CN108929550A - A kind of vegetable fiber environmental protection material and preparation method thereof - Google Patents
A kind of vegetable fiber environmental protection material and preparation method thereof Download PDFInfo
- Publication number
- CN108929550A CN108929550A CN201810930679.2A CN201810930679A CN108929550A CN 108929550 A CN108929550 A CN 108929550A CN 201810930679 A CN201810930679 A CN 201810930679A CN 108929550 A CN108929550 A CN 108929550A
- Authority
- CN
- China
- Prior art keywords
- parts
- environmental protection
- vegetable
- protection material
- silk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of vegetable fiber environmental protection materials and preparation method thereof, it is related to environment-friendly materials technical field, in parts by mass, the vegetable fiber environmental protection material include 8-10 parts of butadiene-styrene copolymer, 2-4 parts of styrene, 12-18 parts of vegetable silk, 0.5-1 parts of zinc stearate, 8-12 parts of sodium bentonite, 3-4 parts of starch, 6-10 parts of carbon dust, 5-15 parts of calcium carbonate, 2-5 parts of oil, sawdust 1-5 parts thin, 10-20 parts of epoxy resin, 1-3 parts of toughener, 10-15 parts of K resin, it is flax silk 5-10 parts thin, 30-50 parts of clean water.Heat-resisting, wear-resisting property is good using vegetable fiber environmental protection material of the invention, toughness is strong, long service life.Suitable for promoting, by adding vegetable silk in raw material, so that material is more environmentally-friendly, and vegetable fiber environmental protection material has the effect of that intensity is high.
Description
Technical field
The present invention relates to environment-friendly materials fields, and in particular to a kind of vegetable fiber environmental protection material and preparation method thereof.
Background technique
Electric wire is made of one or a few soft conducting wire, and outer bread is with light and soft sheath;Cable is by one or several
Root insulating bag conducting wire composition, outside is wrapped again with metal or tough and tensile outer layer made of rubber.Cable and electric wire are generally all by core wire, insulation
Three component part compositions of foreskin and protection crust.The characteristic of common cable is as follows: the ethylene propylene rubber insulated neoprene shield of CEF--
Set, flame retardant power cable for ship.CVV-- polyvinyl chloride insulation, insulated polyvinyl-chloride-sheathed marine flame-proof power cable.
There is not environmentally friendly enough, production processing technology is cumbersome, cost is excessively high for the covering material that prior art uses
Problem, therefore, it is necessary to design a kind of vegetable fiber environmental protection material and preparation method thereof for being able to solve problem above.
Summary of the invention
The problem to be solved by the invention is to provide a kind of vegetable fiber environmental protection materials and preparation method thereof.
The purpose of the present invention can be achieved through the following technical solutions:
A kind of vegetable fiber environmental protection material, in parts by mass, the vegetable fiber environmental protection material include butadiene-styrene
8-10 parts of copolymer, 2-4 parts of styrene, 12-18 parts of vegetable silk, 0.5-1 parts of zinc stearate, sodium bentonite 8-12
Part, 3-4 parts of starch, 6-10 parts of carbon dust, 5-15 parts of calcium carbonate, 2-5 parts of oil, sawdust 1-5 parts thin, 10-20 parts of epoxy resin, toughening
1-3 parts of agent, 10-15 parts of K resin, it is flax silk 5-10 parts thin, 30-50 parts of clean water.
Further, the vegetable fiber environmental protection material includes 10 parts of butadiene-styrene copolymer, styrene 3 part, thread
15 parts of shape plant fiber, 0.8 part of zinc stearate, 10 parts of sodium bentonite, 4 parts of starch, 8 parts of carbon dust, 10 parts of calcium carbonate, oil 3 parts,
Thin 3 parts of sawdust, 15 parts of epoxy resin, 2 parts of toughener, 12 parts of K resin, 8 parts of thin flax silk, 40 parts of clean water.
