CN108947467A - A kind of road pattern sign coating and road line marker based on phosphorus magnesium material - Google Patents
A kind of road pattern sign coating and road line marker based on phosphorus magnesium material Download PDFInfo
- Publication number
- CN108947467A CN108947467A CN201810798808.7A CN201810798808A CN108947467A CN 108947467 A CN108947467 A CN 108947467A CN 201810798808 A CN201810798808 A CN 201810798808A CN 108947467 A CN108947467 A CN 108947467A
- Authority
- CN
- China
- Prior art keywords
- bucket
- road
- stirring
- line marker
- magnesium material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of road pattern sign coating and road line marker based on phosphorus magnesium material, and the road pattern sign coating includes that magnesium phosphate cement, additive, admixture, pigment, bead are uniformly mixed;The road line marker includes the raw material bucket being installed in rack, pigment bucket, bucket, stirring bucket, transfer hopper, driving motor, control device, spray head and infrared ambulator, driving motor output shaft is connect by transmission shaft with wheel, raw material bucket, pigment bucket, bucket pass through connecting pipe respectively and are connected to stirring bucket entrance, stirring bucket, transfer hopper and spray head are sequentially communicated, driving motor control terminal, control device and infrared ambulator composition control circuit;Using technical solution of the present invention, by the way that infrared ambulator is arranged in bottom of the frame, road line marker is monitored relative to the position on road in real time, further according to the operation of monitored results control rack Shang Ge executing agency, improves scribing line construction efficiency and drawn line quality.
Description
Technical field
The invention belongs to road construction equipment technology field more particularly to a kind of road pattern sign coatings based on phosphorus magnesium material
And road line marker.
Background technique
Currently, with the rapid development of our country's economy, a large amount of road has been built in China in recent years, road line marker is main
For drawing various traffic signs, such as zebra stripes, zebra crossing, divisional line etc. on different kinds of roads road surface, right
It during road carries out scribing line construction, first has to select suitable mechanical equipment according to the surface state of road, for example, holding sway
When road is narrow, big machinery construction equipment is difficult to enter or has to close road in the construction process, influences
Traffic order, at this moment, with regard to being suitable for crossing using small-sized lines on road surface equipment or using manual method, however, existing
Compact road scoring equipment in use, often occur scribing line irregularity, especially cross to curved road
When, it is necessary to each section of road is detected using manual method, consumes a large amount of hand labor time, construction progress is slow
Slowly, construction efficiency is not high.
Summary of the invention
In order to solve the above technical problems, the present invention provides a kind of road pattern sign coatings based on phosphorus magnesium material and road to draw
Line machine.
The present invention is achieved by the following technical programs.
The present invention provides a kind of road pattern sign coating based on phosphorus magnesium material, including following components raw material according to following quality
Number is uniformly mixed:
The magnesium phosphate cement is to be made after dead burned magnesia and monoammonium phosphate are mixed according to the ratio uniform of 1~4:1.
In addition, the present invention also provides a kind of road sign paintings using as claimed in claim 1 or 2 based on phosphorus magnesium material
The road line marker of material, including rack, be separately installed in the rack raw material bucket, pigment bucket, bucket, stirring bucket, transfer hopper,
Driving motor and control device, the bottom of the frame are equipped with spray head and infrared ambulator towards ground, the driving electricity
Machine output shaft is connect by transmission shaft with wheel, and the raw material bucket, pigment bucket, bucket pass through connecting pipe respectively and stirring bucket enters
Mouth connection, stirring bucket outlet are connected to the transfer hopper entrance, and the transfer hopper outlet is connected to by delivery pipe with the spray head,
The driving motor control terminal and the control device output end are electrically connected, the control device input terminal and the infrared ray
Rangefinder is electrically connected.
The raw material bucket, pigment bucket and bucket bottom are from top to bottom sequentially installed with solenoid valve and automatic weighing device, electromagnetism
Valve and automatic weighing device control terminal are electrically connected with the control device output end.
The infrared ambulator quantity is two, respectively symmetrically is installed at left and right sides of the bottom of the frame.
Stirring motor is installed on the stirring bucket outer wall, is equipped with stirring blade within the stirring bucket, stirring motor is defeated
Shaft is protruded within stirring bucket and is linked together with stirring blade, and stirring motor control terminal and the control device output end are electrical
Connection.
