CN109049924A - A kind of high insulation shielding band and preparation method thereof - Google Patents
A kind of high insulation shielding band and preparation method thereof Download PDFInfo
- Publication number
- CN109049924A CN109049924A CN201810928910.4A CN201810928910A CN109049924A CN 109049924 A CN109049924 A CN 109049924A CN 201810928910 A CN201810928910 A CN 201810928910A CN 109049924 A CN109049924 A CN 109049924A
- Authority
- CN
- China
- Prior art keywords
- insulation shielding
- preparation
- shielding band
- cloth
- high insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of high insulation shielding bands, are made of upper-layer functionality complex fabric cloth, middle layer conductive black colloid layer and lower layer's function and service fiber cloth.The present invention also provides the preparation methods of the high insulation shielding band, select high resiliency empire cloth made of function and service fiber, make high viscosity conduction compound binding agent with polymerization technique, are made using clipping dry-lamination process and vacuum drying.The high insulation shielding band tool surface insulation, inner conductive shielding, heat-resisting, light specific gravity, softness, it is easy to be wrapped, environmentally friendly the features such as, be widely used.
Description
Technical field
The present invention relates to a kind of high insulation shielding bands and preparation method thereof, belong to cable material field.
Background technique
In the structural detail of cable, the belt wrapping layer of different materials and structure is the important component of the construction of cable
One of.In rubber and cable in plastics cable, the major function of belt wrapping layer is: (1) it is all to increase insulated wire cores mechanical strength
The rubber insulation core of discontinuous vulcanization, the especially insulated wire cores of longitudinal wrap method, wrapped rubberized tape to enhance its mechanical strength,
It prevents from that insulation pressure occurs partially during transport, after-combustion and when sulfurizing pot vulcanization, scratch;Rubber insulation cold working longitudinal wrap method
, it is easy to produce to roll to stitch and split and the defect in the quality such as delamination.Certain improvement can be obtained after wrapped rubberized tape.(2) stranding
Band, when multicore cable stranding, many constructions of cable require the gap between core to be filled with fiber and other material, then wrap with
Rubberized tape, paper tape, nonwoven fabric belts, mylar tape, polypropylene film band, fiberglass cloth tape, polyethylene and polychlorostyrene second
Alkene band.It is provided according to product standard, the belt that technological operation performance should be selected good requires belt high mechanical strength, not mutually
Sliding.Stranding becomes solid circle entirety, processes convenient for lower process after band tightens.(3) centering of shielded layer band,
The insulated wire cores of high voltage power cable, for the return conductors for improving field distribution and when as short circuit, usually first in insulated wire
One layer of semiconducting rubber or plastics are extruded on core, further around one layer of copper strips of packet.The wrapped semiconducting fibers band conduct of some product requirements
Shielded layer.Communication, control, instrument and cable for electronic computer, often require around copper-clad/polyester or aluminium/polyester composite band.
Therefore, in cable factory, it can be seen that the belting machine and lapping head of all styles of pattern.
And being exclusively used in cable shield performance band is copper strips, aluminium strip and extremely least a portion of lead sheath, they all have excellent
Shielding properties and good electric conductivity more, but the disadvantage is that because of surface naked protective layer, in the case where cable is damaged rupture event,
Band easily conductive in the case where contacting power conditions, electric shock, electric leakage are shielded, especially no metal ingredient is being required to do conductor and shielding
In the special cable of layer, the underground cable of metal ingredient can not be measured with good shielding properties and metal detector, at present
Other metal materials can not have above-mentioned function.
Summary of the invention
The technical issues of in order to solve in the prior art, the present invention provides a kind of surface insulation, internal layers to have conducting screen
It covers, the heat resistant type band of non-metallic composition, there is surface insulation, inner conductive shielding, heat-resisting, light specific gravity, softness, easily wrapped
Feature.
The present invention provides a kind of high insulation shielding band, upper layer is function and service fiber cloth (1), and middle layer is conductive charcoal
Black glue body (2), lower layer are function and service fiber cloth (3), see Fig. 1.
The present invention also provides the preparation methods of the high insulation shielding band, which is characterized in that preparation method includes
Following steps:
1) high resiliency empire cloth made of function and service fiber is selected;
2) high viscosity conduction compound binding agent is made with polymerization technique: mainly using conductive nano hollow carbon nanometer
Pipe and aqueous acrylic emulsion, and crosslinking agent, dispersing agent and water is added, under room temperature, condition of high voltage, high-speed stirred is to get viscous
Tie agent;
3) high speed and dry compounding machine and foamed and sprayed gluing paint-on technique are used, high resiliency empire cloth is answered with binder
It closes;
4) vacuum drying.
