CN108864874A - Anticoagulant ice coating coated on road surface - Google Patents
Anticoagulant ice coating coated on road surface Download PDFInfo
- Publication number
- CN108864874A CN108864874A CN201810379281.4A CN201810379281A CN108864874A CN 108864874 A CN108864874 A CN 108864874A CN 201810379281 A CN201810379281 A CN 201810379281A CN 108864874 A CN108864874 A CN 108864874A
- Authority
- CN
- China
- Prior art keywords
- parts
- road surface
- ice
- coated
- diethyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anticoagulant ice coating coated on road surface, including epoxy modification acrylate resin, polyurethane resin, -1 cyclopropyl ethyl ketone of 2- bromo- 2 (2- fluorophenyl), 2- (2- nitrobenzene amido) -3- cyano -5- methylthiophene, N, N- diethyl propargylamine propane sulfonic acid sodium, 3- glycidyl ether oxypropyltrimethoxysilane, septichen phenyl ester, hydroxyethyl cellulose, triphenyl phosphate, 2,2,4- trimethyl -1,3- pentanediol diisobutyrate, light absorber, tackifier, levelling agent;With good freezing, water resistance, resistance to ag(e)ing, crack resistance and absorption of solar energy, in use process, the anticoagulant ice agent release in part in anticoagulant ice coating, reduce the freezing point of ice and snow, along with vehicle external force is destroyed, it promotes ice and snow gradually to dissolve, to alleviate the generation that road crust coagulates ice.The coating can be laid with rapidly on new, old pavement, and can not destroy bituminous pavement overall structure, and the solidifying ice that not only can effectively alleviate road surface occurs, but also without any side effects to former road surface.
Description
Technical field
The present invention relates to ground surface material, in particular to a kind of anticoagulant ice coating coated on road surface.
Background technique
In early winter or season in the last days of winter, temperature changes in temperature alternating, the snowfall of road surface is gradually melted under Driving Loading,
Thin ice are easily formed under negative temperature effect, pavement skid resistance condition sharply declines.Ice and snow leads to vehicle tyre attachment coefficient significantly
It reduces.Therefore, it gets on the car in ice and snow road and is easy skidding, sideslip, braking distance significantly extends, and has seriously affected the operation of vehicle
Stability and safety, traffic accident incidence are higher.Existing anticoagulant ice additive is excessively used due to inorganic salts to environment
Larger damage is caused, it is especially larger to the corrosion impact of bridge reinforcement, and existing anticoagulant ice additive heat resistance is poor, it cannot
The production technology for meeting hot mixing method pitch blend composition, due to itself mechanical property difference and then page influences the wearability of bituminous pavement and strong
Degree.
Summary of the invention
In view of this, the purpose of the present invention is to provide a kind of anticoagulant ice coating coated on road surface, before ice and snow arriving
Anticoagulant ice coating is coated in advance on road surface, and the solidifying ice that not only can effectively alleviate road surface occurs, but also to former road surface without any
Side effect.
