CN108976641A - A kind of environment friendly plastic rubber floor and its manufacturing method - Google Patents
A kind of environment friendly plastic rubber floor and its manufacturing method Download PDFInfo
- Publication number
- CN108976641A CN108976641A CN201810489458.6A CN201810489458A CN108976641A CN 108976641 A CN108976641 A CN 108976641A CN 201810489458 A CN201810489458 A CN 201810489458A CN 108976641 A CN108976641 A CN 108976641A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment friendly
- plastic rubber
- rubber floor
- friendly plastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environment friendly plastic rubber floor, the environment friendly plastic rubber floor is made from the following raw materials in parts by weight: 70-80 parts of calcium carbonate, PVC50-55 parts, 20-30 parts of polyaminoester emulsion, 30-35 parts of ethylene glycol ether ester, 15-20 parts of butyl acetate, 20-25 parts of maleic anhydride, 15-25 parts of biomass vegetable oil, 5-10 parts of nano silica, 5-10 parts of chitin, 5-10 parts of calcium carbonate, 3-5 parts of anti-aging agent, 3-5 parts of crosslinking agent.Environment-friendly type plastic adhesive floor of the present invention has preferable flexibility, light resistance, weatherability, nontoxic, degradable, and plastic floor raw material of the invention is cheap, simple process, is suitable for heavy industrialization and uses, practical.
Description
Technical field
The present invention relates to plastic material technical field, in particular to a kind of environment friendly plastic rubber floor and its manufacturing method.
Background technique
Plastic floor i.e. PVC floor, main component are pvc material.PVC floor since its pattern is abundant,
Color is various and is widely used in the various aspects with business at home.Plastic floor is that popular one kind is novel in the world today
Light body floor decorative material, also referred to as " light body material ", are a kind of products very popular in American-European and Asia Japan and Korea S, fashionable
Foreign countries initially enter Chinese market from the beginning of the eighties, and big and medium-sized cities at home have obtained universal approval so far, and use is non-
It is often extensive, such as the various fields such as indoor family, hospital, school, office building, factory, public place, supermarket, business, stadiums
Institute.
In existing plastic floor, plasticizer generallys use dioctyl phthalate (DOP) or terephthalic acid (TPA) two
Monooctyl ester (DOTP).Wherein, dioctyl phthalate is more toxic, and degradation capability is very low, is easy after plastic floor is discarded
Cause environmental pollution；Dioctyl terephthalate toxicity is lower, relatively safety, but equally exists that degradation capability is lower to ask
Topic, equally pollutes the environment for this purpose, it is proposed that a kind of environment friendly plastic rubber floor and its manufacturing method.
Summary of the invention
The main purpose of the present invention is to provide a kind of environment friendly plastic rubber floor and its manufacturing methods, can effectively solve background
The problems in technology.
To achieve the above object, the technical scheme adopted by the invention is as follows:
A kind of environment friendly plastic rubber floor and its manufacturing method, the environment friendly plastic rubber floor are made from the following raw materials in parts by weight: carbonic acid
70-80 parts of calcium, PVC50-55 parts, 20-30 parts of polyaminoester emulsion, 30-35 parts of ethylene glycol ether ester, butyl acetate 15-20
Part, 20-25 parts of maleic anhydride, 15-25 parts of biomass vegetable oil, 5-10 parts of nano silica, 5-10 parts of chitin, carbon
Sour calcium 5-10 parts, 3-5 parts of anti-aging agent, 3-5 parts of crosslinking agent.
A kind of manufacturing method on environment friendly plastic rubber floor, comprising the following steps:
(1), each raw material for standby is weighed according to parts by weight；
(2), step (1) is weighed into obtain each interior progress calendering process processing of raw material addition kneading machine, controlling kneading machine temperature is
150-180 DEG C, mixing time is 60-80 minutes；
(3), it will be cooled to 60-70 DEG C by the material being kneaded, is then rolled using tri-roll press machine, wherein upper roll temperature
It is 155-165 DEG C, middle roll temperature is 170-180 DEG C, and lower roll temperatures are 150-160 DEG C；
(4), the product that calendering machining obtains is subjected to cooling, formed, both obtain finished product.
Compared with prior art, the invention has the following beneficial effects: environment-friendly type plastic adhesive floors of the present invention to have preferably
Flexibility, light resistance, weatherability, nontoxic, degradable, plastic floor raw material of the invention is cheap, simple process, is suitable for extensive
Industrialization is used, practical.
