CN108905044A - A kind of the sport rope skipping of wear-resisting type noctilucence and preparation method - Google Patents
A kind of the sport rope skipping of wear-resisting type noctilucence and preparation method Download PDFInfo
- Publication number
- CN108905044A CN108905044A CN201810800498.8A CN201810800498A CN108905044A CN 108905044 A CN108905044 A CN 108905044A CN 201810800498 A CN201810800498 A CN 201810800498A CN 108905044 A CN108905044 A CN 108905044A
- Authority
- CN
- China
- Prior art keywords
- layer
- wear
- steel wire
- coated
- resisting type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of sport rope skippings of wear-resisting type noctilucence and preparation method, including flexible wire ropes, silicone grease filled layer, steel wire braiding layer, tinfoil wrapping layer, Noctilucent material layer and transparent wear, flexible wire ropes are coated on interior by silicone grease filled layer cladding, steel wire braiding layer is coated on outside silicone grease filled layer, tinfoil wrapping layer is coated on outside steel wire braiding layer, Noctilucent material layer is coated on outside tinfoil wrapping layer, and transparent wear is coated on outside Noctilucent material layer.The present invention passes through the flexible wire ropes inside the protection of silicone grease filled layer; not only act as the effect of lubrication; it can also play the role of anti-oxidant antirust; tinfoil package can not only make flexible wire ropes be protected from light and further it is anti-oxidant, also have certain reflecting effect, improve the brightness of Noctilucent material; the continuous illumination time of Noctilucent material can also be improved; transparent wear made of formula especially of the invention, the transparent wear with wear-resisting property can be improved service life, have the value of popularization and application.
Description
Technical field
The present invention relates to a kind of sports goods more particularly to a kind of sport is skipped rope with wear-resisting type noctilucence and preparation method.
Background technique
Rope skipping, is the motor play that a people or everybody do various jump actions in the rope that a ring is put.In the prior art
Rope skipping generally uses the rope made of hemp or wirerope etc, but wirerope surface is not wear-resisting, gets rusty easily, in addition, using the rope made of hemp
It is not durable, in night outdoor in use, not seeing Chu Shengzi, influences very much user experience, accordingly, there exist rooms for improvement yet yet.
Summary of the invention
The object of the invention is that providing a kind of rope skipping of sport wear-resisting type noctilucence and system to solve the above-mentioned problems
Preparation Method.
The present invention is achieved through the following technical solutions above-mentioned purpose：
A kind of sport of the present invention is skipped rope with wear-resisting type noctilucence, including flexible wire ropes, silicone grease filled layer, steel wire braiding layer, tin
The flexible wire ropes are coated on interior, institute by paper bag covering layer, Noctilucent material layer and transparent wear, the silicone grease filled layer cladding
Steel wire braiding layer to be stated to be coated on outside the silicone grease filled layer, the tinfoil wrapping layer is coated on outside the steel wire braiding layer,
The Noctilucent material layer is coated on outside the tinfoil wrapping layer, and the transparent wear is coated on outside the Noctilucent material layer.
Preferably, the flexible wire ropes are that the steel wire of multiply diameter 0.1mm is twisted into the flexible wire ropes of diameter 2mm.
Preferably, the steel wire braiding layer is that the braided steel wire of diameter 0.1mm forms.
Preferably, the tinfoil wrapping layer is that the masking foil of single layer 0.1mm thickness wraps up layer 2-3.
Preferably, the Noctilucent material layer be rare earth material luminescent powder and flexible-epoxy it is mixing cured made of noctilucence
Material.By weight, contain the luminescent powder 15%, the flexible-epoxy 62%, curing agent 23% for every part.
Preferably, the transparent wear is natural rubber, aluminium oxide Ultramicro-powder, chromium oxide, zirconium oxide, acrylic resin
It mixes.By weight, every part containing the natural rubber 75%, the aluminium oxide Ultramicro-powder 10%, the chromium oxide 5%, described
Zirconium oxide 5%, the acrylic resin 5%.
