CN108978043A - A kind of recycling processing technology of waste textile and preparation method thereof - Google Patents
A kind of recycling processing technology of waste textile and preparation method thereof Download PDFInfo
- Publication number
- CN108978043A CN108978043A CN201810862372.3A CN201810862372A CN108978043A CN 108978043 A CN108978043 A CN 108978043A CN 201810862372 A CN201810862372 A CN 201810862372A CN 108978043 A CN108978043 A CN 108978043A
- Authority
- CN
- China
- Prior art keywords
- waste textile
- hot pressing
- recycling
- waste
- processing technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention is a kind of recycling processing technology of waste textile, is made of waste textile processed material and adhesive；Waste textile processed material include cotton fiber, flaxen fiber, woollen goods, chemical fibre class, blended fibre knitwears through crushing be made；Preparation method, including expect, mixed glue, making sheet, finished product, solidification waste textile fiber base cured plate is made.Cured plate of the present invention, simple process, material requested are less, cost is relatively low, are conducive to the recycling of waste textile, reduce the pollution to environment.
Description
Technical field
The present invention relates to waste textile utilization technology fields, and in particular to a kind of recycling of waste textile
Processing technology and preparation method thereof.
Background technique
Waste textile includes waste and old natural cotton fiber and chemical fibre, is usually all as garbage disposal, processing is most
Simple mode is exactly to burn, and is easy pollution air, it is also necessary to a no small processing cost.
If waste and old textile can be recycled, energy consumption is not only saved, it is thus also avoided that a large amount of waste and old spinning
Fabric is as garbage environment pollution.The composition of waste textile currently on the market is complex, and the fiber of composition is also various each
The product for producing and producing also seldom is seen waste textile recycling in sample, the outer market of Now Domestic.
Summary of the invention
For the recycling of waste textile, the present invention provides a kind of making sheet environmental protection, the waste textile of safety are fine
Wiki cured plate and preparation method thereof.
The present invention is achieved by the following technical solutions:
A kind of recycling processing technology of waste textile, which is characterized in that specific steps are as follows:
1) expect: the waste textile raw material of recycling being sent in high-temperature sterilization equipment and is carried out disinfection, by the raw material after disinfection
It is sent to dedicated flaker and waste textile fibre debris is made.
2) it mixes glue: being sufficiently mixed waste textile fibre debris and adhesive by blender.
3) fibre debris and adhesive making sheet: are made by the fiber solidifying plate of primary waste textile by mould shape.
4) finished product: solidification waste textile fiberboard is made by high temperature hot pressing, wherein the hot pressing temperature of high temperature hot pressing machine
For 30-280 degree, hot pressing time -1300 seconds 50 seconds.
The invention has the benefit that by the waste textile fiber treatment of this case and the technique of simple making sheet, production
Fiber solidifying plate manufacture craft out is simple, material requested is also few, and the cured plate that the raw material after the element that disappears is produced is more environmentally friendly, dry
Only, healthy, cost is relatively low for the cotton fiber plate of this programme production, is conducive to the recycling of waste textile, reduces to environment
Pollution.Using high temperature hot pressing technique, increases timber intensity and increase the smoothness of waste textile fiberboard, market prospects
Preferably, the present invention can also plate body as needed difference remove to change the material of required colloid or change part fibre composition to
Preferably improve the applicability of product.
Specific embodiment
The present invention is described in further details below in conjunction with specific embodiment.
A kind of recycling processing technology of waste textile, which is characterized in that specific steps are as follows:
1) expect: the waste textile raw material of recycling being sent in high-temperature sterilization equipment and is carried out disinfection, by the raw material after disinfection
It is sent to dedicated flaker and waste textile fibre debris is made.
2) it mixes glue: being sufficiently mixed waste textile fibre debris and adhesive by blender.
3) fibre debris and adhesive making sheet: are made by the fiber solidifying plate of primary waste textile by mould shape.
4) finished product: solidification waste textile fiberboard is made by high temperature hot pressing, wherein the hot pressing temperature of high temperature hot pressing machine
For 30-280 degree, hot pressing time -1300 seconds 50 seconds.
The above examples are only used to illustrate the technical scheme of the present invention and are not limiting, those of ordinary skill in the art are to this hair
Other modifications or equivalent replacement that bright technical solution is made, as long as it does not depart from the spirit and scope of the technical scheme of the present invention,
It is intended to be within the scope of the claims of the invention.
Claims (1)
1. a kind of recycling processing technology of waste textile, which is characterized in that specific steps are as follows:
1) expect: the waste textile raw material of recycling being sent in high-temperature sterilization equipment and is carried out disinfection, by the raw material after disinfection
It is sent to dedicated flaker and waste textile fibre debris is made；
2) it mixes glue: being sufficiently mixed waste textile fibre debris and adhesive by blender；
3) fibre debris and adhesive making sheet: are made by the fiber solidifying plate of primary waste textile by mould shape；
4) finished product: solidification waste textile fiberboard is made by high temperature hot pressing, wherein the hot pressing temperature of high temperature hot pressing machine is 30-
280 degree, hot pressing time -1300 seconds 50 seconds.