CN108762000A - A kind of 3D glass exposures film manufacture craft - Google Patents
A kind of 3D glass exposures film manufacture craft Download PDFInfo
- Publication number
- CN108762000A CN108762000A CN201810463783.5A CN201810463783A CN108762000A CN 108762000 A CN108762000 A CN 108762000A CN 201810463783 A CN201810463783 A CN 201810463783A CN 108762000 A CN108762000 A CN 108762000A
- Authority
- CN
- China
- Prior art keywords
- film
- curved surface
- glass
- exposures
- manufacture craft
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of 3D glass exposures film manufacture crafts, include the following steps:(1)To 3D curved surface film prerinse;(2)Plasma cleans are carried out to the 3D curved surface films;(3)Film layer used in isolation UV light is sprayed to the 3D curved surface films;(4)Prebake conditions are carried out to the film layer on the 3D curved surface films;(5)UV exposure curings are carried out to the film layer on the 3D curved surface films;(6)Hot setting baking is carried out to the film layer on the 3D curved surface films;(7)Laser engraving pattern is carried out to the film layer on the 3D curved surface films.
Description
Technical field
The present invention relates to a kind of 3D glass exposures film manufacture crafts.
Background technology
Graph exposure is to transfer a pattern to by photochemical reaction using geometric figure on the film and be covered in base version
A kind of technique on photosensitive film, because the architectural characteristic of 3D bend glasses is that two sides is bent or four sides is bent, traditional screen printing
Brush can not use, and pattern exposure process is adaptable strong, selectively relatively low to shape of product structural requirement, is employed for
3D bend glasses are processed.
Traditional 3D bend glass exposure films are usually quartz glass chromium plating film or molybdenum film, are 2D planes.Because pattern by
There are aliasing when 2D glass is projected to 3D curved surfaces, therefore the poor accuracy period is long in manufacturing process.The exposure of 3D bend glasses is luxuriant and rich with fragrance
The shape that woods can realize the film and carry between object is arranged in pairs or groups, and makes design configuration can 1:It is difficult to solve industry on product for 1 Correct exposure
Topic;And 3D bend glass exposure film manufacture crafts, there are complex manufacturing technology, the period is long, the high problem of monolithic cost,
It cannot be satisfied 3D bend glass exposure film batch making demands.
Invention content
In view of this, the object of the present invention is to provide a kind of manufacture craft is simple, the period is short, the low 3D glass of manufacturing cost
Exposure film manufacture craft.
The present invention is realized using following scheme:A kind of 3D glass exposures film manufacture craft, includes the following steps:(1)It is right
3D curved surface film prerinse;(2)Plasma cleans are carried out to the 3D curved surface films;(3)Isolation UV light institute is sprayed to the 3D curved surface films
Use film layer;(4)Prebake conditions are carried out to the film layer on the 3D curved surface films;(5)It is solid that UV exposures are carried out to the film layer on the 3D curved surface films
Change;(6)Hot setting baking is carried out to the film layer on the 3D curved surface films;(7)Radium-shine carving is carried out to the film layer on the 3D curved surface films
Needle drawing shape.
Further, step(2)In, during plasma cleans air pressure be set as 0.2-0.4kg/cm2.
Further, step(3)In, the thicknesses of layers of spraying is 8-15 μm.
Further, step(4)In, prebake conditions temperature is 70-100 DEG C, and the prebake conditions time is:6-10min.
Further, step(5)In, UV exposure energies are:1500-2500mj, time for exposure be:8-12S.
Further, step(6)In, hot setting temperature:150-180 DEG C, the hot setting time:20-40min.
Further, step(7)In, the speed of radium-shine parameter is:1000-2000mm/s, electric current are:05-1.5A, frequency
For:60-100HZ.
Compared with prior art, the invention has the advantages that:3D bend glasses exposure film of the present invention makes work
Skill makes simply, and the time is short, cheap, selectively low to product structure characteristic, can generate institute according to known product pattern
The shape and size needed can be widely used in the production field of 3D glass exposure films making into the accurate film.
To make the objectives, technical solutions, and advantages of the present invention more comprehensible, specific embodiment and phase will be passed through below
Attached drawing is closed, invention is further described in detail.
