CN108976220A - The conjugated compound of the formula dibenzo heptene thioxanthene of spiral shell containing 9,9- and preparation and application - Google Patents
The conjugated compound of the formula dibenzo heptene thioxanthene of spiral shell containing 9,9- and preparation and application Download PDFInfo
- Publication number
- CN108976220A CN108976220A CN201810870156.3A CN201810870156A CN108976220A CN 108976220 A CN108976220 A CN 108976220A CN 201810870156 A CN201810870156 A CN 201810870156A CN 108976220 A CN108976220 A CN 108976220A
- Authority
- CN
- China
- Prior art keywords
- thioxanthene
- heptene
- spiral shell
- dibenzo
- formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to electroluminescent material technical fields, disclose conjugated compound and the preparation and application of one kind dibenzo heptene thioxanthene Han 9,9- spiral shell formula.The conjugated compound for containing 9,9- spiral shell formula dibenzo heptene thioxanthene has general structure shown in formula 1 or formula 2, wherein R1And R2The conjugate unit or alkyl and the simultaneously-substituted conjugate unit of alkoxy that aromatic heterocycle, the aromatic heterocycle of carbon silicon hydrogen atom composition, the alkyl of C1~C24, alkyl-substituted conjugate unit, the alkoxy that aromatic heterocycle, the carbon sulphur hydrogen atom of aromatic heterocycle, carbon nitrogen oxygen hydrogen atom composition that aromatic rings, the carbon nitrogen hydrogen atom constituted for the identical or different ethylene support group with electron, acetylene support group, hydrocarbon atom is constituted are constituted replace.Gained compound of the invention has fluorescence, and the external quantum efficiency of device can be obviously improved as the luminescent layer of organic electroluminescent LED.
Description
Technical field
The invention belongs to electroluminescent material technical fields, and in particular to one kind dibenzo heptene thioxanthene Han 9,9- spiral shell formula
Conjugated compound and preparation and application.
Background technique
Organic electroluminescent LED (OLED) because have efficiently, low voltage drive, be easy to large area preparation and panchromatic aobvious
The advantages that showing has broad application prospects, and obtains the extensive concern of people.The research starts from the last century 50's, until
Doctor Deng Qingyun of Kodak in 1987 is equal to use sandwich device architecture in patent US4356429, develops
OLED device light emission luminance under 10V direct voltage drive reaches 1000cd/m2, OLED is made to obtain epoch-making development.?
In past 20 years, using novel light-emitting body, the OLED device of especially organic-heavy metal complex phosphorescent emitters is obtained
No small success.However, due to more difficult acquisition band gap phosphor, can satisfy at present efficient pure blue shine (yCIE <
0.15, yCIE+xCIE < 0.30) phosphorescent emitters quantity is very rare, and relative to green and red phosphorescence material,
Selection also has comparable challenge for the material of main part with high triplet energy of blue phosphorescent.Therefore, blue phosphorus is developed
The material of main part of luminescent material has very urgent practical application request.Currently, exploitation has smaller single line with ambipolar
State-triplet difference material of main part, becoming design, efficiently the low material of main part to roll-off has great importance.Meanwhile it sending out
It is still very necessary to open up efficient, stable blue luminescence body.It, can using blue fluorescent material in view of various factors
So that the full-color display of OLED or the practical production of white-light illuminating reduce cost and simplify manufacturing process.But it is previous classical
Blue organic fluorescence materials can be divided into n-type molecule from molecular structure, p-type molecule, they want in device work
It shows as that electronics is leading or to show as hole leading, thus is difficult to realize the balance of carrier, so as to cause device current
Efficiency and quantum efficiency are relatively low.And Donor-Acceptor (D-A) type molecule is simply designed, although bipolarity biography can be able to achieve
It is defeated, achieve the purpose that equilbrium carrier, but since the Intramolecular electron transfer between electron unit and electrophilic subelement is made
With the band gap of compound can be made to narrow, lead to glow peak red shift, it is difficult to obtain ideal blue-light-emitting.Overcome this tired
It is difficult, it is necessary to selection have receptor combination of the proper strength to electrical donor and electrophilicity at molecule, intramolecular charge is turned
Control is moved in certain degree, the blue organic fluorescence materials that performance is good, excitation purity is high could be obtained.
