CN108914614A - A kind of manufacturing method of good woven fabric composite sheet - Google Patents
A kind of manufacturing method of good woven fabric composite sheet Download PDFInfo
- Publication number
- CN108914614A CN108914614A CN201811063373.8A CN201811063373A CN108914614A CN 108914614 A CN108914614 A CN 108914614A CN 201811063373 A CN201811063373 A CN 201811063373A CN 108914614 A CN108914614 A CN 108914614A
- Authority
- CN
- China
- Prior art keywords
- composite sheet
- woven fabric
- parts
- astringent sense
- good woven
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of manufacturing method of good woven fabric composite sheet, includes the following steps：Good woven fabric is impregnated in containing in immersion liquid by step 1；Step 2 successively squeezes the good woven fabric handled by step 1, plates, secondary extrusion；Step 3 coats coating liquid；Step 4, solidification, are washed, and drying obtains composite sheet semi-finished product；Printing treatment is carried out in step 5, the composite sheet semi-finished product obtained in step 4 using astringent sense inorganic agent, obtains astringent sense on-slip composite sheet；Astringent sense on-slip composite sheet obtained in step 5 is embossed processing by step 6；Step 7 carries out secondary printing processing using astringent sense inorganic agent on the astringent sense on-slip composite sheet handled by step 6, obtains the good woven fabric composite sheet of finished product.A kind of manufacturing method of good woven fabric composite sheet of the present invention, the good woven fabric composite sheet produced are suitable for production protective gloves, this based sheet is not easy to skid meeting water, and anti-slip effect is good.
Description
Technical field
The present invention relates to fabric manufacturing technology fields, and in particular to be a kind of good woven fabric composite sheet manufacturing method.
Background technique
In some special industries, such as oil well operation, operation on the sea, since working environment is more severe, worker needs
Wear protective gloves.For the ease of worker operation, this kind of protective gloves is usually made of aqueous PU on-slip material, but this kind of protection
Gloves meet water and are easy to skid, and antiskid effect is poor, is unfavorable for the operation of worker instead.
Summary of the invention
The purpose of the present invention is to provide a kind of manufacturing method of good woven fabric composite sheet, the good woven fabric composite sheet produced
Material is suitable for production protective gloves, this based sheet is not easy to skid meeting water, and anti-slip effect is good.
In order to achieve the above objectives, solution of the invention is：
A kind of manufacturing method of good woven fabric composite sheet, includes the following steps：
Good woven fabric is impregnated in containing in immersion liquid by step 1, and described includes the component of following parts by weight containing immersion liquid：100 parts of water,
10~15 parts of DMF；
The good woven fabric handled by step 1 is passed through compression roller and squeezes by step 2, by four-wheel ironing roller 120~
It plates at 130 DEG C, so that moisture content is down to 45~50%, then passes through another common ironing roller and carried out at 150 DEG C~155 DEG C
Secondary extrusion plates；
Step 3 coats coating liquid on the surface of the good woven fabric handled by step 2, and the coating liquid includes following weight
The component of part：It 100 parts of oiliness polyurethane resin, 60~65 parts of DMF, 3~4 parts of colorant, 0.5~1.0 part of abscess regulator, takes off
0.3~0.5 part of DMF auxiliary agent, 5~6 parts of miberal powder, 0.5~2.0 part of astringent sense agent WH-500；
The good woven fabric handled by step 3 is put into coagulating basin and solidifies by step 4, then washes, dries by rinsing bowl
It is dry, obtain the composite sheet semi-finished product that surface is formed with oiliness PU coating；
Printing treatment is carried out in step 5, the composite sheet semi-finished product obtained in step 4 using astringent sense inorganic agent, is obtained
Surface is formed with the astringent sense on-slip composite sheet of astringent sense anti-slip layer；
Astringent sense on-slip composite sheet obtained in step 5 is embossed processing by step 6, and embossing temperature is 210~220
DEG C, embossing pressure is 5~6kg；
Step 7 is carried out at secondary printing on the astringent sense on-slip composite sheet handled by step 6 using astringent sense inorganic agent
Reason, obtains the good woven fabric composite sheet of finished product；
In step 5 and step 7, the astringent sense inorganic agent includes the component of following parts by weight：
70~80 parts of 100 parts of astringent sense agent BC-5189-1, DMF, 40~50 parts of MEK, 20~25 parts of mill base；The astringent sense
The consumption of inorganic agent is 0.015~0.020kg/YD.
