CN108877486A - in-mold label film and preparation method thereof - Google Patents
in-mold label film and preparation method thereof Download PDFInfo
- Publication number
- CN108877486A CN108877486A CN201810818044.3A CN201810818044A CN108877486A CN 108877486 A CN108877486 A CN 108877486A CN 201810818044 A CN201810818044 A CN 201810818044A CN 108877486 A CN108877486 A CN 108877486A
- Authority
- CN
- China
- Prior art keywords
- film
- silver
- laser
- layer
- mold label
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of in-mold label film and preparation method thereof, in-mold label film includes polymer base material film, thermoplastic film in silver print film and ethylene-vinyl acetate copolymer mould, silver print film includes the first adhesive layer, silver-plated laser film, second adhesive layer and transparent protective layer, the silver-plated laser film includes polymer-based bottom and laser silver layer, silver-plated laser film makes the in-mold label film have excellent glossy degree, in addition, the transparent protective layer is while guaranteeing that the information on in-mold label film is complete and clearly displays to consumer, also play a part of the extraneous damage of protection to the in-mold label film, furthermore, the present invention also provides a kind of preparation methods of in-mold label film.
Description
Technical field
The present invention relates to a kind of label materials, more particularly to a kind of in-mold label film and preparation method thereof.
Background technique
In order to make plastic bottle achieve the purpose that indicate content or decoration, in traditional handicraft, producer all holds in plastic cement
Pattern or text is added in device surface.The method generallyd use is after plastic bottle molding, then on plastic bottle surface to transfer
Or screen painting mode carries out secondary operation.And picture on surface made of printing in this way or text are short of aesthetic feeling, can not cause to disappear
Expense person's note that even easily falls off, and loses decoration functions, while the higher cost of secondary operation.
Currently, most be widely used in using paper labels and plastic label due to both label simple production process
On various containers, for example, oil bottle, articles for washing bottle, bottle for cosmetics etc., however this label for being pasted on container exterior, if
It is chronically in wet environment, for example, being pasted on the label on the containers such as Shampoo bottle, shower cream bottle, facial cleanser bottle, it is easy to
Mouldy, content show it is unclear, even fall off, thus lose mark content or decoration effect.
In addition, existing plastic bottle also begins to use in-mold label film, in-mold label film refers to pre-printed paper
Opening and closing are coated with special hot melt adhesive at object or thin sumptuous label, the back side, are placed on mould before plastic blown, injection molding or thermoforming
Inside type, to generate plastic bottle or basin.Label forms a whole with container, label and bottle body substantially in the same plane,
The edge of invisible label, just looking like is printed directly on picture and text on bottle body surface equally, to make to be pasted on plastic bottle
Label be not easily stripped.However, the glossiness that current this label film still has printing layer is not high enough, and lack to printing layer
Protection and the problem of be easily worn.
Summary of the invention
The purpose of the present invention is overcoming shortcoming in the prior art, provide that a kind of glossiness is good and anti abrasive mould
Interior label film and preparation method thereof.
The purpose of the present invention is achieved through the following technical solutions:
A kind of in-mold label film, including:
Polymer base material film, the polymer base material film have the inner surface and the outer surface;
Silver print film, the silver print film include the first adhesive layer, silver-plated laser film, the second adhesive layer and transparent guarantor
Sheath, first adhesive layer are adhered on the outer surface of the polymer base material film, and the silver-plated laser film includes macromolecule
Basal layer and laser silver layer, the polymer-based bottom are adhered to first adhesive layer far from the polymer base material film
One side on, laser silver layer plating is set to one side of the polymer-based bottom far from first adhesive layer
On, second adhesive layer is adhered on one side of the laser silver layer far from the polymer-based bottom, described
Bright protective layer is adhered to second adhesive layer far from the laser silver layer one side;
Thermoplastic film in ethylene-vinyl acetate copolymer mould, thermoplastic film is bonded in the ethylene-vinyl acetate copolymer mould
In on the inner surface of the polymer base material film, thermoplastic film is far from the macromolecule in the ethylene-vinyl acetate copolymer mould
Netted exhaust grid is offered on the one side of base material film.
In one embodiment, the polymer base material film with a thickness of 9 microns~16 microns.
In one embodiment, it is arranged on one side of the laser silver layer far from the polymer-based bottom and swashs
The radium-shine mark part of light.
In one embodiment, the thickness of first adhesive layer is identical as the thickness of second adhesive layer.
In one embodiment, the silver print film with a thickness of 23 microns~34 microns.
In one embodiment, it is provided on one side of the transparent protective layer far from second adhesive layer multiple
Transparent lug.
In one embodiment, the distance between transparent lug described in each adjacent two is equal.
In one embodiment, the transparent lug has drops structure.
In one embodiment, the transparent lug has crescent shape structure.
A kind of preparation method of in-mold label film, includes the following steps:
Polymer base material film is provided;
First bonding agents are subjected to melting operation in advance, then while hot on the outer surface coated in polymer base material film, then,
The polymer-based end lamination of silver-plated laser film is overlayed in first bonding agents, after first bonding agents solidification, obtains first
Adhesive layer;
Laser operation is carried out on the plating silver layer of the silver-plated laser film using laser technique, obtains laser
Radium-shine silver layer;
Second bonding agents are subjected to melting operation in advance, then are coated on the laser silver layer while hot, then while hot will
The transparent protective layer of the silver-plated laser film covers in second bonding agents, after second bonding agents solidification, obtains
Second adhesive layer;
Ethylene-vinyl acetate copolymer is coated on the inner surface of polymer base material film, and in the ethyl vinyl acetate second
Netted exhaust grid is formed on one side of the thermoplastic film far from the polymer base material film in alkene copolymer mould, obtains in-mold labels
Film.
Above-mentioned in-mold label film and preparation method thereof on two surfaces of polymer base material film by being arranged silver print film
With thermoplastic film in ethylene-vinyl acetate copolymer mould, the silver print film for being especially directly facing spectators further includes the first bonding
Layer, silver-plated laser film, the second adhesive layer and transparent protective layer, wherein the silver-plated laser film enables to the in-mold labels
Film has more excellent glossy degree, and corrodes more resistant to ink and obstruct steam, to enhance the mark of the in-mold label film
Performance and decorative performance are known, in addition, the transparent protective layer is guaranteeing that the information on in-mold label film is complete and clearly displays
While to consumer, also play a part of the extraneous damage of protection to the in-mold label film, in this way, above-mentioned in-mold label film phase
For existing common label, there are more excellent glossiness and stronger abrasion resistance properties.
Detailed description of the invention
In order to illustrate the technical solution of the embodiments of the present invention more clearly, below will be to needed in the embodiment attached
Figure is briefly described, it should be understood that the following drawings illustrates only certain embodiments of the present invention, therefore is not construed as pair
The restriction of range for those of ordinary skill in the art without creative efforts, can also be according to this
A little attached drawings obtain other relevant attached drawings.
Fig. 1 is the structural schematic diagram of the in-mold label film of one embodiment of the invention;
Fig. 2 is the structural schematic diagram of the in-mold label film of further embodiment of this invention;
Fig. 3 is the step flow chart of the preparation method of the in-mold label film of one embodiment of the invention;
Fig. 4 is the step flow chart of the preparation method of the in-mold label film of further embodiment of this invention.
Specific embodiment
To facilitate the understanding of the present invention, a more comprehensive description of the invention is given in the following sections with reference to the relevant attached drawings.In attached drawing
Give better embodiment of the invention.But the invention can be realized in many different forms, however it is not limited to herein
Described embodiment.On the contrary, the purpose of providing these embodiments is that making to understand more the disclosure
Add thorough and comprehensive.
It should be noted that it can directly on the other element when element is referred to as " being fixed on " another element
Or there may also be elements placed in the middle.When an element is considered as " connection " another element, it, which can be, is directly connected to
To another element or it may be simultaneously present centering elements.Term as used herein " vertical ", " horizontal ", " left side ",
" right side " and similar statement for illustrative purposes only, are not meant to be the only embodiment.
Unless otherwise defined, all technical and scientific terms used herein and belong to technical field of the invention
The normally understood meaning of technical staff is identical.Term as used herein in the specification of the present invention is intended merely to description tool
The purpose of the embodiment of body, it is not intended that in the limitation present invention.Term " and or " used herein includes one or more
Any and all combinations of relevant listed item.
Referring to Fig. 1, the in-mold label film 10a of an embodiment, including:Polymer base material film 110, silver print film 120
With thermoplastic film 130 in ethylene-vinyl acetate copolymer mould.
It is appreciated that by will be in polymer base material film 110, silver print film 120 and ethylene-vinyl acetate copolymer mould
Thermoplastic film 130 stacks gradually to form label construction, is placed on inside model before plastic blown, injection molding or thermoforming to generate plastics
Container, so that label forms a whole with plastic containers, and the surface of label and plastic containers is substantially in the same plane, sees
It just look like label to be directly melted in on plastic containers surface the same, great aesthetic feeling, and be not easy to send out less than the raised brim of label
It is mould or fall off, play the role of good mark content and decoration.
