CN108864834A - A kind of antirusting paint - Google Patents
A kind of antirusting paint Download PDFInfo
- Publication number
- CN108864834A CN108864834A CN201810820808.2A CN201810820808A CN108864834A CN 108864834 A CN108864834 A CN 108864834A CN 201810820808 A CN201810820808 A CN 201810820808A CN 108864834 A CN108864834 A CN 108864834A
- Authority
- CN
- China
- Prior art keywords
- parts
- added
- antirusting paint
- acrylic emulsion
- micro mist
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to protective coating technical fields, and in particular to a kind of antirusting paint.The component of antirusting paint includes:Styrene-acrylic emulsion, pure-acrylic emulsion, composite tackifier, zinc magnesium alloy micro mist, iron oxide red, aluminium triphosphate, polyethylene oxide polypropylene oxide monobutyl base ether, anti-flash rusting agent, titanium dioxide, alcohol ester 12, preservative, defoaming agent, dispersing agent and water.Wherein, composite tackifier is a kind of by the compound special composition being prepared of the substances such as mucopolysaccharide, modified cellulose and converted starch;Contain alkyl imidazole morpholine amide, alkylbenzotriazole, sodium nitrite and disodium ethylene diamine tetraacetate in anti-flash rusting agent;The weatherability of this antirusting paint is strong, and anti-oxidant, corrosion resistance protrudes;And adhesive force intensity with higher, heat-resisting and resistance to low temperature are preferable, it is not easy to fall off.
Description
Technical field
The present invention relates to protective coating technical fields, and in particular to a kind of antirusting paint.
Background technique
Antirusting paint is that one kind protects metal surfaces from the chemistry of atmosphere, seawater etc. or the coating of electrochemical corrosion.?
Antirusting paint is coated in metal surface can effectively avoid the direct invasion of various corrosive substances in atmosphere, maximumlly extend
Metal service life.Conventional use of antirust paint substantially oiliness and two kinds aqueous.Oily antirust varniss makes material surface is greasy to go
Except difficulty, it has been rarely employed.Oily antirust varniss is easy to use, cheap, but because containing the Toxics such as nitrite, chromate
Matter, larger to operator's harm, country has limited use, and such properties of product are single, are not able to satisfy magnetic alloy material
Antirust requirement.
Antirusting paint currently on the market is broadly divided into physical and chemical rust coating two major classes.The former by pigment and
The appropriate cooperation of paint vehicle forms fine and close paint film to prevent the intrusion of corrosive substance, such as iron oxide red, aluminium powder, graphite antirust paint;
The latter acts on by the chemistry suppression rust of rust resisting pigment, such as red lead, zinc chromate anti-rust paint.The purposes of antirust paint is very extensive, traffic,
Building, electric power, mechanical, the every field such as ship, chemical industry have application.
Current market sales of aqueous rust-proof coatings are mainly made of components such as water-base resin and functional stuffings, and function is filled out
The difference of material determines the performance characteristics and application scenarios of different antirusting paints.Although most of antirusting paint is filled out by function
The collocation and improvement of material, so that the corrosion-resistant antioxygenic property of coating is greatly improved, the protective performance of coating is very outstanding.
But most of aqueous rust-proof coatings all have a problem of adhesive force intensity and anti-aging property deficiency, coating it is cold-resistant with it is resistance to
Hot property is poor, and in extreme temperature conditions, film layer is easy to fall off.
Invention patent mandate notification number CN103665991B discloses a kind of Automotive epoxy resin anti-rust paint and its preparation side
Method, the coating composition in the technical solution includes ethyl acetate, epoxy resin, maleic anhydride, ferroso-ferric oxide, nanometer two
Silica, titanium dioxide, zinc oxide, calcium carbonate, diethylenetriamine and film-forming resin.Although the antirust paint improves the anti-of coating
Rust performance, toughness and mechanical light intensity, but the adhesive property under the adhesive force intensity and high and low temperature state of coating is still poor;
There is the space further improved in performance.
Summary of the invention
Aiming at the problems existing in the prior art, the present invention provides a kind of antirusting paint, this antirusting paint it is weather-proof
Property it is strong, anti-oxidant, corrosion resistance is prominent;And adhesive force intensity with higher, heat-resisting and resistance to low temperature is preferable, does not allow
It is easy to fall off.
