CN109021335A - A kind of formula of microballoon free foaming acrylonitrile butadiene packing material - Google Patents
A kind of formula of microballoon free foaming acrylonitrile butadiene packing material Download PDFInfo
- Publication number
- CN109021335A CN109021335A CN201810772892.5A CN201810772892A CN109021335A CN 109021335 A CN109021335 A CN 109021335A CN 201810772892 A CN201810772892 A CN 201810772892A CN 109021335 A CN109021335 A CN 109021335A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- microballoon
- limited
- plasticizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of formulas of microballoon free foaming acrylonitrile butadiene packing material.Raw material constituent mass number in the formula are as follows: 100 parts of nitrile rubber, 300 ~ 700 parts of butyl acetate, 30 ~ 50 parts of reinforcing agent, 3 ~ 5 parts of anti-aging agent, 1 ~ 3 part of promotor, 1 ~ 8 part of vulcanizing agent, 5 ~ 15 parts of plasticizer, 3 ~ 15 parts of microballoon foaming agent.Raw material components used in inventive formulation are low in cost, and prepared sealing material is wear-resisting, oil resistant, water resistance are good and environmentally protective, are widely used, have a vast market foreground.
Description
Technical field
The invention belongs to sealing material technical field, in particular to it is a kind of with microballoon foaming agent be main foaming component it is micro-
Ball blown rubber formulation.
Background technique
Nitrile rubber has excellent oil resistivity, wearability, air-tightness, because of the good feature of its physical mechanical property, fourth
Nitrile rubber is often applied in all kinds of oil resistant molded articles.The sealing material prepared by nitrile rubber clad metal sheet that foams has good
Good sealing performance plays a significant role in fields such as automobile oil pan sealing, water pump sealings.But at present used in the country
Such material quality control of foaming agent preparation is bad, and product quality is difficult to ensure.Microballoon foaming agent foam dimensionally stable and sulphur
Change system conformability is good, it is low to require, and is mainly used in frothed latex, such as sofa, mattress are manufactured, but in blown rubber
There is not application.Microballoon foaming agent is successfully applied to nitrile rubber/metal plate free foaming system by the present invention, has prepared hair
Uniform, easily operated foaming system is steeped, the research blank of domestic foaming nitrile rubber sealing plate has been filled up, day can be replaced completely
Sheet and American-European Related product are that the excellent sealing material of one kind has a vast market foreground.
Summary of the invention
The object of the present invention is to provide a kind of formulas of microballoon free foaming acrylonitrile butadiene packing material.
The specific technical proposal is:
A kind of formula of microballoon free foaming acrylonitrile butadiene packing material, raw material constituent mass number in the formula are as follows: butyronitrile rubber
100 parts of glue, 300 ~ 700 parts of butyl acetate, 30 ~ 50 parts of reinforcing agent, 3 ~ 5 parts of anti-aging agent, 1 ~ 3 part of promotor, 1 ~ 8 part of vulcanizing agent,
5 ~ 15 parts of plasticizer, 3 ~ 15 parts of microballoon foaming agent.
The reinforcing agent is but not limited to one of carbon black, white carbon black, zinc oxide and Corvic or a variety of.
The anti-aging agent is but not limited to one of amines antioxidants, ketone amines antioxidants and p phenylenediamine type antioxidant
Or it is a variety of.
The promotor is but not limited to thuriam acceserator, thiazole accelerator, xanthate accelerator and secondary
One of sulfonamides promotor is a variety of.
The vulcanizing agent is but not limited in organic peroxide, insoluble sulfur, aminated compounds and resin curative
It is one or more.
The plasticizer is but not limited to phthalic ester plasticizer, fatty acid ester plasticiser and epoxy ester series and increases
Mould one of agent or a variety of.
The microballoon foaming agent is but not limited to thermoplastic polyurethane microballoon foaming agent, 10 ~ 60 microns of Microsphere Size, foams
Temperature is 130 ~ 190 DEG C, and volume frothing percentage is 60 ~ 200.
Raw material components used in inventive formulation are low in cost, and prepared sealing material is wear-resisting, oil resistant, water resistance
Can be good and environmentally protective, it is widely used, has a vast market foreground.
Detailed description of the invention
Fig. 1 is the scanning electron microscope of sealing material obtained by microballoon blown rubber formulation provided in the embodiment of the present invention 1
Photo.
Fig. 2 is the scanning electron microscope of sealing material obtained by microballoon blown rubber formulation provided in the embodiment of the present invention 4
Photo.
Specific embodiment
Embodiment 1:
A kind of formula of microballoon free foaming acrylonitrile butadiene packing material, raw material constituent mass number in the formula are as follows: butyronitrile rubber
100 parts of glue, 500 parts of butyl acetate, 30 parts of carbon black, 5 parts of zinc oxide, 1 part of insoluble sulfur HD OT20, cumyl peroxide
5 parts, 8 parts of plasticizer DOP dioctyl phthalate, 3 parts of diphenyl-para-phenylene diamine of anti-aging agent N- (1,3- dimethyl) butyl-N'-, promote
1 part of benzothiazole sulfonamide of agent N- cyclohexyl -2-, 0.5 part of dibenzothiazyl disulfide, tetramethylthiuram disulfide
0.5 part, 5 parts of microballoon foaming agent.
