CN108950707A - A kind of more hollow profiled fibre spinneret plate for producing and production method - Google Patents
A kind of more hollow profiled fibre spinneret plate for producing and production method Download PDFInfo
- Publication number
- CN108950707A CN108950707A CN201811068041.9A CN201811068041A CN108950707A CN 108950707 A CN108950707 A CN 108950707A CN 201811068041 A CN201811068041 A CN 201811068041A CN 108950707 A CN108950707 A CN 108950707A
- Authority
- CN
- China
- Prior art keywords
- spinneret
- spinning
- hollow
- hollow profiled
- spinnerette body
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to technical field of fibre production, especially a kind of more hollow profiled fibre spinneret plate for producing, including spinnerette body, several spinneret orifices are provided on spinnerette body, the spinneret orifice includes being located at spinnerette body to input the regular cavernous structure of one end close to raw material and export the special-shaped central hole structure of one end close to raw material positioned at spinnerette body, and regular cavernous structure and special-shaped central hole structure are interconnected and penetrate through spinnerette body.A kind of production method of more hollow profiled fibres using the spinneret, specific production stage are as follows: raw material screening, raw material drying, high-temperature fusion, spiral squeezing, spinneret spray, and cooling oils, coiling and molding.A kind of obtained more hollow profiled fibre spinneret plate for producing of the present invention and production method, more hollow profiled fibres of production have the characteristics that bulkiness height, elasticity is good, warmth retention property is strong, it is soft it is smooth, resilience is good, spreadability is good.
Description
Technical field
The present invention relates to technical field of fibre production, especially a kind of more hollow profiled fibre spinneret plate for producing and production
Method.
Background technique
Synthetic fibers are since the forties comes out, with the incomparable superiority of its many natural fiber, such as: elasticity height,
It is corrosion-resistant, be not afraid of and damage by worms, get the favour of people and rapidly develop.With increasing and added value for synthetic fibers new function
It is continuously improved, textile and industrial goods made of synthetic fibers are increasingly liked by people.But general melting
Synthetic fibers made of spinning, since its structural form is relatively simple, compared with natural fiber, no matter from structure or performance
On still have quite poor away from.
Currently, its cross sectional shape of the heterotypic fibre produced in the market mainly has triangle, three leaves, pentagon, cross, flat
Shape, C-shaped, T shape etc., shape is simpler, fiber surface low in glossiness, and there is easy dirty, easy pilling, water imbibition is poor, bulkiness
The disadvantages of difference, feel is poor, and elasticity is small.It is had an optimistic view of by more and more chemical fiber enterprises in the market of doughnut.
Summary of the invention
A kind of the purpose of the present invention is to solve the deficiencies of the above technologies and provide fiber fluffy and warming of capable of being promoted
The more hollow profiled fibre spinneret plate for producing and production method of property.
In order to achieve the above object, a kind of more hollow profiled fibre spinneret plate for producing designed by the present invention, including spray
Filament plate ontology, is provided with several spinneret orifices on spinnerette body, and the spinneret orifice includes being located at spinnerette body close to former
The regular cavernous structure of material input one end and the special-shaped central hole structure for exporting one end close to raw material positioned at spinnerette body, regular hole
Shape structure and special-shaped central hole structure are interconnected and penetrate through spinnerette body, wherein the shape of the horizontal cross-section of special-shaped hollow structure
It is arranged in a linear and is formed by the double semi arch type holes of multiple groups, every group of double semi arch type holes face setting by two semicircle annular distance intervals
It is formed, and there is also gaps between two groups of adjacent double semi arch type holes.
Special-shaped hollow structure in each spinneret orifice is made of four groups of double semi arch type holes.
Regular cavernous structure is hollow cylindrical hole, during the junction between special-shaped hollow structure and regular cavernous structure is
Empty circular cone structure transition, and the larger diameter end of hollow cone platform structure is connect with regular cavernous structure, hollow cone platform knot
The smaller diameter end of structure is connect with special-shaped hollow structure.
The quantity of spinneret orifice is 30, and the spinneret orifice arranges on spinnerette body in multi-ring annular, and each circle
Circle is the axial centre of spinnerette body.
A kind of production method of more hollow profiled fibres using the spinneret, specific production stage are as follows: raw material screening,
Raw material drying, high-temperature fusion, spiral squeezing, spinneret spray, and cooling oils, coiling and molding.