In order to achieve the above object, the present invention is achieved through the following technical solutions:
A kind of antirusting paint, according to mass fraction, the component of antirusting paint includes:80-90 parts of styrene-acrylic emulsion, pure-acrylic emulsion 15-
30 parts, 6-9 parts of composite tackifier, 3-7 parts of zinc magnesium alloy micro mist, 2-4 parts of iron oxide red, 2-3 parts of aluminium triphosphate, polycyclic oxygen second
1-3 parts of base ether of alkane polypropylene oxide monobutyl, 1.4-1.9 parts of anti-flash rusting agent, 15-20 parts of titanium dioxide, 12 0.3-0.8 parts of alcohol ester,
0.5-1.5 parts of preservative, 0.3-0.6 parts of defoaming agent, 1.2-1.5 parts of dispersing agent, 15-20 parts of water.
Preferably, according to mass fraction, the component of antirusting paint includes:84-87 parts of styrene-acrylic emulsion, pure-acrylic emulsion 18-22
Part, 7-8 parts of composite tackifier, 5-6 parts of zinc magnesium alloy micro mist, 2.5-3.5 parts of iron oxide red, 2.2-2.6 parts of aluminium triphosphate, gather
1.3-2.4 parts of base ether of ethylene oxide polypropylene oxide monobutyl, 1.5-1.8 parts of anti-flash rusting agent, 17-19 parts of titanium dioxide, alcohol ester 12
0.4-0.6 parts, 0.7-0.9 parts of preservative, 0.3-0.5 parts of defoaming agent, 1.2-1.4 parts of dispersing agent, 16-18 parts of water.
It is further preferred that according to mass fraction, the component of antirusting paint includes:86 parts of styrene-acrylic emulsion, pure-acrylic emulsion 20
Part, 8 parts of composite tackifier, 5.5 parts of zinc magnesium alloy micro mist, 3 parts of iron oxide red, 2.4 parts of aluminium triphosphate, polyethylene oxide polycyclic
1.8 parts of Ethylene Oxide single-butyl ether, 1.7 parts of anti-flash rusting agent, 18 parts of titanium dioxide, 12 parts of alcohol ester, 0.8 part of preservative, defoaming agent
0.4 part, 1.3 parts of dispersing agent, 17 parts of water.
In the present invention, the preparation method of composite tackifier includes the following steps:
(1)According to mass fraction, the sodium hydroxide solution of 90 parts of 15wt% is added in reaction kettle, 50 parts of lignin are added
The uniform stirring into solution, and dispersion liquid is heated to 45-48 DEG C, then by 6.4 parts of hydroquinones and 3.6 parts of tert-butyl o benzene
Diphenol is added in reaction kettle, continues to be stirring evenly and then adding into 10 part 25% of formalin, the temperature in heating reaction kettle is extremely
65-70 DEG C, then 2.4 parts of tannic acids are added, after mixing evenly, it is the mixed of 180-200cp that material in reactor, which is cooked into viscosity,
Object A is closed, it is spare;
(2)100 parts of biological starch are added in 160 parts of deionized waters, are stirred evenly, then 2 parts is added into dispersion liquid and contains
There is the phosphate buffer of mesophilicα-diastase, the potency of the mesophilicα-diastase in buffer is 10000U/g, by dispersion liquid
Temperature is increased to 65-70 DEG C, keeps the temperature enzyme digestion reaction 2-3h then from hydrochloric acid is added into enzymolysis liquid and adjusts the pH value of enzymolysis liquid
To 4-4.3,30 parts of calcium gluconates and 7 parts of magnesium carbonate are added, adjust the pH value of dispersion liquid after being uniformly dispersed with sodium hydroxide
It for 5.3-5.5, will be filtered after dispersion liquid activated carbon adsorption, obtain filtrate, filtrate passes through 100-110 DEG C of spray drying treatment
After obtain micro mist B;
(3)200 parts of deionized waters are added into reaction kettle, is heated to 55-60 DEG C, 80 parts of micro mist B is then added to reaction kettle
In;By 6.8 parts of polyethylene glycol, 3.7 parts of diethylene glycol butyl ethers and 12.5 parts of alkenyl succinic anhydrides are added to 30 parts of isopropanol solvents
In sufficiently dissolve, during solution is added in reaction kettle, under nitrogen atmosphere protection, 40- is reacted with 95-100 DEG C of temperature
60min will filter after product activated carbon adsorption after reaction, micro mist C obtained after being then spray-dried filtrate;
(4)75 parts of micro mist C, 30 parts of mucopolysaccharides, 13 parts of propylene oxide and 4 parts of vinyl sulfonic acids are added in reaction kettle, then plus
Enter 500 parts of deionized waters, 8-10min is stirred with 30-35 DEG C of temperature, 25 parts of mixture A are added in reaction kettle, uniformly
Stirring is completely dispersed to mixture A, continues heating reaction 1.5-2h, finally by product with 100-105 DEG C of temperature drying and powder
It is broken, obtain required composite tackifier.