The polymer base material film 110 has the inner surface and the outer surface.It is appreciated that the polymer base material film 110 is made
For the support construction of in-mold label film 10a, there is the inner surface and the outer surface, silver print film 120 and ethylene-can be respectively set
Thermoplastic film 130 in acetate ethylene copolymer mould, so that in-mold label film 10a after molding has more excellent performance.In addition,
The polymer base material film 110 also needs to have good mechanical performance as the support construction of in-mold label film 10a, to meet
During plastic blown, injection molding or thermoforming are to combine in-mold label film and plastic containers together, there is certain branch
Support effect avoids the problems such as curling or fold occur in forming process, while can also carry out with other layers of material secured
Bonding, lamination is prevented, and can have good syncretizing effect with plastic containers, for example, described polymer-based
Material film 110 is polyolefins film or polyester film, and for another example, the polymer base material film 110 is high-density polyethylene resin
Base material film, high density polyvinyl-chloride resin base material film, high density poly propylene resin base material film, butyl nitrile EP rubbers base material film,
Organic siliconresin substrate film or amino resins substrate film, the high-density polyethylene resin substrate, the high density polyvinyl-chloride
Resin base material, the high density poly propylene resin base material, the butyl nitrile EP rubbers substrate, the organic siliconresin substrate or
The amino resins substrate can keep preferable intensity, so, it is possible so that mould in the higher and lower situation of temperature
Interior label film has good mechanical performance.
In one of the embodiments, the polymer base material film 110 with a thickness of 9 microns~16 microns.It is appreciated that
The polymer base material film 110 can play preferably support work with a thickness of 9 microns~16 microns to in-mold label film 10a
With, while there is better mechanical performance.Certainly, in other embodiments, the thickness of the macromolecule resin substrate film 110
It can be other values, the thickness of macromolecule resin substrate film 110 can be adjusted according to actual needs.
Referring to Fig. 1, the silver print film 120 includes the first adhesive layer 121, silver-plated laser film 122, the second adhesive layer
123 and transparent protective layer 124, first adhesive layer 121 is adhered on the outer surface of the polymer base material film 110, described
Silver-plated laser film 122 includes polymer-based bottom and laser silver layer, and it is viscous that the polymer-based bottom is adhered to described first
It connects on one side of the layer 121 far from the polymer base material film 110, the laser silver layer plating is set to the polymer-based end
For layer far from the one side of first adhesive layer 121, it is separate that second adhesive layer 123 is adhered to the laser silver layer
On the one side of the polymer-based bottom, the transparent protective layer 124 is adhered to second adhesive layer 123 and swashs far from described
On the radium-shine silver layer one side of light.
It is appreciated that the silver print film 120 is mainly used for showing the content or identification information of plastic containers, also
Decoration function is played, the attention of consumer can be attracted.In order to avoid in-mold label film because glossiness is inadequate, or because making
The problem of with being easily worn in the process and it is caused not have good mark and decoration function, the in-mold label film of the present embodiment
The silver print film 120 of 10a includes the first adhesive layer 121, silver-plated laser film 122, the second adhesive layer 123 and transparent protective layer
124, first adhesive layer 121 is adhered on the outer surface of the polymer base material film 110, is played the silver print film
120 carry out be bonded effect with the polymer base material film 110, while making the overall structure of the in-mold label film 10a more
Stick on conjunction and stabilization, is provided with silver-plated laser film 122 on first adhesive layer 121, it will be understood that laser film is generally using meter
It is calculation machine dot matrix photoetching technique, 3D true color holography technology, multiple with dynamic imaging techniques etc., through molding have rainbow dynamic,
The hologram image of three-dimensional stereo effect is transferred to polypropylene film (BOPP), polyester film (PET), polyvinyl chloride film (PVC)
Or on band coating substrate, commodity packaging surface is then made to obtain certain laser effect in the way of compound, thermoprint, transfer etc.
The features such as fruit has anti-counterfeiting performance strong, beautiful, green, environmental protection, bright color, resistance to ink erosion and barrier steam, and surface has
There is rainbow dynamic effect.In this way, the silver-plated laser film 122 that the in-mold label film in the present embodiment is arranged, enables to institute
In-mold label film is stated with more excellent glossy degree, and corrodes more resistant to ink and obstructs steam, to enhance in the mould
The mark performance and decorative performance of label film.Further, the silver-plated laser film 122 includes polymer-based bottom and laser radium
Silver layer is penetrated, the polymer-based bottom is adhered to one side of first adhesive layer 121 far from the polymer base material film 110
On, laser silver layer plating is set on one side of the polymer-based bottom far from first adhesive layer 121, can be with
Understand, the polymer-based bottom it is necessary to have preferable stability and stretches strong as the substrate of the silver-plated laser film 122
Degree, for example, the polymer-based bottom is polyester film, it will be understood that polyester film has glossiness good, and mechanical performance is excellent
Good, rigidity, hardness and toughness are high, puncture-resistant, rub resistance, high temperature resistant and low temperature, chemical resistance, oil resistivity, air-tightness and
The good feature of fragrance protectiveness so, it is possible so that the reflecting feel and crocking resistance of the silver-plated laser film 122 are more preferable;It can be with
Understand, the laser silver layer has good corrosion resistance and glossy degree, so, it is possible to further increase described silver-plated
The glossy degree and wearability of laser film 122, so that the identification and decorative performance of the in-mold label film are stronger;Into
One step, the second adhesive layer 123 and transparent protective layer 124, second adhesive layer are also provided in the silver-plated laser film 122
It is adhered on one side of the laser silver layer far from the polymer-based bottom, the transparent protective layer 124 is adhered to
Second adhesive layer 123 is far from the laser silver layer one side;In this way, second adhesive layer 123 can be by institute
It states transparent protective layer 124 and the silver-plated laser film 122 is bonded, further improve the whole of the in-mold label film 10a
Body structural stability.It should be noted that existing in-mold label film and causes using much due to lacking protective effect
It has been worn in journey, so that the mark and decoration function that label should have are lost, in this way, the in-mold label film of the present embodiment
10a is provided with transparent protective layer 124 to realize and play a part of the extraneous damage of protection, while energy to the in-mold label film 10a
Enough so that the information on label more completely and is clearly displayed to consumer, for example, the transparent protective layer 124 is transparent poly-
Ester film, transparent, oriented stretched polypropene film or transparent polyvinyl chloride film can so play in-mold label film well
Protective effect, it is more wear-resistant in use.
In one embodiment, it is arranged on one side of the laser silver layer far from the polymer-based bottom and swashs
The radium-shine mark part of light.It is appreciated that the laser silver layer has good corrosion resistance and glossy degree, so, it is possible
The glossy degree and wearability for further increasing the silver-plated laser film 122, so that the mark of the in-mold label film
Property and decorative performance are stronger, in the present embodiment, in order to further increase the mark performance of the silver-plated laser film 122, also in institute
Setting laser mark part on one side of the laser silver layer far from the polymer-based bottom is stated, so, it is possible to mark
Know information such as graph text information be set on laser mark part, so as to improve the in-mold label film identification and
It is decorative.
In one embodiment, the thickness phase of the thickness of first adhesive layer 121 and second adhesive layer 123
Together.It is appreciated that first adhesive layer 121 is carried out as by the polymer base material film 110 and the laser silver layer
The intermediate member of bonding, and second adhesive layer 123 is used as the laser silver layer and the transparent protective layer 124
The intermediate member being bonded, the thickness of first adhesive layer 121 situation identical as the thickness of second adhesive layer 123
Under, it enables to each layer structural bond power inside the in-mold label film more uniform, so, it is possible so that the mould internal standard
Overall structure and the performance for signing film 10a are more stable.
In one embodiment, the silver print film 120 with a thickness of 23 microns~34 microns.It is appreciated that institute
Intermediate member of the silver print film 120 as in-mold label film 10a is stated, the content or mark letter of display plastic containers are played
The effect of breath and decoration then will increase production cost if the thickness of the silver print film 120 is too thick, in this way, the plating
Silver-colored print film 120 with a thickness of 23 microns~34 microns, while can reach with excellent glossiness and identification, again
Cost can be controlled, certainly, in other embodiments, the thickness of the silver print film 120 is also possible to other values, silver-plated print
The thickness of brush film 120 can be adjusted according to actual needs.
In one embodiment, it is arranged on one side of the transparent protective layer 121 far from second adhesive layer 123
There are multiple transparent lugs.It is appreciated that the transparent protective layer 124 mainly plays the information printed on in-mold label film 10a
The effect of protection, influences to watch to avoid being worn in use, meanwhile, transparent protective layer 121 is used as consumer most
The outer membrane being immediately seen is provided with multiple transparent lugs and in-mold label film 10a is enabled to have more visual effect, and dicoration is more
By force, it meanwhile, it is capable to make the frictional force on the surface in-mold label film 10a stronger, can be contacted in use with consumer
It is more bonded, avoids sliding, in addition, when in-mold label film 10a is sent into the die cavity of plastic packaging containers by manipulator,
The transparent lug can generate stronger frictional resistance with manipulator, avoid falling off during at production, in this way, described
Bright protective layer 124 is provided with multiple transparent lugs on the one side far from second adhesive layer 123 can enhance in-mold labels
The dicoration and raising production efficiency of film 10a.
In one embodiment, the distance between transparent lug described in each adjacent two is equal.It is appreciated that per adjacent
The distance between two transparent lugs are equal, so that the transparent lug is evenly distributed on the transparent protective layer 124
And it is neat, it so, it is possible so that the whole visual effect of the transparent protective layer 124 is more preferable, while can enhance in the mould
The glossy degree of label film 10a.
In one embodiment, the transparent lug has drops structure.It is appreciated that the shape of the transparent lug
Shape structure is different, can play different decorative effect and using effect, and in the present embodiment, the transparent lug has water droplet
Shape structure, so, it is possible so that the in-mold label film 10a have more excellent decorative effect and using when be less susceptible to slide
It falls.