Be also equipped with battery and charging-discharging controller in the rack, the battery feed output end respectively with stirring
Motor, driving motor control terminal are electrically connected, and the battery control terminal is defeated by charging-discharging controller and the control device
Outlet electrical connection.
Delivery pump is also connected in the middle part of the delivery pipe, delivery pump control terminal and the control device are electrically connected.
Filter screen is also equipped between the transfer hopper bottom and delivery pipe inlet.
Bead bucket is also equipped in the rack, bead bucket installation site is located at the road based on phosphorus magnesium material
The scraper plate with ground face contact is also installed in the rear side of pen machine direction of travel, bead bucket bottom.
The beneficial effects of the present invention are: technical solution of the present invention is used, by drawing in the road based on phosphorus magnesium material
Line motor spindle be arranged infrared ambulator, in real time to the road line marker based on phosphorus magnesium material relative to the position on road into
Row monitoring monitors in real time in signal feeding control device obtained and carries out processing and operation, then passes through control device to vehicle
Upper various executing agencies issue corresponding instruction, make these executing agency's coordinated operations and work, make to export road in stirring bucket
The speed and vehicle travel speed that the speed and vehicle travel speed of mark coating match, spray head made to spray road pattern sign coating
Match, raw material bucket, pigment bucket and bucket is made to configure raw material according to suitable match ratio, meeting makes the road based on phosphorus magnesium material
The demand that road pen machine is crossed while advancing improves scribing line construction efficiency, alleviates labor intensity, improves scribing line
Quality is filtered the road pattern sign coating that will be crossed in addition, delivery pipe inlet is mounted with filter screen, makes to spray
The road pattern sign coating that head sprays more uniformly is sprayed on road, and filters out impurity therein, improves drawn line quality, and
And delivery pump blocking is effectively prevented, it protects the normal table of delivery pump to run, extends service life, by being arranged in machine
The road pattern sign coating of sprinkling on the ground is smoothed out immediately, makes the uniform shakedown of road pattern sign coating by the bead bucket of frame bottom
It spreads out, makes the coating content adhered at the lines each point drawn out more evenly, further improve drawn line quality.
Detailed description of the invention
Fig. 1 is structural schematic diagram of the invention;
In figure: 1- raw material bucket, 2- pigment bucket, 3- bucket, 4- rack, 5- handle, 6- antiskid glue sleeve, 7- stirring motor, 9-
Charging-discharging controller, 10- battery, 11- control device, 12- bead bucket, 13- scraper plate, 15- infrared ambulator, 16- spray
Head, 17- delivery pipe, 18- delivery pump, 19- filter screen, 20- driving motor, 21- transmission shaft, 22- transfer hopper, 23- wheel, 24-
Car light, 25- stirring bucket, 26- stirring blade, 27- automatic weighing device, 28- solenoid valve.
Specific embodiment
Be described further below technical solution of the present invention, but claimed range be not limited to it is described.
As shown in Figure 1, the present invention provides a kind of road pattern sign coating and road line marker based on phosphorus magnesium material, the base
Including in the road pattern sign coating of phosphorus magnesium material is a kind of road road sign based on polymer-type aqueous made of magnesium phosphate cement
Will coating, the road pattern sign coating are mixed by following each component according to following mass fraction proportion:
Further, magnesium phosphate cement be dead burned magnesia and monoammonium phosphate in proportion: the mixture of 1~4:1;Weight
Burned magnesium oxide feature are as follows: 1600 DEG C or more burnt magnesite, content of magnesia be 88%~95%, fineness be 80~
400 mesh;Monoammonium phosphate feature are as follows: the monoammonium phosphate of industrial products rank, nutrient are not less than 58%, and fineness is 60~400 mesh.
Further, additive be borax, defoaming agent and water-reducing agent, borax feature are as follows: the other borax of technical grade, purity with
Mass percent is not less than 95%, and fineness is 60~400 mesh;Defoaming agent is organic silicon powder defoaming agent;
Further, admixture be flyash, metakaolin mixture, feature are as follows: flyash: metakaolin=2~4:
1, flyash grade is not less than second class powered coal ash, and fineness is 200~1600 mesh;Metakaolin is 800 DEG C or more burnt height
Ridge soil, fineness are 800~1600 mesh.