Wherein, step(2)In biological starch select tapioca, cornstarch, in potato starch and glutinous rice starch
One kind.
Step(4)In mucopolysaccharide select guar gum or xanthan gum.
Preferably, the average grain diameter of zinc magnesium alloy micro mist is 0.5-5 μm.
Preferably, alkyl imidazole morpholine amide, alkylbenzotriazole, sodium nitrite and ethylenediamine tetraacetic are contained in anti-flash rusting agent
Acetic acid disodium, four content ratio are 4:1:3:3.
Preferably, defoaming agent is polyoxyethylene polyoxy propyl alcohol amidogen ether, dimethyl silicone polymer or polyoxyethylene polyoxypropylene
Glycerin ether.
The preparation method of antirusting paint provided by the invention is:
According to mass fraction, styrene-acrylic emulsion and pure-acrylic emulsion are added in Scattered Kettle, are heated to 75-80 DEG C, insulated and stirred point
It dissipates uniformly, then composite tackifier is added to the water, is heated to 55-60 DEG C and stirs to get gelatinization slurry, gelatinization slurry is added
Enter into Scattered Kettle, continues to be stirred 8-10min with the revolving speed of 550-600r/min and multiple emulsion, then by tripolyphosphate
Aluminium, polyethylene oxide polypropylene oxide monobutyl base ether, zinc magnesium alloy micro mist and iron oxide red are added in Scattered Kettle, with 650-
The revolving speed decentralized processing 10-15min of 800r/min then sequentially adds dispersing agent, titanium dioxide, preservative, anti-flash rusting agent, defoaming
Agent and alcohol ester 12 will obtain material and are cooled to room temperature, sealed package obtains with identical revolving speed decentralized processing 25-30min
Required antirusting paint.
The present invention has following beneficial effect:
For the type antirusting paint using the compound of styrene-acrylic emulsion and pure-acrylic emulsion as emulsion system, the appropriate addition of pure-acrylic emulsion can
To enhance the anti-aging property and waterproof performance of coating on the basis of excessively not exceeding cost budgeting.In order to enhance aqueous painting
Expect the adhesive force intensity to metal base, a kind of special composite tackifier is specially added in lotion.The composite tackifier is
It is a kind of by the compound special composition being prepared of the substances such as mucopolysaccharide, modified cellulose and converted starch;The substance has good
The viscosity and adhesive force intensity of resin emulsion can be improved in good Efficient Adhesive Promotion, and the type composition also has by good phase
Capacitive and dispersibility after dispersing in emulsion system, will not occur cohesion or self-adhesion generate " pimple group ", this makes antirusting paint
The more uniform stabilization of property;Film-formation result is more outstanding.
In addition, composite tackifier, aluminium triphosphate and polyethylene oxide polypropylene oxide monobutyl base ether three are in lotion
In system after dispersion reaction, it can produce synergistic effect, significantly improve the stability of antirusting paint, so that antirusting paint is extreme
Under high temperature and low-temperature condition, good adhesion strength and adhewsive action can be still kept, avoids film layer from cracking or fall off, loses
Protective action.
The type antirusting paint can both be formed by lotion, iron oxide red, titanium dioxide filler and the second-class substance of alcohol ester ten and be caused
Close protection film layer, is sealed metallic substrate surface, reaches antirust, corrosion resistant effect;Zinc magnesium alloy can also be passed through
The electrochemical corrosion effect of powder further promotes the corrosion resistance of coating;And the addition of anti-flash rusting agent, then it can be to avoid gold
The miniature rust spot for belonging to substrate surface corrodes metal base inside rust-proof coating;Therefore the protective of the type antirusting paint
It can protrude very much.
