CN109023652A - A kind of preparation method of summer women skirt fabric - Google Patents
A kind of preparation method of summer women skirt fabric Download PDFInfo
- Publication number
- CN109023652A CN109023652A CN201811242765.0A CN201811242765A CN109023652A CN 109023652 A CN109023652 A CN 109023652A CN 201811242765 A CN201811242765 A CN 201811242765A CN 109023652 A CN109023652 A CN 109023652A
- Authority
- CN
- China
- Prior art keywords
- fabric
- fiber
- cattail wool
- preparation
- cattail
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of summer women skirt fabric, fabric uses Profile Polyester Fibre, has preferably hygroscopicity, excellent moisture absorbing and sweat releasing, splendid gas permeability, drapability than conventional imitative silk face fabric；Cattail wool fiber is added and cocoon fiber progress is blended, enhances the anti-microbial property and moisture permeability of fabric；By carrying out guar gum protection to cattail wool fiber, the antibiotic effective ingredient of guarantee cattail wool fiber as far as possible will not be destroyed；The whiteness of fabric can be promoted by carrying out light sodium carbonate+ultrasonication to cattail wool fiber.
Description
Technical field
The present invention relates to field of textile more particularly to a kind of preparation methods of summer women skirt fabric.
Background technique
That there is prices is high for silk fabric, intensity is low, wears no resistance, not easy to wash, and maintenance difficulty is big etc. is difficult to overcome
Problem, for this purpose, there is many silk-like fabrics to enter market, this kind of fabric by using many chemical fibre raw materials combine it is unique or
Silk-like fabric is made in preferred preparation process, to overcome many deficiencies of silk fabric.
Disclosed document, as the Chinese patent of Patent No. CN1096333A disclose it is a kind of using three different polyamide fibre cospinnings it is thin
Denier filament does organizine, and fine-denier polyamide fiber low stretch yarn does tram, and fabric construction is using variation plain weave；Publication No. CN1021270522A
Chinese patent disclose a kind of crease-shedding simulation fabric facing material, the fabric use twill-weave, front use super fine denier polyamide fibre DTY,
Reverse side uses polyamide fibre 6DTY, carries out weaving completion in embedding woven method；The Chinese patent of Publication No. CN102011244A discloses
A kind of simulated silk flash fabric, the fabric broadwise utilize raw material using the short fine processing method combined that interweaves of natural fiber
Different tinctorial property, shrinkage, wearability, mention intensity, wearability, coloured light degree and comfort level of fabric etc. greatly
It is high.As the development of textile industry imitates silk technology more now to make silk-like fabric imitate silk, super silk in performance and function
Pay attention to a variety of differential, functional technical integration to play, highlights the mutual fusion of the technologies such as spinning, weaving, dyeing and finishing.
The present invention is in order to reach better Silk effect, and by the way of blended, it is true that part is added in blended yarn weaved fabric
Silk fiber and a small amount of cattail wool fiber, that is, can reach extraordinary Silk effect.
Summary of the invention
Technical problems based on background technology, the invention proposes a kind of preparation sides of summer women skirt fabric
Method.
Technical scheme is as follows:
A kind of preparation method of summer women skirt fabric, comprising the following steps:
A, it woven fabric: uses polyester fiber, cocoon fiber and modified cattail wool fiber for raw material, base is made using water-jet loom
Cloth；
B, starching, oil: fabric prepared by step A carries out starching and oiling treatment；
C, desizing refining: desizing refining processing is carried out using low bath raio high-pressure injection overflow machine, technology preparation and condition are such as
Under: pH value 7.5-8.5 is bathed in desizing, refining agent: 2-4g/L, NaOH:1-2g/L, bath raio: 1:10-15, temperature: 75-80 DEG C, when
Between: 35-40min；
D, Alkali reduction: after the completion of desizing refining, then alkali decrement treatment is carried out, treatment conditions 35%NaOH100-140g/
L, temperature: 100-110 DEG C, the time: 5-10min；
E, rear shaping and drying: immersion 5-10min first is carried out with the neopelex solution of 2-5%, is then carried out
100 DEG C of clear water pad, then drying and shaping under the conditions of 170-190 DEG C；
F, it arranges: after shaping and drying, summer women skirt fabric proposed by the present invention can be obtained.
