CN108943314A - A kind of wood-based plate and preparation method thereof - Google Patents
A kind of wood-based plate and preparation method thereof Download PDFInfo
- Publication number
- CN108943314A CN108943314A CN201810694726.8A CN201810694726A CN108943314A CN 108943314 A CN108943314 A CN 108943314A CN 201810694726 A CN201810694726 A CN 201810694726A CN 108943314 A CN108943314 A CN 108943314A
- Authority
- CN
- China
- Prior art keywords
- parts
- wood
- based plate
- spare
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to artificial board technology fields, more particularly to a kind of wood-based plate and preparation method thereof, is mainly crushed, boiling processing, dry, group embryo, hot-forming and etc. is made through raw material by raw materials such as sawdust, bamboo scraps, peanut shell, stalk, bagasse, exquisite grass, Rhododendron molle, artemisia annua, mouse muscle, the lily of the valley, digitalis lanata, camphortree leaf, Basil, flame nettle, silicic acid powder, worm pyrethroids powder, rectorite particle, natural gum material and organic solvents.Wood-based plate made from wood-based plate produced by the present invention has the excellent performances such as moisture absorption, sound insulation, heat-insulated, fire-retardant, the erosion of ant, cockroach, mouse, bacterium etc. can effectively be walked quickly and kept away, erosion ratio decline, service life extends, performance is good, to improve the economic benefit of wood-based plate, and preparation process is simple, easy to produce.
Description
Technical field
The present invention relates to artificial board technology fields, and in particular to a kind of wood-based plate and preparation method thereof.
Background technique
Wood-based plate is centainly to be machined using timber or other non-wood plants as raw material and be separated into various unit materials
Afterwards, apply or do not apply adhesive and other additives it is glued made of plate or molded article.It mainly include glued board, wood shavings
The three categories product such as (particle) plate and fiberboard, extension product and deep processed product reach hundreds of.The birth of wood-based plate, mark
Timber processing modernization period beginning.But wood-based plate long-time service will receive gnawing for ant, cockroach, mouse etc., sternly
It shortens the working life again.
Summary of the invention
Goal of the invention of the invention is: in view of the above problems, providing a kind of wood-based plate and preparation method thereof, system
The wood-based plate obtained has the excellent performances such as moisture absorption, sound insulation, heat-insulated, fire-retardant, can effectively walk quickly and keep away ant, cockroach, mouse, bacterium etc.
It corroding, erosion ratio decline, service life extends, and performance is good, so that the economic benefit of wood-based plate is improved, and preparation process is simple,
It is easy to produce.
To achieve the goals above, The technical solution adopted by the invention is as follows:
A kind of wood-based plate is mainly made of following raw material: 20-40 parts of sawdust, 15-20 parts of bamboo scraps, peanut shell 5-7
Part, 3-5 parts of stalk, 10-15 parts of bagasse, exquisite 10-20 parts of grass, 10-15 parts of Rhododendron molle, 12-14 parts of artemisia annua, mouse muscle
13-15 parts, 5-7 parts of the lily of the valley, 5-10 parts of digitalis lanata, 10-13 parts of camphortree leaf, 11-13 parts of Basil, 12-14 parts of flame nettle,
2-4 parts of silicic acid powder, 3-5 parts of worm pyrethroids powder, 3-7 parts of rectorite particle, 20-30 parts of natural gum material and 10-15 parts of organic solvent.
Preferably, be mainly made of following raw material: 30 parts of sawdust, 17 parts of bamboo scraps, 6 parts of peanut shell, 4 parts of stalk,
13 parts of bagasse, careless 15 parts exquisite, 13 parts of Rhododendron molle, 13 parts of artemisia annua, 14 parts of mouse muscle, 6 parts of the lily of the valley, 7 parts of digitalis lanata,
11.5 parts of camphortree leaf, 12 parts of Basil, 13 parts of flame nettle, 3 parts of silicic acid powder, 4 parts of worm pyrethroids powder, 5 parts of rectorite particle, natural gum
25 parts and 13 parts of organic solvent of material.
