CN108796342A - A kind of no nickel and the corrosion-resistant jewellery seedling silver alloy for having excellent die casting performance - Google Patents
A kind of no nickel and the corrosion-resistant jewellery seedling silver alloy for having excellent die casting performance Download PDFInfo
- Publication number
- CN108796342A CN108796342A CN201810904052.XA CN201810904052A CN108796342A CN 108796342 A CN108796342 A CN 108796342A CN 201810904052 A CN201810904052 A CN 201810904052A CN 108796342 A CN108796342 A CN 108796342A
- Authority
- CN
- China
- Prior art keywords
- alloy
- jewellery
- nickel
- corrosion
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of no nickel and has the corrosion-resistant jewellery seedling silver alloy of excellent die casting performance.According to weight percent, the ingredient of the alloy is:P:0.5-0.8wt.%,Bi:3.0-3.5wt.%,Sn:4.0-5.0wt.%,Te:0.4-0.6wt.%,Al:2.0-3.5wt.%,Fe:5.0-8.0wt.%,Ag:40.0-50.0wt.%, surplus are copper.The phenomenon that material provides a kind of solution of materialogy for China's seedling silver alloy, and environmental protection can be had and not generate allergy by not only making seedling silver products after processing, and the alloy has excellent die casting performance.The implementation and industrialization of the material can effectively push the demand of the update of China's jewellery industry product and industry upgrading.
Description
Technical field
The present invention relates to technical field of alloy, specifically, being related to a kind of silver alloy.
Background technology
Fine silver price in noble metal is relatively low, various because that can be processed into good ductility, soft texture
Form is just liked by people since ancient times, and is widely used in manufacture jewellery, tableware and various ornaments.Fine silver matter is soft, though
Convenient for the processing of traditional ornaments, but it is unfavorable for embedding gem.And since hardness is low, after ornaments experience wear, surface will produce carefully
Small cut, makes surface gloss decline, and influences beauty.In order to overcome these disadvantages of fine silver, people to be added in silver various
Alloying element come improve silver mechanics and other performance, which forms silver alloy.
Miao Yin is a kind of distinctive silver alloy of Miao ethnic group, generally adds copper-nickel alloy, nickel etc..Silver content is 20-60wt% in Miao Yin,
With good processing performance.Seedling Silver Jewelry was once a kind of form that Miao ethnic group hoards wealth, by pressure, it is few, the complexity such as carve, hug
Manual process various fancy are made, formed great national characters Miao ethnic group decorations.There is the popular this silver of many ethnic groups in Yunnan
Decorations, such as the finery of Miao ethnic group, jewellery also maintain the tradition of system silver by hand in Miao Zhai.Why popular seedling Silver Jewelry is, main to go back
It is to be its exquisite manufacture craft and unique jewellery pattern.The artistic characteristics showed in Miao ethnic group's silver jeweleries, and it is very frightened
People's.Many Miao ethnic group wear in area silver jeweleries and are particular about to be mostly beautiful.Miao Yin is forged into various technique jewellery and ornament, decoration
People's lives, more and more women like wearing seedling Silver Jewelry, and more and more ornaments of arranging in pairs or groups can select seedling silver-colored.
China metal surface process history is long, and manufacture skill is consummate, various in style, unique style.It is prepared using Tibetan silver
Jewellery and vessel, keep processing stage more and more finer.The progress of development and science and technology now with handicraft, uses tool
A variety of exploitations, the processing of ornaments is more and more exquisiter, on the basis of inheriting tradition in intension again have new expression.In conjunction with material
Matter itself the characteristics of, using process of surface treatment appropriate, impart the more appeal of Tibetan silver texture and expressive force.