Preferably, the melt prepared is delivered to booster pump pressurization, melt cooler cooling through melt conveying pipeline
Afterwards, each spinning manifold is diverted to by distributing valve；By measuring pump-metered, squeezed out after melt injection spinning pack filtering, then through ring
Quenching is made as-spun fibre, and every 10 beam of as-spun fibre is one, every two merge after by traveller, oiling device, lead
Enter up- coiler coiling and molding after silk hook, pre- network, the first hot-rolling, the second hot-rolling；Wherein spin manifold temperature control is 270 when spinning
DEG C, filament spinning component pressure is 15MPa, and spinning temperature is 270 DEG C, and ring blowing air pressure is 20Pa, and wind-warm syndrome is 20 DEG C；Spinning speed is
4000m/min, for the control of the first heat roller temperature at 80 DEG C, speed is 1200 m/min, and the second heat roller temperature is controlled at 110 DEG C, speed
Degree is 4000 m/min.
It is another preferred, the melt prepared is delivered to booster pump pressurization, melt cooler cooling through melt conveying pipeline
Afterwards, each spinning manifold is diverted to by distributing valve；By measuring pump-metered, polyester fondant injection spinning pack squeezes out after filtering, then
Be made as-spun fibre through ring wind quenching, every 10 beam of as-spun fibre is one, every two merge after by traveller, oil dress
It sets, enter up- coiler coiling and molding after traveller, pre- network, the first hot-rolling, the second hot-rolling；Wherein spin manifold temperature controls when spinning
It is 275 DEG C, filament spinning component pressure is 17MPa, and spinning temperature is 265 DEG C, and ring blowing air pressure is 22Pa, and wind-warm syndrome is 21 DEG C, spinning
Speed is 4000m/min, and for the control of the first heat roller temperature at 78 DEG C, speed is 1300 m/min, and the control of the second heat roller temperature exists
110 DEG C, speed is 4000 m/min.
A kind of obtained more hollow profiled fibre spinneret plate for producing of the present invention and production method, production it is how hollow
Profiled filament have the characteristics that bulkiness is high, elasticity is good, warmth retention property is strong, it is soft it is smooth, resilience is good, spreadability is good, extensively
It is general to be applied to gum sprayed cotton, spin the fields such as plumage cotton, bedding, insulated cold wear, toy, bunting.
Production special spinning jet of the present invention due to using aforementioned production method and above-mentioned technical pattern, first will when production
The melt prepared after booster pump pressurization, melt cooler are cooling, is further separated by melt conveying pipeline by distributing valve
Each spinning manifold, by measuring pump-metered, polyester fondant squeezes out after being sent to spinning pack filtering, by circular blow wind or cross air blasting
Cooling and solidifying, drawn form fiber.The melt come out from double semi arch type holes of spinneret, according to extruding principle and melt body stream
Principle is learned in change, and being surround among 4 groups of formation after spraying in hole has the how hollow fiber type in gap, and 4 groups of double semi arch type holes
The shape of assembled arrangement is exactly the global shape of strand cross section.Since the capillary principle of nature is imported textile by the present invention
Exploitation, makes the capillary that 30 channels can be formed in fiber, it is thus possible to quick water suction, water delivery, diffusion and volatilization, to keep
Skin it is dry and comfortable.The cross-sectional area coverage rate of the more hollow profiled fibers of the present invention is between 70%-80%, in fiber quality (weight
Amount) in identical situation, the common heterotypic fibre of surface area ratio increases 50%-60%, thus substantially improves the bulkiness of fiber, bullet
Property, so that fiber is had the feel of natural fabric, capillary effect and gas permeability are very high, and wicking capacity substantially exceeds common heterotypic fibre and spins
Fabric is more more than cotton.
The present invention can be produced using existing mature technology process, not need the update of equipment, saving is produced into
This.
Added value of product of the invention is relatively high, and better results for generation.
Application field of the invention is extensive, such as production military clothes；Make high-grade suit fabric；Make petrochemical industry row
Industry, coal industry, electromechanical industries dustproof and anti-explosion clothes；Make health care and the dustless Anti-bacterial clothing of food service industry；Make electronics industry
Garment for clean room；Make industrial production work clothes；Make carpet and family's spun articles；Make static removal hairbrush.