Specific embodiment
Below with reference to embodiment, further description of the specific embodiments of the present invention, and following embodiment is only used for more
Technical solution of the present invention is clearly demonstrated, and not intended to limit the protection scope of the present invention.
In following embodiment, the preparation method of composite tackifier includes the following steps:
(1)According to mass fraction, the sodium hydroxide solution of 90 parts of 15wt% is added in reaction kettle, 50 parts of lignin are added
The uniform stirring into solution, and dispersion liquid is heated to 47 DEG C, then by 6.4 parts of hydroquinones and 3.6 parts of tert-butyl o benzene two
Phenol is added in reaction kettle, continues to be stirring evenly and then adding into 10 part 25% of formalin, the temperature in heating reaction kettle to 68
DEG C, then 2.4 parts of tannic acids are added, after mixing evenly, material in reactor is cooked into viscosity is 190cp mixture A, it is standby
With;
(2)100 parts of biological starch are added in 160 parts of deionized waters, are stirred evenly, then 2 parts is added into dispersion liquid and contains
There is the phosphate buffer of mesophilicα-diastase, the potency of the mesophilicα-diastase in buffer is 10000U/g, by dispersion liquid
Temperature is increased to 67 DEG C, keeps the temperature enzyme digestion reaction 2.5h, then from hydrochloric acid is added into enzymolysis liquid, adjust the pH value of enzymolysis liquid to
4.2,30 parts of calcium gluconates and 7 parts of magnesium carbonate are added, are with the pH value that sodium hydroxide adjusts dispersion liquid after being uniformly dispersed
5.4, it will be filtered after dispersion liquid activated carbon adsorption, obtain filtrate, filtrate obtains micro mist after 105 DEG C of spray drying treatment
B;
(3)200 parts of deionized waters are added into reaction kettle, is heated to 57 DEG C, then 80 parts of micro mist B is added in reaction kettle;
By 6.8 parts of polyethylene glycol, 3.7 parts of diethylene glycol butyl ethers and 12.5 parts of alkenyl succinic anhydrides are added in 30 parts of isopropanol solvents and fill
Point dissolution during solution is added in reaction kettle, under nitrogen atmosphere protection, reacts 50min, reaction knot with 98 DEG C of temperature
Shu Hou will filter after product activated carbon adsorption, micro mist C obtained after being then spray-dried filtrate;
(4)75 parts of micro mist C, 30 parts of mucopolysaccharides, 13 parts of propylene oxide and 4 parts of vinyl sulfonic acids are added in reaction kettle, then plus
Enter 500 parts of deionized waters, 9min is stirred with 33 DEG C of temperature, 25 parts of mixture A are added in reaction kettle, uniform stirring is extremely
Mixture A is completely dispersed, and continues heating reaction 1.7h, finally product is dried and crushed with 103 DEG C of temperature, needed for obtaining
Composite tackifier.
Wherein, step(2)In biological starch select tapioca.
Step(4)In mucopolysaccharide select xanthan gum.
Embodiment 1
A kind of antirusting paint, according to mass fraction, the component of antirusting paint includes:It is 80 parts of styrene-acrylic emulsion, 15 parts of pure-acrylic emulsion, multiple
6 parts of tackifier of conjunction, 3 parts of zinc magnesium alloy micro mist, 2 parts of iron oxide red, 2 parts of aluminium triphosphate, polyethylene oxide polypropylene oxide list
1 part of butyl ether, 1.4 parts of anti-flash rusting agent, 1 part of titanium dioxide, 12 parts of alcohol ester, 0.5 part of preservative, 0.3 part of defoaming agent, dispersion
1.2 parts of agent, 15 parts of water.
Wherein, the average grain diameter of zinc magnesium alloy micro mist is 0.5-5 μm.
Contain alkyl imidazole morpholine amide, alkylbenzotriazole, sodium nitrite and ethylenediamine tetra-acetic acid two in anti-flash rusting agent
Sodium, four content ratio are 4:1:3:3.
Defoaming agent is polyoxyethylene polyoxy propyl alcohol amidogen ether.