According to foreign media, most women for wearing alloy earrings are susceptible to pain redness, blister symptom.Coin,
It can also cause allergic reaction after belt joint even telephone set contact skin.Reason is that these articles contain nickel, industry
Most common skin contact allergin in production.Studies have shown that nickel can be attached to a kind of special immune system protein matter
On, during which participates in the harmful invasion substance of body identification.Nickel can trigger a kind of specific proteins in immune system
Immune response, cause the allergic symptoms such as scorching hot, itch, redness.In the internal of impacted people, immune system can nickel as
A kind of infectious substance, when immune system response is too drastic, body just will appear a series of classical symptoms, such as it is scorching hot, itch, be red
Swollen, blister etc..A series of biochemical reaction can be caused, blood flow increase, tissue leakage, immunocyte is caused to pour in,
Ultimately form infection.
In addition, silver is readily generated a kind of extremely poorly soluble silver salt when encountering hydrogen sulfide gas or sulphion in air,
As long as silver meets the hydrogen sulfide gas or sulphion of several trillion to tens part per trillion in air, just produced in silver surface
Silver sulfide.Because silver sulfide is grey black, with the aggravation of reaction, silver sulfide, which increases, to be thickened, silver surface color just by
Step is by the last blackening of leucismus xanthochromia ash.The source of Air Hydrogen Sulfide is a variety of.It is the excrement of humans and animals first through meticulous
Bacterium generates a large amount of hydrogen sulfide after decomposing, and hydrogen sulfide is also generated after the protein corruption in plant.In addition also contain in the sweat of people
There is sulphur, the sulphur caused by sewage and garbage emission in silver tarnish, especially urban air can be made when it is contacted with silverware
It is more surprising to change hydrogen.
But regrettably, there is no form series abundant as karat gold for seedling silver alloy at present.With in recent years
Carry out the arrival of seedling silver jewellery storm, seedling Silver Jewelry sells well street corner, and demand dramatically increases.In the technology side of processing of ornament
Face, the Silver Jewelry factory in China have it is fairly horizontal, it is three-dimensional if any the hollow electrotyping forming for representing current international jewellery most up-to-date techniques
Stereoscopic vehicle is spent;There are the full-automatic chain assembly line processed of leading domestic jewellery technology, precision to lose casting assembly line;Also a little gold, sandblasting,
The fashion skills such as coloured silk plating.And the seedling silver alloy product that the positive Devoting Major Efforts To Developing of domestic production man is new, market is met with brand and technology
It examines and challenges.
Invention content
The purpose of the present invention is to overcome the deficiency in the prior art, provides a kind of no nickel and has the corrosion resistant of excellent die casting performance
Lose jewellery seedling silver alloy.
To achieve the goals above, the present invention adopts the following technical scheme that:
A kind of no nickel and the corrosion-resistant jewellery seedling silver alloy for having excellent die casting performance.By weight percentage, the group of alloy
As P:0.5-0.8wt.%,Bi:3.0-3.5wt.%,Sn:4.0-5.0wt.%,Te:0.4-0.6wt.%,Al:2.0-
3.5wt.%,Fe:5.0-8.0wt.%,Ag:40.0-50.0wt.%, surplus are copper.
A kind of above-mentioned no nickel and the corrosion-resistant jewellery seedling silver alloy for having excellent die casting performance, include the following steps:It will
As above the raw material matched is added in the electric induction furnace under ar gas environment, and uses graphite crucible;It is kept the temperature at 1400 degree when melting
It is 10 minutes, uniform by Efco-Northrup furnace electromagnetic agitation;1 minute being kept the temperature at 1400 degree after stirring evenly and being cast come out of the stove;Alloy pours
Casting uses the punching block of diameter 20-30mm, and is cooled down by the way of water cooling.The ingot casting of gained is rolled at room temperature, often
It is 20-30% that passage, which rolls lower amount,;It is 400 degree per intermediate anneal temperature after rolling twice, keeps the temperature 0.5 hour;Finally material is rolled
At the alloy sheets that thickness is 10-20mm;In jewellery forming process, needs to carry out vacuum annealing process, eliminate in process
Stress;Wherein, temperature is 420 degree, and the time is 0.4 hour.