It up to now, is sulphur dibenzofuran, phosphorus oxygen, triphen for the skeleton of the most of vapor deposition molecule of organic electro-optic device
The units such as amine are core, and are but rarely reported with the organic light emission small molecule that 9,9- spiral shell formula dibenzo heptene thioxanthene is core.
So far Organic Light Emitting Diode has been achieved for considerable progress, and by phosphorescence hydridization, we can be obtained
The very high white light parts of the simple efficiency of device architecture.And the efficiency of this phosphorescence hydridization device be largely dependent upon it is glimmering
The efficiency of light, therefore the efficient fluorescent material of development still has very important meaning.
Summary of the invention
In place of the above shortcoming and defect of the existing technology, the primary purpose of the present invention is that providing one kind contains 9,
The conjugated compound of 9- spiral shell formula dibenzo heptene thioxanthene.The material structure is single, molecular weight determine, have preferable dissolubility and
Film forming.
Another object of the present invention is to provide the systems of the conjugated compound of the above-mentioned formula of spiral shell containing 9,9- dibenzo heptene thioxanthene
Preparation Method.
A further object of the present invention is to provide the conjugated compounds of the above-mentioned formula of spiral shell containing 9,9- dibenzo heptene thioxanthene to have
Application in machine photoelectric device.
The object of the invention is achieved through the following technical solutions:
A kind of conjugated compound of the dibenzo heptene thioxanthene Han 9,9- spiral shell formula, it is described to contain 9,9- spiral shell formula dibenzo heptene thioxanthene
Conjugated compound have the general structure as shown in following formula 1 or formula 2:
Wherein R1And R2For the identical or different ethylene support group with electron, acetylene support group, hydrocarbon atom structure
At aromatic rings, carbon nitrogen hydrogen atom constitute aromatic heterocycle, carbon nitrogen oxygen hydrogen atom constitute aromatic heterocycle, carbon sulphur hydrogen atom constitute
Aromatic heterocycle, carbon silicon hydrogen atom constitute aromatic heterocycle, C1~C24 alkyl, alkyl-substituted conjugate unit, alkoxy take
The simultaneously-substituted conjugate unit of conjugate unit or alkyl and alkoxy in generation.
The synthetic method of the above-mentioned conjugated compound for containing 9,9- spiral shell formula dibenzo heptene thioxanthene, includes the following steps:
(1) 2- bromophenyl diphenyl sulfide reacts under n-BuLi catalysis with dibenzosuberenone, obtains 9,9- spiral shell formula hexichol
And heptene thioxanthene, it is then reacted with bromine, obtains bromine and replace 9,9- spiral shell formula dibenzo heptene thioxanthene；
(2) bromine obtained by step (1) is replaced into 9,9- spiral shell formula dibenzo heptene thioxanthene and R1And R2The compound of base passes through
Suzuki coupling, Buchwald-Hartwig coupling or copper are catalyzed halogenated aryl hydrocarbon ammoxidation, or bromine obtained by step (1) is taken
For 9,9- spiral shell formula dibenzo heptene thioxanthene after hydrogen peroxide oxidation with R1And R2The compound of base by Suzuki be coupled,
Buchwald-Hartwig coupling or copper are catalyzed halogenated aryl hydrocarbon ammoxidation, obtain the dibenzo heptene thiophene containing 9,9- spiral shell formula
The conjugated compound of ton.
Application of the conjugated compound of the above-mentioned formula of spiral shell containing 9,9- dibenzo heptene thioxanthene in organic electro-optic device.
The conjugated compound of the above-mentioned formula of spiral shell containing 9,9- dibenzo heptene thioxanthene is as organic light-emitting diode layer material
Application.
Concrete application process includes: in the hole transmission layer (formal dress device) or electron transfer layer being located on ito glass
Pass through vacuum evaporation or the conjugation chemical combination of the solution coating preparation formula of spiral shell containing 9,9- dibenzo heptene thioxanthene on (flip device)
Object film is as luminescent layer, and then vapor deposition or solution coating electron transfer layer (formal dress device) or hole pass on the light-emitting layer
Defeated layer (flip device), then evaporation metal electrode, obtain organic light emitting diode device.
Compared to current material and technology, the invention has the following advantages and beneficial effects:
(1) the conjugated compound structure of the dibenzo heptene thioxanthene of the invention Han 9,9- spiral shell formula is single, and molecular weight determines, is convenient for
Purification, multi-stage synthesis reproducibility is good, and is convenient for research structure-performance relationship.