Preferably, the natural gum material is mainly by one in the gum arabic of equal mass ratioes, lignin glue, shellac and rosin
Kind or a variety of mix.
Preferably, the organic solvent is mainly by one of acetone, methyl ethyl ketone and ethyl acetate of equal mass ratioes or more
Kind mixes.
The production method of wood-based plate as described above, specifically includes the following steps:
(1) it after sawdust, bamboo scraps, peanut shell, stalk and bagasse being gone removal of impurities, crushes, crosses 100-200 mesh, mixed
Object A is closed, it is spare；
(2) water is added to surface is not expected admittedly excessively toward said mixture A, is uniformly mixed, maintain temperature after being heated to boiling
It is 50-70 DEG C, continues boiling 1-2h, pick up rinsed clean, drain surface moisture, it is spare；
(3) by exquisite grass, Rhododendron molle, artemisia annua, mouse muscle, the lily of the valley, digitalis lanata, camphortree leaf, Basil and color leaf
It after grass removal of impurities is cleaned, crushes, 2-3 times of water is added, be heated to maintaining temperature after boiling being 60-80 DEG C of progress infusion 20-30min, it is standby
With；
(4) the mixture A for handling step (2) well is added in step (3), after mixing evenly, continues infusion 1-2h, passes through
Rinse 2-3 times after filter, then filter residue is placed in baking oven dry to moisture content be less than 5%, it is spare；
(5) natural gum material is dissolved in organic solvent, filter residue, silicic acid powder, worm pyrethroids after adding step (4) drying
Powder and rectorite particle, are uniformly mixed, and obtain mixture, spare；
(6) mixture of step (5) being put into assembly in mold, progress is hot-forming, and it is cooling, the wood-based plate is made.
Preferably, pressure when hot-forming described in step (6) is 30-50Pa, and temperature is 150-250 DEG C, when pressing
Between be 10-20min.
In conclusion by adopting the above-described technical solution, the beneficial effects of the present invention are:
Wood-based plate of the invention is mainly by sawdust, bamboo scraps, peanut shell, stalk, bagasse, exquisite grass, Rhododendron molle, chrysanthemum
Wormwood artemisia, mouse muscle, the lily of the valley, digitalis lanata, camphortree leaf, Basil, flame nettle, silicic acid powder, worm pyrethroids powder, rectorite particle, day
The right raw materials such as sizing material and organic solvent crush through raw material, boiling processing, dry, group embryo, hot-forming and etc. are made；Wherein,
Effective component contained in exquisite grass, Rhododendron molle, artemisia annua and mouse muscle has good avoidance effect to mouse etc.；The lily of the valley and hair
Effective component contained in flower digitalis has severe toxicity, there is poisoning and walk quickly and keep away bacterium, ant, cockroach, mouse etc.；Camphortree leaf, nine
Effective component contained in layer tower and flame nettle can not only effectively walk quickly and keep away ant, cockroach, mouse etc., also there is certain sterilization to kill
Worm effect；Silicic acid powder and worm pyrethroids powder have sterilization and disinsection effect；Wood-based plate made of the addition of rectorite particle not only has suction
Wet, sound insulation, heat-proof quality, but also there is fire protecting performance；Wood-based plate made from these raw materials has moisture absorption, sound insulation, heat-insulated, resistance
The excellent performances such as combustion can effectively walk quickly and keep away the erosion of ant, cockroach, mouse, bacterium etc., erosion ratio decline, and service life extends, property
Can be good, so that the economic benefit of wood-based plate is improved, and preparation process is simple, it is easy to produce.
Specific embodiment
Technical solution of the present invention will be clearly and completely described below, it is clear that described embodiment is only
A part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, those of ordinary skill in the art
Every other embodiment obtained without making creative work, shall fall within the protection scope of the present invention.
