CN108834913A - 一种葵花复合材质纯植物无公害猫砂及其生产方法 - Google Patents
一种葵花复合材质纯植物无公害猫砂及其生产方法 Download PDFInfo
- Publication number
- CN108834913A CN108834913A CN201810650581.1A CN201810650581A CN108834913A CN 108834913 A CN108834913 A CN 108834913A CN 201810650581 A CN201810650581 A CN 201810650581A CN 108834913 A CN108834913 A CN 108834913A
- Authority
- CN
- China
- Prior art keywords
- sunflower
- parts
- tremella
- cat litter
- agaric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种葵花复合材质纯植物无公害猫砂及其生产方法，属于宠物清洁垫料用品加工领域。包括葵花秸秆40～80份，葵花盘30～60份，葵花籽壳30～60份，银耳1.5～3份，木耳0.5～2份；葵花秸秆、葵花盘、葵花籽壳经微波有限碳化、微波高压复合膨润增稠、造粒成型杀菌一体化完成等方法生产葵花秸秆纯植物无公害猫砂。本发明产品具有吸水性强、吸水后结团快、团块牢固、有效包埋异味、便于清理、无粉尘、无污染等优点；最大限度避免宠物猫罹患泌尿道症候群疾病。使用后的葵花秸秆纯植物猫砂自然状态下可崩解、改良土壤，不污染环境，拓宽了葵花秸秆的应用范围，生产过程对环境友好，无废渣、废汽及有害物质产生。
Description
技术领域
本发明属于宠物清洁垫料用品加工领域，尤其是指一种纯植物无公害猫砂及其生产方法。
背景技术
猫砂是一种家养宠物垫料，是人们饲养的猫用来掩埋粪便和尿液的物体，有较好的吸水性，一般会与猫砂盆（或称猫厕所）一并使用，将适量的猫砂倒于猫砂盆内，受过训练的猫当需要排泄时便会走进猫砂盆排泄，并用猫砂将粪便进行掩埋。早期的猫砂主要是以不凝结的猫砂为主，主要是为了收纳猫便。随着猫砂技术的不断进步，又出现了凝结砂、木砂、水晶砂、膨润土砂等，更便于清理猫粪便。一般猫砂会添加除臭剂/防腐剂等化学产品，猫踩上后会沾到脚上并带到其它地方，造成污染。合格的猫砂要求具有良好的凝结力、吸水性、掩臭力，粉尘量小。目前几乎所有的猫砂都是非金属矿物的无机吸附材料，如海泡石、膨润土、硅藻土、凹凸棒石等，粉尘很大。据报道，西方发达国家每年消耗宠物垫土数十万吨。近年来，随着我国人民生活水平的提高，城市民居高楼化、花园化，家养宠物垫土的使用越来越多。
目前，市场上销售的猫砂种类有普通猫砂、结团型猫砂、水晶猫砂、木粉猫砂和纸屑猫砂。膨润土猫砂是目前使用最普遍的猫砂，以膨润土为主要成分，为结团型猫砂，外观白色或灰白色的小颗粒。使用时，猫砂产品很快吸干粪便里的水分，结成硬团，可以用猫砂铲铲出扔掉。随着猫砂的消耗，补充即可，不需全盆放弃。这种猫砂粉尘量较大，造成居室内粉尘污染，易导致与宠物共同居住的人过敏诱发呼吸道疾病、鼻炎等。另外无机矿物猫砂弃置环境中极难分解，造成土壤及环境污染。另外黏土猫砂主要成分是颗粒非常小的（＜2μm）可塑的硅铝酸盐及少量镁、铁、钠、钾和钙，目前没有合适的处理办法，用过的大量矿物黏土猫砂丢弃在垃圾点，不但对周围环境造成了不良影响，同时造成资源的浪费。而且传统猫砂中含有的石膏等碱性物质，是导致猫咪泌尿道症候群（特别是公猫）的原因之一。
目前有报道国外以木粉、膨润土粉为主要原料，经挤压成形、胶粉包衣，制成宠物垫圈颗粒猫砂。国内有专利报道的植物猫砂制备方法几乎全部加入黄原胶、瓜尔胶、果胶、魔芋胶、变性淀粉等胶质或聚乙烯醇、乙醛等化学物质作为粘结剂，例如201110227976.9“一种天然植物猫砂”、201410329874.1“豆粕、豌豆渣化学改性及用以制备猫砂的方法”、201310232981.8“秸秆质宠物用猫砂的制备方法”、201611158768.7“幼猫专用猫砂及其制备方法”等。而不添加任何添加剂的纯植物猫砂，目前国内外均未有报道。
