CN108774523A - A kind of red germanic acid magnesium barium fluorescent powder of novel display - Google Patents
A kind of red germanic acid magnesium barium fluorescent powder of novel display Download PDFInfo
- Publication number
- CN108774523A CN108774523A CN201810736648.3A CN201810736648A CN108774523A CN 108774523 A CN108774523 A CN 108774523A CN 201810736648 A CN201810736648 A CN 201810736648A CN 108774523 A CN108774523 A CN 108774523A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- weight
- red
- fluorescent powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of red germanic acid magnesium barium fluorescent powders of novel display, are made of component A, component B and component C, are made of parts by weight meter, component A is:Ba(2‑x)MgGe2O7:Eu3+x, 0 < x < 1, parts by weight are 5-10 parts;Component B is:Sb2O31-2.4 part, CaF22.5-4 part, BaOAl2O34.5-7 part, SrCO30.8-1.5 parts;Component C is:M1aScbM2cNdCe:XCe, wherein M1 be selected from thulium Y, La, Gd, Lu it is one or more, M2 be selected from Si, Al, Ga, B element it is one or more;Also, 0 < a < 2,0 < b < 2,3≤c≤5,5≤d<7,0≤e≤2,0 x≤0.2 <, parts by weight are 0.5-0.8 parts.The present invention can roast to obtain required fluorescent powder at a lower temperature, and the grain size of gained fluorescent powder is very small, and its pattern can be different by regulating and controlling different fused salt types.
Description
Technical field
The invention belongs to rare earth luminescent material fields, and in particular to a kind of red germanic acid magnesium barium fluorescent powder of novel display.
Background technology
Currently, realizing that the main path of white light LEDs is with blue light (440-470nm) LED chip excitated fluorescent powder complex group
At white light.There are two types of common combination sides:First, blue-light LED chip and yellow fluorescent powder combination;Secondly being blue-light LED chip
It is combined with red, green emitting phosphor.Wherein, garnet structure yellow fluorescent powder (YAG) matching blue-light LED chip because its efficiently,
It makes the advantages that simple and is widely used, but since spectrum poor continuity, red light portion lack, cause white light LED part
Colour rendering index is relatively low, colour temperature is higher, it is difficult to meet high-quality lighting demand.Therefore, on this basis by add rouge and powder or
High color rendering index (CRI) white light is obtained by the way of, green emitting phosphor excitated red using blue chip.
In recent years, as the increasingly raising of people's living standard and semiconductor illumination technique are constantly progressive, people are to strong
The concern consciousness enhancing of health and quality life, the requirement to illumination have been increasingly turned to from simple environmental protection and energy saving comfortable to health
Pursuit.Tradition is composed White LED by blue LED die and other color fluorescence bodies, and it is unbalanced that there are emission wavelengths, green
The shortcomings of coloured light excalation, the peak strength for being particularly present blue light is higher, easily causes physiology, psychology of people etc.
The problem of, it is difficult to meet the needs of people are to health.Therefore, researcher propose to be applied in combination in purple LED chip red (R),
The White LED of green (G), blue (B) fluorophor, compared with blue chip, this method purple light conversion of white light is more efficient, light
Spectral structure is balanced, and colour rendering index is relatively more preferable, but the chemistry and thermal stability etc. to fluorescent powder is put forward higher requirements, urgently
Suitable high density energy excitation to be developed, meet full spectrum high-quality illumination, suitable for purple or it is near ultraviolet excitated it is novel it is blue,
Green, red fluorescence powder.
Invention content
The purpose of the present invention is to provide a kind of red germanic acid magnesium barium fluorescent powders of novel display.
The purpose of the present invention can be achieved through the following technical solutions:
A kind of red germanic acid magnesium barium fluorescent powder of novel display, is made of component A, component B and component C, by parts by weight meter
Composition, component A are:Ba(2-x)MgGe2O7:Eu3+x, 0 < x < 1, parts by weight are 5-10 parts;Component B is:Sb2O3 1-
2.4 parts, CaF22.5-4 part, BaOAl2O34.5-7 part, SrCO30.8-1.5 parts;Component C is:M1aScbM2cNdCe:XCe,
Wherein M1 is selected from the one or more of thulium Y, La, Gd, Lu, and M2 is selected from one kind or more of Si, Al, Ga, B element
Kind;Also, 0 < a < 2,0 < b < 2,3≤c≤5,5≤d<7,0≤e≤2,0 x≤0.2 <, parts by weight are 0.5-0.8 parts.
Preferably, the red germanic acid magnesium barium fluorescent powder of a kind of novel display, by component A, component B and component C groups
At being made of parts by weight meter, component A is:Ba(2-x)MgGe2O7:Eu3+x, 0 < x < 1, parts by weight are 5 parts;Component B is:
Sb2O31 part, CaF23 parts, BaOAl2O35 parts, SrCO31 part;Component C is:M1aScbM2cNdCe:XCe, wherein M1 are selected from dilute
Earth metal element Y, La, Gd, Lu's is one or more, M2 be selected from Si, Al, Ga, B element it is one or more;Also, 0 < a <
2,0 < b < 2,3≤c≤5,5≤d<7,0≤e≤2,0 x≤0.2 <, parts by weight are 0.5 part.
