CN108948950A - A kind of formula based on improvement coating tolerance - Google Patents
A kind of formula based on improvement coating tolerance Download PDFInfo
- Publication number
- CN108948950A CN108948950A CN201810584153.3A CN201810584153A CN108948950A CN 108948950 A CN108948950 A CN 108948950A CN 201810584153 A CN201810584153 A CN 201810584153A CN 108948950 A CN108948950 A CN 108948950A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- solvent
- follows
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of based on the formula for improving coating tolerance, including the first component and the second component, first component includes bisphenol A type epoxy resin, polyoxyethylene polyoxy propyl alcohol amidogen ether, silane coupling agent, organobentonite, talcum powder, the first solvent, and second component includes vinyl triamine, the second solvent.By the above-mentioned means, it is of the invention based on the formula for improving coating tolerance, there is extraordinary anti-corrosion effect, it is resistant to the corrosion of the chemicals such as acid, alkali, salt, oil, free from the influence of the external environment, long service life, later period does not need to be repaired, and has extraordinary using effect.
Description
Technical field
The present invention relates to paint fields, more particularly to a kind of based on the formula for improving coating tolerance.
Background technique
Coating, in the entitled paint of Chinese tradition.Coating is a kind of material, and this material can use different construction technologies
Coated in object surface, is formed and adhered to securely, with some strength, continuous solid film.The film common name film formed in this way,
Also known as paint film or coating.Coating is usually to be added or do not added pigment, filler based on resin or oil or lotion, added phase
Auxiliary agent is answered, the thick liquid being formulated with organic solvent or water.It is outer vulnerable to acid, alkali etc. after existing coating long-time use
The corrosion of boundary's chemicals is easy to influence to use.
Summary of the invention
The invention mainly solves the technical problem of providing a kind of based on the formula for improving coating tolerance, using effect
It is good.
In order to solve the above technical problems, one technical scheme adopted by the invention is that: it provides a kind of resistance to based on coating is improved
By the formula of property, including the first component and the second component, first component includes that bisphenol A type epoxy resin, polyoxyethylene are poly-
Oxygen propyl alcohol amidogen ether, silane coupling agent, organobentonite, talcum powder, the first solvent, second component include vinyl triamine,
Second solvent, the content of first component are as follows: in parts by weight, 20-26 parts of bisphenol A type epoxy resin, polyoxyethylene polyoxy
1-5 parts of propyl alcohol amidogen ether, 3-7 parts of silane coupling agent, 9-13 parts of organobentonite, 11-16 parts of talcum powder, 28-34 parts of the first solvent,
The content of second component are as follows: in parts by weight, 60-70 parts of vinyl triamine, 20-30 parts of the second solvent.
In a preferred embodiment of the present invention, the content of first component are as follows: in parts by weight, bisphenol type epoxy
20 parts of resin, 5 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, 3 parts of silane coupling agent, 13 parts of organobentonite, 11 parts of talcum powder, first
34 parts of solvent, the content of second component are as follows: in parts by weight, 60 parts of vinyl triamine, 30 parts of the second solvent.
In a preferred embodiment of the present invention, the content of first component are as follows: in parts by weight, bisphenol type epoxy
26 parts of resin, 1 part of polyoxyethylene polyoxy propyl alcohol amidogen ether, 7 parts of silane coupling agent, 9 parts of organobentonite, 16 parts of talcum powder, first
28 parts of solvent, the content of second component are as follows: in parts by weight, 70 parts of vinyl triamine, 20 parts of the second solvent.
In a preferred embodiment of the present invention, the content of first component are as follows: in parts by weight, bisphenol type epoxy
21 parts of resin, 4 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, 4 parts of silane coupling agent, 12 parts of organobentonite, 12 parts of talcum powder, first
33 parts of solvent, the content of second component are as follows: in parts by weight, 62 parts of vinyl triamine, 28 parts of the second solvent.