In one embodiment, the transparent lug has crescent shape structure.It is appreciated that the shape of the transparent lug
Shape structure is different, can play different decorative effect and using effect, and in the present embodiment, the transparent lug has crescent moon
Shape structure, so, it is possible so that the in-mold label film 10a have more excellent decorative effect and using when be less susceptible to slide
It falls.
Referring to Fig. 1, the bonding of thermoplastic film 130 is the polymer base material in the ethylene-vinyl acetate copolymer mould
On the inner surface of film 110, thermoplastic film 130 is far from the polymer base material film 110 in the ethylene-vinyl acetate copolymer mould
Netted exhaust grid is offered on one side.It is appreciated that 130 conduct of thermoplastic film in the ethylene-vinyl acetate copolymer mould
In-mold label film 10a carries out the component that crosslinking is merged with plastic containers, and thermoplastic film is set in the ethylene-vinyl acetate copolymer mould
It is placed on the inner surface of the polymer base material film 110, it can be in plastic blown, injection molding or thermoforming by the in-mold labels
Film and plastic containers are cross-linked to form an entirety;Further, in order to avoid in-mold label film 10a is merged with plastic containers
When generate bubble, to generate defective products, thermoplastic film 130 is far from the high score in the ethylene-vinyl acetate copolymer mould
Netted exhaust grid is offered on the one side of sub- base material film 110, so, it is possible will be between in-mold label film 10a and plastic containers
Bubble be quickly discharged, became one in this way, being conducive to in-mold label film 10a with plastic containers, become a part of container,
And then play the role of more preferably identifying and decorating.
In one embodiment, in the ethylene-vinyl acetate copolymer mould thermoplastic film 130 with a thickness of 35 microns~
50 microns.If being appreciated that the thickness of thermoplastic film 130 in the ethylene-vinyl acetate copolymer mould is too small, then it is unfavorable for institute
It states in-mold label film 10a and plastic containers crosslinking melt forms an entirety, or curling and fold occurs, in this way, this implementation
In example, in the ethylene-vinyl acetate copolymer mould thermoplastic film 130 with a thickness of 35 microns~50 microns, enable to described
Thermoplastic film 130 is even closer in conjunction with the other structures of the in-mold label film 10a in ethylene-vinyl acetate copolymer mould,
So that the overall structure of the in-mold label film 10a is more stable, especially one can be preferably formed with plastic containers
A entirety.
Above-mentioned in-mold label film on two surfaces of polymer base material film by being arranged silver print film and ethyl vinyl acetate second
Thermoplastic film in alkene copolymer mould, be especially directly facing spectators silver print film further include the first adhesive layer, silver-plated laser film,
Second adhesive layer and transparent protective layer, wherein it is more excellent that the silver-plated laser film enables to the in-mold label film to have
Glossy degree, and more resistant to ink corrode and obstruct steam, to enhance the mark performance and dicoration of the in-mold label film
Can, in addition, the transparent protective layer is while guaranteeing that the information on in-mold label film is complete and clearly displays to consumer,
Also play a part of the extraneous damage of protection to the in-mold label film, in this way, above-mentioned in-mold label film is relative to existing common
Label has more excellent glossiness and stronger abrasion resistance properties.
Referring to Fig. 2, the in-mold label film 10c of another embodiment, which is characterized in that including:Polymer base material film 310,
Thermoplastic film 330 in silver print film 320 and ethylene-vinyl acetate copolymer mould.
It is appreciated that by will be in polymer base material film 310, silver print film 320 and ethylene-vinyl acetate copolymer mould
Thermoplastic film 330 stacks gradually to form label construction, is placed on inside model before plastic blown, injection molding or thermoforming to generate plastics
Container, so that label forms a whole with plastic containers, and the surface of label and plastic containers is substantially in the same plane, sees
It just look like label to be directly melted in on plastic containers surface the same, great aesthetic feeling, and be not easy to send out less than the raised brim of label
It is mould or fall off, play the role of good mark content and decoration.
The polymer base material film 310 has the inner surface and the outer surface.It is appreciated that the polymer base material film 310 is made
For the support construction of in-mold label film, there is the inner surface and the outer surface, silver print film 320 and ethylene-vinegar can be respectively set
Thermoplastic film 330 in sour ethylene copolymer mould, so that in-mold label film 10c after molding has more excellent performance.In addition, institute
It states polymer base material film 310 as the support construction of in-mold label film 10c also to need that there is good mechanical performance, to meet
During plastic blown, injection molding or thermoforming are to combine in-mold label film and plastic containers together, there is certain support
Effect avoids the problems such as fold occurs in forming process, while can also merge effect with good with plastic containers material
Fruit, for example, the polymer base material film 310 is polyolefins film or polyester film, for another example, the polymer base material film
310 for high-density polyethylene resin base material film, high density polyvinyl-chloride resin base material film, high density poly propylene resin base material film,
Butyl nitrile EP rubbers base material film, organic siliconresin substrate film or amino resins substrate film, the high-density polyethylene resin base
Material, the high density polyvinyl-chloride resin base material, the high density poly propylene resin base material, the butyl nitrile EP rubbers base
Material, the organic siliconresin substrate or the amino resins substrate in the higher and lower situation of temperature, can keep compared with
Good intensity so, it is possible so that in-mold label film 10c has good mechanical performance.
Referring to Fig. 2, the silver print film 320 includes the first adhesive layer 321, silver-plated laser film 322, the second adhesive layer
323 and transparent protective layer 324, first adhesive layer 321 is adhered on the outer surface of the polymer base material film 310, described
Silver-plated laser film 322 includes polymer-based bottom and laser silver layer, and it is viscous that the polymer-based bottom is adhered to described first
It connects on one side of the layer 321 far from the polymer base material film 310, the laser silver layer plating is set to the polymer-based end
For layer far from the one side of first adhesive layer 321, it is separate that second adhesive layer 323 is adhered to the laser silver layer
On the one side of the polymer-based bottom, the transparent protective layer 324 is adhered to second adhesive layer far from the laser
On radium-shine silver layer one side.
It is appreciated that the silver print film 320 is mainly used for showing the content or identification information of plastic containers, also
Decoration function is played, the attention of consumer can be attracted.In order to avoid in-mold label film 10c because glossiness is inadequate, Huo Zheyin
The problem of being easily worn in use and it is caused not have good mark and decoration function, the mould internal standard of the present embodiment
The silver print film 320 for signing film 10c includes the first adhesive layer 321, silver-plated laser film 322, the second adhesive layer 323 and transparency protected
Layer 324, first adhesive layer 321 is adhered on the outer surface of the polymer base material film 310, is played the silver print
Film 320 carries out be bonded effect with the polymer base material film 310, while making the overall structure of the in-mold label film 10c
It is more bonded and stablizes, silver-plated laser film 322 is provided on first adhesive layer 321, it will be understood that laser film generally uses
Computer dot matrix photoetching technique, 3D true color holography technology, multiple and dynamic imaging techniques etc. are moved through molding handle with rainbow
State, three-dimensional stereo effect hologram image be transferred to polypropylene film (BOPP), polyester film (PET), polyvinyl chloride film
(PVC) or on band coating substrate, then commodity packaging surface is made to obtain certain laser in the way of compound, thermoprint, transfer etc.
The features such as laser effect has anti-counterfeiting performance strong, beautiful, green, environmental protection, bright color, resistance to ink erosion and barrier steam, and
Surface has rainbow dynamic effect.In this way, the silver-plated laser film 322 that the in-mold label film 10c in the present embodiment is arranged, energy
It enough so that the in-mold label film 10c has more excellent glossy degree, and corrodes more resistant to ink and obstructs steam, to enhance
The mark performance and decorative performance of the in-mold label film 10c.Further, the silver-plated laser film 322 includes macromolecule
Basal layer and laser silver layer, the polymer-based bottom are adhered to first adhesive layer 321 far from described polymer-based
On the one side of material film 310, the laser silver layer plating is set to the polymer-based bottom far from first adhesive layer 321
One side on, it will be understood that it is necessary to have preferable steady as the substrate of the silver-plated laser film for the polymer-based bottom
Qualitative and tensile strength, for example, the polymer-based bottom is polyester film, it will be understood that polyester film has glossiness good,
Good mechanical performance, rigidity, hardness and toughness are high, puncture-resistant, rub resistance, high temperature resistant and low temperature, chemical resistance, oil resistant
Property, air-tightness and the good feature of fragrance protectiveness, so, it is possible reflecting feel and rub resistance so that the silver-plated laser film 322
It can be more preferable;It is appreciated that the laser silver layer has good corrosion resistance and glossy degree, so, it is possible further
Improve the glossy degree and wearability of the silver-plated laser film 322 so that the identification of the in-mold label film 10c and
Decorative performance is stronger;Further, the second adhesive layer 323 and transparent protective layer are also provided on the silver-plated laser film 322
324, second adhesive layer 323 is adhered on one side of the laser silver layer far from the polymer-based bottom, institute
It states transparent protective layer 324 and is adhered to second adhesive layer 323 far from the laser silver layer one side;In this way, described
The transparent protective layer 324 and the silver-plated laser film 322 can be bonded by the second adhesive layer 323, be further improved
The overall structure stability of the in-mold label film 10c.It should be noted that existing in-mold label film 10c is much due to lacking
Weary protective effect, and cause to be worn in use, to lose the mark and decoration function that label should have, such as
This, the in-mold label film 10c of the present embodiment plays the in-mold label film 10c with realization provided with transparent protective layer 324 anti-
The effect of the extraneous damage of shield, while enabling to the information on label more complete and clearly displaying to consumer, for example, institute
Stating transparent protective layer 324 is transparent polyester film, transparent, oriented stretched polypropene film or transparent polyvinyl chloride film, such energy
It is enough to play a good protective effect to in-mold label film, it is more wear-resistant in use.
