CN109047593A - A kind of knotting method of steel wire - Google Patents
A kind of knotting method of steel wire Download PDFInfo
- Publication number
- CN109047593A CN109047593A CN201810753081.0A CN201810753081A CN109047593A CN 109047593 A CN109047593 A CN 109047593A CN 201810753081 A CN201810753081 A CN 201810753081A CN 109047593 A CN109047593 A CN 109047593A
- Authority
- CN
- China
- Prior art keywords
- steel wire
- adhesive tape
- parts
- winding
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of steel wire knotting method prepares cutting nippers, masking tape and prepares two steel wires to link together, according to winding 7-12 circle mutually is carried out, reserves sufficient length the end of a thread opposite direction and winds 7-12 circle mutually, extra the end of a thread is normally knotted again;It is cemented at winding, and will be cemented at each winding and knotting using adhesive tape, and refined as far as possible using masking tape.It knots in this way, steel wire junction is secured, and detection rupture pull force is higher than the rupture pull force of steel wire itself, can significantly reduce and thread the time in operation process, and increasing production capacity reduces cost.
Description
Technical field
The present invention relates to electroplating diamond wire saw production lines, and in particular to a kind of steel wire knotting method.
Background technique
Diamond wire is the mainstream cutting material of domestic hard material instantly.Diamond wire is the abbreviation of diamond cutting secant, also
Position diamond cut line or diamond line referred to as.In diamond wire production process, due to the length limitation of every volume bus, bus makes
With terminating or residue length is not able to satisfy during normal production, need to carry out bus replacement, according to conventional steel wire knotting method,
Such as directly knot to be unable to reach and answer effective, the speed of steel wire is lower after knotting, wastes time, and influences production capacity, while mistake
Absent-mindedness is easy in journey at knotting, causes broken string etc. abnormal.
Summary of the invention
Technical problem to be solved by the present invention lies in overcome the prior art to provide a kind of steel wire knotting method.
To achieve the above object, the invention provides the following technical scheme:
A kind of steel wire knotting method, it is characterised in that:
Prepare cutting nippers, masking tape and prepare two steel wires to link together, winds 7-12 circle mutually according to progress,
It reserves sufficient length the end of a thread opposite direction and winds 7-12 circle mutually, extra the end of a thread is normally knotted again;
It is cemented at winding, and will be cemented at each winding and knotting using adhesive tape, and refined as far as possible using masking tape.
Further technology: the adhesive tape is high viscosity High-strength adhesive tape.
Further technology: the adhesive tape includes the substrate stacked gradually, the first rubber layer and the second adhesive layer.
Further technology: the substrate is selected from paper, plastic film, cloth, metal foil or polymer composites.
Further technology: second adhesive layer includes that the following component of parts by weight is prepared: 150-250 portions of rubbers
Glue, 5-20 part filler, 10-40 parts of tackifier, 10-20 parts of coupling agents and 10-15 parts of antioxidant.
Further technology: the filler is selected from barium titanate, strontium titanates, barium strontium titanate, lead zirconate titanate, silicon carbide, nitridation
One of boron, aluminium oxide, titanium dioxide, silica, zinc oxide or zinc sulphide or at least two combination.
Further technology: the preparation method includes the following steps:
By each component melting mixing of the first dielectric layer, the first rubber compound is formed;
The rubber is squeezed out by screw extruder, the calendering formation on substrate, then semi-solid preparation is handled, and forms first
Dielectric layer;
By each component melting mixing of the second adhesive layer, rubber compound is formed;
The rubber compound is squeezed out by screw extruder, the calendering formation in first rubber layer obtains the glue
Band.
The utility model has the advantages that
It knots in this way, steel wire junction is secured, and detection rupture pull force is higher than the rupture pull force of steel wire itself, can be with
It significantly reduces and threads the time in operation process, increasing production capacity reduces cost;
This method is primarily adapted for use in knotting when steel wire is replaced, and improves replacement steel wire speed, saves time, Ke Yijin
The promotion of row production capacity.
Specific embodiment
In order to be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, tie below
Specific embodiment is closed, the present invention is further explained.
Embodiment 1: a kind of steel wire knotting method prepares cutting nippers, masking tape and prepares two steel to link together
Line reserves sufficient length the end of a thread opposite direction and winds 7-12 circle mutually, again by extra the end of a thread according to winding 7-12 circle mutually is carried out
Normally knotted;
It is cemented at winding, and will be cemented at each winding and knotting using adhesive tape, and refined as far as possible using masking tape.
Adhesive tape includes the substrate stacked gradually, the first rubber layer and the second adhesive layer.
Substrate is selected from paper, plastic film, cloth, metal foil or polymer composites.