Further, pigment is inorganic pigment, feature are as follows: synthetic inorganic pigment, fineness are 100~400 mesh;Inorganic pigment
Contained in the activity of metal oxide be below the activity of magnesia, further act as aquation magnesium phosphate and aquation ammonium magnesium phosphate
The aggregate of crystal structure improves the stability of material.
Further, bead feature are as follows: the granule size range of glass microballoon is 100~1000 microns;Glass used
Glass microballon, most of is the bead of spheroidal, and this glass microballoon needs to be surface-treated by special process, so that microballon
Surface is not influenced vulnerable to moisture content, steam, and refraction coefficient is not less than 1.4 at normal temperature;
The road pattern sign coating is a kind of road pattern sign coating of aqueous polymer-type, is wieldy road sign
Paint;Construction is coated on road surface, good, early strength high 1h compression strength 30MPa or more, flexural strength 5MPa with infiltration wetability
Above, closure adhesive force is strong, quick-drying is wear-resisting, resistance to water logging solarization, it is non-slip, easy for construction (can construct at a lower temperature,
5 DEG C), it is at low cost, be easy to recoat etc. overall merits, especially its low VOC value (almost without);This phosphorus magnesium material main body is water
Base, it is non-ignitable not quick-fried, nontoxic, therefore give the environment after construction site security reliability, the health care of construction personnel, construction
Protection, brings the result of affirmative;Road pattern sign coating preparation process is simple, can be carried out continuous preparation and constructs, is time-consuming short,
And environmental protection and energy saving.
Not only intensity is high for the road pattern sign coating, and setting time it is controllable, with road deck adhesive property is good, service life
It is long.Selected high density magnesia and monoammonium phosphate, monoammonium phosphate and magnesia reaction rate be faster than same type monopotassium phosphate,
Monosodium phosphate, the intensity prepared using monoammonium phosphate is higher, and is classified as 1~4 using mass ratio between magnesia and monoammonium phosphate:
1, magnesia is excessive, guarantees that phosphate component is reacted thoroughly completely, and the complete magnesium oxide particle of unreacted, its own intensity is high, makees
For aggregate, micro aggregate effect is generated, further increases the intensity of phosphorus magnesium material, magnesium oxide particle fineness is between 80~400 mesh
Effect is optimal.The bubble generated during dephosphorization magnesium material mix is removed using defoaming agent, improves compactness, improves intensity.Using
Water-reducing agent improves the fluidity of phosphorus magnesium material, lowers water consumption, improves phosphorus magnesium material workability and guarantees high intensity simultaneously.Using
Borax adjusts the setting time of phosphorus magnesium material as retarder by adjusting volume, and being recommended to use, effect in range is best,
And intensity is negatively affected small.Using flyash and metakaolin with reactivity, flyash is presented spherical shape, plays and fill out
Microscopic voids are filled, while improving phosphorus magnesium material workability, so that compactness improves between phosphorus magnesium material and road deck, interface is viscous
Tie closer, the effect that fineness of pulverized-coal ash plays within the scope of 200~1600 mesh is best;And in flyash, metakaolin
It reacts between activated aluminum component and phosphate and magnesia in phosphorus magnesium material, improves phosphorus magnesium material high temperature resistance, mention
Activated aluminum component is more in high service life, especially metakaolin, and metakaolin fineness uses between 800~1600 mesh, activity
Height also avoids excessively high fineness from adversely affecting workability.Being improved using the bead for adding 5~15 parts improves pavement marking paint
Reflecting properties, to improve the safety of driving at night.
The road line marker based on phosphorus magnesium material includes rack 4, and raw material bucket 1, pigment bucket are separately installed in rack 4
2, bucket 3, stirring bucket 25, transfer hopper 22, driving motor 20 and control device 11,4 bottom of rack are equipped with the spray towards ground
First 16 and infrared ambulator 15,20 output shaft of driving motor is connect by transmission shaft 21 with wheel 23, raw material bucket 1, pigment bucket
2, bucket 3 is connected to by connecting pipe with 25 entrance of stirring bucket respectively, and the outlet of stirring bucket 25 is connected to 22 entrance of transfer hopper, is conveyed
22 outlet of bucket is connected to by delivery pipe 17 with spray head 16, and 20 control terminal of driving motor and 11 output end of control device are electrically connected,
11 input terminal of control device and infrared ambulator 15 are electrically connected.
