assembled, it can efficiently high mallow stem hide fiber, calcium titanium tail in adhesion promotion raw material
The ingredients such as miberal powder material, villus powder are filled into polymeric matrix, and are improved the physical property of above-mentioned filler and improved protection
The ability that material interface is damaged from environmental stress.If compounding the ingredient of coupling agent or/and the change of content in the present invention,
Will lead to beneficial effects of the present invention cannot realize well.
(3) compound antioxidant: obtaining through applicant's many experiments, antioxidant 1076, antioxidant 1010, antioxidant DSTP
The synergistic effect of three kinds of ingredients can effectively prevent the progress of wood plastic composite chain reaction of the present invention, with excellent smelly
Oxygen cracking and flex crack protective, can preferably promote the environmental stress resistance of wood plastic composite of the present invention, when above-mentioned antioxygen
Ingredient and used time, it not only can be reduced the dosage of antioxidant but also protection effect can be improved, and played respective antioxygen and prevent old advantage, it can be significant
Improve the service life of wood plastic composite;If the change of the ingredient of compound antioxidant or/and content in the present invention, can lead
Cause beneficial effects of the present invention that cannot realize well.
Certainly, because of the requirement of the mentality of designing and goal of the invention of wood plastic composite of the present invention, remaining component of the invention
Selection and content selection are obviously also non-obvious, and those skilled in the art combine the prior art that can think easily absolutely not
It arrives.This has further embodiment in the preparation method of wood plastic composite of the present invention, can see in conjunction with the embodiment of the present invention
It arrives, preparation method of the invention is designed using three steps, and raw material is added in mixing process by several times in batches, and step is simple and has
Sequence, rather than use the prior art is conventional to be added at one time (such as comparative example 12), this technique is and wood plastics composite of the present invention
What the special proportion of material raw materials for production component was adapted, this technique is only used, just can guarantee that wood plastic composite reacts
The smooth sequential of system carries out, and ensures the wood plastic composite excellent characteristics finally prepared.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, although referring to aforementioned reality
Applying example, invention is explained in detail, for those skilled in the art, still can be to aforementioned each implementation
Technical solution documented by example is modified or equivalent replacement of some of the technical features.It is all in essence of the invention
Within mind and principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (10)
1. a kind of wood plastic composite of high mallow stem hide fiber enhancing, which is characterized in that by following raw material according to parts by weight
Composition:
56-66 parts of polyvinyl chloride resin powder SG-5;
35-42 parts of high mallow stem hide fiber;
5-6.5 parts of maleic anhydride grafted ABS resin;
9-12 parts of tailing powder of calcium titanium;
8-9.5 parts of villus powder;
2-2.7 parts of epoxy aliphatic acid methyl ester;
Easily 1-1.6 parts of T-78 of element of glue;
1.5-2.3 parts of sheep bar powder;
Coupling agent 2.5-3.5 parts of compounding;
0.8-1.1 parts of compound antioxidant.
2. a kind of wood plastic composite of high mallow stem hide fiber enhancing according to claim 1, which is characterized in that by following
Raw material composition according to parts by weight:
SG-556 parts of polyvinyl chloride resin powder;
35 parts of high mallow stem hide fiber;
5 parts of maleic anhydride grafted ABS resin;
9 parts of powder of calcium titanium tailing;
8 parts of villus powder;
2 parts of epoxy aliphatic acid methyl ester;
Easily 1 part of T-78 of element of glue;
1.5 parts of sheep bar powder;
2.5 parts of coupling agent of compounding;
0.8 part of compound antioxidant;
The maleic anhydride grafted ABS resin is made of the maleic anhydride grafted ABS of two breeds of horses, the first maleic anhydride grafted ABS is molten
Melting index is 2g/10min, grafting rate 1.25%;Second of maleic anhydride grafted ABS melt index is 1g/10min, grafting
Rate is 6.50%;And the mass ratio of the first maleic anhydride grafted ABS with second is 2:1.
3. a kind of wood plastic composite of high mallow stem hide fiber enhancing according to claim 2, which is characterized in that described multiple
It is tin coupled SSBR with coupling agent, three kinds of titanate coupling agent 201, rare-earth coupling agent ingredients merge according to mass ratio 2:4:1
It arrives.
4. a kind of wood plastic composite of high mallow stem hide fiber enhancing according to claim 3, which is characterized in that described multiple
With antioxidant be antioxidant 1076, tri- kinds of antioxidant 1010, antioxidant DSTP ingredients merge according to mass ratio 4:3:2.
