CN108840633A - One kind is exempted to paint ecological block brick and its production technology - Google Patents
One kind is exempted to paint ecological block brick and its production technology Download PDFInfo
- Publication number
- CN108840633A CN108840633A CN201810956595.6A CN201810956595A CN108840633A CN 108840633 A CN108840633 A CN 108840633A CN 201810956595 A CN201810956595 A CN 201810956595A CN 108840633 A CN108840633 A CN 108840633A
- Authority
- CN
- China
- Prior art keywords
- block brick
- mine
- brick
- portland cement
- building block
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Exempt to paint ecological block brick the invention discloses one kind, the raw material of above-mentioned building block brick includes no mud river sand, steel Copper Slag, mine tailings, mine tailing, lime stone, portland cement, retarder sodium tripolyphosphate, water-reducing agent by weighing, stirring, mixing, being layered precompressed, blowing the processes such as slag, maintenance and formed, fast, the good feature of load with molding.
Description
Technical field
The present invention relates to house building materials, and in particular to one kind is exempted to paint ecological block brick and its production technology.
Background technique
Building block brick is mainly used for the exterior wall filling of building, interior wall partition, and building block brick has light-weight, good heat insulating
Advantage, however the molding of existing building block brick is poor, has a large amount of gaps that need to additionally paint after the completion of construction, causes engineering time-consuming more, work
People, existing building block brick load is poor, commonly used in household building block brick there is also can not carry white goods the case where.
Summary of the invention
Exempt to paint ecological block brick and its production technology the purpose of the present invention is to provide one kind, existing block is solved with expectation
The molding of block brick is poor, there is the problem of a large amount of gaps need to additionally be painted after the completion of construction.
In order to solve the above technical problems, the present invention uses following technical scheme：One kind is exempted to paint ecological block brick, above-mentioned
The raw material of building block brick includes no mud river sand, steel Copper Slag, mine tailings, mine tailing, lime stone, portland cement, retarder three
Polyphosphate sodium, water-reducing agent.
Preferably, above-mentioned building block brick raw material accounting is no mud river sand 30-40%, steel Copper Slag 20-30%, mine tailings 5-
10%, mine tailing 10-15%, lime stone 5-10%, portland cement 10-20%, retarder sodium tripolyphosphate 1-5%, water-reducing agent 1-
5%。
Preferably, above-mentioned building block brick raw material accounting is no mud river sand 40%, steel Copper Slag 20%, mine tailings 5%, tailing
Powder 10%, portland cement 15%, lime stone 5%, retarder sodium tripolyphosphate 3%, water-reducing agent 2%.
The present invention is also possible that the production technology for exempting to paint ecological block brick, includes the following steps：
S1 will be weighed without mud river sand, steel Copper Slag, mine tailings, mine tailing by electronic scale；
S2 will proportionally be stirred to form aggregate without mud river sand, steel Copper Slag, mine tailings, mine tailing；
The above-mentioned aggregate of S3 is proportionally gradually mixed into lime stone, portland cement and is gradually added into retarder sodium tripolyphosphate, subtracts
Aqua is stirred to obtain mixed soil, and the moisture content of above-mentioned portland cement is 40-50%, stands obtain surface after mixing evenly
Material；
Facing material is put into mold by S4, and is carried out layering precompressed by molding machine and formed brick；
S5 carries out brick to obtain finished product after blowing slag；
The above-mentioned finished product of S6 is transported in curing kilns by conveyer belt, is carried out consolidation by curing kilns and is formed building block brick；
The above-mentioned building block brick of S7 is transported to palletizing system progress stacking by transporting band, is packaged.
Further, the pre- swaging of above-mentioned layering is successively to press, and 5 millimeters of surface thickness, groundwork thickness is 50-70 milli
Rice, porosity 15%.
Further, above-mentioned molding machine is the molding machine with vibration moulding platform, is made in mold more by vibration moulding platform
Fast is covered with material.
Compared with prior art, the beneficial effects of the invention are as follows：Guarantee base's mechanical property by steel Copper Slag, improves
Building block brick bearing capacity meets household carry white goods requirement, fits closely guarantee building block brick by mine tailings, mine tailing
It is molding uniformly to reach primary construction and exempt to paint, reduce cost of human resources, promotion economic benefit.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not used to
Limit the present invention.
Implement 1：
One kind is exempted to paint ecological block brick, and the raw material of above-mentioned building block brick includes no mud river sand, steel Copper Slag, mine tailings, tailing
Powder, lime stone, portland cement, retarder sodium tripolyphosphate, water-reducing agent, by will be without mud river sand, steel Copper Slag, tailing
Slag, mine tailing, portland cement, lime stone have low-cost benefit as raw material, by mine tailing fill mine tailings it
Between larger gap, make its even particle distribution when being used in conjunction with, by steel Copper Slag guarantee base's mechanical property,
Building block brick bearing capacity is improved, viscosity is improved by cement, and then can achieve the effect that once to construct and exempt from painting.
