CN108863141A - A kind of concrete production gelling agent and its production method - Google Patents
A kind of concrete production gelling agent and its production method Download PDFInfo
- Publication number
- CN108863141A CN108863141A CN201810727964.4A CN201810727964A CN108863141A CN 108863141 A CN108863141 A CN 108863141A CN 201810727964 A CN201810727964 A CN 201810727964A CN 108863141 A CN108863141 A CN 108863141A
- Authority
- CN
- China
- Prior art keywords
- parts
- gelling agent
- kilograms
- concrete production
- sulfate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of concrete production gelling agent and its production methods, the concrete production gelling agent includes ammonium sulfate, sodium sulphate, potassium sulfate, ferrous sulfate, magnesium chloride, ammonium chloride, calcium gluconate, stabilizer, modifier and water, and the concrete production gelling agent includes according to parts by weight：30-50 parts of ammonium sulfate, 20-40 parts of sodium sulphate, 2-10 parts of potassium sulfate, 40-50 parts of ferrous sulfate, 35-55 parts of magnesium chloride, 18-28 parts of ammonium chloride, 4-8 parts of calcium gluconate, 1-5 parts of stabilizer, 6-12 parts of modifier and 90-120 parts of water；Concrete production gelling agent of the present invention and its production method have good water conservation water penetration, and related preparation method is simple, the period is short, at low cost, are suitable for industrialized production.
Description
Technical field
The present invention relates to a kind of concrete production gelling agent and its production methods, belong to building material technical field.
Background technique
Pervious concrete is a kind of construction material as made of aggregate, cement minerals admixture, water, additive mix, should
Before the research application in field starts from more than 100 years.Pervious concrete can allow rainwater to flow into underground, and effective recharge of groundwater is alleviated
Urban Underground water level such as sharply declines at some Urban Environmental Problems, is maintaining ecological balance, alleviates the excellent of urban heat land effect
Pavement material is the optimal material for building " sponge city ".However, due to the limitation of various conditions, at present to pervious concrete
Research and extension be also greatly improved space.
The quality of the performance of concrete gelling agent directly influences the property on the permeable road of subsequent water-permeable and water retention brick and laying
Can, therefore a kind of concrete gelling agent of superior performance is needed in the market.
Summary of the invention
The purpose of the present invention is in view of the deficienciess of the prior art, providing that a kind of water permeability is good, intensity is high, cost
The concrete production gelling agent low, non-toxic, anti-aging property is good.
To achieve the above object, the present invention provides a kind of concrete production gelling agent, including ammonium sulfate, sodium sulphate,
Potassium sulfate, ferrous sulfate, magnesium chloride, ammonium chloride, calcium gluconate, stabilizer, modifier and water, the concrete production are used
Gelling agent includes according to parts by weight：30-50 parts of ammonium sulfate, 20-40 parts of sodium sulphate, 2-10 parts of potassium sulfate, ferrous sulfate 40-50
Part, 35-55 parts of magnesium chloride, 18-28 parts of ammonium chloride, 4-8 parts of calcium gluconate, 1-5 parts of stabilizer, 6-12 parts of modifier and water
90-120 parts.
As a further improvement of the foregoing solution, the concrete production is comprised the following components in parts by weight with gelling agent：
30 parts of ammonium sulfate, 20 parts of sodium sulphate, 2 parts of potassium sulfate, 40 parts of ferrous sulfate, 35 parts of magnesium chloride, 18 parts of ammonium chloride, calcium gluconate
4 parts, 1 part of stabilizer, 6 parts of modifier and 100 parts of water.
As a further improvement of the foregoing solution, the modifier is double focusing amine salt, sulfonated lignite, polymer filtrate reducing
One of agent is a variety of.
The present invention proposes a kind of production method of concrete production gelling agent, includes the following steps：S1,30 kilograms are weighed
Ammonium sulfate, 20 kilograms of sodium sulphate, 40 kilograms of ferrous sulfate, 35 kilograms of magnesium chloride, 18 kilograms of ammonium chloride, 2 kilograms
Potassium sulfate and 4 kilograms of calcium gluconate be successively dissolved in 100 kilograms of water；S2, the mixed solution for obtaining S1 carry out
It is sufficiently stirred while carrying out being heated to required temperature sufficiently being dissolved；S3,1 kilogram is then added into solution obtained in S2
Stabilizer, control temperature at 80 DEG C hereinafter, being stirred 20 minutes；S4, the modifier for being eventually adding 6 kilograms, stirring 18 are small
When after obtain the concrete production gelling agent.
