CN108893024A - A kind of low-temperature fast-curing electrochemical aluminum paint - Google Patents

A kind of low-temperature fast-curing electrochemical aluminum paint Download PDF

Info

Publication number
CN108893024A
CN108893024A CN201810554393.9A CN201810554393A CN108893024A CN 108893024 A CN108893024 A CN 108893024A CN 201810554393 A CN201810554393 A CN 201810554393A CN 108893024 A CN108893024 A CN 108893024A
Authority
CN
China
Prior art keywords
parts
solvent
curing
electrochemical aluminum
low
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810554393.9A
Other languages
Chinese (zh)
Inventor
贝文理
陈文�
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHEJIANG JOYA POLYMER TECHNOLOGY Co Ltd
Original Assignee
ZHEJIANG JOYA POLYMER TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHEJIANG JOYA POLYMER TECHNOLOGY Co Ltd filed Critical ZHEJIANG JOYA POLYMER TECHNOLOGY Co Ltd
Priority to CN201810554393.9A priority Critical patent/CN108893024A/en
Publication of CN108893024A publication Critical patent/CN108893024A/en
Pending legal-status Critical Current

Abstract

The present invention relates to technical field of coatings, in particular to a kind of electrochemical aluminum paint.The low-temperature fast-curing electrochemical aluminum paint of one kind designed by the present invention, it includes the component of following parts by weight:10-15 parts of self-crosslinking acrylic resin, 3-5 parts of amino resins, 30-50 parts of solvent, 0.3-1 parts of pigment;The self-crosslinking acrylic resin by following parts by weight Material synthesis:80-100 parts of methyl methacrylate, 26-46 parts of butyl acrylate, 20-35 parts of methacrylic acid, 5-15 parts of N hydroxymethyl acrylamide, 2-5 parts of dibenzoyl peroxide, 200-300 parts of solvent;The solvent is the mixed solvent of ketones solvent and alcohols solvent.Electrochemical aluminum paint of the invention can be realized low-temperature fast-curing film forming, while guarantee there is good temperature tolerance and solvent resistance.