Using technical solution of the present invention, by the way that infrared distance measuring is arranged in the lines on road surface motor spindle based on phosphorus magnesium material
Instrument is in real time monitored the road line marker based on phosphorus magnesium material relative to the position on road, and real time monitoring is obtained
Signal be sent into control device and carry out processing and operation, then by control device on vehicle various executing agencies issue it is corresponding
Instruction, make these executing agency's coordinated operations and work, make the speed and vehicle row of output road pattern sign coating in stirring bucket
Match into speed, the speed of spray head ejection road pattern sign coating and vehicle travel speed is made to match, make raw material bucket, pigment bucket
With bucket according to suitable match ratio configure raw material, meet make that the road line marker based on phosphorus magnesium material is .ed while advancing
The demand of scribing line improves scribing line construction efficiency, alleviates labor intensity, improves drawn line quality, in addition, delivery pipe inlet
It is mounted with filter screen, the road pattern sign coating that will be crossed is filtered, the road pattern sign coating for spraying spray head is more
It is equably sprayed on road, and filters out impurity therein, improve drawn line quality, and it is stifled to effectively prevent delivery pump
Plug, protects the normal table of delivery pump to run, extends service life, will by the way that the bead bucket of bottom of the frame is arranged in
The road pattern sign coating of sprinkling on the ground smoothes out immediately, spreads out and puts on out road pattern sign coating equably, makes the lines drawn out
The coating content adhered at each point more evenly, further improves drawn line quality.
Further, raw material bucket 1, pigment bucket 2 and 3 bottom of bucket are from top to bottom sequentially installed with solenoid valve 28 and automatic title
Measuring device 27, solenoid valve 28 and 27 control terminal of automatic weighing device are electrically connected with 11 output end of control device.
Further, 15 quantity of infrared ambulator is two, respectively symmetrically is installed at left and right sides of 4 bottom of rack.
Using technical solution of the present invention, preferably 15 quantity of infrared ambulator is two, in order to vehicle relative to both sides of the road
The distance of curb carries out real-time monitoring, lays a good foundation to improve drawn line quality.
Further, stirring motor 7 is installed on 25 outer wall of stirring bucket, stirring blade 26 is equipped within stirring bucket 25, stirs
It mixes 7 output shaft of motor and protrudes within stirring bucket 25 and link together with stirring blade 26,7 control terminal of stirring motor and control device
11 output ends are electrically connected.26 quantity of stirring blade is 3 groups, and is axially arranged along 7 output shaft of stirring motor, arbitrary neighborhood two
Spacing is equal between group stirring blade 26.
Further, battery 10 and charging-discharging controller 9,10 power output end of battery point are also equipped in rack 4
It is not electrically connected with stirring motor 7,20 control terminal of driving motor, 10 control terminal of battery passes through charging-discharging controller 9 and control
The electrical connection of 11 output end of device.Delivery pump 18,11 electricity of 18 control terminal of delivery pump and control device are also connected in the middle part of delivery pipe 17
Property connection.Using technical solution of the present invention, solenoid valve 28, automatic weighing device 27, delivery pump 18, infrared range-measurement system 15, driving
Motor 20, battery 10, car light 24, stirring motor 7 are electrically connected with control device 11, charging-discharging controller 9 and battery
10 are electrically connected, and facilitate and control the feeding amount of various raw materials, pigment or water, make road pattern sign coating in strict accordance with phase
The proportion answered is stirred mixing, improves the preparation quality of road pattern sign coating, lays a good foundation to improve drawn line quality.
Further, filter screen 19 is also equipped between 17 inlet of 22 bottom of transfer hopper and delivery pipe.Also pacify in rack 4
Equipped with bead bucket 12,12 installation site of bead bucket is based on the rear side of the road line marker direction of travel of phosphorus magnesium material,
12 bottom of bead bucket is also installed by the scraper plate 13 with ground face contact.Using technical solution of the present invention, the installation of delivery pipe inlet
Filter screen, is filtered the road pattern sign coating that will be crossed, and the road pattern sign coating for spraying spray head is more evenly
Ground is sprayed on road, and filters out impurity therein, improves drawn line quality, and effectively prevents delivery pump blocking, is protected
The normal table operation for having protected delivery pump, extends service life, by the way that the bead bucket of bottom of the frame is arranged in, will be sprayed at
Road pattern sign coating on ground smoothes out immediately, spreads out and puts on out road pattern sign coating equably, makes at the lines each point drawn out
The coating content of attachment more evenly, further improves drawn line quality.
