CN108864578A - A kind of CNC equipment corrosion-resistant nameplate and processing technology - Google Patents
A kind of CNC equipment corrosion-resistant nameplate and processing technology Download PDFInfo
- Publication number
- CN108864578A CN108864578A CN201810658096.9A CN201810658096A CN108864578A CN 108864578 A CN108864578 A CN 108864578A CN 201810658096 A CN201810658096 A CN 201810658096A CN 108864578 A CN108864578 A CN 108864578A
- Authority
- CN
- China
- Prior art keywords
- parts
- nameplate
- corrosion
- resistant
- cnc equipment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of corrosion-resistant nameplate of CNC equipment, the raw material including following parts by weight:20~40 parts of ethylene propylene diene rubber, 15~20 parts of polyethylene, 40~60 parts of steel, 12~18 parts of clay, 3~10 parts of titanium, 3~15 parts of chromium, 2~8 parts of nickel;The nameplate is mixed and made into alloy using steel, titanium, chromium and nickel, and corrosion resistance is strong, and ethylene propylene diene rubber, polyethylene and clay are added in alloy, can reinforce the insulating capacity of alloy, corrosion resistant insulation nameplate is finally made;The invention also provides a kind of CNC equipment processing technologys of corrosion-resistant nameplate, and above-mentioned raw materials are mixed and made into sheet alloy first, carry out performance detection to sheet alloy, and carry out being cut into workpiece to sheet alloy;Then program is selected to carry out carving milling to workpiece, carve characters and processing mounting holes in CNC equipment;Deburring finally is carried out to workpiece, zinc-plated and japanning obtains nameplate;Easy to operate, required material is simple and easy to get, and cost is relatively low, is worthy to be popularized.
Description
Technical field
The present invention relates to CNC equipment nameplate technical field, the corrosion-resistant nameplate of specially a kind of CNC equipment and processing work
Skill.
Background technique
It is a kind of call of Hong Kong over there that CNC, which is called and does computer gong, CNCCH or numerically-controlled machine tool in fact, is passed to continent later
Pearl River Delta is exactly CNC milling machine in fact, is " CNC machining center " with someone in wide, Jiangsu-zhejiang Shanghai Area one.General CNC equipment is usually
Refer to precision machinery processing, CNC lathe for machining, CNC processing milling machine, CNC processing boring and milling machine etc..
Numerically-controlled machine tool is the abbreviation of computer digital control machine tool (Computer numerical control), is a kind of
By the automated machine tool of process control.The control system, which can be handled logically, has control coding or other symbolic instructions regulation
Program, decoded by computer, to make machine tool action and process part, be processed into blank material by Tool in Cutting
Semi-finished product fabricated part etc..
Generally it is furnished with nameplate in CNC equipment, carving characters on the nameplate on distinct device is also different, convenient for equipment type
Number, the essential informations such as power are identified.But existing nameplate poor corrosion resistance, often equipment is also in normal use, and nameplate
What is be corroded already is smudgy, is unfavorable for identifying by essential information of the nameplate to equipment.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the existing defects, provide a kind of corrosion-resistant nameplate of CNC equipment and
Processing technology can effectively solve the problems in background technique.
To achieve the above object, the present invention provides the following technical solutions:A kind of corrosion-resistant nameplate of CNC equipment, including with
The raw material of lower parts by weight:20~40 parts of ethylene propylene diene rubber, 15~20 parts of polyethylene, 40~60 parts of steel, 12~18 parts of clay, titanium
3~10 parts, 3~15 parts of chromium, 2~8 parts of nickel.
As a preferred technical solution of the present invention, the corrosion-resistant nameplate of a kind of CNC equipment, including it is following heavy
Measure the raw material of part:25~35 parts of ethylene propylene diene rubber, 18 parts of polyethylene, 45~55 parts of steel, 14~16 parts of clay, 5~8 parts of titanium,
6~12 parts of chromium, 4~6 parts of nickel.
As a preferred technical solution of the present invention, the corrosion-resistant nameplate of a kind of CNC equipment, including it is following heavy
Measure the raw material of part:29~31 parts of ethylene propylene diene rubber, 16~18 parts of polyethylene, 48~50 parts of steel, 15 parts of clay, 5~7 parts of titanium,
8~10 parts of chromium, 4~6 parts of nickel.