葵花，学名向日葵（Helianthus annuus），别名太阳花，是菊科向日葵属的植物，一年生高大草本，茎直立，高1～3米，粗壮，被白色粗硬毛，不分枝或有时上部分枝。葵花耐旱，产果实葵花籽可作为油料来源，亦可生食或熟食。葵花茎质地坚硬，纤维含量高而且均一，木质素含量接近木材，其灰分含丰富碳酸钾。我国每年近千万吨的葵花秸秆，未得到充分利用。
发明内容
本发明提供一种葵花复合材质纯植物无公害猫砂及其生产方法，以解决猫砂目前存在的吸水性差、吸水后结团慢、团块不牢固、不便清理、有粉尘和污染的问题。
本发明采取的技术方案是，由下列重量份的原料和步骤得到的：
葵花秸秆40～80份，葵花盘30～60份，葵花籽壳30～60份，银耳1.5～3份，木耳0.5～2份；
（一）葵花秸秆、葵花盘、葵花籽壳净化及微波有限碳化处理
将葵花秸秆、葵花盘、葵花籽壳流动水喷淋去除表面积尘及泥土，然后置于隧道式微波处理装置中，单层放置，不得有叠加，以免受热不均，选取微波频率为2450MHz，物料中心温度130～155℃，时间5～20min，冷却至常温，粉碎，得到粒度80～100目碳化葵花秸秆粉、葵花盘粉、葵花籽壳粉备用；
（二）银耳、木耳微波高压复合膨润增稠处理
洁净的干燥银耳、木耳，喷淋润湿，使其吸水量达到其干重的3～5倍，然后置于微波振荡装置中，选取微波频率为2450MHz，物料中心温度100～110℃，时间5～10min，使银耳、木耳组织软化、膨润，然后置于高压反应釜中，于120～126℃、25～35min条件下进行增稠处理，赋予木耳及银耳适当的黏度，然后取出破碎，使其可全部通过100～120目，备用；
（三）造粒、成型、杀菌一体化完成
将经步骤（一）、（二）处理的物料混合均匀，调整混合物料水分质量百分含量为28～38%，然后将混合物料利用高温高压瞬间挤出装置、于110～140℃条件下进行造粒、成型、杀菌一体化完成处理，得到粒度2～5mm的不规则圆形颗粒，然后干燥至水分含量3～4%，干燥后颗粒的粒度1～3mm，即为具有良好吸水力的纯植物猫砂。
本发明优点：产品目测无杂质，无异味，表面光滑，手指用力可捻碎，水泡可快速蹦开呈碎屑且不漂浮，结团快、团块牢固和吸味功能强、有效包埋异味、吸水性强、效果好，被水湿透不穿底，吸水性≥400(体积%)，成球时间＜80s。而黏土或矿物猫砂吸水率≥220，粒度0.75～3mm，水份≤15%，成球时间＜90s。本发明产品采用葵花秸秆及食用菌银耳、木耳为原料，原料纯天然，而且产品经高温高压制成，不添加任何添加剂、化学品，不含碱性矿物质，无毒副作用，便于清理、无粉尘、无污染，最大限度避免宠物猫罹患泌尿道症候群疾病。用后的葵花秸秆猫砂自然状态下可缓慢崩解，异味少，耗损率低，使用寿命长，使用方便，可冲入马桶或丢弃，不污染环境。本发明产品不但对猫健康无任何不良影响，即使猫咪或家人误食也无伤害。另外本专利产品采用纯天然植物原料，可快速降解，所以用后的猫砂可作为具有改良土壤作用的有机肥使用，充分利用秸秆资源，对环境无污染。产品优于黏土等其他矿物猫砂。本发明猫砂除适于宠物猫，也适于其他家养宠物垫圈用。
具体实施方式
实施例1
由下列重量份的原料和步骤得到的：
葵花秸秆40份，葵花盘30份，葵花籽壳30份，银耳1.5份，木耳0.5份；
（一）葵花秸秆、葵花盘、葵花籽壳净化及微波有限碳化处理
将葵花秸秆、葵花盘、葵花籽壳流动水喷淋去除表面积尘及泥土，然后置于隧道式微波处理装置中，单层放置，不得有叠加，以免受热不均，选取微波频率为2450MHz，物料中心温度130℃，时间20min，冷却至常温，粉碎，得到粒度80～100目碳化葵花秸秆粉、葵花盘粉、葵花籽壳粉备用；
