CN108911652A - A kind of universal waterproofing slurry - Google Patents
A kind of universal waterproofing slurry Download PDFInfo
- Publication number
- CN108911652A CN108911652A CN201810855075.6A CN201810855075A CN108911652A CN 108911652 A CN108911652 A CN 108911652A CN 201810855075 A CN201810855075 A CN 201810855075A CN 108911652 A CN108911652 A CN 108911652A
- Authority
- CN
- China
- Prior art keywords
- water
- slurry
- universal
- preservative
- styrene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to Size Technology field, especially a kind of universal waterproofing slurry, the slurry is made of following mass parts：High alumina cement：35-45；Water-reducing agent：5-10；Styrene-acrylic emulsion：15-25；Preservative：3-5；Defoaming agent：2-4；Lithium carbonate：8-15；Water：10-15.The invention has the advantages that slurry prepared by the present invention has waterproof action.
Description
Technical field
The present invention relates to Size Technology field, especially a kind of universal waterproofing slurry.
Background technique
Slurry is a kind of bi-component waterproof material for being exclusively used in buildings waterproof, by powder part and liquid material part by certain ratio
Example proportion composition.Existing slurry waterproof performance is poor.
Summary of the invention
In order to overcome the shortcomings of existing slurry, the present invention provides a kind of universal waterproofing slurries.
The technical solution adopted by the present invention to solve the technical problems is：A kind of universal waterproofing slurry, the slurry by
Following mass parts composition：
High alumina cement：35-45；Water-reducing agent：5-10；Styrene-acrylic emulsion：15-25；Preservative：3-5；Defoaming agent：2-4；Lithium carbonate：8-
15；Water：10-15.
It according to another embodiment of the invention, further comprise that the slurry is made of following mass parts：High alumina cement：
45；Water-reducing agent：5；Styrene-acrylic emulsion：15；Preservative：3；Defoaming agent：2；Lithium carbonate：8；Water：10.
It according to another embodiment of the invention, further comprise that the slurry is made of following mass parts：High alumina cement：
35；Water-reducing agent：10；Styrene-acrylic emulsion：25；Preservative：5；Defoaming agent：4；Lithium carbonate：15；Water：15.
It according to another embodiment of the invention, further comprise that the slurry is made of following mass parts：High alumina cement：
40；Water-reducing agent：8；Styrene-acrylic emulsion：20；Preservative：4；Defoaming agent：3；Lithium carbonate：10；Water：12.
The invention has the advantages that slurry prepared by the present invention has waterproof action.
Specific embodiment
A kind of universal waterproofing slurry, the slurry are made of following mass parts：
High alumina cement：35-45；Water-reducing agent：5-10；Styrene-acrylic emulsion：15-25；Preservative：3-5；Defoaming agent：2-4；Lithium carbonate：8-
15；Water：10-15.
It according to another embodiment of the invention, further comprise that the slurry is made of following mass parts：High alumina cement：
45；Water-reducing agent：5；Styrene-acrylic emulsion：15；Preservative：3；Defoaming agent：2；Lithium carbonate：8；Water：10.
It according to another embodiment of the invention, further comprise that the slurry is made of following mass parts：High alumina cement：
35；Water-reducing agent：10；Styrene-acrylic emulsion：25；Preservative：5；Defoaming agent：4；Lithium carbonate：15；Water：15.
It according to another embodiment of the invention, further comprise that the slurry is made of following mass parts：High alumina cement：
40；Water-reducing agent：8；Styrene-acrylic emulsion：20；Preservative：4；Defoaming agent：3；Lithium carbonate：10；Water：12.
Claims (4)
1. a kind of universal waterproofing slurry, characterized in that the slurry is made of following mass parts：
High alumina cement：35-45；Water-reducing agent：5-10；Styrene-acrylic emulsion：15-25；Preservative：3-5；Defoaming agent：2-4；Lithium carbonate：8-
15；Water：10-15.
2. a kind of universal waterproofing slurry according to claim 1, characterized in that the slurry is by following mass parts group
At：High alumina cement：45；Water-reducing agent：5；Styrene-acrylic emulsion：15；Preservative：3；Defoaming agent：2；Lithium carbonate：8；Water：10.
3. a kind of universal waterproofing slurry according to claim 1, characterized in that the slurry is by following mass parts group
At：High alumina cement：35；Water-reducing agent：10；Styrene-acrylic emulsion：25；Preservative：5；Defoaming agent：4；Lithium carbonate：15；Water：15.
4. a kind of universal waterproofing slurry according to claim 1, characterized in that the slurry is by following mass parts group
At：High alumina cement：40；Water-reducing agent：8；Styrene-acrylic emulsion：20；Preservative：4；Defoaming agent：3；Lithium carbonate：10；Water：12.