CN108859297A - A kind of fire-retardant sportswear fabric - Google Patents
A kind of fire-retardant sportswear fabric Download PDFInfo
- Publication number
- CN108859297A CN108859297A CN201811001389.6A CN201811001389A CN108859297A CN 108859297 A CN108859297 A CN 108859297A CN 201811001389 A CN201811001389 A CN 201811001389A CN 108859297 A CN108859297 A CN 108859297A
- Authority
- CN
- China
- Prior art keywords
- moisture absorption
- wearing layer
- weight
- parts
- absorption layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of fire-retardant sportswear fabric, including wearing layer and moisture absorption layer, and the wearing layer is pasted onto the upper side of moisture absorption layer, and compared with prior art, the present invention has following beneficial effect：Wear-resisting and anti-ultraviolet function is realized, while also improving the effect of moisture absorption and hydrofuge, improves comforts of use, and it is smelly to have the function of that antibacterial presses down, and improves safety in utilization.
Description
Technical field
The present invention is a kind of fire-retardant sportswear fabric, belongs to fabric preparation technical field.
Background technique
Sportswear fabric generally refers to the fabric of clothes when movement, and such fabric is in fact with the in the majority of terylene.Firstly the need of
Function be rapid-curing cutback because needing largely to perspire during exercise, wear the really very absorbing sweat of the clothes of pure cotton, but sweat is all inhaled in clothing
On clothes, clothes is got wet, and is difficult evaporated.And many sportswear fabrics, such as the CLIMAFIT of ADIDAS and NIKE
There are also the ATDRY of Li Ning by DRIFIT, are all the materials for having spent many funds to find out, and are all 100% terylene, such face
Material can be such that you has gone out after sweat, rapidly sweat evaporation, so you do not feel as the sense of heaviness of any clothes, will not paste
With, it may be said that be the dressing first choice of vigorous exercise.
However existing sportswear fabric does not have fire-retardant function, and abrasion resistant effect is poor, and is not easy to ultraviolet light
Stopped, while also reducing moisture absorption, therefore, urgent need wants a kind of fire-retardant sportswear fabric to solve above-mentioned steps.
Summary of the invention
In view of the deficienciess of the prior art, it is an object of the present invention to provide a kind of fire-retardant sportswear fabric, to solve above-mentioned back
The problem of being proposed in scape technology.
To achieve the goals above, the present invention is to realize by the following technical solutions：A kind of fire-retardant sportswear fabric, packet
Wearing layer and moisture absorption layer are included, the wearing layer is pasted onto the upper side of moisture absorption layer, including following preparation process：
Firstly, the terylene of the selection bamboo charcoal fiber of 30-60 parts by weight, the Fypro of 40-70 parts by weight, 25-45 parts by weight
The viscose rayon of fiber and 55-75 parts by weight；
Then, bamboo charcoal fiber and Fypro are put into antimicrobial solvent and are impregnated, soaking time 15-30min,
It then takes out, and bamboo charcoal fiber as warp and is referred on the textile machine, then using Fypro as weft, and be connected to
On weft insertion device, to prepare wearing layer, then arranged using polyester fiber as warp on the textile machine, then with viscose rayon
It is connected to weft insertion device as weft, to prepare moisture absorption layer；
Then, wearing layer and moisture absorption layer are carried out registration process by user of service, and bonding is applied between wearing layer and moisture absorption layer
Agent, then wearing layer and moisture absorption layer are put into press device and carry out pressing molding by user of service, pressing time 20-
25min；
Subsequently, user of service takes out wearing layer and moisture absorption layer inside press device, and is put into the defeated of fabric roller
It send in equipment, and arranges fire retardant spray pipe on fabric roller, and realize that fire retardant spray pipe is directed at wearing layer, then wearing layer
And moisture absorption layer is conveyed on conveying equipment, then fabric roller is to drive fire retardant spray pipe to rotate, then fire retardant
Spray pipe is by the upper surface of fire retardant even application to wearing layer；
Finally, by after spraying wearing layer and moisture absorption layer removed from conveying equipment, and be placed on drying frame and carry out
Sunning processing, sunning time are 10-15h.
Further, the bamboo charcoal fiber for choosing 40 parts by weight chooses the Fypro of 60 parts by weight as warp
As weft, so that wearing layer be made, this wearing layer anti-uv-ray is strong；The bamboo charcoal fiber of 60 parts by weight is chosen as warp
Line chooses the Fypro of 40 parts by weight as weft, so that wearing layer be made, this wearing layer wear-resistant strength is high.