(2) the conjugated compound material of the formula dibenzo heptene thioxanthene of spiral shell containing 9,9- of the invention have lower biochemical temperature and
Decomposition temperature, film morphology are stablized.
(3) conjugated compound of the formula dibenzo heptene thioxanthene of spiral shell containing 9,9- of the invention can be by changing the chemical structure connected
Effectively regulate and control the conjugate length and luminous color of the material.
(4) conjugated compound of the formula dibenzo heptene thioxanthene of spiral shell containing 9,9- of the invention is by changing containing repairing on aromatic structure
Adorn group, can further improve the physical characteristic of the material and the photoelectric device performance based on it, by with it is reported in the literature
Material comparison discovery, the device performance of the material based on this patent obtain larger raising.
Detailed description of the invention
Absorption and emission spectra figure of the Fig. 1 for P3 used in embodiment 10 in dichloromethane solution.
Fig. 2 and Fig. 3 is respectively in embodiment 10 using Current density-voltage-brightness of the P3 as luminescent layer obtained device
Graph of relation and luminance-current efficiency-power efficiency relation curve figure.
Absorption and emission spectra figure of the Fig. 4 for P6 used in embodiment 11 in dichloromethane solution.
Fig. 5 and Fig. 6 is respectively the electric current in embodiment 11 using P6 and comparison DMAc-DPS as luminescent layer obtained device
Density vs. voltage-brightness relationship curve figure and luminance-current efficiency-power efficiency relation curve figure.
Specific embodiment
Present invention will now be described in further detail with reference to the embodiments and the accompanying drawings, but embodiments of the present invention are unlimited
In this.
Embodiment 1
(1) 2- bromophenyl diphenyl sulfide (11mmol, 2.93g) is dissolved in the anhydrous THF of 60ml, is cooled to -78 DEG C, is added dropwise to
N-BuLi (14.36mmol) keeps the temperature 1 hour, dibenzosuberenone (10mmol, 2.06g) is dissolved in 30mlTHF, is added dropwise
To reaction system, overnight.It is extracted with dichloromethane, it is dry, silica gel chromatographic column is crossed, white solid is obtained.By obtain direct plus
Enter in glacial acetic acid, be heated to reflux, be added 15ml concentrated hydrochloric acid, generate solid precipitating, suction filtration obtain white solid product M1 (2.7g,
Yield 50%).
(2) M1 (2.7g, 7.7mmol) is dissolved in the glacial acetic acid of 50mL, is heated to reflux.The liquid of 2 times of molar equivalents is added
Bromine, reaction is overnight.It is extracted with dichloromethane, washes, it is dry, solvent is removed under reduced pressure and obtains white solid M2, yield 90%.
(3) M2 and 50mL glacial acetic acid is added in 100mL there-necked flask, after stirring, 30% hydrogen peroxide of 10mL is added, heats
Ethyl alcohol is added after cooling overnight in reflux, filters, solvent is removed under reduced pressure and obtains white solid M3, yield 97%.
The present embodiment reaction process is shown below:
Embodiment 2
(1) by M2 (1.5mmol, 0.81g), carbazole (3.3ml, 0.57g), CuI (0.23g), K2CO3(0.55g), C18O6
(0.1g) is dissolved in DMPU, is heated 180 DEG C, overnight, is extracted with dichloromethane, dry, extraction, is crossed column and is obtained 0.83g containing 9,9-
The conjugated compound P1 of spiral shell formula dibenzo heptene thioxanthene, yield 82%.
(2) by M3 (1.5mmol, 0.81g), carbazole (3.3ml, 0.57g), CuI (0.23g), K2CO3(0.55g), C18O6
(0.1g) is dissolved in DMPU, is heated 180 DEG C, overnight, is extracted with dichloromethane, dry, extraction, is crossed column and is obtained 0.83g containing 9,9-
The conjugated compound P2 of spiral shell formula dibenzo heptene thioxanthene, yield 80%.