Further, handle 5 is also equipped in rack 4,5 installation site of handle is based on the lines on road surface of phosphorus magnesium material
The rear side of machine direction of travel, 5 outer surface of handle are also wrapped on antiskid glue sleeve 6.Car light 24 is also equipped in rack 4, car light 24 is pacified
Holding position is based on the front side of the road line marker direction of travel of phosphorus magnesium material.Using technical solution of the present invention, convenient for applying
Worker person carries out scribing line construction to road at night, reduces the influence to traffic order, is convenient to pass through people by handle 5
Work pushes vehicle to advance, and convenient for transfer construction equipment, and due to being equipped with driving motor in rack, construction personnel is turning
When moving vehicle, very big physical strength will not be expended, labor intensity is alleviated.
Claims (10)
1. a kind of road pattern sign coating based on phosphorus magnesium material, it is characterised in that: including following components raw material according to following quality
Number is uniformly mixed:
2. the road pattern sign coating as described in claim 1 based on phosphorus magnesium material, it is characterised in that: the magnesium phosphate cement is
Dead burned magnesia and monoammonium phosphate are made after mixing according to the ratio uniform of 1:1~4:1.
3. a kind of road line marker using the road pattern sign coating as claimed in claim 1 or 2 based on phosphorus magnesium material, feature
It is: including rack (4), raw material bucket (1), pigment bucket (2), bucket (3), stirring bucket is separately installed on the rack (4)
(25), transfer hopper (22), driving motor (20) and control device (11), rack (4) bottom are equipped with the spray towards ground
Head (16) and infrared ambulator (15), driving motor (20) output shaft are connect by transmission shaft (21) with wheel (23),
The raw material bucket (1), pigment bucket (2), bucket (3) are connected to by connecting pipe with stirring bucket (25) entrance respectively, stirring bucket
(25) outlet is connected to the transfer hopper (22) entrance, and transfer hopper (22) outlet passes through delivery pipe (17) and the spray head
(16) it is connected to, driving motor (20) control terminal and the control device (11) output end are electrically connected, the control device
(11) input terminal and the infrared ambulator (15) are electrically connected.
4. the road line marker as claimed in claim 3 based on phosphorus magnesium material, it is characterised in that: the raw material bucket (1), pigment
Bucket (2) and bucket (3) bottom is from top to bottom sequentially installed with solenoid valve (28) and automatic weighing device (27), solenoid valve (28) and oneself
Dynamic weigher (27) control terminal is electrically connected with the control device (11) output end.
5. the road line marker as claimed in claim 3 based on phosphorus magnesium material, it is characterised in that: the infrared ambulator
(15) quantity is two, respectively symmetrically is installed at left and right sides of the rack (4) bottom.
6. the road line marker as claimed in claim 3 based on phosphorus magnesium material, it is characterised in that: stirring bucket (25) outer wall
On be equipped with stirring motor (7), be equipped with stirring blade (26) within the stirring bucket (25), stirring motor (7) output shaft protrudes into
It links together within stirring bucket (25) with stirring blade (26), stirring motor (7) control terminal and the control device (11) are defeated
Outlet is electrically connected.
7. the road line marker as claimed in claim 3 based on phosphorus magnesium material, it is characterised in that: also pacify on the rack (4)
Equipped with battery (10) and charging-discharging controller (9), battery (10) power output end respectively with stirring motor (7), drive
Dynamic motor (20) control terminal is electrically connected, and battery (10) control terminal is filled by charging-discharging controller (9) and the control
Set the electrical connection of (11) output end.
8. the road line marker as claimed in claim 7 based on phosphorus magnesium material, it is characterised in that: in the middle part of the delivery pipe (17)
It is also connected with delivery pump (18), delivery pump (18) control terminal and the control device (11) are electrically connected.
9. the road line marker as claimed in claim 3 based on phosphorus magnesium material, it is characterised in that: transfer hopper (22) bottom
Filter screen (19) are also equipped between delivery pipe (17) inlet.
10. the road line marker as claimed in claim 3 based on phosphorus magnesium material, it is characterised in that: also pacify on the rack (4)
Equipped with bead bucket (12), bead bucket (12) installation site is located at the road line marker direction of travel based on phosphorus magnesium material
Rear side, bead bucket (12) bottom also install with ground face contact scraper plate (13).