CN108978297A - A method of using cyanurotriamide modified low formaldehyde emission uf resin continuous-stable papermaking - Google Patents
A method of using cyanurotriamide modified low formaldehyde emission uf resin continuous-stable papermaking Download PDFInfo
- Publication number
- CN108978297A CN108978297A CN201810752857.7A CN201810752857A CN108978297A CN 108978297 A CN108978297 A CN 108978297A CN 201810752857 A CN201810752857 A CN 201810752857A CN 108978297 A CN108978297 A CN 108978297A
- Authority
- CN
- China
- Prior art keywords
- parts
- stage
- prepares
- obtains
- paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of methods using cyanurotriamide modified low formaldehyde emission uf resin continuous-stable papermaking, this method is using 200 parts -220 parts of poplar wood material of preparation by weight, 15 parts -20 parts of talcum powder, 8 parts -10 parts of lime stone, 19 parts -21 parts of acetaldehyde, 5.5 parts -6.5 parts of urea, 12.5 parts -13 parts of melamine, 25 parts -30 parts of peach branch, 2 parts -3 parts of cellulase aqua, 2 parts -3 parts of silicate bacteria microbial inoculum, 5 parts -8 parts of white-rot fungi microbial inoculum, enough potassium hydroxide solutions, enough acetic acid, enough hydrogen peroxide are raw material, process includes 6 steps: raw material prepare, virgin fibers are produced, the processing of cell wall ulceration, gluedization processing, pre-profiling, dry degerming and paper forming processes.The present invention is from a wealth of sources, at low cost, manufacturing process is easily realized, can continuously manufacture, fiber is complete, environmentally protective nuisanceless, fiber yield height, adaptation industrialized mass production, quality are stablized.
Description
Technical field
The present invention relates to pulp technology for making paper more particularly to a kind of cyanurotriamide modified low formaldehyde emission uf resin of use are continuously steady
Determine the method for papermaking.
Background technique
For a long time, paper-making industry is always putative to the destruction and pollution of environment, and is the big row of energy consumption
Industry.A large amount of exhaust gas and waste water can be discharged in the operations such as boiling, bleaching, washing in paper conventional production practices, can seriously pollute
With deteriorate ecological environment, wherein it is poisonous and hazardous with the melamine modified urea-formaldehyde resin that formaldehyde is basic raw material be at present most
Common wet strength agent causes a large amount of pollutions and complete hidden danger.For solve the problems, such as this with long-term existence, it is contour with synthetic resin
Molecular material is primary raw material, and the composite material collectively constituted with certain organic or inorganic particle components is conventional wet strong to replace
The technology of agent is fast-developing.It is answered as Publication No. CN1515739A Chinese patent literature is reported with modified grammite mineral
A kind of compound papermaking material that condensating fiber and 50%-95% plant fiber collectively constitute.Although it uses modified grammite mineral
Fiber is instead of a part of papermaking plant fiber, but essence and operating procedure all still fall within traditional papermaking, cannot still belong to ring
Protect the scope of papermaking.The documents such as CN1378909A and CN1480485A are then reported respectively by polyethylene (PE) and appropriate inorganic
The synthetic paper material of miberal powder or superfine mineral powder composition, CN1381347A are reported with polyethylene (PE) or polypropylene (PP) and nothing
The synthetic paper material of machine miberal powder form, CN1912241A report common by PP, PE or polyvinyl chloride (PVC) and calcium carbonate superfine powder
The synthetic paper material of composition, CN1381521A report the synthetic paper manufacturing method by polyolefin and calcium carbonate superfine powder for filler
Deng.The common ground for the composite material for manufacturing synthetic paper that these documents are reported, is all first by inorganic mineral powder surface
After coupling processing, then by each series lubricant agent, antistatic agent, brighten or colored colorant or light promote degradation agent and matrix tree is added
Rouge utilizes synthesis paper forming device machine-shaping.Thus its common problem is, since the synthetic paper of these materials manufacture does not have hair
Pore and the material that do not absorb water, printability is far short of what is expected compared with wood pulp paper, and for printing, plasticity is extremely low.And contained due to higher
The use of the resin of amount, the recycling that paper is discarded after using is difficult, will cause corresponding pollution to environment, lacks the ring of real meaning
It protects.And if increasing the content of inorganic mineral powder, because the compatibility and dispersibility of inorganic mineral powder and matrix resin are poor, Yi Zao
At surface shedding, printing is influenced, while having an effect on product stability, resistance to tearing and resistance to tortuosity, and when high filler loading capacity, it is right
Equipment and technique are more demanding, and investment is huge, easily more than one hundred million members, and product cost is above plain paper several times, and overall cost is high
In traditional wood pulp paper, competitiveness can not be promoted.Therefore current environment protection method papermaking quality, cost, in terms of all
It is difficult to contend with traditional paper, hinders its production and application.
