CN108887895A - A kind of composite stone material heating desktop and its manufacturing method - Google Patents
A kind of composite stone material heating desktop and its manufacturing method Download PDFInfo
- Publication number
- CN108887895A CN108887895A CN201810569074.5A CN201810569074A CN108887895A CN 108887895 A CN108887895 A CN 108887895A CN 201810569074 A CN201810569074 A CN 201810569074A CN 108887895 A CN108887895 A CN 108887895A
- Authority
- CN
- China
- Prior art keywords
- marble
- bottom plate
- printed board
- panel
- desktop
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of composite stone material heating desktop and its manufacturing method, composite stone material heats desktop including using marble bottom plate, marble panel and printed board, printed board is equipped with mica heating plate and power supply circuit, marble surface back is equipped with chamber resettling, printed board obverse and reverse passes through cloud stone glue respectively and bonds together with marble panel, marble bottom plate, and power supply circuit accesses input power by cable;Its manufacturing method includes:Grinding marble bottom plate and panel, Milling Process leakage through-hole and chamber resettling, drying and processing, preparation printed board, pressurization bonding marble panel, marble bottom plate and printed board;Using technical solution of the present invention, manufacturing process is simplified, increases the structural strength of heating desktop, extend service life, improve heating desktop surface smoothness, make it have more attractive moulding, the heating desktop can with braced frame composition Table capable of heating carry out using.
Description
Technical field
The invention belongs to equipment technology field more particularly to a kind of composite stone material heating desktop and its manufacturing methods of warming oneself.
Background technique
With the raising of people 's material life level, in cold winter, various electric heating appliances are widely used, existing
Various heaters generally make power supply that heater strip be made to distribute thermal energy, then enable a person to be transferred to each position on human body, in order to
Keep the shape of heater more attractive, so that heater and indoor various furniture, decorative piece is constituted unified style, often by heater
Shape fabricating becomes consistent with the appearance of certain furniture, such as electric-heating table, Tea table with electric heating means etc., is not only easy to use but also saves heating
The parking space of device indoors.In various stone materials, marble has excellent appearance and smooth appearance, by marble stone
Material is used for manufactured various furniture, is well received by consumers, currently, the heater desktop being made using stone of marble
Finding is few, is generally put together by four fan-shaped panels and a piece of circular central panel or muti-piece marble slabstone is laminated and made
Be made, in corresponding control circuit is embedded in, in this way made of heater desktop, surface smoothness is poor, no
Beauty, and due to marble slab out-of-flatness makes between the marble slabstone of stacking adhesive strength highly, not lead to the desktop that heats
It is easy to appear deformation in use, service life is shorter.
Summary of the invention
In order to solve the above technical problems, the present invention provides a kind of composite stone material heating desktop and its manufacturing methods;
The present invention is achieved by the following technical programs;
The present invention provides a kind of composite stone material heating desktop, mainly includes marble bottom plate, marble panel and printing
Plate, the printed board front are equipped with muti-piece mica heating plate, and the printing back is provided with and the mica heating plate electricity
Property connection power supply circuit, the marble surface back is equipped with chamber resettling, and the marble surface back passes through cloud stone glue
It is bonded on the printed board front and is contained in the mica heating plate within chamber resettling, the printing back
Through adhered by marble adhesive on the marble bottom plate, the power supply circuit accesses input power by cable.
The heating power of the mica heating plate is 400W.
It is additionally provided with leakage through-hole on the marble bottom plate, is additionally provided with protective door at the leakage through-hole port.
Be additionally provided on the marble bottom plate with the wire casing that is connected to of leakage through-hole, the cable be contained in wire casing with
It is interior, control switch is also connected on the cable, control switch is installed on the marble plate outer side wall.
In addition, including the following steps the present invention also provides a kind of composite stone material heating desktop manufacturing method:
Step 1:Two pieces of marble slabs are taken, grinding is carried out to two pieces of marble slabs fronts and reverse side, is made described
Two pieces of marble slabs fronts and reverse side surface roughness reach 12.5 microns or less;
Step 2:Milling Process is carried out to two pieces of marble slabs described in step 1, wherein block of marble plate
Upper Milling Process goes out to leak through-hole, and as marble bottom plate, Milling Process goes out chamber resettling in another piece of marble slabs,
As marble panel;
Step 3:Marble bottom plate, marble panel in step 2 after Milling Process is put into baking oven will be attached
In the moisture drying on its outer surface, then be placed at shady and cool ventilation, allow to cool to room temperature;
Step 4:It takes glass mat as substrate, silk screen mask is made in pre-designed circuit diagram, using silk screen
The method of printing prints out power supply circuit on substrate back, and several via holes are processed on substrate, and printed board is made;
Step 5:Cloud stone glue is coated on manufactured printed board obverse and reverse in step 4, is dried passing through in step 3
Marble panel, marble bottom plate after dry-cure are bonded in respectively on printed board obverse and reverse, and to marble panel,
Apply appropriate pressure on marble bottom plate, after marble adhesive curing, is bonded in marble panel, printed board and marble bottom plate
Together.