（二）银耳、木耳微波高压复合膨润增稠处理
洁净的干燥银耳、木耳，喷淋润湿，使其吸水量达到其干重的3倍，然后置于微波振荡装置中，选取微波频率为2450MHz，物料中心温度100℃，时间10min，使银耳、木耳组织软化、膨润，然后置于高压反应釜中，于120℃、25min条件下进行增稠处理，赋予木耳及银耳适当的黏度，然后取出破碎，使其可全部通过100～120目，备用；
（三）造粒、成型、杀菌一体化完成
将经步骤（一）、（二）处理的物料混合均匀，调整混合物料水分质量百分含量为28%，然后将混合物料利用高温高压瞬间挤出装置于140℃条件下进行造粒、成型、杀菌一体化完成处理，得到粒度2～5mm的不规则圆形颗粒，然后干燥至水分含量3～4%，干燥后颗粒的粒度1～3mm，即为具有良好吸水力的纯植物猫砂。
实施例2
由下列重量份的原料和步骤得到的：
葵花秸秆80份，葵花盘60份，葵花籽壳60份，银耳3份，木耳2份；
（一）葵花秸秆、葵花盘、葵花籽壳净化及微波有限碳化处理
将葵花秸秆、葵花盘、葵花籽壳流动水喷淋去除表面积尘及泥土，然后置于隧道式微波处理装置中，单层放置，不得有叠加，以免受热不均，选取微波频率为2450MHz，物料中心温度155℃，时间5min，冷却至常温，粉碎，得到粒度80～100目碳化葵花秸秆粉、葵花盘粉、葵花籽壳粉备用；
（二）银耳、木耳微波高压复合膨润增稠处理
洁净的干燥银耳、木耳，喷淋润湿，使其吸水量达到其干重的5倍，然后置于微波振荡装置中，选取微波频率为2450MHz，物料中心温度110℃，时间5min，使银耳、木耳组织软化、膨润，然后置于高压反应釜中，于126℃、35min条件下进行增稠处理，赋予木耳及银耳适当的黏度，然后取出破碎，使其可全部通过100～120目，备用；
（三）造粒、成型、杀菌一体化完成
将经步骤（一）、（二）处理的物料混合均匀，调整混合物料水分质量百分含量为38%，然后将混合物料利用高温高压瞬间挤出装置、于110℃条件下进行造粒、成型、杀菌一体化完成处理，得到粒度2～5mm的不规则圆形颗粒，然后干燥至水分含量3～4%，干燥后颗粒的粒度1～3mm，即为具有良好吸水力的纯植物猫砂。
实施例3
由下列重量份的原料和步骤得到的：
葵花秸秆60份，葵花盘45份，葵花籽壳45份，银耳2.3份，木耳1.2份；
（一）葵花秸秆、葵花盘、葵花籽壳净化及微波有限碳化处理
将葵花秸秆、葵花盘、葵花籽壳流动水喷淋去除表面积尘及泥土，然后置于隧道式微波处理装置中，单层放置，不得有叠加，以免受热不均,选取微波频率为2450MHz，物料中心温度142.5℃，时间12.5min，冷却至常温，粉碎，得到粒度80～100目碳化葵花秸秆粉、葵花盘粉、葵花籽壳粉备用；
（二）银耳、木耳微波高压复合膨润增稠处理
洁净的干燥银耳、木耳，喷淋润湿，使其吸水量达到其干重的4倍，然后置于微波振荡装置中，选取微波频率为2450MHz，物料中心温度105℃，时间7.5min，使银耳、木耳组织软化、膨润，然后置于高压反应釜中，于123℃、305min条件下进行增稠处理，赋予木耳及银耳适当的黏度，然后取出破碎，使其可全部通过100～120目，备用；
（三）造粒、成型、杀菌一体化完成
将经步骤（一）、（二）处理的物料混合均匀，调整混合物料水分质量百分含量为33%，然后将混合物料利用高温高压瞬间挤出装置于125℃条件下进行造粒、成型、杀菌一体化完成处理，得到粒度2～5mm的不规则圆形颗粒，然后干燥至水分含量3～4%，干燥后颗粒的粒度1～3mm，即为具有良好吸水力的纯植物猫砂。
实施例4
由下列重量份的原料和步骤得到的：
葵花秸秆40份，葵花盘60份，葵花籽壳30份，银耳1.5份，木耳2份；
（一）葵花秸秆、葵花盘、葵花籽壳净化及微波有限碳化处理
将葵花秸秆、葵花盘、葵花籽壳流动水喷淋去除表面积尘及泥土，然后置于隧道式微波处理装置中，单层放置，不得有叠加，以免受热不均；选取微波频率为2450MHz，物料中心温度130℃，时间20min，冷却至常温，粉碎，得到粒度80～100目碳化葵花秸秆粉、葵花盘粉、葵花籽壳粉备用；
