CN1088238A - antifouling paint - Google Patents
antifouling paint Download PDFInfo
- Publication number
- CN1088238A CN1088238A CN93119120A CN93119120A CN1088238A CN 1088238 A CN1088238 A CN 1088238A CN 93119120 A CN93119120 A CN 93119120A CN 93119120 A CN93119120 A CN 93119120A CN 1088238 A CN1088238 A CN 1088238A
- Authority
- CN
- China
- Prior art keywords
- amine
- acid
- antifouling paint
- paint compositions
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The dirt of shell suppresses by a kind of amine of following structural formula:
R in the formula
1Be diterpene deutero-univalence hydrocarbyl and R
2And R
3Respectively do for oneself hydrogen, have the alkyl of 1 to 18 carbon atom or have 6 aryl to twelve carbon atom.This amine plays the paint adhesion agent and to the biocides of Hai Sheng.Antifouling paint compositions can comprise a kind of pigment and as the described amine of binding agent.Equally, antifouling paint compositions comprises that the acid groups as binding agent passes through the protected acid functional polymers of monoamine group, forms the salt of the organic solvent dissolution of polymkeric substance.
Description
The present invention relates to antifouling paint.Antifouling paint normally adopts the organism of Hai Sheng to discharge biocide as the shell finish paint, with the organism that prevents Hai Sheng such as: shellfish belongs to deposition and the growth of animal and algae.
Traditional antifouling paint comprises the binding agent of the relative inertness of the pigment that has the object of killing livestock, and the pigment of the described object of killing livestock oozes out from coating.What used always already in binding agent is Vinylite, particularly vinylchlorid/acetate ethylene copolymer, and rosin.To be the insoluble and coating of seawater adopt high pigment concentration to ooze out guaranteeing based on this resin to Vinylite, and there is the contact between the granules of pigments in the result.Rosin is a kind of hard brittle resin, and it is dissolving a little in seawater.Biocide pigment in use little by little oozes out from the rosin binder matrix, stays the matrix of rosin skeleton, and the result scrubs the shell surface, allows the deep of biocide pigment from paint film ooze out.
Most of in recent years successful anti-pollution paint, for example described in the English Patent 1457590, be based on a kind of polymeric binder biocide three organotin parts that chemically bond already, by seawater with biocide part " automatic polishing copolymer " coating of hydrolysis step by step.The polymkeric substance that partly comes from three organotins of hydrolysis becomes dissolved seawater, and the biocide of outermost layer coating is consumed as a result, and ship is swept by the surface of the motion shell of seawater.Discharge the automatic polishing copolymer coating of non-biocide, be described in European patent 69559 and the European Patent Application No. 232006.
International patent application no WO84/02915 has described a kind of hydrolyzable film forming water and has not dissolved the antifouling paint of curing groups polymeric binder again that has that is subject to the seawater etch, is represented by following structural formula:
X is hydrogen or methyl in the formula, and R is that alkyl, aryl, aralkyl or three organosilicons part and B are the residue of the unsaturated comonomer of alkene chain.That had found hydrolysis slightly easily in fact already does not give the radicals R of polymer dissolution in seawater such as benzyl, aminoalkyl group or alkylhalide group, and the group of easier hydrolysis such as trialkyl silica group gives polymkeric substance and easily is hydrolyzed into faint film on a kind of mechanical sense in seawater.
Day, unexamined number of patent application 54-64633 of the present disclosure described the antifouling biocide of a kind of Hai Sheng, and it is a kind of long-chain (12 to 18 carbon atoms) chain fat primary amine or its salt.Day unexamined number of patent application 54-110322 of the present disclosure has described some long-chain (12 to 18 carbon atoms) chain fat second month in a season or tertiary amine as marine antifoulant.
United States Patent (USP) 4675051 described a kind of in seawater dissolved marine antifouling coating progressively, it comprises rosin and contains the binding agent of the resin that the fat polyamine reaction of at least one uncle or secondary amine group produces.
