CN108789187A - A kind of bronze base diamond grinding wheel and preparation method thereof - Google Patents
A kind of bronze base diamond grinding wheel and preparation method thereof Download PDFInfo
- Publication number
- CN108789187A CN108789187A CN201810749042.3A CN201810749042A CN108789187A CN 108789187 A CN108789187 A CN 108789187A CN 201810749042 A CN201810749042 A CN 201810749042A CN 108789187 A CN108789187 A CN 108789187A
- Authority
- CN
- China
- Prior art keywords
- mixture
- grinding wheel
- abrasive material
- powder
- abrasive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of bronze base diamond grinding wheel and preparation method thereof, is related to super hard abrasive field;Grinding wheel includes steel core, abrasive material circle, and steel core and abrasive material circle are combined by resin glue caking agent, and abrasive material circle is prepared by diamond abrasive, metallic bond and additional adhesive;Metallic bond contains Cu60Sn40 powder and Ti powder;Abrasive material circle forms:Diamond abrasive, metallic bond and hole;Preparation method:1) diamond abrasive, Cu60Sn40 powder and Ti powder are uniformly mixed, obtain mixture A;2) additional adhesive is uniformly mixed with mixture A, obtains mixture B;3) mixture B is dried;4) by the mixture B sievings after drying;5) by the mixture B after sieving, cold moudling;6) by abrasive material circle green compact, it is sintered postcooling under inert gas atmosphere, obtains abrasive material circle green body;7) resin glue caking agent is used, abrasive material circle green body and steel core are bonded, bronze base diamond grinding wheel is made.
Description
Technical field
The present invention relates to super hard abrasive fields, and in particular to a kind of bronze base diamond grinding wheel and preparation method thereof.
Background technology
With modern mechanical processing towards high-precision, at high speed, hard processing, dry processing (no coolant liquid) and reduce cost etc.
Direction is developed, and quite high requirement is proposed to grinding tool performance.Traditional silicon carbide and corundum conventional abrasive material mold cannot be complete
The current high speed of full up foot, efficient, high-precision grinding requirement, therefore various excellent wear-resisting properties are developed, it can carry out for a long time steady
Surely the superhard removing material processed is inevitable development trend.Currently used superhard removing material includes diamond and cube nitrogen
Change two kinds of abrasive materials of boron.Diamond is most hard material and wearability is extremely strong, is suitable for high-speed grinding and superfine grinding.Buddha's warrior attendant
Stone sand wheel is highly suitable for grinding material such as non-ferric metal alkyl materials, carbide, glass, pottery harder, frangible, that abrasive dust is shorter
Porcelain, quartz ware and semiconductor and chip material.The grinding efficiency of diamond super-hard abrasive tool (grinding wheel), machining accuracy and wear-resisting
Property etc. performances be High-speed & Precision Grinding processing in critical issue.
The bonding agent that fixed grain is used in super-hard abrasive tool is the key factor for influencing super-hard abrasive tool performance.Traditional is super
Hard grind tool (grinding wheel) mostly uses the techniques manufactures such as resin, ceramics, metallic bond sintering and plating, the problem is that monocrystalline
Grain is only embedded in by machinery embedding in bonding agent and electroplated layer, weaker with bonding agent and electroplated layer intermolecular forces.It is specific next
It says, although resinoid bond is easier processing and modifies, but poor heat resistance, and bond strength is low, and abrasive material falls off seriously, serious shadow
Ring efficiency;Vitrified bond finishing is relatively easy, and temperature in use is high, however brittleness is big, and toughness and fatigability are poor, Yi Fa
Raw embrittlement, it is difficult to be used for High-speed machining.Although it is strong that metallic bond is sintered heat resistance, usually between bonding agent and abrasive grain not
Enhanced primary treatment can be generated, thus abrasive grain is only embedded in by machinery embedding in bonding agent, hold is limited;In metal plating
Abrasive grain is also only mechanically embedded.Therefore it is easy to lead to the entirety of grinding wheel because abrasive material falls off in particle and to remove in flakes with coating
Failure, such situation are especially apparent in more unmanageable material high efficient grinding;In addition, plating thickness, abrasive material proud exposure
Low, chip space is small, and when grinding is easy to fail because the adherency of chip blocks.