Description

A kind of low-temperature fast-curing electrochemical aluminum paint
Technical field
The present invention relates to technical field of coatings, in particular to a kind of electrochemical aluminum paint.
Background technique
With China's economic development, living standards of the people are improved, to the exquisite journey of the product packagings such as cigarette, wine product, tealeaves Degree has a higher requirement, and it is exquisite be packaged with the class for being conducive to improve product brand, so anodized aluminium is as a kind of new Emerging package means, increasingly by the attention of packaging industry.Anodized aluminium, it is also known as gold stamping, mostly using polyester film as basement membrane, It is coated with the material of the various coated coatings with different chemical property thereon, the gum for being coated with similar thermosol after aluminizing again applies Material, then production process is completed using hot moulding and hot stamping technique.
In process of production, it in order to allow coating to reach quick-drying purpose, needs to be toasted at high temperature, baking temperature Degree is at 180 DEG C or more.The hot setting film forming of coating requires height to process conditions, affected by environment big, and needs chargeable heat Can, production cost is relatively high.A kind of electrochemical aluminum paint that can be realized low-temperature fast-curing film forming thus is needed, to substitute mesh It is preceding that there are the hot setting film forming coatings of more problem.
Summary of the invention
It is an object of the invention to overcome the deficiencies of the prior art and provide one kind can be realized low-temperature fast-curing film forming, Guarantee the electrochemical aluminum paint with good temperature tolerance and solvent resistance simultaneously.
In order to achieve the above object, a kind of low-temperature fast-curing electrochemical aluminum paint designed by the present invention, it includes such as The component of lower parts by weight:
10-15 parts of self-crosslinking acrylic resin
3-5 parts of amino resins
30-50 parts of solvent
0.3-1 parts of pigment
The self-crosslinking acrylic resin by following parts by weight Material synthesis:80-100 parts of methyl methacrylate, acrylic acid 26-46 parts of butyl ester, 20-35 parts of methacrylic acid, 5-15 parts of N hydroxymethyl acrylamide, 2-5 parts of dibenzoyl peroxide, solvent 200-300 parts;The solvent is the mixed solvent of ketones solvent and alcohols solvent.
Preferably, the ketones solvent is one or both of butanone, acetone.
Preferably, the alcohols solvent is one or both of isopropanol and ethyl alcohol.
The self-crosslinking acrylic resin is prepared via a method which to obtain:It is passed through nitrogen 5min into reaction vessels, removes Oxygen in dereaction device;Addition solvent, N hydroxymethyl acrylamide, part dibenzoyl peroxide and three points after ventilation One of mix monomer, mix monomer be methyl methacrylate, butyl acrylate and methacrylic acid, start at 75 DEG C into Row pre-reaction 30min;Reaction temperature is increased to start to drip when mixed system temperature in reaction vessels reaches 82 DEG C of set temperature Adding remaining mix monomer and initiator dibenzoyl peroxide, control rate of addition drips off remaining mix monomer in 3.5h, Add remaining initiator after the reaction was continued 1h, then carry out 82 DEG C of heat insulation experiments, soaking time 3h, after completion of the reaction it is cooling go out Material.
Preferably, the amino resins is etherified melamine polyimide resin;
As further preferred, the amino resins is one in U.S.'s cyanogen spy 325, cyanogen spy 303, cyanogen spy 1156 and cyanogen spy 216 Kind is several.
Preferably, the solvent is one or more of isopropanol, ethyl alcohol, butanone, cyclohexanone and toluene.
The acrylic resin of self-crosslinking, the outstanding feature of the acrylic resin are used in electrochemical aluminum paint formula of the invention In a resin, on the one hand this resin can provide good for paint film for the addition for being self-cross linking monomer and high acid value collective effect Good adhesive property, mechanical property and solvent resistance;It on the other hand can be by the addition of Ammonia so that resin itself has Water-soluble feature, this water-soluble resin degree of cross linking is higher, superior performance;Secondly, molten using ketone in terms of the selection of solvent On the one hand the mixing of the mixed solvent of agent and alcohols solvent, both solvents makes resin have good dissolubility(Lower viscous Under degree, the molecular weight of resin can be made to reach the requirement of needs);On the other hand make resin that there is good water solubility, pass through Neutralization can make resin become water-base resin;Last both solvents itself are low boiling point solvents, can be realized the low of resin Warm quick-drying requirement.
There is also innovations in preparation method for the acrylic resin.The addition of N hydroxymethyl acrylamide is needed anti-first It answers in vessel and monomer carries out heating pre-reaction;Secondly using the mixing list of whole N hydroxymethyl acrylamide and one third Body pre-reaction, i.e. N hydroxymethyl acrylamide excessive response, excessive N hydroxymethyl acrylamide can be in addition mix monomers When, it allows N hydroxymethyl acrylamide sufficiently to participate in reaction, improves resin savings rate, and then the crosslinking for improving self-crosslinking resin is close Degree;Meanwhile using the mixed solvent having compared with strong solubility, guarantee the crosslink density of resin;If the dissolution energy of solvent itself Power is weaker, and the viscosity of resin system can be increased sharply in synthetic reaction process, on the one hand may result in sudden and violent poly-, another party's face The movement of molecule segment is rung, so that cross-linking reaction is more difficult to carry out, and then influences the crosslink density of resin.
The performance detection index of self-crosslinking acrylic resin of the present invention is as follows:
1, the viscosity 2000Mpa.S of synthetic resin
2,40 mg/KOH of resinous acid value
3, resin solid content 40%
4,120 DEG C of resin cure temperature;Time 30-50s