Embodiment 2：
The present invention provides painting ecological block brick is exempted from, raw material accounting is no mud river sand 40%, steel Copper Slag 20%, mine tailings
10%, mine tailings 5%, mine tailing 10%, portland cement 15%, lime stone 5%, retarder sodium tripolyphosphate 3%, water-reducing agent 2%；On
The production technology for exempting to paint ecological block brick is stated, is included the following steps：S1 will be without mud river sand, steel Copper Slag, mine tailings, tailing
Powder is weighed by electronic scale, and S2 will proportionally be stirred shape without mud river sand, steel Copper Slag, mine tailings, mine tailing
At aggregate；The above-mentioned aggregate of S3 be proportionally gradually mixed into lime stone, portland cement and be gradually added into retarder sodium tripolyphosphate,
Water-reducing agent is stirred to obtain mixed soil, and the moisture content of above-mentioned portland cement is 40-50%, stands obtain table after mixing evenly
Plane materiel material；Facing material is put into mold by S4, and is carried out layering precompressed by molding machine and formed brick；S5 carries out brick to blow slag
After obtain finished product；The above-mentioned finished product of S6 is transported in curing kilns by conveyer belt, is carried out consolidation by curing kilns and is formed building block brick, S7
Above-mentioned building block brick is transported to palletizing system progress stacking by transporting band, is packaged；Its weighing is claimed by projection electronic weighing, and stirring passes through
Blender weighs and is placed in blender top, and raw material automatically engages progress aggregate stirring in blender, stirring after weighing
Cement is put into after 0.5 to 2 small times, cement and aggregate makes the moisture content 40-50% of cement in Jia Shui after mixing evenly,
Data are obtained by hygrothermograph, convenient for addition water；When blender carries out blowing after mixing evenly, pass through mixing belt conveyer
It will be delivered in the hopper of molding machine, product, which can according to need, is added different pigment, readily available different color.
Embodiment 3：
The present invention provides painting ecological block brick is exempted from, raw material accounting is no mud river sand 40%, steel Copper Slag 20%, mine tailings
15%, mine tailing 5%, cement 20%；The above-mentioned production technology for exempting to paint ecological block brick, includes the following steps：S1 will be without mud river
Sand, steel Copper Slag, mine tailings, mine tailing are weighed by electronic scale, S2 will without mud river sand, steel Copper Slag, mine tailings,
Mine tailing proportionally is stirred to form aggregate；The above-mentioned aggregate of S3 proportionally gradually lime stone, portland cement and gradually
Addition retarder sodium tripolyphosphate, water-reducing agent are stirred to obtain mixed soil, and the moisture content of above-mentioned portland cement is 40-50%,
It stands after mixing evenly and obtains surfacing；Facing material is put into mold by S4, and is carried out layering precompressed by molding machine and formed
Brick；S5 carries out brick to obtain finished product after blowing slag；The above-mentioned finished product of S6 is transported in curing kilns by conveyer belt, passes through curing kilns
Consolidate and form building block brick, the above-mentioned building block brick of S7 is transported to palletizing system progress stacking by transporting band, is packaged；It weighs logical
It crosses projection electronic weighing to claim, stirring weighs by blender and is placed in blender top, raw material automatically engages blender after weighing
Middle progress aggregate stirring puts into lime stone, portland cement after stirring for 0.5 to 2 small times, and portland cement and aggregate stir
In Jia Shui after uniformly, the moisture content 40-50% of portland cement is made by retarder sodium tripolyphosphate, water-reducing agent, passes through temperature
Wet meter obtains data, convenient for addition water；When blender carries out blowing after mixing evenly, will be transmitted by mixing belt conveyer
It into the hopper of molding machine, is carried out by way of successively pressing, the bottom of 5 millimeters of first precompressed, then 50-70 millimeters of precompressed of base
Layer, finally laying surface layer carries out precompressed again makes its porosity 15%, passes through multiple-prepressing and forms an entirety.