Anticoagulant ice coating coated on road surface of the invention, the coating raw material includes following components by weight:
25-40 parts of epoxy modification acrylate resins, 10-20 parts of polyurethane resins, 3-8 parts of 2- bromo- 2 (2- fluorophenyl) -1
Cyclopropyl ethyl ketone, 2-6 part 2- (2- nitrobenzene amido) -3- cyano -5- methylthiophene, 5-10 parts of N, N- diethyl propargylamine propane
Sodium sulfonate, 4-12 parts of 3- glycidyl ether oxypropyltrimethoxysilanes, 5-10 parts of septichen phenyl esters, 5-10 parts of hydroxyls
Ethyl cellulose, 1-5 portion triphenyl phosphate, 1-3 parts of 2,2,4- trimethyl -1,3- pentanediol diisobutyrates, 1-3 parts of light absorptions
Agent, 1-3 parts of tackifier, 1-3 parts of levelling agents;
Further, the coating raw material includes following components by weight:
35 parts of epoxy modification acrylate resins, 15 parts of polyurethane resins, 5 parts of -1 cyclopropyl second of 2- bromo- 2 (2- fluorophenyl)
Ketone, 4 parts of 2- (2- nitrobenzene amido) -3- cyano -5- methylthiophenes, 7 parts of N, N- diethyl propargylamine propane sulfonic acid sodium, 8 parts of 3-
Glycidyl ether oxypropyltrimethoxysilane, 7 parts of septichen phenyl esters, 7 parts of hydroxyethyl celluloses, 3 parts of tricresyl phosphates
Phenyl ester, 2 parts of 2,2,4- trimethyl -1,3- pentanediol diisobutyrates, 2 parts of light absorbers, 2 parts of tackifier, 2 parts of levelling agents;
Further, the light absorber is grouped as by the group of following parts by weight:8~12 parts of methanol, 85~95 parts of ethyl alcohol,
1,1 '-diethyl -3,3 '-two (γ-sulfopropyl) 5,5 '-two 0.05~0.15 part of trifluoromethyl miaow carbon cyanines sodium salts, 3,3- diethyl
0.05~0.15 part of salt compounded of iodine of sulphur carbon cyanines of base -9- methyl;38~42 DEG C of dissolutions will be heated to after above-mentioned article all mixing, can obtained
Obtain light optical absorbing agent;
Further, the tackifier are the mixture of polyethylene glycol stearate diester and hydroxyethyl cellulose;
Further, the levelling agent is polyether polyester azo polyether polyeste.
Beneficial effects of the present invention:The coating has good freezing, water resistance, resistance to ag(e)ing, crack resistance and too
It is positive can absorbability, in use process, the anticoagulant ice agent release in part, reduces the freezing point of ice and snow, adds vehicle in anticoagulant ice coating
External force is destroyed, and is promoted ice and snow and is gradually dissolved, to alleviate the generation that road crust coagulates ice.The coating can be new, old
It is laid with rapidly on road surface, and bituminous pavement overall structure can not be destroyed, not only can effectively alleviate the solidifying ice hair on road surface
It is raw and without any side effects to former road surface.
Specific embodiment
Embodiment one
The anticoagulant ice coating coated on road surface of the present embodiment, the coating raw material includes following components by weight:
25 parts of epoxy modification acrylate resins, 10 parts of polyurethane resins, 3 parts of -1 cyclopropyl second of 2- bromo- 2 (2- fluorophenyl)
Ketone, 2 parts of 2- (2- nitrobenzene amido) -3- cyano -5- methylthiophenes, 5 parts of N, N- diethyl propargylamine propane sulfonic acid sodium, 4 parts of 3-
Glycidyl ether oxypropyltrimethoxysilane, 5 parts of septichen phenyl esters, 5 parts of hydroxyethyl celluloses, 1 part of tricresyl phosphate
Phenyl ester, 1 part of 2,2,4- trimethyl -1,3- pentanediol diisobutyrate, 1 part of light absorber, 1 part of tackifier, 1 part of levelling agent.
In the present embodiment, the light absorber is grouped as by the group of following parts by weight:8 parts of methanol, 85 parts of ethyl alcohol, 1,
1 '-diethyl -3,3 '-two (γ-sulfopropyl) 5,5 '-two 0.05 part of trifluoromethyl miaow carbon cyanines sodium salts, 3,3- diethyl -9- methyl
0.05 part of salt compounded of iodine of sulphur carbon cyanines;38 DEG C of dissolutions will be heated to after above-mentioned article all mixing, can be obtained light optical absorbing agent;The thickening
Agent is the mixture of polyethylene glycol stearate diester and hydroxyethyl cellulose;
The levelling agent is polyether polyester azo polyether polyeste.