A kind of preparation method that sport is skipped rope with wear-resisting type noctilucence of the present invention, includes the following steps：
（1）The steel wire of diameter 0.1mm is twisted into the flexible wire ropes of diameter 2mm；
（2）By the braided steel wire of diameter 0.1mm in step（1）Flexible wire ropes surface formed steel wire；
（3）By step（2）Steel wire net surface coating silicone grease, and the gap for the flexible wire ropes being substantially filled in steel wire
In；
（4）The masking foil of single layer 0.1mm thickness is wrapped up into layer 2-3 to step（3）Wirerope surface after coating silicone grease；
（5）Luminescent powder is mixed with flexible-epoxy, and add curing agent carry out it is uniformly mixed, be coated on step（4）Tin
Foil paper surface is coated again after to be solidified, until thickness reaches 0.2mm；
（6）Natural rubber is subjected to heating and melting, aluminium oxide Ultramicro-powder, chromium oxide, zirconium oxide, acrylic resin is added and is stirred
It mixes uniformly, step is coated under keeping warm mode（5）Noctilucent material layer surface, coated after cooled and solidified again, until thickness
Reach 0.5-0.8mm, noctilucence rope skipping is made after cooled and solidified.
The beneficial effects of the present invention are：
The present invention is a kind of rope skipping of sport wear-resisting type noctilucence and preparation method, and compared with prior art, the present invention passes through silicone grease
Flexible wire ropes inside filled layer protection, not only act as the effect of lubrication, moreover it is possible to play the role of anti-oxidant antirust, tinfoil packet
Wrap up in can not only make flexible wire ropes be protected from light and further it is anti-oxidant, also have certain reflecting effect, improve Noctilucent material
Brightness, moreover it is possible to improve the continuous illumination time of Noctilucent material, transparent wear made of formula especially of the invention, have resistance to
The transparent wear of mill performance can be improved service life, have the value of popularization and application.
Detailed description of the invention
Fig. 1 is structural schematic diagram of the invention.
In figure：1- flexible wire ropes, 2- silicone grease filled layer, 3- steel wire braiding layer, 4- tinfoil wrapping layer, 5- Noctilucent material
Layer, 6- transparent wear.
Specific embodiment
The present invention will be further explained below with reference to the attached drawings：
As shown in Figure 1：A kind of sport of the present invention is skipped rope with wear-resisting type noctilucence, including flexible wire ropes, silicone grease filled layer, steel wire
Braiding layer, tinfoil wrapping layer, Noctilucent material layer and transparent wear, the silicone grease filled layer are coated the flexible wire ropes packet
In being overlying on, the steel wire braiding layer is coated on outside the silicone grease filled layer, and the tinfoil wrapping layer is coated on the steel wire
Outside braiding layer, the Noctilucent material layer is coated on outside the tinfoil wrapping layer, and the transparent wear is coated on the noctilucence material
Outside the bed of material.
Preferably, the flexible wire ropes are that the steel wire of multiply diameter 0.1mm is twisted into the flexible wire ropes of diameter 2mm.
Preferably, the steel wire braiding layer is that the braided steel wire of diameter 0.1mm forms.
Preferably, the tinfoil wrapping layer is that the masking foil of single layer 0.1mm thickness wraps up layer 2-3.
Preferably, the Noctilucent material layer be rare earth material luminescent powder and flexible-epoxy it is mixing cured made of noctilucence
Material.By weight, contain the luminescent powder 15%, the flexible-epoxy 62%, curing agent 23% for every part.
Preferably, the transparent wear is natural rubber, aluminium oxide Ultramicro-powder, chromium oxide, zirconium oxide, acrylic resin
It mixes.By weight, every part containing the natural rubber 75%, the aluminium oxide Ultramicro-powder 10%, the chromium oxide 5%, described
Zirconium oxide 5%, the acrylic resin 5%.