A kind of antifouling paint compositions according to the present invention comprises a kind of binding agent and pigment, and it is characterized in that described binding agent to small part comprises the amine of following structural formula:
R ' is from diterpene deutero-univalence hydrocarbyl and R in the formula
2And R
3Respectively do for oneself hydrogen, have the alkyl of 1 to 18 carbon atom or the aryl of 6 to 12 carbon atoms.
According to a kind of method that suppresses the shell dirt of the present invention, comprise a kind of amine of the following structural formula that is applied to shell:
R ', R in the formula
2And R
3As top defined.
The amine of structure formula I is not only as binding agent but also as the marine anti-pollution biocide.This amine is preferably from the rosin deutero-.The rosiny primary structure is sylvic acid (abietic acid), and it is and other diterpene acid blended.This amine is preferably uncle or secondary amine.Secondary amine, R in the formula as an example
2Being methyl, may be antagonism such as the more effective biocide of shell-fish dirt, and primary amine may be the more effective biocide of antagonism algae.From rosin deutero-primary amine is dehydroabietylamine, commercially sells with " rosin Amine D D " form, and its primary structure is:
The corresponding second month in a season or tertiary amine as an example, can adopt N-methyl or the N of rosin Amine D D respectively, N-dimethyl derivative.
The amine of structure formula I is the more effective ocean of the amide group amine biocide that discloses than in United States Patent (USP) 4675051.The amine of structure formula I can be used for shell and other ocean surface as transparent antifouling varnish separately.This amine can be used as the paint adhesion agent with pigment simultaneously, and it can have or can not have the anti-soil activity.The amine of mentioning in above-mentioned Japanese patent application No. 54-64633 and 54-110322 also is not suitable for as the antifouling paint binding agent or does not add binding agent and use as antifouling varnish, because when using as coating, they are not dried to the film that is not clamminess.
This tackiness agent of antifouling paint compositions according to a kind of preferred type of the present invention is the amine of structure formula I and the mixture of other resin, preferable film-forming resin, and it is to dissolve a little or the swollen film-forming resin in seawater.As an example, this class tackiness agent can contain 10 to 90%, preferably the amine of 35 to 80% weight and 90 to 10%, preferably other resin of 65 to 20% weight.The binder for film formation resin that this class can be used together with amine is the rosin of rosin or maleation or the rosin of Fu Mahua.This blended binding agent dissolved matrix antifouling paint in known manner is used in etch in the seawater.This blended binding agent can be used as transparent antifouling paint or and pigment, preferably with the pigment of biocide such as Red copper oxide, forming antifouling paint.Equally, this amine can mix by insoluble film-forming resin with water, for example: and vinylic-ether polymer, such as: vinyl acetate between to for plastic/vinyl isobutyl ether multipolymer, as an example, this is to sell for " Laroflex " form with trade names.This amine also can with to the resin of the less sensitivity of water such as vinyl chloride-base polymer, particularly vinylchlorid/acetate ethylene copolymer or polymeric amide are used in combination, particularly the polymeric amide that forms from dipolymer lipid acid such as: sell with trade names " Versamid " form.In this case, it may be preferably be slightly soluble in or and the seawater reaction such as the pigment of pigment volume concentration (PVC)s such as Red copper oxide and/or zinc oxide.This amine also can be with have atoxic from polish binder polymer as: described at United States Patent (USP) 4593055 or European Patent Application No. 232006, or have the organotin automatic polishing copolymer as described in English Patent 1457590.
The amine of structure formula I also can adopt the mixture with one or more other high molecular weight amines to form a kind of according to antifouling paint tackiness agent of the present invention.For example: it can with a kind of long-chain (12 to 20 carbon atoms) aliphatic amine such as n-Laurylamine, cetylamine, octadecane amine or oleyl amine, or the mixture of this class amine, as an example such as: the form with tallow amine, hydrogenant tallow amine, theobroma oil amine or N-methyl theobroma oil amine is sold.Though this class long-chain amine is when using separately and be not suitable as paint adhesion agent or lacquer class binding agent, they in plastifying diterpene amine such as: may be useful among the rosin Amine D D.The mixture of these amines preferably contains the amine of the structure formula I of at least 50% weight, as an example as 60 to 90%.Correspondingly, this long-chain fat amine or the quantity that preferably exists based on the weight of binding agent (comprising amine) like that are from 5 to 50% weight.Comprise the amine of structure formula I and the mixture of rosin and long-chain fat amine according to a kind of preferable antifouling paint binding agent of the present invention or the composition of antifouling varnish, for example: the mixture of the aliphatic amide of the rosin Amine D D of 10-90% weight, the rosin of 5-65% weight and 5-50% weight.