And environmentally friendly paper technology in the prior art is limited to the missing of technical field and practical experience, currently on the market still
That one kind is not from a wealth of sources, at low cost, manufacturing process is easily realized in detail, can continuously be manufactured, fiber is complete, environmentally protective no public affairs
Evil, fiber yield are high, adapt to the stable papermaking process of industrialized mass production, quality.Therefore it is wide to be badly in need of a kind of source in the market
General, at low cost, manufacturing process is easily realized in detail, can continuously be manufactured, fiber is complete, environmentally protective nuisanceless, fiber yield is high, suitable
The papermaking process for answering industrialized mass production, quality stable.
Summary of the invention
To solve drawbacks described above existing in the prior art, the present invention is intended to provide a kind of from a wealth of sources, at low cost, manufacture
Technique is easily realized in detail, can continuously be manufactured, fiber is complete, environmentally protective nuisanceless, fiber yield height, adaptation industrial mass life
The stable papermaking process of quality.
In order to achieve the above-mentioned object of the invention, the invention adopts the following technical scheme: a kind of use cyanurotriamide modified low aldehyde
The method of Lauxite continuous-stable papermaking, it is characterised in that the following steps are included:
1) raw material prepare
1. basic raw material prepare: by weight preparation 200 parts -220 parts of poplar wood material, 15 parts -20 parts of talcum powder,
8 parts -10 parts of lime stone, 19 parts -21 parts of acetaldehyde, 5.5 parts -6.5 parts of urea, 12.5 parts -13 parts of melamine, 25 part -30 of peach branch
Part;
2. activating adjuvant to prepare: preparing 2 parts -3 parts of cellulase aqua containing mass fraction 1%;
3. microorganism auxiliary material prepares: containing concentration 1 × 107cfu/ml-1×1082 part -3 of the silicate bacteria microbial inoculum of cfu/ml
Part contains concentration 1 × 107cfu/ml-1×1085 parts -8 parts of the white-rot fungi microbial inoculum of cfu/ml;
4. technique auxiliary material prepares: preparing the potassium hydroxide solution, enough acetic acid, enough dioxygens of enough mass concentrations 30%
Water;
2) virgin fibers are produced
1. by the stage 1) the poplar wood material that 1. prepares of step cleans up the wood that rear mechanical slice is thickness 1mm-2mm
Wood chip is soaked after -2 days 1 day and obtains wood chip to be processed by piece;By the stage 1) peach branch that 1. prepares of step obtains after being soaked -10 days 8 days
Must be soaked peach branch;
2. taking out 1. peach branch that step was soaked uses mechanical system break into slag, colloid original slurry material is obtained;
3) cell wall ulceration is handled
1. by the stage 2) in the colloid original slurry material addition that 2. obtains of step water and be tuned into paste, obtain stand-by slurry;
2. the stage 1 is added in 1. stand-by slurry that step obtains) 2. cellulase aqua that step prepares, it is warming up to 25
DEG C -30 DEG C, and 5h-8h is kept, obtain spongiocyte wall ulceration matrix;
4) gluingization is handled
1. by the stage 1) 1. whole acetaldehyde that step prepares, the urea of mass ratio 1/3-2/5, mass ratio 1/3-2/5 three
Poly cyanamid is uniformly mixed, and the stage 1 is added dropwise into mixed liquor) potassium hydroxide solution that 4. prepares of step to pH value 8-9, is warming up to 92
DEG C -98 DEG C, the stage 1 is added dropwise after keeping the temperature 22min-25min) acetic acid that 4. prepares of step, until pH value 5.5-6, continues to keep the temperature
16min-18min;Potassium hydroxide solution is added dropwise again to pH value 6.5-7, then adds urea, the quality of mass ratio 1/3-2/5
Melamine than 1/3-2/5 continues to keep the temperature 42min-45min;Then potassium hydroxide solution is added dropwise to pH value 8-9, adds
Remaining melamine continues to keep the temperature 32min-35min;It is cooled to 55 DEG C -65 DEG C again, remaining urea is added, after continuation of insurance
Warm 15min-18min obtains chemical adhesive;
2. in the stage 3) stage 2 is added in the cell wall ulceration Medium Culture that 2. obtains of step) wood to be processed that 1. obtains of step
