CN108968247A - A kind of production method of DIY jewellery - Google Patents
A kind of production method of DIY jewellery Download PDFInfo
- Publication number
- CN108968247A CN108968247A CN201810852559.5A CN201810852559A CN108968247A CN 108968247 A CN108968247 A CN 108968247A CN 201810852559 A CN201810852559 A CN 201810852559A CN 108968247 A CN108968247 A CN 108968247A
- Authority
- CN
- China
- Prior art keywords
- wax
- pattern
- jewellery
- decoration
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production methods of DIY jewellery, comprising the following steps: makes nut and screw portion by B metal；The wax-pattern two of wax-pattern one and decoration after making the first connector removing screw portion；Screw rod is connected to wax-pattern one into wax-pattern component one；Nut is inlayed to wax-pattern two into wax-pattern component two；By wax-pattern component one, two planting wax trees；Wax-pattern kind tree is put on into steel legendary venomous insect；Plaster mold is made in calcium plaster injection steel legendary venomous insect；Steel legendary venomous insect high temperature is dewaxed；Liquid A metal is injected into plaster mold；Metalwork in plaster mold is taken out, by holding mould, polishing obtains the first connector and decoration module；First connector is connected to chain ends and forms chain module；By nut and screw rod, string according to the sequence that a chain module connects a decoration module.The present invention can be avoided occur being not connected firmly between two kinds of metals of production jewellery by the problem of, and manufactured jewellery can also arbitrarily change style by way of freely assembling.
Description
Technical field
The present invention relates to bullion technical fields, more particularly to a kind of production method of jewellery.
Background technique
It usually needs to link together on two different metals in jewellery, jewellery sector, and generallys use welding
Mode, such as firelock welding, laser welding, electric welding are used, however not only technical requirements are high for welding procedure, but also are easy to appear
The problems such as more than rosin joint, not secured enough, waste product.Also, with the improvement of living standards, people also get over personalized requirement
Come higher, when people enter different places, participates in different social activity, when even wearing different dress ornaments, all may
The bullion that different styles can be replaced is worn；Therefore, in order to attract customer, many bullion manufacturers from the structure of product,
It works hard in function, appearance material, design produces diversified jewellery product for customer's selection；But for existing
For any a jewellery product, function and style are all often single fixations, it is therefore desirable to be equipped with a plurality of jewellery in case
Replacement is worn, and is also difficult to keep new meaning after wearing for a long time.
Summary of the invention
For overcome the deficiencies in the prior art, the present invention provides a kind of production method of DIY jewellery, it can be avoided system
Make occur being not connected firmly the problem leaned on, more than waste product between two kinds of metals of jewellery, and the jewellery through this method production can be with
Arbitrarily change the style of jewellery by way of freely assembling.
The technical solution adopted by the present invention to solve the technical problems is:
A kind of production method of DIY jewellery, the jewellery include chain module and decoration module, and chain module includes chain
With the first connector for being connected to chain ends, one end of the first connector is provided with screw rod, and the decoration module includes dress
Decorations body and the nut for being embedded in decoration two sides, the chain and decoration all have a variety of patterns, the production side of the jewellery
Method makes the screw portion of nut and the first connector by auxiliary material B metal the following steps are included: step 1；Step 2, system
The wax-pattern two of wax-pattern one and decoration after making the first connector removing screw portion；Screw rod is connected to wax-pattern one by step 3
Wax-pattern component one is formed on corresponding position；The two sides that nut is mounted to wax-pattern two are formed into wax-pattern component two；Step 4, by wax
Two planting wax tree of membrane module one and wax-pattern component；Wax-pattern kind tree is put on steel legendary venomous insect by step 5；Calcium plaster is injected steel legendary venomous insect by step 6
Wax-pattern kind tree is not crossed, then vacuumizes and plaster mold is made, then stood；Steel legendary venomous insect is placed in high temperature furnace and takes off by step 7
Wax；Step 8 will melt into the main material A metal injection plaster mold of liquid, be then allowed to stand；Step 9 is taken out in plaster mold
Metalwork, then metalwork is rinsed until residual gypsum is detached from from metalwork completely with hydraulic giant；Step 10, by metalwork by holding
Mould, polishing, polishing obtain the first connector and decoration module；First connector is connected to the end shape of chain by step 11
Chaining module；Step 12, by being threadedly engaged between screw rod on nut and the first connector, according to a chain module
The sequence for connecting a decoration module, chain module and decoration module are strung.