Detailed description of the invention
Fig. 1 is the arrangement schematic diagram of spinneret orifice on spinneret of the present invention；
Fig. 2 is special-shaped hollow structure schematic diagram on spinneret of the present invention；
Fig. 3 is the schematic cross-section of spinneret orifice of the present invention.
Specific embodiment
The present invention will be further described below by way of embodiments in conjunction with the accompanying drawings.
Embodiment 1:
As shown in Figure 1, Figure 2, Figure 3 shows, a kind of more hollow profiled fibre spinneret plate for producing of the present embodiment description, including spinneret
Ontology 1, is provided with several spinneret orifices 2 on spinnerette body 1, and the spinneret orifice 2 includes being located at spinnerette body 1 close to former
The regular cavernous structure 6 of material input one end and the special-shaped central hole structure for exporting one end close to raw material positioned at spinnerette body 1, rule
Cavernous structure 6 and special-shaped central hole structure are interconnected and penetrate through spinnerette body 1, wherein the horizontal cross-section of special-shaped hollow structure 3
Shape be arranged in a linear and formed by the double semi arch type holes 4 of multiple groups, every group of double semi arch type holes 4 are by two semicircle annular distance interval phases
Face is arranged to be formed, and there is also gaps between two groups of adjacent double semi arch type holes 4.
Special-shaped hollow structure 3 in each spinneret orifice 2 is made of four groups of double semi arch type holes 4.
Regular cavernous structure 6 is hollow cylindrical hole, the junction between special-shaped hollow structure 3 and regular cavernous structure 6
For 5 transition of hollow cone platform structure, and the larger diameter end of hollow cone platform structure 5 is connect with regular cavernous structure 6, hollow circle
The smaller diameter end of frustum structure 5 is connect with special-shaped hollow structure 3.
The quantity of spinneret orifice 2 is 30, and the spinneret orifice 2 arranges on spinnerette body 1 in multi-ring annular, and each circle
Circle be spinnerette body 1 axial centre.
Embodiment 2:
A kind of production method of more hollow profiled fibres using spinneret described in embodiment 1 of the present embodiment description, it is specific raw
Produce step are as follows: raw material screening, raw material drying, high-temperature fusion, spiral squeezing, spinneret spray, and cooling oils, coiling and molding.
By the melt prepared after melt conveying pipeline is delivered to booster pump pressurization, melt cooler cooling, by distributing
Valve is diverted to each spinning manifold；By measuring pump-metered, squeezed out after melt injection spinning pack filtering, then through ring wind quenching system
As-spun fibre is obtained, every 10 beam of as-spun fibre is one, by traveller, oiling device, traveller, pre- net after every two merging
Enter up- coiler coiling and molding after network, the first hot-rolling, the second hot-rolling；Wherein spin manifold temperature control is 270 DEG C when spinning, spinning group
Part pressure is 15MPa, and spinning temperature is 270 DEG C, and ring blowing air pressure is 20Pa, and wind-warm syndrome is 20 DEG C；Spinning speed is 4000m/
Min, for the control of the first heat roller temperature at 80 DEG C, speed is 1200 m/min, and the control of the second heat roller temperature is in 110 DEG C, speed
4000 m/min。
Embodiment 3:
A kind of production method of more hollow profiled fibres using spinneret described in embodiment 1 of the present embodiment description, it is specific raw
Produce step are as follows: raw material screening, raw material drying, high-temperature fusion, spiral squeezing, spinneret spray, and cooling oils, coiling and molding.