Compared with prior art, the present invention has the advantages that:
(1)Miao Yin is a kind of distinctive silver alloy of Miao ethnic group, generally adds copper-nickel alloy, nickel etc..Silver content is 20-60wt%, tool in Miao Yin
There is good processing performance.Due to the use of copper-nickel alloy(Most commonly corronil), or it is added to nickel, cause nickel in jewellery
Content it is very high, during the normal wearing of jewellery, enter in human body since nickel becomes nickel ion, cause wearer appearance
Nickel allergy.In addition, Miss's the whole body silver jeweleries contains in seedling stockaded village, ornaments mostly up to hundreds of, exceed twenty or thirty again up to half people height, component
Jin.Thus, the phenomenon that skin and nickel contact and generates nickel allergy and probability, also considerably increase.In order to solve these problems, carry
The market occupancy volume of high seedling silver alloy and jewellery, this patent provides a kind of not nickeliferous seedling silver alloy, and the material is with excellent
Different corrosion resistance and die casting performance.
(2)The material has carried out advanced materialogy design, and the selection of alloying component and content make in process of setting
Dendrite is obviously refined, and the temperature that dendrite is linked to be skeleton is made to postpone.While setting temperature declines, the purification of alloying element
Effect makes impurity thing, gas content substantially reduce, and improves the mobility of solution.Jewellery silver alloy is in casting process
Hot crackability is also to weigh the important indicator of material property.Temperature model of the alloy of present patent application protection due to expanding solidification
It encloses, makes alloy there is longer time to carry out feeding to solidification shrinkage in process of setting, while can also reduce alloy and solidify
Contraction distortion amount in journey, improves the ability of its thermal crack resistant.
(3)The material has excellent reuse performance.For casting ornament craft, casting technique yield rate generally compared with
It is low, the returns such as a large amount of running channel, waste product are will produce in production process.Jewellery enterprise is based on production cost and efficiency, always wishes
It hopes and uses returns as far as possible.Since alloy is in fusion process, inevitably the problems such as generation volatilization, oxidation, air-breathing,
Therefore it casts each time, certain variation can all occur for the ingredient of alloy, influence the metallurgical quality and casting character of alloy.Alloy
The reuse performance of degradation problem and alloy itself during reuse has substantial connection.The conjunction of present patent application protection
For gold due to having carried out performance optimization, the fusing point of alloy is relatively low(820-850 degree), chance that molten metal and casting mold react
With degree smaller, and the anti-air-breathing oxidability of alloy is stronger, and the degree of purity of molten metal improves, and improves the reuse of alloy
Energy.The appearance profile that the alloy casts jewelry piece after 5 reuses is clear, and any surface finish illustrates to close without apparent blackspot or discoloration
The reuse of gold is functional.Thus, the industrialization of the material can not only improve yield rate, can also be big by multiple reuse
It is big to reduce production cost.
(4)The advantages that alloy flowability is good, and filling performance is favourable, shrinkage cavity formability is small, and molten metal is inspiratory small.It
The thin-section casting of high dimensional accuracy and low surface roughness can be produced, it is 1mm's that die casting wall thickness, which can reach minimum wall thickness (MINI W.),
Casting can cast out the aperture of a diameter of 0.3mm or so.In corrosive environment, the protective film of passivation can be formed, this film is in difference
Medium in, since unpolarizing is as a result, to show different corrosion resistances, to strong acid, strong basicity sweat
Corrosion resistance is also relatively stablized.Alloy corrosion rate under maritime environment is 1.510-4Mm/, thus use the material system
Standby jewellery, which use under relevant environment in 4, does not all have apparent corrosion phenomenon.And traditional seedling silver jewellery is using 4
It will there is a phenomenon where apparent sulfide stainings after month.It is contemplated that the implementation and industrialization of the material will obtain it is excellent
Economic benefit and social benefit.