It is lower than the fusing point of the B metal as the fusing point of A metal described in above-mentioned technical proposal.
Further, the hardness of the B metal is greater than the A metal.
Further, the A metal is gold or silver, and the B metal is stainless steel.
Further, in step 6 calcium plaster by land plaster and water according to the ratio of 1Kg land plaster addition 0.4L water in vacuum
In stir.
Further, in step 6 time of repose at 1 hour or more.
Further, in step 7, according to 150 DEG C of 1 hours of burning, 250 DEG C of 1 hours of burning, 350 DEG C of burnings 2 hours, 450
DEG C burn 1 hour, 450 DEG C be gradually heated to 700 DEG C processes burn 2 hours, last 700 DEG C of constant temperature calcinations 1 hour sequence
High temperature dewaxing.
Further, the casting of A metal is completed in step 8 using vacuum casting machine.
Further, in step 8 time of repose at 20 minutes or more.
The beneficial effects of the present invention are: the company using the jewellery of production method of the present invention production, between two of them metal
Connecing is realized by way of casting, and compared with the welding manner that existing jewellery sector generallys use, technical requirements are opposite
It is lower, and can guarantee the connection between screw portion and the first connector other parts, between nut and decoration all more
Add solid and reliable, will not occur the problem more than waste product because of reasons such as rosin joints；And will not occur ugly welding on jewellery
Point, so that jewellery are more beautiful.Moreover, because being detachable by the cooperation of screw rod and nut between chain module and decoration module
Connection, therefore user by the chain module of different patterns and can decorate mould according to the hobby of oneself and use occasion etc. completely
Block carries out permutation and combination and assembles to string, so that reaching arbitrarily change jewellery style, moment keeps wearing ornaments new meaning
Purpose.
Detailed description of the invention
Present invention will be further explained below with reference to the attached drawings and examples.
Fig. 1 is the structural schematic diagram of heretofore described chain module；
Fig. 2 is the structural schematic diagram of heretofore described first connector；
Fig. 3 is the structural schematic diagram of heretofore described decoration module；
Fig. 4, Fig. 5, Fig. 6 are the overall structure signal using the jewellery for three kinds of styles for having the method for the present invention to make respectively
Figure.
Specific embodiment
It include chain module 1 and decoration module 2 using the DIY jewellery that production method of the invention makes referring to figs. 1 to 6,
Chain module 1 includes chain 11 and the first connector 12 for being connected to 11 end of chain, and one end of the first connector 12 is provided with
Screw rod 121, the decoration module 2 include decoration 21 and the nut 22 for being embedded in 21 two sides of decoration, 11 He of chain
Decoration 21 all has a variety of patterns, the production methods of the jewellery the following steps are included:
Step 1 makes 121 part of screw rod of nut 22 and the first connector 12 by auxiliary material B metal；
Step 2, the wax-pattern two of wax-pattern one and decoration 21 after making the first connector 12 removing 121 part of screw rod；
Screw rod 121 is connected to formation wax-pattern component one on the corresponding position of wax-pattern one by step 3；Nut 22 is mounted to
The two sides of wax-pattern two form wax-pattern component two；
Step 4, by two planting wax tree of wax-pattern component one and wax-pattern component；
Wax-pattern kind tree is put on steel legendary venomous insect by step 5；
Calcium plaster injection steel legendary venomous insect is not crossed wax-pattern kind tree, then vacuumizes 5 minutes or more, plaster mold is made by step 6,
It carries out again standing one hour or more；Wherein calcium plaster adds the ratio of 0.4L water true according to 1Kg land plaster by land plaster and water
It stirs in the air；
Steel legendary venomous insect is placed in high temperature furnace and dewaxes by step 7；It is 150 DEG C first 1 hour of burning, most with slow evaporation
Moisture is avoided because the calcination of too high-temperature, which leads to moisture excessive evaporation, makes plaster mold occur splitting powder, loosen situations such as, and gypsum
There is the bright and smooth of the final metal product surface that will affect that casting obtains when the problems such as splitting powder and loosening in mould, and leads to surface quality
It reduces；Then, 250 DEG C of 1 hours of burning, wax is made gradually to melt and ooze；Then, 350 DEG C of 2 hours of burning, then 450 DEG C of burnings
1 hour, further to make moisture evaporation thorough；Then 450 DEG C of processes for being gradually heated to 700 DEG C burn 2 hours, finally
700 DEG C constant temperature calcination 1 hour so that plaster mold is more solid, further ensure that the quality of end product.Specifically, high temperature
Furnace uses electrothermal furnace, to facilitate control furnace temperature.