By the melt prepared after melt conveying pipeline is delivered to booster pump pressurization, melt cooler cooling, by distributing
Valve is diverted to each spinning manifold；By measuring pump-metered, squeezed out after polyester fondant injection spinning pack filtering, then air-cooled through circular blow
But be made as-spun fibre, every 10 beam of as-spun fibre is one, every two merge after by traveller, oiling device, traveller, pre-
Enter up- coiler coiling and molding after network, the first hot-rolling, the second hot-rolling；Wherein spin manifold temperature control is 275 DEG C when spinning, spinning
Component pressure is 17MPa, and spinning temperature is 265 DEG C, and ring blowing air pressure is 22Pa, and wind-warm syndrome is 21 DEG C, spinning speed 4000m/
Min, for the control of the first heat roller temperature at 78 DEG C, speed is 1300 m/min, and the control of the second heat roller temperature is in 110 DEG C, speed
4000 m/min。
Claims (7)
1. a kind of more hollow profiled fibre spinneret plate for producing, including spinnerette body, it is characterized in that: being set on spinnerette body
Be equipped with several spinneret orifices, the spinneret orifice include positioned at spinnerette body close to raw material input one end regular cavernous structure and
The special-shaped central hole structure of one end is exported close to raw material positioned at spinnerette body, regular cavernous structure is mutually interconnected with special-shaped central hole structure
Lead to and penetrate through spinnerette body, wherein the shape of the horizontal cross-section of special-shaped hollow structure is linearly arranged by the double semi arch type holes of multiple groups
Column are formed, and every group of double semi arch type holes face setting by two semicircle annular distance intervals and formed, and two groups of adjacent double semi arches
There is also gaps between type hole.
2. a kind of more hollow profiled fibre spinneret plate for producing according to claim 1, it is characterized in that: in each spinneret orifice
Special-shaped hollow structure be made of four groups of double semi arch type holes.
3. a kind of more hollow profiled fibre spinneret plate for producing according to claim 2, it is characterized in that: regular cavernous structure
For hollow cylindrical hole, the junction between special-shaped hollow structure and regular cavernous structure is hollow cone platform structural transition, and
The larger diameter end of hollow cone platform structure is connect with regular cavernous structure, the smaller diameter end and abnormity of hollow cone platform structure
Hollow structure connection.
4. a kind of more hollow profiled fibre spinneret plate for producing according to claim 1 or 2 or 3, it is characterized in that: spinneret orifice
Quantity be 30, the spinneret orifice arranges on spinnerette body in multi-ring annular, and the circle of each circle is spinneret
The axial centre of ontology.
5. a kind of production method of more hollow profiled fibres using spinneret as described in claim 1, it is characterized in that: specific raw
Produce step are as follows: raw material screening, raw material drying, high-temperature fusion, spiral squeezing, spinneret spray, and cooling oils, coiling and molding.
6. the production method of a kind of more hollow profiled fibres according to claim 4, it is characterized in that: the melt that will be prepared
After melt conveying pipeline is delivered to booster pump pressurization, melt cooler cooling, each spinning manifold is diverted to by distributing valve；Pass through
Pump-metered is measured, is squeezed out after melt injection spinning pack filtering, then as-spun fibre, as-spun fibre every 10 is made through ring wind quenching
Shu Weiyi root, it is laggard by traveller, oiling device, traveller, pre- network, the first hot-rolling, the second hot-rolling after every two merging
Enter up- coiler coiling and molding；Wherein spin manifold temperature control is 270 DEG C when spinning, and filament spinning component pressure is 15MPa, and spinning temperature is
270 DEG C, ring blowing air pressure is 20Pa, and wind-warm syndrome is 20 DEG C；Spinning speed is 4000m/min, and the first heat roller temperature is controlled 80
DEG C, speed is 1200 m/min, and for the control of the second heat roller temperature at 110 DEG C, speed is 4000 m/min.
7. the production method of a kind of more hollow profiled fibres according to claim 4, it is characterized in that: the melt that will be prepared
After melt conveying pipeline is delivered to booster pump pressurization, melt cooler cooling, each spinning manifold is diverted to by distributing valve；Pass through
Pump-metered is measured, is squeezed out after polyester fondant injection spinning pack filtering, then as-spun fibre, as-spun fibre is made through ring wind quenching
Every 10 beam is one, by traveller, oiling device, traveller, pre- network, the first hot-rolling, the second hot-rolling after every two merging
Enter up- coiler coiling and molding afterwards；Wherein spin manifold temperature control is 275 DEG C when spinning, and filament spinning component pressure is 17MPa, spinning temperature
Degree is 265 DEG C, and ring blowing air pressure is 22Pa, and wind-warm syndrome is 21 DEG C, spinning speed 4000m/min, and the control of the first heat roller temperature exists
78 DEG C, speed is 1300 m/min, and for the control of the second heat roller temperature at 110 DEG C, speed is 4000 m/min.