Piece, stage 1) 1. chemical adhesive that step the silicate microbial bacterial agent, white-rot fungi microbial inoculum and the step that 3. prepare obtain, is mixed
Merging stirs evenly, and is then sealed processing to mixture, is kept for -8 days 5 days, obtains reaction mixture;
3. the reaction mixture 2. step is sealed after takes out, with the stage 1) the step talcum powder, the lime stone that 1. prepare be mixed
Again using 40 DEG C -50 DEG C slowly drying after closing uniformly, until mixture become include the glue peptone of solid powder, wooden coexist of addling
State obtains stand-by glue solid mixture;
5) pre-profiling
1. by the stage 4) the stand-by binder that 3. obtains of step using pure water rinse to passing through machinery again after no longer weightless
It squeezes the moisture content squeezed out in remaining Solid content and is pressed into thin paper slurry page, obtain body paper base;
2. 1. body paper base that step obtains is used into the stage 1) hydrogen peroxide that 1. prepares of step bleaches to whiteness 65%-
80%, obtain bleaching ground paper;
6) dry degerming and paper forming processes
1. by the stage 5) the bleaching ground paper that obtains is heated to 120 DEG C -130 DEG C, machinery is carried out again after keeping 12min-15min
Press polish and arrangement molding, that is, paper needed for obtaining.
Compared with prior art, by adopting the above-described technical solution, the invention has the following advantages that (1) is different from
Papermaking process in the prior art, wood material of the invention further include peach branch (with the usual fruit tree branch trimmed or fall naturally
Bifurcation, without individually felling, therefore at low cost), since to compare trunk much greater for very thin peach branch specific surface area, it is present in
The natural gum (coming from peach branch) of surface and subsurface is very rich, according to related research, peach branch wooden structures and branch table
It is intradermal that rich in compositions such as galactolipin, rhamnose, phlorose aldehydic acid, adhesivity is high, moisture content is high, hydrophily is high, good toughness, but
Adhesive strength is slightly lower, and using biotechnology, their cell wall is decomposed using cellulase, on the one hand obtains more, living
Property stronger adhesivity substance, be on the one hand polysaccharide (cell wall, cellulose, lignin etc.) by stable cell wall breakdown, be
Later period tackified finish and prevent insect pest and addle (timber easily it is infested and addle on the one hand since it is in neutral environment, another party
Face containing sugared object provides basic nutrients due to cell wall etc. for microorganism and polypide) it lays a solid foundation.(2) work as work
Property sticky matter be sufficiently precipitated after, be added as the wooden original slurry material of matrix, silicate microbial bacterial agent and white-rot fungi microbial inoculum,
All nutrients are decomposed into alcohols sticky matter and acidic materials using white-rot fungi, easily solidify work using silicate microorganism
Property group principle by the adhesivity substance absorption solidification of activation at a grid entirety, increase original strong in succession between each group
Degree;After the adhesivity that is over substance and solidification and bonding, wooden binding force is on the one hand greatly strengthened, water is on the other hand also made
Divide and be sufficiently precipitated, while finally considerably increasing the internal bond strength of paper;On the one hand the sterilization treatment that an apt word added to clinch the point makes partial moisture
On the other hand abjection goes out except the microorganism that can be survived under acidic environment, keeps particieboard more stable.(3) due to wood shavings sheet separation
It inside fills out and is filled with resinae not soluble in water or gummy substance, therefore the paper that the present invention produces is compared to routine techniques papermaking
Water resistance it is more excellent, while whole nontoxic, the anti-corruption of insect prevention, printing performance are excellent.(4) although extracting or dividing from peach branch
Solution obtains more sticky glue substance, but this substance for promoted paper it is wet strong when strong (binding force the is strong) intensity of viscosity it is low
