CN108977076A - A kind of wood guitar maintaining agent preparation method - Google Patents
A kind of wood guitar maintaining agent preparation method Download PDFInfo
- Publication number
- CN108977076A CN108977076A CN201810747045.3A CN201810747045A CN108977076A CN 108977076 A CN108977076 A CN 108977076A CN 201810747045 A CN201810747045 A CN 201810747045A CN 108977076 A CN108977076 A CN 108977076A
- Authority
- CN
- China
- Prior art keywords
- maintaining agent
- agent preparation
- guitar
- wooden guitar
- wood guitar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wooden guitar maintaining agent preparation methods, are made of deionized water, kaolin, Sucrose Fatty Acid Ester, diatomite, sodium molybdate, paraffin, ammonium polyacrylate, aqueous acrylic emulsion；Compared with prior art, the lotion maintaining agent of formula support of the invention, it is directed to the wooden guitar maintenance of no lacquer painting, the surface damp-proof and moth-proof of the wooden guitar timber can effectively be prevented, improve the service life of the wooden guitar timber, when use only needs to be coated on wooden guitar surface, then with cloth wiped clean, it is easy to use, it has the value of popularization and application.
Description
Technical field
The present invention relates to a kind of musical instrument care products more particularly to a kind of wooden guitar maintaining agent preparation methods.
Background technique
The wooden guitar is exactly the acoustic guitar of here, it may be said that for being opposite electric guitar and bass, not over effect
Fruit device and pure earthquake motion sounding.In the prior art, also there is part on the most baking vanish surface in the surface of the wooden guitar without baking vanish surface,
The tone color of the wooden guitar without baking vanish surface is preferable, and thus one, the wooden of the wooden guitar on no baking vanish surface is easy for damaging, and
Not humidity etc., accordingly, there exist rooms for improvement.
Summary of the invention
The object of the invention is that providing a kind of wooden guitar maintaining agent preparation method to solve the above-mentioned problems.
The present invention through the following technical solutions to achieve the above objectives:
The present invention is by deionized water, kaolin, Sucrose Fatty Acid Ester, diatomite, sodium molybdate, paraffin, ammonium polyacrylate, aqueous acrylamide
Yogurt liquid is made；
Preparation method the following steps are included:
(1) deionized water, kaolin, Sucrose Fatty Acid Ester, diatomite, sodium molybdate, paraffin are added in stirred tank and are heated to 90-
100 DEG C, constant temperature stirring is carried out after material dissolution；
(2) ammonium polyacrylate is added, aqueous acrylic emulsion continues to stir, cooling in merging mold after mixing evenly
It solidifies blocking to get finished product.
Preferably, the mixing speed of the step (1) is 400-600r/min.The mixing time of the step (1) is 10-
20min。
Preferably, the mixing speed of the step (2) is 200-300r/min.The mixing time of the step (2) is 10-
15min。
Preferably, by weight, contain the deionized water 3%, the kaolin 2%, the Sucrose Fatty Acid Ester 6%, institute for every part
State diatomite 3%, the sodium molybdate 2%, the paraffin 75%, the ammonium polyacrylate 2%, the aqueous acrylic emulsion
5%.
The beneficial effects of the present invention are:
The present invention is a kind of wooden guitar maintaining agent preparation method, compared with prior art, the cream of formula support of the invention
Body maintaining agent is directed to the wooden guitar maintenance of no lacquer painting, can effectively prevent the surface damp-proof and moth-proof of the wooden guitar timber, improve
The service life of the wooden guitar timber, when use, only need to be coated on wooden guitar surface, then with cloth wiped clean, user
Just, it has the value of popularization and application.
Specific embodiment
The invention will be further described below:
The present invention is by deionized water, kaolin, Sucrose Fatty Acid Ester, diatomite, sodium molybdate, paraffin, ammonium polyacrylate, aqueous acrylamide
Yogurt liquid is made；
Preparation method the following steps are included:
(3) deionized water, kaolin, Sucrose Fatty Acid Ester, diatomite, sodium molybdate, paraffin are added in stirred tank and are heated to 90-
100 DEG C, constant temperature stirring is carried out after material dissolution；
(4) ammonium polyacrylate is added, aqueous acrylic emulsion continues to stir, cooling in merging mold after mixing evenly
It solidifies blocking to get finished product.
Preferably, the mixing speed of the step (1) is 400-600r/min.The mixing time of the step (1) is 10-
20min。
Preferably, the mixing speed of the step (2) is 200-300r/min.The mixing time of the step (2) is 10-
15min。
Preferably, by weight, contain the deionized water 3%, the kaolin 2%, the Sucrose Fatty Acid Ester 6%, institute for every part
State diatomite 3%, the sodium molybdate 2%, the paraffin 75%, the ammonium polyacrylate 2%, the aqueous acrylic emulsion
5%.
Basic principles and main features and advantages of the present invention of the invention have been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (6)
1. a kind of wood guitar maintaining agent preparation method, it is characterised in that: by deionized water, kaolin, Sucrose Fatty Acid Ester, diatomite, molybdenum
Sour sodium, paraffin, ammonium polyacrylate, aqueous acrylic emulsion are made；
Preparation method the following steps are included:
(1) deionized water, kaolin, Sucrose Fatty Acid Ester, diatomite, sodium molybdate, paraffin are added in stirred tank and are heated to 90-100 DEG C,
Constant temperature stirring is carried out after material dissolution；
(2) addition ammonium polyacrylate, aqueous acrylic emulsion continue to stir, and are placed in cooled and solidified in mold after mixing evenly
It is blocking to get finished product.
2. wood guitar maintaining agent preparation method according to claim 1, it is characterised in that: the stirring speed of the step (1)
Degree is 400-600r/min.
3. wood guitar maintaining agent preparation method according to claim 1, it is characterised in that: when the stirring of the step (1)
Between be 10-20min.
4. wood guitar maintaining agent preparation method according to claim 1, it is characterised in that: the stirring speed of the step (2)
Degree is 200-300r/min.
5. wood guitar maintaining agent preparation method according to claim 1, it is characterised in that: when the stirring of the step (2)
Between be 10-15min.
6. wood guitar maintaining agent preparation method according to claim 1, it is characterised in that: by weight, every part containing described
Deionized water 3%, the kaolin 2%, the Sucrose Fatty Acid Ester 6%, the diatomite 3%, the sodium molybdate 2%, the paraffin
75%, the ammonium polyacrylate 2%, the aqueous acrylic emulsion 5%.