CN109023127A - Corrosion-resistant rail in high speed railway production method - Google Patents
Corrosion-resistant rail in high speed railway production method Download PDFInfo
- Publication number
- CN109023127A CN109023127A CN201811239631.3A CN201811239631A CN109023127A CN 109023127 A CN109023127 A CN 109023127A CN 201811239631 A CN201811239631 A CN 201811239631A CN 109023127 A CN109023127 A CN 109023127A
- Authority
- CN
- China
- Prior art keywords
- rail
- corrosion
- high speed
- speed railway
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention designs seamed high-speed steel rail field of production, especially a kind of raising rail surface layer chromium nickel aluminium carbon component, and utilize chromising and carburizing principle, improve the corrosion-resistant rail in high speed railway production method of rail surface layer corrosion resisting property and anti-decarburization capacity, using the rolling waste heat of steel rail rolling, apply the acceleration cooling down operation of 1-3 DEG C/s to rail, after the heat treatment operation, heat-treatment of rail waste heat is recycled, hot melt zinc liquid is sprayed to Rail Surface.The rail surface layer that the present invention obtains is rich in anti-corrosion substance zinc layers, improves the comprehensive performance and surface layer corrosion resisting property of rail.Rail steel carbon content is 0.3-0.7%, tensile strength 500-900MPa, elongation percentage >=10%, excellent anti-corrosion performance.Finally obtained rail case carbon is normal segregation, the chromium nickel alumin(i)um alloy material that decarburized layer deepness is shallower and surface layer is excellent rich in corrosion resisting property, anti-corrosion and reduce decarburized layer deepness to improve rail surface layer.Present invention is particularly suitable among the production of corrosion-resistant rail in high speed railway.
Description
Technical field
The present invention designs seamed high-speed steel rail field of production, especially a kind of corrosion-resistant rail in high speed railway production method.
Background technique
With the development of domestic and international high-speed rail, high-speed rail construction and high-speed rail line upkeep in rail and surface quality propose
Higher requirement.In tunnel or coastal environments, rail corrosion has become one and more outstanding asks rail for high-speed railway
The main reason for inscribing, also becoming road under rail defects and failures.Due to safety and economy that rail uses, excessive anti-corrosion can not be added
Alloying element, can only carry out the production supply of material with carbon or microalloy rail, can not carry out effective anti-corrosion using rail matrix.
Currently, Rail Production producer mainly carries out anti-corrosion, but rail corrosion resisting property or ring with Rail Surface spraying interleaving agent both at home and abroad
Guarantor's problem is undesirable.
Rail for high-speed railway need to carry out pre- grinding process to rail tread in being laid with use process, both reconditioning steel
Track surface also wants thinning surface decarburized layer, to reduce rail corrugation phenomenon.The too deep decarburized layer in rail surface layer, bring are to beat
The difficulty and cost of mill.To reduce steel rail grinding depth, railway parent company once required rail factory decarburized layer deepness≤0.3mm,
But domestic Rail Production producer lumber recovery is lower, is finally still checked and accepted with rail factory decarburized layer deepness≤0.5mm.Therefore, it reduces
Decarburized layer becomes another rail for high-speed railway problem.
Due to high-speed rail train axis heavy and light, the speed of service is very fast, therefore rail for high-speed railway is required with strength reduction
The supply of material of U71Mn rolled, rail strength are that existing steel grade is minimum, but requires toughness plasticity higher.
Summary of the invention
Technical problem to be solved by the invention is to provide a kind of raising rail surface layer chromium nickel aluminium carbon components, and utilize chromising
With carburizing principle, the corrosion-resistant rail in high speed railway production method of rail surface layer corrosion resisting property and anti-decarburization capacity is improved.
The technical solution adopted by the present invention to solve the technical problems is: corrosion-resistant rail in high speed railway production method, benefit
With the rolling waste heat of steel rail rolling, apply the acceleration cooling down operation of 1-3 DEG C/s to rail, after the heat treatment operation, recycles
Heat-treatment of rail waste heat sprays hot melt zinc liquid to Rail Surface.
Further, the coating thickness for spraying hot melt zinc liquid to Rail Surface is 0.1-0.5mm.