A method of preparing vegetable fiber environmental protection material described in claim 1-2 any one, the preparation method
Specifically includes the following steps:
Step 1: preparing butadiene-styrene copolymer 8-10 parts, 2-4 parts of styrene, vegetable silk as requested
12-18 parts, 0.5-1 parts of zinc stearate, 8-12 parts of sodium bentonite, 3-4 parts of starch, 6-10 parts of carbon dust, 5-15 parts of calcium carbonate, oil
2-5 parts, sawdust 1-5 parts thin, 10-20 parts of epoxy resin, flax silk 5-10 parts thin, 1-3 parts of toughener, 10-15 parts of K resin, cleaning
30-50 parts of water;
Step 2: calcium carbonate, oil, thin sawdust, epoxy resin, thin flax silk are mixed, in addition clean water stirs 5-8 minutes
To mixture a;
Step 3: the styrene of the amount, vegetable silk, zinc stearate, K resin are first carried out ball milling, then send close
In mill or kneader at 65 DEG C -75 DEG C mixing or mediate 15-20 minute, finally discharge, it is cooling, broken, obtain mixture
b;
Step 4: mixture b is transposed in reactor, butadiene-benzene is slowly added into after being warming up to 105 DEG C -115 DEG C
Ethylene copolymer stirs with being kneaded 12-18 minutes, obtains mixture c;
Step 5: after starch, carbon dust, sodium bentonite, toughener are mixed, be added the obtained mixture a of step 2 and
The mixture c that step 4 obtains;
Step 6: being stirred evenly after the mixture addition clean water obtained to step 5 with blender, the speed of stirring is
1800r/min stirs 8-10min;
It is squeezed Step 7: carrying out melting at 110 DEG C -115 DEG C into the mixture investment extruder that step 6 stirs evenly
Out, the vegetable fiber environmental protection material is obtained after drying.
Further, the oil is the mixture of one of paraffin oil, naphthenic oil or both.
Further, the plant fiber is cotton fiber, silk fiber, bamboo fibre, tossa, one in ramee
Kind.
Further, the temperature melted in extruder described in step 7 is 110 DEG C.
Further, first stage injection pressure is 90bar, second stage injection pressure in extruder described in step 7
Power is 80bar, and phase III injection pressure is 70bar.
Further, the pressure kept in the step 7 is 80bar, and being kept for the time of pressure is 4 seconds, when described cooling
Between be 20 seconds.
Using technical solution of the present invention, preparation step is reasonable, and convenient for operation, process is free from environmental pollution, and prepares
Synthesis vegetable fiber environmental protection material out is heat-resisting, wear-resisting property is good, and toughness is strong, long service life.Suitable for promoting, by former material
Vegetable silk is added in material, so that material is more environmentally-friendly, and vegetable fiber environmental protection material has the effect of that intensity is high.
Specific embodiment
To be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, below with reference to
Specific embodiment, the present invention is further explained.
Embodiment 1:
A kind of vegetable fiber environmental protection material, in parts by mass, the vegetable fiber environmental protection material include butadiene-styrene
8 parts of copolymer, 2 parts of styrene, 12 parts of vegetable silk, 0.5 part of zinc stearate, 8 parts of sodium bentonite, 3 parts of starch, carbon dust
6 parts, 5 parts of calcium carbonate, 2 parts of oil, 1 part of thin sawdust, 10 parts of epoxy resin, 1 part of toughener, 10 parts of K resin, 5 parts of thin flax silk, cleaning
30 parts of water.