Preferably, the weight percent of the polyester fiber is 70-80%, and the weight percent of cocoon fiber is 15-
25%, the weight percent of modified cattail wool fiber is surplus.
Preferably, the polyester fiber is Profile Polyester Fibre.
Preferably, the preparation method of the modification cattail wool fiber, comprising the following steps:
A, the inflorescence on clip cattail, takes the cattail wool on inflorescence, cattail wool is dried, and obtains cattail wool fiber；
B, neopelex being dissolved in deionized water, is stirred evenly, addition vinegar acid for adjusting pH value is 5.5-6,
Cattail wool fiber is added, stirs 10-15min；
C, sodium bicarbonate is added, adjusting pH is 8.0-8.5, the precipitated calcium carbonate of micron grain size is added, 50-80kHz's
Under ultrasonic frequency, 5-8min is handled；
D, vinegar acid for adjusting pH value is added as 5.5-6, under the ultrasonic frequency of 8-20kHz, handles 2-3min；
E, it is put into 5-8% guar gum solution after taking out cattail wool fiber and impregnates 10-15min；It dries at normal temperature, i.e.,
It can.
Preferably, in the step c, the partial size of the precipitated calcium carbonate of micron grain size is 30-120 μm.
Preferably, in the step e, being dried at normal temperature to moisture content is 5-10%.
Cattail wool alias: the Gu at the western side of Shandong Weishan Lake such as water candle, Calceolaria, wild candle, raupo, hair wax (Shaanxi call)
Abundant ground.The vegetation such as various reeds, the stem or leaf of cattail are abounded on lake, among wetland shallow water.2 month weather gradually warm up expose the surface, start to give birth to
It is long, just it is cattail pollen, is grown to the cattail's spike eight, September, its tiny villus is fluffy such as cotton after the autumn cattail's spike is completely dry, the cattail's spike parched
It can must not touch when not in use, even a little scraping collision, the cattail's spike has been reformed into " Magic wand ", the Pu of a piece consolidation of moment
Stick has just popped into a glob of cattail wool, whiffet, that cattail wool just floats in the sky, grab all grab less than.In every late autumn, work as breeze
Cross, local tiny villus dances in the air over the sky, becomes a kind of landscape, enable it is many come this poet, singer be all reluctant to leave lyric, Zhong Duoyou
People cannot forget for a long time after seeing this scape.
Cattail wool is applied to pillow and core mostly as filler at present, compared with silk and natural feather, cattail wool is light and short,
It is strongly small, it is traditional pillow filler material.And cattail wool fiber is kept warm, and is breathed freely, the characteristics of faint scent and health care is that it becomes the modern times
The house non-defective unit of life.
Typha pollen can be used as medicine, and be commonly called as cattail pollen, and cattail pollen has long applicating history in China, have activating microcirculation and removing stasis medicinal, stop
Blood analgesia, treating stranguria effect, and there is excellent mosquito-repelling function.
In the present invention, cattail wool fiber is carried out under slightly acidic condition, surfactant processing is carried out, by cattail wool fiber table
The wax in face removes, and then adjusts pH to alkalescence, the precipitated calcium carbonate of micron grain size is added, further carries out to cattail wool fiber
Ultrasonication not only can further be removed the wax of cattail wool fiber surface, and can remove cattail wool fiber surface
Other impurities can also promote the whiteness of cattail wool fiber surface；The processing method can also save the special aroma of cattail wool fiber；
Then to prevent cattail wool under alkalinity and hot conditions, antibiotic effective ingredient will receive influence, then carry out to cattail wool fiber surface
The protection of guar gum cladding adds surfactant until the rear shaping and drying the step of, at high temperature with clear water by guar gum
Elution.