Unless otherwise defined, all technical and scientific terms used herein and belong to technical field of the invention
The normally understood meaning of technical staff is identical.Term as used herein in the specification of the present invention is intended merely to description tool
The purpose of the embodiment of body, it is not intended that in the limitation present invention.Term " and or " used herein includes one or more phases
Any and all combinations of the listed item of pass.
Embodiment 1
A kind of wood-based plate is mainly made of following raw material: 20 parts of sawdust, 15 parts of bamboo scraps, 5 parts of peanut shell, stalk 3
Part, 10 parts of bagasse, careless 10 parts exquisite, 10 parts of Rhododendron molle, 12 parts of artemisia annua, 13 parts of mouse muscle, 5 parts of the lily of the valley, digitalis lanata 5
It is part, 10 parts of camphortree leaf, 11 parts of Basil, 12 parts of flame nettle, 2 parts of silicic acid powder, 3 parts of worm pyrethroids powder, 3 parts of rectorite particle, natural
20 parts of sizing material and 10 parts of organic solvent；
Wherein, natural gum material is mainly mixed by the gum arabic and lignin glue of equal mass ratioes；Organic solvent is main
For acetone.
The expectation of said ratio is prepared into wood-based plate using following methods, specifically includes the following steps:
(1) it after sawdust, bamboo scraps, peanut shell, stalk and bagasse being gone removal of impurities, crushes, sieves with 100 mesh sieve, obtain mixture
A, it is spare；
(2) water is added to surface is not expected admittedly excessively toward said mixture A, is uniformly mixed, maintain temperature after being heated to boiling
It is 50 DEG C, continues boiling 1h, pick up rinsed clean, drain surface moisture, it is spare；
(3) by exquisite grass, Rhododendron molle, artemisia annua, mouse muscle, the lily of the valley, digitalis lanata, camphortree leaf, Basil and color leaf
It after grass removal of impurities is cleaned, crushes, 2 times of water is added, be heated to maintaining temperature after boiling being 60 DEG C of progress infusion 20min, it is spare；
(4) the mixture A for handling step (2) well is added in step (3), after mixing evenly, continues infusion 1h, through filtering
Afterwards rinse 2 times, then by filter residue be placed in baking oven dry to moisture content be less than 5%, it is spare；
(5) natural gum material is dissolved in organic solvent, filter residue, silicic acid powder, worm pyrethroids after adding step (4) drying
Powder and rectorite particle, are uniformly mixed, and obtain mixture, spare；
(6) mixture of step (5) is put into assembly in mold, carries out hot-forming, pressure 30Pa, temperature 150
DEG C, pressing time 10min is cooling, and the wood-based plate is made.
Embodiment 2
A kind of wood-based plate is mainly made of following raw material: 30 parts of sawdust, 17 parts of bamboo scraps, 6 parts of peanut shell, stalk 4
Part, 13 parts of bagasse, careless 15 parts exquisite, 13 parts of Rhododendron molle, 13 parts of artemisia annua, 14 parts of mouse muscle, 6 parts of the lily of the valley, digitalis lanata 7
Part, 11.5 parts of camphortree leaf, 12 parts of Basil, 13 parts of flame nettle, 3 parts of silicic acid powder, 4 parts of worm pyrethroids powder, rectorite particle 5 part, day
Right 25 parts and 13 parts of organic solvent of sizing material；
Wherein, natural gum material is mainly mixed by the shellac and rosin of equal mass ratioes；Organic solvent mainly by etc. quality
The methyl ethyl ketone and ethyl acetate of ratio mix.
