CN109014024A - A kind of antifriction alloy cast(ing) surface processing material - Google Patents
A kind of antifriction alloy cast(ing) surface processing material Download PDFInfo
- Publication number
- CN109014024A CN109014024A CN201811016338.0A CN201811016338A CN109014024A CN 109014024 A CN109014024 A CN 109014024A CN 201811016338 A CN201811016338 A CN 201811016338A CN 109014024 A CN109014024 A CN 109014024A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- ing
- alloy cast
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Material is handled the invention discloses a kind of antifriction alloy cast(ing) surface, and the processing material is by following weight fraction ratio at being grouped as: 2-5 parts of alumina silicate, 2-5 parts of calcium-base bentonite, 5-11 parts of diatomite, 2-5 parts of silica flour, 3-7 parts of olive mountain flour, 1-3 parts of schmigel, 11-14 parts of dextrine powder, 2-5 parts of aluminum sulfate part, 11-13 parts of polyvinyl alcohol, 14-16 parts of brown iron oxide, 7-9 parts of n-octyl alcohol, 6-8 parts of nano-attapulgite, 5-11 parts of plant ash, 2-5 parts of sodium orthophosphate.The present invention effectively increases cast(ing) surface wearability and corrosion resistance, furthermore, the present invention can be while casting, disposably complete the alloy strengthening process on its surface, not only simplify technique, and strengthening layer is made with respect to the wearability of basis material to be about 2-3 times, opposite basis material acid-resistant corrosion is about 5 times.
Description
Technical field
The invention belongs to field of surface treatment more particularly to a kind of antifriction alloy cast(ing) surface to handle material.
Background technique
Casting and daily life have substantial connection, the application especially in agricultural machinery.Agricultural machinery and implement apparatus for work is in work
Chang Huiyu sandy soil directly contact during work, often stone and the grains of sand containing hard particles in sandy soil.Agricultural machinery and implement apparatus for work exists
It is on active service in such environment, by strong abrasive wear, when soil acidity or alkalinity is stronger, to agricultural machinery and implement apparatus for work surface
Corrosivity is also very serious, but also can induce corrosion-abrasion synergy, shortens the service life of agricultural machinery and implement apparatus for work.Agriculture
What equipment apparatus for work surface was subject to wash away, the interaction of corrosion, wear, corrosiveness and attrition and attack, is one
Dynamic process complicated and changeable and strong environmental factor dependence, thus to the performance requirement of agricultural machinery and implement apparatus for work height.
Due to use the materials such as grey white cast-iron, stainless steel to be difficult to meet the requirements under this synergic wear operating condition or at
This is higher, thus generallys use the method for improving the surface abrasion resistance of agricultural machinery and implement apparatus for work.Currently, making to improve agricultural machinery and implement
The surface abrasion resistance of industry device, usually after agricultural machinery and implement apparatus for work casting and forming, then plus one of alloy heat treatment procedure into
Row is strengthened, such as carries out secondary hardening to it using chemical heat treatment method (case-carbonizing, surface carburization).So cause
The complexity of agricultural machinery and implement manufacturing process, in addition some large farm machineries carry out to it secondary hardening technique and guarantee upper inconvenience.
In addition, also having using improving the surface abrasion resistance of agricultural machinery and implement by the way of agricultural machinery and implement surface coating paint, however it is limited to apply
The wear-resisting property of material causes the effect of which not fully up to expectations.
Summary of the invention
It is an object of the invention to overcome problem above of the existing technology, provide at a kind of antifriction alloy cast(ing) surface
Manage material.
To realize above-mentioned technical purpose and the technique effect, the invention is realized by the following technical scheme:
A kind of antifriction alloy cast(ing) surface handles material, and the processing material is by following weight fraction ratio at being grouped as: silicic acid
2-5 parts of aluminium, 2-5 parts of calcium-base bentonite, 5-11 parts of diatomite, 2-5 parts of silica flour, 3-7 parts of olive mountain flour, 1-3 parts of schmigel, paste
11-14 parts of fine powder, 2-5 parts of aluminum sulfate part, 11-13 parts of polyvinyl alcohol, 14-16 parts of brown iron oxide, 7-9 parts of n-octyl alcohol, nanometer is recessed
6-8 parts of convex stick soil, 5-11 parts of plant ash, 2-5 parts of sodium orthophosphate, 1-9 parts of diatomite, 2-7 parts of starch paste, lignin sulfonic acid 2-7
Part, 3-5 parts of sodium carboxymethylcellulose, 4-9 parts of silica solution, 2-4 parts of nanometer scale ceramics powder, 11-21 parts of modified graphene, carboxylic first
Base sodium cellulosate 12-23,4-9 parts of mica powder, 0.5-0.8 parts of ferric oxide red powder, 20-27 parts of two component polyurethane, hollow glass
7-9 parts of microballon, 12-15 parts of triphenyl phosphite, 2-6 parts of phenolic resin, 15-25 parts of acrylic acid modified polyurethane, brown alundum powder
2-4 parts, 11-15 parts of nano-ceramic powder, 5-8 parts of white alundum powder, 1-5 parts of sodium benzoate, 3-7 parts of borosilicic acid rock cenosphere, alcohol
1-5 parts of acid resin, 2-4 parts of aluminum phosphate, 2-11 parts of white glue with vinyl, 9-12 parts of ceramic, 4-11 parts of titanium dioxide, 3-9 parts of curing agent,
3-7 parts of epoxy resin.