Further, the polyester fiber for choosing 25 parts by weight as warp, make by the viscose rayon for choosing 75 parts by weight
For weft, so that moisture absorption layer be made, this moisture absorption layer moisture absorption is high；The polyester fiber of 45 parts by weight is chosen as warp, is chosen
The viscose rayon of 55 parts by weight is as weft, so that moisture absorption layer be made, this moisture absorption layer is easily dry, easy cleaning, and elasticity is high.
Further, the antimicrobial solvent is a kind of silver ion antimicrobial agent.
Further, described adhesive is a kind of polyurethane hot melt of moisturecuring.
Further, the fire retardant is a kind of Fire Retardant of The Expoxy Resin.
Beneficial effects of the present invention：A kind of fire-retardant sportswear fabric of the invention, the present invention pass through addition wearing layer and suction
The design of wet layer realizes wear-resisting and anti-ultraviolet function, while also improving the effect of moisture absorption and hydrofuge, improves
Comforts of use, and it is smelly to have the function of that antibacterial presses down, and improves safety in utilization.
Detailed description of the invention
Upon reading the detailed description of non-limiting embodiments with reference to the following drawings, other feature of the invention,
Objects and advantages will become more apparent upon：
Fig. 1 is a kind of structural schematic diagram of fire-retardant sportswear fabric of the present invention；
In figure：1- wearing layer, 2- moisture absorption layer.
Specific embodiment
To be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, below with reference to
Specific embodiment, the present invention is further explained.
Referring to Fig. 1, the present invention provides a kind of technical solution：A kind of fire-retardant sportswear fabric, including wearing layer 1 and moisture absorption
Layer 2, wearing layer 1 is pasted onto the upper side of moisture absorption layer 2, including following preparation process：
Firstly, the terylene of the selection bamboo charcoal fiber of 30-60 parts by weight, the Fypro of 40-70 parts by weight, 25-45 parts by weight
The viscose rayon of fiber and 55-75 parts by weight；
Then, bamboo charcoal fiber and Fypro are put into antimicrobial solvent and are impregnated, soaking time 15-30min,
It then takes out, and bamboo charcoal fiber as warp and is referred on the textile machine, then using Fypro as weft, and be connected to
On weft insertion device, to prepare wearing layer 1, then using polyester fiber as warp, arrangement is on the textile machine, then fine with viscose glue
Dimension is connected to weft insertion device as weft, to prepare moisture absorption layer 2；
Then, wearing layer 1 and moisture absorption layer 2 are carried out registration process by user of service, and are applied between wearing layer 1 and moisture absorption layer 2
Adhesive, then wearing layer 1 and moisture absorption layer 2 are put into press device and carry out pressing molding by user of service, the pressing time
For 20-25min；
Subsequently, user of service takes out wearing layer 1 and moisture absorption layer 2 inside press device, and is put into fabric roller
On conveying equipment, and fire retardant spray pipe is arranged on fabric roller, and realize that fire retardant spray pipe is directed at wearing layer 1, it is then resistance to
Mill layer 1 and moisture absorption layer 2 are conveyed on conveying equipment, and then fabric roller is to drive fire retardant spray pipe to rotate, then
Fire retardant spray pipe is by fire retardant even application to the upper surface of wearing layer 1；
Finally, by after spraying wearing layer 1 and moisture absorption layer 2 removed from conveying equipment, and it is enterprising to be placed on drying frame
Row sunning processing, sunning time are 10-15h.
As an embodiment of the present invention：The bamboo charcoal fiber of 40 parts by weight is chosen as warp, chooses 60 parts by weight
Fypro is as weft, so that wearing layer 1 be made, this 1 anti-uv-ray of wearing layer is strong；Choose the bamboo charcoal of 60 parts by weight
Fiber chooses the Fypro of 40 parts by weight as weft as warp, so that wearing layer 1 be made, this wearing layer 1 is wear-resisting strong
Degree is high.
