CN108774357A - A kind of Wines packing transparent box and its production technology - Google Patents
A kind of Wines packing transparent box and its production technology Download PDFInfo
- Publication number
- CN108774357A CN108774357A CN201810662733.XA CN201810662733A CN108774357A CN 108774357 A CN108774357 A CN 108774357A CN 201810662733 A CN201810662733 A CN 201810662733A CN 108774357 A CN108774357 A CN 108774357A
- Authority
- CN
- China
- Prior art keywords
- parts
- bottle
- packing
- plastic
- transparent box
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Wines packing transparent box, are related to box technology field, including each component of following parts by weight is prepared：65-70 parts of polypropylene, 4-5 parts of brightening agent, 10-15 parts of titanium dioxide, 6-8 parts of ultramarine, 3-7 parts of hydroquinone, 5-15 parts of triacetin, 50-90 parts of poly methylene poly phenyl poly isocyanate, 10-18 parts of polyacrylamide, 1-5 parts of stabilizer.The production technology of the packing box comprises the following steps that：(1) pretreatment of raw material；(2) batch mixing；(3) wire vent；(4) silk is received；(5) it weaves；(6) it dyes；(7) labeling.The present invention is a kind of drinks outer packing and its processing technology; using waste plastic as raw material; environmental protection and saving makes bottle by special process and weaves outer coatings, beautiful and generous; intention is full; it attracts eyeball, and plastic wire braided fabric heavily fortified point is without hard, it is light, intensity is high, has good cushioning effect; it can be very good protection bottle, convenience in transport sale.
Description
Technical field
The present invention relates to packing box fields, and in particular to a kind of Wines packing transparent box and its production technology.
Background technology
Wine is a kind of liquid commodity, on nowadays dazzling store shelf, mirrors the often wine of people's eyes first
Outer packing -- wine box.Wine box packaging play the role of to the sale of wine it is very important, especially its attract consumer, increase
Added value of product meets consumer's spiritual demand, consolidates the effect of brand and corporate image, is increasingly recognized by people, special
It is not certain valuable drinks, packaging often highlights its value, therefore the packaging of novel intention can often promote the pin of wine
It sells.Invention describes a kind of drinks outer packing and its processing technologys, and using waste plastic as raw material, environmental protection and saving, process is special
Technique makes bottle braiding outer coatings, and beautiful and generous, intention is full, attracts eyeball, and plastic wire braided fabric heavily fortified point has without hard
Good cushioning effect can be very good protection bottle, convenience in transport sale.
Invention content
In view of the deficiencies of the prior art, the purpose of the present invention is to provide a kind of drinks outer packing and its processing technologys.
Present invention solves the technical problem that following technical scheme may be used to realize：
The present invention specifically uses following technical scheme to achieve the goals above：
A kind of Wines packing transparent box, including each component of following parts by weight are prepared：65-70 parts of polypropylene brightens
4-5 parts of agent, 10-15 parts of titanium dioxide, 6-8 parts of ultramarine, 3-7 parts of hydroquinone, 5-15 parts of triacetin, the more benzene of polymethylene
Isocyanates 50-90 parts of Quito, 10-18 parts of polyacrylamide, 1-5 parts of stabilizer.
A kind of production technology of Wines packing transparent box, the technique procedure of processing are：
(1) pretreatment of raw material：Respectively to polypropylene, brightening agent, titanium dioxide, ultramarine, hydroquinone, triacetin,
Poly methylene poly phenyl poly isocyanate, polyacrylamide and stabilizer are dried to 110-120 DEG C, drying time 28-
Then 33min is crushed respectively again, particle diameter is 2-4mm after crushing；
(2) batch mixing：Each feed particles that step (1) obtains are uniformly mixed by list of ingredients；
(3) wire vent：The mixed raw material that step (2) is obtained is sent into plastic extruder, and thickness is squeezed out by plastic extruder
Degree is the plastic foil of 0.5-0.6mm, is first cooled to 85-95 DEG C to the plastic foil of extrusion, then using filament cutter to modeling after cooling
Expect film chopping, wherein the temperature of extruded stock bar is 185-210 DEG C in plastic extruder, and the rotating speed of extruded stock bar is 40-44r/
The temperature of min, threeway are 195-215 DEG C, and the drum rotation speed of filament cutter is 26-29r/min；
(4) silk is received：It silk made from wire vent step will be passed through be wound up into and receive on lead screw, when winding, the rotating speed for receiving lead screw was
25-30r/min；
(5) it weaves：On the basis of bottle, the silk received on lead screw is woven into bottle shape outer packing around bottle；
(6) it dyes：The bottle shape outer packing that step (5) obtains is subjected to colored drawing dyeing, room temperature after dyeing with acrylic paints
Under dry；
(7) labeling：The label with color printing is sticked on the outer surface of the outer packing after drying to dress up up to bottle outsourcing
Product.
