CN109016047A - A kind of production technology of timber - Google Patents
A kind of production technology of timber Download PDFInfo
- Publication number
- CN109016047A CN109016047A CN201810951111.9A CN201810951111A CN109016047A CN 109016047 A CN109016047 A CN 109016047A CN 201810951111 A CN201810951111 A CN 201810951111A CN 109016047 A CN109016047 A CN 109016047A
- Authority
- CN
- China
- Prior art keywords
- door
- timber
- plate
- production technology
- polyvinyl chloride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention proposes a kind of production technology of timber, comprising the following steps: S1, drying of wood blanking, baking is handled after timber is steamed, and makes the moisture content 8 ~ 12% of timber.S2, door-plate processing, carry out engraving for door-plate and scrape, and are laid with a polyvinyl chloride film on door-plate surface later, are then placed in plastics sucking moulding in Packing Machine, door-plate surface is made to be covered with a polyvinyl chloride transparent film layer.S3, group embryo compacting, by wood combination Cheng Menxin, gluing carries out cold pressing pressure maintaining to curable adhesive layer after enclosing door-plate, obtains preliminary molding door leaf.S4, spray painting polishing, paint in door leaf surface, the paint face of out-of-flatness are polished after drying.Door leaf good airproof performance made of the production technology of timber proposed by the present invention has excellent waterproof and dampproof performance, and the case where can prevent season cracking.
Description
Technical field
The present invention relates to a kind of production technologies of timber.
Background technique
Solid Door refers to that the material of production timber is taken from the natural wood or real-wood integrated material of forest.Existing solid wood
Door is process by drying, the processes such as blanking, scrape, mill shape, assembling, polish, painting mostly.Rely primarily on the property of paint
Matter improves the surface property of Solid Door, and since the combination air-tightness of paint and Solid Door is inadequate, door leaf is easy to be influenced by weather,
Lead to season cracking or the mouldy deformation of dampness.
Summary of the invention
In order to overcome the deficiencies of the prior art, the present invention proposes a kind of production technology of timber, manufactured door leaf good airproof performance,
With excellent waterproof and dampproof performance, and the case where season cracking can be prevented.
The present invention proposes a kind of production technology of timber, comprising the following steps:
S1, drying of wood blanking
Baking is handled after timber is steamed, and makes the moisture content 8~12% of timber.
S2, door-plate processing
Door-plate is carried out engraving to scrape, a polyvinyl chloride film is laid on door-plate surface later, is then placed in Packing Machine
Plastics sucking moulding makes door-plate surface be covered with a polyvinyl chloride transparent film layer.
S3, group embryo compacting
By wood combination Cheng Menxin, gluing carries out cold pressing pressure maintaining to curable adhesive layer after enclosing door-plate, obtains preliminary molding
Door leaf.
S4, spray painting polishing
It paints in door leaf surface, the paint face of out-of-flatness is polished after drying.
Further, the polyvinyl chloride film is made of by mass percentage following components: 95.78% polyvinyl chloride tree
Rouge, 4% dioctyl adipate, 0.2% disulfide group acetic acid isooctyl stannous methide, 0.02% colorant.The addition of colorant
Help to adjust the unification of film color.
Further, the temperature of door-plate and polyvinyl chloride film in Packing Machine is 220~226 DEG C, and the plastic uptake time is 80
~90s.
Further, the described cold pressing pressure maintaining operation is carried out using cold press or cold stamping die, the cold pressing time for 12h~
24h。
Beneficial effects of the present invention:
The present invention by forming a fine and close PVC film layer in door-plate surface suction plastic, make door body surface and external environment every
Absolutely, with excellent waterproof and dampproof performance, and the case where prevent season cracking.The present invention is thin using the PVC of special formulation
Film, guarantees the compactness of PVC film layer, and the anti-deformation nature that the film is excellent, and securely adsorbs after door-plate plastics sucking moulding, is not easy
Deformation falls off.