Plasticizer mass fraction is lower in the formula, foamed material can not fully wrapped around microballoon foaming agent, to make its pressure
Contracting resilience performance reduces.
Embodiment 2:
A kind of formula of microballoon free foaming acrylonitrile butadiene packing material, raw material constituent mass number in the formula are as follows: butyronitrile rubber
100 parts of glue, 500 parts of butyl acetate, 30 parts of carbon black, 5 parts of zinc oxide, 1 part of insoluble sulfur HD OT20, cumyl peroxide
5 parts, 8 parts of plasticizer DOP dioctyl phthalate, 3 parts of diphenyl-para-phenylene diamine of anti-aging agent N- (1,3- dimethyl) butyl-N'-, promote
Into 1 part of benzothiazole sulfonamide of agent N- cyclohexyl -2-, 0.5 part of dibenzothiazyl disulfide, tetramethylthiuram disulfide
0.5 part, 5 parts of microballoon foaming agent.
It is same as Example 1, in above-mentioned formula gained sealing material can not fully wrapped around microballoon foaming agent, to make its pressure
Contracting resilience performance reduces.
Embodiment 3:
A kind of formula of microballoon free foaming acrylonitrile butadiene packing material, raw material constituent mass number in the formula are as follows: butyronitrile rubber
100 parts of glue, 500 parts of butyl acetate, 30 parts of carbon black, 5 parts of zinc oxide, 1 part of insoluble sulfur HD OT20, cumyl peroxide
5 parts, 8 parts of plasticizer DOP dioctyl phthalate, 3 parts of diphenyl-para-phenylene diamine of anti-aging agent N- (1,3- dimethyl) butyl-N'-, promote
Into 1 part of benzothiazole sulfonamide of agent N- cyclohexyl -2-, 0.5 part of dibenzothiazyl disulfide, tetramethylthiuram disulfide
0.5 part, 5 parts of microballoon foaming agent.
The formula improves plasticizer mass fraction, and foaming agent is fully wrapped around by nitrile rubber, but foaming agent mass fraction
Insufficient, obtained sealing material frothing percentage is lower.
Embodiment 4:
A kind of formula of microballoon free foaming acrylonitrile butadiene packing material, raw material constituent mass number in the formula are as follows: butyronitrile rubber
100 parts of glue, 500 parts of butyl acetate, 30 parts of carbon black, 5 parts of zinc oxide, 1 part of insoluble sulfur HD OT20, cumyl peroxide
5 parts, 8 parts of plasticizer DOP dioctyl phthalate, 3 parts of diphenyl-para-phenylene diamine of anti-aging agent N- (1,3- dimethyl) butyl-N'-, promote
Into 1 part of benzothiazole sulfonamide of agent N- cyclohexyl -2-, 0.5 part of dibenzothiazyl disulfide, tetramethylthiuram disulfide
0.5 part, 5 parts of microballoon foaming agent.
Same as Example 3, above-mentioned formula improves plasticizer mass fraction, and foaming agent is fully wrapped around by nitrile rubber,
Foaming agent mass fraction is improved, frothing percentage is obviously improved, and obtained sealing material compression recovery performance is good, Waterproofing/oilproofing performance,
Tear resistance reaches national quality examination criteria.
Claims (1)
1. a kind of formula of microballoon free foaming acrylonitrile butadiene packing material, it is characterised in that raw material constituent mass part in the formula
Number are as follows: 100 parts of nitrile rubber, 300 ~ 700 parts of butyl acetate, 30 ~ 50 parts of reinforcing agent, 3 ~ 5 parts of anti-aging agent, 1 ~ 3 part of promotor, sulphur
1 ~ 8 part of agent, 5 ~ 15 parts of plasticizer, 3 ~ 15 parts of microballoon foaming agent;
The reinforcing agent is but not limited to one of carbon black, white carbon black, zinc oxide and Corvic or a variety of;
The anti-aging agent is but not limited to one of amines antioxidants, ketone amines antioxidants and p phenylenediamine type antioxidant or more
Kind;
The promotor is but not limited to thuriam acceserator, thiazole accelerator, xanthate accelerator and secondary sulphonyl
One of amine type accelerator is a variety of;
The vulcanizing agent is but not limited to one in organic peroxide, insoluble sulfur, aminated compounds and resin curative
Kind is a variety of;
The plasticizer is but not limited to phthalic ester plasticizer, fatty acid ester plasticiser and epoxy ester series plasticizer
One of or it is a variety of;
The microballoon foaming agent is but not limited to thermoplastic polyurethane microballoon foaming agent, and 10 ~ 60 microns of Microsphere Size, blowing temperature
It is 130 ~ 190 DEG C, volume frothing percentage is 60 ~ 200.