Further, the spraying temperature for spraying hot melt zinc liquid to Rail Surface is 400-600 DEG C.
Further, it is 0.1-0.9%, Si that the matrixed ingredient percent of the rail, which is respectively as follows: C content,
Content be 0.1-0.8%, Mn content be 0.15-1.2%, Cr≤0.4%, V≤0.020%, Nb≤0.40%, P≤
0.025%, S≤0.025%, surplus are Fe and inevitable impurity.
Further, casting mode of the rail in casting are as follows: take low S's to enter furnace molten iron, take high alkalinity
Refining slag, and whole process protection is poured.
Further, carburant used in the casting process is anthracite and low N alloy.
Further, the rail prevents from connecing with air in the LF heating process in casting using foaming agent
It touches and prevents to suck excessive N.
Further, the slab that the rail obtains after being cast, which enters burial pit, carries out slow cooling.
Further, the rail is after the heated austenite of casting is uniform, carried out using the giant of >=18MPa
Tunneling boring efficient dephosphorization.
Further, steel rail rolling method is universal rolling technique.
The beneficial effects of the present invention are: the rail surface layer that the present invention obtains improves rail rich in anti-corrosion substance zinc layers
Comprehensive performance and surface layer corrosion resisting property.Rail steel carbon content be 0.3-0.7%, tensile strength 500-900MPa, elongation percentage >=
10%, excellent anti-corrosion performance.In addition, carrying out composite rolling in rail steel billet since the present invention utilizes carburizing and chromising principle
Afterwards, finally obtained rail case carbon is normal segregation, the chromium that decarburized layer deepness is shallower and surface layer is excellent rich in corrosion resisting property
Nickel alumin(i)um alloy material, with improve rail surface layer it is anti-corrosion and reduce decarburized layer deepness.Present invention is particularly suitable for corrosion-resistant high-speed irons
Among the production of rail for road.
Specific embodiment
Corrosion-resistant rail in high speed railway production method applies 1-3 DEG C/s's to rail using the rolling waste heat of steel rail rolling
Accelerate cooling down operation, after the heat treatment operation, recycle heat-treatment of rail waste heat, hot melt zinc liquid is sprayed to Rail Surface.It is logical
The corrosion-resistant rail for high-speed railway that aforementioned production method obtains is crossed, surface layer is rich in anti-corrosion substance zinc layers, improves the comprehensive of rail
Close performance and surface layer corrosion resisting property.Rail steel carbon content be 0.3-0.7%, tensile strength 500-900MPa, elongation percentage >=10%,
Excellent anti-corrosion performance.
In order to further increase the precision of operation, it can choose such scheme, i.e., hot melt zinc sprayed to Rail Surface
When liquid, preferably satisfy following parameter: the coating thickness that hot melt zinc liquid is sprayed to Rail Surface is 0.1-0.5mm, and to rail
The spraying temperature of surface spraying hot melt zinc liquid is 400-600 DEG C.
Rail also has corresponding requirement as respective treated basis, the present invention, wherein preferably the rail is matrixed
Learn ingredient percent be respectively as follows: C content be 0.1-0.9%, Si content be 0.1-0.8%, Mn content be 0.15-1.2%,
Cr≤0.4%, V≤0.020%, Nb≤0.40%, P≤0.025%, S≤0.025%, surplus be Fe and inevitably it is miscellaneous
Matter, to guarantee final product quality.
In addition, the present invention is also creative to improve the premise processing of rail in order to guarantee final products quality,
Preferred embodiment is as follows: casting mode of the rail in casting are as follows: and it takes low S's to enter furnace molten iron, takes high alkalinity refining slag,
And whole process protection be poured, and preferably: carburant used in the casting process be anthracite and low N alloy, and
It is preferred that the rail prevents from contacting and prevent to suck with air in the LF heating process in casting using foaming agent
More N, and the slab that preferably rail obtains after pouring enter burial pit progress slow cooling, and the preferably rail exists
After heated austenite of casting is uniform, tunneling boring efficient dephosphorization is carried out using the giant of >=18MPa, and preferably rail rolls
Method processed is universal rolling technique.Above-mentioned preferred embodiment can allow rail preferably with technology of the invention to matching, thus
Increase substantially the final quality of product.