As a preferred technical solution of the present invention, the corrosion-resistant nameplate of a kind of CNC equipment, including it is following heavy
Measure the raw material of part:30 parts of ethylene propylene diene rubber, 17 parts of polyethylene, 60 parts of steel, 15 parts of clay, 6 parts of titanium, 9 parts of chromium, 5 parts of nickel.
As a preferred technical solution of the present invention, the polyethylene can be waste plastic, and the steel can be steel scrap.
The invention also provides a kind of CNC equipment processing technologys of corrosion-resistant nameplate, include the following steps:
S1. ethylene propylene diene rubber, polyethylene, steel, clay, titanium, chromium and the nickel of preferred above-mentioned specific gravity;
S2. by ethylene propylene diene rubber, polyethylene, steel, titanium, chromium and the nickel melting mixing in step S1, clay is then added, finally
It is molded, die casting obtains alloy after being cooled and shaped, take out sheet alloy;
S3. deburring is carried out to sheet alloy obtained in step S2;
S4. sheet alloy obtained in step S3 is detected using associated assay devices;
S5. the size and dosage for making nameplate as needed, are selected the sheet alloy of suitable size, are existed using corresponding blanking die
Die cut goes out workpiece on sheet alloy;
S6. different programs is selected in CNC equipment according to the needs of nameplate text;
S7. carving milling is carried out to the resulting workpiece of step S5 using CNC equipment and carved characters, use the program selected in step S6
Carve corresponding text, and processing mounting holes;
S8. deburring again is carried out to the workpiece after imprinting;
S9. workpiece obtained in step S8 is electroplated, it is zinc-plated to workpiece surface;
S10. the workpiece to surface after zinc-plated carries out japanning, carries out filling out paint to figure, text and symbol, and nameplate is made.
As a preferred technical solution of the present invention, the raw material of different molten conditions is mixed in the step S2
When, it is mixed in such a way that the raw material that fusing point is high pours into low-melting raw material.
It mainly include material to the detection of sheet alloy in the step S4 as a preferred technical solution of the present invention
The detection such as ingredient, hardness and corrosion resistance.
As a preferred technical solution of the present invention, carrot-free method is to change in the step S3 and the step S8
Learn deburring, electrochemical deburring, ultrasonic wave deburring, giant injection deburring or magnetic force deburring.
Compared with prior art, the invention proposes a kind of corrosion-resistant nameplates of CNC equipment, mixed using steel, titanium, chromium and nickel
Alloy is made in conjunction, and corrosion resistance is strong, and ethylene propylene diene rubber, polyethylene and clay are added in alloy, can reinforce the insulation of alloy
Corrosion resistant insulation nameplate is finally made in ability;The invention also provides a kind of processing works of corrosion-resistant nameplate of CNC equipment
CNC equipment can be used to be processed for skill, and easy to operate, required material is simple and easy to get, and cost is relatively low, is worthy to be popularized.
Specific embodiment
Combined with specific embodiments below the present invention is made further to explain, it is clear that described embodiment is only this hair
Bright a part of the embodiment, instead of all the embodiments.Based on the embodiments of the present invention, those of ordinary skill in the art are not having
Every other embodiment obtained under the premise of creative work is made, shall fall within the protection scope of the present invention.
Embodiment one
The present invention provides a kind of CNC equipment corrosion-resistant nameplate, the raw material including following parts by weight:35 parts of ethylene propylene diene rubber,
18 parts of waste plastic, 50 parts of steel scrap, 15 parts of clay, 8 parts of titanium, 10 parts of chromium, 5 parts of nickel.