Step 8 will melt into the main material A metal injection plaster mold of liquid, be then allowed to stand 20 minutes or more；In order to make
Liquid A metal is sufficiently full of type chamber, in the present embodiment, specifically, the casting of A metal is completed using vacuum casting machine；In order to
Liquid A metal is avoided to impact the nut 22 and screw rod 121 of B metal material, the fusing point of A metal should be lower than B metal；
Step 9 takes out the metalwork in plaster mold, then rinses metalwork until residual gypsum is completely from metal with hydraulic giant
It is detached from part；
Step 10, by metalwork by holding mould, polishing, polishing obtain the first connector 12 and decoration module 2；
The end that first connector 12 is connected to chain 11 is formed chain module 1 by step 11；
Step 12, through being threadedly engaged between screw rod 121 on nut 22 and the first connector 12, described in one
Chain module 1 connects the sequence of a decoration module 2, and chain module 1 and decoration module 2 are strung.
Jewellery are made by the above method, the connection between two of them metal is realized by way of casting, with
The welding manner that existing jewellery sector generallys use is compared, and technical requirements are relatively low, and can guarantee 121 part of screw rod
Connection between 12 other parts of the first connector, between nut 22 and decoration 21 is all stronger reliable, will not be because of void
There is the problem more than waste product in the reasons such as weldering, and will not occur ugly pad on jewellery, so that jewellery are more beautiful.
In the present embodiment, specifically, the chain 11 has a variety of patterns, therefore by the way that chain 11 to be connect with first
Part 12 connects the chain module 1 of available a variety of patterns；The decoration 21 has a variety of patterns, such as can be fabricated to Eight Diagrams
Shape, ball-point pen type, heart, lock shape etc., therefore it is combined to the decoration module 2 of available a variety of patterns with nut 22；Moreover, by
It is to be detachably connected by the cooperation of screw rod 121 and nut 22, therefore user is complete between chain module 1 and decoration module 2
The chain module 1 of different patterns and decoration module 2 can be carried out simultaneously by permutation and combination according to the hobby of oneself and use occasion etc. entirely
Assembling strings, and arbitrarily changes jewellery style to reach, the moment keeps the purpose of wearing ornaments new meaning.
In the present embodiment, chain 11, specifically, first one end of connector 12 far from screw rod 121 are connected for convenience
It is provided with connection ring 122, and chain 11 is connected by connection ring 122.
In the present embodiment, specifically, the noble metals such as preferred gold and silver of main material A metal constitute nut 22 and the first connection
The auxiliary material B metal selection of 121 part of screw rod in part 12 is made of metal material more higher than A metal hardness, such as is adopted
With stainless steel etc..Using the noble metals such as gold and silver and corrosion resistance, two kinds of metals such as stainless steel strong, more higher than gold and silver hardness are same
When cast jewellery a component, can both possess the color brightness and value of the noble metals such as gold and silver in appearance, avoid ugly
Pad, can also allow at link and possess the high rigidity and corrosion resistance of the metals such as stainless steel, keep jewellery both good-looking or securely.