Using the precipitated calcium carbonate of 30-120 μm of partial size, first is that precipitated calcium carbonate is using the carbonic acid being chemically synthesized
Calcium, impurity content is very low, will not pollute to fiber, influence whiteness；Second is that adjusting pH after precipitated calcium carbonate is disposed
It is most acid, continue ultrasonication, the precipitated calcium carbonate of web surface can be dissolved, mode is subsequent to cause shadow to fiber
It rings；Third is that selecting the precipitated calcium carbonate of 30-120 μm of partial size, partial size is too small, poor processing effect, and partial size crosses conference to fiber
Intensity impacts.
The invention has the beneficial effects that: 1, fabric use Profile Polyester Fibre, has than conventional imitative silk face fabric and preferably inhales
Moist, excellent moisture absorbing and sweat releasing, splendid gas permeability, drapability；2, cattail wool fiber is added and cocoon fiber progress is blended, enhances
The anti-microbial property and moisture permeability of fabric；3, by carrying out guar gum protection to cattail wool fiber, guarantee cattail wool fiber as far as possible
Antibiotic effective ingredient will not be destroyed；4, face can be promoted by carrying out light sodium carbonate+ultrasonication to cattail wool fiber
The whiteness of material.
Specific embodiment
Embodiment 1:
A kind of preparation method of summer women skirt fabric, comprising the following steps:
A, it woven fabric: uses polyester fiber, cocoon fiber and modified cattail wool fiber for raw material, base is made using water-jet loom
Cloth；
B, starching, oil: fabric prepared by step A carries out starching and oiling treatment；
C, desizing refining: desizing refining processing is carried out using low bath raio high-pressure injection overflow machine, technology preparation and condition are such as
Under: it is 8.1 that pH value is bathed in desizing, refining agent: 3g/L, NaOH:1.8g/L, bath raio: 1:14, temperature: 78 DEG C, the time: 36min；
D, Alkali reduction: after the completion of desizing refining, then carrying out alkali decrement treatment, treatment conditions 35%NaOH125g/L, temperature
Degree: 107 DEG C, the time: 9min；
E, rear shaping and drying: immersion 6min first is carried out with 3.5% neopelex solution, then carries out 100
DEG C clear water pads, then drying and shaping under the conditions of 185 DEG C；
F, it arranges: after shaping and drying, summer women skirt fabric proposed by the present invention can be obtained.
The weight percent of the polyester fiber is 78%, and the weight percent of cocoon fiber is 18%, modified cattail wool
The weight percent of fiber is 4%.
The polyester fiber is triangle Profile Polyester Fibre.
The preparation method of the modification cattail wool fiber, comprising the following steps:
A, the inflorescence on clip cattail, takes the cattail wool on inflorescence, cattail wool is dried, and obtains cattail wool fiber；
B, neopelex is dissolved in deionized water, is stirred evenly, it is 5.8 that vinegar acid for adjusting pH value, which is added, is added
Enter cattail wool fiber, stirs 12min；
C, sodium bicarbonate is added, adjusting pH is 8.2, the precipitated calcium carbonate of micron grain size is added, in the ultrasonic wave frequency of 65kHz
Under rate, 7min is handled；
D, it is added under the ultrasonic frequency that vinegar acid for adjusting pH value is 5.6,10kHz, handles 2.5min；
E, it is put into 7% guar gum solution after taking out cattail wool fiber and impregnates 11min；It dries at normal temperature.
In the step c, the partial size of the precipitated calcium carbonate of micron grain size is 30-120 μm.
In the step e, being dried at normal temperature to moisture content is 6%.