（二）银耳、木耳微波高压复合膨润增稠处理
洁净的干燥银耳、木耳，喷淋润湿，使其吸水量达到其干重的3倍，然后置于微波振荡装置中，选取微波频率为2450MHz，物料中心温度110℃，时间10min，使银耳、木耳组织软化、膨润，然后置于高压反应釜中，于120℃、25min条件下进行增稠处理，赋予木耳及银耳适当的黏度，然后取出破碎，使其可全部通过100～120目，备用；
（三）造粒、成型、杀菌一体化完成
将经步骤（一）、（二）处理的物料混合均匀，调整混合物料水分质量百分含量为28%，然后将混合物料利用高温高压瞬间挤出装置于140℃条件下进行造粒、成型、杀菌一体化完成处理，得到粒度2～5mm的不规则圆形颗粒，然后干燥至水分含量3～4%，干燥后颗粒的粒度1～3mm，即为具有良好吸水力的纯植物猫砂。
Claims (2)
1.一种葵花复合材质纯植物无公害猫砂，其特征在于，是由下列重量份的原料和步骤得到的：
葵花秸秆40～80份，葵花盘30～60份，葵花籽壳30～60份，银耳1.5～3份，木耳0.5～2份；
（一）葵花秸秆、葵花盘、葵花籽壳净化及微波有限碳化处理
将葵花秸秆、葵花盘、葵花籽壳流动水喷淋去除表面积尘及泥土，然后置于隧道式微波处理装置中，单层放置，不得有叠加，以免受热不均，选取微波频率为2450MHz，物料中心温度130～155℃，时间5～20min，冷却至常温，粉碎，得到粒度80～100目碳化葵花秸秆粉、葵花盘粉、葵花籽壳粉备用；
（二）银耳、木耳微波高压复合膨润增稠处理
洁净的干燥银耳、木耳，喷淋润湿，使其吸水量达到其干重的3～5倍，然后置于微波振荡装置中，选取微波频率为2450MHz，物料中心温度100～110℃，时间5～10min，使银耳、木耳组织软化、膨润，然后置于高压反应釜中，于120～126℃、25～35min条件下进行增稠处理，赋予木耳及银耳适当的黏度，然后取出破碎，使其可全部通过100～120目，备用；
（三）造粒、成型、杀菌一体化完成
将经步骤（一）、（二）处理的物料混合均匀，调整混合物料水分质量百分含量为28～38%，然后将混合物料利用高温高压瞬间挤出装置、于110～140℃条件下进行造粒、成型、杀菌一体化完成处理，得到粒度2～5mm的不规则圆形颗粒，然后干燥至水分含量3～4%，干燥后颗粒的粒度1～3mm，即为具有良好吸水力的纯植物猫砂。
2.如权利要求1所述的一种葵花复合材质纯植物无公害猫砂的生产方法，其特征在于，包括下列重量份的原料和步骤：
葵花秸秆40～80份，葵花盘30～60份，葵花籽壳30～60份，银耳1.5～3份，木耳0.5～2份；
（一）葵花秸秆、葵花盘、葵花籽壳净化及微波有限碳化处理
将葵花秸秆、葵花盘、葵花籽壳流动水喷淋去除表面积尘及泥土，然后置于隧道式微波处理装置中，单层放置，不得有叠加，以免受热不均，选取微波频率为2450MHz，物料中心温度130～155℃，时间5～20min，冷却至常温，粉碎，得到粒度80～100目碳化葵花秸秆粉、葵花盘粉、葵花籽壳粉备用；
（二）银耳、木耳微波高压复合膨润增稠处理
洁净的干燥银耳、木耳，喷淋润湿，使其吸水量达到其干重的3～5倍，然后置于微波振荡装置中，选取微波频率为2450MHz，物料中心温度100～110℃，时间5～10min，使银耳、木耳组织软化、膨润，然后置于高压反应釜中，于120～126℃、25～35min条件下进行增稠处理，赋予木耳及银耳适当的黏度，然后取出破碎，使其可全部通过100～120目，备用；
（三）造粒、成型、杀菌一体化完成
将经步骤（一）、（二）处理的物料混合均匀，调整混合物料水分质量百分含量为28～38%，然后将混合物料利用高温高压瞬间挤出装置、于110～140℃条件下进行造粒、成型、杀菌一体化完成处理，得到粒度2～5mm的不规则圆形颗粒，然后干燥至水分含量3～4%，干燥后颗粒的粒度1～3mm，即为具有良好吸水力的纯植物猫砂。