Invention content
To solve the above-mentioned problems, the present invention provides a kind of bronze base diamond grinding wheel and preparation method thereof, the grinding wheels
It is a kind of skive that can be born during high-speed grinding compared with big load, while there is outstanding impact resistance and good
Shape retention, specific technical solution is as follows:
A kind of bronze base diamond grinding wheel of the present invention comprising steel core, abrasive material circle, steel core and abrasive material circle pass through resin glue
Binder combines, wherein abrasive material circle is prepared from the following components by mass percentage:Diamond abrasive:35~60%, metal
Bonding agent:40~60%, additional adhesive:10~30%, diamond abrasive, metallic bond and additional adhesive quality percentage
Than the sum of be 100%;The mass percent that the metallic bond contains ingredient is:Cu60Sn40 powder:40~70%, Ti
Powder:The sum of 35~65%, Cu60Sn40 powder and Ti powder mass percents are 100%;Abrasive material circle is formed by percent by volume:Gold
Hard rock abrasive material 15~50%, metallic bond 10~45%, hole 20~45%, diamond abrasive, metallic bond and hole
The sum of percent by volume be 100%.
The particle size range of the Cu60Sn40 powder and Ti powder is 30~350 μm.
The additional adhesive is acrylic emulsion.
A kind of preparation method of bronze base diamond grinding wheel of the present invention, includes the following steps:
Step 1, batch mixing:
By a kind of composition proportion of bronze base diamond grinding wheel, diamond abrasive, Cu60Sn40 powder and Ti powder are mixed equal
It is even, mixture A is made;
Step 2, batch mixing:
By a kind of composition proportion of bronze base diamond grinding wheel, additional adhesive is uniformly mixed with mixture A, is made mixed
Close material B;
Step 3, it dries:
Mixture B is heated to 50~150 DEG C, is dried in mass ratio, the mixture B after drying:Mixing before drying
Expect B=80~95%;
Step 4, it is sieved:
By the mixture B sievings after drying, it is 20~300 mesh to cross grit number;
Step 5, it is molded:
By the mixture B after sieving, uniformly putting into mold, cold moudling, pressure is 40~200MPa, pressurize 20~
Abrasive material circle green compact are made in 120min;
Step 6, it is sintered:
(1) it by abrasive material circle green compact, is sintered under inert gas atmosphere, with the heating rate of 3~10 DEG C/min, from room temperature liter
Temperature is to 800~1050 DEG C of sintering temperature, 10~150min of sintering time;
(2) sintering postcooling is extremely come out of the stove for≤40 DEG C, and abrasive material circle green body is made;
Step 7, it bonds:
With resin glue caking agent, abrasive material circle green body and steel core are bonded, go Burr removal, finishing molding that bronze fund is made
Hard rock grinding wheel.
Above-mentioned a kind of bronze base diamond grinding wheel and preparation method thereof, wherein:
In the step 1, incorporation time is 2~8h.
It in the step 2, stirs by mixing, mixing time is 1~6h.
In the step 3, drying soaking time is 1~3h.
In the step 4, it is sieved 2~8 times.
In the step 5, cold moudling uses hydraulic press.
In the step 6, inert gas is argon gas.
A kind of bronze base diamond grinding wheel of the present invention and preparation method thereof, compared with prior art, has the beneficial effect that:
(1) there is bronze base diamond grinding wheel of the invention fabulous thermal conductivity can quickly reduce grinding workpiece surface
Temperature improve grinding speed to reduce power attenuation;Additional adhesive in formula is conducive to the formation of product hole,
The space for accommodating the abrasive grain to fall off can effectively be increased, the utilization of abrasive material is more abundant, while metallic bond has extremely strong handle
Holding force;Grinding wheel has the characteristics that grinding efficiency is high, grinding temperature is low, power attenuation is low, good processing accuracy, service life are long.