Embodiment 2:
A kind of preparation method of summer women skirt fabric, comprising the following steps:
A, it woven fabric: uses polyester fiber, cocoon fiber and modified cattail wool fiber for raw material, base is made using water-jet loom
Cloth；
B, starching, oil: fabric prepared by step A carries out starching and oiling treatment；
C, desizing refining: desizing refining processing is carried out using low bath raio high-pressure injection overflow machine, technology preparation and condition are such as
Under: pH value 7.5-8.5 is bathed in desizing, refining agent: 2g/L, NaOH:1g/L, bath raio: 1:15, temperature: 80 DEG C, the time: 35min；
D, Alkali reduction: after the completion of desizing refining, then carrying out alkali decrement treatment, treatment conditions 35%NaOH140g/L, temperature
Degree: 110 DEG C, the time: 10min；
E, rear shaping and drying: first carrying out immersion 10min with 5% neopelex solution, then carries out 100 DEG C
Clear water pads, then drying and shaping under the conditions of 190 DEG C；
F, it arranges: after shaping and drying, summer women skirt fabric proposed by the present invention can be obtained.
The weight percent of the polyester fiber is 70%, and the weight percent of cocoon fiber is 25%, modified cattail wool
The weight percent of fiber is 5%.
The polyester fiber is star Profile Polyester Fibre.
The preparation method of the modification cattail wool fiber, comprising the following steps:
A, the inflorescence on clip cattail, takes the cattail wool on inflorescence, cattail wool is dried, and obtains cattail wool fiber；
B, neopelex is dissolved in deionized water, is stirred evenly, it is 6 that vinegar acid for adjusting pH value, which is added, is added
Cattail wool fiber stirs 10min；
C, sodium bicarbonate is added, adjusting pH is 8.5, the precipitated calcium carbonate of micron grain size is added, in the ultrasonic wave frequency of 50kHz
Under rate, 8min is handled；
D, it is added under the ultrasonic frequency that vinegar acid for adjusting pH value is 5.5,20kHz, handles 2min；
E, it is put into 8% guar gum solution after taking out cattail wool fiber and impregnates 10min；It dries at normal temperature.
In the step c, the partial size of the precipitated calcium carbonate of micron grain size is 30-120 μm.
In the step e, being dried at normal temperature to moisture content is 10%.
Embodiment 3:
A kind of preparation method of summer women skirt fabric, comprising the following steps:
A, it woven fabric: uses polyester fiber, cocoon fiber and modified cattail wool fiber for raw material, base is made using water-jet loom
Cloth；
B, starching, oil: fabric prepared by step A carries out starching and oiling treatment；
C, desizing refining: desizing refining processing is carried out using low bath raio high-pressure injection overflow machine, technology preparation and condition are such as
Under: pH value 7.5-8.5 is bathed in desizing, refining agent: 2g/L, NaOH:2g/L, bath raio: 1:10, temperature: 75-80 DEG C, the time: 35-
40min；
D, Alkali reduction: after the completion of desizing refining, then carrying out alkali decrement treatment, treatment conditions 35%NaOH100g/L, temperature
Degree: 100 DEG C, the time: 5min；
E, rear shaping and drying: first carrying out immersion 5min with 5% neopelex solution, then carries out 100 DEG C
Clear water pads, then drying and shaping under the conditions of 190 DEG C；
F, it arranges: after shaping and drying, summer women skirt fabric proposed by the present invention can be obtained.
Preferably, the weight percent of the polyester fiber is 80%, and the weight percent of cocoon fiber is 15%, is changed
Property cattail wool fiber weight percent be 5%.
Preferably, the polyester fiber is triangle Profile Polyester Fibre.
Preferably, the preparation method of the modification cattail wool fiber, comprising the following steps:
A, the inflorescence on clip cattail, takes the cattail wool on inflorescence, cattail wool is dried, and obtains cattail wool fiber；
B, neopelex is dissolved in deionized water, is stirred evenly, it is 5.5 that vinegar acid for adjusting pH value, which is added, is added
Enter cattail wool fiber, stirs 15min；
C, sodium bicarbonate is added, adjusting pH is 8.0, the precipitated calcium carbonate of micron grain size is added, in the ultrasonic wave frequency of 80kHz
Under rate, 5min is handled；
D, it is added under the ultrasonic frequency that vinegar acid for adjusting pH value is 6,8kHz, handles 3min；
E, it is put into 5% guar gum solution after taking out cattail wool fiber and impregnates 15min；It dries at normal temperature.