Preferably, the plastic foil of extrusion is cooled down using cooling water in the step (3), the temperature of cooling water is 85-95
℃。
Preferably, the stabilizer is organic tin stabilizer.
Preferably, the polypropylene is polypropylene waste plastic.
In conclusion by adopting the above-described technical solution, the beneficial effects of the invention are as follows：
The present invention is a kind of drinks outer packing and its processing technology, and using waste plastic as raw material, environmental protection and saving, process is special
Technique makes bottle braiding outer coatings, and beautiful and generous, intention is full, attracts eyeball, and plastic wire braided fabric heavily fortified point is without hard, matter
Gently, intensity is high, has good cushioning effect, can be very good protection bottle, convenience in transport sale.
Specific implementation mode
In order to which those skilled in the art are better understood from the present invention, the present invention is made into one with reference to following embodiment
Step detailed description：
Embodiment 1：
A kind of Wines packing transparent box, including each component of following parts by weight are prepared：65 parts of polypropylene, brightening agent 4
Part, 10 parts of titanium dioxide, 6 parts of ultramarine, 3 parts of hydroquinone, 5 parts of triacetin, poly methylene poly phenyl poly isocyanate 50
Part, 10 parts of polyacrylamide, 1 part of stabilizer.
A kind of production technology of Wines packing transparent box, the technique procedure of processing are：
(1) pretreatment of raw material：Respectively to polypropylene, brightening agent, titanium dioxide, ultramarine, hydroquinone, triacetin,
Poly methylene poly phenyl poly isocyanate, polyacrylamide and stabilizer are dried to 110 DEG C, drying time 28min, then again
It crushes respectively, particle diameter is 2mm after crushing；
(2) batch mixing：Each feed particles that step (1) obtains are uniformly mixed by list of ingredients；
(3) wire vent：The mixed raw material that step (2) is obtained is sent into plastic extruder, and thickness is squeezed out by plastic extruder
Degree is the plastic foil of 0.5mm, is first cooled to 85 DEG C to the plastic foil of extrusion, then cut to plastic foil after cooling using filament cutter
Silk, wherein the temperature of extruded stock bar is 185 DEG C in plastic extruder, and the rotating speed of extruded stock bar is 40r/min, the temperature of threeway
It it is 195 DEG C, the drum rotation speed of filament cutter is 2r/min；
(4) silk is received：It silk made from wire vent step will be passed through be wound up into and receive on lead screw, when winding, the rotating speed for receiving lead screw was
25r/min；
(5) it weaves：On the basis of bottle, the silk received on lead screw is woven into bottle shape outer packing around bottle；
(6) it dyes：The bottle shape outer packing that step (5) obtains is subjected to colored drawing dyeing, room temperature after dyeing with acrylic paints
Under dry；
(7) labeling：The label with color printing is sticked on the outer surface of the outer packing after drying to dress up up to bottle outsourcing
Product.
Preferably, the plastic foil of extrusion is cooled down using cooling water in the step (3), the temperature of cooling water is 85 DEG C.
Preferably, the stabilizer is organic tin stabilizer.
Preferably, the polypropylene is polypropylene waste plastic.
The present invention is a kind of drinks outer packing and its processing technology, and using waste plastic as raw material, environmental protection and saving, process is special
Technique makes bottle braiding outer coatings, and beautiful and generous, intention is full, attracts eyeball, and plastic wire braided fabric heavily fortified point is without hard, matter
Gently, intensity is high, has good cushioning effect, can be very good protection bottle, convenience in transport sale.
