CN109049907A - Food packaging plastic sheet/PE film composite material and preparation method - Google Patents
Food packaging plastic sheet/PE film composite material and preparation method Download PDFInfo
- Publication number
- CN109049907A CN109049907A CN201810685807.1A CN201810685807A CN109049907A CN 109049907 A CN109049907 A CN 109049907A CN 201810685807 A CN201810685807 A CN 201810685807A CN 109049907 A CN109049907 A CN 109049907A
- Authority
- CN
- China
- Prior art keywords
- plastic sheet
- film
- sheet material
- monolayer
- composite material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention discloses a kind of food packaging plastic sheet/PE film composite material, has monolayer plastic sheet material, the monolayer plastic sheet material is directly compound with PE film, and the thickness of PE film is at least 0.03mm.Preparation method successively carries out in accordance with the following steps: PE film roll cylinder being placed in double pressing ends of i.e. painting type laminating machine, monolayer plastic sheet material reel drum is placed in the gluing end of i.e. painting type laminating machine;Monolayer plastic sheet material passes through lick roller kiss-coating;Monolayer plastic sheet material after kiss-coating enters drying box, is dried surface glue with 30 ~ 40 DEG C;The monolayer plastic sheet material of drying is sent to double pressing ends and PE film and is bonded;Winding.Operation of the present invention is simple, due to, without PP and EVOH, therefore greatly reducing product cost (50% or more), and improve transparent plastic sheet material transparency and product surface glossiness in composite material.
Description
Technical field
The present invention relates to a kind of food packaging material, especially a kind of easy to operate, low cost, product surface gloss beauty
Food packaging plastic sheet/PE the film composite material and preparation method seen.
Background technique
Currently, the inner surface for being applied to the food package boxes such as fresh meat controlled atmospheric packing, aquatic products and vacuum stretching box is PE film,
Production method is formed into after the composite material for being covered with PE film and box body is made by inhaling vacuum forming, and composite material therein can be used
I.e. painting type laminating machine is completed.That is the technique of painting type laminating machine mainly unreels, glue be coated and dried, be compound, winding etc., i.e., will
Plastic film reel is placed in the gluing end of i.e. painting type laminating machine, and monolayer plastic sheet material (PET, PP or PS etc.) reel is placed in and is applied
Then plastic film is entered back into drying box, by lick roller kiss-coating with 70 DEG C or so of temperature by double pressing ends of type laminating machine
Plastic film surface glue is dried, then the plastic film of drying is sent to double pressing ends and plastic sheet and is bonded, winding.
Low Temperature Thermal sealer since PE film is very thin, such as by kiss-coating, drying and etc. and it is directly compound with plastic sheet, i.e.,
So that drying box temperature is down to 20 DEG C, PE film also will appear cross-direction shrinkage, longitudinal extensional and can not entirely overlay on plastic sheet
Material surface.Therefore existing preparation method is first will to pass through multi-layer co-extruded formation PP/EVOH/PE composite plastic containing PE, PP and EVOH
Expect film, is then again overlayed on PP/EVOH/PE composite membrane on plastic sheet by being painting type laminating machine, so that PE film position
In the inner surface of packing box.The PP/EVOH/PE composite plastic film existing market price of high price is that (32600 yuan/ton) directly mention
The cost of packing box material is risen, and reduces transparent plastic sheet material transparency and product surface glossiness.
Summary of the invention
The present invention be in order to solve above-mentioned technical problem present in the prior art, provide a kind of easy to operate, low cost,
Food packaging plastic sheet/PE the film composite material and preparation method of product surface gloss beauty.
The technical solution of the invention is as follows: a kind of food packaging plastic sheet/PE film composite material has monolayer plastic
Sheet material, the monolayer plastic sheet material is directly compound with PE film, and the thickness of the PE film is at least 0.03mm.
The monolayer plastic sheet material is PET, PP or PS.