Its processing technology, includes the following steps:
S1. ethylene propylene diene rubber, polyethylene, steel, clay, titanium, chromium and the nickel of preferred above-mentioned specific gravity;
S2. when mixing, fusing point is high by ethylene propylene diene rubber, polyethylene, steel, titanium, chromium and the nickel melting mixing in step S1
Raw material pours into low-melting raw material, and clay is then added, is finally molded, and die casting obtains alloy after being cooled and shaped, and takes out and closes
Golden plate material;
S3. deburring is carried out to sheet alloy obtained in step S2 using ultrasonic wave deburring;
S4. using associated assay devices to the material composition of sheet alloy obtained in step S3, hardness and corrosion resistance etc. into
Row detection;
S5. the size and dosage for making nameplate as needed, are selected the sheet alloy of suitable size, are existed using corresponding blanking die
Die cut goes out workpiece on sheet alloy;
S6. different programs is selected in CNC equipment according to the needs of nameplate text;
S7. carving milling is carried out to the resulting workpiece of step S5 using CNC equipment and carved characters, use the program selected in step S6
Carve corresponding text, and processing mounting holes;
S8. deburring again is carried out to the workpiece after imprinting using ultrasonic wave deburring;
S9. workpiece obtained in step S8 is electroplated, it is zinc-plated to workpiece surface;
S10. the workpiece to surface after zinc-plated carries out japanning, carries out filling out paint to figure, text and symbol, and nameplate is made.
Embodiment two
The present invention provides a kind of CNC equipment corrosion-resistant nameplate, the raw material including following parts by weight:30 parts of ethylene propylene diene rubber,
17 parts of waste plastic, 49 parts of steel scrap, 15 parts of clay, 6 parts of titanium, 10 parts of chromium, 5 parts of nickel.
Its processing technology, includes the following steps:
S1. ethylene propylene diene rubber, polyethylene, steel, clay, titanium, chromium and the nickel of preferred above-mentioned specific gravity;
S2. when mixing, fusing point is high by ethylene propylene diene rubber, polyethylene, steel, titanium, chromium and the nickel melting mixing in step S1
Raw material pours into low-melting raw material, and clay is then added, is finally molded, and die casting obtains alloy after being cooled and shaped, and takes out and closes
Golden plate material;
S3. deburring is carried out to sheet alloy obtained in step S2 using ultrasonic wave deburring;
S4. using associated assay devices to the material composition of sheet alloy obtained in step S3, hardness and corrosion resistance etc. into
Row detection;
S5. the size and dosage for making nameplate as needed, are selected the sheet alloy of suitable size, are existed using corresponding blanking die
Die cut goes out workpiece on sheet alloy;
S6. different programs is selected in CNC equipment according to the needs of nameplate text;
S7. carving milling is carried out to the resulting workpiece of step S5 using CNC equipment and carved characters, use the program selected in step S6
Carve corresponding text, and processing mounting holes;
S8. deburring again is carried out to the workpiece after imprinting using ultrasonic wave deburring;
S9. workpiece obtained in step S8 is electroplated, it is zinc-plated to workpiece surface;
S10. the workpiece to surface after zinc-plated carries out japanning, carries out filling out paint to figure, text and symbol, and nameplate is made.
Embodiment three
The present invention provides a kind of CNC equipment corrosion-resistant nameplate, the raw material including following parts by weight:30 parts of ethylene propylene diene rubber,
17 parts of waste plastic, 60 parts of steel scrap, 15 parts of clay, 6 parts of titanium, 9 parts of chromium, 5 parts of nickel.
Its processing technology, includes the following steps:
S1. ethylene propylene diene rubber, polyethylene, steel, clay, titanium, chromium and the nickel of preferred above-mentioned specific gravity;
S2. when mixing, fusing point is high by ethylene propylene diene rubber, polyethylene, steel, titanium, chromium and the nickel melting mixing in step S1
Raw material pours into low-melting raw material, and clay is then added, is finally molded, and die casting obtains alloy after being cooled and shaped, and takes out and closes
Golden plate material;
S3. deburring is carried out to sheet alloy obtained in step S2 using ultrasonic wave deburring;
S4. using associated assay devices to the material composition of sheet alloy obtained in step S3, hardness and corrosion resistance etc. into
Row detection;
S5. the size and dosage for making nameplate as needed, are selected the sheet alloy of suitable size, are existed using corresponding blanking die
Die cut goes out workpiece on sheet alloy;
S6. different programs is selected in CNC equipment according to the needs of nameplate text;
S7. carving milling is carried out to the resulting workpiece of step S5 using CNC equipment and carved characters, use the program selected in step S6
Carve corresponding text, and processing mounting holes;
S8. deburring again is carried out to the workpiece after imprinting using ultrasonic wave deburring;
S9. workpiece obtained in step S8 is electroplated, it is zinc-plated to workpiece surface;
S10. the workpiece to surface after zinc-plated carries out japanning, carries out filling out paint to figure, text and symbol, and nameplate is made.