The present embodiment reaction process is shown below:
Embodiment 3
(1) by M2 (1.5mmol, 0.81g), tert-butyl carbazole (3.3ml, 0.92g), CuI (0.23g), K2CO3
(0.55g), C18O6(0.1g) is dissolved in DMPU, is heated 180 DEG C, overnight, is extracted with dichloromethane, and dry, extraction is crossed column and obtained
The conjugated compound P3 of 0.83g dibenzo heptene thioxanthene Han 9,9- spiral shell formula, yield 82%.1HNMR:8.33-8.34(d,2H),
8.14-8.16(d,4H),7.65-7.67(d,4H),7.56-7.58(d,4H),5.49-5.51(d,4H),7.41-7.44(d,
4H), 7.29-7.31 (m, 4H), 7.17-7.18 (d, 4H), 1.43 (d, 18H).
(2) by M3 (1.5mmol, 0.81g), carbazole (3.3ml, 0.57g), CuI (0.23g), K2CO3(0.55g), C18O6
(0.1g) is dissolved in DMPU, is heated 180 DEG C, overnight, is extracted with dichloromethane, dry, extraction, is crossed column and is obtained 0.83g containing 9,9-
The conjugated compound P4 of spiral shell formula dibenzo heptene thioxanthene, yield 80%.1HNMR:8.85-8.84(d,2H),8.14-8.16(d,
4H),7.65-7.67(d,4H),7.56-7.58(d,4H),5.49-5.51(d,4H),7.41-7.44(d,4H),7.29-7.31
(m,4H),7.17-7.18(d,4H),1.43(d,18H)。
The present embodiment reaction process is shown below:
Embodiment 4
(1) by M2 (1.5mmol, 0.81g), acridine (3.5ml, 0.72g), as 100 milliliters of toluene of solvent, 60 milligrams
Palladium acetate, tri-tert phosphorus (0.5mmol, 0.11g) and 0.75 gram of potassium carbonate.It is heated to reflux down and is stirred to react 24 hours.It is cooling
Afterwards, mixed liquor is poured into 200 milliliters of water, and product is extracted with dichloromethane.Anhydrous magnesium sulfate dries organic phase, goes after separation
Except solvent, white solid is obtained with silica gel chromatographic column separating-purifying, high-purity is obtained in sublimed under vacuum after drying and contains
The conjugated compound P5 (1.24g, yield 86%) of 9,9- spiral shell formula dibenzo heptene thioxanthenes.
(2) by M3 (1.5mmol, 0.81g), acridine (3.5ml, 0.72g), as 100 milliliters of toluene of solvent, 60 milligrams
Palladium acetate, tri-tert phosphorus (0.5mmol, 0.11g) and 0.75 gram of potassium carbonate.It is heated to reflux down and is stirred to react 24 hours.It is cooling
Afterwards, mixed liquor is poured into 200 milliliters of water, and product is extracted with dichloromethane.Anhydrous magnesium sulfate dries organic phase, goes after separation
Except solvent, white solid is obtained with silica gel chromatographic column separating-purifying, high-purity is obtained in sublimed under vacuum after drying and contains
The conjugated compound P6 (1.26g, yield 87%) of 9,9- spiral shell formula dibenzo heptene thioxanthenes.
The present embodiment reaction process is shown below:
Embodiment 5
(1) by M2 (1.5mmol, 0.81g), phenoxazine (3.5ml, 0.68g), as 100 milliliters of toluene of solvent, 60 millis
Gram palladium acetate, tri-tert phosphorus (0.5mmol, 0.11g) and 0.75 gram of potassium carbonate.It is heated to reflux down and is stirred to react 24 hours.It is cold
But after, mixed liquor is poured into 200 milliliters of water, and product is extracted with dichloromethane.Anhydrous magnesium sulfate dries organic phase, after separation
Solvent is removed, white solid is obtained with silica gel chromatographic column separating-purifying, obtains high-purity in sublimed under vacuum after drying
The conjugated compound P7 (1.21g, yield 85%) of the spiral shell formula dibenzo heptene thioxanthene containing 9,9-.
(2) by M3 (1.5mmol, 0.81g), phenoxazine (3.5ml, 0.72g), as 100 milliliters of toluene of solvent, 60 millis
Gram palladium acetate, tri-tert phosphorus (0.5mmol, 0.11g) and 0.75 gram of potassium carbonate.It is heated to reflux down and is stirred to react 24 hours.It is cold
But after, mixed liquor is poured into 200 milliliters of water, and product is extracted with dichloromethane.Anhydrous magnesium sulfate dries organic phase, after separation
Solvent is removed, white solid is obtained with silica gel chromatographic column separating-purifying, obtains high-purity in sublimed under vacuum after drying
The conjugated compound P8 (1.22g, yield 83%) of the spiral shell formula dibenzo heptene thioxanthene containing 9,9-.