In step 3, coating weight of the coating liquid on the surface of good woven fabric is 1.10~1.15kg/m.
In step 4, the water temperature of the rinsing bowl is 25~30 DEG C, and the temperature of the drying is 160~170 DEG C.
In step 5, described print uses 150 mesh printing roller printing, and in step 7, the printing is using 200 mesh printing roll marks
Brush.
After adopting the above technical scheme, a kind of manufacturing method of good woven fabric composite sheet of the present invention, has below beneficial to effect
Fruit：
(1) astringent sense agent is added in coating liquid, so that the PU coating that good woven fabric surface is formed, which has, increases puckery anti-slip effect, when
When good woven fabric composite sheet is made as protective gloves, though in operation composite sheet surface slightly wear, be also able to maintain compared with
Good anti-slip effect；
(2) astringent sense inorganic agent is printed on composite sheet, so that composite sheet has good astringent sense, sheet material meets water
It is not easy to skid, further improves the anti-slip effect of composite sheet；
(3) composite sheet semi-finished product are handled by the way of printing-embossing-printing, the second printing plays
Color effect is repaired, the color difference as caused by high temperature embossing color-change can be prevented, in addition, this technique first printed and be embossed again is taken,
Due to being printed on the reticulate pattern of scrim surfaces formation, the reticulate pattern that can prevent the second printing from generating in this way before destroying when embossing
With print generation before reticulate pattern between overlap, avoid on finished product generate interference line.
Specific embodiment
In order to further explain the technical solution of the present invention, being explained in detail below by specific embodiment the present invention
It states.
Embodiment one
A kind of manufacturing method of good woven fabric composite sheet, includes the following steps：
Good woven fabric is impregnated in containing in immersion liquid, including the component of following parts by weight containing immersion liquid by step 1：100 parts of water, DMF
15 parts；
Step 2 squeezes the good woven fabric handled by step 1 across compression roller, by four-wheel ironing roller at 120 DEG C
Lower pressing then passes through another common ironing roller and carries out secondary extrusion pressing at 150 DEG C, make so that moisture content is down to 50%
Obtaining becomes smooth by the good woven fabric of dipping；
Step 3 coats coating liquid on the surface of the good woven fabric handled by step 2, and coating liquid includes following parts by weight
Component：100 parts of oiliness polyurethane resin, 60 parts of DMF, 4 parts of colorant, 0.5 part of abscess regulator, take off 0.3 part of DMF auxiliary agent, miberal powder
5 parts, 1.5 parts of astringent sense agent WH-500；Coating weight of the coating liquid on the surface of good woven fabric is 1.15kg/m；
The good woven fabric handled by step 3 is put into coagulating basin and solidifies by step 4, the water for being then 30 DEG C by water temperature
Washing trough washing, dries at 170 DEG C, obtains the composite sheet semi-finished product that surface is formed with oiliness PU coating；
Step 5, the composite sheet semi-finished product obtained in step 4 using astringent sense inorganic agent are formed with the one of oiliness PU coating
The printing treatment that 150 mesh print rollers are carried out on face obtains to surface and is formed with the astringent sense on-slip composite sheet of astringent sense anti-slip layer, printing
In treatment process, the consumption of astringent sense inorganic agent is 0.020kg/YD；
Astringent sense on-slip composite sheet obtained in step 5 is embossed processing by step 6, and the embossing temperature of knurling rolls is
210 DEG C, embossing pressure 6kg；
Step 7 is formed with astringent sense anti-slip layer in the astringent sense on-slip composite sheet handled by step 6 using astringent sense inorganic agent
One side on carry out the secondary printing processing of 200 mesh print rollers, obtain the good woven fabric composite sheet of finished product, it is puckery during printing treatment
The consumption for feeling inorganic agent is 0.015kg/YD；
In step 5 and step 7, astringent sense inorganic agent includes the component of following parts by weight：
70 parts of 100 parts of astringent sense agent BC-5189-1, DMF, 50 parts, 20 parts of mill base of MEK (butanone is used as solvent).
In the present embodiment, astringent sense agent WH-500 is commercially available by Yantai Fusong Chemical Co., Ltd., astringent sense agent BC-5189-1
It is commercially available by Jiangsu Baoze Polymer Material Co., Ltd., DMF is bought by Jiangshan Chemical Co Ltd, Zhejiang
It arrives, mill base is commercially available by Shanghai Kai Shiai coating Co., Ltd.
The good woven fabric composite sheet of finished product that the present embodiment obtains is used to make protective gloves, anti-slip effect is good.
