CN108977152A - A kind of epoxy resin dry-hang glue - Google Patents
A kind of epoxy resin dry-hang glue Download PDFInfo
- Publication number
- CN108977152A CN108977152A CN201810914523.5A CN201810914523A CN108977152A CN 108977152 A CN108977152 A CN 108977152A CN 201810914523 A CN201810914523 A CN 201810914523A CN 108977152 A CN108977152 A CN 108977152A
- Authority
- CN
- China
- Prior art keywords
- epoxy resin
- epoxy
- dry
- hang glue
- curing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of epoxy resin dry-hang glues, and including mutually immiscible epoxy resin and epoxy amine curing agent, the epoxy resin has the small molecule monomer of one or more epoxy groups, and the epoxy amine curing agent is polynary amine curing agent.Epoxy resin accounts for the 20-50% of dry-hang glue total weight；Polyamine curing agent accounts for the 10-50% of dry-hang glue total weight.The raw material of the epoxy resin and polyamine curing agent that get colors complementary reconciles mixing, and the color for belonging to respective component disappears, with being mixed into white.When site operation stirs, being disappeared with epoxy resin and polyamine curing agent component colors becomes white as matching ratio, and solidifies at normal temperature.
Description
Technical field
The present invention relates to chemical raw material field, especially a kind of epoxy resin dry-hang glue.
Background technique
Because epoxy resin has excellent physical and chemical properties, shrinking percentage is small when solidifying, with most Building woods
Material has firm binding force, and condition of cure is alternative big.These good characteristics of epoxy resin are applied to it extensively
Electronics field and the field of building materials.
Epoxy resin includes: high performance earth material, the reinforcing of building structure and repairing, structure in the application of building field
The permanent positioning of part is fixed.In processing of stone industry, epoxy resin can be used to repair plate face and outer wall stone wall surface dry-hang part
Fixation glue.
Solidifying for epoxy resin is different from the solidification of common unsaturated polyester resin, and unsaturated polyester resin solidification is to draw
Radical polymerization caused by agent is sent out, epoxy resin cure is then that component directly participates in reacting, and epoxy group forms length in conjunction with amido
The three-dimensional structure of chain.So component is deployed in epoxide equivalent ratio when allotment epoxy resin veneer system, it is finally converted into weight
Amount ratio.In order to obtain the cured product of optimal performance, the mixing of component should be as close possible to specified weight ratio.
When worker deploys epoxy resin dry-hang glue for exterior wall dried hanging firmware at the scene, the usage amount of component is usually to estimate
Taken amount is counted, when estimating that taken amount differs larger with specified ratio, is not only wasted raw material, its performance after the adhesive curing recalled
Also optimum state is not achieved.
Therefore, when finding a kind of allotment of construction at the scene, construction worker can be helped relatively accurately to estimate taken amount, to obtain
The epoxy resin dry-hang glue for obtaining designated ratio as accurate as possible, for guaranteeing that construction quality has important meaning.
Summary of the invention
In order to realize the simple appraisal and mixture of epoxy resin dry-hang glue, the present invention provides a kind of epoxy resin is cladding
Glue, including mutually immiscible epoxy resin and polyamine curing agent.The epoxy resin has one or more epoxy groups
Small molecule monomer.Epoxy resin accounts for the 20-50% of dry-hang glue total weight；Polyamine curing agent accounts for the 10- of dry-hang glue total weight
50%.
Because containing one or more epoxy group three-dimensional netted crosslinking can be generated with polynary amine, it is generally preferable to
Molecular weight of epoxy resin is several hundred to 1,000, and molecular weight of epoxy resin is bigger, and fusing point is higher, and operability is poorer, so epoxy resin
Select the liquid epoxies of small-molecular-weight.It is sweet that the epoxy resin is selected from glycidyl ether type epoxy resin, bisphenol A-type shrinks
Oily ether, glycidyl amine epoxy resin, ethylene oxidic ester epoxy resin, alicyclic ring based epoxy resin are chosen any one kind of them or various kinds of resin is mixed
It closes.