Second adhesive layer includes that the following component of parts by weight is prepared: 150 parts of rubber, 5 parts of fillers, 10 parts of tackifier,
10 parts of coupling agents and 10 parts of antioxidant.
Filler is selected from barium titanate, strontium titanates, barium strontium titanate, lead zirconate titanate, silicon carbide, boron nitride, aluminium oxide, titanium dioxide
One of titanium, silica, zinc oxide or zinc sulphide or at least two combination.
Preparation method includes the following steps:
By each component melting mixing of the first dielectric layer, the first rubber compound is formed;
The rubber is squeezed out by screw extruder, the calendering formation on substrate, then semi-solid preparation is handled, and forms first
Dielectric layer;
By each component melting mixing of the second adhesive layer, rubber compound is formed;
The rubber compound is squeezed out by screw extruder, the calendering formation in first rubber layer obtains the glue
Band.
Embodiment 2: a kind of steel wire knotting method prepares cutting nippers, masking tape and prepares two steel to link together
Line reserves sufficient length the end of a thread opposite direction and winds 7-12 circle mutually, again by extra the end of a thread according to winding 7-12 circle mutually is carried out
Normally knotted;
It is cemented at winding, and will be cemented at each winding and knotting using adhesive tape, and refined as far as possible using masking tape.
Adhesive tape includes the substrate stacked gradually, the first rubber layer and the second adhesive layer.
Substrate is selected from paper, plastic film, cloth, metal foil or polymer composites.
Second adhesive layer includes that the following component of parts by weight is prepared: 250 parts of rubber, 20 parts of fillers, 40 parts of tackifier,
20 parts of coupling agents and 15 parts of antioxidant.
Filler is selected from barium titanate, strontium titanates, barium strontium titanate, lead zirconate titanate, silicon carbide, boron nitride, aluminium oxide, titanium dioxide
One of titanium, silica, zinc oxide or zinc sulphide or at least two combination.
Preparation method includes the following steps:
By each component melting mixing of the first dielectric layer, the first rubber compound is formed;
The rubber is squeezed out by screw extruder, the calendering formation on substrate, then semi-solid preparation is handled, and forms first
Dielectric layer;
By each component melting mixing of the second adhesive layer, rubber compound is formed;
The rubber compound is squeezed out by screw extruder, the calendering formation in first rubber layer obtains the glue
Band.
Unit | Embodiment 1 | Embodiment 2 | |
180 ° of peel strengths | N/25mm | 6 | 6 |
Tensile strength | N/cm | 42 | 38 |
Elongation at break | % | 165 | 160 |
It is found that this law adhesive tape peel strength and drawstring intensity are all higher from table, it is suitable for steel cable and knots.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (7)
1. a kind of steel wire knotting method, it is characterised in that:
Prepare cutting nippers, masking tape and prepare two steel wires to link together, according to winding 7-12 circle mutually is carried out, reserves
Sufficient length the end of a thread opposite direction winds mutually 7-12 circle, and extra the end of a thread is normally knotted again;
It is cemented at winding, and will be cemented at each winding and knotting using adhesive tape, and refined as far as possible using masking tape.
2. a kind of steel wire knotting method according to claim 1, it is characterised in that: the adhesive tape is that high viscosity is high-strength
Spend adhesive tape.
3. a kind of steel wire knotting method according to claim 1, it is characterised in that: the adhesive tape includes stacking gradually
Substrate, the first rubber layer and the second adhesive layer.
4. a kind of steel wire knotting method according to claim 3, it is characterised in that: it is thin that the substrate is selected from paper, plastics
Film, cloth, metal foil or polymer composites.
5. a kind of steel wire knotting method according to claim 3, it is characterised in that: second adhesive layer includes weight
The following component of amount part is prepared: 150-250 parts of rubber, 5-20 parts of fillers, 10-40 parts of tackifier, 10-20 parts of coupling agents and
10-15 parts of antioxidant.
6. a kind of steel wire knotting method according to claim 5, it is characterised in that: the filler be selected from barium titanate,
Strontium titanates, barium strontium titanate, lead zirconate titanate, silicon carbide, boron nitride, aluminium oxide, titanium dioxide, silica, zinc oxide or vulcanization
One of zinc or at least two combination.
7. a kind of steel wire knotting method according to claim 1, it is characterised in that: the adhesive tape preparation method includes such as
Lower step:
By each component melting mixing of the first dielectric layer, the first rubber compound is formed;
The rubber is squeezed out by screw extruder, the calendering formation on substrate, then semi-solid preparation is handled, and forms the first dielectric
Layer;
By each component melting mixing of the second adhesive layer, rubber compound is formed;
The rubber compound is squeezed out by screw extruder, the calendering formation in first rubber layer obtains the adhesive tape.