The present embodiment reaction process is shown below:
Embodiment 6
(1) by M2 (1.5mmol, 0.81g), phenthazine (3.5ml, 0.68g), as 100 milliliters of toluene of solvent, 60 millis
Gram palladium acetate, tri-tert phosphorus (0.5mmol, 0.11g) and 0.75 gram of potassium carbonate.It is heated to reflux down and is stirred to react 24 hours.It is cold
But after, mixed liquor is poured into 200 milliliters of water, and product is extracted with dichloromethane.Anhydrous magnesium sulfate dries organic phase, after separation
Solvent is removed, white solid is obtained with silica gel chromatographic column separating-purifying, obtains high-purity in sublimed under vacuum after drying
The conjugated compound P9 (1.21g, yield 85%) of the spiral shell formula dibenzo heptene thioxanthene containing 9,9-.
(2) by M3 (1.5mmol, 0.81g), phenthazine (3.5ml, 0.72g), as 100 milliliters of toluene of solvent, 60 millis
Gram palladium acetate, tri-tert phosphorus (0.5mmol, 0.11g) and 0.75 gram of potassium carbonate.It is heated to reflux down and is stirred to react 24 hours.It is cold
But after, mixed liquor is poured into 200 milliliters of water, and product is extracted with dichloromethane.Anhydrous magnesium sulfate dries organic phase, after separation
Solvent is removed, white solid is obtained with silica gel chromatographic column separating-purifying, obtains high-purity in sublimed under vacuum after drying
The conjugated compound P10 (1.22g, yield 83%) of the spiral shell formula dibenzo heptene thioxanthene containing 9,9-.
The present embodiment reaction process is shown below:
Embodiment 7
(1) by M2 (1.08g, 3.5mmol) and N, N- diphenyl -4- (4,4,5,5- tetramethyls -1,3, penta boron of 2- dioxa
Alkane -2- base) aniline (2.6g, 7mmol) is added in 250ml single-necked flask, 120ml toluene, 40ml ethyl alcohol and 30ml 2M is added
Wet chemical, then be added 100mg triphenylphosphine zeroth order palladium, ventilate half an hour, displace the oxygen in reaction system
Gas, ventilation finish sealing, and 90-100 DEG C of heating is reacted 18-24 hours, and cooling, methylene chloride extraction, organic phase is dry, too short
Column, petroleum ether: methylene chloride=5:1 crosses column, obtains white solid product P11 (3.6g, yield 90%).
(2) by M3 (1.08g, 3.5mmol) and N, N- diphenyl -4- (4,4,5,5- tetramethyls -1,3, penta boron of 2- dioxa
Alkane -2- base) aniline (2.6g, 7mmol) is added in 250ml single-necked flask, 120ml toluene, 40ml ethyl alcohol and 30ml 2M is added
Wet chemical, then be added 100mg triphenylphosphine zeroth order palladium, ventilate half an hour, displace the oxygen in reaction system
Gas, ventilation finish sealing, and 90-100 DEG C of heating is reacted 18-24 hours, and cooling, methylene chloride extraction, organic phase is dry, too short
Column, petroleum ether: methylene chloride=1:1 crosses column, obtains white solid product P12 (3.70g, yield 92%).
The present embodiment reaction process is shown below:
Embodiment 8
(1) by M2 (1.08g, 3.5mmol) and 9- phenyl -3- (4,4,5,5- tetramethyls -1,3,2- dioxaborolan -
2- yl) carbazole (2.6g, 7mmol) is added in 250ml single-necked flask, 120ml toluene, 40ml ethyl alcohol and 30ml 2M is added
Then the triphenylphosphine zeroth order palladium of 100mg is added in wet chemical, ventilate half an hour, displace the oxygen in reaction system,
Ventilation finishes sealing, and 90-100 DEG C of heating is reacted 18-24 hours, and cooling, methylene chloride extraction, organic phase is dry, crosses short column, stone
Oily ether: methylene chloride=5:1 crosses column, obtains white solid product P13 (3.6g, yield 90%).