Referring to Fig. 2, thermoplastic film 330 includes transition adhesive layer 331, highly dense in the ethylene-vinyl acetate copolymer mould
Spend in ethylene-vinyl acetate copolymer mould thermoplastic layer 333, institute in thermoplastic layer 332 and low density ethylene-acetate ethylene copolymer mould
It states transition adhesive layer 331 to be adhered on the inner surface of the polymer base material film 310, the high density ethylene-vinyl acetate is total
Thermoplastic layer 332 is adhered on one side of the transition adhesive layer 331 far from the polymer base material film 310 in polymers mould, institute
It states thermoplastic layer 333 in low density ethylene-acetate ethylene copolymer mould and is adhered to the high density ethylene-acetate ethylene copolymer mould
On one side of the interior thermoplastic layer 332 far from the transition adhesive layer 331, in the low density ethylene-acetate ethylene copolymer mould
Thermoplastic layer 333 offers netted row on the one side far from thermoplastic layer 332 in the high density ethylene-acetate ethylene copolymer mould
Gas grid, wherein the netted exhaust grid includes that a plurality of be spaced apart is set to the low density ethylene-vinyl acetate copolymerization
Transverse roller pressure in object mould on one side of the thermoplastic film far from thermoplastic layer in the high density ethylene-acetate ethylene copolymer mould
Air drain and it is a plurality of be spaced apart be set to the low density ethylene-acetate ethylene copolymer mould in thermoplastic film far from described highly dense
Spend longitudinal roll-in air discharge duct in ethylene-vinyl acetate copolymer mould on the one side of thermoplastic layer, each transverse roller pressure
Air drain is perpendicular with each longitudinal roll-in air discharge duct respectively.
It is appreciated that thermoplastic film 330 is used as in-mold label film 10c and plastics in the ethylene-vinyl acetate copolymer mould
Container carries out the component of crosslinking fusion, can be in plastic blown, injection molding or thermoforming by the in-mold label film 10c and plastics
Container is cross-linked to form an entirety;Further, in order to enable in-mold label film 10c preferably merges formation one with plastic containers
A entirety, thermoplastic film 330 includes transition adhesive layer 331, high density ethylene-acetic acid in the ethylene-vinyl acetate copolymer mould
Thermoplastic layer 333 in thermoplastic layer 332 and low density ethylene-acetate ethylene copolymer mould in ethylene copolymer mould.It is appreciated that described
Transition adhesive layer 331 can be by thermoplastic film 330 in the ethylene-vinyl acetate copolymer mould in the polymer base material film 310
Be bonded so that the internal structure of the in-mold label film 10c be more bonded it is compact;And the high density ethylene-acetic acid second
Thermoplastic layer 332 enables to the in-mold label film 10c to be preferably crosslinked with plastic containers in alkene copolymer mould, Ke Yili
Solution, the copolymer of ethylene-vinyl acetate copolymer ethylene and vinylacetate, with easy processing, compatibility is good, amount of deflection is high, soft
High, anti-aging, weatherability the is good advantage of toughness, and it is inviscid at normal temperature, it can be made by the hot pressing of certain condition
Melting and crosslinking curing are generated, becomes fully transparent, the highdensity ethylene-vinyl acetate copolymer is relative to described low close
The degree of cross linking for spending ethylene-vinyl acetate copolymer is higher, for example, the acetic acid of the highdensity ethylene-vinyl acetate copolymer
Ethylene contents are 5wt%-20wt%, be so, it is possible so that thermoplastic layer in the high density ethylene-acetate ethylene copolymer mould
332 with plastic containers when being crosslinked, and certain crosslinked action is played, so that in-mold label film and plastic containers are cross-linked to form one
A entirety, further, in the low density ethylene-acetate ethylene copolymer mould thermoplastic layer 333 as in-mold label film 10c with
Plastic containers, which carry out immediate component, crosslinking degree lower low density ethylene-acetate ethylene copolymer when crosslinking fusion, to be had
It is preferably crosslinked conducive to thermoplastic layer 333 in the low density ethylene-acetate ethylene copolymer mould with plastic containers, for example,
The vinyl acetate content of the low density ethylene-acetate ethylene copolymer is 15wt%-45wt%, in this way, the high density second
In alkene-acetate ethylene copolymer mould in thermoplastic layer 332 and the low density ethylene-acetate ethylene copolymer mould thermoplastic layer 333 into
Row combines, and the effect for enabling to in-mold label film 10c to merge with the crosslinking of plastic containers is more preferable.Further, described low close
Thermoplastic layer 333 is far from thermoplastic layer in the high density ethylene-acetate ethylene copolymer mould in degree ethylene-vinyl acetate copolymer mould
Netted exhaust grid is offered on 332 one side, wherein the netted exhaust grid includes that a plurality of be spaced apart is set to the institute
Thermoplastic layer 333 is stated in low density ethylene-acetate ethylene copolymer mould far from the high density ethylene-acetate ethylene copolymer mould
Transverse roller pressure air drain and a plurality of be spaced apart on the one side of thermoplastic layer 332 are set to the low density ethylene-acetic acid
One side of the thermoplastic layer 333 far from thermoplastic layer 332 in the high density ethylene-acetate ethylene copolymer mould in ethylene copolymer mould
On longitudinal roll-in air discharge duct, each transverse roller pressure air drain is perpendicular with each longitudinal roll-in air discharge duct respectively.It can
To understand, in order to avoid generating bubble during being merged in-mold label film 10c with plastic containers, described low close
Netted exhaust grid is offered on the one side of thermoplastic layer 333 in degree ethylene-vinyl acetate copolymer mould, so that mould internal standard
Label film 10c is more perfectly bonded with plastic containers progress, and further, the netted exhaust grid includes that a plurality of interval is set
The transverse roller pressure air drain and a plurality of spaced longitudinal roll-in air discharge duct set, and each transverse roller pressure air drain point
It is not perpendicular with each longitudinal roll-in air discharge duct, it so, it is possible the gas so that between the in-mold label film 10c and plastic containers
The more preferable more thoroughly discharge of bubble.
Above-mentioned in-mold label film is by will be in polymer base material film, silver print film and ethylene-vinyl acetate copolymer mould
Thermoplastic film stacks gradually to form label construction, wherein silver print film further includes the first adhesive layer, silver-plated laser film, second viscous
Connect layer and transparent protective layer, enable to the in-mold label film have more excellent glossy degree, and more resistant to ink corrode and
Steam is obstructed, so that the mark performance and decorative performance of the in-mold label film are enhanced, in addition, the transparent protective layer makes
The in-mold label film has good abrasion resistance properties;In addition, thermoplastic film further included in ethylene-vinyl acetate copolymer mould
Cross thermoplastic layer and low density ethylene-acetate ethylene copolymer Mo Neire in adhesive layer, high density ethylene-acetate ethylene copolymer mould
Layer is moulded, and is also provided with netted exhaust grid in the low density ethylene-acetate ethylene copolymer mould on the one side of thermoplastic film,
The exhaust performance between in-mold label film and plastic containers is substantially increased, the generation of bubble is avoided.
Referring to Fig. 3, the preparation method of the in-mold label film of an embodiment, includes the following steps:
S110, polymer base material film is provided.
It, can be as the subsequent substrate for preparing in-mold label film, it will be understood that macromolecule by providing polymer base material film
Base material film as in-mold label film support construction it is necessary to have good physical mechanical property and chemical property, can satisfy
During plastic blown, injection molding or thermoforming are to combine in-mold label film and plastic containers together, there is certain branch
Support effect avoids the problems such as curling or fold occur in forming process, while can also carry out with other layers of material secured
Bonding, lamination is prevented, and can have good syncretizing effect with plastic containers, for example, described polymer-based
Material film be polyolefins film or polyester film, for another example, the polymer base material film be high-density polyethylene resin base material film,
High density polyvinyl-chloride resin base material film, high density poly propylene resin base material film, butyl nitrile EP rubbers base material film, organosilicon tree
Rouge base material film or amino resins substrate film, the high-density polyethylene resin substrate, the high density polyvinyl-chloride resin base material,
The high density poly propylene resin base material, the butyl nitrile EP rubbers substrate, the organic siliconresin substrate or the amino
Resin base material can keep preferable intensity, so, it is possible so that in-mold label film in the higher and lower situation of temperature
With good mechanical performance.
In order to make polymer base material film that there is better mechanical performance, for example, the polymer base material film is micro- with a thickness of 9
Rice~16 microns, so, it is possible to play in-mold label film better supporting role, while having better mechanical performance.When
So, in other embodiments, the thickness of the macromolecule resin substrate film is also possible to other values, macromolecule resin substrate film
Thickness can be adjusted according to actual needs.
S120, first bonding agents are subjected to melting operation in advance, then while hot on the outer surface coated in polymer base material film,
Then, the polymer-based end lamination of silver-plated laser film is overlayed in first bonding agents, after first bonding agents solidification, is obtained
First adhesive layer.
By the way that first bonding agents are carried out melting operation, then while hot on the outer surface coated in polymer base material film, then,
The polymer-based end lamination of silver-plated laser film is overlayed in first bonding agents, the first adhesive layer can be obtained after solidification to be cooled.
