CN108822537A - Hardy type PA-6 intermingling material formula - Google Patents

Hardy type PA-6 intermingling material formula Download PDF

Info

Publication number
CN108822537A
CN108822537A CN201810830475.1A CN201810830475A CN108822537A CN 108822537 A CN108822537 A CN 108822537A CN 201810830475 A CN201810830475 A CN 201810830475A CN 108822537 A CN108822537 A CN 108822537A
Authority
CN
China
Prior art keywords
parts
material formula
intermingling material
hardy type
doa
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201810830475.1A
Other languages
Chinese (zh)
Inventor
曹小明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Taizhou Tianchuang Technology Service Co Ltd
Original Assignee
Taizhou Tianchuang Technology Service Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Taizhou Tianchuang Technology Service Co Ltd filed Critical Taizhou Tianchuang Technology Service Co Ltd
Priority to CN201810830475.1A priority Critical patent/CN108822537A/en
Publication of CN108822537A publication Critical patent/CN108822537A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a kind of hardy type PA-6 intermingling material formula, it is equipped in every 100 parts of PA-6 resins：21~23 parts of EPDM, 5~7 parts of PP-g-MAH, 1~2 part of HSt, 3~4% dioctyl adipates（DOA）.The present invention significantly improves cold tolerance.

Description

Hardy type PA-6 intermingling material formula
Technical field
The present invention relates to a kind of polymer composite formula, especially a kind of PA-6 intermingling material formula.
Background technique
PA-6 intermingling material has preferable toughness, but resistance to low temperature is to be improved.
Summary of the invention
In view of the deficiencies of the prior art, the present invention proposes a kind of hardy type PA-6 blendings that can significantly improve resistance to low temperature Material prescription.
The present invention is achieved through the following technical solutions technical goal.
Hardy type PA-6 intermingling material formula, thes improvement is that：It is equipped in every 100 parts of PA-6 resins：21~23 parts EPDM, 5~7 parts of PP-g-MAH, 1~2 part of HSt, 3~4% dioctyl adipates（DOA）.
Preferably, it is equipped in every 100 parts of PA-6 resins：22~22.5 parts of EPDM, 5.5~6 parts of PP-g-MAH, 1~1.5 part HSt, 3~3.5% dioctyl adipates（DOA）.
Compared with prior art, the present invention having the positive effect that：Add dioctyl adipate（DOA）, significantly improve Cold tolerance.
Specific embodiment
Below with reference to embodiment, the invention will be further described.
Embodiment 1：
Hardy type PA-6 intermingling material formula is equipped in every 100 parts of PA-6 resins：21 parts of EPDM, 5 parts of PP-g-MAH, 1 part of HSt, 3% dioctyl adipate（DOA）.
Embodiment 2：
Hardy type PA-6 intermingling material formula is equipped in every 100 parts of PA-6 resins：23 parts of EPDM, 7 parts of PP-g-MAH, 2 parts of HSt, 4% dioctyl adipate（DOA）.

Claims (2)

1. a kind of hardy type PA-6 intermingling material formula, it is characterised in that：It is equipped in every 100 parts of PA-6 resins：21~23 parts EPDM, 5~7 parts of PP-g-MAH, 1~2 part of HSt, 3~4% dioctyl adipates（DOA）.
2. hardy type PA-6 intermingling material formula according to claim 1, it is characterised in that：In every 100 parts of PA-6 resins It is equipped with：22~22.5 parts of EPDM, 5.5~6 parts of PP-g-MAH, 1~1.5 part of HSt, 3~3.5% dioctyl adipates（DOA）.
CN201810830475.1A 2018-07-26 2018-07-26 Hardy type PA-6 intermingling material formula Withdrawn CN108822537A (en)