Description of the drawings
Fig. 1 is that flow is embodied in 3D curved surfaces film manufacture craft of the present invention;
Fig. 2 is 3D curved surfaces film finished product drawing vertical view of the present invention;
The positions Fig. 3 3D curved surfaces film finished figure front elevation views of the present invention.
Specific implementation mode
As shown in Fig. 1 ~ 3, a kind of 3D glass exposures film manufacture craft includes the following steps:(1)It is pre- to the 3D curved surface films
Cleaning, removes the spot on surface or the impurity of dust fall;(2)Plasma cleans are carried out to the 3D curved surface films, removal surface is pre- clear
The stain left after washing;(3)Film layer used in isolation UV light is sprayed to the 3D curved surface films;(4)To the film on the 3D curved surface films
Layer carries out prebake conditions, to carry out precuring to film layer;(5)UV exposure curings are carried out to the film layer on the 3D curved surface films, with to spray
Film layer carries out photochemical reaction curing process;(6)Hot setting baking is carried out to the film layer on the 3D curved surface films;(7)To 3D songs
Film layer on the film of face carries out laser engraving pattern, and respective shapes and the high-precision size film are produced by product drawing requirement,
Process the required 3D curved surface films;It is multiple that the 3D glass exposure jig exposure film manufacture crafts can solve current manufacture craft
Miscellaneous, the period is long, the high problem of monolithic cost, can fully meet 3D bend glass exposure film batch making demands.
In the present embodiment, step(2)In, during plasma cleans air pressure be set as 0.2-0.4kg/cm2.
In the present embodiment, step(3)In, the thicknesses of layers of spraying is 8-15 μm.
In the present embodiment, step(4)In, prebake conditions temperature is 70-100 DEG C, and the prebake conditions time is:6-10min.
In the present embodiment, step(5)In, UV exposure energies are:1500-2500mj, time for exposure be:8-12S.
In the present embodiment, step(6)In, hot setting temperature:150-180 DEG C, the hot setting time:20-40min.
In the present embodiment, step(7)In, the speed of radium-shine parameter is:1000-2000mm/s, electric current are:05-1.5A,
Frequency is:60-100HZ.
The 3D bend glass exposure film manufacture crafts make simply, and the time is short, cheap, select product structure characteristic
Selecting property is low, and required shape and size can be generated according to known product pattern into the accurate film, can be widely used in 3D glass
The production field that glass exposure film makes.
Above-listed preferred embodiment, has been further described the object, technical solutions and advantages of the present invention, is answered
Understand, the foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all essences in the present invention
With within principle, any modification, equivalent replacement, improvement and so on should all be included in the protection scope of the present invention god.
Claims (7)
1. a kind of 3D glass exposures film manufacture craft, it is characterised in that:Include the following steps:(1)It is pre- to the 3D curved surface films clear
It washes;(2)Plasma cleans are carried out to the 3D curved surface films;(3)Film layer used in isolation UV light is sprayed to the 3D curved surface films;(4)To 3D
Film layer on the curved surface film carries out prebake conditions;(5)UV exposure curings are carried out to the film layer on the 3D curved surface films;(6)To 3D curved surfaces
Film layer on the film carries out hot setting baking;(7)Laser engraving pattern is carried out to the film layer on the 3D curved surface films.
2. 3D glass exposures film manufacture craft according to claim 1, it is characterised in that:Step(2)In, plasma is clear
Air pressure is set as 0.2-0.4kg/cm2 during clean.
3. 3D glass exposures film manufacture craft according to claim 1, it is characterised in that:Step(3)In, the film of spraying
Layer thickness is 8-15 μm.
4. 3D glass exposures film manufacture craft according to claim 1, it is characterised in that:Step(4)In, prebake conditions temperature
Degree is 70-100 DEG C, and the prebake conditions time is:6-10min.
5. 3D glass exposures film manufacture craft according to claim 1, it is characterised in that:Step(5)In, UV exposes energy
Amount is:1500-2500mj, time for exposure be:8-12S.
6. 3D glass exposures film manufacture craft according to claim 1, it is characterised in that:Step(6)In, hot setting
Temperature:150-180 DEG C, the hot setting time:20-40min.
7. 3D glass exposures film manufacture craft according to claim 1, it is characterised in that:Step(7)In, radium-shine parameter
Speed be:1000-2000mm/s, electric current are:05-1.5A, frequency are:60-100HZ.