A method of preparing above-mentioned vegetable fiber environmental protection material, the preparation method specifically includes the following steps:
Step 1: as requested prepare 8 parts of butadiene-styrene copolymer, 2 parts of styrene, 12 parts of vegetable silk,
0.5 part of zinc stearate, 8 parts of sodium bentonite, 3 parts of starch, 6 parts of carbon dust, 5 parts of calcium carbonate, oily 2 parts, 1 part of thin sawdust, asphalt mixtures modified by epoxy resin
10 parts of rouge, 1 part of toughener, 10 parts of K resin, 5 parts of thin flax silk, 30 parts of clean water;
Step 2: calcium carbonate, oil, thin sawdust, epoxy resin, thin flax silk are mixed, obtained in addition clean water stirs 5 minutes
Mixture a;
Step 3: the styrene of the amount, vegetable silk, zinc stearate, K resin are first carried out ball milling, then send close
In mill or kneader at 65 DEG C mixing or mediate 15 minutes, finally discharging, it is cooling, broken, obtain mixture b;
Step 4: mixture b is transposed in reactor, it is total that butadiene-styrene is slowly added into after being warming up to 105 DEG C
Polymers stirs with being kneaded 12 minutes, obtains mixture c;
Step 5: after starch, carbon dust, sodium bentonite, toughener are mixed, be added the obtained mixture a of step 2 and
The mixture c that step 4 obtains;
Step 6: being stirred evenly after the mixture addition clean water obtained to step 5 with blender, the speed of stirring is
1800r/min stirs 8min;
Step 7: melting extrusion is carried out at 110 DEG C into the mixture investment extruder that step 6 stirs evenly, it is dry
After obtain the vegetable fiber environmental protection material.
Further, the oil is the mixture of one of paraffin oil, naphthenic oil or both.
Further, the plant fiber is cotton fiber, silk fiber, bamboo fibre, tossa, one in ramee
Kind.
Further, the temperature melted in extruder described in step 7 is 110 DEG C.
Further, first stage injection pressure is 90bar, second stage injection pressure in extruder described in step 7
Power is 80bar, and phase III injection pressure is 70bar.
Embodiment 2:
A kind of vegetable fiber environmental protection material, in parts by mass, the vegetable fiber environmental protection material include butadiene-styrene
0 part of copolymer 1,4 parts of styrene, 18 parts of vegetable silk, 1 part of zinc stearate, 12 parts of sodium bentonite, 4 parts of starch, carbon dust
10 parts, 15 parts of calcium carbonate, oil 5 parts, 5 parts of thin sawdust, 20 parts of epoxy resin, 3 parts of toughener, 15 parts of K resin, 10 parts of thin flax silk,
50 parts of clean water.
A method of preparing above-mentioned vegetable fiber environmental protection material, the preparation method specifically includes the following steps:
Step 1: preparing 10 parts of butadiene-styrene copolymer, 4 parts of styrene, vegetable silk 18 as requested
Part, 1 part of zinc stearate, 12 parts of sodium bentonite, 4 parts of starch, 10 parts of carbon dust, 15 parts of calcium carbonate, oily 5 parts, 5 parts of thin sawdust, ring
20 parts of oxygen resin, 3 parts of toughener, 15 parts of K resin, 10 parts of thin flax silk, 50 parts of clean water;
Step 2: calcium carbonate, oil, thin sawdust, epoxy resin, thin flax silk are mixed, obtained in addition clean water stirs 8 minutes
Mixture a;
Step 3: the styrene of the amount, vegetable silk, zinc stearate, K resin are first carried out ball milling, then send close
In mill or kneader at 75 DEG C mixing or mediate 20 minutes, finally discharging, it is cooling, broken, obtain mixture b;
Step 4: mixture b is transposed in reactor, it is total that butadiene-styrene is slowly added into after being warming up to 115 DEG C
Polymers stirs with being kneaded 18 minutes, obtains mixture c;
Step 5: after starch, carbon dust, sodium bentonite, toughener are mixed, be added the obtained mixture a of step 2 and
The mixture c that step 4 obtains;
Step 6: being stirred evenly after the mixture addition clean water obtained to step 5 with blender, the speed of stirring is
1800r/min stirs 10min;
Step 7: melting extrusion is carried out at 115 DEG C into the mixture investment extruder that step 6 stirs evenly, it is dry
After obtain the vegetable fiber environmental protection material.
Further, the oil is the mixture of one of paraffin oil, naphthenic oil or both.
Further, the plant fiber is cotton fiber, silk fiber, bamboo fibre, tossa, one in ramee
Kind.
Further, the temperature melted in extruder described in step 7 is 110 DEG C.