Antifouling paint binding agent or lacquer can contain the amine of structure formula I and high-molecular weight, the preferably mixture of polymeric polyamines respectively.This class polyamines can commercially have been bought, especially for curing agent for epoxy resin.From " Versamid " of dipolymer fatty acid derived polymeric amide amino-functional normally.The polymeric amide of selling with trade names " Casamid " is respectively the polymeric amide as the amino-functional of solidifying agent, and it and water are dispersible.Usually thickness too when these polyamines of selling as solidifying agent are used alone as paint adhesion agent or lacquer, but when and form gratifying film when mixing use such as the diterpene of rosin Amine D D.We find " Casamid " polyamines such as: " Casamid 360 " have and kill halobiontic performance.Though the ocean of these polyamines is more less than the effect of the amine of structure formula I with biocide, all components that this mixture is provided at binding agent or lacquer have marine organisms property extremely.This class mixture preferably comprises 50% at least, more preferably be the amine of the structure formula I of 60 to 90% weight.
Another antifouling paint compositions according to the present invention comprises pigment and as the functional film-forming polymer of a kind of acid of binding agent; its acid groups is protected by hydrolyzable blocking group; said composition comprises having the composition of marine organisms performance extremely, it is characterized in that the monoamine group of described hydrolyzable blocking group for the amine salt of a kind of organic solvent soluble polymkeric substance of formation.
The present invention further provides the method that is used to suppress the shell dirt; comprise to shell use have a marine organisms performance extremely and comprise can film-forming polymer as the sour official of binding agent; its acid groups is characterized in that the monoamine group of described hydrolyzable blocking group for the amine salt of a kind of organic solvent soluble polymkeric substance of formation by the protected coating composition of hydrolyzable blocking group.
The functional polymkeric substance of acid is preferably equivalent in 240 to 600 carboxylic acid functional polymer.Preferable acid functional polymers is the addition copolymer of one or more unsaturated acid or anhydrides of alkene family, for example: vinylformic acid, methacrylic acid, toxilic acid, maleic anhydride, fumaric acid, methylene-succinic acid or itaconic anhydride, vinyl benzoic acid (for example: right-vinyl benzoic acid), 3-butenoic acid or propenoic acid beta-carboxylic ethyl ester or methacrylic ester is at least with an alkene family unsaturated comonomer addition copolymerization.Preferably methacrylic acid or acrylic acid multipolymer.(preferable equivalent 240 to 600 is equivalent to the acrylic acid content of 14.3 to 35.8% weight and the methacrylic acid content of 16.7 to 41.7% weight).Acid mono preferably with one or more unreacted comonomer copolymerization that have acid groups, for example: the ester of acrylic acid or methacrylic acid such as methyl acrylate, methyl methacrylate, ethyl propenoate, butyl acrylate or methacrylic acid 2-ethylhexyl, vinylbenzene, vinyl cyanide, vinyl acetate between to for plastic, vinyl butyrate, vinylchlorid or vinyl pyridine.Terpolymer may be preferable, for example: methacrylic acid formic acid or Jia Jibingxisuanyizhi, they are tending towards forming a kind of dura mater, can be used for combining such as: ethyl propenoate or particularly at the alkyl acrylate of 3 to 8 carbon atoms of moieties butyl acrylate for example, it helps to form than the softish film with acrylate.As an example, a kind of acrylate of replacement can be used as a kind of of comonomer.The preferable acid polymer of this class has 1,000 to 100,000 molecular weight.The equivalent of this acid polymer (calculating with acid groups) the best is 300 to 440, is equivalent to the content that acrylic or methacrylic acid contains 15 to 30% weight.