Embodiment 4：
The present invention provides painting ecological block brick is exempted from, raw material accounting is no mud river sand 40%, steel Copper Slag 20%, mine tailings
5%, mine tailing 15%, cement 20%；The above-mentioned production technology for exempting to paint ecological block brick, includes the following steps：S1 will be without mud river
Sand, steel Copper Slag, mine tailings, mine tailing are weighed by electronic scale, S2 will without mud river sand, steel Copper Slag, mine tailings,
Mine tailing proportionally is stirred to form aggregate；The above-mentioned aggregate of S3 is proportionally gradually mixed into lime stone, portland cement,
Portland cement and aggregate make containing for portland cement by retarder sodium tripolyphosphate, water-reducing agent after mixing evenly in Jia Shui
Water rate is 40-50%, stands obtain surfacing after mixing evenly；Facing material is put into mold by S4, and is carried out by molding machine
It is layered precompressed and forms brick；S5 carries out brick to obtain finished product after blowing slag；The above-mentioned finished product of S6 is transported to curing kilns by conveyer belt
In, consolidate by curing kilns and form building block brick, the above-mentioned building block brick of S7 by transport band be transported to palletizing system progress stacking,
It is packaged；Its weighing is claimed by projection electronic weighing, and stirring weighs by blender and claims to be placed in blender top, raw material after weighing
Progress aggregate stirring in blender is automatically engaged, puts into lime stone, portland cement, silicate after stirring for 0.5 to 2 small times
In Jia Shui, the moisture content of portland cement is made by retarder sodium tripolyphosphate, water-reducing agent after mixing evenly for cement and aggregate
40-50% obtains data by hygrothermograph, convenient for addition water；When blender carries out blowing after mixing evenly, pass through mixing
Belt conveyer will be delivered in the hopper of molding machine, and above-mentioned molding machine is the molding machine with vibration moulding platform, pass through vibration
Workbench makes to be covered with material in mold faster, is repeatedly being compressed after being covered with material by pressure head, is forming entirety, entirely through
For trigger by Product transport into delivery system, product is transported in curing kilns using delivery system and is conserved, conserve
For steam initial set, at 50~70 DEG C, curing time is 1.5-2 hours for room temperature control, and the product after maintenance is transported to stacking machine will
Stacking is carried out to product, is packaged outbound after stacking.
Although reference be made herein to invention has been described for multiple explanatory embodiments of the invention, however, it is to be understood that
Those skilled in the art can be designed that a lot of other modification and implementations, these modifications and implementations will fall in this Shen
It please be within disclosed scope and spirit.More specifically, it is disclosed, in the scope of the claims in the application, it can be to master
The building block and/or layout for inscribing composite configuration carry out a variety of variations and modifications.In addition to what is carried out to building block and/or layout
Outside modification and improvement, to those skilled in the art, other purposes also be will be apparent.
Claims (6)
1. one kind is exempted to paint ecological block brick, it is characterised in that：The raw material of the building block brick includes no mud river sand, steel copper mine
Slag, mine tailings, mine tailing, lime stone, portland cement, retarder sodium tripolyphosphate, water-reducing agent.
2. according to claim 1 exempt to paint ecological block brick, it is characterised in that：The building block brick raw material accounting is no mud
River sand 30-40%, steel Copper Slag 20-30%, mine tailings 5-10%, mine tailing 10-15%, lime stone 5-10%, portland cement
10-20%, retarder sodium tripolyphosphate 1-5%, water-reducing agent 1-5%.
3. according to claim 1 exempt to paint ecological block brick, it is characterised in that：The building block brick raw material accounting is no mud
River sand 40%, steel Copper Slag 20%, mine tailings 5%, mine tailing 10%, portland cement 15%, lime stone 5%, retarder trimerization phosphorus
Sour sodium 3%, water-reducing agent 2%.
4. a kind of production technology for exempting to paint ecological block brick, it is characterised in that：Include the following steps：S1 will be without mud river sand, steel
Iron Copper Slag, mine tailings, mine tailing are weighed by electronic scale, and S2 will be without mud river sand, steel Copper Slag, mine tailings, tailing
Powder proportionally is stirred to form aggregate；Aggregate described in S3 is proportionally gradually mixed into lime stone, portland cement and gradually
Addition retarder sodium tripolyphosphate, water-reducing agent are stirred to obtain mixed soil, and the moisture content of the portland cement is 40-50%,
It stands after mixing evenly and obtains surfacing；Facing material is put into mold by S4, and is carried out layering precompressed by molding machine and formed
Brick；S5 carries out brick to obtain finished product after blowing slag；Finished product described in S6 is transported in curing kilns by conveyer belt, passes through curing kilns
Consolidate and form building block brick, building block brick described in S7 is transported to palletizing system progress stacking by transporting band, is packaged.
5. according to claim 4 exempt to paint ecological block brick production technology, it is characterised in that：The pre- swaging of the layering is
Successively pressure, 5 millimeters of surface thickness, groundwork thickness is 50-70 millimeters, porosity 15%.
6. according to claim 4 exempt to paint ecological block brick production technology, it is characterised in that：The molding machine be with
The molding machine of vibration moulding platform makes to be covered with material in mold faster by vibration moulding platform.