Embodiment two
The anticoagulant ice coating coated on road surface of the present embodiment, the coating raw material includes following components by weight:
40 parts of epoxy modification acrylate resins, 20 parts of polyurethane resins, 8 parts of -1 cyclopropyl second of 2- bromo- 2 (2- fluorophenyl)
Ketone, 6 parts of 2- (2- nitrobenzene amido) -3- cyano -5- methylthiophenes, 10 parts of N, N- diethyl propargylamine propane sulfonic acid sodium, 12 parts
3- glycidyl ether oxypropyltrimethoxysilane, 10 parts of septichen phenyl esters, 10 parts of hydroxyethyl celluloses, 5 parts of phosphorus
Triphenyl phosphate ester, 3 parts of 2,2,4- trimethyl -1,3- pentanediol diisobutyrates, 3 parts of light absorbers, 3 parts of tackifier, 3 parts of levellings
Agent.
In the present embodiment, the light absorber is grouped as by the group of following parts by weight:12 parts of methanol, 95 parts of ethyl alcohol, 1,
1 '-diethyl -3,3 '-two (γ-sulfopropyl) 5,5 '-two 0.15 part of trifluoromethyl miaow carbon cyanines sodium salts, 3,3- diethyl -9- methyl
0.15 part of salt compounded of iodine of sulphur carbon cyanines;42 DEG C of dissolutions will be heated to after above-mentioned article all mixing, can be obtained light optical absorbing agent;The thickening
Agent is the mixture of polyethylene glycol stearate diester and hydroxyethyl cellulose;
The levelling agent is polyether polyester azo polyether polyeste.
Embodiment three
The anticoagulant ice coating coated on road surface of the present embodiment, the coating raw material includes following components by weight:
25 parts of epoxy modification acrylate resins, 20 parts of polyurethane resins, 3 parts of -1 cyclopropyl second of 2- bromo- 2 (2- fluorophenyl)
Ketone, 6 parts of 2- (2- nitrobenzene amido) -3- cyano -5- methylthiophenes, 5 parts of N, N- diethyl propargylamine propane sulfonic acid sodium, 12 parts of 3-
Glycidyl ether oxypropyltrimethoxysilane, 5 parts of septichen phenyl esters, 10 parts of hydroxyethyl celluloses, 1 part of tricresyl phosphate
Phenyl ester, 3 parts of 2,2,4- trimethyl -1,3- pentanediol diisobutyrates, 1 part of light absorber, 3 parts of tackifier, 1 part of levelling agent.
In the present embodiment, the light absorber is grouped as by the group of following parts by weight:8 parts of methanol, 95 parts of ethyl alcohol, 1,
1 '-diethyl -3,3 '-two (γ-sulfopropyl) 5,5 '-two 0.05 part of trifluoromethyl miaow carbon cyanines sodium salts, 3,3- diethyl -9- methyl
0.15 part of salt compounded of iodine of sulphur carbon cyanines;39 DEG C of dissolutions will be heated to after above-mentioned article all mixing, can be obtained light optical absorbing agent;The thickening
Agent is the mixture of polyethylene glycol stearate diester and hydroxyethyl cellulose;
The levelling agent is polyether polyester azo polyether polyeste.
Example IV
The anticoagulant ice coating coated on road surface of the present embodiment, the coating raw material includes following components by weight:
40 parts of epoxy modification acrylate resins, 10 parts of polyurethane resins, 8 parts of -1 cyclopropyl second of 2- bromo- 2 (2- fluorophenyl)
Ketone, 2 parts of 2- (2- nitrobenzene amido) -3- cyano -5- methylthiophenes, 10 parts of N, N- diethyl propargylamine propane sulfonic acid sodium, 4 parts of 3-
Glycidyl ether oxypropyltrimethoxysilane, 10 parts of septichen phenyl esters, 5 parts of hydroxyethyl celluloses, 5 parts of tricresyl phosphates
Phenyl ester, 1 part of 2,2,4- trimethyl -1,3- pentanediol diisobutyrate, 3 parts of light absorbers, 1 part of tackifier, 3 parts of levelling agents.