The expectation of said ratio is prepared into wood-based plate using following methods, specifically includes the following steps:
(1) it after sawdust, bamboo scraps, peanut shell, stalk and bagasse being gone removal of impurities, crushes, crosses 150 meshes, obtain mixture
A, it is spare；
(2) water is added to surface is not expected admittedly excessively toward said mixture A, is uniformly mixed, maintain temperature after being heated to boiling
It is 60 DEG C, continues boiling 1.5h, pick up rinsed clean, drain surface moisture, it is spare；
(3) by exquisite grass, Rhododendron molle, artemisia annua, mouse muscle, the lily of the valley, digitalis lanata, camphortree leaf, Basil and color leaf
It after grass removal of impurities is cleaned, crushes, 2.5 times of water is added, be heated to maintaining temperature after boiling being 70 DEG C of progress infusion 25min, it is spare；
(4) the mixture A for handling step (2) well is added in step (3), after mixing evenly, continues infusion 1.5h, passes through
Rinse 3 times after filter, then filter residue is placed in baking oven dry to moisture content be less than 5%, it is spare；
(5) natural gum material is dissolved in organic solvent, filter residue, silicic acid powder, worm pyrethroids after adding step (4) drying
Powder and rectorite particle, are uniformly mixed, and obtain mixture, spare；
(6) mixture of step (5) is put into assembly in mold, carries out hot-forming, pressure 40Pa, temperature 200
DEG C, pressing time 15min is cooling, and the wood-based plate is made.
Embodiment 3
A kind of wood-based plate is mainly made of following raw material: 40 parts of sawdust, 20 parts of bamboo scraps, 7 parts of peanut shell, stalk 5
Part, 15 parts of bagasse, careless 20 parts exquisite, 15 parts of Rhododendron molle, 14 parts of artemisia annua, 15 parts of mouse muscle, 7 parts of the lily of the valley, digitalis lanata
10 parts, 13 parts of camphortree leaf, 13 parts of Basil, 14 parts of flame nettle, 4 parts of silicic acid powder, 5 parts of worm pyrethroids powder, rectorite particle 7 part, day
Right 30 parts and 15 parts of organic solvent of sizing material；
Wherein, natural gum material is mainly mixed by gum arabic, lignin glue, shellac and the rosin of equal mass ratioes；Have
Solvent is mainly mixed by acetone, methyl ethyl ketone and the ethyl acetate of equal mass ratioes.
The expectation of said ratio is prepared into wood-based plate using following methods, specifically includes the following steps:
(1) it after sawdust, bamboo scraps, peanut shell, stalk and bagasse being gone removal of impurities, crushes, crosses 200 meshes, obtain mixture
A, it is spare；
(2) water is added to surface is not expected admittedly excessively toward said mixture A, is uniformly mixed, maintain temperature after being heated to boiling
It is 70 DEG C, continues boiling 2h, pick up rinsed clean, drain surface moisture, it is spare；
(3) by exquisite grass, Rhododendron molle, artemisia annua, mouse muscle, the lily of the valley, digitalis lanata, camphortree leaf, Basil and color leaf
It after grass removal of impurities is cleaned, crushes, 3 times of water is added, be heated to maintaining temperature after boiling being 80 DEG C of progress infusion 30min, it is spare；
(4) the mixture A for handling step (2) well is added in step (3), after mixing evenly, continues infusion 2h, through filtering
Afterwards rinse 3 times, then by filter residue be placed in baking oven dry to moisture content be less than 5%, it is spare；
(5) natural gum material is dissolved in organic solvent, filter residue, silicic acid powder, worm pyrethroids after adding step (4) drying
Powder and rectorite particle, are uniformly mixed, and obtain mixture, spare；
(6) mixture of step (5) is put into assembly in mold, carries out hot-forming, pressure 50Pa, temperature 250
DEG C, pressing time 20min is cooling, and the wood-based plate is made.
Wood-based plate made from 1-3 of the embodiment of the present invention and commercially available synthetic plate are carried out correlated performance detection comparison by applicant,
The results are shown in Table 1:
The correlated performance detection of 1 each group wood-based plate of table
| Classification | It is commercially available | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| The erosion ratios such as cockroach, ant % | 25 | 5.6 | 4.1 | 3.6 |
| Service life/year | 5.5 | 7.3 | 7.8 | 8.5 |
From 1 data of table it is found that wood-based plate made from the application can effectively walk quickly and keep away invading for ant, cockroach, mouse, bacterium etc.