As a further improvement of the foregoing solution, the median granularity of quality of concrete production gelling agent is 600-
1600 microns.
As a further improvement of the foregoing solution, the mixing time in the S2 is 50 minutes, and required temperature is controlled 55
℃-60℃。
As a further improvement of the foregoing solution, every in the step S1 to add after a kind of raw material then stirs 10-15 minutes
A kind of raw material is added down again.
Beneficial effects of the present invention are：This concrete production gelling agent and its production method cementation are strong, apply
Range is wide, and concrete production is added in concrete with gelling agent and carries out road pavement, and road surface water-permeable and water retention performance is good, and road
The pressure-proof and snap-resistent intensity in face is big, wearability, frost resistance are all improved；
Concrete production gelling agent has a good water conservation water penetration, and related preparation method it is simple,
Period is short, at low cost, is suitable for industrialized production.
Specific embodiment
In order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below in conjunction with implementation of the invention
Example, is clearly and completely described the technical solution of the embodiment of the present invention.Obviously, described embodiment is of the invention
A part of the embodiment, instead of all the embodiments.Based on described the embodiment of the present invention, those of ordinary skill in the art
Every other embodiment obtained, shall fall within the protection scope of the present invention.
It is effectively improved under the premise of there is guarantee road items physical index An embodiment provides one kind
The water-permeable and water retention of concrete improves the compression strength of cement, the concrete production gelling agent of wearability.
A kind of concrete production gelling agent provided in an embodiment of the present invention, including ammonium sulfate, sodium sulphate, potassium sulfate, sulphur
Sour ferrous iron, magnesium chloride, ammonium chloride, calcium gluconate, stabilizer, modifier and water, the concrete production are pressed with gelling agent
Include according to parts by weight：30-50 parts of ammonium sulfate, 20-40 parts of sodium sulphate, 2-10 parts of potassium sulfate, 40-50 parts of ferrous sulfate, magnesium chloride
35-55 parts, 18-28 parts of ammonium chloride, 4-8 parts of calcium gluconate, 1-5 parts of stabilizer, 6-12 parts of modifier and 90-120 parts of water.
Further, the modifier is one of double focusing amine salt, sulfonated lignite, polymer filtrate reducer or more
Kind.
Embodiment 1
A kind of production method of concrete production gelling agent, includes the following steps：100 kilograms are added in agitating device
Water, then weigh 30 kilograms of ammonium sulfate, 20 kilograms of sodium sulphate, 40 kilograms of ferrous sulfate, 35 kilograms of magnesium chloride, 18
Kilogram ammonium chloride, 2 kilograms of potassium sulfate and 4 kilograms of calcium gluconate and divide according to the sequence interval of above-mentioned weighing 30
Clock is added sequentially in agitating device, it is every a kind of raw material is added after, then need stirring that a kind of original can at least be added down after ten minutes
Material；Then agitating device is heated, so that solution-stabilized in agitating device is stirred again at 65 DEG C or so, is stirred
Mixing the time is 20 minutes or so, until raw material is completely dissolved in water；Then 1 kilogram of stabilizer, control are added in mixed solution
Temperature processed is at 80 DEG C hereinafter, being stirred 20 minutes；It is eventually adding 6 kilograms of modifier, stirring obtains in quality after 18 hours
The concrete production gelling agent that value granularity is 600-1600 microns.
Embodiment 2
A kind of production method of concrete production gelling agent, includes the following steps：115 kilograms are added in agitating device
Water, then weigh 40 kilograms of ammonium sulfate, 30 kilograms of sodium sulphate, 45 kilograms of ferrous sulfate, 45 kilograms of magnesium chloride, 24
Kilogram ammonium chloride, 6 kilograms of potassium sulfate and 6 kilograms of calcium gluconate and divide according to the sequence interval of above-mentioned weighing 30
Clock is added sequentially in agitating device, it is every a kind of raw material is added after, then a kind of original can be added down after needing stirring at least 15 minutes
Material；Then agitating device is heated, so that solution-stabilized in agitating device is stirred again at 65 DEG C or so, is stirred
Mixing the time is 25 minutes or so, until raw material is completely dissolved in water；Then 3 kilograms of stabilizer, control are added in mixed solution
Temperature processed is at 80 DEG C hereinafter, being stirred 25 minutes；It is eventually adding 9 kilograms of modifier, stirring obtains in quality after 22 hours
The concrete production gelling agent that value granularity is 600-1600 microns.