In addition, sour functional polymkeric substance is the polymkeric substance that contains sulfuric acid, phosphoric acid or phosphorous acid (acid phosphate) group.If adopt one of them acid groups, preferably they also exist in the polymkeric substance of addition, for example: the undersaturated phosphoric acid of a kind of alkene family, phosphorous acid or vitriolic addition copolymer.The example of this class unsaturated acid is vinyl phosphoric acid, vinylbenzene phosphoric acid, 2-acrylamido propane phosphoric acid, ethylidene-1,2-bisphosphate, hydroxyethyl acrylate monophosphate, vinyl sulfuric acid, 2-acrylamide amino-2-methyl propane sulfuric acid, methylallyl sulfuric acid and vinylbenzene sulfuric acid.The polymkeric substance that contains stronger acid groups such as: sulfate group, possible tool is than high equivalent weight, for example: in 500 to 5000 scopes, preferably in 1000 to 2000 scopes.
The monoamine that is used to form amine salt or acid functional polymers preferably comprises at least a organic group that contains at least 8 carbon atoms, more preferably contain 8 to 20 carbon atoms, and preferably, be that a kind of organism to Hai Sheng is virose amine, may become transparent antifouling varnish maybe may be colored if this used class amine produces amine salt.As an example, this monoamine can be the diterpene deutero-amine of structure formula I, is preferably the rosin deutero-, as an example: as rosin Amine D D.This toxic amine can be selected a kind of aliphatic amine, the organic group that contains 12 to 20 carbon atoms, for example: straight chained alkyl or alkenyl amine, such as: n-Laurylamine, cetylamine, octadecane amine or oleyl amine or from the mixture that is present in natural fat and oils aliphatic series deutero-amine such as tallow amine or hydrogenated tallow amine or theobroma oil amine.The amine that wherein can be used as blocking group be the aralkyl amine such as: those are commercial sells with " Phenalkamines " trade mark.
If the amine salt of the acid functional polymers that forms with non-biocide amine, this coating composition should contain the ocean biocide.This coating preferably contains pigment, and described pigment may be the same with biocide with the ocean.
Forming amine salt from acid functional polymers is not dissolved in the water basically and controls the dissolution rate of acid functional polymers in seawater.This amine salt dipping in seawater for a long time can for example progressively dissolve: be used for shell.This amine salt progressively is released in the seawater.The acid functional polymers that keeps is transformed into free acid or anionic form and becomes seawater soluble and step by step from the housing removing of ship step by step.Play self-polishing coating so contain the coating of the amine salt of sour functional polymkeric substance.When adopting biocidal amine, the performance of this coating is very similar to known organotin copolymer coating, and what discharge step by step is combined in the polymer biocidal agent with polymeric binder and becomes smooth from the shell dissolving.
Through the acid functional polymers of protection preferably can be by accordingly through acid functional monomer's addition polymerization preparation of protection, that is: the unsaturated acid of polymerisable vinyl such as the amine salt of acrylic or methacrylic acid and one or more comonomer addition copolymerizations.Preferably; be aggregated in a kind of organic solvent and carry out; such as: under 60 to 100 ℃ of temperature, adopt free agent catalyzer such as benzoyl peroxide or Diisopropyl azodicarboxylate at dimethylbenzene, toluene, butylacetate, butanols, butyl cellosolve or acetate methoxyl group propyl ester.Preferably reaction produces a kind of amine salt and polymerization need not to separate this salt to amine salt with amine by acid monomer such as: acrylic acid or methacrylic acid in a kind of solution of polar organic solvent, though can separate if desired.In addition, can make the protection radical reaction to form amine salt by sour functional multipolymer and amine through the acid functional polymers of protection with free carboxy.This amine salt can simply mix formation by the solution of amine and sour functional polymkeric substance, preferably, and in a kind of organic solvent, such as: form in aromatic hydrocarbon, ketone, alcohol or the ether alcohol.