In order to melt first bonding agents preferably, for example, first bonding agents are added under the conditions of 150 DEG C~230 DEG C of temperature
In reaction kettle, 30min~45min is mixed to complete melting, is coated with onto the outer surface of polymer base material film;For another example,
In order to enable the polymer-based end lamination of silver-plated laser film can be preferably bonded after overlaying in first bonding agents, for example, using
Clad steel pressure roller overlays on the polymer-based end lamination of silver-plated laser film in first bonding agents;For another example, in order to enable it is polymer-based
The polymer-based bottom of material film and silver-plated laser film is bonded closer, lamination is avoided, for example, the first bonding agents packet
Include each component of following mass parts:It 10~28 parts of epoxy resin, 6~18 parts of polyurethane, 4~14 parts of methyl methacrylate and helps
3~10 parts of agent;For another example, the auxiliary agent is hydroxyethyl cellulose or dodecyl sodium sulfate, be so, it is possible so that the macromolecule
The polymer-based bottom of base material film and silver-plated laser film is bonded even closer.
S130, laser operation is carried out on the plating silver layer of the silver-plated laser film using laser technique, obtained
To laser silver layer.
Laser operation is carried out on the plating silver layer of the silver-plated laser film by using laser technique, it can
Obtain laser silver layer.It can be real it is appreciated that carrying out laser operation on the plating silver layer of the silver-plated laser film
Cash belongs to the combination with nonmetallic materials, the graph text information of great aesthetic feeling is formed, while having perfect visual effect, after being conducive to
It is continuous to be prepared that glossiness is more preferable and the better in-mold label film of decorative effect.Glossy degree and aesthetics are more excellent in order to obtain
Good laser silver layer, for example, the 3D true color holography technology will swash on the plating silver layer of the silver-plated laser film
The radium-shine operation of light, obtains laser silver layer, so, it is possible so that the reflecting feel and crocking resistance of the silver-plated laser film more
It is good;For another example, the plating silver layer is silver-plated polyester film, it will be understood that polyester film has glossiness good, and mechanical performance is excellent
Good, rigidity, hardness and toughness are high, puncture-resistant, rub resistance, high temperature resistant and low temperature, chemical resistance, oil resistivity, air-tightness and
The good feature of fragrance protectiveness so, it is possible so that the reflecting feel and crocking resistance of the silver-plated laser film are more preferable;For another example, will
The plating silver layer of the silver-plated laser film is put into laser machine, carries out radium-shine behaviour according to required radium-shine graph text information
Make, for example, the distance between plating silver layer of laser head and the silver-plated laser film is that 20cm~35cm for another example swashs
The radium-shine energy of the radium-shine processing of light is 200W~800W, and radium-shine temperature is 150-200 DEG C, and the radium-shine time is 10s~30s, in this way,
It can be prepared that glossiness is higher and the higher laser silver layer of aesthetic degree.
S140, second bonding agents are subjected to melting operation in advance, then be coated on the laser silver layer while hot, then take advantage of
Heat covers the transparent protective layer of the silver-plated laser film in second bonding agents, after second bonding agents solidification,
Obtain the second adhesive layer.
It is coated on the laser silver layer, then takes advantage of by the way that second bonding agents are carried out melting operation in advance, then while hot
Heat covers the transparent protective layer of the silver-plated laser film in second bonding agents, after second bonding agents solidification,
It can obtain the second adhesive layer.In order to enable second bonding agents carry out Flashmelt, for example, in 160 DEG C~240 DEG C of temperature strip
Under part, second bonding agents are added in reaction kettle, 25min~45min are mixed to complete melting, re-coating swashs to described
On the outer surface of the radium-shine silver layer of light;For another example, also viscous second in order to enable subsequent be prepared more resistant in-mold label film
It connects and covers transparent protective layer in agent, it should be noted that existing in-mold label film causes much due to lacking protective effect
It has been worn in use, so that the mark and decoration function that label should have are lost, in this way, in the mould of the present embodiment
Label film is provided with transparent protective layer to realize and play a part of the extraneous damage of protection to the in-mold label film, while can make
Information on label is more complete and clearly display to consumer, for example, the transparent protective layer be transparent polyester film,
Transparent, oriented stretched polypropene film or transparent polyvinyl chloride film can so play good protection to in-mold label film and make
With more wear-resistant in use.For another example, in order to enable what the transparent protective layer and the laser silver layer were bonded
It is closer, lamination is avoided, for example, the second bonding agents include each component of following mass parts:Butyl acrylate 4~13
Part, 6~14 parts of methyl methacrylate, 7~18 parts of methacrylic acid, 22~30 parts of tackifying resin and 4~18 parts of antistatic agent;
For another example, the antistatic agent is quaternary cationics, polyoxyethylene alkyl amine compound, polyol fatty acid
At least one of ester, alkanolamide;It so, it is possible that better second adhesive layer of adhesive property is prepared, so that institute
State transparent protective layer and the laser silver layer bonding it is closer so that the overall structure of in-mold label film is more sticked on
It closes, avoids lamination.
S150, ethylene-vinyl acetate copolymer is coated on the inner surface of polymer base material film, and in the ethylene-
Netted exhaust grid is formed on one side of the thermoplastic film far from the polymer base material film in acetate ethylene copolymer mould, obtains mould
Interior label film.
It, can after cooling and solidifying by the way that ethylene-vinyl acetate copolymer to be coated on the inner surface of polymer base material film
Obtain thermoplastic film in ethylene-vinyl acetate copolymer mould, it will be understood that thermoplastic film in the ethylene-vinyl acetate copolymer mould
The component that crosslinking is merged, thermoplastic film in the ethylene-vinyl acetate copolymer mould are carried out with plastic containers as in-mold label film
It is set on the inner surface of the polymer base material film, it can be in plastic blown, injection molding or thermoforming by the in-mold labels
Film and plastic containers are cross-linked to form an entirety;Further, when being merged in order to avoid in-mold label film with plastic containers
Bubble is generated, to generate defective products, thermoplastic film is far from the polymer base material in the ethylene-vinyl acetate copolymer mould
Netted exhaust grid is offered on the one side of film, so, it is possible the bubble between in-mold label film and plastic containers is quick
Discharge, becames one with plastic containers in this way, being conducive to in-mold label film, becomes a part of container, and then play more preferable mark
The effect known and decorated.
The preparation method of above-mentioned in-mold label film, by the outer surface that first bonding agents are coated in polymer base material film
On, then the polymer-based end lamination of silver-plated laser film is overlayed in first bonding agents and obtains the first adhesive layer, and uses laser
Radium art carries out laser operation on the plating silver layer of silver-plated laser film, obtains laser silver layer, then in laser radium
It penetrates and coats second bonding agents on silver layer, and the transparent protective layer of silver-plated laser film is covered and obtains second in second bonding agents
Ethylene-vinyl acetate copolymer is finally coated on the inner surface of polymer base material film and obtains ethene-vinyl acetate by adhesive layer
Thermoplastic film in copolymer mould, while netted exhaust grid is formed on one side, so, it is possible to obtain have it is excellent glossy
The in-mold label film of degree, in addition, the transparent protective layer guarantee that the information on in-mold label film is complete and clearly display to
While consumer, also play a part of the extraneous damage of protection to the in-mold label film.
Referring to Fig. 4, the preparation method of the in-mold label film of another embodiment, includes the following steps:
S310, polymer base material film is provided.
It, can be as the subsequent substrate for preparing in-mold label film, it will be understood that macromolecule by providing polymer base material film
Base material film as in-mold label film support construction it is necessary to have good physical mechanical property and chemical property, can satisfy
During plastic blown, injection molding or thermoforming are to combine in-mold label film and plastic containers together, there is certain branch
Support effect avoids the problems such as curling or fold occur in forming process, while can also carry out with other layers of material secured
Bonding, lamination is prevented, and can have good syncretizing effect with plastic containers, for example, described polymer-based
Material film be polyolefins film or polyester film, for another example, the polymer base material film be high-density polyethylene resin base material film,
High density polyvinyl-chloride resin base material film, high density poly propylene resin base material film, butyl nitrile EP rubbers base material film, organosilicon tree
Rouge base material film or amino resins substrate film, the high-density polyethylene resin substrate, the high density polyvinyl-chloride resin base material,
The high density poly propylene resin base material, the butyl nitrile EP rubbers substrate, the organic siliconresin substrate or the amino
Resin base material can keep preferable intensity, so, it is possible so that in-mold label film in the higher and lower situation of temperature
With good mechanical performance.
In order to make polymer base material film that there is better mechanical performance, for example, the polymer base material film is micro- with a thickness of 9
Rice~16 microns, so, it is possible to play in-mold label film better supporting role, while having better mechanical performance.When
So, in other embodiments, the thickness of the macromolecule resin substrate film is also possible to other values, macromolecule resin substrate film
Thickness can be adjusted according to actual needs.
S320, first bonding agents are subjected to melting operation in advance, then while hot on the outer surface coated in polymer base material film,
Then, the polymer-based end lamination of silver-plated laser film is overlayed in first bonding agents, after first bonding agents solidification, is obtained
First adhesive layer.
By the way that first bonding agents are carried out melting operation, then while hot on the outer surface coated in polymer base material film, then,
The polymer-based end lamination of silver-plated laser film is overlayed in first bonding agents, the first adhesive layer can be obtained after solidification to be cooled.