(2) by M3 (1.08g, 3.5mmol) and 9- phenyl -3- (4,4,5,5- tetramethyls -1,3,2- dioxaborolan -
2- yl) carbazole (2.6g 7mmol) is added in 250ml single-necked flask, 120ml toluene, 40ml ethyl alcohol and 30ml 2M is added
Then the triphenylphosphine zeroth order palladium of 100mg is added in wet chemical, ventilate half an hour, displace the oxygen in reaction system,
Ventilation finishes sealing, and 90-100 DEG C of heating is reacted 18-24 hours, and cooling, methylene chloride extraction, organic phase is dry, crosses short column, stone
Oily ether: methylene chloride=1:1 crosses column, obtains white solid product P14 (3.70g, yield 92%).
The present embodiment reaction process is shown below:
Embodiment 9
(1) 250ml single-necked flask is added to by M2 (1.08g, 3.5mmol) and to carbazole borate ester (2.6g, 7mmol)
In, the wet chemical of 120ml toluene, 40ml ethyl alcohol and 30ml 2M is added, the triphenylphosphine zeroth order of 100mg is then added
Palladium is ventilated half an hour, and the oxygen in reaction system is displaced, and ventilation finishes sealing, and 90-100 DEG C of heating is reacted 18-24 hours,
Cooling, methylene chloride extraction, organic phase is dry, crosses short column, petroleum ether: methylene chloride=5:1 crosses column, obtains white solid product
P15 (3.6g, yield 90%).
(2) M3 (1.08g, 3.5mmol) is added to 250ml single-necked flask to carbazole borate ester (2.6g 7mmol)
In, the wet chemical of 120ml toluene, 40ml ethyl alcohol and 30ml 2M is added, the triphenylphosphine zeroth order of 100mg is then added
Palladium is ventilated half an hour, and the oxygen in reaction system is displaced, and ventilation finishes sealing, and 90-100 DEG C of heating is reacted 18-24 hours,
Cooling, methylene chloride extraction, organic phase is dry, crosses short column, petroleum ether: methylene chloride=1:1 crosses column, obtains white solid product
P16 (3.70g, yield 92%).
The present embodiment reaction process is shown below:
Embodiment 10
Preparation and photoelectric properties of the present embodiment using P3 as Organic Light Emitting Diode (OLED) device of luminescent layer are surveyed
Test result:
Ito glass is handled after ultrasonic cleaning with oxygen-Plasma, and the square resistance of ito glass is 10 Ω/cm2。
Hole injection layer is HAT-CN, and hole transmission layer is NPB and TCTA, and luminescent layer is using the spiral shell containing 9,9- obtained by the embodiment of the present invention 3
The conjugated compound P3 of formula dibenzo heptene thioxanthene, electron transfer layer use TPBI.Cathode electrode uses LiF/Al metal.ITO
Apply positive bias between metal electrode, the characteristic of device is tested under different electric currents.
NPB refers to that N, N'- diphenyl-N, N'- (1- naphthalene) -1,1'- biphenyl -4,4'- diamines, TCTA refer to 4,4', 4 "-three
(carbazole -9- base) triphenylamine, TPBI refer to 1,3,5- tri- (1- phenyl -1-H- benzo [d] imidazoles -2-) benzene.Structure is as follows:
Absorption and emission spectra figure of the P3 used in the present embodiment in dichloromethane solution is as shown in Figure 1.Using P3 conduct
The Current density-voltage of luminescent layer obtained device-brightness relationship curve figure and luminance-current efficiency-power efficiency relation curve
Figure is as shown in Figures 2 and 3 respectively.Obtained device photoelectric properties test data such as table 1:
Table 1
Embodiment 11
Preparation and photoelectric properties of the present embodiment using P6 as Organic Light Emitting Diode (OLED) device of luminescent layer are surveyed
Test result:
Ito glass is handled after ultrasonic cleaning with oxygen-Plasma, and the square resistance of ito glass is 10 Ω/cm2。
Hole injection layer is TAPC, and luminescent layer uses the conjugation of the dibenzo heptene thioxanthene Han 9,9- spiral shell formula obtained by the embodiment of the present invention 4
It closes object P6 to be entrained in main body DPEPO, electron transfer layer uses DPEPO and TmPyPB.Cathode electrode uses LiF/Al metal.