As an embodiment of the present invention：The polyester fiber of 25 parts by weight is chosen as warp, chooses 75 parts by weight
Viscose rayon is as weft, so that moisture absorption layer 2 be made, this 2 moisture absorption of moisture absorption layer is high；The polyester fiber for choosing 45 parts by weight is made
For warp, the viscose rayon of 55 parts by weight is chosen as weft, so that moisture absorption layer 2 be made, this moisture absorption layer 2 is easily dry, easy cleaning, bullet
Property it is high.
As an embodiment of the present invention：Antimicrobial solvent is a kind of silver ion antimicrobial agent.
As an embodiment of the present invention：Adhesive is a kind of polyurethane hot melt of moisturecuring.
As an embodiment of the present invention：Fire retardant is a kind of Fire Retardant of The Expoxy Resin.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention, for this field skill
For art personnel, it is clear that invention is not limited to the details of the above exemplary embodiments, and without departing substantially from spirit of the invention or
In the case where essential characteristic, the present invention can be realized in other specific forms.Therefore, in all respects, should all incite somebody to action
Embodiment regards exemplary as, and is non-limiting, the scope of the present invention by appended claims rather than on state
Bright restriction, it is intended that including all changes that fall within the meaning and scope of the equivalent elements of the claims in the present invention
It is interior.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (6)
1. a kind of fire-retardant sportswear fabric, including wearing layer and moisture absorption layer, the wearing layer are pasted onto the upper side of moisture absorption layer,
It is characterized in that：Including following preparation process：
Firstly, the terylene of the selection bamboo charcoal fiber of 30-60 parts by weight, the Fypro of 40-70 parts by weight, 25-45 parts by weight
The viscose rayon of fiber and 55-75 parts by weight；
Then, bamboo charcoal fiber and Fypro are put into antimicrobial solvent and are impregnated, soaking time 15-30min,
It then takes out, and bamboo charcoal fiber as warp and is referred on the textile machine, then using Fypro as weft, and be connected to
On weft insertion device, to prepare wearing layer, then arranged using polyester fiber as warp on the textile machine, then with viscose rayon
It is connected to weft insertion device as weft, to prepare moisture absorption layer；
Then, wearing layer and moisture absorption layer are carried out registration process by user of service, and bonding is applied between wearing layer and moisture absorption layer
Agent, then wearing layer and moisture absorption layer are put into press device and carry out pressing molding by user of service, pressing time 20-
25min；
Subsequently, user of service takes out wearing layer and moisture absorption layer inside press device, and is put into the defeated of fabric roller
It send in equipment, and arranges fire retardant spray pipe on fabric roller, and realize that fire retardant spray pipe is directed at wearing layer, then wearing layer
And moisture absorption layer is conveyed on conveying equipment, then fabric roller is to drive fire retardant spray pipe to rotate, then fire retardant
Spray pipe is by the upper surface of fire retardant even application to wearing layer；
Finally, by after spraying wearing layer and moisture absorption layer removed from conveying equipment, and be placed on drying frame and carry out
Sunning processing, sunning time are 10-15h.
2. a kind of fire-retardant sportswear fabric according to claim 1, it is characterised in that：The bamboo charcoal for choosing 40 parts by weight is fine
Dimension is used as warp, chooses the Fypro of 60 parts by weight as weft, so that wearing layer, this wearing layer uvioresistant energy be made
Power is strong；The bamboo charcoal fiber of 60 parts by weight is chosen as warp, the Fypro of 40 parts by weight is chosen as weft, to be made
Wearing layer, this wearing layer wear-resistant strength are high.
3. a kind of fire-retardant sportswear fabric according to claim 1, it is characterised in that：The terylene for choosing 25 parts by weight is fine
Dimension is used as warp, chooses the viscose rayon of 75 parts by weight as weft, so that moisture absorption layer be made, this moisture absorption layer moisture absorption is high；
The polyester fiber of 45 parts by weight is chosen as warp, chooses the viscose rayon of 55 parts by weight as weft, so that moisture absorption layer is made,
This moisture absorption layer is easily dry, easy cleaning, and elasticity is high.
4. a kind of fire-retardant sportswear fabric according to claim 1, it is characterised in that：The antimicrobial solvent is a kind of silver ion
Antibacterial agent.
5. a kind of fire-retardant sportswear fabric according to claim 1, it is characterised in that：Described adhesive is a kind of moisturecuring
Polyurethane hot melt.
6. a kind of fire-retardant sportswear fabric according to claim 1, it is characterised in that：The fire retardant is a kind of epoxy resin
Fire retardant.