(2) preparation method provided by the invention, since sintering time is short, the characteristic of abrasive material is not damaged, sintering temperature
Degree, metallic bond, porosity and the control of time make grinding wheel have good thermal conductivity and larger appearance during the work time
Receive the space of metal fillings and abrasive material, be not easy to block during high-speed grinding, grinding is sharp, and grinding accuracy is high, and with from
Sharp property.
Specific implementation mode
With reference to specific implementation case, the invention will be further described, but the invention is not limited in these to implement
Example.
In following embodiment, inert gas is argon gas.
Embodiment 1
A kind of bronze base diamond grinding wheel comprising steel core, abrasive material circle, steel core and abrasive material circle pass through resin glue caking agent knot
It closes, wherein abrasive material circle is prepared from the following components by mass percentage:Diamond abrasive:40%, metallic bond:45%,
Additional adhesive:15%, the sum of diamond abrasive, metallic bond and additional adhesive mass percent are 100%;Described
The mass percent that metallic bond contains ingredient is:Cu60Sn40 powder:50%, Ti powder:50%, Cu60Sn40 powder and Ti silty
It is 100% to measure the sum of percentage;Abrasive material circle is formed by percent by volume:Diamond abrasive 35%, metallic bond 38%, hole
Gap 27%, diamond abrasive, metallic bond and hole the sum of percent by volume be 100%;The diamond abrasive,
The grain size of Cu60Sn40 powder and Ti powder is 50 μm;The additional adhesive is acrylic emulsion.
The preparation method of above-mentioned skive, includes the following steps:
Step 1, batch mixing:
By a kind of composition proportion of skive, diamond abrasive, Cu60Sn40 powder and Ti powder are uniformly mixed, mixed
Time is 1h, and mixture A is made;
Step 2, batch mixing:
By a kind of composition proportion of skive, additional adhesive is mixed with mixture A and is stirred by mixing,
Mixing time is 1h, and mixture B is made;
Step 3, it dries:
Mixture B is heated to 75 DEG C, drying soaking time is 1h, in mass ratio, the mixture B after drying:Before drying
Mixture B=92%;
Step 4, it is sieved:
By the mixture B sievings after drying, it is 100 mesh to cross grit number, is sieved 3 times;
Step 5, it is molded:
It uniformly puts into mold, the mixture B after sieving using hydraulic press cold moudling, pressure 75MPa, pressurize
Abrasive material circle green compact are made in 40min;
Step 6, it is sintered:
(1) it by abrasive material circle green compact, is sintered under inert gas atmosphere, with the heating rate of 10 DEG C/min, from room temperature
To 960 DEG C of sintering temperature, sintering time 30min;
(2) sintering postcooling is extremely come out of the stove for≤40 DEG C, and abrasive material circle green body is made;
Step 7, it bonds:
With resin glue caking agent, abrasive material circle green body and steel core are bonded, go Burr removal, finishing molding that bronze fund is made
Hard rock grinding wheel.
Embodiment 2
A kind of bronze base diamond grinding wheel comprising steel core, abrasive material circle, steel core and abrasive material circle pass through resin glue caking agent knot
It closes, wherein abrasive material circle is prepared from the following components by mass percentage:Diamond abrasive:40%, metallic bond:40%,
Additional adhesive:20%, the sum of diamond abrasive, metallic bond and additional adhesive mass percent are 100%;Described
The mass percent that metallic bond contains ingredient is:Cu60Sn40 powder:55%, Ti powder:45%, Cu60Sn40 powder and Ti silty
It is 100% to measure the sum of percentage;Abrasive material circle is formed by percent by volume:Diamond abrasive 37%, metallic bond 32%, hole
Gap 31%, diamond abrasive, metallic bond and hole the sum of percent by volume be 100%;The diamond abrasive,
The grain size of Cu60Sn40 powder and Ti powder is 100 μm;The additional adhesive is acrylic emulsion.