Apply positive bias between ITO and metal electrode, the characteristic of device is tested under different electric currents.Comparative device be DMAc-DPS and
DMTDAc。
TAPC refers to 4,4'- cyclohexyl two [N, N- bis- (4- aminomethyl phenyl) aniline], and TmPyPB refers to 1,3,5- tri- [(3- hexichol
Base) -3- phenyl] benzene, DPEPO refers to two [2- ((oxo) diphenylphosphino) phenyl] ethers.Structure is as follows:
Absorption and emission spectra figure of the P6 used in the present embodiment in dichloromethane solution is as shown in Figure 4.Using P6 and right
Current density-voltage-brightness relationship curve figure and luminance-current efficiency-function than DMAc-DPS as luminescent layer obtained device
Rate relationship between efficiency curve graph difference is as shown in Figure 5 and Figure 6.Obtained device photoelectric properties test data such as table 2:
Table 2
As can be seen from the above results, the conjugated compound of present invention gained dibenzo heptene thioxanthene Han 9,9- spiral shell formula is compared
The external quantum efficiency of OLED device of the existing DMAc-DPS and DMTDAc material as luminescent layer is obviously improved.
The above embodiment is a preferred embodiment of the present invention, but embodiments of the present invention are not by above-described embodiment
Limitation, other any changes, modifications, substitutions, combinations, simplifications made without departing from the spirit and principles of the present invention,
It should be equivalent substitute mode, be included within the scope of the present invention.
Claims (4)
1. a kind of conjugated compound of the dibenzo heptene thioxanthene Han 9,9- spiral shell formula, it is characterised in that described to contain 9,9- spiral shell formula dibenzo
The conjugated compound of heptene thioxanthene has the general structure as shown in following formula 1 or formula 2:
Wherein R1And R2It is constituted for the identical or different ethylene support group with electron, acetylene support group, hydrocarbon atom
The virtue that aromatic heterocycle, the carbon sulphur hydrogen atom of aromatic heterocycle, carbon nitrogen oxygen hydrogen atom composition that aromatic rings, carbon nitrogen hydrogen atom are constituted are constituted
Fragrant heterocycle, the aromatic heterocycle that carbon silicon hydrogen atom is constituted, the alkyl of C1~C24, alkyl-substituted conjugate unit, alkoxy replace
Conjugate unit or the simultaneously-substituted conjugate unit of alkyl and alkoxy.
2. the synthetic method of the conjugated compound of one kind dibenzo heptene thioxanthene Han 9,9- spiral shell formula described in claim 1, including
Following steps:
(1) 2- bromophenyl diphenyl sulfide reacts under n-BuLi catalysis with dibenzosuberenone, obtains 9,9- spiral shell formula dibenzo heptan
Alkene thioxanthene, then reacts with bromine, obtains bromine and replaces 9,9- spiral shell formula dibenzo heptene thioxanthene；
(2) bromine obtained by step (1) is replaced into 9,9- spiral shell formula dibenzo heptene thioxanthene and R1And R2The compound of base passes through Suzuki idol
Connection, Buchwald-Hartwig coupling or copper are catalyzed halogenated aryl hydrocarbon ammoxidation, or bromine obtained by step (1) is replaced 9,9- spiral shell
Formula dibenzo heptene thioxanthene after hydrogen peroxide oxidation with R1And R2The compound of base passes through Suzuki coupling, Buchwald-
Hartwig coupling or copper are catalyzed halogenated aryl hydrocarbon ammoxidation, obtain the conjugation of the dibenzo heptene thioxanthene Han 9,9- spiral shell formula
Compound.
3. conjugated compound the answering in organic electro-optic device of the formula of spiral shell containing 9,9- dibenzo heptene thioxanthene described in claim 1
With.
4. the conjugated compound of the formula of spiral shell containing 9,9- dibenzo heptene thioxanthene according to claim 3 is in organic electro-optic device
Application, it is characterised in that concrete application process include: be located at ito glass on hole transmission layer on passing through vacuum evaporation
Or then the conjugated compound film of solution coating preparation dibenzo heptene thioxanthene Han 9,9- spiral shell formula is shining as luminescent layer
Vapor deposition or solution coat electron transfer layer, then evaporation metal electrode on layer, obtain Organic Light Emitting Diode formal dress device；Or
Pass through vacuum evaporation or the solution coating preparation formula of spiral shell containing 9,9- dibenzo heptene on the electron transfer layer on ito glass
For the conjugated compound film of thioxanthene as luminescent layer, then vapor deposition or solution coat hole transmission layer on the light-emitting layer, then steam
Metallized electrode obtains Organic Light Emitting Diode flip device.