The epoxy hardener is preferable over polyamine curing agent, and polyamine curing agent has the advantages of normal temperature cure, is cured
Colloid is water-fast, acid and alkali-resistance, solvent resistant.And other curing agent such as anhydride curing agent usually wants heating cure, room temperature is difficult to solidify and apply
Work difficulty is big, and it is advantageous in polyamine curing agent.The polynary amine curing agent is selected from aliphatic aminated compounds, alicyclic
Aminated compounds, aromatic amines compound and combination, are such as selected from: ethylenediamine, hexamethylene diamine, diethylenetriamine, triethylene tetramine,
Tetraethylenepentamine, diethylenetriamine=acrylonitrile copolymer, polyetheramine, m-phenylene diamine (MPD), two aminodiphenylmethane, isophorone
Diamines and combinations thereof.Curing agent preferably uses polyamine curing agent, have it is easy for construction, curing performance is excellent, have it is water-fast, it is acidproof
Many advantages, such as alkali, solvent resistant.
The epoxy resin has the small molecule monomer of one or more epoxy groups.The present invention is directed to propose a kind of basis
Principle modulation small-molecular-weight liquid epoxy epoxy resin, the polyamine curing agent of complementary colors are applied to the preparation of stone material dry suspending glue
Technique.It is component A by preparing based on small-molecular-weight liquid epoxies, is that primary raw material preparation is by polyamine curing agent
B component.The color of two components is respectively complementary colours, when with complementary colours component A and B component reach estimated ratio and mix after,
The color for belonging to respective component disappears, and forms the mixture of white.Construction worker can be helped relatively accurately to estimate to take in this way
Amount.A, specific step is as follows for the preparation of B, two components:
Component A includes 20-50 parts of small-molecular-weight liquid epoxies, epoxy active diluent: 3-10 parts；Inert filler:
30-50 parts；White carbon black: 7-10 parts；The organic color of green or the organic color of blue: 0.1-0.5 parts.B component includes polyamine
10-50 parts of diluents of curing agent: 3-10 parts of inert fillers: 30-50 parts；White carbon black: 7-10 parts；Red organic color or yellow
Organic color 0.1-0.5 parts, be white after component A and B component mixing, colloid can be in normal temperature cure and with excellent resistance to
Water, acid and alkali-resistance, solvent-proof performance.
Preferably, the epoxy resin dry-hang glue further includes solvent, auxiliary agent, coupling agent, inert filler.Its proportion is as follows:
Liquid epoxies: 20-50%, epoxy active diluent 3-10%；Inert filler: 30-50%；White carbon black: 7-10%；It is polynary
Amine hardener: 10-50%.
The epoxy active diluent includes butyl glycidyl ether, ethylene glycol diglycidylether, phenyl glycidyl
Ether, the glycidol ether of some single active groups and multi-active base group such as glycidyl ether.
The inert filler include powdered whiting, talcum powder, silicon powder, kaolin, aluminium hydroxide, light calcium, etc. one
A little inorganic fillers, above-described white carbon black include the white carbon black of vapor phase method and the white carbon black of sedimentation.
The color is all Britain's SWADA Si Wada fluorescent pigment, the Stirling Britain Sterling210 line fluorescent face
Material, South Korea's rising sun is at fluorescent pigment or other commercially available fluorescent pigments.
Compared with prior art, epoxy resin dry-hang glue of the present invention, passes through preferred epoxy and epoxy hardener
It is mutually mixed, epoxy resin selects the liquid epoxies of small-molecular-weight, the preferred polyamine curing agent of epoxy hardener, curability
Can be excellent, there is water-fast, acid and alkali-resistance, solvent resistant and other effects.By the way that, at white, site operation stirs after the allotment mixing of the two component
When, being disappeared with epoxy resin and polyamine curing agent component colors as white is matching ratio, it can be achieved that simply estimating and mixing
Match, and solidify at normal temperature, the epoxy resin dry-hang glue of function admirable is obtained, in bending elastic modulus, compression shear strength, Re Chu
It is superior to existing epoxy resin dry-hang glue in the performance indicators such as reason, Frozen-thawed cycled, realizes that compounding is simple, has excellent performance, can grasp
The property made is strong and other effects.