In order to melt first bonding agents preferably, for example, first bonding agents are added under the conditions of 150 DEG C~230 DEG C of temperature
In reaction kettle, 30min~45min is mixed to complete melting, is coated with onto the outer surface of polymer base material film;For another example,
In order to enable the polymer-based end lamination of silver-plated laser film can be preferably bonded after overlaying in first bonding agents, for example, using
Clad steel pressure roller overlays on the polymer-based end lamination of silver-plated laser film in first bonding agents;For another example, in order to enable it is polymer-based
The polymer-based bottom of material film and silver-plated laser film is bonded closer, lamination is avoided, for example, the first bonding agents packet
Include each component of following mass parts:It 10~28 parts of epoxy resin, 6~18 parts of polyurethane, 4~14 parts of methyl methacrylate and helps
3~10 parts of agent;For another example, the auxiliary agent is hydroxyethyl cellulose or dodecyl sodium sulfate, be so, it is possible so that the macromolecule
The polymer-based bottom of base material film and silver-plated laser film is bonded even closer.
S330, laser operation is carried out on the plating silver layer of the silver-plated laser film using laser technique, obtained
To laser silver layer.
Laser operation is carried out on the plating silver layer of the silver-plated laser film by using laser technique, it can
Obtain laser silver layer.It can be real it is appreciated that carrying out laser operation on the plating silver layer of the silver-plated laser film
Cash belongs to the combination with nonmetallic materials, the graph text information of great aesthetic feeling is formed, while having perfect visual effect, after being conducive to
It is continuous to be prepared that glossiness is more preferable and the better in-mold label film of decorative effect.Glossy degree and aesthetics are more excellent in order to obtain
Good laser silver layer, for example, the 3D true color holography technology will swash on the plating silver layer of the silver-plated laser film
The radium-shine operation of light, obtains laser silver layer, so, it is possible so that the reflecting feel and crocking resistance of the silver-plated laser film more
It is good;For another example, the plating silver layer is silver-plated polyester film, it will be understood that polyester film has glossiness good, and mechanical performance is excellent
Good, rigidity, hardness and toughness are high, puncture-resistant, rub resistance, high temperature resistant and low temperature, chemical resistance, oil resistivity, air-tightness and
The good feature of fragrance protectiveness so, it is possible so that the reflecting feel and crocking resistance of the silver-plated laser film are more preferable;For another example, will
The plating silver layer of the silver-plated laser film is put into laser machine, carries out radium-shine behaviour according to required radium-shine graph text information
Make, for example, the distance between plating silver layer of laser head and the silver-plated laser film is that 20cm~35cm for another example swashs
The radium-shine energy of the radium-shine processing of light is 200W~800W, and radium-shine temperature is 150 DEG C -200 DEG C, and the radium-shine time is 10s~30s, such as
This, can be prepared that glossiness is higher and the higher laser silver layer of aesthetic degree.
S340, second bonding agents are subjected to melting operation in advance, then be coated on the laser silver layer while hot, then take advantage of
Heat covers the transparent protective layer of the silver-plated laser film in second bonding agents, after second bonding agents solidification,
Obtain the second adhesive layer.
It is coated on the laser silver layer, then takes advantage of by the way that second bonding agents are carried out melting operation in advance, then while hot
Heat covers the transparent protective layer of the silver-plated laser film in second bonding agents, after second bonding agents solidification,
It can obtain the second adhesive layer.In order to enable second bonding agents carry out Flashmelt, for example, in 160 DEG C~240 DEG C of temperature strip
Under part, second bonding agents are added in reaction kettle, 25min~45min are mixed to complete melting, re-coating swashs to described
On the outer surface of the radium-shine silver layer of light;For another example, also viscous second in order to enable subsequent be prepared more resistant in-mold label film
It connects and covers transparent protective layer in agent, it should be noted that existing in-mold label film causes much due to lacking protective effect
It has been worn in use, so that the mark and decoration function that label should have are lost, in this way, in the mould of the present embodiment
Label film is provided with transparent protective layer to realize and play a part of the extraneous damage of protection to the in-mold label film, while can make
Information on label is more complete and clearly display to consumer, for example, the transparent protective layer be transparent polyester film,
Transparent, oriented stretched polypropene film or transparent polyvinyl chloride film can so play good protection to in-mold label film and make
With more wear-resistant in use.For another example, in order to enable what the transparent protective layer and the laser silver layer were bonded
It is closer, lamination is avoided, for example, the second bonding agents include each component of following mass parts:Butyl acrylate 4~13
Part, 6~14 parts of methyl methacrylate, 7~18 parts of methacrylic acid, 22~30 parts of tackifying resin and 4~18 parts of antistatic agent;
For another example, the antistatic agent is quaternary cationics, polyoxyethylene alkyl amine compound, polyol fatty acid
At least one of ester, alkanolamide;It so, it is possible that better second adhesive layer of adhesive property is prepared, so that institute
State transparent protective layer and the laser silver layer bonding it is closer so that the overall structure of in-mold label film is more sticked on
It closes, avoids lamination.
S350, polyurethane adhesive and high density ethylene-acetate ethylene copolymer be subjected to melting operation in advance respectively, is taken advantage of
The polyurethane adhesive is coated on the inner surface of the polymer base material film by heat, then while hot by the high density ethylene-
Acetate ethylene copolymer is coated on the polyurethane adhesive, after polyurethane adhesive solidification, obtains transition bonding
Layer obtains high density ethylene-acetate ethylene copolymer Mo Neire after the high density ethylene-acetate ethylene copolymer solidification
Mould layer.
Refer in strand it is appreciated that polyurethane adhesive is used as containing carbamate groups (- NHCOO-) or different
The adhesive of cyanic acid ester group (- NCO), polyurethane adhesive not only have excellent shear strength and impact property, are applicable in
In various structural bonding fields, and have excellent flexible nature, has excellent rubber property, adapt to different heat expansion
The bonding of coefficient substrate, it is formed between substrate has soft-hard transition zone, and not only bonding force is strong, while also having excellent
Buffering, shock-absorbing function.The low temperature and ultralow temperature performance of polyurethane gluing stick are more than the adhesive of every other type.In order to mention
The adhesive property of high transition adhesive layer, the polyurethane adhesive in the present embodiment are the agent of polyisocyanates gluing, contain isocyanates
At least one of adhesive for polyurethane, hydroxyl adhesive for polyurethane and polyurethane resin gluing agent of base, in this way, subsequent energy
It is enough thermoplastic layer in high density ethylene-acetate ethylene copolymer mould is carried out with the polymer base material film it is be bonded so that the mould
The internal structure of interior label film is more bonded compact
It is appreciated that ethylene-vinyl acetate copolymer is the copolymer of ethylene and vinylacetate, there is easy processing, phase
The advantage that capacitive is good, amount of deflection is high, flexibility is high, anti-aging, weatherability is good, and it is inviscid at normal temperature, by certain item
The hot pressing of part can make it generate melting and crosslinking curing, become fully transparent, and high density ethylene-acetate ethylene copolymer phase
It is higher for low density ethylene-acetate ethylene copolymer degree of cross linking, for example, the high density ethylene-acetate ethylene copolymer
Vinyl acetate content be 5wt%-20wt%, so, it is possible so that subsequent obtained high density ethylene-acetate ethylene copolymer
When thermoplastic layer and plastic containers are crosslinked in mould, crosslinked action is played, so that in-mold label film is cross-linked to form with plastic containers
One entirety.
By the way that the polyurethane adhesive and the high density ethylene-acetate ethylene copolymer are first carried out melting behaviour respectively
Make, enables to the polyurethane adhesive and the high density ethylene-acetate ethylene copolymer to be easier to carry out coating operation, be
Melt the polyurethane adhesive and the high density ethylene-acetate ethylene copolymer preferably, for example, 140 DEG C~
Under the conditions of 250 DEG C of temperature, the polyurethane adhesive is added in reaction kettle, 20min~40min is mixed to complete
Melting, for another example, under the conditions of 170 DEG C~280 DEG C of temperature, the high density ethylene-acetate ethylene copolymer is added to instead
It answers in kettle, 25min~50min is mixed to complete melting, then, the polyurethane adhesive after melting is coated while hot
On the inner surface of the polymer base material film, then, then the high density ethylene-acetate ethylene copolymer after melting taken advantage of
Heat is coated on the polyurethane adhesive, after polyurethane adhesive solidification, transition adhesive layer is obtained, to described highly dense
After spending ethylene-vinyl acetate copolymer solidification, thermoplastic layer in high density ethylene-acetate ethylene copolymer mould is obtained.
S360, low density ethylene-acetate ethylene copolymer is subjected to melting operation in advance, it is described while hot by low-density second
Alkene-acetate ethylene copolymer is coated in the high density ethylene-acetate ethylene copolymer mould on thermoplastic layer, and then, use is cold
Pressure anilox roll carries out cold press operation on the ethylene-vinyl acetate copolymer, obtains low density ethylene-acetate ethylene copolymer
Thermoplastic layer in mould, and in the low density ethylene-acetate ethylene copolymer mould thermoplastic layer far from the high density ethylene-acetic acid
Netted exhaust grid is formed in ethylene copolymer mould on the one side of thermoplastic layer, obtains in-mold label film.