Erosion, erosion ratio have dropped about 80%, and service life extends about 43%, and performance is good, to improve the economic benefit of wood-based plate.
Above description is the detailed description for the present invention preferably possible embodiments, but embodiment is not limited to this hair
Bright patent claim, it is all the present invention suggested by technical spirit under completed same changes or modifications change, should all belong to
In the covered the scope of the patents of the present invention.
Claims (6)
1. a kind of wood-based plate, which is characterized in that be mainly made of following raw material: 20-40 parts of sawdust, 15-20 parts of bamboo scraps,
5-7 parts of peanut shell, 3-5 parts of stalk, 10-15 parts of bagasse, exquisite 10-20 parts of grass, 10-15 parts of Rhododendron molle, artemisia annua 12-14
Part, 13-15 parts of mouse muscle, 5-7 parts of the lily of the valley, 5-10 parts of digitalis lanata, 10-13 parts of camphortree leaf, 11-13 parts of Basil, color leaf
12-14 parts careless, 2-4 parts of silicic acid powder, 3-5 parts of worm pyrethroids powder, 3-7 parts of rectorite particle, 20-30 parts of natural gum material and organic solvent
10-15 parts.
2. wood-based plate according to claim 1, which is characterized in that be mainly made of following raw material: 30 parts of sawdust,
17 parts of bamboo scraps, 6 parts of peanut shell, 4 parts of stalk, 13 parts of bagasse, careless 15 parts exquisite, 13 parts of Rhododendron molle, 13 parts of artemisia annua, mouse muscle
14 parts, 6 parts of the lily of the valley, 7 parts of digitalis lanata, 11.5 parts of camphortree leaf, 12 parts of Basil, 13 parts of flame nettle, 3 parts of silicic acid powder, worm chrysanthemum
4 parts of ester powder, 5 parts of rectorite particle, 25 parts of natural gum material and 13 parts of organic solvent.
3. wood-based plate according to claim 1 or 2, it is characterised in that: the natural gum material mainly by equal mass ratioes Ah
It draws one of uncle's natural gum, lignin glue, shellac and rosin or a variety of mixes.
4. wood-based plate according to claim 1 or 2, it is characterised in that: the organic solvent is mainly by the third of equal mass ratioes
One of ketone, methyl ethyl ketone and ethyl acetate a variety of mix.
5. the production method of wood-based plate described in any one of -4 according to claim 1, which is characterized in that specifically include following step
It is rapid:
(1) it after sawdust, bamboo scraps, peanut shell, stalk and bagasse being gone removal of impurities, crushes, crosses 100-200 mesh, obtain mixture
A, it is spare；
(2) water is added to surface is not expected admittedly excessively toward said mixture A, is uniformly mixed, maintain temperature for 50- after being heated to boiling
70 DEG C, continues boiling 1-2h, pick up rinsed clean, drain surface moisture, it is spare；
(3) exquisite grass, Rhododendron molle, artemisia annua, mouse muscle, the lily of the valley, digitalis lanata, camphortree leaf, Basil and flame nettle are removed
It is miscellaneous clean after, crush, 2-3 times of water be added, be heated to maintaining temperature after boiling being 60-80 DEG C of progress infusion 20-30min, it is spare；
(4) the mixture A for handling step (2) well is added in step (3), after mixing evenly, continues infusion 1-2h, after filtering
Then filter residue is placed in baking oven and dries to moisture content as less than 5% by rinsing 2-3 time, spare；
(5) natural gum material is dissolved in organic solvent, add step (4) it is dry after filter residue, silicic acid powder, worm pyrethroids powder and
Rectorite particle, is uniformly mixed, and obtains mixture, spare；
(6) mixture of step (5) being put into assembly in mold, progress is hot-forming, and it is cooling, the wood-based plate is made.
6. the production method of wood-based plate according to claim 5, it is characterised in that: when hot-forming described in step (6)
Pressure be 30-50Pa, temperature be 150-250 DEG C, pressing time 10-20min.