Specific implementation mode
Embodiment 1
A kind of no nickel and the corrosion-resistant jewellery seedling silver alloy for having excellent die casting performance.By weight percentage, the group of alloy
As P:0.5wt.%,Bi:3.0wt.%,Sn:4.0wt.%,Te:0.4wt.%,Al:2.0wt.%,Fe:5.0wt.%,Ag:
40.0wt.%, surplus are copper.A kind of above-mentioned no nickel and the corrosion-resistant jewellery seedling silver alloy for having excellent die casting performance, including such as
Lower step:As above the raw material matched is added in the electric induction furnace under ar gas environment, and uses graphite crucible;When melting
1400 degree keep the temperature 10 minutes, uniform by Efco-Northrup furnace electromagnetic agitation;1 minute being kept the temperature at 1400 degree after stirring evenly and being poured cast out
Stove;Alloy casting uses the punching block of diameter 20-30mm, and is cooled down by the way of water cooling.By the ingot casting of gained at room temperature into
Row rolling, it is 20-30% that every time, which rolls lower amount,;It is 400 degree per intermediate anneal temperature after rolling twice, keeps the temperature 0.5 hour;Finally
Material is rolled into the alloy sheets that thickness is 10-20mm;In jewellery forming process, needs to carry out vacuum annealing process, eliminate
Stress in process;Wherein, temperature is 420 degree, and the time is 0.4 hour.
The advantages that alloy flowability is good, and filling performance is favourable, shrinkage cavity formability is small, and molten metal is inspiratory small.It can
To produce the thin-section casting of high dimensional accuracy and low surface roughness, die casting wall thickness can reach the casting that minimum wall thickness (MINI W.) is 1mm
Part can cast out the aperture of a diameter of 0.3mm or so.In corrosive environment, the protective film of passivation can be formed, this film is different
In medium, since unpolarizing is as a result, to show different corrosion resistances, strong acid, strong basicity sweat are resisted
Corrosivity is also relatively stablized.It is used in 4 under relevant environment using the jewellery of the material preparation and is all sent out without apparent corrosion phenomenon
It is raw.And traditional seedling silver jewellery will there is a phenomenon where apparent sulfide stainings after using 4 months.
Embodiment 2
A kind of no nickel and the corrosion-resistant jewellery seedling silver alloy for having excellent die casting performance.By weight percentage, the group of alloy
As P:0.8wt.%,Bi:3.5wt.%,Sn:5.0wt.%,Te:0.6wt.%,Al:3.5wt.%,Fe:8.0wt.%,Ag:
50.0wt.%, surplus are copper.A kind of above-mentioned no nickel and the corrosion-resistant jewellery seedling silver alloy for having excellent die casting performance, including such as
Lower step:As above the raw material matched is added in the electric induction furnace under ar gas environment, and uses graphite crucible;When melting
1400 degree keep the temperature 10 minutes, uniform by Efco-Northrup furnace electromagnetic agitation;1 minute being kept the temperature at 1400 degree after stirring evenly and being poured cast out
Stove;Alloy casting uses the punching block of diameter 20-30mm, and is cooled down by the way of water cooling.By the ingot casting of gained at room temperature into
Row rolling, it is 20-30% that every time, which rolls lower amount,;It is 400 degree per intermediate anneal temperature after rolling twice, keeps the temperature 0.5 hour;Finally
Material is rolled into the alloy sheets that thickness is 10-20mm;In jewellery forming process, needs to carry out vacuum annealing process, eliminate
Stress in process;Wherein, temperature is 420 degree, and the time is 0.4 hour.
The advantages that alloy flowability is good, and filling performance is favourable, shrinkage cavity formability is small, and molten metal is inspiratory small.It can
To produce the thin-section casting of high dimensional accuracy and low surface roughness, die casting wall thickness can reach the casting that minimum wall thickness (MINI W.) is 1mm
Part can cast out the aperture of a diameter of 0.3mm or so.In corrosive environment, the protective film of passivation can be formed, this film is different
In medium, since unpolarizing is as a result, to show different corrosion resistances, strong acid, strong basicity sweat are resisted
Corrosivity is also relatively stablized.It is used in 4 under relevant environment using the jewellery of the material preparation and is all sent out without apparent corrosion phenomenon
It is raw.And traditional seedling silver jewellery will there is a phenomenon where apparent sulfide stainings after using 4 months.