Specific embodiment
As follows in conjunction with specific embodiments, application scheme is further described:
Embodiment 1
A kind of production technology of timber, comprising the following steps:
S1, drying of wood blanking
Baking is handled after timber is steamed, and makes the moisture content 8~12% of timber；
S2, door-plate processing
Door-plate is carried out engraving to scrape, a polyvinyl chloride film is laid on door-plate surface later, is then placed in Packing Machine
Plastics sucking moulding, the temperature in Packing Machine are 220~226 DEG C, and the plastic uptake time is 80~90s.Door-plate surface is set to be covered with a polychlorostyrene
Ethylene transparent film layer.The polyvinyl chloride film is made of by mass percentage following components: 95.78% Corvic,
4% dioctyl adipate, 0.2% disulfide group acetic acid isooctyl stannous methide, 0.02% colorant.
S3, group embryo compacting
By wood combination Cheng Menxin, gluing enclose after door-plate using cold press or cold stamping die carry out cold pressing pressure maintaining 12h~
For 24 hours to curable adhesive layer, preliminary molding door leaf is obtained.
S4, spray painting polishing
It paints in door leaf surface, the paint face of out-of-flatness is polished after drying.
The timber of 1 technique of the present embodiment manufacture and comparative example (timber of PVC free film layer) are compared into test:
1, moisture-proof test
It is higher than 70% in relative humidity, temperature is tested in the environment of being 25 DEG C.
| Water-cut variation | Embodiment 1 (moisture content: %) | Comparative example (moisture content: %) |
| 0 day | 10% | 10% |
| 15 days | 11.5% | 16% |
| 30 days | 12% | 23% |
2, anti-drying cracking test
It is lower than 30% in relative humidity, temperature is tested in the environment of being 35 DEG C.
| Water-cut variation | Embodiment 1 (moisture content: %) | Comparative example (moisture content: %) |
| 0 day | 10% | 10% |
| 15 days | 10% | 8% |
| 30 days | 9% | 5% |
The present invention is being painted by forming a fine and close PVC film layer in door-plate surface suction plastic, make door body surface with
External environment isolation, moisture content are protected from environmental smaller, to guarantee that product has excellent waterproof and dampproof performance, and prevent
The case where season cracking.
It is that above-mentioned preferred embodiment should be regarded as application scheme embodiment for example, all with application scheme thunder
Same, approximate or technology deduction, replacement, improvement for making based on this etc., are regarded as the protection scope of this patent.
Claims (4)
1. a kind of production technology of timber, which comprises the following steps:
S1, drying of wood blanking
Baking is handled after timber is steamed, and makes the moisture content 8~12% of timber；
S2, door-plate processing
Door-plate is carried out engraving to scrape, a polyvinyl chloride film is laid on door-plate surface later, is then placed in plastic uptake in Packing Machine
Molding, makes door-plate surface be covered with a polyvinyl chloride transparent film layer；
S3, group embryo compacting
By wood combination Cheng Menxin, gluing carries out cold pressing pressure maintaining to curable adhesive layer after enclosing door-plate, obtains preliminary molding door leaf；
S4, spray painting polishing
It paints in door leaf surface, the paint face of out-of-flatness is polished after drying.
2. the production technology of timber according to claim 1, which is characterized in that the polyvinyl chloride film is by following components
It forms by mass percentage: 95.78% Corvic, 4% dioctyl adipate, 0.2% disulfide group acetic acid isooctyl two
Methyl tin, 0.02% colorant.
3. the production technology of timber according to claim 2, which is characterized in that door-plate and polyvinyl chloride film are in Packing Machine
In temperature be 220~226 DEG C, the plastic uptake time be 80~90s.
4. the production technology of timber according to claim 1, which is characterized in that the cold pressing pressure maintaining operation is using cold pressing
Machine or cold stamping die carry out, and the cold pressing time is 12h~for 24 hours.