Preferably, the red germanic acid magnesium barium fluorescent powder of a kind of novel display, by component A, component B and component C groups
At being made of parts by weight meter, component A is:Ba(2-x)MgGe2O7:Eu 3+x, 0 < x < 1, parts by weight are 8 parts;Component B
For:Sb2O32 parts, CaF23 parts, BaOAl2O35 parts, SrCO31 part;Component C is:M1aScbM2cNdCe:XCe, wherein M1 are selected
From the one or more of thulium Y, La, Gd, Lu, M2 be selected from Si, Al, Ga, B element it is one or more;Also, 0
< a < 2,0 < b < 2,3≤c≤5,5≤d<7,0≤e≤2,0 x≤0.2 <, parts by weight are 0.6 part.
Beneficial effects of the present invention:The outer surface waterproof material of the present invention protects liquid crystal display well, prevents family
Outer liquid crystal display is for a long time by the erosion of rainwater and fog.
Specific implementation mode
With reference to specific embodiment, present invention is further described in detail.
Embodiment 1:
A kind of red germanic acid magnesium barium fluorescent powder of novel display, is prepared from the following raw materials in parts by weight:By component A,
Component B and component C compositions, are made of, component A is parts by weight meter:Ba(2-x)MgGe 2O7:Eu3+x, 0 < x < 1, parts by weight
It is 5 parts;Component B is:Sb2O31 part, CaF22.5 parts, BaOAl2O34.5 parts, SrCO30.8 part;Component C is:
M1aScbM2cNdCe:XCe, wherein M1 are selected from the one or more of thulium Y, La, Gd, Lu, and M2 is selected from Si;Also, a
=1, b=1, c=4, d=6, e=2, x=0.2, parts by weight are 0.5 part.
Embodiment 2:
A kind of red germanic acid magnesium barium fluorescent powder of novel display, is prepared from the following raw materials in parts by weight:By component A,
Component B and component C compositions, are made of, component A is parts by weight meter:Ba(2-x)MgGe2O7:Eu3+x, 0 < x < 1, parts by weight
It is 5 parts;Component B is:Sb2O31 part, CaF23 parts, BaOAl2O35 parts, SrCO31 part;Component C is:M1aScbM2cNdCe:
XCe, wherein M1 are selected from the one or more of rare-earth metals La, and M2 is selected from the one or more of Ga elements;Also, a=
1.5, b=1.5, c=4, d=5, e=2, x=0.2, parts by weight are 0.5 part.
Embodiment 3:
A kind of red germanic acid magnesium barium fluorescent powder of novel display, is prepared from the following raw materials in parts by weight:By component A,
Component B and component C compositions, are made of, component A is parts by weight meter:Ba(2-x)MgGe2O7:Eu3+x, 0 < x < 1, parts by weight
It is 8 parts;Component B is:Sb2O32 parts, CaF23 parts, BaOAl2O35 parts, SrCO31 part;Component C is:M1aScbM2cNdCe:
XCe, wherein M1 are selected from thulium Gd, M2 and are selected from B element;Also, a=0.8, b=1.5, c=3.5, d=5.5, e=
1.5, x=0.1, parts by weight are 0.6 part.
Above content is only citing made for the present invention and explanation, affiliated those skilled in the art are to being retouched
The specific embodiment stated does various modifications or additions or substitutes by a similar method, as long as it does not deviate from the concept of invention
Or beyond the scope defined by this claim, it is within the scope of protection of the invention.
Claims (3)
1. a kind of red germanic acid magnesium barium fluorescent powder of novel display, which is characterized in that it is made of component A, component B and component C, by
Parts by weight meter forms, and component A is:Ba(2-x)MgGe2O7:Eu3+x, 0 < x < 1, parts by weight are 5-10 parts;Component B is:Sb2O3
1-2.4 part, CaF22.5-4 part, BaOAl2O34.5-7 part, SrCO30.8-1.5 parts;Component C is:M1aScbM2cNdCe:
XCe, wherein M1 be selected from thulium Y, La, Gd, Lu it is one or more, M2 be selected from Si, Al, Ga, B element one kind or
It is a variety of;Also, 0 < a < 2,0 < b < 2,3≤c≤5,5≤d<7,0≤e≤2,0 x≤0.2 <, parts by weight 0.5-0.8
Part.
2. a kind of red germanic acid magnesium barium fluorescent powder of novel display according to claim 1, which is characterized in that by component A,
Component B and component C compositions, are made of, component A is parts by weight meter:Ba(2-x)MgGe2O7:Eu3+x, 0 < x < 1, parts by weight 5
Part;Component B is:Sb2O31 part, CaF23 parts, BaOAl2O35 parts, SrCO31 part;Component C is:M1aScbM2cNdCe:XCe,
Wherein M1 is selected from the one or more of thulium Y, La, Gd, Lu, and M2 is selected from one kind or more of Si, Al, Ga, B element
Kind;Also, 0 < a < 2,0 < b < 2,3≤c≤5,5≤d<7,0≤e≤2,0 x≤0.2 <, parts by weight are 0.5 part.
3. a kind of red germanic acid magnesium barium fluorescent powder of novel display according to claim 1, which is characterized in that by component A,
Component B and component C compositions, are made of, component A is parts by weight meter:Ba(2-x)MgGe2O7:Eu3+x, 0 < x < 1, parts by weight 8
Part;Component B is:Sb2O32 parts, CaF23 parts, BaOAl2O35 parts, SrCO31 part;Component C is:M1aScbM2cNdCe:XCe,
Wherein M1 is selected from the one or more of thulium Y, La, Gd, Lu, and M2 is selected from one kind or more of Si, Al, Ga, B element
Kind;Also, 0 < a < 2,0 < b < 2,3≤c≤5,5≤d<7,0≤e≤2,0 x≤0.2 <, parts by weight are 0.6 part.