The preparation method of above-mentioned skive, includes the following steps:
Step 1, batch mixing:
By a kind of composition proportion of skive, diamond abrasive, Cu60Sn40 powder and Ti powder are uniformly mixed, mixed
Time is 1h, and mixture A is made;
Step 2, batch mixing:
By a kind of composition proportion of skive, additional adhesive is mixed with mixture A and is stirred by mixing,
Mixing time is 1h, and mixture B is made;
Step 3, it dries:
Mixture B is heated to 75 DEG C, drying soaking time is 1h, in mass ratio, the mixture B after drying:Before drying
Mixture B=92%;
Step 4, it is sieved:
By the mixture B sievings after drying, it is 100 mesh to cross grit number, is sieved 3 times;
Step 5, it is molded:
It uniformly puts into mold, the mixture B after sieving using hydraulic press cold moudling, pressure 75MPa, pressurize
Abrasive material circle green compact are made in 40min;
Step 6, it is sintered:
(1) it by abrasive material circle green compact, is sintered under inert gas atmosphere, with the heating rate of 10 DEG C/min, from room temperature
To 960 DEG C of sintering temperature, sintering time 30min;
(2) sintering postcooling is extremely come out of the stove for≤40 DEG C, and abrasive material circle green body is made;
Step 7, it bonds:
With resin glue caking agent, abrasive material circle green body and steel core are bonded, go Burr removal, finishing molding that bronze fund is made
Hard rock grinding wheel.
Embodiment 3
A kind of bronze base diamond grinding wheel comprising steel core, abrasive material circle, steel core and abrasive material circle pass through resin glue caking agent knot
It closes, wherein abrasive material circle is prepared from the following components by mass percentage:Diamond abrasive:35%, metallic bond:42%,
Additional adhesive:23%, the sum of diamond abrasive, metallic bond and additional adhesive mass percent are 100%;Described
The mass percent that metallic bond contains ingredient is:Cu60Sn40 powder:60%, Ti powder:40%, Cu60Sn40 powder and Ti silty
It is 100% to measure the sum of percentage;Abrasive material circle is formed by percent by volume:Diamond abrasive 35%, metallic bond 30%, hole
Gap 35%, diamond abrasive, metallic bond and hole the sum of percent by volume be 100%;The diamond abrasive,
The grain size of Cu60Sn40 powder and Ti powder is 150 μm;The additional adhesive is acrylic emulsion.
The preparation method of above-mentioned skive, includes the following steps:
Step 1, batch mixing:
By a kind of composition proportion of skive, diamond abrasive, Cu60Sn40 powder and Ti powder are uniformly mixed, mixed
Time is 1h, and mixture A is made;
Step 2, batch mixing:
By a kind of composition proportion of skive, additional adhesive is mixed with mixture A and is stirred by mixing,
Mixing time is 1h, and mixture B is made;
Step 3, it dries:
Mixture B is heated to 75 DEG C, drying soaking time is 1h, in mass ratio, the mixture B after drying:Before drying
Mixture B=92%;
Step 4, it is sieved:
By the mixture B sievings after drying, it is 100 mesh to cross grit number, is sieved 3 times;
Step 5, it is molded:
It uniformly puts into mold, the mixture B after sieving using hydraulic press cold moudling, pressure 75MPa, pressurize
Abrasive material circle green compact are made in 40min;
Step 6, it is sintered:
(1) it by abrasive material circle green compact, is sintered under inert gas atmosphere, with the heating rate of 10 DEG C/min, from room temperature
To 960 DEG C of sintering temperature, sintering time 30min;
(2) sintering postcooling is extremely come out of the stove for≤40 DEG C, and abrasive material circle green body is made;
Step 7, it bonds:
With resin glue caking agent, abrasive material circle green body and steel core are bonded, go Burr removal, finishing molding that bronze fund is made
Hard rock grinding wheel.