The performance detection index of electrochemical aluminum paint of the present invention is as follows:
1, trimming shape is good after allotment is aluminized, no remained on surface
2,110 DEG C of pressing experiment coatings are without shining coloured silk
3, the colourless aluminium segregation phenomenon of coating
4, coating is without obvious firkin phenomenon.
Specific embodiment
Embodiment 1
A kind of low-temperature fast-curing electrochemical aluminum paint, it includes the component of following parts by weight:
10 parts of self-crosslinking acrylic resin
Etherified melamine polyimide resin(U.S. cyanogen spy 325)5 parts
30 parts of isopropanol
1 part of pigment
The self-crosslinking acrylic resin by following parts by weight Material synthesis:80 parts of methyl methacrylate, butyl acrylate 46 parts, 20 parts of methacrylic acid, 15 parts of N hydroxymethyl acrylamide, 2 parts of dibenzoyl peroxide, 200 parts of solvent;The solvent For the mixed solvent of butanone and isopropanol.
The self-crosslinking acrylic resin is prepared via a method which to obtain:It is passed through nitrogen 5min into reaction vessels, removes Oxygen in dereaction device;Addition solvent, N hydroxymethyl acrylamide, part dibenzoyl peroxide and three points after ventilation One of mix monomer, mix monomer be methyl methacrylate, butyl acrylate and methacrylic acid, start at 75 DEG C into Row pre-reaction 30min;Reaction temperature is increased to start to drip when mixed system temperature in reaction vessels reaches 82 DEG C of set temperature Adding remaining mix monomer and initiator dibenzoyl peroxide, control rate of addition drips off remaining mix monomer in 3.5h, Add remaining initiator after the reaction was continued 1h, then carry out 82 DEG C of heat insulation experiments, soaking time 3h, after completion of the reaction it is cooling go out Material.
Embodiment 2
A kind of low-temperature fast-curing electrochemical aluminum paint, it includes the component of following parts by weight:
15 parts of self-crosslinking acrylic resin
Etherified melamine polyimide resin(Cyanogen spy 303)3 parts
50 parts of ethyl alcohol
0.3 part of pigment
The self-crosslinking acrylic resin by following parts by weight Material synthesis:100 parts of methyl methacrylate, butyl acrylate 26 parts, 35 parts of methacrylic acid, 5 parts of N hydroxymethyl acrylamide, 5 parts of dibenzoyl peroxide, 300 parts of solvent;The solvent For the mixed solvent of acetone and ethyl alcohol.
The self-crosslinking acrylic resin is prepared via a method which to obtain:It is passed through nitrogen 5min into reaction vessels, removes Oxygen in dereaction device;Addition solvent, N hydroxymethyl acrylamide, part dibenzoyl peroxide and three points after ventilation One of mix monomer, mix monomer be methyl methacrylate, butyl acrylate and methacrylic acid, start at 75 DEG C into Row pre-reaction 30min;Reaction temperature is increased to start to drip when mixed system temperature in reaction vessels reaches 82 DEG C of set temperature Adding remaining mix monomer and initiator dibenzoyl peroxide, control rate of addition drips off remaining mix monomer in 3.5h, Add remaining initiator after the reaction was continued 1h, then carry out 82 DEG C of heat insulation experiments, soaking time 3h, after completion of the reaction it is cooling go out Material.
Embodiment 3
A kind of low-temperature fast-curing electrochemical aluminum paint, it includes the component of following parts by weight:
12 parts of self-crosslinking acrylic resin
Etherified melamine polyimide resin(Cyanogen spy 1156)4 parts
40 parts of butanone
0.5 part of pigment
The self-crosslinking acrylic resin by following parts by weight Material synthesis:90 parts of methyl methacrylate, butyl acrylate 34 parts, 28 parts of methacrylic acid, 10 parts of N hydroxymethyl acrylamide, 3 parts of dibenzoyl peroxide, 250 parts of solvent;The solvent For the mixed solvent of butanone and ethyl alcohol.
The self-crosslinking acrylic resin is prepared via a method which to obtain:It is passed through nitrogen 5min into reaction vessels, removes Oxygen in dereaction device;Addition solvent, N hydroxymethyl acrylamide, part dibenzoyl peroxide and three points after ventilation One of mix monomer, mix monomer be methyl methacrylate, butyl acrylate and methacrylic acid, start at 75 DEG C into Row pre-reaction 30min;Reaction temperature is increased to start to drip when mixed system temperature in reaction vessels reaches 82 DEG C of set temperature Adding remaining mix monomer and initiator dibenzoyl peroxide, control rate of addition drips off remaining mix monomer in 3.5h, Add remaining initiator after the reaction was continued 1h, then carry out 82 DEG C of heat insulation experiments, soaking time 3h, after completion of the reaction it is cooling go out Material.
Embodiment 4
A kind of low-temperature fast-curing electrochemical aluminum paint, it includes the component of following parts by weight:
13 parts of self-crosslinking acrylic resin
Etherified melamine polyimide resin(Cyanogen spy 325 and cyanogen spy 216)3.5 part
38 parts of toluene
0.6 part of pigment
The self-crosslinking acrylic resin by following parts by weight Material synthesis:95 parts of methyl methacrylate, butyl acrylate 40 parts, 30 parts of methacrylic acid, 9 parts of N hydroxymethyl acrylamide, 4 parts of dibenzoyl peroxide, 265 parts of solvent;The solvent For the mixed solvent of butanone, acetone, isopropanol and ethyl alcohol.
The self-crosslinking acrylic resin is prepared via a method which to obtain:It is passed through nitrogen 5min into reaction vessels, removes Oxygen in dereaction device;Addition solvent, N hydroxymethyl acrylamide, part dibenzoyl peroxide and three points after ventilation One of mix monomer, mix monomer be methyl methacrylate, butyl acrylate and methacrylic acid, start at 75 DEG C into Row pre-reaction 30min;Reaction temperature is increased to start to drip when mixed system temperature in reaction vessels reaches 82 DEG C of set temperature Adding remaining mix monomer and initiator dibenzoyl peroxide, control rate of addition drips off remaining mix monomer in 3.5h, Add remaining initiator after the reaction was continued 1h and then carry out 82 DEG C of heat insulation experiments, soaking time 3h, after completion of the reaction it is cooling go out Material.