(tearable), thus present invention employs do not have to use in routine techniques using liquid acetaldehyde as the cyanurotriamide modified low of raw material
Aldehyde Lauxite carries out that supplement is glued, and the binding force of this adhesive and cellulose changes compared to the melamine in routine techniques
Property Lauxite want poor, and the paper embrittlement phenomena after gluing is obvious, thus while being used alone does not have use value, but with this
The peach branch organic gel of invention forms good and apparent complementary effect when being used cooperatively, and this material itself and peach branch are organic
Glue can dissolve each other, thus reach few low aldehyde effect using chemical organic gel, and what worth one said is to be different from formaldehyde room temperature
Down it is gaseous state, generally wants use soluble in water, is liquid under acetaldehyde room temperature, does not have to addition aqueous medium in the present invention, thus it is dirty
Dye and consumption reduce and paper degree of purity is more preferable, improves environmental-protecting performance.(5) among other advantages, the present invention is due to having both
The characteristic of toughness glue and brittleness glue, thus the paper produced also has that unit G fineness is thin, soft, color is good, toughness and resistance to
Mill property is strong, has unique resilience, has stronger vertical and horizontal intensity, and stable uniform, moisture absorption is breathed freely and the skill of antibiotic rate
Art effect, with technical purpose perfect matching of the invention.Therefore the present invention is with from a wealth of sources, at low cost, manufacturing process is detailed
It easily realizes, can continuously manufacture, fiber is complete, environmentally protective nuisanceless, fiber yield height, adaptation industrialized mass production, quality
Stable characteristic.
Specific embodiment
Embodiment 1:
A method of using cyanurotriamide modified low formaldehyde emission uf resin continuous-stable papermaking, it is characterised in that including following
Step:
1) raw material prepare
1. basic raw material prepare: by weight preparation poplar wood material 200Kg, talcum powder 20Kg, lime stone 10Kg,
Acetaldehyde 21Kg, urea 6.5Kg, melamine 13Kg, peach branch 30Kg;
2. activating adjuvant to prepare: preparing the cellulase aqua 3Kg containing mass fraction 1%;
3. microorganism auxiliary material prepares: containing concentration 1 × 107cfu/ml-1×108The silicate bacteria microbial inoculum 3Kg of cfu/ml, contain
Concentration 1 × 107cfu/ml-1×108The white-rot fungi microbial inoculum 8Kg of cfu/ml;
4. technique auxiliary material prepares: preparing the potassium hydroxide solution, enough acetic acid, enough dioxygens of enough mass concentrations 30%
Water;
2) virgin fibers are produced
1. by the stage 1) the poplar wood material that 1. prepares of step cleans up the wood that rear mechanical slice is thickness 1mm-2mm
Wood chip is soaked after 2 days and obtains wood chip to be processed by piece;By the stage 1) peach branch that 1. prepares of step obtains the peach that is soaked after being soaked 10 days
Branch;
2. taking out 1. peach branch that step was soaked uses mechanical system break into slag, colloid original slurry material is obtained;
3) cell wall ulceration is handled
1. by the stage 2) in the colloid original slurry material addition that 2. obtains of step water and be tuned into paste, obtain stand-by slurry;
2. the stage 1 is added in 1. stand-by slurry that step obtains) 2. cellulase aqua that step prepares, it is warming up to 30
DEG C, and 8h is kept, obtain spongiocyte wall ulceration matrix;
4) gluingization is handled
1. by the stage 1) 1. whole acetaldehyde that step prepares, the urea of mass ratio 1/3-2/5, mass ratio 1/3-2/5 three
Poly cyanamid is uniformly mixed, and the stage 1 is added dropwise into mixed liquor) potassium hydroxide solution that 4. prepares of step to pH value 8-9, is warming up to 92
DEG C -98 DEG C, the stage 1 is added dropwise after keeping the temperature 22min-25min) acetic acid that 4. prepares of step, until pH value 5.5-6, continues to keep the temperature
16min-18min;Potassium hydroxide solution is added dropwise again to pH value 6.5-7, then adds urea, the quality of mass ratio 1/3-2/5
Melamine than 1/3-2/5 continues to keep the temperature 42min-45min;Then potassium hydroxide solution is added dropwise to pH value 8-9, adds