Embodiment 4
A kind of bronze base diamond grinding wheel comprising steel core, abrasive material circle, steel core and abrasive material circle pass through resin glue caking agent knot
It closes, wherein abrasive material circle is prepared from the following components by mass percentage:Diamond abrasive:35%, metallic bond:40%,
Additional adhesive:25%, the sum of diamond abrasive, metallic bond and additional adhesive mass percent are 100%;Described
The mass percent that metallic bond contains ingredient is:Cu60Sn40 powder:60%, Ti powder:40%, Cu60Sn40 powder and Ti silty
It is 100% to measure the sum of percentage;Abrasive material circle is formed by percent by volume:Diamond abrasive 35%, metallic bond 28%, hole
Gap 37%, diamond abrasive, metallic bond and hole the sum of percent by volume be 100%;The diamond abrasive,
The grain size of Cu60Sn40 powder and Ti powder is 200 μm;The additional adhesive is acrylic emulsion.
The preparation method of above-mentioned skive, includes the following steps:
Step 1, batch mixing:
By a kind of composition proportion of skive, diamond abrasive, Cu60Sn40 powder and Ti powder are uniformly mixed, mixed
Time is 1h, and mixture A is made;
Step 2, batch mixing:
By a kind of composition proportion of skive, additional adhesive is mixed with mixture A and is stirred by mixing,
Mixing time is 1h, and mixture B is made;
Step 3, it dries:
Mixture B is heated to 75 DEG C, drying soaking time is 1h, in mass ratio, the mixture B after drying:Before drying
Mixture B=92%;
Step 4, it is sieved:
By the mixture B sievings after drying, it is 100 mesh to cross grit number, is sieved 3 times;
Step 5, it is molded:
It uniformly puts into mold, the mixture B after sieving using hydraulic press cold moudling, pressure 75MPa, pressurize
Abrasive material circle green compact are made in 40min;
Step 6, it is sintered:
(1) it by abrasive material circle green compact, is sintered under inert gas atmosphere, with the heating rate of 10 DEG C/min, from room temperature
To 960 DEG C of sintering temperature, sintering time 30min;
(2) sintering postcooling is extremely come out of the stove for≤40 DEG C, and abrasive material circle green body is made;
Step 7, it bonds:
With resin glue caking agent, abrasive material circle green body and steel core are bonded, go Burr removal, finishing molding that bronze fund is made
Hard rock grinding wheel.
Embodiment 5
A kind of bronze base diamond grinding wheel comprising steel core, abrasive material circle, steel core and abrasive material circle pass through resin glue caking agent knot
It closes, wherein abrasive material circle is prepared from the following components by mass percentage:Diamond abrasive:45%, metallic bond:45%,
Additional adhesive:10%, the sum of diamond abrasive, metallic bond and additional adhesive mass percent are 100%;Described
The mass percent that metallic bond contains ingredient is:Cu60Sn40 powder:50%, Ti powder:50%, Cu60Sn40 powder and Ti silty
It is 100% to measure the sum of percentage;Abrasive material circle is formed by percent by volume:Diamond abrasive 42%, metallic bond 38%, hole
Gap 24%, diamond abrasive, metallic bond and hole the sum of percent by volume be 100%;The diamond abrasive,
The grain size of Cu60Sn40 powder and Ti powder is 200 μm;The additional adhesive is acrylic emulsion.