Further, first stage injection pressure is 90bar, second stage injection pressure in extruder described in step 7
Power is 80bar, and phase III injection pressure is 70bar.
Further, the pressure kept in the step 7 is 80bar, and being kept for the time of pressure is 4 seconds, when described cooling
Between be 20 seconds.
Embodiment 3:
A kind of vegetable fiber environmental protection material, in parts by mass, the vegetable fiber environmental protection material include butadiene-styrene
9 parts of copolymer, 3 parts of styrene, 15 parts of vegetable silk, 0.6 part of zinc stearate, 9 parts of sodium bentonite, 3.5 parts of starch, carbon
It is 8 parts of powder, 9 parts of calcium carbonate, 4 parts of oil, 3 parts of thin sawdust, 15 parts of epoxy resin, 2 parts of toughener, 13 parts of K resin, 7 parts of thin flax silk, clear
45 parts of clean water.
A method of preparing above-mentioned vegetable fiber environmental protection material, the preparation method specifically includes the following steps:
Step 1: as requested prepare 9 parts of butadiene-styrene copolymer, 3 parts of styrene, 15 parts of vegetable silk,
0.6 part of zinc stearate, 9 parts of sodium bentonite, 3.5 parts of starch, 8 parts of carbon dust, 9 parts of calcium carbonate, oily 4 parts, 3 parts of thin sawdust, epoxy
15 parts of resin, 2 parts of toughener, 13 parts of K resin, 7 parts of thin flax silk, 45 parts of clean water;
Step 2: calcium carbonate, oil, thin sawdust, epoxy resin, thin flax silk are mixed, obtained in addition clean water stirs 7 minutes
Mixture a;
Step 3: the styrene of the amount, vegetable silk, zinc stearate, K resin are first carried out ball milling, then send close
In mill or kneader at 70 DEG C mixing or mediate 18 minutes, finally discharging, it is cooling, broken, obtain mixture b;
Step 4: mixture b is transposed in reactor, it is total that butadiene-styrene is slowly added into after being warming up to 110 DEG C
Polymers stirs with being kneaded 16 minutes, obtains mixture c;
Step 5: after starch, carbon dust, sodium bentonite, toughener are mixed, be added the obtained mixture a of step 2 and
The mixture c that step 4 obtains;
Step 6: being stirred evenly after the mixture addition clean water obtained to step 5 with blender, the speed of stirring is
1800r/min stirs 9min;
Step 7: melting extrusion is carried out at 113 DEG C into the mixture investment extruder that step 6 stirs evenly, it is dry
After obtain the vegetable fiber environmental protection material.
Further, the oil is the mixture of one of paraffin oil, naphthenic oil or both.
Further, the plant fiber is cotton fiber, silk fiber, bamboo fibre, tossa, one in ramee
Kind.
Further, the temperature melted in extruder described in step 7 is 110 DEG C.
Further, first stage injection pressure is 80bar, second stage injection pressure in extruder described in step 7
Power is 80bar, and phase III injection pressure is 70bar.
Further, the pressure kept in the step 7 is 80bar, and being kept for the time of pressure is 6 seconds, when described cooling
Between be 20 seconds.
Using technical solution of the present invention, preparation step is reasonable, and convenient for operation, process is free from environmental pollution, and prepares
Synthesis vegetable fiber environmental protection material out is heat-resisting, wear-resisting property is good, and toughness is strong, long service life.Suitable for promoting, by former material
Vegetable silk is added in material, so that material is more environmentally-friendly, and vegetable fiber environmental protection material has the effect of that intensity is high.
Obviously present invention specific implementation is not subject to the restrictions described above, as long as using method concept and skill of the invention
The improvement for the various unsubstantialities that art scheme carries out, or not improved the conception and technical scheme of the invention are directly applied to it
Its occasion, it is within the scope of the present invention.