Further, the epoxy resin is bisphenol A epoxide resin or glycidyl ester epoxy resin.
Further, the curing agent is the mixture of polyamide curing agent and m-phenylene diamine (MPD) curing agent.
Further, the finish materials further include the ingredient of following weight fraction ratio: micro/nano level tourmaline 10
Part, 5 parts of silica, 5 parts of closed-cell expanded perlite, 6 parts of nano-attapulgite, 15 parts of toluene, 4 parts of ethylbenzene, 4 parts of graphite powder,
5 parts of lignin sulfonic acid, 11 parts of paraxylene.
The beneficial effects of the present invention are:
The present invention effectively increases cast(ing) surface wearability and corrosion resistance, in addition, the present invention can be while casting, once
Property completes the alloy strengthening process on its surface, not only simplifies technique, and make strengthening layer with respect to basis material wearability about
It is 2-3 times, opposite basis material acid-resistant corrosion is about 5 times.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's all other embodiment obtained without creative efforts belongs to the model that the present invention protects
It encloses.
Embodiment 1:
A kind of antifriction alloy cast(ing) surface handles material, and processing material is by following weight fraction ratio at being grouped as: alumina silicate 2
Part, 2 parts of calcium-base bentonite, 5 parts of diatomite, 2 parts of silica flour, 3 parts of olive mountain flour, 1 part of schmigel, 11 parts of dextrine powder, aluminum sulfate
2 parts of part, 11 parts of polyvinyl alcohol, 14 parts of brown iron oxide, 7 parts of n-octyl alcohol, 6 parts of nano-attapulgite, 5 parts of plant ash, sodium orthophosphate 2
Part, 1 part of diatomite, 2 parts of starch paste, 2 parts of lignin sulfonic acid, 3 parts of sodium carboxymethylcellulose, 4 parts of silica solution, nanometer scale ceramics
It is 2 parts of powder, 11 parts of modified graphene, 12 parts of sodium carboxymethylcellulose, 0.5 part of ferric oxide red powder, 20 parts of two component polyurethane, empty
7 parts of heart glass microballoon, 12 parts of triphenyl phosphite, 2 parts of phenolic resin, 15 parts of acrylic acid modified polyurethane, 2 parts of brown alundum powder,
11 parts of nano-ceramic powder, 5 parts of white alundum powder, 1 part of sodium benzoate, 3 parts of borosilicic acid rock cenosphere, 1 part of alkyd resin, aluminum phosphate
2 parts, 2 parts of white glue with vinyl, 9 parts of ceramic, 4 parts of titanium dioxide, 3 parts of curing agent, 3 parts of epoxy resin, epoxy resin is bisphenol-A epoxy
Resin or glycidyl ester epoxy resin, curing agent are the mixture of polyamide curing agent and m-phenylene diamine (MPD) curing agent, surface
Processing material further includes the ingredient of following weight fraction ratio: 10 parts of micro/nano level tourmaline, 5 parts of silica, and closed-cell expanded treasure
5 parts of pearl rock, 6 parts of nano-attapulgite, 15 parts of toluene, 4 parts of ethylbenzene, 4 parts of graphite powder, 5 parts of lignin sulfonic acid, paraxylene 11
Part.