Embodiment 3
A kind of no nickel and the corrosion-resistant jewellery seedling silver alloy for having excellent die casting performance.By weight percentage, the group of alloy
As P:0.6wt.%,Bi:3.2wt.%,Sn:4.5wt.%,Te:0.5wt.%,Al:2.8wt.%,Fe:5.8wt.%,Ag:
42.0wt.%, surplus are copper.A kind of above-mentioned no nickel and the corrosion-resistant jewellery seedling silver alloy for having excellent die casting performance, including such as
Lower step:As above the raw material matched is added in the electric induction furnace under ar gas environment, and uses graphite crucible;When melting
1400 degree keep the temperature 10 minutes, uniform by Efco-Northrup furnace electromagnetic agitation;1 minute being kept the temperature at 1400 degree after stirring evenly and being poured cast out
Stove;Alloy casting uses the punching block of diameter 20-30mm, and is cooled down by the way of water cooling.By the ingot casting of gained at room temperature into
Row rolling, it is 20-30% that every time, which rolls lower amount,;It is 400 degree per intermediate anneal temperature after rolling twice, keeps the temperature 0.5 hour;Finally
Material is rolled into the alloy sheets that thickness is 10-20mm;In jewellery forming process, needs to carry out vacuum annealing process, eliminate
Stress in process;Wherein, temperature is 420 degree, and the time is 0.4 hour.
The advantages that alloy flowability is good, and filling performance is favourable, shrinkage cavity formability is small, and molten metal is inspiratory small.It can
To produce the thin-section casting of high dimensional accuracy and low surface roughness, die casting wall thickness can reach the casting that minimum wall thickness (MINI W.) is 1mm
Part can cast out the aperture of a diameter of 0.3mm or so.In corrosive environment, the protective film of passivation can be formed, this film is different
In medium, since unpolarizing is as a result, to show different corrosion resistances, strong acid, strong basicity sweat are resisted
Corrosivity is also relatively stablized.It is used in 4 under relevant environment using the jewellery of the material preparation and is all sent out without apparent corrosion phenomenon
It is raw.And traditional seedling silver jewellery will there is a phenomenon where apparent sulfide stainings after using 4 months.
Claims (3)
1. a kind of no nickel and the corrosion-resistant jewellery seedling silver alloy for having excellent die casting performance;By weight percentage, alloy
Group becomes P:0.5-0.8wt.%,Bi:3.0-3.5wt.%,Sn:4.0-5.0wt.%,Te:0.4-0.6wt.%,Al:2.0-
3.5wt.%,Fe:5.0-8.0wt.%,Ag:40.0-50.0wt.%, surplus are copper.
2. a kind of no nickel and have the corrosion-resistant jewellery seedling silver alloy of excellent die casting performance according to claim 1, it is special
Sign is to include following smelting step:As above the raw material matched is added in the electric induction furnace under ar gas environment, and uses stone
Black crucible;10 minutes are kept the temperature at 1400 degree when melting, it is uniform by Efco-Northrup furnace electromagnetic agitation;It is protected at 1400 degree after stirring evenly
Temperature 1 minute and cast come out of the stove;Alloy casting uses the punching block of diameter 20-30mm, and is cooled down by the way of water cooling.
3. a kind of no nickel and have the corrosion-resistant jewellery seedling silver alloy of excellent die casting performance according to claim 1, it is special
Sign is to use step comprising following:The ingot casting of gained is rolled at room temperature, it is 20-30% that every time, which rolls lower amount,;Every two
Intermediate anneal temperature is 400 degree after secondary rolling, keeps the temperature 0.5 hour;Material is finally rolled into the alloy that thickness is 10-20mm
Plate;In jewellery forming process, needs to carry out vacuum annealing process, eliminate the stress in process;Wherein, temperature 420
Degree, time are 0.4 hour.