The sour functional polymkeric substance of the amine of structure formula I or amine protection can adopt traditional coating mixing process and pigment to mix to provide to have pigment volume concentration (PVC) at 25 to 55% composition.This pigment is preferably sl. sol. pigment, the solubleness that has in seawater is from 0.5 to 10ppm(weight) solubleness, as for example: Red copper oxide, the inferior ketone of thiocyanic acid, zinc oxide, ethylenebis (dithiocarbamic acid) zinc, ziram, zinc diethyldithiocarbamate or the inferior ketone of ethylenebis (dithiocarbamic acid).The slightly soluble pigment of these copper and zn cpds is common ocean biocide.These pigment produce water soluble metallic compound under seawater eroding, granules of pigments fails to remain in coating surface as a result.Can adopt the mixture of slightly soluble pigment, for example: the mixture of Red copper oxide, cuprous thiocyanate or ethylenebis (dithiocarbamic acid) zinc, they are the thing pigment of killing livestock efficiently, can mix with zinc oxide, less as the biocide effect, but dissolving a little quickly in seawater.The sour functional polymkeric substance of the amine of structure formula I and amine protection can with the pigment of alkalescence such as: Red copper oxide or zinc oxide mix the gelification of using and not producing binding agent, are different from the sour functional polymkeric substance that contains free carboxylic acid groups.The gelification of this amine salt protection acid groups antagonism basic color.
This coating composition can add or conversion contain with the nonreactive pigment of seawater and can be seawater camber insoluble (solubleness is lower than 0.5ppm weight) such as titanium dioxide or ferric oxide or pigment dyestuff such as phthalocyanine pigment.The insoluble pigment of this class height preferably adopt at least coating portion the pigment component be less than 40% weight, best for being less than 20%.
What this antifouling paint also can contain is nonmetallic to marine organisms Liferous biocide, for example: the isothiazolones of TMTD, methylene-bis (thiocyanic ester), Vancide 89, replacement or 2-methylthio group-4-spy-butyl amino-6-cyclopropyl amino-sym-triazine.
Antifouling paint of the present invention is usually with at a kind of organic solvent, for example: the aromatic hydrocarbon of dimethylbenzene or toluene, or such as: the aliphatic hydrocrbon of petroleum solvent, such as the ester of N-BUTYL ACETATE, acetic acid ethoxy ethyl ester or acetic acid methoxyl group propyl ester, such as: the alcohol of butanols or butyl cellosolve or such as: use in the solution of the ketone of methyl iso-butyl ketone (MIBK) or methyl isoamyl ketone.
In addition, antifouling paint of the present invention can be the aqueous composition of the mixable solubility promoter of a kind of Shui Heshui of containing.The example of adoptable solubility promoter such as: the alcohols of butanols, such as: the glycol ether of methoxypropanol, methyl cellosolve, butyl cellosolve and ethoxy ethanol and such as the ester class of acetic acid methoxyl group propyl ester.The amine of structure formula I, and this acid functional polymers is dissolved in the mixture of this class water and solubility promoter, but does not dissolve basically in water with the amine protection of the organic group that contains at least 8 carbon atoms.Aqueous composition comprises as the polyamines of the amine of the structure formula I of binding agent and dilutable water such as the mixture of " Casamid 360 ", only needs the organic cosolvent of low levels, as an example, is less than every liter 200 grams.
The present invention is described by following examples.
Embodiment 1
The rosin Amine D D of 30% volume and " Laroflex " of 20% volume (vinyl acetate between to for plastic/vinyl isobutyl ether multipolymer) are dissolved in the solvent systems of methyl isoamyl ketone of " Shellsol " aromatic hydrocarbon that comprises 37.5% volume and 12.5% volume, obtain a kind of transparent hard antifouling varnish.
The antifouling property of the lacquer of embodiment 1 adopts and oozes out experimental test.In this test, the plaque of film that scribbles the lacquer of embodiment 1 is immersed in take out in the container of artificial seawater and in a week and once floods one day again in less sea container.Test seawater test from smaller container then each time to the toxicity of the organism of genus artemia (extra large shrimp) and double eyebrow algae spp (unicellular algae) Hai Sheng.The test each time that this seawater sample had contacted with film already in 8 weeks all shows positive toxicity, shows that its ocean oozes out in the whole prolongation cycle from coating continuously with biotic pesticide.