In a preferred embodiment of the present invention, the content of first component are as follows: in parts by weight, bisphenol type epoxy
25 parts of resin, 2 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, 6 parts of silane coupling agent, 10 parts of organobentonite, 15 parts of talcum powder, first
29 parts of solvent, the content of second component are as follows: in parts by weight, 68 parts of vinyl triamine, 23 parts of the second solvent.
In a preferred embodiment of the present invention, the content of first component are as follows: in parts by weight, bisphenol type epoxy
24 parts of resin, 3 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, 5 parts of silane coupling agent, 11 parts of organobentonite, 14 parts of talcum powder, first
31 parts of solvent, the content of second component are as follows: in parts by weight, 65 parts of vinyl triamine, 25 parts of the second solvent.
The beneficial effects of the present invention are: it is of the invention based on the formula for improving coating tolerance, there is extraordinary anti-corrosion
Effect is resistant to the corrosion of the chemicals such as acid, alkali, salt, oil, and free from the influence of the external environment, long service life, the later period is not
It is repaired, there is extraordinary using effect.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiments of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's all other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
Embodiment one:
It provides a kind of based on the formula for improving coating tolerance, including the first component and the second component, first component
Including bisphenol A type epoxy resin, polyoxyethylene polyoxy propyl alcohol amidogen ether, silane coupling agent, organobentonite, talcum powder, first molten
Agent, second component include vinyl triamine, the second solvent.The content of first component are as follows: in parts by weight, bisphenol-A
20 parts of type epoxy resin, 5 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, 3 parts of silane coupling agent, 13 parts of organobentonite, talcum powder 11
Part, 34 parts of the first solvent, the content of second component are as follows: in parts by weight, 60 parts of vinyl triamine, 30 parts of the second solvent.
Embodiment two:
It provides a kind of based on the formula for improving coating tolerance, including the first component and the second component, first component
Including bisphenol A type epoxy resin, polyoxyethylene polyoxy propyl alcohol amidogen ether, silane coupling agent, organobentonite, talcum powder, first molten
Agent, second component include vinyl triamine, the second solvent.The content of first component are as follows: in parts by weight, bisphenol-A
26 parts of type epoxy resin, 1 part of polyoxyethylene polyoxy propyl alcohol amidogen ether, 7 parts of silane coupling agent, 9 parts of organobentonite, talcum powder 16
Part, 28 parts of the first solvent, the content of second component are as follows: in parts by weight, 70 parts of vinyl triamine, 20 parts of the second solvent.
Embodiment three:
It provides a kind of based on the formula for improving coating tolerance, including the first component and the second component, first component
Including bisphenol A type epoxy resin, polyoxyethylene polyoxy propyl alcohol amidogen ether, silane coupling agent, organobentonite, talcum powder, first molten
Agent, second component include vinyl triamine, the second solvent.The content of first component are as follows: in parts by weight, bisphenol-A
21 parts of type epoxy resin, 4 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, 4 parts of silane coupling agent, 12 parts of organobentonite, talcum powder 12
Part, 33 parts of the first solvent, the content of second component are as follows: in parts by weight, 62 parts of vinyl triamine, 28 parts of the second solvent.
Example IV:
It provides a kind of based on the formula for improving coating tolerance, including the first component and the second component, first component
Including bisphenol A type epoxy resin, polyoxyethylene polyoxy propyl alcohol amidogen ether, silane coupling agent, organobentonite, talcum powder, first molten
Agent, second component include vinyl triamine, the second solvent.The content of first component are as follows: in parts by weight, bisphenol-A
25 parts of type epoxy resin, 2 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, 6 parts of silane coupling agent, 10 parts of organobentonite, talcum powder 15
Part, 29 parts of the first solvent, the content of second component are as follows: in parts by weight, 68 parts of vinyl triamine, 23 parts of the second solvent.