A kind of preparation method of above-mentioned food packaging plastic sheet/PE composite material, it is characterised in that successively according to such as
Lower step carries out:
A., PE film roll cylinder is placed in double pressing ends of i.e. painting type laminating machine, monolayer plastic sheet material reel drum is placed in i.e. painting type overlay film
The gluing end of machine;
B. monolayer plastic sheet material passes through lick roller kiss-coating;
C. the monolayer plastic sheet material after kiss-coating enters drying box, is dried surface glue with 30 ~ 40 DEG C;
D. the monolayer plastic sheet material of drying is sent to double pressing ends and PE film and is bonded;
E. it winds.
The present invention has overturned the preparation method that conventional plastic sheet material covers PE film, and PE film roll cylinder is placed in double pressures of i.e. painting type laminating machine
End is closed, plastic sheet reel is placed in the gluing end of i.e. painting type laminating machine, and by adjusting the temperature of dryer (30 ~ 40 DEG C),
So that the PE film of price lower (15000 yuan/ton) directly can entirely overlay on monolayer plastic sheet material, food package box use is made
Composite material, it is easy to operate.Due to, without PP and EVOH, therefore greatly reducing product cost, and improve transparent in composite material
Plastic sheet transparency and product surface glossiness.
Detailed description of the invention
Fig. 1 is the food packaging plastic sheet of the embodiment of the present invention/PE film composite material sectional view.
Specific embodiment
Embodiment 1:
Food packaging plastic sheet/PE composite material preparation method of the invention successively carries out in accordance with the following steps:
A. it will be placed in double pressing ends of existing i.e. painting type laminating machine with a thickness of the PE film roll cylinder of 0.03mm, single-layer PET sheet material is rolled up
Cylinder is placed in the gluing end of i.e. painting type laminating machine;
B. single-layer PET sheet material passes through lick roller kiss-coating;
C. the single-layer PET sheet material after kiss-coating enters drying box, and adjustment drying box temperature is 30 DEG C, by surface drying adhesive;
D. the single-layer PET sheet material of drying is sent to double pressing ends and PE film and is bonded;
E. it winds.
Composite material as shown in Figure 1 is made, i.e. monolayer plastic sheet material 1 is directly compound with PE film 2.
Embodiment 2:
Food packaging plastic sheet/PE composite material preparation method of the invention successively carries out in accordance with the following steps:
A. it will be placed in double pressing ends of existing i.e. painting type laminating machine with a thickness of the PE film roll cylinder of 0.035mm, single layer PP sheet material is rolled up
Cylinder is placed in the gluing end of i.e. painting type laminating machine;
B. single layer PP sheet material passes through lick roller kiss-coating;
C. the single layer PP sheet material after kiss-coating enters drying box, and adjustment drying box temperature is 35 DEG C, by surface drying adhesive;
D. the single layer PP sheet material of drying is sent to double pressing ends and PE film and is bonded;
E. it winds.
Composite material as shown in Figure 1 is made, i.e. monolayer plastic sheet material 1 is directly compound with PE film 2.
Embodiment 3:
Food packaging plastic sheet/PE composite material preparation method of the invention successively carries out in accordance with the following steps:
A. it will be placed in double pressing ends of existing i.e. painting type laminating machine with a thickness of the PE film roll cylinder of 0.04mm, single layer PS sheet material is rolled up
Cylinder is placed in the gluing end of i.e. painting type laminating machine;
B. single layer PS sheet material passes through lick roller kiss-coating;
C. the single layer PS sheet material after kiss-coating enters drying box, and adjustment drying box temperature is 40 DEG C, by surface drying adhesive;
D. the single layer PS sheet material of drying is sent to double pressing ends and PE film and is bonded;
E. it winds.
Composite material as shown in Figure 1 is made, i.e. monolayer plastic sheet material 1 is directly compound with PE film 2.
Claims (3)
1. a kind of food packaging plastic sheet/PE film composite material, has monolayer plastic sheet material (1), it is characterised in that: the list
Layer plastic sheet (1) is directly compound with PE film (2), and the thickness of the PE film (2) is at least 0.03mm.
2. food packaging plastic sheet/PE film composite material according to claim 1, it is characterised in that: the single layer modeling
Media sheet (1) is PET, PP or PS.
3. a kind of preparation method of food packaging plastic sheet/PE film composite material as described in claim 1, it is characterised in that
Successively carry out in accordance with the following steps:
A., PE film roll cylinder is placed in double pressing ends of i.e. painting type laminating machine, monolayer plastic sheet material reel drum is placed in i.e. painting type overlay film
The gluing end of machine;
B. monolayer plastic sheet material passes through lick roller kiss-coating;
C. the monolayer plastic sheet material after kiss-coating enters drying box, is dried surface glue with 30 ~ 40 DEG C;
D. the monolayer plastic sheet material of drying is sent to double pressing ends and PE film and is bonded;
E. it winds.