Specific embodiment
The present invention provides a kind of epoxy resin dry-hang glues, including mutually immiscible epoxy resin and epoxy amine curing agent.
The preferred polyamine curing agent of epoxy amine curing agent, epoxy resin account for the 20-50% of dry-hang glue total weight；Polyamine curing agent accounts for dry
The 10-50% of kiss-coating total weight.
The epoxy resin dry-hang glue further includes solvent, auxiliary agent, coupling agent, inert filler.Its proportion is as follows: liquid epoxy
Resin: 20-50%, epoxy active diluent 3-10%；Inert filler: 30-50%；White carbon black: 7-10%；Polynary amine curing
Agent: 10-50%.
Wherein, the epoxy resin has the small molecule monomer of one or more epoxy groups.It preferably is selected from glycidol ether
Based epoxy resin, bisphenol A-type glycidol ether, glycidyl amine epoxy resin, ethylene oxidic ester epoxy resin, alicyclic ring class epoxy
Resin or mixture including at least one aforementioned epoxy resins.
The polynary amine curing agent is selected from aliphatic aminated compounds, alicyclic amines compound, aromatic amines chemical combination
Object and combination, are such as selected from: ethylenediamine, hexamethylene diamine, diethylenetriamine, triethylene tetramine, tetraethylenepentamine, diethylenetriamine=
Acrylonitrile copolymer, polyetheramine, m-phenylene diamine (MPD), two aminodiphenylmethane, isophorone diamine and combinations thereof.
The epoxy active diluent includes butyl glycidyl ether, ethylene glycol diglycidylether, phenyl glycidyl
Ether, the glycidol ether of some single active groups and multi-active base group such as glycidyl ether.
The inert filler include powdered whiting, talcum powder, silicon powder, kaolin, aluminium hydroxide, light calcium, etc. one
A little inorganic fillers, above-described white carbon black include the white carbon black of vapor phase method and the white carbon black of sedimentation.
The color is all Britain's SWADA Si Wada fluorescent pigment, the Stirling Britain Sterling210 line fluorescent face
Material, South Korea's rising sun is at fluorescent pigment or other commercially available fluorescent pigments.
Embodiment 1
Epoxy dry-hang glue is divided into component A and B component, is component A by preparing based on small-molecular-weight liquid epoxies, by
Polyamine curing agent is that primary raw material preparation is B component.A, specific step is as follows for the preparation of B, two components:
Component A includes 20 parts of the 828 small-molecular-weight liquid epoxies of epoxy resin of Sanmu Group Corp, Jiangsu, and epoxy is living
Property diluent be commercially available phenyl glycidyl ether: 5 parts, inert filler be 1000 mesh calcium carbonate: 25 parts, white carbon black be Degussa A-
200 gas-phase silicas: 7 parts, Britain's SWADA Si Wada fluorescence green: 0.1 part.Asphalt mixtures modified by epoxy resin is sequentially added under normal temperature and pressure conditions
Rouge, epoxy active diluent, filler, white carbon black, fluorescence green simultaneously disperse 30 minutes under conditions of 200 turns, and observe scattered
Either with or without particle, pigment is either with or without being uniformly dispersed.Until there is no particle, until pigment is uniformly dispersed.