Embodiment five:
It provides a kind of based on the formula for improving coating tolerance, including the first component and the second component, first component
Including bisphenol A type epoxy resin, polyoxyethylene polyoxy propyl alcohol amidogen ether, silane coupling agent, organobentonite, talcum powder, first molten
Agent, second component include vinyl triamine, the second solvent.The content of first component are as follows: in parts by weight, bisphenol-A
24 parts of type epoxy resin, 3 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, 5 parts of silane coupling agent, 11 parts of organobentonite, talcum powder 14
Part, 31 parts of the first solvent, the content of second component are as follows: in parts by weight, 65 parts of vinyl triamine, 25 parts of the second solvent.
The beneficial effects of the present invention are:
One, it is described based on improve coating tolerance formula have extraordinary anti-corrosion effect, be resistant to acid, alkali,
The corrosion of the chemicals such as salt, oil；
Two, described free from the influence of the external environment based on the formula for improving coating tolerance, long service life, the later period is not required to
It is repaired, there is extraordinary using effect.
The above description is only an embodiment of the present invention, is not intended to limit the scope of the invention, all to utilize this hair
Equivalent structure or equivalent flow shift made by bright description is applied directly or indirectly in other relevant technology necks
Domain is included within the scope of the present invention.
Claims (6)
1. a kind of based on the formula for improving coating tolerance, which is characterized in that including the first component and the second component, described first
Component includes bisphenol A type epoxy resin, polyoxyethylene polyoxy propyl alcohol amidogen ether, silane coupling agent, organobentonite, talcum powder,
One solvent, second component include vinyl triamine, the second solvent, the content of first component are as follows: in parts by weight, double
20-26 parts of phenol A type epoxy resin, 1-5 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, 3-7 parts of silane coupling agent, organobentonite 9-13
Part, 11-16 parts of talcum powder, 28-34 parts of the first solvent, the content of second component are as follows: in parts by weight, vinyl triamine
60-70 parts, 20-30 parts of the second solvent.
2. according to claim 1 based on the formula for improving coating tolerance, which is characterized in that first component contains
Amount are as follows: in parts by weight, 20 parts of bisphenol A type epoxy resin, 3 parts of silane coupling agent, has 5 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether
13 parts of machine bentonite, 11 parts of talcum powder, 34 parts of the first solvent, the content of second component are as follows: in parts by weight, vinyl three
60 parts of amine, 30 parts of the second solvent.
3. according to claim 1 based on the formula for improving coating tolerance, which is characterized in that first component contains
Amount are as follows: in parts by weight, 26 parts of bisphenol A type epoxy resin, 7 parts of silane coupling agent, has 1 part of polyoxyethylene polyoxy propyl alcohol amidogen ether
9 parts of machine bentonite, 16 parts of talcum powder, 28 parts of the first solvent, the content of second component are as follows: in parts by weight, vinyl three
70 parts of amine, 20 parts of the second solvent.
4. according to claim 1 based on the formula for improving coating tolerance, which is characterized in that first component contains
Amount are as follows: in parts by weight, 21 parts of bisphenol A type epoxy resin, 4 parts of silane coupling agent, has 4 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether
12 parts of machine bentonite, 12 parts of talcum powder, 33 parts of the first solvent, the content of second component are as follows: in parts by weight, vinyl three
62 parts of amine, 28 parts of the second solvent.
5. according to claim 1 based on the formula for improving coating tolerance, which is characterized in that first component contains
Amount are as follows: in parts by weight, 25 parts of bisphenol A type epoxy resin, 6 parts of silane coupling agent, has 2 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether
10 parts of machine bentonite, 15 parts of talcum powder, 29 parts of the first solvent, the content of second component are as follows: in parts by weight, vinyl three
68 parts of amine, 23 parts of the second solvent.
6. according to claim 1 based on the formula for improving coating tolerance, which is characterized in that first component contains
Amount are as follows: in parts by weight, 24 parts of bisphenol A type epoxy resin, 5 parts of silane coupling agent, has 3 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether
11 parts of machine bentonite, 14 parts of talcum powder, 31 parts of the first solvent, the content of second component are as follows: in parts by weight, vinyl three
65 parts of amine, 25 parts of the second solvent.