The DIY jewellery made of production method of the invention, either necklace, bangle, foot chain etc., can also be chain
Ear pendant or ring of formula etc..Moreover, described above is also better embodiment of the invention, but the present invention is not limited to above-mentioned
Embodiment should all fall into protection model of the invention as long as the technical effect of the present invention is achieved by any identical or similar means for it
Within enclosing.
Claims (9)
1. a kind of production method of DIY jewellery, which is characterized in that the jewellery include chain module (1) and decoration module (2),
Chain module (1) includes chain (11) and the first connector (12) for being connected to chain (11) end, the first connector (12)
One end is provided with screw rod (121), and the decoration module (2) includes decoration (21) and the spiral shell for being embedded in decoration (21) two sides
Female (22), the chain (11) and decoration (21) all have a variety of patterns, the production methods of the jewellery the following steps are included:
Step 1 makes screw rod (121) part of nut (22) and the first connector (12) by auxiliary material B metal；
Step 2, the wax-pattern two of wax-pattern one and decoration (21) after making the first connector (12) removing screw rod (121) part；
Screw rod (121) is connected to formation wax-pattern component one on the corresponding position of wax-pattern one by step 3；Nut (22) is mounted to
The two sides of wax-pattern two form wax-pattern component two；
Step 4, by two planting wax tree of wax-pattern component one and wax-pattern component；
Wax-pattern kind tree is put on steel legendary venomous insect by step 5；
Calcium plaster injection steel legendary venomous insect is not crossed wax-pattern kind tree, then vacuumizes and plaster mold is made, then stood by step 6；
Steel legendary venomous insect is placed in high temperature furnace and dewaxes by step 7；
Step 8 will melt into the main material A metal injection plaster mold of liquid, be then allowed to stand；
Step 9 takes out the metalwork in plaster mold, then rinses metalwork until residual gypsum is completely from metalwork with hydraulic giant
It is detached from；
Step 10, by metalwork by holding mould, polishing, polishing obtain the first connector (12) and decoration module (2)；
The end that first connector (12) is connected to chain (11) is formed chain module (1) by step 11；
Step 12, by being threadedly engaged between screw rod (121) on nut (22) and the first connector (12), according to an institute
The sequence that chain module (1) connects a decoration module (2) is stated, chain module (1) and decoration module (2) are strung.
2. a kind of production method of DIY jewellery according to claim 1, it is characterised in that: the fusing point of the A metal is lower than
The fusing point of the B metal.
3. a kind of production method of DIY jewellery according to claim 2, it is characterised in that: the hardness of the B metal is greater than
The A metal.
4. a kind of production method of DIY jewellery according to claim 3, it is characterised in that: the A metal is golden or silver,
The B metal is stainless steel.
5. a kind of production method of DIY jewellery according to claim 1-4, it is characterised in that: stone in step 6
Cream slurry is stirred by land plaster and water according to the ratio of 1Kg land plaster addition 0.4L water in a vacuum.
6. a kind of production method of DIY jewellery according to claim 1-4, it is characterised in that: quiet in step 6
The time is set at 1 hour or more.
7. a kind of production method of DIY jewellery according to claim 1 to 4, it is characterised in that: in step 7, according to
150 DEG C of 1 hours of burning, 250 DEG C of 1 hours of burning, 350 DEG C of 2 hours of burning, 450 DEG C of 1 hours of burning, 450 DEG C be gradually heated to
700 DEG C of process burns 2 hours, the dewaxing of last 700 DEG C of constant temperature calcinations 1 hour sequence high temperature.
8. a kind of production method of DIY jewellery according to claim 1-4, it is characterised in that: adopted in step 8
The casting of A metal is completed with vacuum casting machine.
9. a kind of production method of DIY jewellery according to claim 1-4, it is characterised in that: quiet in step 8
The time is set at 20 minutes or more.