The preparation method of antirusting paint provided in this embodiment is:
According to mass fraction, styrene-acrylic emulsion and pure-acrylic emulsion are added in Scattered Kettle, are heated to 75 DEG C, insulated and stirred dispersion is equal
It is even, then composite tackifier is added to the water, 55 DEG C is heated to and stirs to get gelatinization slurry, gelatinization slurry is added to dispersion
In kettle, continues to be stirred 8min with the revolving speed of 550r/min and multiple emulsion, then gather aluminium triphosphate, polyethylene oxide
Propylene oxide single-butyl ether, zinc magnesium alloy micro mist and iron oxide red are added in Scattered Kettle, at the revolving speed dispersion of 650r/min
10min is managed, sequentially adds dispersing agent, titanium dioxide, preservative, anti-flash rusting agent, defoaming agent and alcohol ester 12, then with identical turn
Fast decentralized processing 25min, will obtain material and is cooled to room temperature, and sealed package obtains required antirusting paint.
Embodiment 2
A kind of antirusting paint, according to mass fraction, the component of antirusting paint includes:It is 90 parts of styrene-acrylic emulsion, 30 parts of pure-acrylic emulsion, multiple
9 parts of tackifier of conjunction, 7 parts of zinc magnesium alloy micro mist, 4 parts of iron oxide red, 3 parts of aluminium triphosphate, polyethylene oxide polypropylene oxide list
3 parts of butyl ether, 1.9 parts of anti-flash rusting agent, 20 parts of titanium dioxide, 12 parts of alcohol ester, 1.5 parts of preservative, 0.6 part of defoaming agent, dispersion
1.5 parts of agent, 20 parts of water.
Wherein, the average grain diameter of zinc magnesium alloy micro mist is 0.5-5 μm.
Contain alkyl imidazole morpholine amide, alkylbenzotriazole, sodium nitrite and ethylenediamine tetra-acetic acid two in anti-flash rusting agent
Sodium, four content ratio are 4:1:3:3.
Defoaming agent is dimethyl silicone polymer.
The preparation method of antirusting paint provided in this embodiment is:
According to mass fraction, styrene-acrylic emulsion and pure-acrylic emulsion are added in Scattered Kettle, are heated to 80 DEG C, insulated and stirred dispersion is equal
It is even, then composite tackifier is added to the water, 60 DEG C is heated to and stirs to get gelatinization slurry, gelatinization slurry is added to dispersion
In kettle, continue to be stirred 10min with the revolving speed of 600r/min and multiple emulsion, then by aluminium triphosphate, polyethylene oxide
Polypropylene oxide monobutyl base ether, zinc magnesium alloy micro mist and iron oxide red are added in Scattered Kettle, are dispersed with the revolving speed of 800r/min
15min is handled, sequentially adds dispersing agent, titanium dioxide, preservative, anti-flash rusting agent, defoaming agent and alcohol ester 12, then with identical
Revolving speed decentralized processing 30min, will obtain material and is cooled to room temperature, and sealed package obtains required antirusting paint.
Embodiment 3
A kind of antirusting paint, according to mass fraction, the component of antirusting paint includes:It is 86 parts of styrene-acrylic emulsion, 20 parts of pure-acrylic emulsion, multiple
8 parts of tackifier of conjunction, 5.5 parts of zinc magnesium alloy micro mist, 3 parts of iron oxide red, 2.4 parts of aluminium triphosphate, polyethylene oxide polycyclic oxygen third
1.8 parts of alkane single-butyl ether, 1.7 parts of anti-flash rusting agent, 18 parts of titanium dioxide, 12 parts of alcohol ester, 0.8 part of preservative, defoaming agent 0.4
Part, 1.3 parts of dispersing agent, 17 parts of water.
Wherein, the average grain diameter of zinc magnesium alloy micro mist is 0.5-5 μm.
Contain alkyl imidazole morpholine amide, alkylbenzotriazole, sodium nitrite and ethylenediamine tetra-acetic acid two in anti-flash rusting agent
Sodium, four content ratio are 4:1:3:3.
Defoaming agent is polyoxyethylene polyoxypropylene glycerin ether.
The preparation method of antirusting paint provided in this embodiment is:
According to mass fraction, styrene-acrylic emulsion and pure-acrylic emulsion are added in Scattered Kettle, are heated to 77 DEG C, insulated and stirred dispersion is equal
It is even, then composite tackifier is added to the water, 57 DEG C is heated to and stirs to get gelatinization slurry, gelatinization slurry is added to dispersion
In kettle, continues to be stirred 9min with the revolving speed of 580r/min and multiple emulsion, then gather aluminium triphosphate, polyethylene oxide
Propylene oxide single-butyl ether, zinc magnesium alloy micro mist and iron oxide red are added in Scattered Kettle, at the revolving speed dispersion of 700r/min
13min is managed, sequentially adds dispersing agent, titanium dioxide, preservative, anti-flash rusting agent, defoaming agent and alcohol ester 12, then with identical turn
Fast decentralized processing 26min, will obtain material and is cooled to room temperature, and sealed package obtains required antirusting paint.