Embodiment 2：
A kind of Wines packing transparent box, including each component of following parts by weight are prepared：70 parts of polypropylene, brightening agent 5
Part, 15 parts of titanium dioxide, 8 parts of ultramarine, 7 parts of hydroquinone, 15 parts of triacetin, poly methylene poly phenyl poly isocyanate 90
Part, 18 parts of polyacrylamide, 5 parts of stabilizer.
A kind of production technology of Wines packing transparent box, the technique procedure of processing are：
(1) pretreatment of raw material：Respectively to polypropylene, brightening agent, titanium dioxide, ultramarine, hydroquinone, triacetin,
Poly methylene poly phenyl poly isocyanate, polyacrylamide and stabilizer are dried to 120 DEG C, drying time 33min, then again
It crushes respectively, particle diameter is 4mm after crushing；
(2) batch mixing：Each feed particles that step (1) obtains are uniformly mixed by list of ingredients；
(3) wire vent：The mixed raw material that step (2) is obtained is sent into plastic extruder, and thickness is squeezed out by plastic extruder
Degree is the plastic foil of 0.6mm, is first cooled to 95 DEG C to the plastic foil of extrusion, then cut to plastic foil after cooling using filament cutter
Silk, wherein the temperature of extruded stock bar is 210 DEG C in plastic extruder, and the rotating speed of extruded stock bar is 44r/min, the temperature of threeway
It it is 215 DEG C, the drum rotation speed of filament cutter is 29r/min；
(4) silk is received：It silk made from wire vent step will be passed through be wound up into and receive on lead screw, when winding, the rotating speed for receiving lead screw was
30r/min；
(5) it weaves：On the basis of bottle, the silk received on lead screw is woven into bottle shape outer packing around bottle；
(6) it dyes：The bottle shape outer packing that step (5) obtains is subjected to colored drawing dyeing, room temperature after dyeing with acrylic paints
Under dry；
(7) labeling：The label with color printing is sticked on the outer surface of the outer packing after drying to dress up up to bottle outsourcing
Product.
Preferably, the plastic foil of extrusion is cooled down using cooling water in the step (3), the temperature of cooling water is 95 DEG C.
Preferably, the stabilizer is organic tin stabilizer.
Preferably, the polypropylene is polypropylene waste plastic.
After above-mentioned processing step, drinks outer packing is obtained, using waste plastic as raw material, environmental protection and saving, process is special
Technique makes bottle braiding outer coatings, and beautiful and generous, intention is full, attracts eyeball, and plastic wire braided fabric heavily fortified point has without hard
Good cushioning effect can be very good protection bottle, convenience in transport sale.
Embodiment 3：
A kind of Wines packing transparent box, including each component of following parts by weight are prepared：68 parts of polypropylene, brightening agent 5
Part, 12 parts of titanium dioxide, 7 parts of ultramarine, 5 parts of hydroquinone, 10 parts of triacetin, poly methylene poly phenyl poly isocyanate 70
Part, 15 parts of polyacrylamide, 4 parts of stabilizer.
A kind of production technology of Wines packing transparent box, the technique procedure of processing are：
(1) pretreatment of raw material：Respectively to polypropylene, brightening agent, titanium dioxide, ultramarine, hydroquinone, triacetin,
Poly methylene poly phenyl poly isocyanate, polyacrylamide and stabilizer are dried to 115 DEG C, drying time 30min, then again
It crushes respectively, particle diameter is 3mm after crushing；
(2) batch mixing：Each feed particles that step (1) obtains are uniformly mixed by list of ingredients；
(3) wire vent：The mixed raw material that step (2) is obtained is sent into plastic extruder, and thickness is squeezed out by plastic extruder
Degree is the plastic foil of 0.6mm, is first cooled to 90 DEG C to the plastic foil of extrusion, then cut to plastic foil after cooling using filament cutter
Silk, wherein the temperature of extruded stock bar is 200 DEG C in plastic extruder, and the rotating speed of extruded stock bar is 44r/min, the temperature of threeway
It it is 195 DEG C, the drum rotation speed of filament cutter is 28r/min；
(4) silk is received：It silk made from wire vent step will be passed through be wound up into and receive on lead screw, when winding, the rotating speed for receiving lead screw was
28r/min；
(5) it weaves：On the basis of bottle, the silk received on lead screw is woven into bottle shape outer packing around bottle；
(6) it dyes：The bottle shape outer packing that step (5) obtains is subjected to colored drawing dyeing, room temperature after dyeing with acrylic paints
Under dry；
(7) labeling：The label with color printing is sticked on the outer surface of the outer packing after drying to dress up up to bottle outsourcing
Product.