Embodiment 3
A kind of production method of concrete production gelling agent, includes the following steps：120 kg is added in agitating device
Water, then weigh 50 kilograms of ammonium sulfate, 40 kilograms of sodium sulphate, 50 kilograms of ferrous sulfate, 55 kilograms of magnesium chloride, 28
Kilogram ammonium chloride, 10 kilograms of potassium sulfate and 8 kilograms of calcium gluconate and according to the sequence interval of above-mentioned weighing 30
Minute be added sequentially in agitating device, it is every a kind of raw material is added after, then need stirring that lower one kind can at least be added after twenty minutes
Raw material；Then agitating device is heated, so that solution-stabilized in agitating device is stirred again at 65 DEG C or so,
Mixing time is 30 minutes or so, until raw material is completely dissolved in water；Then 5 kilograms of stabilizer is added in mixed solution,
Temperature is controlled at 80 DEG C hereinafter, being stirred 25 minutes；It is eventually adding 12 kilograms of modifier, stirring obtained quality after 24 hours
The concrete production gelling agent that median particle is 600-1600 microns.
To sum up, a kind of concrete production gelling agent according to above embodiments and its production method bonding are made
With it is strong, have a wide range of application, concrete production is added in concrete with gelling agent and carries out road pavement, road surface water-permeable and water retention
Can be good, and the pressure-proof and snap-resistent intensity on road surface is big, wearability, frost resistance are all improved；
Concrete production gelling agent has a good water conservation water penetration, and related preparation method it is simple,
Period is short, at low cost, is suitable for industrialized production.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims
Variation is included within the present invention.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (7)
1. a kind of concrete production gelling agent, including ammonium sulfate, sodium sulphate, potassium sulfate, ferrous sulfate, magnesium chloride, ammonium chloride,
Calcium gluconate, stabilizer, modifier and water, it is characterised in that：The concrete production gelling agent is according to parts by weight packet
It includes：30-50 parts of ammonium sulfate, 20-40 parts of sodium sulphate, 2-10 parts of potassium sulfate, 40-50 parts of ferrous sulfate, 35-55 parts of magnesium chloride, chlorine
Ammonium 18-28 parts of change, 4-8 parts of calcium gluconate, 1-5 parts of stabilizer, 6-12 parts of modifier and 90-120 parts of water.
2. a kind of concrete production gelling agent according to claim 1, it is characterised in that：The concrete production glue
Solidifying agent comprises the following components in parts by weight：30 parts of ammonium sulfate, 20 parts of sodium sulphate, 2 parts of potassium sulfate, 40 parts of ferrous sulfate, magnesium chloride
35 parts, 18 parts of ammonium chloride, 4 parts of calcium gluconate, 1 part of stabilizer, 6 parts of modifier and 100 parts of water.
3. a kind of concrete production gelling agent according to claim 1, it is characterised in that：The modifier is double focusing
One of amine salt, sulfonated lignite, polymer filtrate reducer are a variety of.
4. a kind of production method of concrete production gelling agent according to claim 1 to 3, includes the following steps：
S1, the ammonium sulfate for weighing 30 kilograms, 20 kilograms of sodium sulphate, 40 kilograms of ferrous sulfate, 35 kilograms of magnesium chloride, 18 public affairs
Ammonium chloride, 2 kilograms of potassium sulfate and 4 kilograms of the calcium gluconate of jin are successively dissolved in 100 kilograms of water；
S2, the mixed solution that S1 is obtained be sufficiently stirred while carrying out being heated to required temperature sufficiently being dissolved；
S3, the stabilizer that 1 kilogram is then added into solution obtained in S2, control temperature at 80 DEG C hereinafter, being stirred 20
Minute；
S4, the modifier for being eventually adding 6 kilograms, stirring obtained the concrete production gelling agent after 18 hours.
5. a kind of production method of concrete production gelling agent according to claim 4, it is characterised in that：The coagulation
The median granularity of quality of autochthonal production gelling agent is 600-1600 microns.
6. a kind of production method of concrete production gelling agent according to claim 4, it is characterised in that：In the S2
Mixing time be 50 minutes, required temperature control at 55 DEG C -60 DEG C.
7. a kind of production method of concrete production gelling agent according to claim 4, it is characterised in that：The step
Every add after a kind of raw material then stirs 10-15 minutes adds down a kind of raw material again in S1.