Further, in the step 1) in high resiliency empire cloth, warp thread selects polyester filament 50-150dtex, density
30-40 root/cm, weft yarn select in alkali or alkali-free, 45 two strands or 21-33 branch sub-thread silks, density 10-20 root/cm.
Further, the composition and percentage of binder are made in the step 2) are as follows:
Further, step 3) the high speed dry compound machine oven temperature is set as 70-120 DEG C, and the speed of service is
100 ms/min of <, coated with adhesive content is 20-30g/m2。
The present invention also provides the high insulation shielding bands to prepare the application in cable internal layer twining package tape.
The technical effect that the present invention reaches:
1. by high insulation shielding band made from present invention process, grammes per square metre < 300g/m2;Tensile strength > 200N/
Cm, elongation > 20%, heat resistance is strong, and 180 DEG C of long-term work, at 200 DEG C, 5 minutes contraction < 5%;The resistance to class of insulation is
2kV, surface does not puncture within 3 minutes;Sheet resistance < 100 Ω, volume resistance the < 1*10 of intermediate conductive layer2, meet ROHS standard.
2. the high insulation shielding band obtained using preparation process of the invention, can be widely used in extra-high-tension cable, height
The wrapped shielding of mine cable internal layer is pressed, the more unique cable applied to non-metal conductor manufacture has and shields, is anti-radiation, anti-
The special cable of the requirements such as ultraviolet light.Such as: military fiber optic cable (metal detector can not detect) can be made, be used for military underground work
Thing blindage, for the outer protection protection such as oil storage pipeline, feed channel, thunder-lightning.
Detailed description of the invention
Fig. 1 high insulation shielding band Structure of cross section schematic diagram wherein 1 be function and service fiber cloth, 2 be conductive black glue
Body, 3 be function and service fiber cloth.
Specific embodiment
Below in conjunction with specific embodiment, the present invention will be further described.It should be understood that following embodiment is merely to illustrate this
Invention is not for limiting the scope of the invention.
The preparation method of the high insulation shielding band of embodiment 1
1) high resiliency empire cloth made of function and service fiber is selected;Warp thread selects polyester filament 50-150dtex, density
30-40 root/cm, weft yarn select in alkali or alkali-free, 45 two strands or 21-33 branch sub-thread silks, density 10-20 root/cm.
2) high viscosity conduction compound binding agent is made with polymerization technique: mainly using conductive nano hollow carbon nanometer
Pipe and aqueous acrylic emulsion, and crosslinking agent, dispersing agent and water is added, under room temperature, condition of high voltage, high-speed stirred is to get viscous
Tie agent;The composition and percentage of binder are as follows: acrylic acid 30%, hollow carbon nanotube 10%, crosslinking agent formaldehyde 3%, water 50%,
Dispersing agent 7%.
3) high speed and dry compounding machine and foamed and sprayed gluing paint-on technique are used, high resiliency empire cloth is answered with binder
It closes;High speed and dry compounding machine oven temperature is set as 70-120 DEG C, and the speed of service is < 100 ms/min, and coated with adhesive content is
20-30g/m2
4) vacuum drying.
The preparation method of the high insulation shielding band of embodiment 2
1) high resiliency empire cloth made of function and service fiber is selected;Warp thread selects polyester filament 50-150dtex, density
30-40 root/cm, weft yarn select in alkali or alkali-free, 45 two strands or 21-33 branch sub-thread silks, density 10-20 root/cm.
2) high viscosity conduction compound binding agent is made with polymerization technique: mainly using conductive nano hollow carbon nanometer
Pipe and aqueous acrylic emulsion, and crosslinking agent, dispersing agent and water is added, under room temperature, condition of high voltage, high-speed stirred is to get viscous
Tie agent;The composition and percentage of binder is made are as follows: acrylic acid 30%, hollow carbon nanotube 10%, crosslinking agent formaldehyde 3%, water
52%, dispersing agent 5%.
3) high speed and dry compounding machine and foamed and sprayed gluing paint-on technique are used, high resiliency empire cloth is answered with binder
It closes;High speed and dry compounding machine oven temperature is set as 70-120 DEG C, and the speed of service is < 100 ms/min, and coated with adhesive content is
20-30g/m2
4) vacuum drying.