In the present embodiment, the light absorber is grouped as by the group of following parts by weight:12 parts of methanol, 85 parts of ethyl alcohol, 1,
1 '-diethyl -3,3 '-two (γ-sulfopropyl) 5,5 '-two 0.15 part of trifluoromethyl miaow carbon cyanines sodium salts, 3,3- diethyl -9- methyl
0.05 part of salt compounded of iodine of sulphur carbon cyanines;41 DEG C of dissolutions will be heated to after above-mentioned article all mixing, can be obtained light optical absorbing agent;The thickening
Agent is the mixture of polyethylene glycol stearate diester and hydroxyethyl cellulose;
The levelling agent is polyether polyester azo polyether polyeste.
Embodiment five
The anticoagulant ice coating coated on road surface of the present embodiment, the coating raw material includes following components by weight:
28 parts of epoxy modification acrylate resins, 10 parts of polyurethane resins, 6 parts of -1 cyclopropyl second of 2- bromo- 2 (2- fluorophenyl)
Ketone, 5 parts of 2- (2- nitrobenzene amido) -3- cyano -5- methylthiophenes, 5 parts of N, N- diethyl propargylamine propane sulfonic acid sodium, 12 parts of 3-
Glycidyl ether oxypropyltrimethoxysilane, 7 parts of septichen phenyl esters, 5 parts of hydroxyethyl celluloses, 5 parts of tricresyl phosphates
Phenyl ester, 2 parts of 2,2,4- trimethyl -1,3- pentanediol diisobutyrates, 1 part of light absorber, 3 parts of tackifier, 2 parts of levelling agents.
In the present embodiment, the light absorber is grouped as by the group of following parts by weight:11 parts of methanol, 88 parts of ethyl alcohol, 1,
1 '-diethyl -3,3 '-two (γ-sulfopropyl) 5,5 '-two 0.08 part of trifluoromethyl miaow carbon cyanines sodium salts, 3,3- diethyl -9- methyl
0.05 part of salt compounded of iodine of sulphur carbon cyanines;41 DEG C of dissolutions will be heated to after above-mentioned article all mixing, can be obtained light optical absorbing agent;The thickening
Agent is the mixture of polyethylene glycol stearate diester and hydroxyethyl cellulose;
The levelling agent is polyether polyester azo polyether polyeste.
Embodiment six
The anticoagulant ice coating coated on road surface of the present embodiment, the coating raw material includes following components by weight:
35 parts of epoxy modification acrylate resins, 15 parts of polyurethane resins, 5 parts of -1 cyclopropyl second of 2- bromo- 2 (2- fluorophenyl)
Ketone, 4 parts of 2- (2- nitrobenzene amido) -3- cyano -5- methylthiophenes, 7 parts of N, N- diethyl propargylamine propane sulfonic acid sodium, 8 parts of 3-
Glycidyl ether oxypropyltrimethoxysilane, 7 parts of septichen phenyl esters, 7 parts of hydroxyethyl celluloses, 3 parts of tricresyl phosphates
Phenyl ester, 2 parts of 2,2,4- trimethyl -1,3- pentanediol diisobutyrates, 2 parts of light absorbers, 2 parts of tackifier, 2 parts of levelling agents.
In the present embodiment, the light absorber is grouped as by the group of following parts by weight:10 parts of methanol, 90 parts of ethyl alcohol, 1,
1 '-diethyl -3,3 '-two (γ-sulfopropyl) 5,5 '-two 0.1 part of trifluoromethyl miaow carbon cyanines sodium salts, 3,3- diethyl -9- methyl
0.1 part of salt compounded of iodine of sulphur carbon cyanines;40 DEG C of dissolutions will be heated to after above-mentioned article all mixing, can be obtained light optical absorbing agent;The thickening
Agent is the mixture of polyethylene glycol stearate diester and hydroxyethyl cellulose;
The levelling agent is polyether polyester azo polyether polyeste.