Embodiment
Embodiment 1
The present embodiment and corresponding comparative example select following rail chemical component
1 embodiment rail chemical component of table/%
Comparative example in the present invention uses chemical component identical with embodiment, heating, rolling and burning optimization on line technique.
Corrosion resistant material is carried out to steel billet using processing method of the invention and sprays rolling process, wherein 1# to 5# is different
Carburetting thickness, 6# are that comparative example does not carry out attachment processing.Then, 6 samples are using identical heating, rolling and burning optimization on line
Technique production.
2 embodiment of table and comparative example steel billet carburetting thickness
According to TB/T 2344-2012 requirement, the inspection of rail head decarburized layer deepness is carried out to 6 rail samples respectively, examines knot
Fruit is as shown in table 3.
3 embodiment of table and comparative example rail decarburized layer deepness
Period soaking corrosion is carried out in embodiment and comparative example rail according to GB/T 19746 and 2375 standard of TB/T respectively to add
Fast corrosion test, the NaCl solution that corrosive agent is 2%, etching time 200h, test result are shown in Table 4.
4 embodiment of the present invention of table and the abrasion of comparative example rail head of rail
The rail that the present invention has chosen identical chemical component simultaneously compares, in embodiment, at used five kinds
Reason mode is the method in the present invention.The comparing result of table 1 to table 4 show by steel billet carry out plasma cladding processing,
Rail decarburized layer deepness is substantially reduced, and corrosion resisting property improves.
In conclusion the production method of corrosion-resistant rail for high-speed railway provides one kind and has for improving steel in the present invention
While rail corrosion resisting property, the effective ways of rail head of rail decarburized layer deepness are reduced, product is suitable for domestic and international high-speed rail route.
Claims (10)
1. corrosion-resistant rail in high speed railway production method, it is characterised in that: using the rolling waste heat of steel rail rolling, apply to rail
The acceleration cooling down operation of 1-3 DEG C/s recycles heat-treatment of rail waste heat after the heat treatment operation, sprays heat to Rail Surface
Molten zinc liquid.
2. corrosion-resistant rail in high speed railway production method as described in claim 1, it is characterised in that: spray heat to Rail Surface
The coating thickness of molten zinc liquid is 0.1-0.5mm.
3. corrosion-resistant rail in high speed railway production method as claimed in claim 2, it is characterised in that: spray heat to Rail Surface
The spraying temperature of molten zinc liquid is 400-600 DEG C.
4. corrosion-resistant rail in high speed railway production method as claimed in claim 1,2 or 3, it is characterised in that: the rail
It is 0.1-0.9%, Si content be 0.1-0.8%, Mn content is 0.15- that matrixed ingredient percent, which is respectively as follows: C content,
1.2%, Cr≤0.4%, V≤0.020%, Nb≤0.40%, P≤0.025%, S≤0.025%, surplus are Fe and can not keep away
The impurity exempted from.
5. corrosion-resistant rail in high speed railway production method as claimed in claim 1,2 or 3, it is characterised in that: the rail exists
Casting mode when casting are as follows: take low S's to enter furnace molten iron, take high alkalinity refining slag, and whole process protection is poured.
6. corrosion-resistant rail in high speed railway production method as claimed in claim 5, it is characterised in that: institute in the casting process
The carburant used is anthracite and low N alloy.
7. corrosion-resistant rail in high speed railway production method as claimed in claim 5, it is characterised in that: the rail is in casting
LF heating process in, using foaming agent to preventing from contacting and prevent to suck excessive N with air.
8. corrosion-resistant rail in high speed railway production method as claimed in claim 5, it is characterised in that: the rail is after pouring
Obtained slab enters burial pit and carries out slow cooling.
9. corrosion-resistant rail in high speed railway production method as claimed in claim 5, it is characterised in that: the rail is passed through in casting
Heat austenite it is uniform after, carry out tunneling boring efficient dephosphorization using the giant of >=18MPa.
10. corrosion-resistant rail in high speed railway production method as claimed in claim 5, it is characterised in that: steel rail rolling method is
Universal rolling technique.