In the step c, the partial size of the precipitated calcium carbonate of micron grain size is 30-120 μm.
In the step e, being dried at normal temperature to moisture content is 5%.
Comparative example 1
Light sodium carbonate+ultrasonication in embodiment 1 is replaced with public in Chinese invention patent CN105887277A
Enzymatic treatment+the ultrasonication opened, remaining preparation method are constant.
Test 1
U.S. Datacolor-2000 whiteness instrument (d/0, xenon lamp) is used to the fabric of embodiment 1-3 and comparative example 1 below
Whiteness detection is carried out, obtained testing result is shown in Table 1.
Table 1: the whiteness testing result (using R457 whiteness formulas) of sample fabric；
| Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative example 1 | |
| Whiteness | 92.6 | 91.8 | 91.8 | 68.4 |
By the above test result it is recognised that the whiteness of sample fabric after treatment dramatically increases.
Test 2
Through detecting, the sample of embodiment 1 has the peat-reek of cattail wool；Peat-reek of the sample of comparative example 1 without cattail wool.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (6)
1. a kind of preparation method of summer women skirt fabric, which comprises the following steps:
A, it woven fabric: uses polyester fiber, cocoon fiber and modified cattail wool fiber for raw material, fabric is made using water-jet loom；
B, starching, oil: fabric prepared by step A carries out starching and oiling treatment；
C, desizing refining: desizing refining processing is carried out using low bath raio high-pressure injection overflow machine, technology preparation and condition are as follows: moving back
Slurry bath pH value 7.5-8.5, refining agent: 2-4g/L, NaOH:1-2g/L, bath raio: 1:10-15, temperature: 75-80 DEG C, the time: 35-
40min；
D, Alkali reduction: after the completion of desizing refining, then carrying out alkali decrement treatment, treatment conditions 35%NaOH100-140g/L, temperature
Degree: 100-110 DEG C, the time: 20-30min；
E, rear shaping and drying: first carrying out immersion 5-10min with the neopelex solution of 2-5%, then carries out 100 DEG C
Clear water pads, then drying and shaping under the conditions of 170-190 DEG C；
F, it arranges: after shaping and drying, summer women skirt fabric proposed by the present invention can be obtained.
2. the preparation method of summer women skirt fabric as described in claim 1, which is characterized in that the polyester fiber
Weight percent is 70-80%, and the weight percent of cocoon fiber is 15-25%, and the weight percent of modified cattail wool fiber is
Surplus.
3. the preparation method of summer women skirt fabric as described in claim 1, which is characterized in that the polyester fiber is
Profile Polyester Fibre.
4. the preparation method of summer women skirt fabric as described in claim 1, which is characterized in that the modification cattail wool is fine
The preparation method of dimension, comprising the following steps:
A, the inflorescence on clip cattail, takes the cattail wool on inflorescence, cattail wool is dried, and obtains cattail wool fiber；
B, neopelex is dissolved in deionized water, is stirred evenly, addition vinegar acid for adjusting pH value is 5.5-6, is added
Cattail wool fiber stirs 10-15min；
C, sodium bicarbonate is added, adjusting pH is 8.0-8.5, the precipitated calcium carbonate of micron grain size is added, in the ultrasound of 50-80kHz
Under wave frequency rate, 5-8min is handled；
D, vinegar acid for adjusting pH value is added as 5.5-6, under the ultrasonic frequency of 8-20kHz, handles 2-3min；
E, it is put into 5-8% guar gum solution after taking out cattail wool fiber and impregnates 10-15min；It dries at normal temperature.
5. the preparation method of summer women skirt fabric as claimed in claim 4, which is characterized in that in the step c, micron
The partial size of the precipitated calcium carbonate of partial size is 30-120 μm.
6. the preparation method of summer women skirt fabric as claimed in claim 4, which is characterized in that in the step e, normal
The lower drying of temperature to moisture content is 5-10%.