It is appreciated that low density ethylene-acetate ethylene copolymer is compared to the friendship of high density ethylene-acetate ethylene copolymer
Connection degree is lower, in this way, it is subsequent in-mold label film and plastic containers are subjected to integral blow, injection molding or thermoforming when, it is described low
Density polyethylene-acetate ethylene copolymer can be preferably crosslinked with plastic containers material, be conducive to in-mold label film and plastics
It is higher that container forms the degree of cross linking, and integrally formed effect is more preferable.For example, low density ethylene-the acetate ethylene copolymer
Vinyl acetate content is 15wt%-45wt%, in this way, thermoplastic in the low density ethylene being subsequently formed-acetate ethylene copolymer mould
Layer be combined with each other with thermoplastic layer in the high density ethylene-acetate ethylene copolymer mould, enables to in-mold label film and plastics
The effect of the crosslinking fusion of container is more preferable.
By the way that low density ethylene-acetate ethylene copolymer is first carried out melting operation, the low close of molten condition can be obtained
Ethylene-vinyl acetate copolymer is spent, to be preferably coated in other surfaces, for example, in 120 DEG C~200 DEG C of temperature strip
Under part, the low density ethylene-acetate ethylene copolymer is added in reaction kettle, 15min~30min is mixed to complete
Melting, then be coated in the high density ethylene-acetate ethylene copolymer mould on thermoplastic layer while hot, then, using cold pressing reticulate pattern
Roller carries out cold press operation on the ethylene-vinyl acetate copolymer, obtains low density ethylene-acetate ethylene copolymer Mo Neire
Mould layer.Further, the cold press operation specifically comprises the following steps:S241, using cold pressing anilox roll, and cold pressing reticulate pattern
The surface of roller coats antitack agent;S242, magnetic powder is added into low density ethylene-acetate ethylene copolymer of molten condition, carries out
Stirring operation obtains mixing slurry;S243, mixing slurry is coated in while hot in the high density ethylene-acetate ethylene copolymer mould
On thermoplastic layer, low density ethylene-acetate ethylene copolymer coating is obtained;S244, low density ethylene-acetate ethylene copolymer is applied
Layer carries out network type cold blocking, and formation includes orthogonal a plurality of spaced transverse roller pressure air drain and a plurality of interval
The netted exhaust grid of longitudinal roll-in air discharge duct of setting, obtains thermoplastic layer in low density ethylene-acetate ethylene copolymer mould.Such as
This, can in the low density ethylene-acetate ethylene copolymer mould thermoplastic layer it is total far from the high density ethylene-vinyl acetate
The in-mold label film of netted exhaust grid is formed in polymers mould on the one side of thermoplastic layer.In order to avoid cold in cold press operation
Anilox roll and the low density ethylene-acetate ethylene copolymer is pressed to carry out adhesion, for example, the antitack agent is small particle titanium dioxide
At least one of the round and smooth glass microballoon in silicon powder, surface, ABS antitack agent and ethylene bis stearamide.In order to make mould internal standard
Label film be molded with plastic containers, be blow molded or thermoforming before, preferably adsorb and fix in mold inner-cavity, avoid sliding, also
Magnetic powder is added in low density ethylene-acetate ethylene copolymer of the molten condition, for example, the magnetic powder is iron oxide magnetic
At least one of powder, chromium dioxide magnetic powder and cobalt-iron oxide magnetic powder, in this way, so enabling to in-mold label film and molding
The inner sidewall of the type chamber of mould is preferably bonded together, and in-mold label film is not likely to produce buckling problems, and surface smoothness is higher,
So that in-mold label film preferably and is more uniformly crosslinking admittedly with the plastic cement molten liquid for the type chamber for being injected into pattern
Change reaction, this magnetic suck effect is highly stable, this is because the size completion of magnetic attraction can be by being added to the mixing slurry
The amount of middle magnetic powder controls, and in actual operation, engineering staff need to only be tested several times according to actual needs to be groped to obtain
Relationship to the inner sidewall of the type chamber of shaping mould, magnetic powder material and magnetic powder quantity and magnetic attraction is flexibly adjusted in subsequent
Section, however, Electrostatic Absorption be it is highly unstable, be very unlikely to control, be entirely by charge extremely rambunctious come realize inhale
Attached power improves the precision of magnetic suck therefore, it is necessary to ensure to mitigate the interference of Electrostatic Absorption by the way that antistatic agent is added.
The preparation method of above-mentioned in-mold label film is arranged after the first adhesive layer is prepared in polymer base material film
Outer surface on, then successively obtain laser silver layer, the second adhesive layer, then cover transparent protective layer in the second adhesive layer
On, the excellent in-mold label film of glossy degree is obtained conducive to subsequent, in addition, transparent protective layer can improve the wear-resistant of in-mold label film
Property, transition adhesive layer is then formed on the inner surface of polymer base material film, and it is total successively to obtain high density ethylene-vinyl acetate
Thermoplastic layer in thermoplastic layer and low density ethylene-acetate ethylene copolymer mould in polymers mould, and it is total in low density ethylene-vinyl acetate
Netted exhaust grid is formed in polymers mould on the one side of thermoplastic layer, has obtained the good in-mold label film of exhaust performance, in this way,
Enable to bubble between in-mold label film and plastic containers quickly and thoroughly discharge, improve after molding in-mold label film and
The integrally-built aesthetics of plastic containers.
It is below specific embodiment part.
Embodiment 1
High-density polyethylene resin base material film is provided;
Under the conditions of 150 DEG C of temperature, first bonding agents are added in reaction kettle, 30min is mixed to completely molten
Melt, then while hot on the outer surface coated in high-density polyethylene resin base material film, it then, will be silver-plated radium-shine using clad steel pressure roller
The polymer-based end lamination of film overlays in first bonding agents, after first bonding agents solidification, obtains the first adhesive layer,
In, first bonding agents include each component of following mass parts:Epoxy resin 10g, polyurethane 6g, methyl methacrylate 4g, hydroxyl
Ethyl cellulose 3g;
Laser operation is carried out on silver-plated polyester film using 3D true color holography technology, obtains laser silver
Layer, wherein laser head is 20cm at a distance from silver-plated polyester film, and radium-shine energy is 200W, and radium-shine temperature is 150
DEG C, the radium-shine time is 10s;
Under the conditions of 160 DEG C of temperature, second bonding agents are added in reaction kettle, 25min is mixed to completely molten
Melt, then is coated on the silver-plated polyester film while hot, then transparent, oriented stretched polypropene film is covered glued second while hot
It connects in agent, after second bonding agents solidification, obtains the second adhesive layer, wherein;Second bonding agents include following mass parts
Each component:4 parts of butyl acrylate, 6 parts of methyl methacrylate, 7 parts of methacrylic acid, 22 parts of tackifying resin and polyol fat
5 parts of acid esters;
High density ethylene-vinyl acetate that the agent of polyisocyanates gluing and vinyl acetate content are 5wt% is copolymerized in advance
Object carries out melting operation respectively, and polyisocyanates gluing agent is coated in the high-density polyethylene resin base material film while hot
On surface, then vinyl acetate content is coated in the polyisocyanic acid for 5wt% high density ethylene-acetate ethylene copolymer while hot
On ester adhesive, after polyisocyanates gluing agent solidification, transition adhesive layer is obtained, is 5wt% to vinyl acetate content
After high density ethylene-acetate ethylene copolymer solidification, thermoplastic layer in high density ethylene-acetate ethylene copolymer mould is obtained.
Under the conditions of 120 DEG C of temperature, the low density ethylene-acetate ethylene copolymer for being 15wt% by vinyl acetate content
Melting operation is carried out, it is described while hot that low density ethylene-acetate ethylene copolymer is coated in the high density ethylene-vinyl acetate
In copolymer mould on thermoplastic layer, then, cold pressing behaviour is carried out on the ethylene-vinyl acetate copolymer using cold pressing anilox roll
Make, obtains thermoplastic layer in low density ethylene-acetate ethylene copolymer mould, and the low density ethylene-acetate ethylene copolymer
Netted exhaust is formed on one side of the thermoplastic layer far from thermoplastic layer in the high density ethylene-acetate ethylene copolymer mould in mould
Grid obtains the in-mold label film of embodiment 1.
Embodiment 2
High density poly propylene resin base material is provided;
Under the conditions of 180 DEG C of temperature, first bonding agents are added in reaction kettle, 30min is mixed to completely molten
Melt, then while hot on the outer surface coated in high density poly propylene resin base material, then, using clad steel pressure roller by silver-plated laser film
Polymer-based end lamination overlay in first bonding agents, after the first bonding agents solidification after, obtain the first adhesive layer, wherein
First bonding agents include each component of following mass parts:Epoxy resin 12g, polyurethane 7g, methyl methacrylate 5g, dodecane
Base sodium sulfonate 4g;
Laser operation is carried out on silver-plated polyester film using 3D true color holography technology, obtains laser silver
Layer, wherein laser head is 25cm at a distance from silver-plated polyester film, and radium-shine energy is 250W, and radium-shine temperature is 160
DEG C, the radium-shine time is 15s;
Under the conditions of 170 DEG C of temperature, second bonding agents are added in reaction kettle, 25min is mixed to completely molten
Melt, then is coated on the silver-plated polyester film while hot, then transparent, oriented stretched polypropene film is covered glued second while hot
It connects in agent, after second bonding agents solidification, obtains the second adhesive layer, wherein;Second bonding agents include following mass parts
Each component:5 parts of butyl acrylate, 8 parts of methyl methacrylate, 9 parts of methacrylic acid, 24 parts of tackifying resin and polyol fat
6 parts of acid esters;
High density ethylene-vinyl acetate that the agent of polyisocyanates gluing and vinyl acetate content are 8wt% is copolymerized in advance
Object carries out melting operation respectively, and polyisocyanates gluing agent is coated in the interior table of the high density poly propylene resin base material while hot
On face, then vinyl acetate content is coated in the polyisocyanates for 8wt% high density ethylene-acetate ethylene copolymer while hot
On adhesive, after polyisocyanates gluing agent solidification, transition adhesive layer is obtained, is 8wt% high to vinyl acetate content
After density polyethylene-acetate ethylene copolymer solidification, thermoplastic layer in high density ethylene-acetate ethylene copolymer mould is obtained.