B component is the IPDA curing agent of ten thousand China's chemistry: 10 parts；Benzyl alcohol: 3 parts；1000 mesh calcium carbonate: 30 parts；Degussa
A-200 gas-phase silica: 7 parts；0.1 part of Britain's SWADA Si Wada fluorescein.Sequentially add under normal temperature and pressure conditions IPDA,
Benzyl alcohol, filler, white carbon black, fluorescein are simultaneously dispersed 30 minutes under conditions of 200 turns, and observe it is scattered either with or without particle,
Pigment is either with or without being uniformly dispersed.Until there is no particle, until pigment is uniformly dispersed.
Embodiment 2
Component A includes 25 parts of the 828 small-molecular-weight liquid epoxies of epoxy resin of Sanmu Group Corp, Jiangsu, and epoxy is living
Property diluent is commercially available phenyl glycidyl ether: 4 parts of inert fillers are 1000 mesh calcium carbonate: 25 parts of white carbon blacks are Degussa A-
200 gas-phase silicas: 8 parts, 0.1 part of Britain's SWADA Si Wada fluorescence green.Asphalt mixtures modified by epoxy resin is sequentially added under normal temperature and pressure conditions
Rouge, epoxy active diluent, filler, white carbon black, fluorescence green simultaneously disperse 30 minutes under conditions of 200 turns, and observe scattered
Either with or without particle, pigment is either with or without being uniformly dispersed.Until there is no particle, until pigment is uniformly dispersed.
B component is the IPDA curing agent of ten thousand China's chemistry: 11 parts；Benzyl alcohol: 3 parts；1000 mesh calcium carbonate: 30 parts；Degussa
A-200 gas-phase silica: 8 parts；Britain's SWADA Si Wada fluorescein: 0.1 part.Sequentially add under normal temperature and pressure conditions IPDA,
Benzyl alcohol, filler, white carbon black, fluorescein are simultaneously dispersed 30 minutes under conditions of 200 turns, and observe it is scattered either with or without particle,
Pigment is either with or without being uniformly dispersed.Until there is no particle, until pigment is uniformly dispersed.
Embodiment 3
Component A includes 20 parts of the 828 small-molecular-weight liquid epoxies of epoxy resin of Sanmu Group Corp, Jiangsu, and epoxy is living
Property diluent be commercially available phenyl glycidyl ether: 5 parts；Inert filler is 1000 mesh calcium carbonate: 30 parts；White carbon black is Degussa A-
200 gas-phase silicas: 8 parts, 0.1 part of Britain's SWADA Si Wada fluorescence green.Asphalt mixtures modified by epoxy resin is sequentially added under normal temperature and pressure conditions
Rouge, epoxy active diluent, filler, white carbon black, fluorescence green simultaneously disperse 30 minutes under conditions of 200 turns, and observe scattered
Either with or without particle, pigment is either with or without being uniformly dispersed.Until there is no particle, until pigment is uniformly dispersed.
B component is the IPDA curing agent of ten thousand China's chemistry: 10 parts；Benzyl alcohol: 3 parts；1000 mesh calcium carbonate: 30 parts；Degussa
A-200 gas-phase silica: 8 parts；0.1 part of Britain's SWADA Si Wada fluorescein.Sequentially add under normal temperature and pressure conditions IPDA,
Benzyl alcohol, filler, white carbon black, fluorescein are simultaneously dispersed 30 minutes under conditions of 200 turns, and observe it is scattered either with or without particle,
Pigment is either with or without being uniformly dispersed.Until there is no particle, until pigment is uniformly dispersed.
Embodiment 4
Component A includes 40 parts of the 828 small-molecular-weight liquid epoxies of epoxy resin of Sanmu Group Corp, Jiangsu, and epoxy is living
Property diluent be commercially available phenyl glycidyl ether: 5 parts；Inert filler is 1000 mesh calcium carbonate: 25 parts；White carbon black is Degussa A-
200 gas-phase silicas: 10 parts, 0.1 part of Britain's SWADA Si Wada fluorescence green.Asphalt mixtures modified by epoxy resin is sequentially added under normal temperature and pressure conditions
Rouge, epoxy active diluent, filler, white carbon black, fluorescence green simultaneously disperse 30 minutes under conditions of 200 turns, and observe scattered
Either with or without particle, pigment is either with or without being uniformly dispersed.Until there is no particle, until pigment is uniformly dispersed.