Specific embodiment
Embodiment 1
A kind of environment friendly plastic rubber floor, the environment friendly plastic rubber floor are made from the following raw materials in parts by weight: 70 parts of calcium carbonate, PVC50
Part, 20 parts of polyaminoester emulsion, 30 parts of ethylene glycol ether ester, 15 parts of butyl acetate, 20 parts of maleic anhydride, biomass are planted
Object oil 15 parts, 5 parts of nano silica, 5 parts of chitin, 5 parts of calcium carbonate, 3 parts of anti-aging agent, 3 parts of crosslinking agent.
A kind of manufacturing method on environment friendly plastic rubber floor, comprising the following steps:
(1), each raw material for standby is weighed according to parts by weight；
(2), step (1) is weighed into obtain each interior progress calendering process processing of raw material addition kneading machine, control kneading machine temperature is 150
DEG C, mixing time is 60 minutes；
(3), 60 DEG C will be cooled to by the material being kneaded, be then rolled using tri-roll press machine, wherein upper roll temperature is
155 DEG C, middle roll temperature is 170 DEG C, and lower roll temperatures are 150 DEG C；
(4), the product that calendering machining obtains is subjected to cooling, formed, both obtain finished product.
Embodiment 2
A kind of environment friendly plastic rubber floor, the environment friendly plastic rubber floor are made from the following raw materials in parts by weight: 75 parts of calcium carbonate, PVC53
Part, 25 parts of polyaminoester emulsion, 33 parts of ethylene glycol ether ester, 18 parts of butyl acetate, 23 parts of maleic anhydride, biomass are planted
Object oil 20 parts, 8 parts of nano silica, 8 parts of chitin, 8 parts of calcium carbonate, 4 parts of anti-aging agent, 4 parts of crosslinking agent.
A kind of manufacturing method on environment friendly plastic rubber floor, comprising the following steps:
(1), each raw material for standby is weighed according to parts by weight；
(2), step (1) is weighed into obtain each interior progress calendering process processing of raw material addition kneading machine, control kneading machine temperature is 160
DEG C, mixing time is 70 minutes；
(3), 65 DEG C will be cooled to by the material being kneaded, be then rolled using tri-roll press machine, wherein upper roll temperature is
160 DEG C, middle roll temperature is 175 DEG C, and lower roll temperatures are 155 DEG C；
(4), the product that calendering machining obtains is subjected to cooling, formed, both obtain finished product.
Embodiment 3
A kind of environment friendly plastic rubber floor, the environment friendly plastic rubber floor are made from the following raw materials in parts by weight: 80 parts of calcium carbonate, PVC55
Part, 30 parts of polyaminoester emulsion, 35 parts of ethylene glycol ether ester, 20 parts of butyl acetate, 25 parts of maleic anhydride, biomass are planted
Object oil 25 parts, 10 parts of nano silica, 10 parts of chitin, 10 parts of calcium carbonate, 5 parts of anti-aging agent, 5 parts of crosslinking agent.
A kind of manufacturing method on environment friendly plastic rubber floor, comprising the following steps:
(1), each raw material for standby is weighed according to parts by weight；
(2), step (1) is weighed into obtain each interior progress calendering process processing of raw material addition kneading machine, control kneading machine temperature is 180
DEG C, mixing time is 80 minutes；
(3), 70 DEG C will be cooled to by the material being kneaded, be then rolled using tri-roll press machine, wherein upper roll temperature is
165 DEG C, middle roll temperature is 180 DEG C, and lower roll temperatures are 160 DEG C；
(4), the product that calendering machining obtains is subjected to cooling, formed, both obtain finished product.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (2)
1. a kind of environment friendly plastic rubber floor, which is characterized in that the environment friendly plastic rubber floor is made from the following raw materials in parts by weight: carbonic acid
70-80 parts of calcium, PVC50-55 parts, 20-30 parts of polyaminoester emulsion, 30-35 parts of ethylene glycol ether ester, butyl acetate 15-20
Part, 20-25 parts of maleic anhydride, 15-25 parts of biomass vegetable oil, 5-10 parts of nano silica, 5-10 parts of chitin, carbon
Sour calcium 5-10 parts, 3-5 parts of anti-aging agent, 3-5 parts of crosslinking agent.
2. a kind of manufacturing method on environment friendly plastic rubber floor, it is characterised in that the following steps are included:
(1) each raw material for standby is weighed according to parts by weight；
(2) step (1) is weighed into obtain each interior progress calendering process processing of raw material addition kneading machine, control kneading machine temperature is 150-
180 DEG C, mixing time is 60-80 minutes；
(3) it will be cooled to 60-70 DEG C by the material being kneaded, is then rolled using tri-roll press machine, wherein upper roll temperature
It is 155-165 DEG C, middle roll temperature is 170-180 DEG C, and lower roll temperatures are 150-160 DEG C；
(4) product that calendering machining obtains is subjected to cooling, formed, both obtain finished product.