Claims (8)
1. a kind of vegetable fiber environmental protection material, which is characterized in that in parts by mass, the vegetable fiber environmental protection material includes fourth two
Alkene -8-10 parts of styrol copolymer, 2-4 parts of styrene, 12-18 parts of vegetable silk, 0.5-1 parts of zinc stearate, sodium base are swollen
Moisten 8-12 parts of soil, 3-4 parts of starch, 6-10 parts of carbon dust, 5-15 parts of calcium carbonate, 2-5 parts of oil, sawdust 1-5 parts thin, epoxy resin 10-
20 parts, 1-3 parts of toughener, 10-15 parts of K resin, it is flax silk 5-10 parts thin, 30-50 parts of clean water.
2. a kind of vegetable fiber environmental protection material according to claim 1, it is characterised in that: in parts by mass, the plant
Fiber environmental material includes 10 parts of butadiene-styrene copolymer, 3 parts of styrene, 15 parts of vegetable silk, zinc stearate
0.8 part, 10 parts of sodium bentonite, 4 parts of starch, 8 parts of carbon dust, 10 parts of calcium carbonate, oil 3 parts, 3 parts of thin sawdust, 15 parts of epoxy resin,
2 parts of toughener, 12 parts of K resin, 8 parts of thin flax silk, 40 parts of clean water.
3. a kind of method for preparing vegetable fiber environmental protection material described in claim 1-2 any one, which is characterized in that described
Preparation method specifically includes the following steps:
Step 1: preparing butadiene-styrene copolymer 8-10 parts, 2-4 parts of styrene, vegetable silk 12- as requested
18 parts, 0.5-1 parts of zinc stearate, 8-12 parts of sodium bentonite, 3-4 parts of starch, 6-10 parts of carbon dust, 5-15 parts of calcium carbonate, oil 2-5
Part, sawdust 1-5 parts thin, 10-20 parts of epoxy resin, flax silk 5-10 parts thin, 1-3 parts of toughener, 10-15 parts of K resin, clean water
30-50 parts;
Step 2: calcium carbonate, oil, thin sawdust, epoxy resin, thin flax silk are mixed, mixed in addition clean water stirs 5-8 minutes
Close object a;
Step 3: first carrying out ball milling, then sending mixer the styrene of the amount, vegetable silk, zinc stearate, K resin
In kneader at 65 DEG C -75 DEG C mixing or mediate 15-20 minute, finally discharge, it is cooling, broken, obtain mixture b;
Step 4: mixture b is transposed in reactor, butadiene-styrene is slowly added into after being warming up to 105 DEG C -115 DEG C
Copolymer stirs with being kneaded 12-18 minutes, obtains mixture c;
Step 5: the mixture a and step that step 2 obtains is added after starch, carbon dust, sodium bentonite, toughener are mixed
Four obtained mixture c;
Step 6: being stirred evenly after the mixture addition clean water obtained to step 5 with blender, the speed of stirring is
1800r/min stirs 8-10min;
Step 7: carrying out melting extrusion at 110 DEG C -115 DEG C into the mixture investment extruder that step 6 stirs evenly, do
The vegetable fiber environmental protection material is obtained after dry.
4. a kind of vegetable fiber environmental protection material according to claim 1, it is characterised in that: the oil is paraffin oil, cycloalkanes
The mixture of one of oil or both.
5. a kind of vegetable fiber environmental protection material according to claim 1, it is characterised in that: the vegetable silk is cotton
One of flower fiber, silk fiber, bamboo fibre, tossa, ramee.
6. a kind of preparation method of vegetable fiber environmental protection material according to claim 3, it is characterised in that: institute in step 7
The temperature melted in the extruder stated is 110 DEG C.
7. a kind of preparation method for synthesizing vegetable fiber environmental protection material according to claim 6, it is characterised in that: step 7
Described in extruder in first stage injection pressure be 90bar, second stage injection pressure be 80bar, the phase III injection
Pressure is 70bar.
8. a kind of preparation method for synthesizing vegetable fiber environmental protection material according to claim 6, it is characterised in that: the step
The pressure kept in rapid seven is 80bar, and being kept for the time of pressure is 4 seconds, and the cooling time is 20 seconds.