Remaining melamine continues to keep the temperature 32min-35min;It is cooled to 55 DEG C -65 DEG C again, remaining urea is added, after continuation of insurance
Warm 15min-18min obtains chemical adhesive;
2. in the stage 3) stage 2 is added in the cell wall ulceration Medium Culture that 2. obtains of step) wood to be processed that 1. obtains of step
Piece, stage 1) 1. chemical adhesive that step the silicate microbial bacterial agent, white-rot fungi microbial inoculum and the step that 3. prepare obtain, is mixed
Merging stirs evenly, and is then sealed processing to mixture, is kept for 8 days, obtains reaction mixture;
3. the reaction mixture 2. step is sealed after takes out, with the stage 1) the step talcum powder, the lime stone that 1. prepare be mixed
Again using 40 DEG C -50 DEG C slowly drying after closing uniformly, until mixture become include the glue peptone of solid powder, wooden coexist of addling
State obtains stand-by glue solid mixture;
5) pre-profiling
1. by the stage 4) the stand-by binder that 3. obtains of step using pure water rinse to passing through machinery again after no longer weightless
It squeezes the moisture content squeezed out in remaining Solid content and is pressed into thin paper slurry page and obtain body paper base;
2. 1. body paper base that step obtains is used into the stage 1) hydrogen peroxide that 1. prepares of step bleaches to whiteness 75%-
80%, obtain bleaching ground paper;
6) dry degerming and paper forming processes
1. by the stage 5) the bleaching ground paper that obtains is heated to 120 DEG C -130 DEG C, keep carrying out again after 15min mechanical press polish and
Molding is arranged, that is, paper needed for obtaining.
Embodiment 2
It is whole consistent with embodiment 1, it is in place of difference:
A method of using cyanurotriamide modified low formaldehyde emission uf resin continuous-stable papermaking, it is characterised in that including following
Step:
1) raw material prepare
1. basic raw material prepare: by weight preparation poplar wood material 220Kg, talcum powder 15Kg, lime stone 8Kg,
Acetaldehyde 19Kg, urea 5.5Kg, melamine 12.5Kg, peach branch 25Kg;
2. activating adjuvant to prepare: preparing the cellulase aqua 2Kg containing mass fraction 1%;
3. microorganism auxiliary material prepares: containing concentration 1 × 107cfu/ml-1×108The silicate bacteria microbial inoculum 2Kg of cfu/ml, contain
Concentration 1 × 107cfu/ml-1×108The white-rot fungi microbial inoculum 5Kg of cfu/ml;
2) virgin fibers are produced
1. by the stage 1) the poplar wood material that 1. prepares of step cleans up the wood that rear mechanical slice is thickness 1mm-2mm
Wood chip is soaked after 1 day and obtains wood chip to be processed by piece;By the stage 1) peach branch that 1. prepares of step obtains the peach that is soaked after being soaked 8 days
Branch;
3) cell wall ulceration is handled
2. the stage 1 is added in 1. stand-by slurry that step obtains) 2. cellulase aqua that step prepares, it is warming up to 25
DEG C, and 5h is kept, obtain spongiocyte wall ulceration matrix;
4) gluingization is handled
2. in the stage 3) stage 2 is added in the cell wall ulceration Medium Culture that 2. obtains of step) wood to be processed that 1. obtains of step
Piece, stage 1) 1. chemical adhesive that step the silicate microbial bacterial agent, white-rot fungi microbial inoculum and the step that 3. prepare obtain, is mixed
Merging stirs evenly, and is then sealed processing to mixture, is kept for 5 days, obtains reaction mixture;
5) pre-profiling
2. 1. body paper base that step obtains is used into the stage 1) hydrogen peroxide that 1. prepares of step bleaches to whiteness 65%-
70%, obtain bleaching ground paper;
6) dry degerming and paper forming processes
1. by the stage 5) the bleaching ground paper that obtains is heated to 120 DEG C -130 DEG C, keep carrying out again after 12min mechanical press polish and
Molding is arranged, that is, paper needed for obtaining.
The foregoing description of the disclosed embodiments, only for can be realized professional and technical personnel in the field or use this
Invention.Various modifications to these embodiments will be readily apparent to those skilled in the art, institute herein
The General Principle of definition can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore,
The present invention will not be limited to the embodiments shown herein, and is to fit to special with principles disclosed herein and novelty
The consistent widest scope of point.