The composite stone material heating desktop manufacturing method further includes by the marble panel, printed board and marble bottom plate
After bonding together, Milling Process is carried out to its each side using milling machine, material extra on side is removed, makes it have
The appearance profile of rule.
It is to the technological parameter of two pieces of marble slabs progress Milling Process described in step 2:Speed of mainshaft 200r/
Min, amount of feeding 5mm/r.
It is to the technological parameter in two pieces of marble slabs fronts and reverse side progress grinding described in step 1:On grinding machine
The skive that granularity is B100 is configured, the grinding wheel diameter is Φ 150mm, grinding speed 30m/s, and the amount of feeding is
20mm/min。
It is to the technological parameter of marble bottom plate, marble panel progress drying and processing described in step 3:It is warm in baking oven
Degree is 80 DEG C~120 DEG C, and the retention time is 5min~10min in baking oven.
Bonding marble panel described in step 5, printed board and marble bottom plate technological parameter be:To marble surface
Applying pressure on plate, marble bottom plate is:400kgf/m2~600kgf/m2, application pressure duration be 20min~
40min, cloud stone glue dosage are 750mL/m2~1000mL/m2, and cloud stone glue solidification temperature is 20 DEG C~35 DEG C.
The beneficial effects of the present invention are:Using technical solution of the present invention, by cloud stone glue directly by printed board and big
Fibrous gypsum plate is bonded together, and simplifies manufacturing process, the glass fiber component contained in printed board and stone material are compound, by marble
Material composition in slabstone sufficiently tenses, to increase the structural strength of heating desktop, extends its service life, is preparing
It heats during desktop, grinding has been carried out to stone of marble surface, the surface for significantly improving heating desktop is flat
Whole degree makes it have more attractive moulding, and makes cloud stone glue between the faying face between printed board and marble slab plate
Sufficiently rolled, keep printed board Nian Jie with marble slabstone stronger, intensity is also higher, which can be with corresponding support
Frame forms the Table capable of heating of complete set, and when not in use, heating desktop can take out from metal framework, saves parking space.
Detailed description of the invention
Fig. 1 is main view of the invention;
Fig. 2 is left view of the invention;
Fig. 3 is the top view of marble bottom plate of the present invention.
In figure:1- marble bottom plate, 2- marble panel, 3- printed board, 4- mica heating plate, 5- protective door, 6- control
Switch, 7- braced frame, 101- leak through-hole, 201- chamber resettling.
Specific embodiment
Be described further below technical solution of the present invention, but claimed range be not limited to it is described;
The present invention provides a kind of composite stone material heating desktop, as shown in Figure 1, Figure 2, Figure 3 shows, including marble bottom plate 1, Dali
Stone panel 2 and printed board 3,3 front of printed board are equipped with muti-piece mica heating plate 4, and 3 back side of printed board is provided with to be added with mica
The power supply circuit that hot plate 4 is electrically connected, 2 back side of marble panel are equipped with chamber resettling 201, and 2 back side of marble panel passes through cloud
For stone gluing together on 3 front of printed board and being contained in mica heating plate 4 within chamber resettling 201,3 back side of printed board is logical
Adhered by marble adhesive is crossed on marble bottom plate 1, power supply circuit accesses input power by cable.
Using technical solution of the present invention, directly printed board and marble slab are bonded together by cloud stone glue, simplified
Manufacturing process, the glass fiber component and stone material contained in printed board is compound, and the material composition in marble slabstone is abundant
It tenses, to increase the structural strength of heating desktop, extends its service life, it is right during preparation heats desktop
Stone of marble surface has carried out grinding, significantly improves the surface smoothness of heating desktop, makes it have more attractive
Moulding, and roll cloud stone glue sufficiently between the faying face between printed board and marble slab plate, make printed board
Nian Jie with marble slabstone stronger, intensity is also higher, which can form complete set with corresponding braced frame
Table capable of heating, when not in use, heating desktop can take out from metal framework, save parking space.