A kind of preparation method that sport is skipped rope with wear-resisting type noctilucence of the present invention, includes the following steps：
（1）The steel wire of diameter 0.1mm is twisted into the flexible wire ropes of diameter 2mm；
（2）By the braided steel wire of diameter 0.1mm in step（1）Flexible wire ropes surface formed steel wire；
（3）By step（2）Steel wire net surface coating silicone grease, and the gap for the flexible wire ropes being substantially filled in steel wire
In；
（4）The masking foil of single layer 0.1mm thickness is wrapped up into layer 2-3 to step（3）Wirerope surface after coating silicone grease；
（5）Luminescent powder is mixed with flexible-epoxy, and add curing agent carry out it is uniformly mixed, be coated on step（4）Tin
Foil paper surface is coated again after to be solidified, until thickness reaches 0.2mm；
（6）Natural rubber is subjected to heating and melting, aluminium oxide Ultramicro-powder, chromium oxide, zirconium oxide, acrylic resin is added and is stirred
It mixes uniformly, step is coated under keeping warm mode（5）Noctilucent material layer surface, coated after cooled and solidified again, until thickness
Reach 0.5-0.8mm, noctilucence rope skipping is made after cooled and solidified.
Basic principles and main features and advantages of the present invention of the invention have been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (9)
1. a kind of sport is skipped rope with wear-resisting type noctilucence, it is characterised in that：It is compiled including flexible wire ropes, silicone grease filled layer, steel wire
Tissue layer, tinfoil wrapping layer, Noctilucent material layer and transparent wear, the silicone grease filled layer cladding coat the flexible wire ropes
In interior, the steel wire braiding layer is coated on outside the silicone grease filled layer, and the tinfoil wrapping layer is coated on the steel wire and compiles
Outside tissue layer, the Noctilucent material layer is coated on outside the tinfoil wrapping layer, and the transparent wear is coated on the Noctilucent material
Layer is outer.
2. sport according to claim 1 is skipped rope with wear-resisting type noctilucence, it is characterised in that：The flexible wire ropes are multiply
The steel wire of diameter 0.1mm is twisted into the flexible wire ropes of diameter 2mm.
3. sport according to claim 1 is skipped rope with wear-resisting type noctilucence, it is characterised in that：The steel wire braiding layer is straight
The braided steel wire of diameter 0.1mm forms.
4. sport according to claim 1 is skipped rope with wear-resisting type noctilucence, it is characterised in that：The tinfoil wrapping layer is single layer
The masking foil of 0.1mm thickness wraps up layer 2-3.
5. sport according to claim 1 is skipped rope with wear-resisting type noctilucence, it is characterised in that：The Noctilucent material layer is rare earth
Noctilucent material made of material luminescent powder and flexible-epoxy are mixing cured.
6. sport according to claim 5 is skipped rope with wear-resisting type noctilucence, it is characterised in that：By weight, every part containing described
Luminescent powder 15%, the flexible-epoxy 62%, curing agent 23%.
7. sport according to claim 1 is skipped rope with wear-resisting type noctilucence, it is characterised in that：The transparent wear is natural
Rubber, aluminium oxide Ultramicro-powder, chromium oxide, zirconium oxide, acrylic resin mix.
8. sport according to claim 7 is skipped rope with wear-resisting type noctilucence, it is characterised in that：By weight, every part containing described
Natural rubber 75%, the aluminium oxide Ultramicro-powder 10%, the chromium oxide 5%, the zirconium oxide 5%, the acrylic resin 5%.
9. the preparation method that a kind of sport is skipped rope with wear-resisting type noctilucence, which is characterized in that include the following steps：
The steel wire of diameter 0.1mm is twisted into the flexible wire ropes of diameter 2mm；
By the braided steel wire of diameter 0.1mm in step（1）Flexible wire ropes surface formed steel wire；
By step（2）Steel wire net surface coating silicone grease, and in the gap for the flexible wire ropes being substantially filled in steel wire；
The masking foil of single layer 0.1mm thickness is wrapped up into layer 2-3 to step（3）Wirerope surface after coating silicone grease；
Luminescent powder is mixed with flexible-epoxy, and add curing agent carry out it is uniformly mixed, be coated on step（4）Masking foil
Surface is coated again after to be solidified, until thickness reaches 0.2mm；
Natural rubber is subjected to heating and melting, aluminium oxide Ultramicro-powder, chromium oxide, zirconium oxide, acrylic resin is added and is stirred
Uniformly, step is coated under keeping warm mode（5）Noctilucent material layer surface, coated after cooled and solidified again, until thickness reaches
Noctilucence rope skipping is made to 0.5-0.8mm, after cooled and solidified.