Claims (1)
1. a kind of method using cyanurotriamide modified low formaldehyde emission uf resin continuous-stable papermaking, it is characterised in that including following step
It is rapid:
1) raw material prepare
1. basic raw material prepares: preparation 200 parts -220 parts of poplar wood material, 15 parts -20 parts of talcum powder, lime by weight
8 parts -10 parts of stone, 19 parts -21 parts of acetaldehyde, 5.5 parts -6.5 parts of urea, 12.5 parts -13 parts of melamine, 25 parts -30 parts of peach branch;
2. activating adjuvant to prepare: preparing 2 parts -3 parts of cellulase aqua containing mass fraction 1%;
3. microorganism auxiliary material prepares: containing concentration 1 × 107cfu/ml-1×1082 parts -3 parts of the silicate bacteria microbial inoculum of cfu/ml contains
Concentration 1 × 107cfu/ml-1×1085 parts -8 parts of the white-rot fungi microbial inoculum of cfu/ml;
4. technique auxiliary material prepares: preparing the potassium hydroxide solution, enough acetic acid, enough hydrogen peroxide of enough mass concentrations 30%;
2) virgin fibers are produced
1. by the stage 1) the poplar wood material that 1. prepares of step cleans up the wood chip that rear mechanical slice is thickness 1mm-2mm, by
Wood chip obtains wood chip to be processed after being soaked -2 days 1 day;By the stage 1) peach branch that 1. prepares of step steeped after being soaked -10 days 8 days
Send out peach branch;
2. taking out 1. peach branch that step was soaked uses mechanical system break into slag, colloid original slurry material is obtained;
3) cell wall ulceration is handled
1. by the stage 2) in the colloid original slurry material addition that 2. obtains of step water and be tuned into paste, obtain stand-by slurry;
2. the stage 1 is added in 1. stand-by slurry that step obtains) the cellulase aqua that 2. prepares of step, be warming up to 25 DEG C-
30 DEG C, and 5h-8h is kept, obtain spongiocyte wall ulceration matrix;
4) gluingization is handled
1. by the stage 1) 1. whole acetaldehyde that step prepares, the urea of mass ratio 1/3-2/5, mass ratio 1/3-2/5 melamine
Amine is uniformly mixed, and the stage 1 is added dropwise into mixed liquor) potassium hydroxide solution that 4. prepares of step to pH value 8-9, be warming up to 92 DEG C-
98 DEG C, the stage 1 is added dropwise after keeping the temperature 22min-25min) acetic acid that 4. prepares of step, until pH value 5.5-6, continues to keep the temperature 16min-
18min;Potassium hydroxide solution is added dropwise again to pH value 6.5-7, then adds urea, the mass ratio 1/3- of mass ratio 1/3-2/5
2/5 melamine continues to keep the temperature 42min-45min;Then potassium hydroxide solution is added dropwise to pH value 8-9, adds remaining
Melamine continues to keep the temperature 32min-35min;It is cooled to 55 DEG C -65 DEG C again, adds remaining urea, continues to keep the temperature
15min-18min obtains chemical adhesive;
2. in the stage 3) stage 2 is added in the cell wall ulceration Medium Culture that 2. obtains of step) step 1. obtain wood chip to be processed, rank
The section chemical adhesive that 1) 1. 3. silicate microbial bacterial agent, white-rot fungi microbial inoculum and step that step prepares obtain, mixing is simultaneously
It stirs evenly, processing then is sealed to mixture, kept for -8 days 5 days, obtain reaction mixture;
3. the reaction mixture 2. step is sealed after takes out, with the stage 1) the step talcum powder, the lime stone that 1. prepare mix
Again using 40 DEG C -50 DEG C slowly drying after even, until mixture is as including, the glue peptone of solid powder, addle the wooden shape coexisted
State obtains stand-by glue solid mixture;
5) pre-profiling
1. by the stage 4) the stand-by binder that 3. obtains of step using pure water rinse to passing through mechanical presses again after no longer weightless
It squeezes out the moisture content in remaining Solid content and is pressed into thin paper slurry page, obtain body paper base;
2. 1. body paper base that step obtains is used into the stage 1) hydrogen peroxide that 1. prepares of step bleaches to whiteness 65%-
80%, obtain bleaching ground paper;
6) dry degerming and paper forming processes
1. by the stage 5) the bleaching ground paper that obtains is heated to 120 DEG C -130 DEG C, mechanical press polish is carried out again after keeping 12min-15min
It is formed with arranging, that is, paper needed for obtaining.