Claims (7)

1. a kind of low-temperature fast-curing electrochemical aluminum paint, it is characterised in that:It includes the component of following parts by weight:
10-15 parts of self-crosslinking acrylic resin
3-5 parts of amino resins
30-50 parts of solvent
0.3-1 parts of pigment
The self-crosslinking acrylic resin by following parts by weight Material synthesis:80-100 parts of methyl methacrylate, acrylic acid 26-46 parts of butyl ester, 20-35 parts of methacrylic acid, 5-15 parts of N hydroxymethyl acrylamide, 2-5 parts of dibenzoyl peroxide, solvent 200-300 parts, the solvent is the mixed solvent of ketones solvent and alcohols solvent.
2. the low-temperature fast-curing electrochemical aluminum paint of one kind according to claim 1, it is characterised in that:The self-crosslinking third Olefin(e) acid resin is prepared via a method which to obtain:It is passed through nitrogen 5min into reaction vessels, removes the oxygen in reactor;Ventilation After the mix monomer of solvent, N hydroxymethyl acrylamide, part dibenzoyl peroxide and one third is added, mixing is single Body is methyl methacrylate, butyl acrylate and methacrylic acid, starts to carry out pre-reaction 30min at 75 DEG C;It increases anti- Temperature is answered, when mixed system temperature in reaction vessels reaches 82 DEG C of set temperature, starts that remaining mix monomer is added dropwise and draws Agent dibenzoyl peroxide is sent out, control rate of addition drips off remaining mix monomer in 3.5h, adds residue after the reaction was continued 1h Initiator, then carry out 82 DEG C of heat insulation experiments, soaking time 3h, after completion of the reaction cooling discharging.
3. the low-temperature fast-curing electrochemical aluminum paint of one kind according to claim 1 or 2, it is characterised in that:The ketone Solvent is one or both of butanone, acetone.
4. the low-temperature fast-curing electrochemical aluminum paint of one kind according to claim 1 or 2, it is characterised in that:The alcohols Solvent is one or both of isopropanol and ethyl alcohol.
5. the low-temperature fast-curing electrochemical aluminum paint of one kind according to claim 1 or 2, it is characterised in that:The amino Resin is etherified melamine polyimide resin.
6. the low-temperature fast-curing electrochemical aluminum paint of one kind according to claim 5, it is characterised in that:The amino resins For U.S. cyanogen spy 325, cyanogen spy 303, cyanogen special one or more of 1156 and cyanogen spy 216.
7. the low-temperature fast-curing electrochemical aluminum paint of one kind according to claim 1 or 2, it is characterised in that:The solvent For one or more of isopropanol, ethyl alcohol, butanone, cyclohexanone and toluene.
CN201810554393.9A 2018-06-01 2018-06-01 A kind of low-temperature fast-curing electrochemical aluminum paint Pending CN108893024A (en)