1, performance test:
1) coating is distributed in culture dish, is spontaneously dried at room temperature;
2) by pure distilled water and it is coated with the culture dish of coating as 5 hours in -5 DEG C of high-low temperature test chamber, distilled water
Form subcooled water;
3) subcooled water is spilt to the water film thickness that coating surface is controlled in coating surface in 1mm or so (1kg/m2), continue
The cryostat in -5 DEG C of environment observes coating surface ice condition at regular intervals.
As a result:The culture dish for being coated with coating can't form firm ice sheet after subcooled water freezing a few hours are added, and be tied
Ice sheet is gently stirred and is loosed off.
2, pathway performance test, coating application resists effect icy on road after 2 weeks obvious, and not by vehicle driving band
It walks.
Finally, it is stated that the above examples are only used to illustrate the technical scheme of the present invention and are not limiting, although referring to compared with
Good embodiment describes the invention in detail, those skilled in the art should understand that, it can be to skill of the invention
Art scheme is modified or replaced equivalently, and without departing from the objective and range of technical solution of the present invention, should all be covered at this
In the scope of the claims of invention.
Claims (5)
1. a kind of anticoagulant ice coating coated on road surface, it is characterised in that:The coating raw material includes following components by weight:
25-40 parts of epoxy modification acrylate resins, 10-20 parts of polyurethane resins, 3-8 parts of -1 cyclopropyls of 2- bromo- 2 (2- fluorophenyl)
Base ethyl ketone, 2-6 part 2- (2- nitrobenzene amido) -3- cyano -5- methylthiophene, 5-10 parts of N, N- diethyl propargylamine propane sulfonic acid
Sodium, 4-12 parts of 3- glycidyl ether oxypropyltrimethoxysilanes, 5-10 parts of septichen phenyl esters, 5-10 parts of ethoxys
Cellulose, 1-5 portion triphenyl phosphate, 1-3 parts of 2,2,4- trimethyl -1,3- pentanediol diisobutyrates, 1-3 parts of light absorbers,
1-3 parts of tackifier, 1-3 parts of levelling agents.
2. the anticoagulant ice coating according to claim 1 coated on road surface, it is characterised in that:The coating raw material is by weight
Part includes following components:
35 parts of epoxy modification acrylate resins, 15 parts of polyurethane resins, 5 parts of -1 cyclopropyl ethyl ketones of 2- bromo- 2 (2- fluorophenyl), 4
Part 2- (2- nitrobenzene amido) -3- cyano -5- methylthiophene, 7 parts of N, N- diethyl propargylamine propane sulfonic acid sodium, 8 parts of 3- shrink
Glyceryl etheroxypropyltrimethoxysilane, 7 parts of septichen phenyl esters, 7 parts of hydroxyethyl celluloses, 3 portions of triphenyl phosphates,
2 parts of 2,2,4- trimethyl -1,3- pentanediol diisobutyrates, 2 parts of light absorbers, 2 parts of tackifier, 2 parts of levelling agents.
3. the anticoagulant ice coating according to claim 2 coated on road surface, it is characterised in that:The light absorber is by as follows
The group of parts by weight is grouped as:8~12 parts of methanol, 85~95 parts of ethyl alcohol, 1,1 '-diethyl -3,3 '-two (γ-sulfopropyl) 5,
0.05~0.15 part of salt compounded of iodine of sulphur carbon cyanines of -9- methyl of 5 '-two 0.05~0.15 part of trifluoromethyl miaow carbon cyanines sodium salts, 3,3- diethyl;
38~42 DEG C of dissolutions will be heated to after above-mentioned article all mixing, can be obtained light optical absorbing agent.
4. the anticoagulant ice coating according to claim 3 coated on road surface, it is characterised in that:The tackifier are poly- second two
The mixture of alcohol double stearates and hydroxyethyl cellulose.
5. the anticoagulant ice coating according to claim 4 coated on road surface, it is characterised in that:The levelling agent is poly- for polyethers
Ester modified organosiloxane.