The preparation method of the high insulation shielding band of embodiment 3
1) high resiliency empire cloth made of function and service fiber is selected;Warp thread selects polyester filament 50-150dtex, density
30-40 root/cm, weft yarn select in alkali or alkali-free, 45 two strands or 21-33 branch sub-thread silks, density 10-20 root/cm.
2) high viscosity conduction compound binding agent is made with polymerization technique: mainly using conductive nano hollow carbon nanometer
Pipe and aqueous acrylic emulsion, and crosslinking agent, dispersing agent and water is added, under room temperature, condition of high voltage, high-speed stirred is to get viscous
Tie agent;The composition and percentage of binder are as follows: acrylic acid 30%, hollow carbon nanotube 12%, crosslinking agent formaldehyde 3%, water 50%,
Dispersing agent 5%.
3) high speed and dry compounding machine and foamed and sprayed gluing paint-on technique are used, high resiliency empire cloth is answered with binder
It closes;High speed and dry compounding machine oven temperature is set as 80 DEG C, and the speed of service is < 100 ms/min, and coated with adhesive content is 28g/
m2
4) vacuum drying.
The preparation method of the high insulation shielding band of embodiment 4
1) high resiliency empire cloth made of function and service fiber is selected;Warp thread selects polyester filament 50-150dtex, density
30-40 root/cm, weft yarn select in alkali or alkali-free, 45 two strands or 21-33 branch sub-thread silks, density 10-20 root/cm.
2) high viscosity conduction compound binding agent is made with polymerization technique: mainly using conductive nano hollow carbon nanometer
Pipe and aqueous acrylic emulsion, and crosslinking agent, dispersing agent and water is added, under room temperature, condition of high voltage, high-speed stirred is to get viscous
Tie agent;The composition and percentage of binder are as follows: acrylic acid 32%, hollow carbon nanotube 10%, crosslinking agent formaldehyde 3%, water 50%,
Dispersing agent 5%.
3) high speed and dry compounding machine and foamed and sprayed gluing paint-on technique are used, high resiliency empire cloth is answered with binder
It closes;High speed and dry compounding machine oven temperature is set as 80 DEG C, and the speed of service is < 100 ms/min, and coated with adhesive content is 28g/
m2
4) vacuum drying.
Effect example
High insulation shielding band obtained, grammes per square metre < 300g/m are prepared by 1-4 of the embodiment of the present invention2;Tensile strength
> 200N/cm, elongation > 20%, heat resistance is strong, and 180 DEG C of long-term work, at 200 DEG C, 5 minutes contraction < 5%;Resistance to insulation
Grade is 2kV, and surface does not puncture within 3 minutes;Sheet resistance < 100 Ω, volume resistance the < 1*10 of intermediate conductive layer2, meet
ROHS standard.
The foregoing is merely presently preferred embodiments of the present invention, is not intended to limit the invention, it is all in spirit of the invention and
Within principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (6)
1. a kind of high insulation shielding band, which is characterized in that upper and lower layer is function and service fiber cloth, and middle layer is conductive black
Colloid.
2. the preparation method of high insulation shielding band described in claim 1, which comprises the following steps:
1) high resiliency empire cloth made of function and service fiber is selected;
2) with polymerization technique make high viscosity conduction compound binding agent: using the hollow carbon nanotube of conductive nano with it is aqueous
Acrylic emulsion, and crosslinking agent, dispersing agent and water is added, under room temperature, condition of high voltage, high-speed stirred is to get binder;
3) high speed and dry compounding machine and foamed and sprayed gluing paint-on technique are used, high resiliency empire cloth and binder is compound;
4) vacuum drying.
3. preparation method according to claim 2, which is characterized in that in the step 1) in high resiliency empire cloth, warp thread
Select polyester filament 50-150dtex, density 30-40 root/cm, weft yarn select in alkali or alkali-free, 45 two strands or 21-33 branch list
Stock silk, density 10-20 root/cm.
4. preparation method according to claim 2, which is characterized in that the composition and hundred of binder is made in the step 2)
Divide ratio are as follows:
5. preparation method according to claim 2, which is characterized in that step 3) the high speed dry compound machine baking oven temperature
Degree is 70-120 DEG C, and the speed of service is < 100 ms/min, and coated with adhesive content is 20-30g/m2。
6. high insulation shielding band made from -5 either method of claim 1 or claim 2 is preparing cable internal layer twining package tape
In application.