Embodiment two
A kind of manufacturing method of good woven fabric composite sheet, includes the following steps：
Good woven fabric is impregnated in containing in immersion liquid, including the component of following parts by weight containing immersion liquid by step 1：100 parts of water, DMF
12 parts；
Step 2 squeezes the good woven fabric handled by step 1 across compression roller, by four-wheel ironing roller at 130 DEG C
Lower pressing then passes through another common ironing roller and carries out secondary extrusion pressing at 155 DEG C, make so that moisture content is down to 45%
Obtaining becomes smooth by the good woven fabric of dipping；
Step 3 coats coating liquid on the surface of the good woven fabric handled by step 2, and coating liquid includes following parts by weight
Component：100 parts of oiliness polyurethane resin, 65 parts of DMF, 4 parts of colorant, 0.7 part of abscess regulator, take off 0.3 part of DMF auxiliary agent, miberal powder
6 parts, 1.8 parts of astringent sense agent WH-500；Coating weight of the coating liquid on the surface of good woven fabric is 1.15kg/m；
The good woven fabric handled by step 3 is put into coagulating basin and solidifies by step 4, the water for being then 30 DEG C by water temperature
Washing trough washing, dries at 170 DEG C, obtains the composite sheet semi-finished product that surface is formed with oiliness PU coating；
Step 5, the composite sheet semi-finished product obtained in step 4 using astringent sense inorganic agent are formed with the one of oiliness PU coating
The printing treatment that 150 mesh print rollers are carried out on face obtains to surface and is formed with the astringent sense on-slip composite sheet of astringent sense anti-slip layer, printing
In treatment process, the consumption of astringent sense inorganic agent is 0.020kg/YD；
Astringent sense on-slip composite sheet obtained in step 5 is embossed processing by step 6, and the embossing temperature of knurling rolls is
215 DEG C, embossing pressure 6kg；
Step 7 is formed with astringent sense anti-slip layer in the astringent sense on-slip composite sheet handled by step 6 using astringent sense inorganic agent
One side on carry out the secondary printing processing of 200 mesh print rollers, obtain the good woven fabric composite sheet of finished product, it is puckery during printing treatment
The consumption for feeling inorganic agent is 0.015kg/YD；
In step 5 and step 7, the astringent sense inorganic agent includes the component of following parts by weight：
75 parts of 100 parts of astringent sense agent BC-5189-1, DMF, 50 parts, 20 parts of mill base of MEK (butanone is used as solvent).
In the present embodiment, astringent sense agent WH-500 is commercially available by Yantai Fusong Chemical Co., Ltd., astringent sense agent BC-5189-1
It is commercially available by Jiangsu Baoze Polymer Material Co., Ltd., DMF is bought by Jiangshan Chemical Co Ltd, Zhejiang
It arrives, mill base is commercially available by Shanghai Kai Shiai coating Co., Ltd.
The good woven fabric composite sheet of finished product that the present embodiment obtains is used to make protective gloves, anti-slip effect is good.
Embodiment three
A kind of manufacturing method of good woven fabric composite sheet, includes the following steps：
Good woven fabric is impregnated in containing in immersion liquid, including the component of following parts by weight containing immersion liquid by step 1：100 parts of water, DMF
10 parts；
Step 2 squeezes the good woven fabric handled by step 1 across compression roller, by four-wheel ironing roller at 125 DEG C
Lower pressing then passes through another common ironing roller and carries out secondary extrusion pressing at 150 DEG C, make so that moisture content is down to 47%
Obtaining becomes smooth by the good woven fabric of dipping；
Step 3 coats coating liquid on the surface of the good woven fabric handled by step 2, and coating liquid includes following parts by weight
Component：100 parts of oiliness polyurethane resin, 62 parts of DMF, 3 parts of colorant, 1.0 parts of abscess regulator, take off 0.5 part of DMF auxiliary agent, miberal powder
5 parts, 2.0 parts of astringent sense agent WH-500；Coating weight of the coating liquid on the surface of good woven fabric is 1.10kg/m；
The good woven fabric handled by step 3 is put into coagulating basin and solidifies by step 4, the water for being then 25 DEG C by water temperature
Washing trough washing, dries at 160 DEG C, obtains the composite sheet semi-finished product that surface is formed with oiliness PU coating；
Step 5, the composite sheet semi-finished product obtained in step 4 using astringent sense inorganic agent are formed with the one of oiliness PU coating
The printing treatment that 150 mesh print rollers are carried out on face obtains to surface and is formed with the astringent sense on-slip composite sheet of astringent sense anti-slip layer, printing
In treatment process, the consumption of astringent sense inorganic agent is 0.020kg/YD；
Astringent sense on-slip composite sheet obtained in step 5 is embossed processing by step 6, and the embossing temperature of knurling rolls is
220 DEG C, embossing pressure 5kg；
Step 7 is formed with astringent sense anti-slip layer in the astringent sense on-slip composite sheet handled by step 6 using astringent sense inorganic agent
One side on carry out the secondary printing processing of 200 mesh print rollers, obtain the good woven fabric composite sheet of finished product, it is puckery during printing treatment
The consumption for feeling inorganic agent is 0.015kg/YD；
In step 5 and step 7, astringent sense inorganic agent includes the component of following parts by weight：
80 parts of 100 parts of astringent sense agent BC-5189-1, DMF, 40 parts, 25 parts of mill base of MEK (butanone is used as solvent).
