CN108754573A - Anodic oxidation acid regurgitation technique - Google Patents
Anodic oxidation acid regurgitation technique Download PDFInfo
- Publication number
- CN108754573A CN108754573A CN201810707418.4A CN201810707418A CN108754573A CN 108754573 A CN108754573 A CN 108754573A CN 201810707418 A CN201810707418 A CN 201810707418A CN 108754573 A CN108754573 A CN 108754573A
- Authority
- CN
- China
- Prior art keywords
- table tune
- slot
- anodic oxidation
- acid solution
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anodic oxidation acid regurgitation techniques, include the following steps;Step A, anode pre-treatment;Step B, sulfuric acid solution is used in anodizing tank, and completes electrolysis film forming in 20 DEG C of temperature, 12v-14V voltages;Step C, into being cleaned in table tune slot, by thermosistor make the temperature of table tune slot at 20 DEG C or less and under the ultrasonic wave cooperation caused by supersonic generator in and gap in remaining acid solution, complete cleaning;Step D, into being cleaned in second table tune slot, the temperature of table tune slot remaining acid solution at 20 DEG C or less and under the ultrasonic wave cooperation caused by supersonic generator in second and in gap is made by thermosistor, completes secondary cleaning;Step E, it is dyed under certain pH value;Step F, is dried in drying box.Present invention setting is reasonable, ensures the efficiency of the effect and cleaning of cleaning, solves the technical deficiency that cannot prevent acid regurgitation completely in the prior art.
Description
Technical field
The invention belongs to anodized technology fields, and in particular to a kind of anodic oxidation acid regurgitation technique.
Background technology
The technique of NMT generally uses at present, and technology development is irregular, and the product acid regurgitation that plastic-aluminum combines still accounts for more very much not
Good ratio (5%~80%).According to existing solution pattern from nanometered disposal, plastic material, injection mold, injection parameters, anode
Equal processing procedures collaboration solves, and be easy to cause and mutually shifts responsibility onto others, delays the situation of project process.When aluminum component and plastics have 0.03mm~
When the gap of 0.05mm sizes, acid solution can be kept in anode oxidation process, acid solution can not be washed out by common table tune,
In dyeing course, acid solution is precipitated, and changes local pH, leads to not the bad referred to as acid regurgitation for normally catching color.Existing table
It is that an Optimization for Ultrasonic Wave and table are adjusted to adjust tank liquor, and acid regurgitation cannot be prevented completely by no matter how optimizing, to more difficult product without bright
Effective fruit.
Invention content
The object of the present invention is to provide a kind of anodic oxidation acid regurgitation techniques, it is intended to which solution cannot prevent completely in the prior art
The technical deficiency of acid regurgitation.
Realize that the technical solution of the object of the invention is a kind of anodic oxidation acid regurgitation technique, anodizing tank, two table tune slots
The thermosistor and supersonic generator being connected with the table tune slot, further include sealing of hole slot and drying box, include the following steps;
Step A, anode pre-treatment;
Step B, sulfuric acid solution is used in anodizing tank, and is electrolyzed to produce in 20 DEG C of temperature, the completion of 12v-14V voltages
Film;
Step C, into being cleaned in table tune slot, make the temperature of table tune slot at 20 DEG C or less by thermosistor and super
Ultrasonic wave cooperation caused by sonic generator is lower to neutralize remaining acid solution in gap, completes cleaning;
Step D, into being cleaned in second table tune slot, by thermosistor make the temperature of table tune slot 20 DEG C or less,
And second under the ultrasonic wave cooperation caused by supersonic generator in and gap in remaining acid solution, complete secondary cleaning;
Step E, it is dyed under certain pH value, and sealing of hole is completed in 85 DEG C~95 DEG C of sealing of hole slot;
Step F is placed in drying box after ultrasonic cleaning and is dried.
In the step A, anode pre-treatment includes oil removing, degreasing, neutralization, chemical polishing and first wash successively.
In stepb, the sulfuric acid solution that sulfuric acid solution is 180g-200g/L.
The LM625 reagents for being 30-50g/L in step C, in table tune slot.
In step D, it is the LM625 reagents of 30-50g/L in table tune slot.
Temperature in step F in drying box is 80 DEG C.
The present invention has the effect of positive:Present invention setting is reasonable, and there are two table tune slots for setting, and table tune slot all connects
It is connected to thermoregulator and supersonic generator, aluminium or plastics part can be made to become larger in low temperature environment intermediate gap, cooperation ultrasound
Wave frequency rate can quickly go out the Tibetan pickling in gap, ensure the efficiency of the effect and cleaning of cleaning, be conducive to following process behaviour
Make, solves the technical deficiency that cannot prevent acid regurgitation completely in the prior art.
Description of the drawings
In order to make the content of the present invention more clearly understood, right below according to specific embodiment and in conjunction with attached drawing
The present invention is described in further detail, wherein:
Fig. 1 is the process flow diagram of the present invention.