The preparation method of above-mentioned skive, includes the following steps:
Step 1, batch mixing:
By a kind of composition proportion of skive, diamond abrasive, Cu60Sn40 powder and Ti powder are uniformly mixed, mixed
Time is 1h, and mixture A is made;
Step 2, batch mixing:
By a kind of composition proportion of skive, additional adhesive is mixed with mixture A and is stirred by mixing,
Mixing time is 1h, and mixture B is made;
Step 3, it dries:
Mixture B is heated to 75 DEG C, drying soaking time is 1h, in mass ratio, the mixture B after drying:Before drying
Mixture B=92%;
Step 4, it is sieved:
By the mixture B sievings after drying, it is 100 mesh to cross grit number, is sieved 3 times;
Step 5, it is molded:
It uniformly puts into mold, the mixture B after sieving using hydraulic press cold moudling, pressure 75MPa, pressurize
Abrasive material circle green compact are made in 40min;
Step 6, it is sintered:
(1) it by abrasive material circle green compact, is sintered under inert gas atmosphere, with the heating rate of 10 DEG C/min, from room temperature
To 960 DEG C of sintering temperature, sintering time 30min;
(2) sintering postcooling is extremely come out of the stove for≤40 DEG C, and abrasive material circle green body is made;
Step 7, it bonds:
With resin glue caking agent, abrasive material circle green body and steel core are bonded, go Burr removal, finishing molding that bronze fund is made
Hard rock grinding wheel.
Claims (7)
1. a kind of bronze base diamond grinding wheel, which is characterized in that grinding wheel includes steel core, abrasive material circle, and steel core and abrasive material circle pass through tree
Fat glue caking agent combines, wherein abrasive material circle is prepared from the following components by mass percentage:Diamond abrasive:35~60%,
Metallic bond:40~60%, additional adhesive:10~30%, diamond abrasive, metallic bond and additional adhesive quality
The sum of percentage is 100%;The mass percent that the metallic bond contains ingredient is:Cu60Sn40 powder:40~70%,
Ti powder:The sum of 35~65%, Cu60Sn40 powder and Ti powder mass percents are 100%;Abrasive material circle is formed by percent by volume:
Diamond abrasive 15~50%, metallic bond 10~45%, hole 20~45%, diamond abrasive, metallic bond and hole
The sum of percent by volume of gap is 100%.
2. a kind of bronze base diamond grinding wheel according to claim 1, which is characterized in that the Cu60Sn40 powder described in grinding wheel
Particle size range with Ti powder is 30~350 μm.
3. a kind of bronze base diamond grinding wheel according to claim 1, which is characterized in that the additional adhesive is third
Olefin(e) acid lotion.
4. a kind of preparation method of bronze base diamond grinding wheel described in claim 1, which is characterized in that include the following steps:
Step 1, batch mixing:
By a kind of composition proportion of bronze base diamond grinding wheel, diamond abrasive, Cu60Sn40 powder and Ti powder are uniformly mixed, made
Obtain mixture A;
Step 2, batch mixing:
By a kind of composition proportion of bronze base diamond grinding wheel, additional adhesive is uniformly mixed with mixture A, mixture is made
B:
Step 3, it dries:
Mixture B is heated to 50~150 DEG C, is dried in mass ratio, the mixture B after drying:Mixture B=before drying
80~95%;
Step 4, it is sieved:
By the mixture B sievings after drying, it is 20~300 mesh to cross grit number;
Step 5, it is molded:
By the mixture B after sieving, uniformly putting into mold, cold moudling, pressure is 40~200MPa, pressurize 20~
Abrasive material circle green compact are made in 120min;
Step 6, it is sintered:
(1) by abrasive material circle green compact, be sintered under inert gas atmosphere, with the heating rate of 3~10 DEG C/min, from room temperature to
800~1050 DEG C of sintering temperature, 10~150min of sintering time;
(2) sintering postcooling is extremely come out of the stove for≤40 DEG C, and abrasive material circle green body is made;
Step 7, it bonds:
With resin glue caking agent, abrasive material circle green body and steel core are bonded, go Burr removal, finishing molding that bronze base diamond is made
Grinding wheel.
5. a kind of preparation method of bronze base diamond grinding wheel according to claim 4, which is characterized in that the step 1
In, incorporation time is 2~8h.
6. a kind of preparation method of bronze base diamond grinding wheel according to claim 4, which is characterized in that the step 2
In, it stirs by mixing, mixing time is 1~6h.
7. a kind of preparation method of bronze base diamond grinding wheel according to claim 4, which is characterized in that the step 3
In, drying soaking time is 1~3h.