In the present embodiment, astringent sense agent WH-500 is commercially available by Yantai Fusong Chemical Co., Ltd., astringent sense agent BC-5189-1
It is commercially available by Jiangsu Baoze Polymer Material Co., Ltd., DMF is bought by Jiangshan Chemical Co Ltd, Zhejiang
It arrives, mill base is commercially available by Shanghai Kai Shiai coating Co., Ltd.
The good woven fabric composite sheet of finished product that the present embodiment obtains is used to make protective gloves, anti-slip effect is good.
Above-described embodiment and non-limiting product form and style of the invention, the ordinary skill people of any technical field
The appropriate changes or modifications that member does it, all should be regarded as not departing from patent category of the invention.
Claims (4)
1. a kind of manufacturing method of good woven fabric composite sheet, it is characterised in that：Include the following steps：
Good woven fabric is impregnated in containing in immersion liquid by step 1, and described includes the component of following parts by weight containing immersion liquid：100 parts of water, DMF
10~15 parts；
Step 2 squeezes the good woven fabric handled by step 1 across compression roller, by four-wheel ironing roller 120~130
Plate at DEG C so that moisture content is down to 45~50%, then pass through another common ironing roller carried out at 150~155 DEG C it is secondary
It squeezes and plates；
Step 3 coats coating liquid on the surface of the good woven fabric handled by step 2, and the coating liquid includes following parts by weight
Component：100 parts of oiliness polyurethane resin, 60~65 parts of DMF, 3~4 parts of colorant, 0.5~1.0 part of abscess regulator, de- DMF is helped
0.3~0.5 part of agent, 5~6 parts of miberal powder, 0.5~2.0 part of astringent sense agent WH-500；
The good woven fabric handled by step 3 is put into coagulating basin and solidifies by step 4, then washes by rinsing bowl, drying obtains
Surface is formed with the composite sheet semi-finished product of oiliness PU coating；
Printing treatment is carried out in step 5, the composite sheet semi-finished product obtained in step 4 using astringent sense inorganic agent, obtains surface
It is formed with the astringent sense on-slip composite sheet of astringent sense anti-slip layer；
Astringent sense on-slip composite sheet obtained in step 5 is embossed processing by step 6, and embossing temperature is 210~220 DEG C, pressure
Flower pressure is 5~6kg；
Step 7 carries out secondary printing processing using astringent sense inorganic agent on the astringent sense on-slip composite sheet handled by step 6,
Obtain the good woven fabric composite sheet of finished product；
In step 5 and step 7, the astringent sense inorganic agent includes the component of following parts by weight：
70~80 parts of 100 parts of astringent sense agent BC-5189-1, DMF, MEK40~50 part, 20~25 parts of mill base；The astringent sense processing
The consumption of agent is 0.015~0.020kg/YD.
2. a kind of manufacturing method of good woven fabric composite sheet according to claim 1, it is characterised in that：It is described in step 3
Coating weight of the coating liquid on the surface of good woven fabric is 1.10~1.15kg/m.
3. a kind of manufacturing method of good woven fabric composite sheet according to claim 1, it is characterised in that：It is described in step 4
The water temperature of rinsing bowl is 25~30 DEG C, and the temperature of the drying is 160~170 DEG C.
4. a kind of manufacturing method of good woven fabric composite sheet according to claim 1, it is characterised in that：It is described in step 5
It prints and uses 150 mesh printing roller printing, in step 7, the printing is using 200 mesh printing roller printing.