CN108972922A - A kind of sapphire crystal ingot draws stick drilling pipe knife - Google Patents
A kind of sapphire crystal ingot draws stick drilling pipe knife Download PDFInfo
- Publication number
- CN108972922A CN108972922A CN201810750684.5A CN201810750684A CN108972922A CN 108972922 A CN108972922 A CN 108972922A CN 201810750684 A CN201810750684 A CN 201810750684A CN 108972922 A CN108972922 A CN 108972922A
- Authority
- CN
- China
- Prior art keywords
- diamond
- carrier
- alloy
- drilling pipe
- volume ratio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of sapphire crystal ingot and draws stick drilling pipe knife, including diamond and carrier alloy, the carrier alloy includes cobalt, copper, aluminium, silver, zinc, and wherein volume ratio shared by cobalt is 65% or more, the carrier alloy and diamond volume ratio, i.e. diamond concentration are 42% to 55%.In the carrier alloy, aluminium, silver, volume ratio shared by zinc are less than 15%.The carrier alloy includes the component of following volume ratio: cobalt 68%, and copper 25%, aluminium 2%, silver 2%, zinc 3%, the diamond concentration is 47%.Cobalt content in alloy carrier is promoted to 65% or more by the present invention, and with copper, aluminium is silver-colored, and zinc is mixed as alloy carrier with diamond, can greatly enhance the wearability of drilling pipe knife.
Description
Technical field
The present invention relates to a kind of alloy material, in particular to a kind of sapphire crystal ingot draws stick drilling pipe knife.
Background technique
After the completion of sapphire crystal ingot preparation, need to dig out crystal bar with drawing stick drilling pipe, draw stick drilling pipe port be equipped with it is cricoid
Drilling pipe knife, current drilling pipe knife draw stick depth generally in 5m or so, and quality preferably most multipotency reaches 8 to 10m, can reach
10m or more depth it is very rare, drill bit mostly uses cobalt alloy as carrier, is mixed with diamond, existing brill
Pipe knife cobalt content is mostly less than 30%, because will lead to the decline of drilling pipe knife wearability after nowadays generally believing that cobalt content improves.
Summary of the invention
In view of the deficiencies of the prior art, the present invention provides a kind of sapphire crystal ingot and draws stick drilling pipe knife.
The technical solution adopted by the present invention is that: a kind of sapphire crystal ingot draws stick drilling pipe knife, including diamond and carrier alloy,
The carrier alloy includes cobalt, copper, aluminium, silver, zinc, and wherein volume ratio shared by cobalt is 65% or more, the carrier alloy and diamond
Volume ratio, i.e. diamond concentration are 42% to 55%.
A kind of sapphire crystal ingot draws stick drilling pipe knife, it is characterized in that: in the carrier alloy, aluminium, silver, body shared by zinc
Product ratio is less than 15%.
A kind of sapphire crystal ingot draws stick drilling pipe knife, it is characterized in that: the carrier alloy includes following volume ratio
Component: cobalt 68%, copper 25%, aluminium 2%, silver 2%, zinc 3%, the diamond concentration are 47%.
Cobalt content in alloy carrier is promoted to 65% or more by the present invention, and with copper, aluminium, silver, zinc is as alloy carrier and gold
Hard rock mixing, can greatly enhance the wearability of drilling pipe knife.
Specific embodiment
Embodiment one:
A kind of sapphire crystal ingot draws stick drilling pipe knife, including diamond and carrier alloy, wherein carrier alloy is by cobalt powder 32%, copper powder
36%, aluminium powder 9%, silver powder 16%, 5% volume ratio of zinc powder composition, diamond and carrier alloy volume ratio, i.e. diamond concentration are 45%,
Diamond grit is 200 μm.It is used under 300 revs/min, feed 3mm/ divided working status according to cutter head made of said ratio, the average longevity
Order 7.5m.
Embodiment two:
A kind of sapphire crystal ingot draws stick drilling pipe knife, including diamond and carrier alloy, wherein carrier alloy is by cobalt powder 44%, copper powder
40%, aluminium powder 4%, silver powder 4%, 8% volume ratio of zinc powder composition, diamond and carrier alloy volume ratio, i.e. diamond concentration are 50%,
Diamond grit is 100 μm.It is used under 300 revs/min, feed 3mm/ divided working status according to cutter head made of said ratio, the average longevity
Order 5.6m.