Performance test
According to the test method in related mandatory national standards, the performance of antirusting paint in the present embodiment is tested, and
" Shanghai Si Jia " board water-based metal antirust industrial paint that the quick coating Co., Ltd sale of Shanghai Songyuan is arranged as a control group, carries out performance
Test comparison obtains following test result:
Table 1:The performance test results of antirusting paint and control group in the present embodiment
The above test data discovery is analyzed, antirusting paint provided in the present invention has impact resistance outstanding and flexibility,
The adhesive force of coating is good, and film strength is high, and corrosion resistance is outstanding, in addition, being compared by conventional antirusting paint, coating of the present invention
Cold tolerance and the result of heat resistance test are also obvious more preferable, and the stability of the type antirusting paint under extreme temperature environment is more
It is good.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, although referring to aforementioned reality
Applying example, invention is explained in detail, for those skilled in the art, still can be to aforementioned each implementation
Technical solution documented by example is modified or equivalent replacement of some of the technical features.It is all in essence of the invention
Within mind and principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (10)
1. a kind of antirusting paint, which is characterized in that according to mass fraction, the component of the antirusting paint includes:Styrene-acrylic emulsion 80-
90 parts, 15-30 parts of pure-acrylic emulsion, 6-9 parts of composite tackifier, 3-7 parts of zinc magnesium alloy micro mist, 2-4 parts of iron oxide red, tripolyphosphate
2-3 parts of aluminium, 1-3 parts of base ether of polyethylene oxide polypropylene oxide monobutyl, 1.4-1.9 parts of anti-flash rusting agent, 15-20 parts of titanium dioxide, alcohol
12 0.3-0.8 parts of ester, 0.5-1.5 parts of preservative, 0.3-0.6 parts of defoaming agent, 1.2-1.5 parts of dispersing agent, 15-20 parts of water.
2. a kind of antirusting paint according to claim 1, it is characterised in that:According to mass fraction, the antirusting paint
Component includes:84-87 parts of styrene-acrylic emulsion, 18-22 parts of pure-acrylic emulsion, 7-8 parts of composite tackifier, 5-6 parts of zinc magnesium alloy micro mist, oxygen
Change iron oxide red 2.5-3.5 parts, 2.2-2.6 parts of aluminium triphosphate, 1.3-2.4 parts of base ether of polyethylene oxide polypropylene oxide monobutyl, prevents
1.5-1.8 parts of flash rusting agent, 17-19 parts of titanium dioxide, 12 0.4-0.6 parts of alcohol ester, 0.7-0.9 parts of preservative, defoaming agent 0.3-0.5
Part, 1.2-1.4 parts of dispersing agent, 16-18 parts of water.
3. a kind of antirusting paint according to claim 1, it is characterised in that:According to mass fraction, the antirusting paint
Component includes:86 parts of styrene-acrylic emulsion, 20 parts of pure-acrylic emulsion, 8 parts of composite tackifier, 5.5 parts of zinc magnesium alloy micro mist, iron oxide red 3
Part, 2.4 parts of aluminium triphosphate, 1.8 parts of ether of polyethylene oxide polypropylene oxide monobutyl base, 1.7 parts of anti-flash rusting agent, titanium dioxide 18
Part, 12 parts of alcohol ester, 0.8 part of preservative, 0.4 part of defoaming agent, 1.3 parts of dispersing agent, 17 parts of water.