Embodiment 2
" Versamid 940 " polyamide resin of the rosin Amine D D of 30% volume and 20% volume is dissolved in the solvent systems of butanols of the dimethylbenzene that comprises 37.5% volume and 12.5% volume, obtains transparent hard antifouling varnish.
Embodiment 3
The rosin of the rosin Amine D D of 30% volume and 20% volume is dissolved among " Shellsol " of 50% volume to form transparent antifouling varnish, can dissolves from shell step by step when in seawater, using over a long time.
The antifouling varnish of embodiment 1 to 3 is sprayed on the plaque, forms transparent filming in each situation.This plaque attached to metal sheet, is immersed in bay, Britain south and is rich in the marine of dirt organism.This plaque did not have dirt at 12 months behind the dipping.
Embodiment 4
The mixture ground and mixed that the rosin of the rosin Amine D D of 80% volume and 20% volume is dissolved in the zinc oxide of the Red copper oxide of mixture in the dimethylbenzene and 93% volume and 7% volume obtains the coating that solids content is 47% volume and the pigment (pigment of this 47% volume refers in the exsiccant paint film) of 47% volumetric concentration.
Embodiment 5
Adopt the mixture of the rosin Amine D D of the rosin of 80% volume and 20% volume to repeat embodiment 4.
With the paint spay-coating of embodiment 4 and 5 on plaque and be immersed in the above-mentioned seawater.They still do not have dirt after 12 months.
Embodiment 4 and 5 coating are tested in the rolling test of the type described in a kind of BP1457590.Described two kinds of coating are because the dissolving of binding agent in seawater demonstrates the progressively reduction of film thickness.The thickness rate that the coating of embodiment 4 reduces is half of successful coml automatic polishing copolymer antifouling paint.The thickness that the coating of embodiment 5 reduces is equal to this coml coating.
Embodiment 6
Be dissolved in " Laroflex " of the rosin Amine D D of 60% volume and 40% volume in " Shellsol " and grind and obtain the coating that solids content is the pigment of 47% volume and 47% volumetric concentration with Red copper oxide.This coating that obtains is that a kind of hard non-etch is coated with (layer) and adorns and be suitable for being used on the fast ship.
Embodiment 7
In a kind of solution, rosin Amine D D is added in this polymers soln with the quantity of 1.03 amidos to an acid groups of above-mentioned polymkeric substance by methacrylic acid/Jia Jibingxisuanyizhi/vinylformic acid methoxyl group ethyl ester free radical catalyzer of 24/56/20,40% volume of the multipolymer by solution polymerization in the dimethyl of 1: 1 volume and butanols mixture solution.
The lacquer that produces adopts the experimental test that oozes out that illustrates among the embodiment 1.
The seawater sample of the coating of contacted embodiment 7 demonstrates stable toxicity basically at the duration of test in whole 8 weeks.
As a comparison, also after tested, it is atoxic that this sample that oozes out is observed when this acid copolymer solution is not used as coating with the amine reaction.
Embodiment 8 and 9
The polymeric amine salts solution and 1.5 of 7.5 embodiment 7 that restrain is restrained Red copper oxide (embodiment 8) mixing and mixes (embodiment 9) to form antifouling paint with 1.5 gram zinc oxide.
The viscosity of embodiment 8 and 9 coating is by after 25 ℃ of test mixing 100 hours of ICI cone and plate viscometer.The coating of embodiment 8 remains on the stable viscosity of mooring less than 10 at 100 hours test periods.The viscosity of the coating of embodiment 9 was not moored less than 40 100 hour testing period.For relatively, mix and be presented in 80 hours viscosity without the coating that polymkeric substance and amine reaction form and rise and surpass 100 pools (being higher than spray application far away) by the functional polymkeric substance of acid and Red copper oxide or zinc oxide.