Under the conditions of 130 DEG C of temperature, the low density ethylene-acetate ethylene copolymer for being 20wt% by vinyl acetate content
Melting operation is carried out, it is described while hot that low density ethylene-acetate ethylene copolymer is coated in the high density ethylene-vinyl acetate
In copolymer mould on thermoplastic layer, then, cold pressing behaviour is carried out on the ethylene-vinyl acetate copolymer using cold pressing anilox roll
Make, obtains thermoplastic layer in low density ethylene-acetate ethylene copolymer mould, and the low density ethylene-acetate ethylene copolymer
Netted exhaust is formed on one side of the thermoplastic layer far from thermoplastic layer in the high density ethylene-acetate ethylene copolymer mould in mould
Grid obtains the in-mold label film of embodiment 2.
Embodiment 3
High density poly propylene resin base material is provided;
Under the conditions of 200 DEG C of temperature, first bonding agents are added in reaction kettle, 30min is mixed to completely molten
Melt, then while hot on the outer surface coated in high density poly propylene resin base material, then, using clad steel pressure roller by silver-plated laser film
Polymer-based end lamination overlay in first bonding agents, after the first bonding agents solidification after, obtain the first adhesive layer, wherein
First bonding agents include each component of following mass parts:Epoxy resin 15g, polyurethane 7g, methyl methacrylate 7g, dodecane
Base sodium sulfonate 5g;
Laser operation is carried out on silver-plated polyester film using 3D true color holography technology, obtains laser silver
Layer, wherein laser head is 26cm at a distance from silver-plated polyester film, and radium-shine energy is 250W, and radium-shine temperature is 160
DEG C, the radium-shine time is 20s;
Under the conditions of 170 DEG C of temperature, second bonding agents are added in reaction kettle, 25min is mixed to completely molten
Melt, then is coated on the silver-plated polyester film while hot, then transparent, oriented stretched polypropene film is covered glued second while hot
It connects in agent, after second bonding agents solidification, obtains the second adhesive layer, wherein;Second bonding agents include following mass parts
Each component:5 parts of butyl acrylate, 8 parts of methyl methacrylate, 9 parts of methacrylic acid, 24 parts of tackifying resin and polyol fat
6 parts of acid esters;
High density ethylene-vinyl acetate that the agent of polyisocyanates gluing and vinyl acetate content are 8wt% is copolymerized in advance
Object carries out melting operation respectively, and polyisocyanates gluing agent is coated in the interior table of the high density poly propylene resin base material while hot
On face, then vinyl acetate content is coated in the polyisocyanates for 8wt% high density ethylene-acetate ethylene copolymer while hot
On adhesive, after polyisocyanates gluing agent solidification, transition adhesive layer is obtained, is 8wt% high to vinyl acetate content
After density polyethylene-acetate ethylene copolymer solidification, thermoplastic layer in high density ethylene-acetate ethylene copolymer mould is obtained.
Under the conditions of 130 DEG C of temperature, the low density ethylene-acetate ethylene copolymer for being 20wt% by vinyl acetate content
Melting operation is carried out, it is described while hot that low density ethylene-acetate ethylene copolymer is coated in the high density ethylene-vinyl acetate
In copolymer mould on thermoplastic layer, then, antitack agent is coated using cold pressing anilox roll, and on the surface of cold pressing anilox roll;It is past molten
Melt in low density ethylene-acetate ethylene copolymer of state and magnetic powder is added, is stirred operation, obtains mixing slurry;By mixing slurry
It is coated in the high density ethylene-acetate ethylene copolymer mould while hot on thermoplastic layer, it is total to obtain low density ethylene-vinyl acetate
Polymers coating;Network type cold blocking is carried out to low density ethylene-acetate ethylene copolymer coating, formation includes orthogonal
The netted exhaust grid of a plurality of spaced transverse roller pressure air drain and a plurality of spaced longitudinal roll-in air discharge duct, obtains
Thermoplastic layer in low density ethylene-acetate ethylene copolymer mould, finally obtains the in-mold label film of embodiment 3.
It is proved through experiment, the in-mold label film being prepared by embodiment 1 to 3, there is excellent glossy degree, so that mould
Information on interior label film can be clear and beautiful display, simultaneously because be provided with transparent protective layer, substantially increase implementation
The abrasion resistance properties of the in-mold label film of example 1 to 3, additionally, due on in-mold label film be provided with netted exhaust grid so that
Bubble between in-mold label film and plastic containers quickly and is thoroughly discharged, and improves the mould internal standard of embodiment 1 to 3 after molding
Sign film and the integrally-built aesthetics of plastic containers.The especially in-mold label film of embodiment 3, also in the low-density of molten condition
It joined magnetic powder in ethylene-vinyl acetate copolymer, so enable to the in-mold label film of embodiment 3 and the type chamber of shaping mould
Inner sidewall be preferably bonded together, and in-mold label film is not likely to produce buckling problems, and surface smoothness is higher so that
In-mold label film preferably and is more uniformly crosslinking curing reaction with the plastic cement molten liquid for the type chamber for being injected into pattern, this
Kind of magnetic suck effect is highly stable, this is because complete can be by being added the amount of the magnetic powder into the mixing slurry for the size of magnetic attraction
It controls, in actual operation, engineering staff need to only be tested several times according to actual needs gropes that shaping mould can be obtained
The inner sidewall of type chamber, the relationship of magnetic powder material and magnetic powder quantity and magnetic attraction carry out flexible modulation, however, electrostatic in subsequent
Absorption be it is highly unstable, be very unlikely to control, be entirely to realize adsorption capacity by charge extremely rambunctious, therefore, need
To ensure to mitigate the interference of Electrostatic Absorption by the way that antistatic agent is added, improve the precision of magnetic suck.
The embodiments described above only express several embodiments of the present invention, and the description thereof is more specific and detailed, but simultaneously
It cannot therefore be construed as limiting the scope of the patent.It should be pointed out that coming for those of ordinary skill in the art
It says, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to protection of the invention
Range.Therefore, the scope of protection of the patent of the invention shall be subject to the appended claims.
Claims (10)
1. a kind of in-mold label film, which is characterized in that including:
Polymer base material film, the polymer base material film have the inner surface and the outer surface;
Silver print film, the silver print film include the first adhesive layer, silver-plated laser film, the second adhesive layer and transparency protected
Layer, first adhesive layer are adhered on the outer surface of the polymer base material film, and the silver-plated laser film includes polymer-based
Bottom and laser silver layer, the polymer-based bottom are adhered to first adhesive layer far from the polymer base material film
On one side, the laser silver layer plating is set on one side of the polymer-based bottom far from first adhesive layer,
Second adhesive layer is adhered on one side of the laser silver layer far from the polymer-based bottom, the transparent guarantor
Sheath is adhered to second adhesive layer far from the laser silver layer one side;
Thermoplastic film in ethylene-vinyl acetate copolymer mould, thermoplastic film bonding is institute in the ethylene-vinyl acetate copolymer mould
On the inner surface for stating polymer base material film, thermoplastic film is far from the polymer base material in the ethylene-vinyl acetate copolymer mould
Netted exhaust grid is offered on the one side of film.
2. in-mold label film according to claim 1, which is characterized in that the polymer base material film with a thickness of 9 microns
~16 microns.
3. in-mold label film according to claim 1, which is characterized in that the laser silver layer is far from the macromolecule
Laser mark part is set on the one side of basal layer.
4. in-mold label film according to claim 1, which is characterized in that the thickness of first adhesive layer and described second
The thickness of adhesive layer is identical.
5. in-mold label film according to claim 1, which is characterized in that the silver print film with a thickness of 23 microns~
34 microns.
6. the transparent protective layer is provided with multiple transparent lugs on the one side far from second adhesive layer.
7. in-mold label film according to claim 6, which is characterized in that between transparent lug described in each adjacent two away from
From equal.
8. in-mold label film according to claim 7, which is characterized in that the transparent lug has drops structure.
9. in-mold label film according to claim 7, which is characterized in that the transparent lug has crescent shape structure.
10. a kind of preparation method of in-mold label film, which is characterized in that include the following steps:
Polymer base material film is provided;
First bonding agents are subjected to melting operation in advance, then then, will be plated on the outer surface coated in polymer base material film while hot
The polymer-based end lamination of silver-colored laser film overlays in first bonding agents, after first bonding agents solidification, obtains the first bonding
Layer;
Laser operation is carried out on the plating silver layer of the silver-plated laser film using laser technique, obtains laser
Silver layer;
Second bonding agents are subjected to melting operation in advance, then are coated on the laser silver layer while hot, then while hot will be described
The transparent protective layer of silver-plated laser film covers in second bonding agents, after second bonding agents solidification, obtains second
Adhesive layer;
Ethylene-vinyl acetate copolymer is coated on the inner surface of polymer base material film, and total in the ethene-vinyl acetate
Netted exhaust grid is formed on one side of the thermoplastic film far from the polymer base material film in polymers mould, obtains in-mold label film.