Preferably, the plastic foil of extrusion is cooled down using cooling water in the step (3), the temperature of cooling water is 90 DEG C.
Preferably, the stabilizer is organic tin stabilizer.
Preferably, the polypropylene is polypropylene waste plastic.
After above-mentioned processing step, drinks outer packing is obtained, using waste plastic as raw material, environmental protection and saving, process is special
Technique makes bottle braiding outer coatings, and beautiful and generous, intention is full, attracts eyeball, and plastic wire braided fabric heavily fortified point has without hard
Good cushioning effect can be very good protection bottle, convenience in transport sale.
It is the embodiment of the present invention as described above.The present invention is not limited to the above-described embodiments, anyone should learn that
The structure change made under the inspiration of the present invention, the technical schemes that are same or similar to the present invention each fall within this
Within the protection domain of invention.
Claims (5)
1. a kind of Wines packing transparent box, which is characterized in that each component including following parts by weight is prepared：Polypropylene 65-
70 parts, 4-5 parts of brightening agent, 10-15 parts of titanium dioxide, 6-8 parts of ultramarine, 3-7 parts of hydroquinone, 5-15 parts of triacetin are more
50-90 parts of polymethylene polyphenyl polyisocyanates, 10-18 parts of polyacrylamide, 1-5 parts of stabilizer.
2. a kind of production technology of Wines packing transparent box as described in claim 1, which is characterized in that the technique processing step
Suddenly it is：
(1) pretreatment of raw material：Respectively to polypropylene, brightening agent, titanium dioxide, ultramarine, hydroquinone, triacetin, mostly Asia
Methyl polyphenyl polyisocyanate, polyacrylamide and stabilizer are dried to 110-120 DEG C, drying time 28-33min, so
It crushes respectively again afterwards, particle diameter is 2-4mm after crushing；
(2) batch mixing：Each feed particles that step (1) obtains are uniformly mixed by list of ingredients；
(3) wire vent：The mixed raw material that step (2) is obtained is sent into plastic extruder, and squeezing out thickness by plastic extruder is
The plastic foil of 0.5-0.6mm is first cooled to 85-95 DEG C to the plastic foil of extrusion, then using filament cutter to plastic foil after cooling
Chopping, wherein the temperature of extruded stock bar is 185-210 DEG C in plastic extruder, and the rotating speed of extruded stock bar is 40-44r/min, three
Logical temperature is 195-215 DEG C, and the drum rotation speed of filament cutter is 26-29r/min；
(4) silk is received：It silk made from wire vent step will be passed through be wound up into and receive on lead screw, when winding, the rotating speed for receiving lead screw was 25-
30r/min；
(5) it weaves：On the basis of bottle, the silk received on lead screw is woven into bottle shape outer packing around bottle；
(6) it dyes：The bottle shape outer packing that step (5) obtains is subjected to colored drawing dyeing with acrylic paints, is dried in the air under room temperature after dyeing
It is dry；
(7) labeling：The label with color printing is sticked on the outer surface of the outer packing after drying up to bottle outer packing finished product.
3. a kind of production technology of Wines packing transparent box according to claim 2, which is characterized in that the step (3)
Middle to be cooled down to the plastic foil of extrusion using cooling water, the temperature of cooling water is 85-95 DEG C.
4. a kind of production technology of Wines packing transparent box according to claim 2, which is characterized in that the stabilizer is
Organic tin stabilizer.
5. a kind of production technology of Wines packing transparent box according to claim 2, which is characterized in that the polypropylene is
Polypropylene waste plastic.