Further, the heating power of mica heating plate 4 is 400W.Leakage through-hole 101, leakage are additionally provided on marble bottom plate 1
Through-hole is additionally provided with protective door 5 at 101 port.Pass through protective door 5, it is convenient to be safeguarded, be safeguarded to printed board.
Further, the wire casing 102 being connected to leakage through-hole 101 is additionally provided on marble bottom plate 1, cable is contained in wire casing
Control switch 6 is also connected within 102, on cable, control switch 6 is installed on 1 lateral wall of marble bottom plate.Using the present invention
The technical solution of offer, heating desktop can be combined into Table capable of heating with frame 7 being made linking together, and wood can be used in braced frame
Matter structure, steel structure or lithoidite texture are made, and when not in use, heating desktop can take out Table capable of heating from metal framework, save
Parking space.
In addition, including the following steps the present invention also provides a kind of composite stone material heating desktop manufacturing method:
Step 1:Two pieces of marble slabs are taken, grinding is carried out to two pieces of marble slabs fronts and reverse side, makes two pieces
Marble slabs front and reverse side surface roughness reach 12.5 microns or less;Further, to two pieces of marble slabs fronts
And the technological parameter of reverse side progress grinding is:The skive that granularity is B100, grinding wheel diameter Φ are configured on grinding machine
150mm, grinding speed 30m/s, amount of feeding 20mm/min.
Step 2:Milling Process is carried out to two pieces of marble slabs in step 1, is milled on block of marble plate wherein
It cuts and processes leakage through-hole 101, as marble bottom plate 1, Milling Process goes out chamber resettling in another piece of marble slabs
201, as marble panel 2;Further, it is to the technological parameter of two pieces of marble slabs progress Milling Process:It is main
Axis revolving speed 200r/min, amount of feeding 5mm/r.
Step 3:Marble bottom plate 1, marble panel 2 in step 2 after Milling Process is put into baking oven will
The moisture drying being attached on its outer surface, then be placed at shady and cool ventilation, allow to cool to room temperature;Further, to Dali
Stone bottom plate 1, marble panel 2 carry out drying and processing technological parameter be:Oven temperature is 80 DEG C~120 DEG C, is protected in baking oven
Holding the time is 5min~10min.
Step 4:It takes glass mat as substrate, silk screen mask is made in pre-designed circuit diagram, using silk screen
The method of printing prints out power supply circuit on substrate back, and several via holes are processed on substrate, and printed board is made
3;
Step 5:Cloud stone glue is coated on manufactured 3 obverse and reverse of printed board in step 4, is dried passing through in step 3
Marble panel 2, marble bottom plate 1 after dry-cure are bonded in respectively on 3 obverse and reverse of printed board, and to marble surface
Apply appropriate pressure on plate 2, marble bottom plate 1, after marble adhesive curing, makes marble panel 2, printed board 3 and marble bottom
Plate 1 bonds together.Further, composite stone material heating desktop manufacturing method further include by marble panel 2, printed board 3 with
After marble bottom plate 1 bonds together, Milling Process is carried out to its each side using milling machine, removes material extra on side
Material makes it have the appearance profile of rule.Further, it is bonded the technique of marble panel 2, printed board 3 and marble bottom plate 1
Parameter is:Applying pressure on marble panel 2, marble bottom plate 1 is:400kgf/m2~600kgf/m2, apply pressure and continue
Time is 20min~40min, and cloud stone glue dosage is 750mL/m2~1000mL/m2, cloud stone glue solidification temperature is 20 DEG C~35 DEG C.
Using technical solution of the present invention, directly printed board and marble slab are bonded together by cloud stone glue, simplified
Manufacturing process, the glass fiber component and stone material contained in printed board is compound, and the material composition in marble slabstone is abundant
It tenses, to increase the structural strength of heating desktop, extends its service life, it is right during preparation heats desktop
Stone of marble surface has carried out grinding, significantly improves the surface smoothness of heating desktop, makes it have more attractive
Moulding, and roll cloud stone glue sufficiently between the faying face between printed board and marble slab plate, make printed board
Nian Jie with marble slabstone stronger, intensity is also higher, which can form complete set with corresponding braced frame
Table capable of heating, when not in use, heating desktop can take out from metal framework, save parking space.