Embodiment 2:
A kind of antifriction alloy cast(ing) surface handles material, and processing material is by following weight fraction ratio at being grouped as: alumina silicate 5
Part, 5 parts of calcium-base bentonite, 11 parts of diatomite, 5 parts of silica flour, 7 parts of olive mountain flour, 3 parts of schmigel, 14 parts of dextrine powder, aluminum sulfate
5 parts of part, 13 parts of polyvinyl alcohol, 16 parts of brown iron oxide, 9 parts of n-octyl alcohol, 8 parts of nano-attapulgite, 11 parts of plant ash, sodium orthophosphate 5
Part, 9 parts of diatomite, 7 parts of starch paste, 7 parts of lignin sulfonic acid, 5 parts of sodium carboxymethylcellulose, 9 parts of silica solution, nanometer scale ceramics
4 parts of powder, 21 parts of modified graphene, sodium carboxymethylcellulose 23,9 parts of mica powder, 0.8 part of ferric oxide red powder, bi-component polyurethane
27 parts of ester, 9 parts of hollow glass micropearl, 15 parts of triphenyl phosphite, 6 parts of phenolic resin, 25 parts of acrylic acid modified polyurethane, palm fibre is just
4 parts of beautiful powder, 15 parts of nano-ceramic powder, 8 parts of white alundum powder, 5 parts of sodium benzoate, 7 parts of borosilicic acid rock cenosphere, alkyd resin 5
Part, 4 parts of aluminum phosphate, 11 parts of white glue with vinyl, 12 parts of ceramic, 11 parts of titanium dioxide, 9 parts of curing agent, 7 parts of epoxy resin, asphalt mixtures modified by epoxy resin
Rouge is bisphenol A epoxide resin or glycidyl ester epoxy resin, and curing agent is polyamide curing agent and m-phenylene diamine (MPD) curing agent
Mixture, finish materials further include the ingredient of following weight fraction ratio: 10 parts of micro/nano level tourmaline, silica 5
Part, 5 parts of closed-cell expanded perlite, 6 parts of nano-attapulgite, 15 parts of toluene, 4 parts of ethylbenzene, 4 parts of graphite powder, lignin sulfonic acid 5
Part, 11 parts of paraxylene.
The present invention effectively increases cast(ing) surface wearability and corrosion resistance, in addition, the present invention can casting while,
The alloy strengthening process for disposably completing its surface, not only simplifies technique, and keeps strengthening layer wear-resisting with respect to basis material
Property be about 2-3 times, opposite basis material acid-resistant corrosion is about 5 times.
In the description of this specification, the description of reference term " one embodiment ", " example ", " specific example " etc. means
Particular features, structures, materials, or characteristics described in conjunction with this embodiment or example are contained at least one implementation of the invention
In example or example.In the present specification, schematic expression of the above terms may not refer to the same embodiment or example.
Moreover, particular features, structures, materials, or characteristics described can be in any one or more of the embodiments or examples to close
Suitable mode combines.
The basic principles, main features and advantages of the present invention have been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.
Claims (4)
1. a kind of antifriction alloy cast(ing) surface handles material, it is characterised in that: the processing material is by following weight fraction ratio
At being grouped as: 2-5 parts of alumina silicate, 2-5 parts of calcium-base bentonite, 5-11 parts of diatomite, 2-5 parts of silica flour, 3-7 parts of olive mountain flour,
It is 1-3 parts of schmigel, 11-14 parts of dextrine powder, 2-5 parts of aluminum sulfate part, 11-13 parts of polyvinyl alcohol, 14-16 parts of brown iron oxide, just pungent
7-9 parts of alcohol, 6-8 parts of nano-attapulgite, 5-11 parts of plant ash, 2-5 parts of sodium orthophosphate, 1-9 parts of diatomite, 2-7 parts of starch paste,
2-7 parts of lignin sulfonic acid, 3-5 parts of sodium carboxymethylcellulose, 4-9 parts of silica solution, 2-4 parts of nanometer scale ceramics powder, modified graphite
11-21 parts of alkene, sodium carboxymethylcellulose 12-23,4-9 parts of mica powder, 0.5-0.8 parts of ferric oxide red powder, two component polyurethane 20-
27 parts, 7-9 parts of hollow glass micropearl, 12-15 parts of triphenyl phosphite, 2-6 parts of phenolic resin, acrylic acid modified polyurethane 15-
25 parts, 2-4 parts of brown alundum powder, 11-15 parts of nano-ceramic powder, 5-8 parts of white alundum powder, 1-5 parts of sodium benzoate, borosilicic acid rock is hollow
3-7 parts of microballon, 1-5 parts of alkyd resin, 2-4 parts of aluminum phosphate, 2-11 parts of white glue with vinyl, 9-12 parts of ceramic, 4-11 parts of titanium dioxide,
3-9 parts of curing agent, 3-7 parts of epoxy resin.
2. a kind of antifriction alloy cast(ing) surface according to claim 1 handles material, it is characterised in that: the epoxy resin
For bisphenol A epoxide resin or glycidyl ester epoxy resin.
3. a kind of antifriction alloy cast(ing) surface according to claim 1 handles material, it is characterised in that: the curing agent is
The mixture of polyamide curing agent and m-phenylene diamine (MPD) curing agent.
4. a kind of antifriction alloy cast(ing) surface according to claim 1 handles material, it is characterised in that: the surface treatment
Material further includes the ingredient of following weight fraction ratio: 10 parts of micro/nano level tourmaline, 5 parts of silica, and closed-cell expanded perlite 5
Part, 6 parts of nano-attapulgite, 15 parts of toluene, 4 parts of ethylbenzene, 4 parts of graphite powder, 5 parts of lignin sulfonic acid, 11 parts of paraxylene.