CN108976096A - A kind of ignition powder for no cutting knife - Google Patents
A kind of ignition powder for no cutting knife Download PDFInfo
- Publication number
- CN108976096A CN108976096A CN201811006402.7A CN201811006402A CN108976096A CN 108976096 A CN108976096 A CN 108976096A CN 201811006402 A CN201811006402 A CN 201811006402A CN 108976096 A CN108976096 A CN 108976096A
- Authority
- CN
- China
- Prior art keywords
- mesh
- ignition powder
- parts
- graphite
- titanium carbide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of ignition powders for no cutting knife.The ignition powder is made of ammonium perchlorate, stannic oxide, titanium carbide, phenolic resin, graphite, aluminium slag mixing, each component parts by weight proportion of composition ignition powder are as follows: 35-50 parts of ammonium perchlorate, 15-30 parts of stannic oxide, 10-20 parts of titanium carbide, 5-15 parts of phenolic resin, 2-8 parts of graphite, 5-10 parts of aluminium slag；The ammonium perchlorate, stannic oxide, titanium carbide, phenolic resin, graphite are 100 mesh of single sieve, the aluminium slag is 80-100 mesh of single sieve, screened and be mixed to prepare three times required ignition powder after above-mentioned each component mixing three times respectively, the screening three times is respectively 100 mesh, 80 mesh and 100 mesh.The present invention has simple for production, and stability is good, the advantages that being ignited main ingredient by high temperature and pressure, ensure the normal use of product.
Description
Technical field
The present invention relates to a kind of ignition powders for no cutting knife, belong to no cutting knife technical field.
Background technique
With the development of self- propagating technology, cutting without cutting for cutting effect is reached by the high temperature energy that powder column reaction generates
Knife, it is simple with its structure, using simplicity, carrying portable, it is highly-safe the advantages that the product for civilian use is gradually switched to by military use product
It promotes the use of, is lighted ignition powder using electric ignition device without cutting knife at present, ignited main ingredient by ignition powder, and it is existing
Ignition powder, which exists, in technology is also easy to produce the quick-fried sound of gas, explodes excessively strong, stability is poor, influences igniting for main ingredient.
Summary of the invention
In view of the above technical problems, the invention aims to provide a kind of ignition powder for no cutting knife, production
Simplicity, stability is good, is ignited main ingredient by high temperature and pressure, ensures the normal use of product.
In order to achieve the above object, the technical solution of the invention is as follows:
A kind of ignition powder for no cutting knife, the ignition powder are by ammonium perchlorate, stannic oxide, titanium carbide, phenol
Urea formaldehyde, graphite, aluminium slag mixing composition, each component parts by weight proportion of composition ignition powder are as follows:
The ammonium perchlorate, stannic oxide, titanium carbide, phenolic resin, graphite are 100 mesh of single sieve, and the aluminium slag is single
80-100 mesh are sieved, is screened three times respectively after above-mentioned each component mixing and is mixed to prepare required ignition powder three times, it is described to sieve three times
Choosing is respectively 100 mesh, 80 mesh and 100 mesh.
The advantages of the present invention are:
1, the ignition powder prepared using technical solution of the present invention will not generate gas burst and quick-fried sound in burning, pass through
Then high temperature and pressure that point generates is ignited main ingredient, and make to ignite more fast and stable, ensures the stability of product when in use.
Specific embodiment
In the following, will the present invention will be described in more detail in conjunction with specific embodiments.
A kind of ignition powder for no cutting knife, the ignition powder are by ammonium perchlorate, stannic oxide, titanium carbide, phenol
Urea formaldehyde, graphite, aluminium slag mixing composition, each component parts by weight proportion of composition ignition powder are as follows:
The ammonium perchlorate, stannic oxide, titanium carbide, phenolic resin, graphite are 100 mesh of single sieve, and the aluminium slag is single
80-100 mesh are sieved, is screened three times respectively after above-mentioned each component mixing and is mixed to prepare required ignition powder three times, it is described to sieve three times
Choosing is respectively 100 mesh, 80 mesh and 100 mesh.
Its specific embodiment:
Embodiment 1
Ignition powder each component parts by weight proportion are as follows:
Embodiment 2
This embodiment differs from embodiment 1 in that each component parts by weight match are as follows:
Embodiment 3
The present embodiment difference from Example 2 is that each component parts by weight match are as follows:
Embodiment 4
The present embodiment difference from Example 3 is that each component parts by weight match are as follows:
Embodiment 5
The present embodiment difference from Example 4 is that each component parts by weight match are as follows:
The above is only the preferred embodiment of the present invention, protection scope of the present invention is not limited merely to above-described embodiment,
All technical solutions belonged under thinking of the present invention all belong to the scope of protection of the present invention.It should be pointed out that for the art
For those of ordinary skill, several modifications and variations without departing from the principles of the present invention should be regarded as protection of the invention
Range.
Claims (1)
1. a kind of ignition powder for no cutting knife, the ignition powder is by ammonium perchlorate, stannic oxide, titanium carbide, phenolic aldehyde
Resin, graphite, aluminium slag mixing composition, each component parts by weight proportion of composition ignition powder are as follows:
The ammonium perchlorate, stannic oxide, titanium carbide, phenolic resin, graphite are 100 mesh of single sieve, and the aluminium slag is single sieve
80-100 mesh are screened three times respectively after above-mentioned each component mixing and are mixed to prepare required ignition powder three times, described to screen three times
Respectively 100 mesh, 80 mesh and 100 mesh.