Claims (10)
- The desktop 1. a kind of composite stone material heats, it is characterised in that:Including marble bottom plate (1), marble panel (2) and printing Plate (3), printed board (3) front are equipped with muti-piece mica heating plate (4), printed board (3) back side be provided with it is described The power supply circuit that mica heating plate (4) is electrically connected, marble panel (2) back side are equipped with chamber resettling (201), described big Fibrous gypsum panel (2) back side on the printed board (3) front and holds the mica heating plate (4) by adhered by marble adhesive It being contained within chamber resettling (201), printed board (3) back side passes through adhered by marble adhesive on the marble bottom plate (1), The power supply circuit accesses input power by cable.
- The desktop 2. composite stone material as described in claim 1 heats, it is characterised in that:The fever function of the mica heating plate (4) Rate is 400W.
- The desktop 3. composite stone material as described in claim 1 heats, it is characterised in that:It is additionally provided on the marble bottom plate (1) It leaks through-hole (101), is additionally provided with protective door (5) at leakage through-hole (101) port.
- The desktop 4. composite stone material as claimed in claim 3 heats, it is characterised in that:It is also set up on the marble bottom plate (1) There is the wire casing (102) being connected to leakage through-hole (101), the cable is contained within wire casing (102), also connects on the cable It is connected to control switch (6), control switch (6) is installed on marble bottom plate (1) lateral wall.
- The desktop manufacturing method 5. a kind of composite stone material heats, it is characterised in that:Include the following steps:Step 1:Two pieces of marble slabs are taken, grinding is carried out to two pieces of marble slabs fronts and reverse side, makes described two pieces Marble slabs front and reverse side surface roughness reach 12.5 microns or less;Step 2:Milling Process is carried out to two pieces of marble slabs described in step 1, is milled on block of marble plate wherein It cuts and processes leakage through-hole (101), as marble bottom plate (1), Milling Process goes out to accommodate in another piece of marble slabs Chamber (201), as marble panel (2);Step 3:Marble bottom plate (1), marble panel (2) in step 2 after Milling Process is put into baking oven will The moisture drying being attached on its outer surface, then be placed at shady and cool ventilation, allow to cool to room temperature;Step 4:It takes glass mat as substrate, silk screen mask is made in pre-designed circuit diagram, using silk-screen printing Method power supply circuit is printed out on substrate back, and process several via holes on substrate, printed board (3) be made;Step 5:Cloud stone glue is coated on manufactured printed board (3) obverse and reverse in step 4, drying will be passed through in step 3 Treated marble panel (2), marble bottom plate (1) are bonded in respectively on printed board (3) obverse and reverse, and to Dali Stone panel (2), marble bottom plate apply appropriate pressure on (1), after marble adhesive curing, make marble panel (2), printed board (3) it bonds together with marble bottom plate (1).
- The desktop manufacturing method 6. composite stone material as claimed in claim 5 heats, it is characterised in that:The composite stone material heating table Face manufacturing method further includes after the marble panel (2), printed board (3) bond together with marble bottom plate (1), making Milling Process is carried out to its each side with milling machine, material extra on side is removed, makes it have the appearance profile of rule.
- The desktop manufacturing method 7. composite stone material as claimed in claim 5 heats, it is characterised in that:To two pieces described in step 2 Marble slabs carry out Milling Process technological parameter be:Speed of mainshaft 200r/min, amount of feeding 5mm/r.
- The desktop manufacturing method 8. composite stone material as claimed in claim 5 heats, it is characterised in that:To two pieces described in step 1 Marble slabs front and reverse side carry out grinding technological parameter be:The boart boart that granularity is B100 is configured on grinding machine Wheel, the grinding wheel diameter are Φ 150mm, grinding speed 30m/s, amount of feeding 20mm/min.
- The desktop manufacturing method 9. composite stone material as claimed in claim 5 heats, it is characterised in that:To Dali described in step 3 Stone bottom plate (1), marble panel (2) carry out drying and processing technological parameter be:Oven temperature is 80 DEG C~120 DEG C, baking oven The interior retention time is 5min~10min.
- The desktop manufacturing method 10. composite stone material as claimed in claim 5 heats, it is characterised in that:It is bonded described in step 5 Marble panel (2), printed board (3) and the technological parameter of marble bottom plate (1) are:To marble panel (2), marble bottom plate (1) applying pressure on is:400kgf/m2~600kgf/m2, application pressure duration is 20min~40min, cloud stone glue dosage For 750mL/m2~1000mL/m2, cloud stone glue solidification temperature is 20 DEG C~35 DEG C.