4. a kind of antirusting paint according to claim 1, it is characterised in that:The preparation method of the composite tackifier includes
Following steps:
(1)According to mass fraction, the sodium hydroxide solution of 90 parts of 15wt% is added in reaction kettle, 50 parts of lignin are added
The uniform stirring into solution, and dispersion liquid is heated to 45-48 DEG C, then by 6.4 parts of hydroquinones and 3.6 parts of tert-butyl o benzene
Diphenol is added in reaction kettle, continues to be stirring evenly and then adding into 10 part 25% of formalin, the temperature in heating reaction kettle is extremely
65-70 DEG C, then 2.4 parts of tannic acids are added, after mixing evenly, it is the mixed of 180-200cp that material in reactor, which is cooked into viscosity,
Object A is closed, it is spare;
(2)100 parts of biological starch are added in 160 parts of deionized waters, are stirred evenly, then 2 parts is added into dispersion liquid and contains
There is the phosphate buffer of mesophilicα-diastase, the potency of the mesophilicα-diastase in buffer is 10000U/g, by dispersion liquid
Temperature is increased to 65-70 DEG C, keeps the temperature enzyme digestion reaction 2-3h then from hydrochloric acid is added into enzymolysis liquid and adjusts the pH value of enzymolysis liquid
To 4-4.3,30 parts of calcium gluconates and 7 parts of magnesium carbonate are added, adjust the pH value of dispersion liquid after being uniformly dispersed with sodium hydroxide
It for 5.3-5.5, will be filtered after dispersion liquid activated carbon adsorption, obtain filtrate, filtrate passes through 100-110 DEG C of spray drying treatment
After obtain micro mist B;
(3)200 parts of deionized waters are added into reaction kettle, is heated to 55-60 DEG C, 80 parts of micro mist B is then added to reaction kettle
In;By 6.8 parts of polyethylene glycol, 3.7 parts of diethylene glycol butyl ethers and 12.5 parts of alkenyl succinic anhydrides are added to 30 parts of isopropanol solvents
In sufficiently dissolve, during solution is added in reaction kettle, under nitrogen atmosphere protection, 40- is reacted with 95-100 DEG C of temperature
60min will filter after product activated carbon adsorption after reaction, micro mist C obtained after being then spray-dried filtrate;
(4)75 parts of micro mist C, 30 parts of mucopolysaccharides, 13 parts of propylene oxide and 4 parts of vinyl sulfonic acids are added in reaction kettle, then plus
Enter 500 parts of deionized waters, 8-10min is stirred with 30-35 DEG C of temperature, 25 parts of mixture A are added in reaction kettle, uniformly
Stirring is completely dispersed to mixture A, continues heating reaction 1.5-2h, finally by product with 100-105 DEG C of temperature drying and powder
It is broken, obtain required composite tackifier.
5. a kind of antirusting paint according to claim 4, it is characterised in that:The step(2)In biological starch select
One of tapioca, cornstarch, potato starch and glutinous rice starch.
6. a kind of antirusting paint according to claim 4, it is characterised in that:The step(4)In mucopolysaccharide select melon
That glue or xanthan gum.
7. a kind of antirusting paint according to claim 1, it is characterised in that:The average grain diameter of the zinc magnesium alloy micro mist is
0.5-5μm。
8. a kind of antirusting paint according to claim 1, it is characterised in that:Contain alkyl imidazoline in the anti-flash rusting agent
Amide, alkylbenzotriazole, sodium nitrite and disodium ethylene diamine tetraacetate, four content ratio are 4:1:3:3.
9. a kind of antirusting paint according to claim 1, it is characterised in that:The defoaming agent is polyoxyethylene polyoxy propyl alcohol
Amidogen ether, dimethyl silicone polymer or polyoxyethylene polyoxypropylene glycerin ether.
10. a kind of antirusting paint described in -9 any one according to claim 1, which is characterized in that the system of the antirusting paint
Preparation Method is:
According to mass fraction, styrene-acrylic emulsion and pure-acrylic emulsion are added in Scattered Kettle, are heated to 75-80 DEG C, insulated and stirred point
It dissipates uniformly, then composite tackifier is added to the water, is heated to 55-60 DEG C and stirs to get gelatinization slurry, gelatinization slurry is added
Enter into Scattered Kettle, continues to be stirred 8-10min with the revolving speed of 550-600r/min and multiple emulsion, then by tripolyphosphate
Aluminium, polyethylene oxide polypropylene oxide monobutyl base ether, zinc magnesium alloy micro mist and iron oxide red are added in Scattered Kettle, with 650-
The revolving speed decentralized processing 10-15min of 800r/min then sequentially adds dispersing agent, titanium dioxide, preservative, anti-flash rusting agent, defoaming
Agent and alcohol ester 12 will obtain material and are cooled to room temperature, sealed package obtains with identical revolving speed decentralized processing 25-30min
Required antirusting paint.