The invention proposes a kind of corrosion-resistant nameplates of CNC equipment, are mixed and made into alloy, corrosion resistant using steel, titanium, chromium and nickel
Corrosion is strong, and ethylene propylene diene rubber, polyethylene and clay are added in alloy, can reinforce the insulating capacity of alloy, finally be made resistance to
The insulation nameplate of corrosion;The invention also provides a kind of processing technologys of corrosion-resistant nameplate of CNC equipment, and CNC equipment can be used
It is processed, easy to operate, required material is simple and easy to get, and cost is relatively low, is worthy to be popularized.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (9)
1. a kind of corrosion-resistant nameplate of CNC equipment, which is characterized in that the raw material including following parts by weight:Ethylene propylene diene rubber 20
~40 parts, 15~20 parts of polyethylene, 40~60 parts of steel, 12~18 parts of clay, 3~10 parts of titanium, 3~15 parts of chromium, 2~8 parts of nickel.
2. a kind of corrosion-resistant nameplate of CNC equipment according to claim 1, which is characterized in that including following parts by weight
Raw material:25~35 parts of ethylene propylene diene rubber, 18 parts of polyethylene, 45~55 parts of steel, 14~16 parts of clay, 5~8 parts of titanium, chromium 6~12
Part, 4~6 parts of nickel.
3. a kind of corrosion-resistant nameplate of CNC equipment according to claim 1, which is characterized in that including following parts by weight
Raw material:29~31 parts of ethylene propylene diene rubber, 16~18 parts of polyethylene, 48~50 parts of steel, 15 parts of clay, 5~7 parts of titanium, chromium 8~10
Part, 4~6 parts of nickel.
4. a kind of corrosion-resistant nameplate of CNC equipment according to claim 1, which is characterized in that including following parts by weight
Raw material:30 parts of ethylene propylene diene rubber, 17 parts of polyethylene, 60 parts of steel, 15 parts of clay, 6 parts of titanium, 9 parts of chromium, 5 parts of nickel.
5. a kind of corrosion-resistant nameplate of CNC equipment according to claim 1, which is characterized in that the polyethylene can be useless
Old plastics, the steel can be steel scrap.
6. a kind of processing technology of the corrosion-resistant nameplate of CNC equipment, it is characterised in that:Include the following steps:
S1. ethylene propylene diene rubber, polyethylene, steel, clay, titanium, chromium and the nickel of preferred above-mentioned specific gravity;
S2. by ethylene propylene diene rubber, polyethylene, steel, titanium, chromium and the nickel melting mixing in step S1, clay is then added, finally
It is molded, die casting obtains alloy after being cooled and shaped, take out sheet alloy;
S3. deburring is carried out to sheet alloy obtained in step S2;
S4. sheet alloy obtained in step S3 is detected using associated assay devices;
S5. the size and dosage for making nameplate as needed, are selected the sheet alloy of suitable size, are existed using corresponding blanking die
Die cut goes out workpiece on sheet alloy;
S6. different programs is selected in CNC equipment according to the needs of nameplate text;
S7. carving milling is carried out to the resulting workpiece of step S5 using CNC equipment and carved characters, use the program selected in step S6
Carve corresponding text, and processing mounting holes;
S8. deburring again is carried out to the workpiece after imprinting;
S9. workpiece obtained in step S8 is electroplated, it is zinc-plated to workpiece surface;
S10. the workpiece to surface after zinc-plated carries out japanning, carries out filling out paint to figure, text and symbol, and nameplate is made.
7. a kind of processing technology of corrosion-resistant nameplate of CNC equipment according to claim 6, which is characterized in that the step
When being mixed the raw material of different molten conditions in rapid S2, using the high raw material of fusing point to be poured into the side in low-melting raw material
Formula mixing.
8. a kind of processing technology of corrosion-resistant nameplate of CNC equipment according to claim 6, which is characterized in that the step
It mainly include the detection such as material composition, hardness and corrosion resistance to the detection of sheet alloy in rapid S4.
9. a kind of processing technology of corrosion-resistant nameplate of CNC equipment according to claim 6, which is characterized in that the step
Carrot-free method is chemical deburring, electrochemical deburring, ultrasonic wave deburring, giant spray in the rapid S3 and step S8
Shoot burr or magnetic force deburring.