Embodiment three:
A kind of sapphire crystal ingot draws stick drilling pipe knife, including diamond and carrier alloy, wherein carrier alloy is by cobalt powder 57%, copper powder
34%, aluminium powder 4%, silver powder 2%, 3% volume ratio of zinc powder composition, diamond and carrier alloy volume ratio, i.e. diamond concentration are 55%,
Diamond grit is 150 μm.It is used under 300 revs/min, feed 3mm/ divided working status according to cutter head made of said ratio, the average longevity
Order 3.5m.
Example IV:
A kind of sapphire crystal ingot draws stick drilling pipe knife, including diamond and carrier alloy, wherein carrier alloy is by cobalt powder 65%, copper powder
20%, aluminium powder 6%, silver powder 2%, 7% volume ratio of zinc powder composition, diamond and carrier alloy volume ratio, i.e. diamond concentration are 42%,
Diamond grit is 180 μm.It is used under 300 revs/min, feed 3mm/ divided working status according to cutter head made of said ratio, the average longevity
Order 14m.
Embodiment five:
A kind of sapphire crystal ingot draws stick drilling pipe knife, including diamond and carrier alloy, wherein carrier alloy is by cobalt powder 68%, copper powder
25%, aluminium powder 2%, silver powder 2%, 3% volume ratio of zinc powder composition, diamond and carrier alloy volume ratio, i.e. diamond concentration are 47%,
Diamond grit is 185 μm.It is used under 300 revs/min, feed 3mm/ divided working status according to cutter head made of said ratio, the average longevity
Order 16m.
Embodiment six:
A kind of sapphire crystal ingot draws stick drilling pipe knife, including diamond and carrier alloy, wherein carrier alloy is by cobalt powder 75%, copper powder
20%, aluminium powder 2%, silver powder 1%, 2% volume ratio of zinc powder composition, diamond and carrier alloy volume ratio, i.e. diamond concentration are 50%,
Diamond grit is 190 μm.It is used under 300 revs/min, feed 3mm/ divided working status according to cutter head made of said ratio, the average longevity
Order 12m.
Embodiment six:
A kind of sapphire crystal ingot draws stick drilling pipe knife, including diamond and carrier alloy, wherein carrier alloy is by cobalt powder 80%, copper powder
10%, aluminium powder 5%, silver powder 2%, 3% volume ratio of zinc powder composition, diamond and carrier alloy volume ratio, i.e. diamond concentration are 55%,
Diamond grit is 200 μm.It is used under 300 revs/min, feed 3mm/ divided working status according to cutter head made of said ratio, the average longevity
Order 8.5m.
As seen from the above-described embodiment, when cobalt content is 30% or more in drilling pipe knife carrier alloy, wear resistance is bad, and
It is on a declining curve with cobalt content raising, but when cobalt content reaches 65%, cutter head wear resistance greatly increases, further experiment verifying
Afterwards, aobvious best according to the drilling pipe knife of the preparation table in actual job is matched in embodiment five, it is preferred embodiment.
Claims (3)
1. a kind of sapphire crystal ingot draws stick drilling pipe knife, including diamond and carrier alloy, it is characterized in that: the carrier alloy includes
Cobalt, copper, aluminium, silver, zinc, wherein volume ratio shared by cobalt is 65% or more, the diamond and carrier alloy volume ratio, i.e. diamond
Concentration is 42% to 55%, and diamond grit is 100-200 μm.
2. a kind of sapphire crystal ingot according to claim 1 draws stick drilling pipe knife, it is characterized in that: in the carrier alloy, aluminium,
For volume ratio shared by silver, zinc less than 15%, diamond grit is 180-200 μm.
3. a kind of sapphire crystal ingot according to claim 2 draws stick drilling pipe knife, it is characterized in that: the carrier alloy includes such as
The component of lower volume ratio: cobalt 68%, copper 25%, aluminium 2%, silver 2%, zinc 3%, the diamond concentration are 47%, diamond grit 185
μm。