B component is the IPDA curing agent of ten thousand China's chemistry: 15 parts of benzyl alcohols: 3 parts；1000 mesh calcium carbonate: 30 parts；Degussa A-
200 gas-phase silicas: 10 parts；0.1 part of Britain's SWADA Si Wada fluorescein.IPDA, benzene are sequentially added under normal temperature and pressure conditions
Methanol, filler, white carbon black, fluorescein are simultaneously dispersed 30 minutes under conditions of 200 turns, and are observed scattered either with or without particle, face
Material is either with or without being uniformly dispersed.Until there is no particle, until pigment is uniformly dispersed.
The epoxy dry-hang glue various aspects of performance prepared according to 1-embodiment of above embodiments 4 and national Its Relevant Technology Standards
It is compared as follows table:
Examined project is according to (dry-hang stone curtain wall epoxy cementing agent) JC 887-2001
According to upper table: epoxy resin dry-hang glue properties of the invention are significantly better than national standard.
Above-mentioned technical proposal only embodies the optimal technical scheme of technical solution of the present invention, those skilled in the art
The principle of the present invention is embodied to some variations that some of them part may be made, belongs to the scope of protection of the present invention it
It is interior.
Claims (10)
1. a kind of epoxy resin dry-hang glue, it is characterised in that: including mutually immiscible epoxy resin and epoxy hardener, the ring
Oxygen resin has the small molecule monomer of one or more epoxy groups.
2. epoxy resin dry-hang glue according to claim 1, it is characterised in that: the epoxy hardener is solid for polynary amine
Agent.
3. epoxy resin dry-hang glue according to claim 2, it is characterised in that: epoxy resin accounts for dry-hang glue total weight
20-50%；Polyamine curing agent accounts for the 10-50% of dry-hang glue total weight.
4. epoxy resin dry-hang glue according to claim 1, it is characterised in that: the epoxy resin dry-hang glue further includes molten
Agent, auxiliary agent, coupling agent, inert filler.
5. epoxy resin dry-hang glue according to claim 4, it is characterised in that: liquid epoxies: 20-50%, epoxy
Reactive diluent 3-10%；Inert filler: 30-50%；White carbon black: 7-10%；Polyamine curing agent: 10-50%.
6. epoxy resin dry-hang glue according to claim 1, it is characterised in that: the epoxy resin is selected from glycidol ether
Based epoxy resin, bisphenol A-type glycidol ether, glycidyl amine epoxy resin, ethylene oxidic ester epoxy resin, alicyclic ring class epoxy
It chooses any one kind of them in resin or the mixture of a variety of epoxy resin.
7. epoxy resin dry-hang glue according to claim 2, it is characterised in that: the polynary amine curing agent is selected from fat
Race's aminated compounds, alicyclic amines compound, aromatic amines compound and combination.
8. epoxy resin dry-hang glue according to claim 7, it is characterised in that: the polynary amine curing agent is selected from: second
Diamines, hexamethylene diamine, diethylenetriamine, triethylene tetramine, tetraethylenepentamine, diethylenetriamine=acrylonitrile copolymer, polyetheramine,
M-phenylene diamine (MPD), two aminodiphenylmethane, isophorone diamine and combinations thereof.
9. epoxy resin dry-hang glue according to claim 1, it is characterised in that: the epoxy resin and epoxy hardener point
Not Wei different colours, and be complementary colours, epoxy resin dry-hang glue allotment is mixed into white.
10. epoxy resin dry-hang glue according to claim 8, it is characterised in that: the epoxy resin can be green, blue
Other colors that color or green and blue mixing generate；Epoxy hardener can be red, and yellow or the mixing of red and yellow produce
Other raw colors.