5. a kind of wood plastic composite of high mallow stem hide fiber enhancing according to claim 4, which is characterized in that described multiple
Condensation material the preparation method is as follows:
(1) it the modification of fiber: takes the cleaning of high mallow stem hide fiber to be chopped, after drying, is placed in steam blasting tank, is in vapor (steam) temperature
108 DEG C, pressure be 0.5MPa under the conditions of heat-insulation pressure keeping, carry out Steam explosion treatment 8min;Again by high mallow stem skin staple fiber in tank
Drying is taken out, soaking and stirring 12min in the NaOH solution that mass fraction is 8% is then added to;Then by high mallow stem skin staple fiber
It is placed in soaking and stirring 24min in organic solvent, it is stand-by to impregnate end taking-up cleaning, drying;
The organic solvent by it is following according to parts by weight at being grouped as: 3 parts of ethyl acetate, 1 part of n-butanol, 1 part of ethyl alcohol, two
1 part of methyl sulfoxide, 2 parts of dimethylbenzene;
(2) polyvinyl chloride resin powder SG-5, modified high mallow stem hide fiber, maleic anhydride grafted ABS tree the mixing of raw material: are taken
Rouge and villus powder are added in mixing machine, are mixed and are stirred under conditions of operating temperature is 155 DEG C, working speed is 600r/min
Mix 8min;Calcium titanium tailing powder, epoxy aliphatic acid methyl ester and compounding coupling agent are added in mixing machine again, keep revolving speed not
Become, 6min is mixed under the conditions of operating temperature is 120 DEG C;Later by sheep bar powder, glue easily element T-78 and compound antioxidant
It is added in mixing machine, keeps revolving speed and mixing temperature constant, stir 5min, mixed material is obtained after mixing;
(3) mixed material the melting extrusion of mixing: is delivered to melting extrusion in extruder.
6. a kind of wood plastic composite of high mallow stem hide fiber enhancing according to claim 1, which is characterized in that by following
Raw material composition according to parts by weight:
66 parts of polyvinyl chloride resin powder SG-5;
42 parts of high mallow stem hide fiber;
6.5 parts of maleic anhydride grafted ABS resin;
12 parts of powder of calcium titanium tailing;
9.5 parts of villus powder;
2.7 parts of epoxy aliphatic acid methyl ester;
Easily 1.6 parts of T-78 of element of glue;
2.3 parts of sheep bar powder;
3.5 parts of coupling agent of compounding;
1.1 parts of compound antioxidant;
The maleic anhydride grafted ABS resin is made of the maleic anhydride grafted ABS of two breeds of horses, the first maleic anhydride grafted ABS is molten
Melting index is 3.5g/10min, grafting rate 1.40%;Second of maleic anhydride grafted ABS melt index is 2.5g/10min,
Grafting rate is 7.20%;And the mass ratio of the first maleic anhydride grafted ABS with second is 2.7:1.8.
7. a kind of wood plastic composite of high mallow stem hide fiber enhancing according to claim 6, which is characterized in that described multiple
It is three kinds of tin coupled SSBR, titanate coupling agent 201, rare-earth coupling agent ingredients according to mass ratio 3.5:7:2.5 conjunction with coupling agent
And obtain.
8. a kind of wood plastic composite of high mallow stem hide fiber enhancing according to claim 7, which is characterized in that described multiple
It is antioxidant 1076 with antioxidant, tri- kinds of antioxidant 1010, antioxidant DSTP ingredients merge according to mass ratio 5.5:4.5:3.5
It arrives.
9. a kind of wood plastic composite of high mallow stem hide fiber enhancing according to claim 8, which is characterized in that described multiple
Condensation material the preparation method is as follows:
(1) it the modification of fiber: takes the cleaning of high mallow stem hide fiber to be chopped, after drying, is placed in steam blasting tank, is in vapor (steam) temperature
112 DEG C, pressure be 0.65MPa under the conditions of heat-insulation pressure keeping, carry out Steam explosion treatment 6.5min;Again by the short fibre of high mallow stem skin in tank
Dimension takes out drying, is then added to soaking and stirring 10.5min in the NaOH solution that mass fraction is 9.5%;Then by high mallow stem skin
Staple fiber is placed in soaking and stirring 27min in organic solvent, and it is stand-by to impregnate end taking-up cleaning, drying;
The organic solvent by it is following according to parts by weight at being grouped as: 4.5 parts of ethyl acetate, 1.8 parts of n-butanol, ethyl alcohol
1.8 parts, 1.8 parts of dimethyl sulfoxide, 2.7 parts of dimethylbenzene;
(2) polyvinyl chloride resin powder SG-5, modified high mallow stem hide fiber, maleic anhydride grafted ABS tree the mixing of raw material: are taken
Rouge and villus powder are added in mixing machine, are mixed and are stirred under conditions of operating temperature is 162 DEG C, working speed is 750r/min
Mix 6.5min;Calcium titanium tailing powder, epoxy aliphatic acid methyl ester and compounding coupling agent are added in mixing machine again, keep revolving speed
It is constant, 4.5min is mixed under the conditions of operating temperature is 128 DEG C;It is later that sheep bar powder, glue easily element T-78 and compounding is anti-
Oxygen agent is added in mixing machine, keeps revolving speed and mixing temperature constant, stirs 3.5min, and mixture is obtained after mixing
Material;
(3) mixed material the melting extrusion of mixing: is delivered to melting extrusion in extruder.
10. a kind of wood plastic composite of the high mallow stem hide fiber enhancing as described in any in claim 1-9 is in building, garden
Woods, packaging, shipping vehicle, toy, sport, the application in farm implements field.