Embodiment 10
Polymeric amine salts solution and the Red copper oxide of 14.4% volume, the wilkinite of 0.25% volume and the silicon-dioxide aerosol of 0.35% volume of the embodiment 7 of 85% volume are ground to form antifouling paint.
This coating is tested and be presented at whole 60 days dipping phase thickness and gradually reduce in rolling circle looping test instrument.The light rate is similar to coml three organotin copolymer antifouling paints.In order to contrast, when acid copolymer mixes with Red copper oxide pigment and is not that the coating dipping that at first produces with the amine reaction took out from rolling circle looping test instrument after one day.
Embodiment 11
The multipolymer for preparing in the solution in dimethylbenzene/butanols that a kind of 30/20/50 vinylformic acid/methyl methacrylate/butyl acrylate such as embodiment 7 describe is added to (to be equivalent to the quantity of acid groups in polymkeric substance) in this multipolymer with rosin Amine D D.Solution that produces and pigment, softening agent and structural agent grind and contain the coating that volume is respectively 30% multipolymer amine salt, 18% Red copper oxide, 1.3% zinc oxide, 4% Tritolyl Phosphate and 2% structural agent with formation.
This paint spay-coating is immersed in then as in the seawater of embodiment 1 to 3 on plaque.The plaque of this coating showed no dirt at 12 months behind the dipping basically.
This coating is tested and show substantially the same in the speed that progressively consumes of coml automatic polishing copolymer antifouling paint on thickness on rolling circle looping test instrument.
Embodiment 12
Rosin Amine D D is dissolved in the butanols and with the polyamines of " Casamid 360 " amino functional with Casamid to rosin Amine D D1: 4 volume ratio is mixed.This blended solution with water is diluted also and the Red copper oxide grinding is an antifouling paint 47%, that contain 196 gram butanols and 24.7 gram water to obtain every liter coating pigment volume concentration (PVC).
Claims (10)
1, a kind of antifouling paint compositions comprises pigment and as the sour functional film-forming polymer of binding agent; its acid groups is protected by hydrolyzable blocking group; said composition comprises having the composition of ocean with biocide character; it is characterized in that described hydrolyzable blocking group is a kind of monoamine, it forms the amine salt of the soluble polymkeric substance of a kind of organic solvent.
2, antifouling paint compositions as claimed in claim 1 is characterized in that described acid functional polymers is a kind of polymkeric substance of carboxylic-acid functional of equivalent 240 to 600.
3, antifouling paint compositions as claimed in claim 1 is characterized in that described acid functional polymers is a kind of functional polymkeric substance of sulfonic acid of equivalent 500 to 5000.
4,, it is characterized in that the amine groups that described monoamine provides comprises that at least one contains the organic group of 8 to 20 carbon atoms as each described antifouling paint compositions of claim 1-3.
5,, it is characterized in that described monoamine has the performance to the marine organisms kill agent as each described antifouling paint compositions of claim 1-3.
6,, it is characterized in that described the monoamine of amido is provided is a kind of a kind of amine with following structural formula as each described antifouling paint compositions of claim 1-3:
R in the formula
1Be diterpene deutero-monovalence alkyl and R
2And R
3Each is respectively hydrogen, has the alkyl of 1 to 18 carbon atom or has 6 aryl to twelve carbon atom.
7, antifouling paint compositions as claimed in claim 1 is characterized in that described monoamine is non-biocides and the coating composition that contains a kind of marine organisms kill agent.
8, antifouling paint compositions as claimed in claim 7 is characterized in that described pigment is a kind of marine organisms kill agent.
9, as each described antifouling paint of claim 1-3, it is characterized in that described pigment be a kind of in seawater dissolved copper and zn cpds.
10, a kind of method that suppresses the shell dirt; comprise to shell use have to marine organisms kill agent performance and as the acid tube of binding agent can film-forming polymer (its acid groups is protected by hydrolyzable blocking group) coating composition, it is characterized in that hydrolyzable blocking group is the monoamine group that a kind of organic solvent dissolution of polymkeric substance listens amine salt to form.