Specific implementation mode
(embodiment 1)
Fig. 1 shows that a kind of specific implementation mode of the present invention, wherein Fig. 1 are the process flow diagram of the present invention.
See Fig. 1, a kind of anodic oxidation acid regurgitation technique, it is intended to which solution cannot prevent the technology of acid regurgitation completely not in the prior art
Foot.
Realize that the technical solution of the object of the invention is a kind of anodic oxidation acid regurgitation technique, anodizing tank, two table tune slots
The thermosistor and supersonic generator being connected with the table tune slot, further include sealing of hole slot and drying box, include the following steps;
Step A, anode pre-treatment;
Step B, sulfuric acid solution is used in anodizing tank, and is electrolyzed to produce in 20 DEG C of temperature, the completion of 12v-14V voltages
Film;
Step C, into being cleaned in table tune slot, make the temperature of table tune slot at 20 DEG C or less by thermosistor and super
Ultrasonic wave cooperation caused by sonic generator is lower to neutralize remaining acid solution in gap, completes cleaning;
Step D, into being cleaned in second table tune slot, by thermosistor make the temperature of table tune slot 20 DEG C or less,
And second under the ultrasonic wave cooperation caused by supersonic generator in and gap in remaining acid solution, complete secondary cleaning;
Step E, it is dyed under certain pH value, and sealing of hole is completed in 85 DEG C~95 DEG C of sealing of hole slot;
Step F is placed in drying box after ultrasonic cleaning and is dried.In the present embodiment, thermosistor is freezing equipment,
Medicament temperature in table tune slot can be controlled at 20 degree hereinafter, minimum be reduced to 1 degree.
In the step A, anode pre-treatment includes oil removing, degreasing, neutralization, chemical polishing and first wash successively.
In stepb, the sulfuric acid solution that sulfuric acid solution is 180g-200g/L.
The LM625 reagents for being 30-50g/L in step C, in table tune slot.
In step D, it is the LM625 reagents of 30-50g/L in table tune slot.
Temperature in step F in drying box is 80 DEG C.
Present invention setting is reasonable, and there are two table tune slots for setting, and table tune slot is all connected with thermoregulator and ultrasound
Wave producer can make aluminium or plastics part become larger in low temperature environment intermediate gap, and cooperation ultrasonic frequency can be quickly by gap
Interior Tibetan pickling goes out, and ensures the efficiency of the effect and cleaning of cleaning, is conducive to subsequent machining operations, solves in the prior art not
It can prevent the technical deficiency of acid regurgitation completely.
Obviously, the above embodiment of the present invention be only to clearly illustrate example of the present invention, and not be pair
The restriction of embodiments of the present invention.For those of ordinary skill in the art, may be used also on the basis of the above description
To make other variations or changes in different ways.There is no necessity and possibility to exhaust all the enbodiments.And these
The obvious changes or variations that the connotation for belonging to of the invention is extended out still fall within protection scope of the present invention.
Claims (6)
1. a kind of anodic oxidation acid regurgitation technique, anodizing tank, two table tune slots and the thermosistor being connected with the table tune slot
And supersonic generator, further include sealing of hole slot and drying box, it is characterised in that:Include the following steps;
Step A, anode pre-treatment;
Step B, sulfuric acid solution is used in anodizing tank, and completes electrolysis film forming in 20 DEG C of temperature, 12v-14V voltages;
Step C, into being cleaned in table tune slot, make the temperature of table tune slot at 20 DEG C or less and in ultrasonic wave by thermosistor
Ultrasonic wave cooperation caused by generator is lower to neutralize remaining acid solution in gap, completes cleaning;
Step D, into being cleaned in second table tune slot, make the temperature of table tune slot at 20 DEG C or less by thermosistor and
Remaining acid solution in ultrasonic wave cooperation lower second of neutralization gap caused by supersonic generator, completes secondary cleaning;
Step E, it is dyed under certain pH value, and sealing of hole is completed in 85 DEG C~95 DEG C of sealing of hole slot;
Step F is placed in drying box after being cleaned in ultrasonic wave and is dried.
2. anodic oxidation acid regurgitation technique according to claim 1, it is characterised in that:In the step A, anode pre-treatment
Include oil removing, degreasing, neutralization, chemical polishing and first wash successively.
3. anodic oxidation acid regurgitation technique according to claim 2, it is characterised in that:In stepb, sulfuric acid solution is
The sulfuric acid solution of 180g-200g/L.
4. anodic oxidation acid regurgitation technique according to claim 3, it is characterised in that:It is 30- in step C, in table tune slot
The LM625 reagents of 50g/L.
5. anodic oxidation acid regurgitation technique according to claim 4, it is characterised in that:In step D, it is 30- in table tune slot
The LM625 reagents of 50g/L.
6. anodic oxidation acid regurgitation technique according to claim 5, it is characterised in that:Temperature in step F in drying box
It is 80 DEG C.